The cupola furnace is used to melt iron and produce cast iron. It has different zones with varying temperatures that require different refractory materials for lining. The combustion zone at the bottom requires acid refractories like alumina and alumina-silicon carbide bricks. The upper zones use materials like gunning mixes, castables and ramming masses containing alumina and silicon carbide to resist basic slag. While basic refractories would normally be used, acid refractories perform better in the cupola's basic slag environment due to protective slag layers formed on the refractory surface.
complete description of foundary workshop of manufacturing practice.in this complete description of tools ,method of moulding and casting used in foundary workshop.
Welding process
Arc Welding
Resistance Welding
Oxy fuel Gas Welding
Other Fusion Welding Processes
Solid State Welding
Weld Quality
Weld ability
Design Considerations in Welding
A cupola furnace is a melting device used in foundries that can be used to melt cast iron, Ni resist iron and some bronzes
Cupola furnace is employed for melting scrap metal or pig iron for production of various cast irons.
complete description of foundary workshop of manufacturing practice.in this complete description of tools ,method of moulding and casting used in foundary workshop.
Welding process
Arc Welding
Resistance Welding
Oxy fuel Gas Welding
Other Fusion Welding Processes
Solid State Welding
Weld Quality
Weld ability
Design Considerations in Welding
A cupola furnace is a melting device used in foundries that can be used to melt cast iron, Ni resist iron and some bronzes
Cupola furnace is employed for melting scrap metal or pig iron for production of various cast irons.
Muffle Furnace is a front-loading box-type oven or kiln used for high-temperature applications such as fusing
glass, creating enamel coatings, ceramics and soldering and brazing articles. Weiber muffle furnace is also used
by chemists in order to determine what proportion of a sample is non-combustible and non-volatile (i.e., ash).
A training seminar on induction furnace by stead fast engineers pvt ltdsteadfast123
A training seminar on induction furnace by stead fast engineers pvt ltd. find here Induction Furnace manufacturers,
Induction heater manufacturers,
Induction Billet heater Manufacturers,
Induction Melting furnace manufacturers,
Induction Furnace Manufacturers in India,
Induction Billet heater manufacturers in India,
Induction heating system,
Induction Melting Furnace for your source need.
Introduction to furnace and its types.
Stead Fast Engineers Pvt Ltd one of the Leading manufacturers of Induction Furnace in india. find here Induction heater,Induction Melting furnace,
Induction heating system,Induction Billet heaterfor your sourcing needs.
A Rotary kiln is a pyroprocessing device used to raise materials to a high temperature (calcination) in a continuous process. Materials produced using rotary kilns include: Cement. Lime.
Digital Transformation and IT Strategy Toolkit and TemplatesAurelien Domont, MBA
This Digital Transformation and IT Strategy Toolkit was created by ex-McKinsey, Deloitte and BCG Management Consultants, after more than 5,000 hours of work. It is considered the world's best & most comprehensive Digital Transformation and IT Strategy Toolkit. It includes all the Frameworks, Best Practices & Templates required to successfully undertake the Digital Transformation of your organization and define a robust IT Strategy.
Editable Toolkit to help you reuse our content: 700 Powerpoint slides | 35 Excel sheets | 84 minutes of Video training
This PowerPoint presentation is only a small preview of our Toolkits. For more details, visit www.domontconsulting.com
Personal Brand Statement:
As an Army veteran dedicated to lifelong learning, I bring a disciplined, strategic mindset to my pursuits. I am constantly expanding my knowledge to innovate and lead effectively. My journey is driven by a commitment to excellence, and to make a meaningful impact in the world.
What are the main advantages of using HR recruiter services.pdfHumanResourceDimensi1
HR recruiter services offer top talents to companies according to their specific needs. They handle all recruitment tasks from job posting to onboarding and help companies concentrate on their business growth. With their expertise and years of experience, they streamline the hiring process and save time and resources for the company.
RMD24 | Debunking the non-endemic revenue myth Marvin Vacquier Droop | First ...BBPMedia1
Marvin neemt je in deze presentatie mee in de voordelen van non-endemic advertising op retail media netwerken. Hij brengt ook de uitdagingen in beeld die de markt op dit moment heeft op het gebied van retail media voor niet-leveranciers.
