The document provides an overview of man-made fibers, including their history, classification, definitions, and applications. It discusses the major steps in the production of man-made staple fibers such as polymerization and spinning. The document also examines properties like crystallinity, molecular weight distribution, and structural models. Additionally, it provides insights into the global synthetic fiber market and common applications of various man-made fibers.
Filament-core yarns are produced to take advantage of both filament and staple fibre properties. They offer good strength and uniformity without sacrificing the staple fibre yarn-like surface characteristics. Core-spun yarns containing spandex provide fabric designers with broad possibilities, because such stretchable yarns can be constructed with a wide range of properties using virtually any type of hard fibres as the cover yarn. However, a disadvantage of the core yarns is that the staple fibre sheath may slip along the filament when being pulled to pass over or when being rubbed by machine parts during further mechanical processes. But it is very easy to produce core-spun yarn containing spandex in a conventional ring frame after doing some modification of the machine.
Introduction to Textile Engineering , Textile Process, Fiber, Yarn,Spinning, Department of Textile , Classification and their flowchart
Visit blog: http://www.merchandisingbangla.com/
Filament-core yarns are produced to take advantage of both filament and staple fibre properties. They offer good strength and uniformity without sacrificing the staple fibre yarn-like surface characteristics. Core-spun yarns containing spandex provide fabric designers with broad possibilities, because such stretchable yarns can be constructed with a wide range of properties using virtually any type of hard fibres as the cover yarn. However, a disadvantage of the core yarns is that the staple fibre sheath may slip along the filament when being pulled to pass over or when being rubbed by machine parts during further mechanical processes. But it is very easy to produce core-spun yarn containing spandex in a conventional ring frame after doing some modification of the machine.
Introduction to Textile Engineering , Textile Process, Fiber, Yarn,Spinning, Department of Textile , Classification and their flowchart
Visit blog: http://www.merchandisingbangla.com/
Pile fabrics: Manufacturing methods include woven pile fabric formation & others methods such as knit pile fabric, tufted pile fabrics etc. A "Terry" or a "Terry Towel" as is generally known is a woven pile fabric formed by slack tension weave process. of weaving.
every natural fiber has unique textile property like Strength elongation and length. these properties are important for making yarn and fabric in the textile industry.
Drawframe is one of the important machines in yarn spinning line. It is prepared for combining and drawing slivers and removing card irregularities of textile fibres.
Pilling is formation of little balls of fibers (pills) on the surface of a fabric which is caused by abrasion in wear.
Pilling is the tendency of fibers to come loose from a fabric surface and form balled particles of fiber
Pile fabrics: Manufacturing methods include woven pile fabric formation & others methods such as knit pile fabric, tufted pile fabrics etc. A "Terry" or a "Terry Towel" as is generally known is a woven pile fabric formed by slack tension weave process. of weaving.
every natural fiber has unique textile property like Strength elongation and length. these properties are important for making yarn and fabric in the textile industry.
Drawframe is one of the important machines in yarn spinning line. It is prepared for combining and drawing slivers and removing card irregularities of textile fibres.
Pilling is formation of little balls of fibers (pills) on the surface of a fabric which is caused by abrasion in wear.
Pilling is the tendency of fibers to come loose from a fabric surface and form balled particles of fiber
Mercerization is a important part ofTextile. May be it help you a lot. I am trying to make it easy and important part are must be included in this slide.Thanks a lot.
fiber strength and fiber fineness are described in detail about the machinery and discussed about new computerized testing machines which are used to determine the strength and fineness of the fiber.
Bicomponent fibers are filaments made up of two different polymers that are extruded from the same spinneret with both polymers contained within the same filament but separated by a fine plane. The two polymers differ in chemical nature or physical properties such as molecular weight
this slide in mercerization is prepared in chemical processing in textile and it could help a lot of students or lecturers who might be looking for web handout, presentation or seminar. it is openly accessible for all.
