The document investigates the relationship between drilling time and depth of cut/kerf width using abrasive jet machining. Experiments were conducted drilling glass, ceramic, and fiber sheets of varying thicknesses. The results show that drilling time increases non-linearly with depth, with more difficult materials taking more time to drill deeper holes due to loss of air pressure and jet energy. Drilling width (kerf) was also measured at different air pressures and times. The kerf width increased with longer drilling times and higher pressures due to greater divergence of the abrasive jet stream.
A Review on Multi-objective Optimization of Process Parameter of Abrasive Wat...IJARIIT
Glass fiber reinforced polymer (GFRP) composites are increasingly being used in a large number of applications in product manufacturing because of the superior advantages they offer compared to other traditional and non-traditional materials such as high strength to weight ratio, high modulus, high fracture toughness, and corrosion and thermal resistance, low cost of production, light weight, inherent strength, weather-resistant finish and variety of surface textures. However conventional machining of Glass fiber reinforced polymer (GFRP) is not so economical and ease, on the other hand non-conventional processes like laser cutting, abrasive water jet machining (AWJM), and electric discharge machining (EDM) etc., have a very good potential in overcoming these machining difficulties. Among these AWJM is commonly employed for very hard and brittle materials due to its Economical and Technical significance.
A Review on Multi-objective Optimization of Process Parameter of Abrasive Wat...IJARIIT
Glass fiber reinforced polymer (GFRP) composites are increasingly being used in a large number of applications in product manufacturing because of the superior advantages they offer compared to other traditional and non-traditional materials such as high strength to weight ratio, high modulus, high fracture toughness, and corrosion and thermal resistance, low cost of production, light weight, inherent strength, weather-resistant finish and variety of surface textures. However conventional machining of Glass fiber reinforced polymer (GFRP) is not so economical and ease, on the other hand non-conventional processes like laser cutting, abrasive water jet machining (AWJM), and electric discharge machining (EDM) etc., have a very good potential in overcoming these machining difficulties. Among these AWJM is commonly employed for very hard and brittle materials due to its Economical and Technical significance.
The abrasive jet machine is classified as a non-conventional machine and in this slide introduction about it the structure and, advantage, and disadvantage
Honing is an abrasive machining process that produces a precision surface on a metal work piece by scrubbing an abrasive stone against it along a controlled path.
Honing is primarily used to improve the geometric form of a surface, but may also improve the surface texture.
The mixture of abrasive particles with high pressurised air impinges through the nozzle towards the brittle material.Abrasive jet machining is done by use of abrasives(AL2O3,SIC,SYNTHETIC DIAMOND,ETC.,) particles. The main components are nozzle,mixing chamber,dehumidifier,regulator and pressure gauge.
How to polish and maintain injection molds?JasmineHL
The polishing described in plastic mold processing is very different from the surface polishing required in other industries. Strictly speaking, the polishing of the mold should be called mirror processing. Not only does it have high requirements for polishing itself, but it also has a high standard for surface flatness, smoothness, and geometric accuracy. Surface polishing generally requires only a shiny surface.
this presentation is about various types of finishing process such as lapping,honing,super finishing ,polishing which performed after the work primary operations are completed.and these various methods are known as secondary operations.
The abrasive jet machine is classified as a non-conventional machine and in this slide introduction about it the structure and, advantage, and disadvantage
Honing is an abrasive machining process that produces a precision surface on a metal work piece by scrubbing an abrasive stone against it along a controlled path.
Honing is primarily used to improve the geometric form of a surface, but may also improve the surface texture.
The mixture of abrasive particles with high pressurised air impinges through the nozzle towards the brittle material.Abrasive jet machining is done by use of abrasives(AL2O3,SIC,SYNTHETIC DIAMOND,ETC.,) particles. The main components are nozzle,mixing chamber,dehumidifier,regulator and pressure gauge.
How to polish and maintain injection molds?JasmineHL
The polishing described in plastic mold processing is very different from the surface polishing required in other industries. Strictly speaking, the polishing of the mold should be called mirror processing. Not only does it have high requirements for polishing itself, but it also has a high standard for surface flatness, smoothness, and geometric accuracy. Surface polishing generally requires only a shiny surface.
this presentation is about various types of finishing process such as lapping,honing,super finishing ,polishing which performed after the work primary operations are completed.and these various methods are known as secondary operations.