Retail media wordt gezien als het nieuwe advertising-medium en ook mediabureaus richten massaal retail media-afdelingen op. Merken die niet in de betreffende winkel liggen staan ook nog niet in de rij om op de retail media netwerken te adverteren. Marvin belicht de uitdagingen die er zijn om echt aansluiting te vinden op die markt van non-endemic advertising.
Putting the SPARK into Virtual Training.pptxCynthia Clay
This 60-minute webinar, sponsored by Adobe, was delivered for the Training Mag Network. It explored the five elements of SPARK: Storytelling, Purpose, Action, Relationships, and Kudos. Knowing how to tell a well-structured story is key to building long-term memory. Stating a clear purpose that doesn't take away from the discovery learning process is critical. Ensuring that people move from theory to practical application is imperative. Creating strong social learning is the key to commitment and engagement. Validating and affirming participants' comments is the way to create a positive learning environment.
The world of search engine optimization (SEO) is buzzing with discussions after Google confirmed that around 2,500 leaked internal documents related to its Search feature are indeed authentic. The revelation has sparked significant concerns within the SEO community. The leaked documents were initially reported by SEO experts Rand Fishkin and Mike King, igniting widespread analysis and discourse. For More Info:- https://news.arihantwebtech.com/search-disrupted-googles-leaked-documents-rock-the-seo-world/
Cracking the Workplace Discipline Code Main.pptxWorkforce Group
Cultivating and maintaining discipline within teams is a critical differentiator for successful organisations.
Forward-thinking leaders and business managers understand the impact that discipline has on organisational success. A disciplined workforce operates with clarity, focus, and a shared understanding of expectations, ultimately driving better results, optimising productivity, and facilitating seamless collaboration.
Although discipline is not a one-size-fits-all approach, it can help create a work environment that encourages personal growth and accountability rather than solely relying on punitive measures.
In this deck, you will learn the significance of workplace discipline for organisational success. You’ll also learn
• Four (4) workplace discipline methods you should consider
• The best and most practical approach to implementing workplace discipline.
• Three (3) key tips to maintain a disciplined workplace.
Attending a job Interview for B1 and B2 Englsih learnersErika906060
It is a sample of an interview for a business english class for pre-intermediate and intermediate english students with emphasis on the speking ability.
Discover the innovative and creative projects that highlight my journey throu...dylandmeas
Discover the innovative and creative projects that highlight my journey through Full Sail University. Below, you’ll find a collection of my work showcasing my skills and expertise in digital marketing, event planning, and media production.
Unveiling the Secrets How Does Generative AI Work.pdfSam H
At its core, generative artificial intelligence relies on the concept of generative models, which serve as engines that churn out entirely new data resembling their training data. It is like a sculptor who has studied so many forms found in nature and then uses this knowledge to create sculptures from his imagination that have never been seen before anywhere else. If taken to cyberspace, gans work almost the same way.
Skye Residences | Extended Stay Residences Near Toronto Airportmarketingjdass
Experience unparalleled EXTENDED STAY and comfort at Skye Residences located just minutes from Toronto Airport. Discover sophisticated accommodations tailored for discerning travelers.
Website Link :
https://skyeresidences.com/
https://skyeresidences.com/about-us/
https://skyeresidences.com/gallery/
https://skyeresidences.com/rooms/
https://skyeresidences.com/near-by-attractions/
https://skyeresidences.com/commute/
https://skyeresidences.com/contact/
https://skyeresidences.com/queen-suite-with-sofa-bed/
https://skyeresidences.com/queen-suite-with-sofa-bed-and-balcony/
https://skyeresidences.com/queen-suite-with-sofa-bed-accessible/
https://skyeresidences.com/2-bedroom-deluxe-queen-suite-with-sofa-bed/
https://skyeresidences.com/2-bedroom-deluxe-king-queen-suite-with-sofa-bed/
https://skyeresidences.com/2-bedroom-deluxe-queen-suite-with-sofa-bed-accessible/
#Skye Residences Etobicoke, #Skye Residences Near Toronto Airport, #Skye Residences Toronto, #Skye Hotel Toronto, #Skye Hotel Near Toronto Airport, #Hotel Near Toronto Airport, #Near Toronto Airport Accommodation, #Suites Near Toronto Airport, #Etobicoke Suites Near Airport, #Hotel Near Toronto Pearson International Airport, #Toronto Airport Suite Rentals, #Pearson Airport Hotel Suites
LA HUG - Video Testimonials with Chynna Morgan - June 2024Lital Barkan
Have you ever heard that user-generated content or video testimonials can take your brand to the next level? We will explore how you can effectively use video testimonials to leverage and boost your sales, content strategy, and increase your CRM data.🤯
We will dig deeper into:
1. How to capture video testimonials that convert from your audience 🎥
2. How to leverage your testimonials to boost your sales 💲
3. How you can capture more CRM data to understand your audience better through video testimonials. 📊
2. 2
CUPOLA FURNACES
For many years, the cupola was the primary method of melting used in iron foundries.
