The document presents an experimental study that evaluated the residual compressive behavior of self-compacting concrete (SCC) mixes exposed to high temperatures up to 600°C. Ten SCC mixes were tested that varied the type and amount of mineral additives used as partial replacements for cement by weight, including metakaolin (5-15%), fly ash (20-30%), and limestone (5-15%). Testing of the mixes included compressive strength, stress-strain behavior, modulus of elasticity, and strain at peak stress at room temperature and after high temperature exposure. The results showed a significant decrease in mechanical properties for all mixes after 200°C, with the mineral additives affecting the variations in residual strength by 24%
The document studies the strength of geopolymer concrete with alkaline solutions of varying molarity. Laboratory tests were conducted on compressive strength, split tensile strength, and flexural strength of geopolymer concrete specimens made with different molarity alkaline solutions. The results showed that specimens with a 12M alkaline solution achieved the highest strengths for compressive strength, split tensile strength, and flexural strength.
IRJET- Review on High Temperature Concrete using Shockwave ApplicationIRJET Journal
The document discusses using shockwaves to improve the fire resistance of concrete. It describes how shockwaves are induced in fresh concrete using a shock tube apparatus. Tests were conducted on concrete subjected to temperatures from 100°C to 700°C for 28 days. The compressive strength of normal concrete was compared to concrete with metakaolin additive and concrete with both metakaolin and induced shockwaves. Results showed that shockwave induction and metakaolin additive can improve the compressive strength retention of concrete exposed to high temperatures.
IRJET- Review on High Temperature Concrete using Shockwave ApplicationIRJET Journal
The document discusses using shockwaves to improve the fire resistance of concrete. It aims to study the effect of inducing shockwaves in concrete using a shock tube apparatus. Tests were conducted on concrete exposed to high temperatures from 100°C to 700°C for 28 days. The performance of normal concrete, shockwave-induced concrete, and concrete with metakaolin or both shockwaves and metakaolin was compared based on compression tests. Previous research found that partially replacing cement with metakaolin or blast furnace slag improved concrete strength, especially at later ages. The inclusion of metakaolin in concrete containing slag prevented early strength loss.
IRJET- Strength and Cost Comparision of Bagasse Concrete with the Applicat...IRJET Journal
This document summarizes research on using sugarcane bagasse cinder concrete (SBCC) and ceramic wool insulation for building walls and roofs. Tests were conducted to determine the optimal mix ratios of bagasse cinder, cement, coal ash and lime to achieve sufficient compressive strength around 20MPa. A mix of 50% bagasse cinder, 20% cement, 10% coal ash and 20% lime performed best. Walls constructed with this mix achieved 11.32MPa strength. Additional tests examined using ceramic wool insulation on SBCC walls and roofs. Insulated surfaces saw temperature reductions of up to 22.4°C compared to uninsulated surfaces, improving thermal comfort while reducing energy costs. The research concludes SB
Effect of elevated temperature on properties of geopolymer concrete: A reviewIRJET Journal
This document provides a literature review on the effect of elevated temperatures on the properties of geopolymer concrete. It summarizes several research papers that studied how geopolymer concrete performs when subjected to temperatures ranging from 200°C to 1000°C. The key findings include:
1) Specimen size and aggregate size were identified as the most important factors affecting strength at high temperatures, with larger sizes performing better.
2) Thermal mismatch between the geopolymer matrix and aggregates causes strength loss at high temperatures above 600°C.
3) Incorporating ground granulated blast furnace slag (GGBFS) can improve mechanical properties but exacerbates damage at high temperatures compared to fly ash geopolym
Study on the Thermal Properties of Mortars with Partial Cement Replacement by...IRJET Journal
The document discusses a study on the thermal properties of cement mortars with partial replacement of cement by ceramic waste powder and barite powder. Various mixes with 10-50% replacement were tested for compressive strength, thermal conductivity, specific heat, decrement factor, and time lag. The CC20 mix, with 20% replacement, performed best with the lowest thermal conductivity and highest specific heat. A thermal analysis of a building wall in COMSOL software found the CC20 plaster provided the best thermal performance by maintaining an inner wall temperature of 26°C when the outer surface was at 34.2°C. The study aims to develop sustainable construction materials that provide good thermal insulation and reduce environmental impacts.
