Concrete, Use nano-materials for the self – healing of cracking
1.
2. Hunting for objects made
of concrete Comparing the hardening of different
kinds of cement by adding salt and
sugar .
Comparing densities of mixed
aggregate at samples Testing properties of concrete
(breaking concrete )
3.
4.
5. a very hard building material made
by mixing together
cement Fine aggregates Coarse aggregates water
11. Time A B C
0 25 21 22
3 24 23 22
6 24 23.5 22
9 24 23 22
12 24 22.5 22
15 24 22 22
12. sample temperature Harding Conclusion
A Slightly increased
then decreased
Quickly Reacted with cement
B Slightly decreased
then increased very
quickly
The fastest Salt act as a positive
catalyst
C Decreased then
Coasted
Very slow Sugar act as a
negative catalyst
13. The results :
1- when we added sugar the hardening rate was decreased
2- when we added salt the hardening rate was increased
21. RESULTwe expect that our
product will prevent and cure
concrete hair cracks by using
bacteria that would grow up until it
completely fills the crack .
22. Conclusion The self-healing bio concrete aims to provide
a cheap and sustainable solution , markedly improving the
lifespan of buildings , bridges and roads .
We recommended to use this product to protect steel
reinforcement from corrosion which increase the life time of
structure