René-Antoine Ferchault de Reaumur built the first cupola furnace in France, about 1720.
It is obtained in different sizes and can be operated for long a time.
As we all know that Cupola furnace is basically used for the production of cast iron. The reason for
using Cupola furnace includes:
Its continuous operating quality.
High melt rates.
Relatively low operating costs.
Ease of operation.
It is an economical furnace for the production of grey cast iron, nodular cast iron and some malleable
iron castings.
APPLICATIONS:
It is highly used in iron foundries for melting purpose.
It is used for melting scrap metal or pig iron.
It is also used for duplexing and triplexing operations for making steels.
It is also used for melting some copper base alloys etc.
It is mostly used in the production of cast iron.
The following diagram shows the basic working principle of Cupola Furnace:
3. 3
OPERATION:
• The charge consisting of Iron, Coke, flux and possible alloying elements, is loaded through a
charging door located less than halfway up the height of the cupola.
Coke is the fuel used to heat the furnace.The iron is usually a mixture of pig iron and scrap.
The flux is a basic compound such as limestone that reacts with coke ash and other impurities
to form slag. The slag serves to cover the melt, protecting it from reaction with the
environment inside the cupola and reducing heat loss.
• The blast is blown through the tuyeres
• These tuyeres are arranged in one or more row around the cupola body.
• Hot gases which ascends from the bottom (combustion zone) preheats the iron in the
preheating zone.
• A slag hole is provided to remove the slag from the melt
• Through the tap hole molten metal is poured into the ladle
• At the top conical cap called the spark arrest is provided to prevent the spark emerging to
outside.
.
4. 4
REFRACTORIES IN CUPOLA FURNACE:
The cupola consists of a vertical cylindrical steel sheet lined inside with acid refractory bricks. The
lining is generally thicker in the lower portion of the cupola as the temperatures are higher than in
upper portion.
In Cupola Furnace, there are different zones having different temperatures and specific purpose.
Keeping it in mind, we use different refractories for lining which fulfills the requirement. Therefore,
we have to fond knowledge about different zones.
Cupola Zones:
Well
Superheating, Combustion or Oxidizing Zone.
Reducing or Protective Zone.
Melting Zone.
Preheating Zone.
Stack
1. Well:
It is the space between the bottom of the Tuyeres and the sand bed. Molten metal collected in
this portion.
2. Combustion or Oxidizing zone:
It is the zone where combustion takes place. The temperature in this zone is about 1800°C.
It extends from the top of the tuyeres to a surface boundary below which all the Oxygen of air is
consumed by combustion, chemical reaction that takes place in the zone is
C(coke) + 02 (from air) → C02 + Heat
3. Reducing zone:
It extends from the top of the combustion zone to the top of the initial coke bed. The CO2
produced in the combustion zone moves up and is reduced to CO. The temperature also drops to
1650°C.
C02 + C2 → CO - Heat
4. Melting zone:
It includes the first layer of pig iron above the initial coke bed. In this zone, the pig iron is
melted. The following reaction takes place.
3Fe + 2CO → Fe3C + C02
5. Preheating zone:
It includes all the layers of cupola charges placed above the melting zone to the top of the last
charge. The layers of charges are heated by the out-going gases. The temperature in the zone up to
1050°C.
6. Stack:
It is the zone beyond the pre-heating zone, through which the hot gases go to the atmosphere.