IRJET- Experimental Study on Residual Characteristics of Concrete Subjected t...IRJET Journal
The document summarizes research on the effects of elevated temperatures on the physical and mechanical properties of concrete. Specifically, it discusses:
1) An experimental study that subjected concrete cube specimens to temperatures of 250°C, 500°C, and 750°C and then tested them to analyze changes in physical, mechanical, and stiffness characteristics.
2) Previous research that also investigated how properties like compressive strength and elastic modulus of concrete are reduced when exposed to high temperatures.
3) The testing involved heating concrete samples to temperatures from 100°C to 1200°C and then analyzing their residual properties and microstructure. The research aimed to better understand how high temperatures impact fire-resistant design of concrete structures.
A Review On Development Of Flyash Based High Strength Geopolymer Concretecedmmantc5411
Geopolymer concrete is the latest development in the field of concrete technology and it is still
developing. Geopolymers are inorganic, stable, hard and non-inflammable binder. The application of
geopolymer binder are in fire resistance fiber composite, sealant industry, tooling aeronautics SPF aluminium,
foundry equipment’s, radioactive toxic waste, ceramic, bricks and other precast concrete. The current review is
aims to put forward the development in geopolymer concrete for the production high strength geopolymer
concrete having strength more than 90MPa. The development of high strength concrete is aimed to reduce
structural member sizes and for economical construction in case of long span bridges and tall buildings. Also
the use flyash in concrete to reduce green gas house emission into the atmosphere by reducing cement usage
The document studies the strength of geopolymer concrete with alkaline solutions of varying molarity. Laboratory tests were conducted on compressive strength, split tensile strength, and flexural strength of geopolymer concrete specimens made with different molarity alkaline solutions. The results showed that specimens with a 12M alkaline solution achieved the highest strengths for compressive strength, split tensile strength, and flexural strength.
IRJET- Review on High Temperature Concrete using Shockwave ApplicationIRJET Journal
The document discusses using shockwaves to improve the fire resistance of concrete. It describes how shockwaves are induced in fresh concrete using a shock tube apparatus. Tests were conducted on concrete subjected to temperatures from 100°C to 700°C for 28 days. The compressive strength of normal concrete was compared to concrete with metakaolin additive and concrete with both metakaolin and induced shockwaves. Results showed that shockwave induction and metakaolin additive can improve the compressive strength retention of concrete exposed to high temperatures.
IRJET- Review on High Temperature Concrete using Shockwave ApplicationIRJET Journal
The document discusses using shockwaves to improve the fire resistance of concrete. It aims to study the effect of inducing shockwaves in concrete using a shock tube apparatus. Tests were conducted on concrete exposed to high temperatures from 100°C to 700°C for 28 days. The performance of normal concrete, shockwave-induced concrete, and concrete with metakaolin or both shockwaves and metakaolin was compared based on compression tests. Previous research found that partially replacing cement with metakaolin or blast furnace slag improved concrete strength, especially at later ages. The inclusion of metakaolin in concrete containing slag prevented early strength loss.
IRJET- Strength and Cost Comparision of Bagasse Concrete with the Applicat...IRJET Journal
This document summarizes research on using sugarcane bagasse cinder concrete (SBCC) and ceramic wool insulation for building walls and roofs. Tests were conducted to determine the optimal mix ratios of bagasse cinder, cement, coal ash and lime to achieve sufficient compressive strength around 20MPa. A mix of 50% bagasse cinder, 20% cement, 10% coal ash and 20% lime performed best. Walls constructed with this mix achieved 11.32MPa strength. Additional tests examined using ceramic wool insulation on SBCC walls and roofs. Insulated surfaces saw temperature reductions of up to 22.4°C compared to uninsulated surfaces, improving thermal comfort while reducing energy costs. The research concludes SB
Effect of elevated temperature on properties of geopolymer concrete: A reviewIRJET Journal
This document provides a literature review on the effect of elevated temperatures on the properties of geopolymer concrete. It summarizes several research papers that studied how geopolymer concrete performs when subjected to temperatures ranging from 200°C to 1000°C. The key findings include:
1) Specimen size and aggregate size were identified as the most important factors affecting strength at high temperatures, with larger sizes performing better.