Biological screening of herbal drugs: Introduction and Need for
Phyto-Pharmacological Screening, New Strategies for evaluating
Natural Products, In vitro evaluation techniques for Antioxidants, Antimicrobial and Anticancer drugs. In vivo evaluation techniques
for Anti-inflammatory, Antiulcer, Anticancer, Wound healing, Antidiabetic, Hepatoprotective, Cardio protective, Diuretics and
Antifertility, Toxicity studies as per OECD guidelines
A Strategic Approach: GenAI in EducationPeter Windle
Artificial Intelligence (AI) technologies such as Generative AI, Image Generators and Large Language Models have had a dramatic impact on teaching, learning and assessment over the past 18 months. The most immediate threat AI posed was to Academic Integrity with Higher Education Institutes (HEIs) focusing their efforts on combating the use of GenAI in assessment. Guidelines were developed for staff and students, policies put in place too. Innovative educators have forged paths in the use of Generative AI for teaching, learning and assessments leading to pockets of transformation springing up across HEIs, often with little or no top-down guidance, support or direction.
This Gasta posits a strategic approach to integrating AI into HEIs to prepare staff, students and the curriculum for an evolving world and workplace. We will highlight the advantages of working with these technologies beyond the realm of teaching, learning and assessment by considering prompt engineering skills, industry impact, curriculum changes, and the need for staff upskilling. In contrast, not engaging strategically with Generative AI poses risks, including falling behind peers, missed opportunities and failing to ensure our graduates remain employable. The rapid evolution of AI technologies necessitates a proactive and strategic approach if we are to remain relevant.
Model Attribute Check Company Auto PropertyCeline George
In Odoo, the multi-company feature allows you to manage multiple companies within a single Odoo database instance. Each company can have its own configurations while still sharing common resources such as products, customers, and suppliers.
Welcome to TechSoup New Member Orientation and Q&A (May 2024).pdfTechSoup
In this webinar you will learn how your organization can access TechSoup's wide variety of product discount and donation programs. From hardware to software, we'll give you a tour of the tools available to help your nonprofit with productivity, collaboration, financial management, donor tracking, security, and more.
Honest Reviews of Tim Han LMA Course Program.pptxtimhan337
Personal development courses are widely available today, with each one promising life-changing outcomes. Tim Han’s Life Mastery Achievers (LMA) Course has drawn a lot of interest. In addition to offering my frank assessment of Success Insider’s LMA Course, this piece examines the course’s effects via a variety of Tim Han LMA course reviews and Success Insider comments.
Francesca Gottschalk - How can education support child empowerment.pptxEduSkills OECD
Francesca Gottschalk from the OECD’s Centre for Educational Research and Innovation presents at the Ask an Expert Webinar: How can education support child empowerment?
June 3, 2024 Anti-Semitism Letter Sent to MIT President Kornbluth and MIT Cor...Levi Shapiro
Letter from the Congress of the United States regarding Anti-Semitism sent June 3rd to MIT President Sally Kornbluth, MIT Corp Chair, Mark Gorenberg
Dear Dr. Kornbluth and Mr. Gorenberg,
The US House of Representatives is deeply concerned by ongoing and pervasive acts of antisemitic
harassment and intimidation at the Massachusetts Institute of Technology (MIT). Failing to act decisively to ensure a safe learning environment for all students would be a grave dereliction of your responsibilities as President of MIT and Chair of the MIT Corporation.
This Congress will not stand idly by and allow an environment hostile to Jewish students to persist. The House believes that your institution is in violation of Title VI of the Civil Rights Act, and the inability or
unwillingness to rectify this violation through action requires accountability.
Postsecondary education is a unique opportunity for students to learn and have their ideas and beliefs challenged. However, universities receiving hundreds of millions of federal funds annually have denied
students that opportunity and have been hijacked to become venues for the promotion of terrorism, antisemitic harassment and intimidation, unlawful encampments, and in some cases, assaults and riots.
The House of Representatives will not countenance the use of federal funds to indoctrinate students into hateful, antisemitic, anti-American supporters of terrorism. Investigations into campus antisemitism by the Committee on Education and the Workforce and the Committee on Ways and Means have been expanded into a Congress-wide probe across all relevant jurisdictions to address this national crisis. The undersigned Committees will conduct oversight into the use of federal funds at MIT and its learning environment under authorities granted to each Committee.
• The Committee on Education and the Workforce has been investigating your institution since December 7, 2023. The Committee has broad jurisdiction over postsecondary education, including its compliance with Title VI of the Civil Rights Act, campus safety concerns over disruptions to the learning environment, and the awarding of federal student aid under the Higher Education Act.
• The Committee on Oversight and Accountability is investigating the sources of funding and other support flowing to groups espousing pro-Hamas propaganda and engaged in antisemitic harassment and intimidation of students. The Committee on Oversight and Accountability is the principal oversight committee of the US House of Representatives and has broad authority to investigate “any matter” at “any time” under House Rule X.