Advance machining processes are used where higher accuracy and surface finish is required. One of them, Abrasive jet machining is a non-traditional machining process in which a high-pressure air stream and abrasive particles impinge on a work surface through a nozzle. Abrasive jet machining (AJM) removes material through the action of a focused beam of abrasive jet directed at the workpiece the resulting erosion can be used for cutting, drilling and debarring etc. With the increase of needs for machining of ceramics, semiconductors, electronic devices and L.C.D., AJM has become a useful technique for micromachining. it is more useful in industries for precision work. Material removal rate during this process affected by different parameters like abrasive particle size, the velocity of abrasive flow rate, gas pressure, standoff distance etc.
Manufacturer, Exporter, Wholesaler, Trader & Retailer of a vast collection of Industrial Blasting Machines, Shot Blasting Machine, Air Operated Blasting Machines, Construction Equipment etc.
Accelerate your Kubernetes clusters with Varnish CachingThijs Feryn
A presentation about the usage and availability of Varnish on Kubernetes. This talk explores the capabilities of Varnish caching and shows how to use the Varnish Helm chart to deploy it to Kubernetes.
This presentation was delivered at K8SUG Singapore. See https://feryn.eu/presentations/accelerate-your-kubernetes-clusters-with-varnish-caching-k8sug-singapore-28-2024 for more details.
UiPath Test Automation using UiPath Test Suite series, part 3DianaGray10
Welcome to UiPath Test Automation using UiPath Test Suite series part 3. In this session, we will cover desktop automation along with UI automation.
Topics covered:
UI automation Introduction,
UI automation Sample
Desktop automation flow
Pradeep Chinnala, Senior Consultant Automation Developer @WonderBotz and UiPath MVP
Deepak Rai, Automation Practice Lead, Boundaryless Group and UiPath MVP
Smart TV Buyer Insights Survey 2024 by 91mobiles.pdf91mobiles
91mobiles recently conducted a Smart TV Buyer Insights Survey in which we asked over 3,000 respondents about the TV they own, aspects they look at on a new TV, and their TV buying preferences.
Builder.ai Founder Sachin Dev Duggal's Strategic Approach to Create an Innova...Ramesh Iyer
In today's fast-changing business world, Companies that adapt and embrace new ideas often need help to keep up with the competition. However, fostering a culture of innovation takes much work. It takes vision, leadership and willingness to take risks in the right proportion. Sachin Dev Duggal, co-founder of Builder.ai, has perfected the art of this balance, creating a company culture where creativity and growth are nurtured at each stage.
Slack (or Teams) Automation for Bonterra Impact Management (fka Social Soluti...Jeffrey Haguewood
Sidekick Solutions uses Bonterra Impact Management (fka Social Solutions Apricot) and automation solutions to integrate data for business workflows.
We believe integration and automation are essential to user experience and the promise of efficient work through technology. Automation is the critical ingredient to realizing that full vision. We develop integration products and services for Bonterra Case Management software to support the deployment of automations for a variety of use cases.
This video focuses on the notifications, alerts, and approval requests using Slack for Bonterra Impact Management. The solutions covered in this webinar can also be deployed for Microsoft Teams.
Interested in deploying notification automations for Bonterra Impact Management? Contact us at sales@sidekicksolutionsllc.com to discuss next steps.
Encryption in Microsoft 365 - ExpertsLive Netherlands 2024Albert Hoitingh
In this session I delve into the encryption technology used in Microsoft 365 and Microsoft Purview. Including the concepts of Customer Key and Double Key Encryption.
Essentials of Automations: Optimizing FME Workflows with ParametersSafe Software
Are you looking to streamline your workflows and boost your projects’ efficiency? Do you find yourself searching for ways to add flexibility and control over your FME workflows? If so, you’re in the right place.