2) Thermal mismatch between the geopolymer matrix and aggregates causes strength loss at high temperatures above 600°C.
3) Incorporating ground granulated blast furnace slag (GGBFS) can improve mechanical properties but exacerbates damage at high temperatures compared to fly ash geopolym
Study on the Thermal Properties of Mortars with Partial Cement Replacement by...IRJET Journal
The document discusses a study on the thermal properties of cement mortars with partial replacement of cement by ceramic waste powder and barite powder. Various mixes with 10-50% replacement were tested for compressive strength, thermal conductivity, specific heat, decrement factor, and time lag. The CC20 mix, with 20% replacement, performed best with the lowest thermal conductivity and highest specific heat. A thermal analysis of a building wall in COMSOL software found the CC20 plaster provided the best thermal performance by maintaining an inner wall temperature of 26°C when the outer surface was at 34.2°C. The study aims to develop sustainable construction materials that provide good thermal insulation and reduce environmental impacts.
IRJET- Experimental Study on Residual Characteristics of Concrete Subjected t...IRJET Journal
The document summarizes research on the effects of elevated temperatures on the physical and mechanical properties of concrete. Specifically, it discusses:
1) An experimental study that subjected concrete cube specimens to temperatures of 250°C, 500°C, and 750°C and then tested them to analyze changes in physical, mechanical, and stiffness characteristics.
2) Previous research that also investigated how properties like compressive strength and elastic modulus of concrete are reduced when exposed to high temperatures.
3) The testing involved heating concrete samples to temperatures from 100°C to 1200°C and then analyzing their residual properties and microstructure. The research aimed to better understand how high temperatures impact fire-resistant design of concrete structures.
A Review On Development Of Flyash Based High Strength Geopolymer Concretecedmmantc5411
Geopolymer concrete is the latest development in the field of concrete technology and it is still
developing. Geopolymers are inorganic, stable, hard and non-inflammable binder. The application of
geopolymer binder are in fire resistance fiber composite, sealant industry, tooling aeronautics SPF aluminium,
foundry equipment’s, radioactive toxic waste, ceramic, bricks and other precast concrete. The current review is
aims to put forward the development in geopolymer concrete for the production high strength geopolymer
concrete having strength more than 90MPa. The development of high strength concrete is aimed to reduce
structural member sizes and for economical construction in case of long span bridges and tall buildings. Also
the use flyash in concrete to reduce green gas house emission into the atmosphere by reducing cement usage
IRJET- An Experimental Study on Effect of Curing Temperature on Geopolymer Co...IRJET Journal
This study experimentally investigated the effect of curing temperature on the properties of geopolymer concrete made with fly ash and foundry sand. Three mixtures were tested with 0%, 10%, and 20% replacement of normal sand with foundry sand. Specimens were cured at ambient temperature or in an oven at temperatures ranging from 60-90°C. Results showed heat curing increased compressive strength, split tensile strength, and flexural strength compared to ambient curing. Replacing 10% normal sand with foundry sand produced the highest strengths. Compressive strength increased up to 70% with heat curing versus ambient. Maximum strength was achieved with 90°C heat curing for 24 hours. In conclusion, heat c
Petrographic investigation to assess condition of concrete exposed to fireIRJET Journal
1. Concrete specimens were heated to temperatures from 200°C to 800°C and then allowed to cool naturally. Rapid chloride permeability tests were then performed on the specimens.
2. Test results found that the structure of pores and microcracks within the concrete impacted chloride ion penetration. Specimens exposed to temperatures up to 200°C showed low chloride penetration, while 400°C exposure showed moderate penetration.
3. High temperature exposure of 800°C resulted in significant cracking in all concrete mixes and rapid chloride permeability values over 400C, indicating high chloride ion penetration. The study found that increased heating temperature leads to higher chloride permeability in the concrete.
