Strength of Materials Lecture - 2
Elastic stress and strain of materials (stress-strain diagram)
Mehran University of Engineering and Technology.
Department of Mechanical Engineering.
This unit covers Types of stresses & strains,
Hooke’s law, stress-strain diagram,
Working stress,
Factor of safety,
Lateral strain,
Poisson’s ratio, volumetric strain,
Elastic moduli,
Deformation of simple and compound bars under axial load,
Analysis of composite bar with varying cross section.
This unit covers Types of stresses & strains,
Hooke’s law, stress-strain diagram,
Working stress,
Factor of safety,
Lateral strain,
Poisson’s ratio, volumetric strain,
Elastic moduli,
Deformation of simple and compound bars under axial load,
Analysis of composite bar with varying cross section.
This presentation is for mechanical engineering/ civil engineering students to help them understand the different type of destructive mechanical testing of materials. The tensile testing, hardness, impact test procedures are explained in detail.
CONTENT:
1. Elastic strain energy
2. Strain energy due to gradual loading
3. Strain energy due to sudden loading
4. Strain energy due to impact loading
5. Strain energy due to shock loading
6. Strain energy due to shear loading
7. Strain energy due to bending (flexure)
8. Strain energy due to torsion
9. Examples
When a body is subjected to gradual, sudden or impact load, the body deforms and work is done upon it. If the elastic limit is not exceed, this work is stored in the body. This work done or energy stored in the body is called strain energy.
When a body is subjected to gradual, sudden or impact load, the body deforms and work is done upon it. If the elastic limit is not exceed, this work is stored in the body. This work done or energy stored in the body is called strain energy.
Some basic defintions of the topics used in Strength of Materials subject. Pictorial presentation is more than details. Many examples are provided as well.
Bending Stresses are important in the design of beams from strength point of view. The present source gives an idea on theory and problems in bending stresses.
This is a ppt which will give u a better understanding of fracture toughness of a material in short time. It also has great exposure to testing method that we do in our laboratory class in undergraduate courses. So good luck with slide.
This presentation is for mechanical engineering/ civil engineering students to help them understand the different type of destructive mechanical testing of materials. The tensile testing, hardness, impact test procedures are explained in detail.
CONTENT:
1. Elastic strain energy
2. Strain energy due to gradual loading
3. Strain energy due to sudden loading
4. Strain energy due to impact loading
5. Strain energy due to shock loading
6. Strain energy due to shear loading
7. Strain energy due to bending (flexure)
8. Strain energy due to torsion
9. Examples
When a body is subjected to gradual, sudden or impact load, the body deforms and work is done upon it. If the elastic limit is not exceed, this work is stored in the body. This work done or energy stored in the body is called strain energy.
When a body is subjected to gradual, sudden or impact load, the body deforms and work is done upon it. If the elastic limit is not exceed, this work is stored in the body. This work done or energy stored in the body is called strain energy.
Some basic defintions of the topics used in Strength of Materials subject. Pictorial presentation is more than details. Many examples are provided as well.
Bending Stresses are important in the design of beams from strength point of view. The present source gives an idea on theory and problems in bending stresses.
This is a ppt which will give u a better understanding of fracture toughness of a material in short time. It also has great exposure to testing method that we do in our laboratory class in undergraduate courses. So good luck with slide.
Terminology for Mechanical Properties The Tensile Test: Stress-Strain Diagram...manohar3970
Terminology for Mechanical Properties
The Tensile Test: Stress-Strain Diagram
Properties Obtained from a Tensile Test
True Stress and True Strain
The Bend Test for Brittle Materials
Hardness of Materials
Democratizing Fuzzing at Scale by Abhishek Aryaabh.arya
Presented at NUS: Fuzzing and Software Security Summer School 2024
This keynote talks about the democratization of fuzzing at scale, highlighting the collaboration between open source communities, academia, and industry to advance the field of fuzzing. It delves into the history of fuzzing, the development of scalable fuzzing platforms, and the empowerment of community-driven research. The talk will further discuss recent advancements leveraging AI/ML and offer insights into the future evolution of the fuzzing landscape.
TECHNICAL TRAINING MANUAL GENERAL FAMILIARIZATION COURSEDuvanRamosGarzon1
AIRCRAFT GENERAL
The Single Aisle is the most advanced family aircraft in service today, with fly-by-wire flight controls.
The A318, A319, A320 and A321 are twin-engine subsonic medium range aircraft.