Join us for an insightful dive into the world of FME parameters, a critical element in optimizing workflow efficiency. This webinar marks the beginning of our three-part “Essentials of Automation” series. This first webinar is designed to equip you with the knowledge and skills to utilize parameters effectively: enhancing the flexibility, maintainability, and user control of your FME projects.
Here’s what you’ll gain:
- Essentials of FME Parameters: Understand the pivotal role of parameters, including Reader/Writer, Transformer, User, and FME Flow categories. Discover how they are the key to unlocking automation and optimization within your workflows.
- Practical Applications in FME Form: Delve into key user parameter types including choice, connections, and file URLs. Allow users to control how a workflow runs, making your workflows more reusable. Learn to import values and deliver the best user experience for your workflows while enhancing accuracy.
- Optimization Strategies in FME Flow: Explore the creation and strategic deployment of parameters in FME Flow, including the use of deployment and geometry parameters, to maximize workflow efficiency.
- Pro Tips for Success: Gain insights on parameterizing connections and leveraging new features like Conditional Visibility for clarity and simplicity.
We’ll wrap up with a glimpse into future webinars, followed by a Q&A session to address your specific questions surrounding this topic.
Don’t miss this opportunity to elevate your FME expertise and drive your projects to new heights of efficiency.
JMeter webinar - integration with InfluxDB and GrafanaRTTS
Watch this recorded webinar about real-time monitoring of application performance. See how to integrate Apache JMeter, the open-source leader in performance testing, with InfluxDB, the open-source time-series database, and Grafana, the open-source analytics and visualization application.
In this webinar, we will review the benefits of leveraging InfluxDB and Grafana when executing load tests and demonstrate how these tools are used to visualize performance metrics.
Length: 30 minutes
Session Overview
-------------------------------------------
During this webinar, we will cover the following topics while demonstrating the integrations of JMeter, InfluxDB and Grafana:
- What out-of-the-box solutions are available for real-time monitoring JMeter tests?
- What are the benefits of integrating InfluxDB and Grafana into the load testing stack?
- Which features are provided by Grafana?
- Demonstration of InfluxDB and Grafana using a practice web application
To view the webinar recording, go to:
https://www.rttsweb.com/jmeter-integration-webinar
Transcript: Selling digital books in 2024: Insights from industry leaders - T...BookNet Canada
The publishing industry has been selling digital audiobooks and ebooks for over a decade and has found its groove. What’s changed? What has stayed the same? Where do we go from here? Join a group of leading sales peers from across the industry for a conversation about the lessons learned since the popularization of digital books, best practices, digital book supply chain management, and more.
Link to video recording: https://bnctechforum.ca/sessions/selling-digital-books-in-2024-insights-from-industry-leaders/
Presented by BookNet Canada on May 28, 2024, with support from the Department of Canadian Heritage.
Software Delivery At the Speed of AI: Inflectra Invests In AI-Powered QualityInflectra
In this insightful webinar, Inflectra explores how artificial intelligence (AI) is transforming software development and testing. Discover how AI-powered tools are revolutionizing every stage of the software development lifecycle (SDLC), from design and prototyping to testing, deployment, and monitoring.
Learn about:
• The Future of Testing: How AI is shifting testing towards verification, analysis, and higher-level skills, while reducing repetitive tasks.
• Test Automation: How AI-powered test case generation, optimization, and self-healing tests are making testing more efficient and effective.
• Visual Testing: Explore the emerging capabilities of AI in visual testing and how it's set to revolutionize UI verification.
• Inflectra's AI Solutions: See demonstrations of Inflectra's cutting-edge AI tools like the ChatGPT plugin and Azure Open AI platform, designed to streamline your testing process.
Whether you're a developer, tester, or QA professional, this webinar will give you valuable insights into how AI is shaping the future of software delivery.
Epistemic Interaction - tuning interfaces to provide information for AI supportAlan Dix
Paper presented at SYNERGY workshop at AVI 2024, Genoa, Italy. 3rd June 2024
https://alandix.com/academic/papers/synergy2024-epistemic/
As machine learning integrates deeper into human-computer interactions, the concept of epistemic interaction emerges, aiming to refine these interactions to enhance system adaptability. This approach encourages minor, intentional adjustments in user behaviour to enrich the data available for system learning. This paper introduces epistemic interaction within the context of human-system communication, illustrating how deliberate interaction design can improve system understanding and adaptation. Through concrete examples, we demonstrate the potential of epistemic interaction to significantly advance human-computer interaction by leveraging intuitive human communication strategies to inform system design and functionality, offering a novel pathway for enriching user-system engagements.
