This document provides a review and update on liners, bases, and cements used in clinical dentistry. It begins by discussing some terminology confusion regarding these materials. It then reviews the clinical applications and uses of liners, bases, and cements to reduce microleakage and subsequent sensitivity. The document categorizes and describes the characteristics and uses of various material types including varnishes, calcium hydroxide, zinc oxide, glass ionomers, and resins that can be used as liners, bases or cements.
A simple presentation to guide a dentist to choose best irrigant for the case. types of irrigants, their properties, advantages and disadvantages and tips has been discussed through this presentation.
A simple presentation to guide a dentist to choose best irrigant for the case. types of irrigants, their properties, advantages and disadvantages and tips has been discussed through this presentation.
Vital pulp therapy plays important role in preserving tooth and tooth vitality in both primary and permanent teeth.
Direct pulp capping, indirect pulp capping, pulpotomy has been covered in this presentation. All materials possibly useful in vital pulp therapy as well as recent advances have been included with all the evidences.
this presentation includes various obturating materials, sealers which are used for binding the gutta percha points inside the root canals, what is difference between standard and non standardized gutta percha and various newer methods for obturation are also included.
Smear layer is a controversial topic in the field of operative dentistry and endodontics. This presentation includes composition, concepts, structure, advantages, disadvantages, and removal methods of smear layer.
Here I present to you the basic concept and definition of endodontic diagnosis and treatment planning. It is presented to the level of mind of undergraduate students.
Vital pulp therapy plays important role in preserving tooth and tooth vitality in both primary and permanent teeth.
Direct pulp capping, indirect pulp capping, pulpotomy has been covered in this presentation. All materials possibly useful in vital pulp therapy as well as recent advances have been included with all the evidences.
this presentation includes various obturating materials, sealers which are used for binding the gutta percha points inside the root canals, what is difference between standard and non standardized gutta percha and various newer methods for obturation are also included.
Smear layer is a controversial topic in the field of operative dentistry and endodontics. This presentation includes composition, concepts, structure, advantages, disadvantages, and removal methods of smear layer.
Here I present to you the basic concept and definition of endodontic diagnosis and treatment planning. It is presented to the level of mind of undergraduate students.
done by : ( ABCD'S &G )
alaa ba-jafar
abrar alshahranii
sahab filfilan
nada alharbi
shahd rajab
Ghadeer suwaimil
I hope that you enjoy and you benefit❤
Indian Dental Academy: will be one of the most relevant and exciting
training center with best faculty and flexible training programs
for dental professionals who wish to advance in their dental
practice,Offers certified courses in Dental
implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic
Dentistry, Periodontics and General Dentistry.
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Bonding agents and its application in prosthodontics / dental implant coursesIndian dental academy
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
IOSR Journal of Dental and Medical Sciences is one of the speciality Journal in Dental Science and Medical Science published by International Organization of Scientific Research (IOSR). The Journal publishes papers of the highest scientific merit and widest possible scope work in all areas related to medical and dental science. The Journal welcome review articles, leading medical and clinical research articles, technical notes, case reports and others.
Critical review on glass ionomer seal under composite resin of obturated root...Ziad Abdul Majid
Introduction: The root canal treated teeth need an adhesive seal for coronal leakage prevention. Glass ionomer sealant is the usual interface used between the coronal restoration and dental hard tissue however when composite resin material is used as a coronal restoration, some dental clinician prefer not to use it. The aim of this review is to determine the need to seal the orifice of an obturated root canal with glass ionomer under composite resin to prevent microleakage. Material and methods: Electronic searches were performed in the Pubmed and Scopus databases using relevant keywords. Textbook searching was also applied. Following selection, articles were fully reviewed to ensure that they met inclusion/ exclusion criteria. Results: The intracoronal sealing abilities of a wide variety of restorative materials have been investigated, assessed and compared within the dental literature. Conclusion: No definitive guidelines were found regarding the use of orifice sealing materials following endodontic treatment. This review was not able to answer the research question, and further investigation is required to achieve this goal.
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
His eva of caoh&bond agnt in direct pulp capping/ rotary endodontic courses b...Indian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Composites /certified fixed orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
acid etching/ rotary endodontic courses by indian dental academyIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
11th publication - Dr Rahul VC Tiwari - Department of oral and Maxillofacial Surgery, SIBAR Institute of Dental Sciences, Takkellapadu,Guntur, Andhra Pradesh - 522509. QUEST JOURNALST
Similar to Liners, bases, and cements in clinical dentistry a review and update (20)
Pulmonary Thromboembolism - etilogy, types, medical- Surgical and nursing man...VarunMahajani
Disruption of blood supply to lung alveoli due to blockage of one or more pulmonary blood vessels is called as Pulmonary thromboembolism. In this presentation we will discuss its causes, types and its management in depth.