• The Committee on Ways and Means has been investigating several universities since November 15, 2023, when the Committee held a hearing entitled From Ivory Towers to Dark Corners: Investigating the Nexus Between Antisemitism, Tax-Exempt Universities, and Terror Financing. The Committee followed the hearing with letters to those institutions on January 10, 202
Unit 8 - Information and Communication Technology (Paper I).pdfThiyagu K
This slides describes the basic concepts of ICT, basics of Email, Emerging Technology and Digital Initiatives in Education. This presentations aligns with the UGC Paper I syllabus.
Acetabularia Information For Class 9 .docxvaibhavrinwa19
Acetabularia acetabulum is a single-celled green alga that in its vegetative state is morphologically differentiated into a basal rhizoid and an axially elongated stalk, which bears whorls of branching hairs. The single diploid nucleus resides in the rhizoid.
Macroeconomics- Movie Location
This will be used as part of your Personal Professional Portfolio once graded.
Objective:
Prepare a presentation or a paper using research, basic comparative analysis, data organization and application of economic information. You will make an informed assessment of an economic climate outside of the United States to accomplish an entertainment industry objective.
Overview on Edible Vaccine: Pros & Cons with Mechanism
OVERVIEW OF MAN-MADE FIBERS
1. OVERVIEW OF MAN-MADE FIBRES
S/N NAMES REGISTRATION NUMBER
1 OCITI INNOCENT OLUR BU/UG/2016/1725
2 NAMIREMBE SUZAN BU/UG/2016/70
3 SHARIFA SHABAN BU/UP/2016/511
2. HISTORY OF MAN-MADE FIBERS
• The first man-made fiber was invented by a Swiss
chemist George Audemars in 1855 who produced
artificial silk.
• Frenchman Hilaire de Chardonnet, realized the first
industrial production of man-made fibers with
cellulose-based fiber (chardonnay silk) in 1891.
• In 1891, a new way to dissolve cellulose and spin
viscose yarn was introduced by Charles F. Cross,
3. CONT’D
• The first patent for the production of synthetic fiber
was filed by Fritz Klatte in 1913 relating to
polyvinylchloride fibers, though mass production was
till 1939.
• In 1930, Wallace H. Carothers from DuPont found the
first polyester out of which, it was possible to draw
fibers but due to its low melting point, he focused on
making polyamide.
• In 1935, Carothers succeeded in spinning polyamide
4. CONT’D
• In 1930, the German Paul Schlack produced polyamide
6(perlon fibers) but mass production started in 1950
due to the war.
• In 1941, J.R. Whinfield and J.T. Dickson invented in
England a melt spinning process for polyester by
polycondensation, which went into mass production
after the war.
• Polyester became the most important man-made fiber
type in the fiber industry.
• In 1942, Robert Hein spun polyacrylonitrile fibers after
5. TYPES OF MAN-MADE FIBRES
The whole group of man-made fibers can be sub-divided
into three major categories(sources where they are
derived):
• Natural polymers, which are man-made fibers derived
from nature.
• Synthetic polymers, which are man-made fibers
produced through additional or condensational
polymerization.
7. DEFINITIONS (ISO STANDARD)
• Man-made fiber; generic name for filament yarn, staple fiber and
monofilaments.
• Filament; man-made fiber of very great length.
• Filament yarn; man-made fiber yarn comprising one or more
filaments.
• Monofilament; filament yarn comprising many filaments up to
30,000 dtex(tow)
• Monofilament yarn; filament yarn consisting a filament with
thickness of up to 0.1mm.
• Tow; filament yarn above 30,000 dtex.
• Staple fiber; fibers of limited length.
8. INTRODUCTION TO FUNDAMENTALS OF MAN-MADE
STAPLE FIBRE SPINNING
Production of man-made staple fiber includes the following
steps:
1. Polymerization.
• The term polymerization defines the process of
macromolecules formation through repetition of basic units.
• Polymerization reactions are activated and controlled during
the process by various parameters, as temperature, pressure,
catalyzers, reaction stabilizers.
• The number of repetitive units is termed degree of
9. CONT’D
• From processing point of view, polymerization can be
carried out by mass treatment, solution or dispersion
(suspension, emulsion).