This document summarizes research on geopolymer concrete, which is an environmentally friendly alternative to traditional Portland cement concrete. It can be created using industrial byproducts such as fly ash and alkaline liquids instead of cement. Several studies discussed found that geopolymer concrete requires high temperature curing but can achieve high strength. The document reviews research showing that replacing fly ash partially with ground granulated blast furnace slag in geopolymer concrete increases strength without the need for oven curing. While research has made progress in developing geopolymer concrete, more information is still needed regarding some aspects of the geopolymerization process.
Study on Strength of Fly Ash Based Geopolymer Concrete Under Heat Curingijsrd.com
fly ash is a noncombustible material obtained from the various thermal power plants. Since fly ash is available in large scale, it is disposed of in rivers and landfills and ponds by thermal industries which are posing danger to environment. Due to high pozzolanic activity of fly ash, efforts are being made to use it as a cement replacement material. GeoPolymer concrete makes 100 percent utilization of fly ash in concrete along with alkaline solutions, as a binder. The cube specimens and beams are casted for 2% and 4% super plasticizers and alkaline to fly ash ratio of 0.35. The compressive strength of cubes is compared to that of conventional cubes at 7, 14 and 28 days .it is observed that GeoPolymer concrete is economical as compared to normal concrete from compressive strength point of view.
A EXPERIMENTAL STUDY ON SELF COMPACTING CONCRETE WHEN SUBJECTED TO ELEVATED TEMPERATURE
To achieve the SCC mix for M40 grade
To obtain optimum Percentage Replacement of cement by GGBS, FLYASH, Micro cement
To find the Mechanical Properties of SCC when subjected to elevated temperature
To draw the conclusions after conducting the Tests.
Effect Of Curing Temperature And Curing Hours On The Properties Of Geo-Polyme...ijceronline
International Journal of Computational Engineering Research (IJCER) is dedicated to protecting personal information and will make every reasonable effort to handle collected information appropriately. All information collected, as well as related requests, will be handled as carefully and efficiently as possible in accordance with IJCER standards for integrity and objectivity.
STUDY OF MECHANICAL AND DURABILITY PROPERTIES OF GEOPOLYMER CONCRETEAbhilash Chandra Dey
This document summarizes a study that evaluated the durability of geopolymer concrete compared to ordinary Portland cement concrete when exposed to seawater. Two geopolymer concrete mixes using 8M and 14M sodium hydroxide solutions and one ordinary Portland cement concrete mix were prepared. Beams and cylinders made with each concrete mix were partially submerged in seawater and an accelerated corrosion test was performed on the reinforced beams by applying a voltage to induce corrosion. The time until cracking occurred due to corrosion was recorded and used to evaluate the durability performance of the different concrete mixes. The test results indicate that geopolymer concrete exhibited better resistance to chloride attack compared to ordinary Portland cement concrete.
The global gas emission is keeping on increasing for which cement industry alone contributes 5%. The enormous water is required for curing of concrete in construction industry which can effectively be used for various purposes. The accelerated carbonation curing shows a way to reduce these emissions in a very effective way by sequestering it in concrete elements. In this paper the effect of accelerated carbonation curing was reviewed on non-reinforced concrete elements (cubes) and reinforced concrete elements (prisms). The CO2 curing showed 60% in strength of cubes and prisms, respectively when compared to water cured specimens. This early age strength through waste gas proves beneficial in terms of reducing in atmospheric pollution and saving the water which is a critical resource now-a-days.
Strength Study of copper slag & Fly Ash With Replacement Of Aggregate's In Co...IRJET Journal
This document discusses a study on using industrial byproducts like fly ash and copper slag to replace aggregates in concrete for road construction. The study aims to address issues with excessive sand usage by finding sustainable alternatives. Concrete samples of different grades were produced by replacing natural sand with copper slag at varying percentages. The samples were tested for load carrying capacity and flexural strength. The results showed that concrete with 100% copper slag replacement performed similarly to normal concrete, indicating that copper slag can successfully replace sand in concrete for roads. The document also reviews several other studies on using industrial wastes in construction and their findings.