Ozempic: Preoperative Management of Patients on GLP-1 Receptor Agonists Saeid Safari
Preoperative Management of Patients on GLP-1 Receptor Agonists like Ozempic and Semiglutide
ASA GUIDELINE
NYSORA Guideline
2 Case Reports of Gastric Ultrasound
Explore natural remedies for syphilis treatment in Singapore. Discover alternative therapies, herbal remedies, and lifestyle changes that may complement conventional treatments. Learn about holistic approaches to managing syphilis symptoms and supporting overall health.
micro teaching on communication m.sc nursing.pdfAnurag Sharma
Microteaching is a unique model of practice teaching. It is a viable instrument for the. desired change in the teaching behavior or the behavior potential which, in specified types of real. classroom situations, tends to facilitate the achievement of specified types of objectives.
Ethanol (CH3CH2OH), or beverage alcohol, is a two-carbon alcohol
that is rapidly distributed in the body and brain. Ethanol alters many
neurochemical systems and has rewarding and addictive properties. It
is the oldest recreational drug and likely contributes to more morbidity,
mortality, and public health costs than all illicit drugs combined. The
5th edition of the Diagnostic and Statistical Manual of Mental Disorders
(DSM-5) integrates alcohol abuse and alcohol dependence into a single
disorder called alcohol use disorder (AUD), with mild, moderate,
and severe subclassifications (American Psychiatric Association, 2013).
In the DSM-5, all types of substance abuse and dependence have been
combined into a single substance use disorder (SUD) on a continuum
from mild to severe. A diagnosis of AUD requires that at least two of
the 11 DSM-5 behaviors be present within a 12-month period (mild
AUD: 2–3 criteria; moderate AUD: 4–5 criteria; severe AUD: 6–11 criteria).
The four main behavioral effects of AUD are impaired control over
drinking, negative social consequences, risky use, and altered physiological
effects (tolerance, withdrawal). This chapter presents an overview
of the prevalence and harmful consequences of AUD in the U.S.,
the systemic nature of the disease, neurocircuitry and stages of AUD,
comorbidities, fetal alcohol spectrum disorders, genetic risk factors, and
pharmacotherapies for AUD.
These lecture slides, by Dr Sidra Arshad, offer a quick overview of physiological basis of a normal electrocardiogram.
Learning objectives:
1. Define an electrocardiogram (ECG) and electrocardiography
2. Describe how dipoles generated by the heart produce the waveforms of the ECG
3. Describe the components of a normal electrocardiogram of a typical bipolar leads (limb II)
4. Differentiate between intervals and segments
5. Enlist some common indications for obtaining an ECG
Study Resources:
1. Chapter 11, Guyton and Hall Textbook of Medical Physiology, 14th edition
2. Chapter 9, Human Physiology - From Cells to Systems, Lauralee Sherwood, 9th edition
3. Chapter 29, Ganong’s Review of Medical Physiology, 26th edition
4. Electrocardiogram, StatPearls - https://www.ncbi.nlm.nih.gov/books/NBK549803/
5. ECG in Medical Practice by ABM Abdullah, 4th edition
6. ECG Basics, http://www.nataliescasebook.com/tag/e-c-g-basics
263778731218 Abortion Clinic /Pills In Harare ,sisternakatoto
263778731218 Abortion Clinic /Pills In Harare ,ABORTION WOMEN’S CLINIC +27730423979 IN women clinic we believe that every woman should be able to make choices in her pregnancy. Our job is to provide compassionate care, safety,affordable and confidential services. That’s why we have won the trust from all generations of women all over the world. we use non surgical method(Abortion pills) to terminate…Dr.LISA +27730423979women Clinic is committed to providing the highest quality of obstetrical and gynecological care to women of all ages. Our dedicated staff aim to treat each patient and her health concerns with compassion and respect.Our dedicated group ABORTION WOMEN’S CLINIC +27730423979 IN women clinic we believe that every woman should be able to make choices in her pregnancy. Our job is to provide compassionate care, safety,affordable and confidential services. That’s why we have won the trust from all generations of women all over the world. we use non surgical method(Abortion pills) to terminate…Dr.LISA +27730423979women Clinic is committed to providing the highest quality of obstetrical and gynecological care to women of all ages. Our dedicated staff aim to treat each patient and her health concerns with compassion and respect.Our dedicated group of receptionists, nurses, and physicians have worked together as a teamof receptionists, nurses, and physicians have worked together as a team wwww.lisywomensclinic.co.za/
Tom Selleck Health: A Comprehensive Look at the Iconic Actor’s Wellness Journeygreendigital
Tom Selleck, an enduring figure in Hollywood. has captivated audiences for decades with his rugged charm, iconic moustache. and memorable roles in television and film. From his breakout role as Thomas Magnum in Magnum P.I. to his current portrayal of Frank Reagan in Blue Bloods. Selleck's career has spanned over 50 years. But beyond his professional achievements. fans have often been curious about Tom Selleck Health. especially as he has aged in the public eye.