Neuro-symbolic is not enough, we need neuro-*semantic*Frank van Harmelen
Neuro-symbolic (NeSy) AI is on the rise. However, simply machine learning on just any symbolic structure is not sufficient to really harvest the gains of NeSy. These will only be gained when the symbolic structures have an actual semantics. I give an operational definition of semantics as “predictable inference”.
All of this illustrated with link prediction over knowledge graphs, but the argument is general.
Assuring Contact Center Experiences for Your Customers With ThousandEyes
I012625461
1. IOSR Journal of Mechanical and Civil Engineering (IOSR-JMCE)
e-ISSN: 2278-1684,p-ISSN: 2320-334X, Volume 12, Issue 6 Ver. II (Nov. - Dec. 2015), PP 54-61
www.iosrjournals.org
DOI: 10.9790/1684-12625461 www.iosrjournals.org 54 | Page
Investigation of Drilling Time V/S Depth of Cut & Kerf Using
Abrasive Jet Machining
Dr.K.Rajasekhara Reddy1
, D.V.Srikanth2
1
Professor, Department of Mechanical Engineering, ST MARTIN’S Engineering College, Secunderabad,
India
2
Associate Professor, Department of Mechanical Engineering,St.Martins Engineering college,
Secunderabad, India
Abstract: Abrasive jet machining (AJM) is a processing non-traditional machine which operates materials
without producing shock and heat. AJM is applied for many purposes like drilling, cutting, cleaning, and
etching operation. The particles of the materials get accelerate in gas stream and are made to focus on
machine. It makes small fracture if particle focuses on the surface and the gas stream includes abrasive
particles and fractured particles away. The process parameters are used like variables which effect metal
removal. They are carrier gas, abrasive, velocity of abrasive, work material, and nozzle tip distance (NTD).In
abrasive jet machining, a focused stream of abrasive particles, carried by high pressure air or gas is made to
impinge on the work surface through a nozzle and the work material is made to impinge on the work surface
through a nozzle and work material is removed by erosion by high velocity abrasive particles. The effect of the
depth of material and the material characteristics on drilling time were investigated and discussed. Through
this work, it was observed that machinability index of the materials drilled plays an important role in AJM
process. The work investigates that there is nonlinear relation in drilling time v/s drilling depth and material of
low machinability takes more time to drill because of as depth increases air pressure losses its cutting ability. It
is also Investigate the effect of kerf and SOD on drilling time.
Index Terms: Abrasive Jet Machining, Drilling, Abrasive, Depth of Cut, SOD.
I. Introduction
An abrasive jet is one of the most recently developed non-traditional manufacturing processes.
Abrasive jets have been used first time in 1980’s for the cutting of glass materials. Here We are going to first
study, how abrasive jet machining or what is the mechanism of material removal. What we have here? Here we
have a nozzle. In this nozzle, there is an opening or a inner diameter which is typically around 1 to 5 millimetre.
Through this nozzle a mixture of gas and abrasive particles are fed. They are fed at a velocity of 150 to 300
meter per second (12). These abrasive particles when they are issued from this particular nozzle they would
interact with my work piece. Typically for abrasive jet machining brittle work piece brittle materials are
machined more efficiently (10). So if you are using abrasive jet machining as a machining process you should
rather try to machine glasses or other brittle materials rather than low carbon steel. Once these abrasive particle,
interact with the work piece, they have some amount of kinetic energy.
As they interact with the work piece that kinetic energy is converted in to mechanical work. They
would intend the surface. They would create a small crater and the kinetic energy would be absorbed with the
work done. For producing this particular crater and in this way with multiple impact gradually we will be getting
a machining. So this is a pure mechanical domain process where the mechanical energy of a high speed abrasive
high speed abrasive is used for machining the material and the machining occurs because of the brittle fracture
of the work piece. Now, let us come to the general description of abrasive jet machining equipment what we
require?