As it is clear that all the Zones i.e. Combustion or Oxidizing zone, Reducing zone, Melting
zone and Preheating zone have different temperatures, that is why different refractory is used in
different zones.
There are two places where refractories are required in Cupola furnace,
One at the side of walls and the other at the bottom because of molten metal, when slag moves
downward there are two possibilities that slag will come in contact with walls and as well as bottom
also.
5. 5
The shell of the cupola, being usually made of steel, has refractory brick and plastic refractory
patching material lining it. The bottom is lined in a similar manner but often a clay and sand
mixture(bod) may be used, as this lining is temporary. Finely divided coal can be mixed with the clay
lining so when heated the coal decomposes and the bod becomes slightly friable, easing the opening
up of the tap holes. The bottom lining is compressed or 'rammed' against the bottom doors. Some
cupolas are fitted with cooling jackets to keep the sides cool and with oxygen injection to make the
coke fire burn hotter.
CUPOLA LINING MATERIALS:
For the lining and patching of Cupola Furnaces, following materials are used:
Standard Fire Bricks (High alumina brick).
Cupola Fire Bricks.
Ultra Gun 55.
Ultra Gun 1600.
Hydra-Max.
RAMWELL.
SURGUN.
CRITERION
Fire clay
Patching Mass
1) STANDARD FIRE BRICKS:
Fire bricks are used for the lining of Cupola.
Standard and special size bricks are also used for specific applications.
According to the content of Al2O3 (alumina) Fire bricks can be divided into fire clay brick and high
alumina brick. As we know that by increasing the percentage of alumina the refractoriness also
increases.
Features:
o Resistance to high temperature, resistance to erosion, resistance to abrasion.
o Excellent compression strength.
o Resistance to acid as well as alkali.
o Excellent heat stability.
6. 6
2) CUPOLA FIRE BRICKS
This shape of brick is known as cupola fire brick as it specially designed for cupola furnace
and cannot be used for other furnace. It can be easily lined on the circular walls of cupola
furnace. Cupola bricks are acknowledged for their supreme quality.
They have precise dimensions.
They have long life.
They have high strength.
Light in weight.
Accurate dimensions.
3) ULTRA GUN 55:
Ultragun55 is a gunning material used in the cupola furnace for the designing and applications in the
melting zone of the cupola furnace. It can be used for lining in the cupola furnace. It is induced or
installed into the blast furnace by a gunning machine called ROTOMAT. It is a high silicon carbide
gunning material and the presence of silicon carbide in higher amount enables it to cause resistance to
slag in the melting zone in which the first layer of pig iron is melted just above the initial coke bed.
7. 7
4) ULTRA GUN 1600:
ULTRAGUN1600 is a low cement gunning material used in the cupola furnace and its purpose is to
take off the hot gases from the cupola furnace which were fed into the cupola furnace with the help of
tuyeres. It is a low cement gunning material which indicates that it has low cement content means it
has low amount of mixing water. It is also installed on the cupola furnace with the help of gunning
machine ROTOMAT.
Difference Between Ultra Gun 55 And Ultra Gun 1600:
The main and the basic difference between the UltraGun55 and UltraGun1600 is of the temperature.
As clear from the name that the temperature of UltraGun55 is lower as compared to Ultragun1600.
This is the reason that UltraGun55 is used in the zone of the Cupola Furnace where the temperature is
lower and ULTRAGUN1600 is used in the higher temperature zone of the Cupola Furnace.
WHAT IS ROTAMAT??
ROTAMAT is a gunning machine used to induce gunning materials into the cupola furnace. It is
usually used by a popular gunmix system called “THE VELCO GUNMIX SYSYTEM”. The gunning
material introduced to the gunning machine is first moistened by compressed air and water which
allows the development of dust and rebound to reduce considerably. As a result we get better gunning
results due to less dust and better moistening and also less cost due to less rebound. The ROTAMAT
consist of a rotor by which we can control the capacity of the gunning material.
GUNNING MATERIAL:
Gunning materials are unshaped refractories commonly used in steel industry for the
maintenance of converter linings.