Follow us on: Pinterest
Introduction
Many have been interested in Tom Selleck health. not only because of his enduring presence on screen but also because of the challenges. and lifestyle choices he has faced and made over the years. This article delves into the various aspects of Tom Selleck health. exploring his fitness regimen, diet, mental health. and the challenges he has encountered as he ages. We'll look at how he maintains his well-being. the health issues he has faced, and his approach to ageing .
Early Life and Career
Childhood and Athletic Beginnings
Tom Selleck was born on January 29, 1945, in Detroit, Michigan, and grew up in Sherman Oaks, California. From an early age, he was involved in sports, particularly basketball. which played a significant role in his physical development. His athletic pursuits continued into college. where he attended the University of Southern California (USC) on a basketball scholarship. This early involvement in sports laid a strong foundation for his physical health and disciplined lifestyle.
Transition to Acting
Selleck's transition from an athlete to an actor came with its physical demands. His first significant role in "Magnum P.I." required him to perform various stunts and maintain a fit appearance. This role, which he played from 1980 to 1988. necessitated a rigorous fitness routine to meet the show's demands. setting the stage for his long-term commitment to health and wellness.
Fitness Regimen
Workout Routine
Tom Selleck health and fitness regimen has evolved. adapting to his changing roles and age. During his "Magnum, P.I." days. Selleck's workouts were intense and focused on building and maintaining muscle mass. His routine included weightlifting, cardiovascular exercises. and specific training for the stunts he performed on the show.
Selleck adjusted his fitness routine as he aged to suit his body's needs. Today, his workouts focus on maintaining flexibility, strength, and cardiovascular health. He incorporates low-impact exercises such as swimming, walking, and light weightlifting. This balanced approach helps him stay fit without putting undue strain on his joints and muscles.
Importance of Flexibility and Mobility
In recent years, Selleck has emphasized the importance of flexibility and mobility in his fitness regimen. Understanding the natural decline in muscle mass and joint flexibility with age. he includes stretching and yoga in his routine. These practices help prevent injuries, improve posture, and maintain mobilit
These simplified slides by Dr. Sidra Arshad present an overview of the non-respiratory functions of the respiratory tract.
Learning objectives:
1. Enlist the non-respiratory functions of the respiratory tract
2. Briefly explain how these functions are carried out
3. Discuss the significance of dead space
4. Differentiate between minute ventilation and alveolar ventilation
5. Describe the cough and sneeze reflexes
Study Resources:
1. Chapter 39, Guyton and Hall Textbook of Medical Physiology, 14th edition
2. Chapter 34, Ganong’s Review of Medical Physiology, 26th edition
3. Chapter 17, Human Physiology by Lauralee Sherwood, 9th edition
4. Non-respiratory functions of the lungs https://academic.oup.com/bjaed/article/13/3/98/278874
NVBDCP.pptx Nation vector borne disease control programSapna Thakur
NVBDCP was launched in 2003-2004 . Vector-Borne Disease: Disease that results from an infection transmitted to humans and other animals by blood-feeding arthropods, such as mosquitoes, ticks, and fleas. Examples of vector-borne diseases include Dengue fever, West Nile Virus, Lyme disease, and malaria.
Couples presenting to the infertility clinic- Do they really have infertility...Sujoy Dasgupta
Dr Sujoy Dasgupta presented the study on "Couples presenting to the infertility clinic- Do they really have infertility? – The unexplored stories of non-consummation" in the 13th Congress of the Asia Pacific Initiative on Reproduction (ASPIRE 2024) at Manila on 24 May, 2024.
Prix Galien International 2024 Forum ProgramLevi Shapiro
June 20, 2024, Prix Galien International and Jerusalem Ethics Forum in ROME. Detailed agenda including panels:
- ADVANCES IN CARDIOLOGY: A NEW PARADIGM IS COMING
- WOMEN’S HEALTH: FERTILITY PRESERVATION
- WHAT’S NEW IN THE TREATMENT OF INFECTIOUS,
ONCOLOGICAL AND INFLAMMATORY SKIN DISEASES?