Figure 1: The Flow of Air and Abrasives towards work
2. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 55 | Page
Typically the mass flow rate of abrasive particles is around 2 to 20 grams per minute. So they are also
consumption rate of abrasive is rather less. Now, as we have discussed we require a gas to propel those abrasive
particles. So other than this abrasive particles this carrier gas would also play an important role. Generally air
can be used or else carbon dioxide or nitrogen can be used. If we are using carbon dioxide or nitrogen, then you
do not require this compressor. Instead of that, you will issue the gas from a gas cylinder. So instead of the
compressor you will issue it from the gas cylinder that is also possible. So as a carrier gas typically air carbon
dioxide and nitrogen is used. Typical density of the air is something around this. Velocity of the gas is around
500 to 700 meter per second. Pressure is around 10 Bar flow rate is around three to five to thirty lpm. One of the
most important parameter is the pressure of this gas carrier gas because depending on the pressure, we will be
getting a particular velocity and that will decide to what extent abrasive particles would be or the abrasive jet
would be abrasive particles should be accelerated(3).
So once abrasive and the carrier gas they have mixed together, we will get the abrasive jet. The drop in
velocity Causes because of the abrasive particles are mixing with the carrier gas. The carrier gas would lose
momentum and will gradually transfer it momentum to the abrasive jet. So that the abrasives can be accelerated
and in the process your velocity with drop down than there is mixing ratio. What is mixing ratio? How much
abrasive you are pumping in to the system as compared to the mass flow rate of the gas. If you are pumping too
much abrasive, they would not be accelerated properly. So mixing ratio is once again a very important
parameter then stand-off distance. How far is your nozzle from the jet from the work piece. At what angle the jet
is interacting with the work piece? If there is no technical or geometrical requirement typically impingement
angle is around 90 degree but it can also be as less as 60 degree, then comes the nozzle material because this
nozzle material has to be such it is handling abrasive particles which are moving through the nozzle at 300 meter
per second. Typically tungsten carbide nozzles are used or even wear resistance sapphire nozzles are used. The
inner nozzles are characterized by their internal diameter and the internal diameter of the nozzle would be 0.2 to
0.8 millimetre. Why they have to be wear resistance? If they are not wear resistance, then you will not get good
life from the nozzle quite often under industrial situation the life expected around hundred hours or ten hours. If
you are getting ten minutes by using steel nozzles, then all the time you would be changing your nozzle there
would be no production. So appreciable life of the nozzle is very important for which we require a wear
resistance nozzle material.
The life of a nozzle must be partly defined by its application. Exacting operations, such as cutting,
required that nozzles be changed more often than when is in etching or cleaning. As nozzles wear, the jet stream
tends to diffuse faster resulting in material damage outside the intended line of cut. This is known as stray
cutting or overspreads. Rectangular nozzles create less overspread when compared with round ones.
The various abrasives used in Abrasive Jet Machine are selected in application. Aluminium oxide, one
of the most commonly used materials, is used to clean, cut and deburr. Silicon carbide, a harder abrasive, is
effective for the same applications as aluminium oxide is usually applied only when the work piece material is
very hard. Silicon carbide is also known as carborundum, is a compound of silicon and carbon with chemical
formula SiC. It occurs in nature as the extremely rare mineral moissanite. Silicon carbide powder has been
mass-produced since 1893 for use as an abrasive. Polishing surfaces to a Matt finish or penning surfaces is
accomplished with glass beads and can therefore be used for heavier cleaning and penning operations. abrasive
particle size is important, abrasive are available in many sizes ranging from 10u to 50u. The similar sizes are
most useful for polishing and cleaning (6,7,9), while the larger sizes are best for cutting and penning.
Abrasives are not reused because “chips” from the work piece material clog nozzle and also the cutting
action of used particles is degraded. Under impact situations plastic deformation in brittle materials occurs only
when small spherical particles impinging on the target surfaces above a certain velocity. Thus there exists a
velocity surface above a certain velocity, which causes plastic deformation resulting in the formation of lateral
cracks. As soon as the spherical particle touches the surface of a flat body contact stresses are setup.