The family offers a choice of engines
Final project report on grocery store management system..pdfKamal Acharya
In today’s fast-changing business environment, it’s extremely important to be able to respond to client needs in the most effective and timely manner. If your customers wish to see your business online and have instant access to your products or services.
Online Grocery Store is an e-commerce website, which retails various grocery products. This project allows viewing various products available enables registered users to purchase desired products instantly using Paytm, UPI payment processor (Instant Pay) and also can place order by using Cash on Delivery (Pay Later) option. This project provides an easy access to Administrators and Managers to view orders placed using Pay Later and Instant Pay options.
In order to develop an e-commerce website, a number of Technologies must be studied and understood. These include multi-tiered architecture, server and client-side scripting techniques, implementation technologies, programming language (such as PHP, HTML, CSS, JavaScript) and MySQL relational databases. This is a project with the objective to develop a basic website where a consumer is provided with a shopping cart website and also to know about the technologies used to develop such a website.
This document will discuss each of the underlying technologies to create and implement an e- commerce website.
Cosmetic shop management system project report.pdfKamal Acharya
Buying new cosmetic products is difficult. It can even be scary for those who have sensitive skin and are prone to skin trouble. The information needed to alleviate this problem is on the back of each product, but it's thought to interpret those ingredient lists unless you have a background in chemistry.
Instead of buying and hoping for the best, we can use data science to help us predict which products may be good fits for us. It includes various function programs to do the above mentioned tasks.
Data file handling has been effectively used in the program.
The automated cosmetic shop management system should deal with the automation of general workflow and administration process of the shop. The main processes of the system focus on customer's request where the system is able to search the most appropriate products and deliver it to the customers. It should help the employees to quickly identify the list of cosmetic product that have reached the minimum quantity and also keep a track of expired date for each cosmetic product. It should help the employees to find the rack number in which the product is placed.It is also Faster and more efficient way.
NO1 Uk best vashikaran specialist in delhi vashikaran baba near me online vas...Amil Baba Dawood bangali
Contact with Dawood Bhai Just call on +92322-6382012 and we'll help you. We'll solve all your problems within 12 to 24 hours and with 101% guarantee and with astrology systematic. If you want to take any personal or professional advice then also you can call us on +92322-6382012 , ONLINE LOVE PROBLEM & Other all types of Daily Life Problem's.Then CALL or WHATSAPP us on +92322-6382012 and Get all these problems solutions here by Amil Baba DAWOOD BANGALI
#vashikaranspecialist #astrologer #palmistry #amliyaat #taweez #manpasandshadi #horoscope #spiritual #lovelife #lovespell #marriagespell#aamilbabainpakistan #amilbabainkarachi #powerfullblackmagicspell #kalajadumantarspecialist #realamilbaba #AmilbabainPakistan #astrologerincanada #astrologerindubai #lovespellsmaster #kalajaduspecialist #lovespellsthatwork #aamilbabainlahore#blackmagicformarriage #aamilbaba #kalajadu #kalailam #taweez #wazifaexpert #jadumantar #vashikaranspecialist #astrologer #palmistry #amliyaat #taweez #manpasandshadi #horoscope #spiritual #lovelife #lovespell #marriagespell#aamilbabainpakistan #amilbabainkarachi #powerfullblackmagicspell #kalajadumantarspecialist #realamilbaba #AmilbabainPakistan #astrologerincanada #astrologerindubai #lovespellsmaster #kalajaduspecialist #lovespellsthatwork #aamilbabainlahore #blackmagicforlove #blackmagicformarriage #aamilbaba #kalajadu #kalailam #taweez #wazifaexpert #jadumantar #vashikaranspecialist #astrologer #palmistry #amliyaat #taweez #manpasandshadi #horoscope #spiritual #lovelife #lovespell #marriagespell#aamilbabainpakistan #amilbabainkarachi #powerfullblackmagicspell #kalajadumantarspecialist #realamilbaba #AmilbabainPakistan #astrologerincanada #astrologerindubai #lovespellsmaster #kalajaduspecialist #lovespellsthatwork #aamilbabainlahore #Amilbabainuk #amilbabainspain #amilbabaindubai #Amilbabainnorway #amilbabainkrachi #amilbabainlahore #amilbabaingujranwalan #amilbabainislamabad
Overview of the fundamental roles in Hydropower generation and the components involved in wider Electrical Engineering.
This paper presents the design and construction of hydroelectric dams from the hydrologist’s survey of the valley before construction, all aspects and involved disciplines, fluid dynamics, structural engineering, generation and mains frequency regulation to the very transmission of power through the network in the United Kingdom.