8. 8
5) HYDRA-MAX:
HYDRAMAX is a high alumina, ultra -low cement castables, containing silicon carbide for superior
slag resistance in the well and siphon box. It is a low cement castable refractory means it has low
cement content and it a castable refractory so usually a cement binder is used like HAC( high alumina
cement) which reacts with the low amount of water and form a strong ceramic bond. The advantage of
using low cement castables are:
They are very dense and porous means they have high porosity.
They are highly wear resistant and abrasion resistant.
They have high resistance to infiltrations i.e. alkalis.
Just like cement, HydraMax is usually supplied dry for mixing and placement on site, it must be
installed behind suitable formwork by internal vibration. It has great importance in cupola furnace.
Low-moisture castable products can be installed via vibration casting or concrete/refractory
pump. Designed for rapid turnaround in hot trough and runner applications. Applications
include trough and runner working linings, precast working and safety lining shapes, tilting
runner linings and castable taphole facing.
6) RAMWELL:
Ramwell linings are high alumina pitch free granular, clay bonded, graphitized ramming
material containing between 10% and 20% silicon carbide used for installation in the well
and syphon box where slag resistance is paramount. RAMWELL is supplied ready to use and
is installed by pneumatic ramming behind robust formwork.
Fused alumina based RAMWELL 90 or RAMWELL PS001 and calcined alumina based RAMWELL
75 ramming materials are recommended for the well, syphon and taphole of the cupola RAMWELL
PS001 or RAMWELL 90 ramming materials are ideally suited to lining the well and syphon box.
Alternatively a cast solution can be archieved with HYDRAMAX AT3A or HYDRAMAX VX
281M. Ultra low cement castable with SiC level from 18% to 31%.
If a castable solution is preferred, then HYDRAMAX AT3A or HYDRAMAX VX281M ultra-low
cement castables are recommended. Combinations such as a castable lining for the well together with
rammables for the syphon box are also possible.
What is Syphon Box??
A place in Cupola Furnace where slag layer is formed after melting is called a Syphon Box.
7) SURGUN
It is a unique range of low cement, gunned castables ideal for the repair and maintenance of
the cupola well and melting zone of the cupola furnaces. SURGUN is supplied dry for
application by the VELCO Gunmix system.
9. 9
8) CRITERION
It is a range of low cement castables supplied dry for mixing and placement on site, it must
be installed behind suitable formwork by internal or external vibration. Chamotte based
CRITERION 50ME is ideally suited for the cupola shaft.
9) FIRE CLAY
Fire clay is the important refractory used in cupola furnace. It is used as binder during lining of
Cupola with bricks. If you are not using fire clay cupola is not complete. In general fire clay joined
two or more refractory bricks by this fire clay acts as mortars that joined two or more things which
strengthen it and also act as refractory. Fire clay are made up of clay containing alumina silicates and
impurities such as alkalis and ironoxide.The alumina content ranges from 25% to 45% depending
upon impurities content and alumina and silicon ratio.
Fire clay are classified as
low duty
medium duty
high duty
super duty
depending upon the alumina range. Fire clay also act as a binder furnace between lining of Cupola
gradesand bricks .fire clay in Cupola Furnace is approximately to 9D to 54D.They are available in IS-
7 and IS-8 grades.fire clay is the most reliable and has a long shelf life. The main use of fireclay in
cupola is to minimize heat resisting barriers between high and low temperatures zones.
10) PATCHING MASSES :
Patching refractories are used where any damage is done or on the places where there is a chance of
failure or damage. Patching refractories are made up of fused silica. Every time after the first heat
cupola needs to be patched with patching masses. These materials are similar to plastic refractories
though have a soft plasticity allowing them to be pounded into place. Patching refractories have some
tremendous qualities that have high density, better thermal stability anti-erosion means they are
resistant to basic slag layer because in cupola Cao and FeO acts as basic slag layer so patching
refractories are also resistant to this. It also helps in increasing the life of refractory lining.
Following is the table showing various refractories in Cupola Furnace with their sizes:
Product Size
Cupola Fire
Bricks
9D to 54D with std. cross section of 4.5”X3”(Inches)
Standard Fire
Bricks
Cross section of 9X4.5X1” 9X4.5X1.5” 9X4.5X2” 9X4.5X3” (Inches)
Fire Clay Fine Clay of -22 mesh.