Experimental Investigation on Durability Properties of Silica Fume blended Hi...IRJET Journal
This study investigated the strength and durability properties of silica fume blended high strength concrete (HSC). Three concrete mixes (M60, M70, M80) were prepared by replacing 15% of cement with silica fume. Compressive strength and sorpitivity tests were conducted on cubes and cylinders cured for 7, 14, and 28 days. Results showed the M70 and M80 mixes achieved higher compressive strengths compared to M60, with M80 reaching 59.89 MPa and 80.09 MPa at 7 and 28 days. Sorpitivity tests found the rate of water penetration decreased with curing time for all mixes, indicating improved durability. The study demonstrated adding silica fume
Performance of Concrete at Elevated Temperatures: Utilizing A Blended Ordinar...IOSR Journals
This study aimed at investigating the effect of subjecting concrete, produced with cement being
partially replaced with saw dust ash (SDA) to elevated temperatures. The performance of the test concrete cubes
was done by exposing them to elevated temperatures of 200oC, 400oC, 600oC and 800oC, and allowed to cool
down to room temperature before testing for their properties. Both the physical and thermal properties of the
concrete cubes were determined. The concrete produced by blending cement with 10% SDA with an average
percentage loss of 23.04% retained more of its compressive strength when exposed to the different
temperatures, than concrete produced using only OPC, which has an average percentage loss of 29.11%. It is
also found that, at an elevated temperature of 800oC, concrete fail totally in flexure due to the effect of high
heat on binding elements. The flexural strength of both the control concrete (at 0% OPC replacement) and
OPC/SDA blended concrete (at 10% OPC replacement) decreased as the temperature is increased. The
replacement of OPC by 10% SDA increased the thermal shock resistance of the concrete by 11 cycles than the
0% OPC concrete at the same temperature. The concrete produced with OPC has better thermal conductivity
than the concrete produced by blending OPC with SDA, as a result, the dislodgement of the concrete edges is
relatively lower in the SDA blended cement concrete than in the OPC concrete. The result shows that, blending
OPC with SDA in concrete performed better at elevated temperatures than concrete produced with only OPC.
Therefore, the replacement of OPC with 10% SDA can be applied as a fire resisting bonding material in
concrete.
IRJET- Partial Replacement of Aggregates in Geopolymer ConcreteIRJET Journal
This document summarizes a study that investigated partially replacing aggregates in geopolymer concrete with industrial waste materials. Geopolymer concrete was produced by completely replacing ordinary Portland cement with fly ash. Fine aggregate was partially replaced with charcoal powder and coarse aggregate was partially replaced with crushed coconut shells. Specimens with 0%, 10%, and 20% aggregate replacement were tested for compressive, tensile, and flexural strength at 7 and 28 days. The 10% replacement mix achieved the highest compressive strength at 28 days. Strength generally decreased as replacement increased. However, using waste materials can reduce environmental impacts while providing adequate strength for construction applications.
Corrosion resistance performance of fly ash blended cement concreteseSAT Journals
Abstract Durability of reinforced concrete with respect to corrosion of reinforcement is one of the major aspects to be considered in the management of civil infrastructure systems. An accelerated laboratory test method developed at SERC where the concrete specimen containing rebar is subjected to polarization under a constant voltage in a sodium chloride solution. It is found that the current response with time follows that of a typical service life model indicating depassivation and corrosion propagation. Index terms- Materials, cement, super plasticizer, workability, compressive strength etc.
Corrosion resistance performance of fly ash blended cement concreteseSAT Publishing House
1) The document describes an experimental study on the corrosion resistance of reinforced concrete with different percentages of fly ash replacement.
2) An accelerated corrosion test method was used where concrete cylinders containing rebar were subjected to polarization in a sodium chloride solution. This simulated rebar corrosion in marine environments.
3) The test results showed that concretes with 30% fly ash replacement had the highest corrosion resistance, with initiation times of 54 and 63 days for M25 and M30 grade concrete, respectively.
4) Graphs of current over time showed changes in slope indicating the initiation time and time for cracking, which increased with higher percentages of fly ash replacement up to 30%.