Author: Robbie Edward Sayers
Collaborators and co editors: Charlie Sims and Connor Healey.
(C) 2024 Robbie E. Sayers
Student information management system project report ii.pdfKamal Acharya
Our project explains about the student management. This project mainly explains the various actions related to student details. This project shows some ease in adding, editing and deleting the student details. It also provides a less time consuming process for viewing, adding, editing and deleting the marks of the students.
Saudi Arabia stands as a titan in the global energy landscape, renowned for its abundant oil and gas resources. It's the largest exporter of petroleum and holds some of the world's most significant reserves. Let's delve into the top 10 oil and gas projects shaping Saudi Arabia's energy future in 2024.
Quality defects in TMT Bars, Possible causes and Potential Solutions.PrashantGoswami42
Maintaining high-quality standards in the production of TMT bars is crucial for ensuring structural integrity in construction. Addressing common defects through careful monitoring, standardized processes, and advanced technology can significantly improve the quality of TMT bars. Continuous training and adherence to quality control measures will also play a pivotal role in minimizing these defects.
Immunizing Image Classifiers Against Localized Adversary Attacksgerogepatton
This paper addresses the vulnerability of deep learning models, particularly convolutional neural networks
(CNN)s, to adversarial attacks and presents a proactive training technique designed to counter them. We
introduce a novel volumization algorithm, which transforms 2D images into 3D volumetric representations.
When combined with 3D convolution and deep curriculum learning optimization (CLO), itsignificantly improves
the immunity of models against localized universal attacks by up to 40%. We evaluate our proposed approach
using contemporary CNN architectures and the modified Canadian Institute for Advanced Research (CIFAR-10
and CIFAR-100) and ImageNet Large Scale Visual Recognition Challenge (ILSVRC12) datasets, showcasing
accuracy improvements over previous techniques. The results indicate that the combination of the volumetric
input and curriculum learning holds significant promise for mitigating adversarial attacks without necessitating
adversary training.
1. 1
Strength of materials-1Strength of materials-1
Unit: Elastic stress andUnit: Elastic stress and
strain behavior of materialsstrain behavior of materials
(stress-strain diagram)(stress-strain diagram)
2. Stress Strain Diagrams
It is a tool for understanding
material behavior under load.
A stress strain diagram help
engineers to select the right
materials for specific loading
conditions. Or
It is a graph that represents how a part
behaves under an increasing load, and
used by engineers when selecting
materials for specific designs. 2
3. 3
•A stress-strain diagram generally contains three regions:
•Elastic region: This portion is generally represented as a
linear relationship between stress and strain. If the load is
released the specimen will return to its original dimensions.
•Plastic region: In this portion, the specimen begins to yield.
The maximum strength of the specimen occurs in this zone.
The specimen endures some permanent deformation that
remains after the load is released.
•Rupture: The point at which a specimen breaks into two
parts.
5. 5
•Stress-strain diagrams are generated
experimentally through the
performance of controlled tensile tests
using fabricated test specimens.
•The applied load and displacement
are monitored during the test, and are
used to calculate stress and strain,
respectively.
8. 8
• The stress-strain diagram differs in form for various
materials.
• Engineering materials are classified as either ductile or
brittle materials.
• A ductile material is one having relatively large tensile
strain up to the point of rupture like structural steel and
aluminum.
• whereas brittle materials has a relatively small strain up to
the point of rupture like cast iron and concrete.
• Ductility: Ability of a material to deform under tensile
load; high % elongation and % reduction of area indicate
ductility.
• Brittleness: material failure with little deformation; low %
elongation and % reduction of area indicate brittleness.
11. Stress-strain Diagram
11
• Proportional Limit (Hooke's Law) : From the origin O to
the point P called proportional limit, the stress-strain curve
is a straight line.
• Force or load is applied axially (no bending)
• This linear relation between elongation and the axial force
causing was first noticed by Sir Robert Hooke’s in 1678
and is called Hooke's Law.
• it states that “within the proportional limit, the stress is
directly proportional to strain”.
The constant of proportionality is called the Modulus of
Elasticity ‘E’ or Young's Modulus and is equal to the slope
of the stress-strain diagram from O to P. Then
13. Stress-strain Diagram
13
• Modulus of elasticity: To describe elastic properties of linear
objects like wires, rods which are stretched or compressed, a
convenient parameter is the ratio of the stress to the strain,
called the "Young's modulus" or "Modulus of Elasticity" of
the material.