Patching Mass Combination of Fine Clay, Special binders and refractory grits up to 7mm.
10. 10
Why we use Acidic Refractories in Basic Atmosphere Instead of Basic
Refractory?
As we know that acidic refractories are used in places where slag and atmosphere are basic and on the
other hand basic refractories are used in places where slag and atmosphere are acidic in nature, but
this is not in the case of Cupola Furnace because there are two distinct types of slags in the cupola. In
the slag layer in the cupola well, the slags contain mostly CaO and SiO2. Above the slag layer the
predominant oxides are CaO and FeO. These slags are much more corrosive in nature and their
corrosiveness is exacerbated by the high temperatures that exist in the regions above the tuyeres.
The CaO-FeO slag above the slag layer is basic hence silica based refractory perform very poorly in
this region. MgO refractory might be best suited for use in this region but due to cost factor, MgO
refractories are not used. However, alumina refractory (which is a neutral refractory) is most often
used in these conditions.
Even alumina refractory is rapidly eroded by slag attack in the region above the tuyeres. This leads to
the considerable loss of heat. Recently, alumina/silicon carbide refractories(which is a combination of
neutral and special refractory) have been used in this region with good results. The improvement
stems from the high thermal conductivity of the refractory. This sufficiently lowers the temperature on
the hot side of the refractory to allow a frozen layer of slag to form which serves to protect the
refractory. This slows the erosion process and leads to heat savings with ensuing benefits of lower
fuel requirements, higher iron temperatures, improved alloy recovery and lower refractory
maintenance, which offsets the extra cost for refractory.
The slag above the taphole is much less corrosive than the slag above the tuyeres. Alumina refractory
or silicon carbide/alumina refractory is most commonly used today. For basic slag operation, the
refractory can be MgO or carbon.
Almost every vessel that holds or produces liquid iron is lined with refractory materials and is
susceptible to refractory erosion by slag. In other circumstances, slags can combine with refractory
materials to form accretions that hamper production. The consequences of refractory problems, loss of
production and the cost to replace the refractory can be serious.
Thus, extending the life of a refractory lining is an important consideration.
Iron oxide is present in large amounts in many of the slags found in foundry vessels and furnaces.
Unfortunately, iron oxide is among the best solvents for refractories, and in particular it is a very good
solvent for silica refractories. The vulnerability of refractories to FeO attack can be roughly judged
by the amount of refractory that will dissolve in pure FeO at 15000
C.
Solubility of Oxides in FeO @15000
C
Al2O3 11%
MgO 5%
SiO2 40%
11. 11
MgO is the least soluble and silica is the most soluble. Thus, silica refractories are the
most susceptible to attack by FeO. For this reason, silica is being used less and less in foundry
applications despite of its very low cost.
MgO has the lowest solubility in FeO. As a basic oxide it dissolves readily in acid slags, which
unfortunately are the most common type of slags generated in the foundry. As a result MgO
refractories are not often used.
Alumina refractories have risen in popularity because they are less sensitive to FeO erosion than silica
and are reasonably resistant to acid slags. A refractory that is gaining popularity is alumina containing
silicon carbide .
Although silicon carbide should react readily with FeO and dissolve in iron, the success of the
refractory is attributed to its high thermal conductivity. This enables the temperature of the refractory
at the iron interface to drop below the freezing point of the slag.
The refractory becomes coated with solid slag which is much less corrosive than the liquid slag.
Owning to the destruction of the refractory lining in cupola furnaces, it operate for periods of 12 to
18 hours and then undergo routine repairs i.e. patching and gunning.
Two or three cupola furnaces are operated alternately when daily or 24 hour iron smelting is required.
Now a days continuous operation water cooled cupolas for cast iron production is used, which made
possible smelting for periods of 100-120 hours routine repair of the refractory lining.
It is very important that in the bottom lining of furnace cement refractories i.e
Hydramix – low moisture cement refractory were installed as the slag was basic and more high
temperature resistant, slag penetration resistant, corrosive resistant and ultra high hot strength
refractories were opted to be used. Moreover it is a common phenomenon that when water is allowed
to be in contact with high temperature molten state materials a very devastating explosion occurs
because of formation of Hydrogen Bomb.