• Engineering-wise; this process can be:
Discontinuous, reagents are entirely pre-loaded into the
reactor and as soon as polymerization is completed, the
products are unloaded. It’s best suited for small-scale
production.
Continuous, reagents are introduced at one end and
10. CONT’D
•The polymers can appear as follows:
Solution, to be conveyed to the spinning
department.
Melted polymer, to be conveyed to the spinning
department or transformed into grains(chips) for
subsequent use.
Suspension, from which the polymer is separated
11. CONT’D
2. Spinning
• This is the process of extrusion of molten polymers
through bored devices(spinnerets) which are able to
solidify in a continuous flow.
3. Dulling: this is the addition of a white dulling
agent (titanium dioxide in grains), to give the fibers a
“dull” appearance, which distinguishes them from the
untreated fibers.
12. CONT’D
• The fiber is termed on the basis of the added quantity of
titanium dioxide (dullness degree) as follows:
Bright fiber: a fiber without or with minimal quantities of
titanium dioxide.
Semi-bright fiber: a slightly delustred fiber(<0.25%).
Semi-dull fiber: delustred fiber with 0.25-0.5% titanium
dioxide contents.
Dull fiber: fiber with 0.5-1% titanium dioxide.
Super-dull fiber: fiber with 1-3% titanium dioxide.
13. CRYSTALLINITY
• Crystallinity refers to the degree of structural order in a
solid. In a crystal, the atoms or molecules are arranged
in a regular, periodic manner.
• The degree of crystallinity has a big influence on
hardness, density, transparency and diffusion.
• The long molecules of a typical fiber-forming material
are able to pack together closely alongside one another,
like sticks in a bundle of faggots. The regularity of
structure brought about by this arrangement results in
regions of crystallinity in the fiber.
14. CONT’D
• These are regions in which a number of molecules are
aligned in such a way that strong forces of attraction
hold the molecules together.
• The bonds developed in this way are not familiar to
chemical bonds, but they are stronger than the normal
forces of attraction exerted between individual
molecules.
• The degree of order introduced by these regions
determines the usefulness of a potential fiber. The
15. CONT’D
• The ratio of crystalline to amorphous regions has an
important influence on the properties of any fiber. In
natural fibers, it is by nature, but in case of man-made
fiber the crystalline-amorphous ratio may be controlled
to a large degree by the condition which the fiber is
produced. This process is known as ‘drawing’ or
‘stretching’.
16. STRUCTURAL MODELS
• The chemical structure of linear polymers determines the degree of
conformational mobility of the chain segments of these molecules.
Both chain mobility and molecular structure, in turn, greatly
influence fiber structure.
• Flexible chain molecules may crystallize partially to form structures
that conform with the classical crystalline–amorphous model(A).
• A: classical structural model of amorphous–crystalline fiber
polymers. Examples are polyamide, polyester, and viscose
rayon. Long period (l)10–30nm.
17. CONT’D
• Spandex fibers, on the other hand, have a special
domain structure, because the chemical structure of
these polymers changes considerably in the various
segments along the polymer chain(B).
• B: structural model of spandex fibers (polyurethane).
Length of hard segment 2.5nm; length of soft segment
15.0nm
18. CONT’D
• The relatively planar structure of aramids and poly-
heterocyclic compounds, their conformational rigidity,
and their tendency to form lyotropic structures in the
spinning solution are consistent with a structural model
in which the inter-crystalline segments are bridged(C).
• C: structural model of aramid fibers (p-structures). No
amorphous phases present; stretched molecules due to
lyotropic structures during fiber formation.
19. CONT’D
• Even more planar molecules form graphite like
structures(D).
• D: structural model of carbon fibers; graphite structure
20. MOLECULAR WEIGHT DISTRIBUTION
• Molecular weight distribution describes the relationship
between the number of moles of each polymer species
(ni) and the molar mass (mi) of that species.
• Different average values can be defined, depending on
the statistical method applied.
• In practice four averages are used, representing
the weighted mean taken with the mole fraction, the
weight fraction, and two other functions which can be
21. CONT’D
• Number average molar mass (Mn).
The number average molar mass is a way of
determining the molecular mass of a polymer.
The number average molecular mass of a polymer can
be determined by gel permeation
chromatography, viscometry.
It can be calculated by:
22. CONT’D
• Weight average molar mass (mw).
The weight average molar mass or weight is another
way of describing the molar mass of a polymer.