- ARTIFICIAL INTELLIGENCE AND ETHICS
- GENE THERAPY
- BEYOND BORDERS: GLOBAL INITIATIVES FOR DEMOCRATIZING LIFE SCIENCE TECHNOLOGIES AND PROMOTING ACCESS TO HEALTHCARE
- ETHICAL CHALLENGES IN LIFE SCIENCES
- Prix Galien International Awards Ceremony
Liners, bases, and cements in clinical dentistry a review and update
1. Print
Liners, Bases, and Cements in Clinical Dentistry A Review and
Update
Category: Materials Created: Friday, 01 August 2003 00:00
Liners, bases, and cements used in clinical dentistry are an important part of restorative and
prosthodontic care and are constantly being improved. However, there is some degree of confusion
in terminology. For example, the term “lining cement” may be used even though the material is
not intended to be used as a cement, or “cement” may be used in reference to certain glass
ionomer materials, when in fact the product is not intended for use as a cement. This confusion
may be related to suggestions that dentists should reevaluate the liners and bases being used.1 A
study published in 1996 indicated that many dental schools could not agree on when to use each
type of material.2
This article will review the clinical applications for liners, bases, and cements and the different
types of materials that are available. Examples of products and manufacturers in each category are
provided, but these are not intended to represent a comprehensive list of available products.
CLINICAL USES
It was generally held that the toxic effects of dental materials were responsible for pulpal
inflammation. More recently, adverse pulpal reactions are believed to be caused by the influx of
bacteria and their toxins into the dentin.3,4 This can lead to pulpal inflammation and possibly
necrosis of pulpal tissue.5 Therefore, the clinician should attempt to reduce or eliminate
microleakage, which would result in reduction and possibly elimination of postoperative
sensitivity.
It has been proposed that secondary caries, marginal discoloration, and marginal gap/fracture
account for the majority of failed restorations.6 These failures occur at the interface between the
restoration and the cavity preparation. Therefore, improving the seal at this interface will reduce
the need for replacement of restorations.
One means of reducing the effects of microleakage is to prevent the development of caries via the
use of appropriate restorative materials. The choice of which material to use is in part determined
by the clinical situation, including the amount of remaining tooth structure. In terms of pulpal
health, it is more beneficial to conserve tooth structure when possible than to remove that same
tooth structure and replace it with a restorative material.7 Meryon demonstrated that a 0.5-mm
thickness of dentin reduces toxicity of a material by 75%, and if that thickness is increased to 1.0
mm, a reduction of 91% is seen.8 This study used materials that were known to have toxic effects.
When these materials came in contact with the test culture cells, a reduction in the number of
viable cells was seen. However, when a layer of dentin (dentin powder) was placed between the
test materials and the cells, an increase in the number of viable cells was seen compared to the
controls. The same holds true with respect to the smear layer. An intact smear layer helps occlude
the dentinal tubules and therefore provides a barrier to bacterial invasion. Since removal of the
smear layer is taught (with respect to resin bonding), one must consider protection of the pulp.
Currently, there are a number of methods for preparing a cavity, including use of a bur, air
abrasives, lasers, and hand instruments. The method by which tooth structure is removed does not
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
1 de 8 28/1/15 9:10
2. affect microleakage.9
Table. Materials used for liners, bases, and cements
Liner Base Cement Advantages Limitations
Varnish X low cost,
long history
of use
washes out
at margins
Calcium
Hydroxide
X X
(temporary)
low cost,
long history
of use
most
effective
when in
contact with
pulp
Zinc Oxide
Eugenol
X X X antibacterial,
long history,
sealing
ability
unable to
withstand
condensation
forces
Zinc
Oxyphosphate
X X long history low pH
Zinc
Polycarboxylate
X X long history thickness
may inhibit
seating of
casting
Glass Ionomer X X X fluoride
release
moisture
sensitive
Resin X X adhesive
strength
moisture,
technique
sensitive
Reprinted with permission of the Academy of General Dentistry
from: Weiner R. Liners, Bases, and Cements: A Solid Foundation.
Gen Dent. 2002; 50: 442-445.
The available materials that can be used as either a liner, a base, or a cement can be divided into 7
categories: varnishes, calcium hydroxide, zinc oxide eugenol/noneugenol zinc oxide, zinc
phosphate, zinc polycarboxylate, glass ionomer, and resin. In different situations, a material can be
considered a liner, a base, or a cement (see Table).