• Young's modulus can be used to predict the elongation or
compression of an object as long as the stress is less than the
yield strength of the material.
• In many materials, the relation between applied stress and the
resulting strain is directly proportional (up to a certain limit),
and a graph representing those two quantities is a straight line.
• The slope of this line is known as Young’s Modulus, or the
"Modulus of ElasticityModulus of Elasticity."
14. The Values of E (Modulus of Elasticity)
14
S.No Materials E (GPa)
1. Steel 200 to 220
2. Cast iron 100 to 160
3. Copper 90 to 110
4. Brass 80 to 90
5. Aluminum 60 to 80
6. Timber 10
15. 15
• Elastic Limit: The limit in which the material will return its original shape
when the load is removed.
• Yield Point: Yield point is the point at which the material will have an
appreciable elongation OR a slight increase in stress above the elastic limit
will result in permanent deformation. This behavior is called yielding for
ductile materials (In Engineering, the transition from elastic behavior to
plastic behavior).
• Less ductile materials such as aluminum and medium to high carbon steels do
not have a well defined yield point. For these materials the yield strength is
typically determined by “offset method” by which a line is drawn parallel to
linear portion of the curve and intersecting at some value most commonly
0.2%. (generally from 0.1% to 0.2%).
• Upper yield point: which corresponds to the load reached just before yield
starts.
• Lower yield point: which corresponding to the load required maintain yield.
Lower yield point should be used to determine the yield strength of the
material.
.
20. Yield strength: you can draw a line parallel to the
initial linear portion, and where this line intersects
the curve is the yield point. The Y coordinate of this
point is the yield strength.
20
Figure: Yield strength determination
21. 21
• Ultimate Strength: The maximummaximum ordinate in the stress-strain
diagram is the ultimate strength or tensile strength. This is the
maximum load the specimen sustains during the test.
• Necking: After the ultimate stress, the cross sectional area begin to
decrease in a region of the specimen because of local instability. This
phenomenon is known as necking. After necking has been
beginning, we note that rupture occurs at an angle of 45 degree with
the original surface of the specimen. This indicates that shear
stresses are responsible for failure of the ductile materials.
• Rapture or Fracture: The specimen spilt into two or more pieces or
break into parts.
• Rapture Strength: is the strength of the material at rupture. This is
also known as the breaking strength.
• Strain Hardening: The stress must be increased to keep elongating
the specimen, until the maximum value has been reached. This is
due to a property of the material known as strain hardening.
22. 22
• Plasticity or plastic deformation: is the opposite of elastic
deformation and is accepted as unrecoverable strain. Plastic
deformation is retained even after the relaxation of the applied
stress.
• Most materials in the linear-elastic category are usually capable
of plastic deformation. Brittle materials, like ceramics, do not
experience any plastic deformation and will fracture under
relatively low stress.
• Consider the difference between a carrot and chewed bubble
gum. The carrot will stretch very little before breaking. The
chewed bubble gum, on the other hand, will plastically deform
enormously before finally breaking.
24. Percent Elongation
24
• A standard measure of the ductility of a
material is its percent elongation, which is
defined as
• Percent elongation = ( LB – Lo ) / Lo) 100
• Where Lo = Initial length of the tensile test
specimen .
• LB = Final length at rupture.
• For commonly used steels, Standard
elongation 21% to 30% are common.
25. Percent Reduction
25
• Percent reduction in area = ( Ao –AB ) / Ao) 100
• Where Ao = Initial area of the specimen.
• AB = Final area at rupture.
• For structural steel , percent reduction in
area of 60 to 70% are common.
• For ductile materials having %E > 5
• For brittle materials having % E < 5
29. Stress strain diagrams for Brittle materials
29
• Brittle materials: such as cast iron, glass, concrete and carbon
fiber (composite materials) are characterized by the fact that
rupture occurs without any prior change in the rate of deformation.
• These do not have a yield point and do not strain harden, which
means that ultimate strength and breaking strength are at same point.
30. Stress strain diagrams for Brittle materials
30
• From the fig. we note the absence of any necking of the specimen in
the case of the brittle materials and observe that rupture occurs
along the surface perpendicular to the load. And we conclude that
normal stresses are responsible for the failure of brittle materials.
31. Stress strain diagrams for Brittle materials
31
0 0.002 0.004 0.0060.008
Strain
0
125
250
375
500
Stress(MPa)
Gray Cast Iron
Characteristic stress-strain curve for
brittle material
Cast Iron
32. 32
• To calculate the engineering stress, the
applied load is divided by the original cross
sectional area;
• however the true stress would be equal to
the load divided by the new deformed cross
sectional area.