Gas cylinders contains gas which is carried out by pipes, passing away from filter, which separates the
dust particles and the pressure regulator is used to maintain the required gas pressure, then the gas collects in
chamber where fine abrasive particles (50micron) are present. Here gas mixes with abrasive and a vibrator is
connected to the chamber for better mixing which vibrates at 50c/s. Then this mixture is carried to the nozzle
which concentrates the mixture at the work piece and erodes the material from the work piece.
Material removal rate of abrasive jet machining is quite high as compared to conventional machining.
The material removal in Abrasive Jet Machining occurs due to brittle fracture (3). There is another
consideration. Once a single abrasive particle interacts with the brittle material there would be a fracture and this
fracture we be assume to be hemispherical and the diameter of the fracture would be the chordal length of the
indentation. As the abrasive particle interacts with the work piece, it will create a small crater. That crater would
be created because abrasive particles are highly kinetic energetic. So the kinetic energy of the abrasive particle
would be absorbed as it creates that crater and the diameter of that particular crater or indentation would be
equal to the chordal length. Another assumption is kinetic energy of the abrasive particles would be considered
3. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 56 | Page
to be fully utilized. It is not partial; whatever is the kinetic energy we will assume that total kinetic energy is
utilized in doing the work done. They would be assumed not to disintegrate and they would be spherical in
shape and the particle size would be characterized by the mean diameter.
This is a process of removal of material by impact erosion through the action of concentrated high
velocity stream of grit abrasives entrained in high velocity gas stream. AJM is different from shot or sand
blasting, as in AJM, finer abrasive grits are used and parameters can be controlled more effectively providing
better control over Product quality. In AJM, generally, the abrasive particles of around 50 microns grit size
would impinge on the work material at velocity of 200 m/s from a nozzle of ID 0.5mm with a standoff distance
of around 2mm. The kinetic energy of the abrasive particles would sufficient to provide material removal due to
brittle fracture of the work piece or even micro cutting by the abrasives.
II. Experimental Work & Methodology
Experimental set up:
Experiments were conducted to confirm the validity of the proposed model as well as the models
found in the literature. The experimental work was carried on a test rig which was designed and
manufactured in the workshops of the Mechanical Engineering Department, ST MARTIN’S Engineering
College, Secunderabad as in Fig (8). The abrasive grits of Silicon Carbide (Sic) was mixed with air stream
ahead of the nozzle and the abrasive flow rate was kept constant throughout the machining process. The jet
nozzle was made of Tungsten Carbide to carry high wear resistance and increase in Life of nozzle. Several
nozzles were manufactured with different bore diameters of 2 mm, 3 mm and 4 mm. drilling of glass, Fibre
and Ceramic sheets was conducted by setting the test rig on the parameters listed in Table 1.
Fig 2: Impingement of Abrasives through Nozzle
Table 1 Process Parameters of AJM
1 Type of abrasive
2 Carrier gas
3 Nozzle tip distance
4 Size of abrasive
5 Velocity of abrasive jet
6 Mixing ratio
7 Work material
8 Nozzle design
9 Shape of cut
4. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 57 | Page
III. Material
Glass, Ceramics and Fibre sheets are used as work piece materials because of their homogeneous
properties (1, 2, 6, 9). The test specimens were cut into square and rectangular shape for machining on AJM unit
having various thicknesses. In machine the initial weights of glass, fibre and ceramic specimens were measured
with the help of digital balance. After machining the final weights were measured with the help of digital
balance to calculate the material removal rate. First the abrasive that was Sic in powder form was fed in the
hopper carefully. After that compressor connections were checked. The glass specimen was properly clamped
on cross slide with the help of various clamps. As the Compressor was switched on, the hopper gate valve was
opened so that abrasive grains were mixed with air jet coming from the compressor and focused on the
specimen with help of nozzle.