This document summarizes a research study on the effect of using electrically precipitated fly ash (EPFA) as a partial replacement for cement in self-compacting concrete (SCC). The study tested SCC mixes with 0-30% EPFA replacement at 5% intervals. Tests were conducted on fresh properties, mechanical properties like compressive strength, and durability properties like rapid chloride permeability and water sorptivity. Results showed that 20% EPFA replacement provided better results than the control SCC mix, improving properties while also providing economic and environmental benefits through reduced cement usage.
This document summarizes a review on the properties of high-performance concrete. It discusses that high-performance concrete incorporates supplementary cementitious materials like fly ash and silica fume to improve strength and durability compared to regular concrete. It describes various supplementary materials used in high-performance concrete like silica fume, alccofine, metakaolin, rice husk ash, and bamboo leaf ash and how they improve properties. It also discusses the effects of aggregates, fibers, and other ingredients on high-performance concrete characteristics. The purpose is to provide information on developing high-performance concrete mixtures with optimized properties.
Design of High Compressive Strength Concrete Mix without AdditivesIJERA Editor
In this paper, the crashed Basalt and uncrushed granite is used in concrete mixes as coarse aggregate. The selected materials, with high specification using special production techniques, the properties ,the mix design procedure and mix proportion of the high strength concrete (HSC) were discussed. Different proportions of Ordinary Portland cement (410,430 and 450) kg/m3 with different crashed Basalt and uncrushed Granite coarse aggregate amount (1120 and 1050) kg/m3 and fine aggregate with fine modulus of 3.65 were used. Eight concrete mixes were prepared: two as control mix for crashed Basalt and uncrushed Granite, three with crashed Basalt and three with uncrushed Granite coarse aggregate with mix amount(410:680:1120,430:610:1050 and 450:550:1050) kg/m3,(cement: fine aggregate: coarse aggregate)respectively. The study showed that the use of granite coarse aggregate in concrete mixes has a clear effect in mix proportion. The compressive strength of concrete was measured at ages of 7, 28 and 56 days and it was found that the granite (Mix3) of (450:550:1050) kg/m3 with w/c of 0.46 give the highest of strength in 28 and 56 days among the abovementioned mixes its 56 and 64 N/mm2 respectively. The paper shows that good results of compressive strength and workability of concrete were obtained when using granite coarse aggregate.
This document summarizes a study that assessed the fresh and hardened properties of self-consolidating concrete (SCC) containing steel, polypropylene, and hybrid fibers at various high temperatures. Four SCC mixtures were tested: a control without fibers, one with 1% polypropylene fibers, one with 1% steel fibers, and one with 0.5% of each steel and polypropylene fibers. All mixtures met standards for workability and passing ability. The inclusion of fibers slightly reduced workability. Mechanical properties generally increased with temperature up to 200°C then decreased at higher temperatures. Fiber-reinforced SCC exhibited improved spalling resistance compared to plain SCC.
This document reviews the development and use of supplementary cementitious materials (SCMs) in self-compacting concrete (SCC). It summarizes past literature on how various calcium-rich and silica-rich SCMs have been used to improve the properties of SCC. The review focuses on the effects of ultra-fine fly ash (UFFA) on the plastic and hardened properties of SCC. It notes that prior studies have examined the use of SCMs like fly ash, slag, and silica fume to enhance workability and strength but that no comprehensive study has looked at the impact of UFFA specifically. The review proposes that future work should examine how UFFA influences SCC properties using an artificial
IRJET- An Experimental Study on Effect of Curing Temperature on Geopolymer Co...IRJET Journal
This study experimentally investigated the effect of curing temperature on the properties of geopolymer concrete made with fly ash and foundry sand. Three mixtures were tested with 0%, 10%, and 20% replacement of normal sand with foundry sand. Specimens were cured at ambient temperature or in an oven at temperatures ranging from 60-90°C. Results showed heat curing increased compressive strength, split tensile strength, and flexural strength compared to ambient curing. Replacing 10% normal sand with foundry sand produced the highest strengths. Compressive strength increased up to 70% with heat curing versus ambient. Maximum strength was achieved with 90°C heat curing for 24 hours. In conclusion, heat c
Petrographic investigation to assess condition of concrete exposed to fireIRJET Journal
1. Concrete specimens were heated to temperatures from 200°C to 800°C and then allowed to cool naturally. Rapid chloride permeability tests were then performed on the specimens.