It can be determined by static light scattering, small
angle neutron scattering, x-ray scattering,
and sedimentation velocity.
It can be calculated as:
23. CONT’D
• Z average molar mass (mz), (z is for centrifugation;
from German zentrifuge).
The z-average molar mass is the third moment or
third power average molar mass. The z-average
molar mass can be determined with
ultracentrifugation. The melt elasticity of a polymer is
dependent on mz
It can be calculated as:
24. CONT’D
• Viscosity average molar mass (mv).
This determines the absolute viscosity of polymer
solution of different concentration.
It can be determined by a viscometer.
It can be calculated as:
25. GLOBAL SYNTHETIC FIBRE MARKET
• The global synthetic fibers market size was valued at USD
51,213.0 million in 2016.
• The superior chemical, physical and mechanical properties
of synthetic fibers are expected to support the market
growth over the forecast period.
1. Regional insight
Asia pacific is estimated to be the fastest-growing region
with a CAGR of 7.0% from 2017 to 2025.
Asia pacific was valued at USD 34,765.2 million in 2016.
26. CONT’D
The increased demand can be attributed to the presence of
a number of applications including clothing, home
furnishing, automotive, and filtration.
The growth of these application segments is expected to
27. CONT’D
2. Application insight
Synthetic fibers exhibit advantageous properties such as
strength, elasticity, lightweight, washability, softness,
cost effectiveness and special properties such as wrinkle
resistance, crease recovery, moisture resistance, and
high lustre. Owing to these factors, these fibers are
preferred in various applications including clothing,
home furnishing, automotive, filtration, construction,
toys, different types of ropes and net manufacturing.
28. CONT’D
The U.S. Market was valued at USD 4,301.6 million in
2016 and is anticipated to register a CAGR of 5.3% from
2017 to 2025. The rising demand from clothing industry
in the U.S. is expected to boost the growth.
29. CONT’D
3. Types insight
The demand for polyester fiber is growing on account of its
useful properties which include abrasion and chemical
resistance. The need for polyester is increasing as affordable
synthetic fiber in clothing application due to rise in middle-
class population in emerging economies.
Asia pacific region is leading in both the production and
consumption of polyester and the trend is expected to
continue over the forecast period. Polyester emerged as the
most significant segment holding share of 48.26% of total
30. CONT’D
4. Competitive insight
The market is fragmented in nature with the presence of several
global and regional players like Toray industries Inc., E. I.
Dupont de Nemours and company, lenzing AG, Indorama
corporation, Mitsubishi chemical holdings corporation and china
petroleum corporation, which comply with the regulatory
framework of different countries.
These companies invest in research and development of
synthetic fibers specific to applications such as filtration,
clothing and home furnishings. They are incorporating backward
31. APPLICATION OF MAN-MADE FIBERS
• Polyester: used as cushioning and insulating material in
pillows, garments etc.
• Cupro: linings, outwear; casual and formal wears with
comfort.
• Viscose: used in making dresses, linings, shirts, shorts,
coats, jackets and other outwears.
• Acetate: cigarette filters and women’s wear due to its
good luster.
32. CONT’D
• Zein: making tough and strong fabrics, warms as wool,
resistant to mildew, insects, sunlight etc.
• Casein fiber: used in blends with wool for soft handle
and warmth.
• Alginate fibers: used in food and drink industries,
pharmacies and chemical industries.
• Elastomer(rubber): specialized application where high
elasticity is necessary in textile structures(bicycle tubes,
33. CONT’D
• Polypropylene: packaging applications due to chemical
resistance and weldability.
• Polyacrylonitrile (PAN): pressure vessels, fishing rods,
military aircraft missile when oxidized.
• Modacrylics: used in where environmental resistance or
flame resistance is required.
• Vinyl fibers: application where low flammability in apparel
is required.
• Polyamide: high abrasion resistance and melting point;
clothing, automotive and body armor.
34. CONT’D
• Glass fibers: mats and fabrics for thermal, sound, electrical
insulation, high strength fabrics.
• Metal fibers: communication lines, stainless steel fibers used
in carpets.
• Carbon fibers: bicycle equipment due to its light weight,
rigidity, strength and stretch resistance.
• Polyurethane: used in home furnishings such as furniture,
bedding and carpet underlay
• Elastane/ spandex: tights, sportswear, swimwear, corsetry