Table 2: CharacteristicsOf Different Variables
IV. Results & Discussions
Experiments are conducted on Glass Ceramic tile and Fibre sheets of Various thicknesses (2mm, 4mm,
6mm,8mm).Keeping Pressure, SOD ,Nozzle Diameter and Abrasive Flow Rate as Constant .The time for each
drilling is noted . The experimental results are Expressed with the help of Table 3,Table 4 . The results of
drilling time versus drilling depth are compared with the help of graphs as shown in Fig(3,4,5). And also the
results of drilling time versus drilling width are compared with the help of graphs as shown in Fig(6,7,8).
The exercise of varying depth of drilling on time of drilling shows that the relation between drilling
time and the depth of drill is not linear. The time to mill as the drilling depth increases are not proportional to
the increase in depth. For a difficult to machine material (low machinability index), the non-linearity effect is
more prominent and rate of increase in drilling time is higher. This could be due to the loss of energy of jet as
depth increases. This is due to the two reasons. One, as the drilling depth increases stand of distance also
increases which causes reduction in jet pressure due to increase in distance and divergence of the stream of jet
which leads to increase in jet foot print as show in fig(3,4,5), And hence take more time to cut. Another reason
can be that depth of drill increases while machining blind pocket, the restricted volume of closed pocket
increases and this causes the loss of energy of the fresh abrasive particles going to strike the work piece due to
their collision with used abrasive particles and chips or work removed while machining.
Table 3 :
Material Depth of cut
(mm)
Time for drilling
(sec)
Glass
2 6.5
4 9.3
6 11.6
8 13.2
Ceramic tile
4 10.8
8 11.3
10 13.1
12 14.0
Fibre sheet
2 5.8
4 6.6
6 8.7
8 11.4
Medium Air , CO2 ,N2
Abrasive SiC, Al2O3 (of size 20μ to 50μ )
Flow rate of abrasive 3 to 20 gram/min
Velocity 150 to 300 m/min
Pressure 2 to 8 kg/cm2
Nozzle size 0.07 to 0.40 mm
Material of nozzle WC, Sapphire
Nozzle life 12 to 300 hr
Standoff distance 0.25 to 15 mm (8mm generally)
Work material Non Metals like glass, ceramics,
and granites. Metals and alloys of hard
materials like germanium, silicon etc
part application Drilling, cutting, deburring ,cleaning
5. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 58 | Page
The Width of Cut (Kerf) of the Material that is machined by Abrasive Jet Machining is the difference
between Top Surface diameter and the Bottom Surface diameter of the tapered portion that was drilled (4) .The
Experiments are conducted to find out the width of cut at various Air Pressures .The time of Machining is also
taken in to consideration for each width of cut (kerf).For these Experiments the air pressure, Abrasive flow rate
and diameter of the nozzle are kept constant.
Table 4 :
Material Width of cut(kerf) (mm) Time
for
drilling
(sec)
Sod
(mm)
Tkw(mm) Bkw(mm) Actual
width
Glass
8 9 6 3 5.3
10 7 4.2 2.8 6.5
12 6.1 3.8 2.3 9.0
14 4.5 3 1.5 12.4
Ceramic
tile
8 7 5 2 15
10 6 4.2 1.8 18
12 4.5 2.9 1.6 23
14 4 3.3 0.7
28
Fibre
sheet
8 8.2 4.8 3.4 5.1
10 6.3 3.7 2.6 6.3
12 4.9 2.8 2.1 7.6
14 3.8 2.2 1.6 9.4
TSD : Top surface Diameter ,BSD : bottom surface Diameter
Figure 3: Drilling Time v/s Depth of cut in AJM for Glass
Figure 4: Drilling Time v/s Depth of cut in AJM for Ceramic Tile
Figure 5: Drilling Time v/s Depth of cut in AJM for Fibre Sheet
6. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 59 | Page
The exercise of varying width of cut (kerf) on time of drilling shows that the relation between drilling
time and the width of drill is not linear (6). The time to mill as the drilling width increases are not proportional
to the increase in kerf. From fig(6,7,8) it is observed that by decrease in width will tends to increase in time but
the relation between time and width of cut is not linear. The width of cut can be reduced by keeping proper
stand of distance between nozzle and work surface. It is also observed that by increase in SOD the time for
cutting will be increased.