2. Test results found that the structure of pores and microcracks within the concrete impacted chloride ion penetration. Specimens exposed to temperatures up to 200°C showed low chloride penetration, while 400°C exposure showed moderate penetration.
3. High temperature exposure of 800°C resulted in significant cracking in all concrete mixes and rapid chloride permeability values over 400C, indicating high chloride ion penetration. The study found that increased heating temperature leads to higher chloride permeability in the concrete.
This document summarizes research on geopolymer concrete, which is an environmentally friendly alternative to traditional Portland cement concrete. It can be created using industrial byproducts such as fly ash and alkaline liquids instead of cement. Several studies discussed found that geopolymer concrete requires high temperature curing but can achieve high strength. The document reviews research showing that replacing fly ash partially with ground granulated blast furnace slag in geopolymer concrete increases strength without the need for oven curing. While research has made progress in developing geopolymer concrete, more information is still needed regarding some aspects of the geopolymerization process.
Study on Strength of Fly Ash Based Geopolymer Concrete Under Heat Curingijsrd.com
fly ash is a noncombustible material obtained from the various thermal power plants. Since fly ash is available in large scale, it is disposed of in rivers and landfills and ponds by thermal industries which are posing danger to environment. Due to high pozzolanic activity of fly ash, efforts are being made to use it as a cement replacement material. GeoPolymer concrete makes 100 percent utilization of fly ash in concrete along with alkaline solutions, as a binder. The cube specimens and beams are casted for 2% and 4% super plasticizers and alkaline to fly ash ratio of 0.35. The compressive strength of cubes is compared to that of conventional cubes at 7, 14 and 28 days .it is observed that GeoPolymer concrete is economical as compared to normal concrete from compressive strength point of view.
A EXPERIMENTAL STUDY ON SELF COMPACTING CONCRETE WHEN SUBJECTED TO ELEVATED TEMPERATURE
To achieve the SCC mix for M40 grade
To obtain optimum Percentage Replacement of cement by GGBS, FLYASH, Micro cement
To find the Mechanical Properties of SCC when subjected to elevated temperature
To draw the conclusions after conducting the Tests.
Effect Of Curing Temperature And Curing Hours On The Properties Of Geo-Polyme...ijceronline
International Journal of Computational Engineering Research (IJCER) is dedicated to protecting personal information and will make every reasonable effort to handle collected information appropriately. All information collected, as well as related requests, will be handled as carefully and efficiently as possible in accordance with IJCER standards for integrity and objectivity.
STUDY OF MECHANICAL AND DURABILITY PROPERTIES OF GEOPOLYMER CONCRETEAbhilash Chandra Dey
This document summarizes a study that evaluated the durability of geopolymer concrete compared to ordinary Portland cement concrete when exposed to seawater. Two geopolymer concrete mixes using 8M and 14M sodium hydroxide solutions and one ordinary Portland cement concrete mix were prepared. Beams and cylinders made with each concrete mix were partially submerged in seawater and an accelerated corrosion test was performed on the reinforced beams by applying a voltage to induce corrosion. The time until cracking occurred due to corrosion was recorded and used to evaluate the durability performance of the different concrete mixes. The test results indicate that geopolymer concrete exhibited better resistance to chloride attack compared to ordinary Portland cement concrete.
The global gas emission is keeping on increasing for which cement industry alone contributes 5%. The enormous water is required for curing of concrete in construction industry which can effectively be used for various purposes. The accelerated carbonation curing shows a way to reduce these emissions in a very effective way by sequestering it in concrete elements. In this paper the effect of accelerated carbonation curing was reviewed on non-reinforced concrete elements (cubes) and reinforced concrete elements (prisms). The CO2 curing showed 60% in strength of cubes and prisms, respectively when compared to water cured specimens. This early age strength through waste gas proves beneficial in terms of reducing in atmospheric pollution and saving the water which is a critical resource now-a-days.