Many clinicians use more than one material beneath a restoration. However, caution is needed
because certain materials are not compatible with each other. For example, Yang and Chan
demonstrated that varnishes can reduce the surface hardness of glass ionomers.10
Following is a definition of liners, bases, and cements, and a discussion of how the 7 categories of
materials are used.
LINERS
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
2 de 8 28/1/15 9:10
3. Liners are materials that are placed as a thin coating (usually 0.5 mm) on the surface of a cavity
preparation. Although they provide a barrier to chemical irritants, they are not used for thermal
insulation or to add bulk to a cavity preparation.11 Furthermore, these materials do not have
sufficient hardness or strength to be used alone in a deep cavity.12 Of the categories listed above,
varnishes, calcium hydroxide, glass ionomers, and resins can be used as liners. Zinc eugenol, zinc
phosphate, and zinc polycarboxylates are generally not used as liners.
Varnish
A varnish is defined as natural gum (copal or resin) dissolved in an organic solvent such as
acetone, chloroform, or ether.13 After the dentin in the cavity preparation is covered with a varnish,
the solvent evaporates, leaving the solute as a thin layer or film. The theory behind a varnish
(example: Copalite/Cooley & Cooley) is that it seals the dentinal tubules, thus reducing the effects
of micro-leakage. When amalgam is first placed, the tooth/amalgam interface is not
microscopically sealed. Eventually the varnish dissolves and is replaced with the corrosion
products of the amalgam.14
There are several fluoride-containing varnishes available (examples: Duraphat, Colgate Oral
Pharmaceuticals; Dura-flor, Pharmascience Inc; Fluor Protector, Ivoclar Vivadent). Although the
FDA has approved these products both as cavity liners and for the treatment of sensitive teeth,
they are not approved for caries prevention.15 However, in Europe, fluoride varnishes have been
used in caries prevention programs/studies since 1968. The results showed a reduction in caries
ranging from 18% to 77%.16 In order for these varnishes to receive approval for use as a method of
caries prevention, the manufacturer would need to submit clinical studies to the FDA, in which
case the varnish would be classified as a drug.
Calcium Hydroxide
It is generally believed that calcium hydroxide (CH) is ideal for direct pulp capping since it
accelerates the formation of reparative dentin. There are 2 reasons for this: first, since the material
is basic (pH of 11), it serves as an irritant stimulating the formation of reparative dentin; and
second, the therapeutic affect of CH may be due to its ability to extract growth
factors from the dentin matrix.17 The result is the formation of a dentin bridge, which allows pulpal
repair. However, these concepts are challenged by Schuurs et al,18 who concluded that although
CH causes the formation of a dentin bridge, this seal does not last. Eventually the pulp will
undergo necrosis as a result of microleakage.
Due to the fact that CH has a basic pH, it is not generally supportive of bacterial growth. When the
base and catalyst portions of CH were tested separately, only the catalyst component was shown to
have any antibacterial effect.19 In addition, since bacterial byproducts are acidic, CH will directly
counteract this acidity and effectively neutralize these byproducts. It for this reason that CH is
placed under zinc phosphate—to help reduce the acidity of the zinc phosphate. CH is available in
chemical- cured forms (example: Dycal, DENTSPLY Caulk) and light-cured forms (example:
Prisma VLC Dycal, DENTSPLY Caulk) .
Glass Ionomer
This material has been available for more than 30 years. A current version of glass ionomer (GI) is
the resin-modified glass ionomer (example: Vitrebond, 3M ESPE). There are 2 clinical benefits
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
3 de 8 28/1/15 9:10
4. attributed to GIs: first is their ability to ionically bond to tooth structure (between the carboxylate
groups in the GI and the calcium ions in the enamel and dentin)20; and second, they release
fluoride. The ability of fluoride to inhibit the formation of secondary caries is established. Prati et
al21 demonstrated that when GI is used as a liner, a reduction in the consequences of microleakage
is seen. They attributed this to its antimicrobial properties. This benefit, along with its ability to
adhere to and seal the dentin,22 has made this material popular as a cavity liner.