As the distance between the face of nozzle and the working surface of the work increases, the diameter
of hole also increases because higher the nozzle tip distance allows the jet to expand before impingement which
may increase vulnerability to external drag from the surrounding environment.
Figure 6: Drilling Time v/s width of cut in AJM for Glass Sheet
Figure 7: Drilling Time v/s width of cut in AJM for Ceramic Tile
7. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 60 | Page
Figure 8: Abrasive Jet Machining Setup established at SMEC
Fig 9: Sic Abrasives of different Grit Sizes
Fig 10 : Glass, Ceramic and Fibre Sheets drilled by AJM Process
V. Conclusion
This work is focused on exploring the effect of material thickness on drilling in drilling time using
abrasive jet machining. For this Experimentation glass, ceramics, fibre sheets are considered due to their
Brittleness where these are difficult to machine by conventional methods. At each of these locations for each of
the work piece material holes are generated of thickness 2,4,6 and 8mm for glass and fibre sheets ,4,8,10,12mm
Ceramic tiles. The influence of time on width of cut (kerf) is also discussed by keeping the variation in SOD’s
.As the Result of the Present work it is observed that drilling time is non-linearly related to material thickness
and he machinability of the material significantly influences the time to drill a hole of specified size . It is also
noticed that the width of cut decreases on decrease in SOD, The drilling time increases with the increment of
Kerf. The work in future may be extended for more depths (less than 2 mm and more than 8 mm for glass and
fibre ,less than 4mm and more than 12mm for ceramics) and with the help of larger drilling time vis-à-vis
material thickness depth data, a mathematical model may be proposed to find out energy loss.
8. Investigation of Drilling Time V/S Depth of Cut & Kerf Using Abrasive Jet Machining
DOI: 10.9790/1684-12625461 www.iosrjournals.org 61 | Page
Acknowledgment
The authors here by thank the authors of the below mentioned references for their valuable contribution
which enabled us make this comparison.
References
[1]. A.EI-Domiaty, H.M.Abd EI –Hafez, and M.A.Shaker(2009) “Drilling of glass sheets by abrasive jet machining”,nWorld
Academy of Science , Engineering and Technology 56.
[2]. M L Neema and P C Pandey. 'Erosion of Glass When Act Upon by an Abrasive Jet' Proceedings of International GI
ConfneTice on Wear of Materials, 1977.
[3]. A. P. Verma and G. K. Lal Publication(1984)“An experimental study of abrasive jet machining”, International Journal of
Machine Tool Design and Research, Volume 24, Issue 1,pp 19-29.
[4]. U.D.Gulhani,P.P.Patkar,S.P.Patel,A.A.Patel et al , Analysis of AJM parameters on kerf width of hard and brittle materials like
ceramics IJDMT. April -2013.
[5]. P K Sarkar and P C Pandey. 'Some Investigations on the Abrasive Jet Machining', Journal of the Institution ofEngineers (India),
vol 56, ME 6, 1976.
[6]. Bhaskar Chandra Kandpal1
* Naveen Kumar2
Rahul Kumar3
Rahul Sharma4
Sagar Deswal5
Machining Of Glass And Ceramic
With Alumina And Silicon Carbide In Abrasive Jet Machining, International Journal of Advanced Engineering Technology,
IJAET/Vol.II/ Issue IV/October-December, 2011/251-256.
[7]. V. K. Jain, S. K. Choudhury and K. M. Ramesh, On the machining of alumina and glass - International Journal of Machine
Tools and Manufacture Volume 42, Issue 11, September 2002, pages269–276.
[8]. Shanmugam D. K., Masood S. H. 2009. An investigation of kerf characteristics in abrasive water jet cutting of layered
composites, International Journal of Material Processing Technology 209: pp 3887–3893.
[9]. Sagar, Ankur(2009) Mathematical Modelling Of Abrasive Jet Machining For Metal Removal Rate On Fiber Glass Using
Abrasive Silicon Carbide. 30-Jul-2009.
[10]. Ingulli .C.N,”Abrasive Jet Machining”Tool and Manufacturing Engg –vol-59 p-28-1967.