• Therefore true stress > engineering stress.
35. 35
Isotropic materials:
– Isotropic materials have elastic properties that are
independent of direction. Most common structural materials
are isotropic.
Anisotropic materials:
– Materials whose properties depend upon direction. An
important class of anisotropic materials is fiber-reinforced
composites.
Homogeneous
– A material is homogeneous if it has the same composition at
every point in the body. A homogeneous material may or may
not be isotropic.
36. 36
Exp: 01: (P-6 R.K Rajput)
A hollow cast iron cylinder 4 m long, 300 mm outer diameter
and thickness of metal 50 mm is subjected to a central load on
the top, when standing straight.
The stress produced is 75× 103
KN / m2
.
Assume E = 1.5 108
KN / m2
.
Find (i) magnitude of the load (ii) longitudinal strain produced
(iii) total decrease in length.
37. 37
Exp: 1.3: (P-7 R.K Rajput)
The following observations were made during a tensile test on
mild steel specimen 40 mm in diameter and 200 mm long.
Elongation with 40 KN load (within the limit of
proportionality); final diameter = 23. 6 mm
δL = 0.0304 mm ; yield load = 161 KN;
Maximum load = 242 KN
Length of specimen at rupture = 249 mm
Determine (a) modulus of elasticity (b) yield point stress
(c ) ultimate stress (d) % Elongation (e) % Reduction
38. 10 - 38
There are three ways of applying a force to enable a crack to propagate:
Mode I fracture – Opening mode (a tensile stress normal to the plane of
the crack).
Mode II fracture – Sliding mode (a shear stress acting parallel to the
plane of the crack and perpendicular to the crack front) i-e in-plane
shearing stress
Mode III fracture – Tearing mode (a shear stress acting parallel to the
plane of the crack and parallel to the crack front), i-e out plane shearing
stress
67. 67
Introduction
Mechanical properties that are important to a design
engineer differ from those that are of interest to the
manufacturing engineer.
In design, mechanical properties such as elastic
modulus and yield strength are important in order to
resist permanent deformation under applied stresses.
Thus, the focus is on the elastic properties.
In manufacturing, the goal is to apply stresses that
exceed the yield strength of the material so as to
deform it to the required shape. Thus, the focus is on
the plastic properties.
68. 68
Introduction
The yield behavior of a material is determined from
the stress-strain relationship under an applied state of
stress (tensile, compressive or shear).
This lab introduces the uniaxial tensile test to
determine the basic mechanical properties of a
material. The main focus of this lab is on the plastic
properties of the material.
The test will be conducted in accordance with the
standards specified by the American Society for
Testing and Materials (ASTM; www.astm.org).
69. 69
Terminology
Ductility:
Ductility can be defined as the amount of deformation
or strain that the material can withstand before failure.
For metal forming processes, increasing the ductility
increases the material formability .
In general, the ductility of the specimen is defined in
terms of the elongation (EL) or the area reduction (AR)
before fracture, i.e.:
70. 70
Terminology
True Stress and Strain:
The true stress (σ) uses the instantaneous or actual area of
the specimen at any given point, as opposed to the original
area used in the engineering values.
The true strain (ε) is defined as the instantaneous
elongation per unit length of the specimen.
The relationship between the true and engineering values is
given by:
71. 71
Terminology
True Stress and Strain:
Note: For a given value of the load and elongation, the true
stress is higher than the Eng. Stress, while the true strain
is smaller than the Eng. Strain.
72. 72
Terminology
Strain Hardening:
In the plastic region, the true stress increases
continuously. This implies that the metal is becoming
stronger as the strain increases. Hence, the name
“Strain Hardening”.
The relationship between true stress and true strain
i.e. the flow curve can be expressed using the power
law:
where K is called the strength coefficient and n the
strain hardening exponent.
73. 73
Objectives
This lab has the following objectives:
Develop an understanding of the basic material
properties from the perspective of manufacturing and
metal forming.
Determine the material properties by conducting a
uniaxial tensile test under ASTM (American Society
for Testing and Materials) specifications.
74. 74
Objectives
Students will be able to:
Perform an ASTM standard test (B557), use proper
equipment terminology, and know the parameters to
control during the test
Collect load vs. elongation data, plot engineering
stress vs. strain, determine the modulus of elasticity,
ASTM 0.2% offset yield strength, ultimate tensile
strength and ductility
Construct a true stress vs. true strain plot and
determine the values of K and n for the material
tested