GIs should not be used as pulp-capping agents. Unlike calcium hydroxide, GI does not promote
the formation of dentin bridges. In fact, in a clinical study, GI was found in the pulp chamber,
which triggered a persistent inflammatory response and appeared to prevent the formation of
dentin bridges.23
One restorative procedure that is often used clinically is known as the “sandwich technique.”24 In
this technique, the lining materials are brought to the cavosurface margin. There are 2 advantages
to this technique when using GI; first, released fluoride has a beneficial effect on the tooth
structure at the margin of the restoration. Donly et al,25 have shown that when this technique is
used, there is less recurrent caries at the margin of restorations. Second, the fluoride that is
released can be subsequently replaced with externally delivered fluoride. This can be via gel,
mouthrinse, or toothpaste, with the gel being most effective.26 GIs, both conventional and resin
modified, are available in both chemical- cured formulations (example: Ketacbond, 3M ESPE) and
light-cured formulations (example: Vitrebond, 3M ESPE). The light-cured products have been
shown to provide a better seal.27 Hand-mixed forms (examples: Vitrebond and Ketacbond) and
encapsulated/cartridge-dispensed forms (example: Fuji Lining LC, GC America) are also
available.
GIs have certain disadvantages. They are extremely sensitive to moisture. A study by Cattani-
Lorente et al,28 demonstrated that when GI comes in contact with water, there is a decrease in its
physical properties. In addition, resin-modified GIs expand after coming in contact with water.
Resin
Of the materials discussed here, resins are the most recent additions to the clinician’s
armamentarium. They are very versatile (generally being of high compressive and tensile
strength), possess low solubility, and are available in different viscosities and different shades.
When resins are used as a cavity liner, it is important to remember that it is the dentin bonding
agent (examples: Clearfil SE Bond, Kuraray America; Excite, Ivoclar Vivadent) that comes into
contact with the dentin. There are different types of dentin bonding agents, and their performance
differs.29 These resins are not recommended for direct pulp capping since, like glass ionomers,
they do not promote the formation of dentin bridges. In fact, there is a persistent mild
inflammatory pulpal response associated with resins when they are used as a direct pulp-capping
agent.30 Studies do confirm, however, that adhesives placed below amalgam restorations reduce
microleakage,31,32 thus supporting the current trend toward this practice of using resin as a liner.
However, the clinician must consider the logistics of using adhesive resin liners. Lining cavities
with copal varnish is faster and less technique-sensitive than using adhesive resin, and resins cost
more and have a limited shelf life.
In an attempt to overcome the polymerization shrinkage associated with traditional composite
resin, a new material—modified hybrid resin—has been developed. A resin with a reduced filler
load, it is referred to as a flowable composite (examples: Unifil Flow, GC America; Tetric Flow,
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
4 de 8 28/1/15 9:10
5. Ivoclar Vivadent). The better flow and reduced modulus of elasticity of these materials
theoretically reduce microleakage by increasing adaptation and by forming a stress-absorbing
layer.33 The result is a decrease in gap formation at the flowable-resin/tooth interface, which will
ultimately lead to a decrease in secondary caries and pulpal inflammation and a longer lasting
restoration.34 Although there is increased adaptation of the resin to the cavity preparation, the
material has a reduced filler content. This leads to an increase in polymerization shrinkage. The
net result, however, is a reduction in gingival microleakage when flowable resin is used, compared
to a conventional composite resin.35
It has been observed that some adhesives do not bond well to dentin in deep cavity preparations.
This makes them more susceptible to polymerization shrinkage stress that develops in deep
cavities.36 Since the bond strength to dentin near the pulp chamber is low, the polymerization
shrinkage that the resin undergoes can cause a gap to form. This was the conclusion reached by
Gordan et al, who also showed that the weakest bond was at the flowable-resin/tooth interface and
dentin near the pulp chamber.37
One study comparing a resin-modified GI, a flowable composite, and a dentin bonding agent
concluded that the resin-modified GI was associated with less microleakage than the other
materials.38
BASES
Bases can be considered as restorative substitutes for the dentin that was removed by caries and/or
the cavity preparation. They act as a barrier against chemical irritation, provide thermal insulation,
and can resist the condensation forces on a tooth when placing a restoration. Also, the clinician
can shape and contour base materials after placement into the cavity preparation.11 Varnishes and
calcium hydroxide materials are not in this category.
Zinc Oxide Eugenol
Zinc oxide eugenol (ZOE) (example: Intermediate Re-storative Material, DENTS-PLY Caulk)
materials provide an excellent seal of the cavity preparation. The ability of ZOE to reduce
postoperative sensitivity is most likely due to41A disadvantage of this material is its inability to
withstand the forces of condensation immediately after placement. The clinician should allow
approximately 24 hours to pass prior to placing amalgam above a ZOE base.
Zinc Oxyphosphate
Zinc oxyphosphate (ZOP) is a powder/liquid combination that is an ideal base material since it can
provide thermal insulation and will allow the condensation of amalgam several minutes after
placement. The material is acidic when placed (pH of approximately 3.5), but rises to a pH of 6.9
after a week. Mixing of the material should be performed on a cold glass slab. This promotes
cooling of the exothermic reaction that occurs when the powder and liquid are combined and
allows the clinician to incorporate more powder with the liquid, thus increasing the physical
properties.
According to ADA Specification No. 96, packages of ZOP contain 20% more liquid than is
necessary to combine with the powder. This is because some of the liquid will evaporate during
use. This specification applies to zinc phosphate, zinc polycarboxylate, and GI together since they
all are water-based. This is important for the clinician to consider. Since the water can evaporate,
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
5 de 8 28/1/15 9:10
6. these materials can become viscous, leading to difficulty in seating crowns. Furthermore, loss of
water will result in a decrease in the pH of the liquid, making the cement less biocompatible.
Examples of ZOP are Zinc Cement (Mission White) and Fleck’s Cement (Mizzy).
Zinc Polycarboxylate
A material that is comparable to ZOP is zinc polycarboxylate (ZPC). The important difference is
the liquid component. The liquid in ZPC is polyacrylic acid, which is quite viscous. Zinc
polycarboxylate adheres to the tooth via an interaction be-tween the carboxylic acid and the
calcium in the dentin. Polyacrylic acid has a very low pH (1.7), but the pH approaches neutrality
upon mixing with the powder. This cannot harm the tooth since the relatively large size of the
polyacrylic acid molecule and/or its ability to combine with protein prevents it from diffusing into
dentin tubules. Durelon and Durelon Maxicaps (3M ESPE) and Hybond zinc polycarboxylate
(Shofu) are examples of this product.
Glass Ionomer and Resin
GIs and resins are generally not used as bases. They do, however, meet a number of the
characteristics of a base; eg, they can be shaped and contoured and provide a chemical barrier.
When used under another restorative material, they are usually employed as a core buildup.
There are reports in the literature that advocate the use of these materials under a final
restoration.42,43 Two studies involved teeth with large carious lesions. The first study involved
complete removal of the caries, followed by filling the cavity with either a GI or a composite
resin.42 At a later visit, the tooth was prepared, leaving the original material as a base. The results
suggested that using either a GI or a composite resin as a base under amalgam was clinically
acceptable. The second study involved partial removal of caries, then the placement of GI over
calcium hydroxide.42 Six to 12 months later, the filling material was removed, and the dentin was
found to be hard and dry. This technique resulted in a reduction in cultivable microorganisms,
thought to be due to sealing the remaining caries from extrinsic substrate.
Examples of GI products that can be used for this purpose include Ketac-Silver (3M ESPE) and
Fuji II LC Core Material (GC America). Paracore (Coltene/Whaledent) and Luxacore
(Zenith/DMG) are examples of resin products.
CEMENTS
Materials that are considered cements can be used for 2 different purposes; the first is to retain
restorations or appliances in a fixed position in the mouth44. The other is as a restorative filling
material, used either alone or with other materials. In this situation, the material would be referred
to as a base.
As with liners and bases, cements also reduce microleakage by sealing the interface between the
tooth and the restoration. Dental cements can be categorized as either temporary (short-term) or
permanent (final). They should (1) have no adverse effects on the pulp tissue, (2) be of low
solubility, (3) have high compressive and tensile strength, and (4) be radiopaque.
It has been suggested that temporary cements be available in compact kits so waste is minimal,
dispensing is controlled, and mixing is easy. They should flow but not drip, be easily cleaned from
both instruments and margins, and have a quick set.45 These suggestions also apply to other types
of materials discussed in this article.
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
6 de 8 28/1/15 9:10
7. Temporary cements
Calcium hydroxide, zinc oxide eugenol/nonzinc oxide eugenol, zinc polycarboxylate, and resins
can be used as temporary cements.
Calcium Hydroxide
Although not usually thought of as a temporary cement, calcium hydroxide, as cited above, is not
harmful to the tooth. It is harder than ZOE-based temporary cements and is easily removed from
the margins of resin and PFM crowns. Also, since it is not eugenol-based, it will not interfere with
the final resin cements (see below). It is available in dentin and ivory shades.
Zinc Oxide Eugenol/Noneugenol Zinc Oxide
ZOE-based materials are known to provide an effective seal at the tooth/restoration interface. ZOE
has been shown to have adverse effects on resin-based products.46,47 However, others were not able
to confirm this.48 Tempbond (Kerr) and Embonte (Cadco) are 2 examples of a ZOE temporary
cement.
For those who use a resin cement as a final cement and want to be confident that the temporary
cement used will not interfere with final luting, noneugenol zinc oxide temporary cements are
available. Although these products (examples: Nogenol, GC America; Temrex TNE, Temrex ) do
not have a sedative effect on the tooth, they are compatible with resin-based provisional
restorations. In fact, since they have been shown to be stronger than ZOE temporary cement, it is
recommended that these products be used with preparations where retention is low.48
Zinc Polycarboxylate
There are 2 zinc polycarboxylate temporary cements (examples: Shofu’s Hybond zinc
polycarboxylate temporary cement soft kit and Ultradent’s Ultratemp) that are available. Both are
eugenol-free. The Hybond product contains fluoride.
Resin
Provilink (Ivoclar Vivadent) and Sensitemp (Sultan Chemists) are examples of provisional resin
cement. This type of temporary cement is ideal for anterior restorations due to its aesthetic
qualities. Since it is a material that is bonded to the tooth, it has excellent retention properties. In
fact, occasionally removal of the temporary restoration proves to be difficult. One disadvantage of
this material is evident after removal of the temporary restoration. The clinician may find brown
stains on the tooth.45 This stain is a potential problem when placing all-ceramic restorations.
Pumicing the preparation prior to cementation should remove the stain. Another problem that the
clinician may encounter with all resin cements is due to the shade of the material. Since these
materials are tooth colored, it might appear to the clinician that all excess cement has been
removed from the margins prior to patient dismissal. The clinician must be very careful when
removing excess cement. This is especially true with certain tooth morphology; for example, in
subgingival regions in proximity to furcations and other areas of tooth concavity.40
Final Cements
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...
7 de 8 28/1/15 9:10
8. Zinc Oxide Eugenol
ZOE, Type II, is used for permanent or final cementation. This material has an inorganic filler
added to the powder and ortho-ethoxybenzoic acid added to the liquid. It appears that this type of
cement is not particularly popular, since there are not many brands available. Also, a review of the
literature did not identify any studies in which a ZOE final cement was comparatively evaluated.
Fynal (DENTSPLY Caulk) is an example of this kind of cement.
Zinc Oxyphosphate/Zinc Polycarboxylate
The liquids in both of these mixtures are acids. Therefore, these products are self-etching. These
cements may demineralize dentin, but this does not occur in a uniform manner. ZOP causes more
demineralization than does ZPC.50 Both of these materials have a long history of clinical use in
dentistry. In fact, a version of ZOP was introduced in the late 1800s and was known as Ames’
black copper cement. It contained copper (cupric oxide 97%) and was found to be germicidal. This
product was eventually discontinued, but was reintroduced as Doc’s Best Red Copper Zinc
Phosphate Cement (Cooley & Cooley). This currently available product contains 7% cupric oxide.
Unlike other ZOP cements, this product has a brown color, which makes it unsuitable for
all-ceramic restorations.
ZPC has a rubbery consistency when setting. Therefore, it is best to remove all excess from the
margins only when it is fully set, or the material may be pulled from under the casting. When
using ZPC, the clinician should be aware that the cement-casting interface is where failure may
occur (ZPC chemically adheres to the tooth). This is in contrast to ZOP, where the cement-tooth
interface is where failure can occur.
Glass Ionomer
GI cement is available in both hand-mixed forms (examples: Fuji I Glass Ionomer Cement, GC
America; CX-Plus GlasIonomer cement, Shofu) and encapsulated/cartridge forms (examples:
FujiCem, GC America; VivaglassCem, Ivoclar Vivadent). These are self-cured formulations.
One disadvantage of using GI as a cement or luting agent is its sensitivity to moisture. In fact,
Mojon et al51 suggest that when using GIs, the involved teeth should be protected from
contamination from saliva for as long as 15 minutes after mixing. In contrast, the resin-modified
GIs (RMGIs) are hydrophilic (water-absorbing). This presents both an advantage and a
disadvantage. The advantage is that the material will expand after coming in contact with
moisture, filling any marginal gaps. The disadvantage is that this same expansion can cause
all-ceramic crowns to fracture. Lastly, it has been suggested that RMGIs are ideal luting agents for
patients who have a high caries index. (Fluoride is released from RMGI.)52 Nevertheless, it might
be difficult or impossible to remove a post cemented with this material.
Resin
Resin-based cements can be grouped into categories based on how they are cured. They can be
either self- or chemical-cured (examples: Parapost Cemen
Liners, Bases, and Cements in Clinical Dentistry A Review a... http://www.dentistrytoday.com/materials/1482--sp-37510084...