Strength Study of copper slag & Fly Ash With Replacement Of Aggregate's In Co...IRJET Journal
This document discusses a study on using industrial byproducts like fly ash and copper slag to replace aggregates in concrete for road construction. The study aims to address issues with excessive sand usage by finding sustainable alternatives. Concrete samples of different grades were produced by replacing natural sand with copper slag at varying percentages. The samples were tested for load carrying capacity and flexural strength. The results showed that concrete with 100% copper slag replacement performed similarly to normal concrete, indicating that copper slag can successfully replace sand in concrete for roads. The document also reviews several other studies on using industrial wastes in construction and their findings.
Experimental Investigation on Durability Properties of Silica Fume blended Hi...IRJET Journal
This study investigated the strength and durability properties of silica fume blended high strength concrete (HSC). Three concrete mixes (M60, M70, M80) were prepared by replacing 15% of cement with silica fume. Compressive strength and sorpitivity tests were conducted on cubes and cylinders cured for 7, 14, and 28 days. Results showed the M70 and M80 mixes achieved higher compressive strengths compared to M60, with M80 reaching 59.89 MPa and 80.09 MPa at 7 and 28 days. Sorpitivity tests found the rate of water penetration decreased with curing time for all mixes, indicating improved durability. The study demonstrated adding silica fume
Performance of Concrete at Elevated Temperatures: Utilizing A Blended Ordinar...IOSR Journals
This study aimed at investigating the effect of subjecting concrete, produced with cement being
partially replaced with saw dust ash (SDA) to elevated temperatures. The performance of the test concrete cubes
was done by exposing them to elevated temperatures of 200oC, 400oC, 600oC and 800oC, and allowed to cool
down to room temperature before testing for their properties. Both the physical and thermal properties of the
concrete cubes were determined. The concrete produced by blending cement with 10% SDA with an average
percentage loss of 23.04% retained more of its compressive strength when exposed to the different
temperatures, than concrete produced using only OPC, which has an average percentage loss of 29.11%. It is
also found that, at an elevated temperature of 800oC, concrete fail totally in flexure due to the effect of high
heat on binding elements. The flexural strength of both the control concrete (at 0% OPC replacement) and
OPC/SDA blended concrete (at 10% OPC replacement) decreased as the temperature is increased. The
replacement of OPC by 10% SDA increased the thermal shock resistance of the concrete by 11 cycles than the
0% OPC concrete at the same temperature. The concrete produced with OPC has better thermal conductivity
than the concrete produced by blending OPC with SDA, as a result, the dislodgement of the concrete edges is
relatively lower in the SDA blended cement concrete than in the OPC concrete. The result shows that, blending
OPC with SDA in concrete performed better at elevated temperatures than concrete produced with only OPC.
Therefore, the replacement of OPC with 10% SDA can be applied as a fire resisting bonding material in
concrete.
IRJET- Partial Replacement of Aggregates in Geopolymer ConcreteIRJET Journal
This document summarizes a study that investigated partially replacing aggregates in geopolymer concrete with industrial waste materials. Geopolymer concrete was produced by completely replacing ordinary Portland cement with fly ash. Fine aggregate was partially replaced with charcoal powder and coarse aggregate was partially replaced with crushed coconut shells. Specimens with 0%, 10%, and 20% aggregate replacement were tested for compressive, tensile, and flexural strength at 7 and 28 days. The 10% replacement mix achieved the highest compressive strength at 28 days. Strength generally decreased as replacement increased. However, using waste materials can reduce environmental impacts while providing adequate strength for construction applications.
Corrosion resistance performance of fly ash blended cement concreteseSAT Journals
Abstract Durability of reinforced concrete with respect to corrosion of reinforcement is one of the major aspects to be considered in the management of civil infrastructure systems. An accelerated laboratory test method developed at SERC where the concrete specimen containing rebar is subjected to polarization under a constant voltage in a sodium chloride solution. It is found that the current response with time follows that of a typical service life model indicating depassivation and corrosion propagation. Index terms- Materials, cement, super plasticizer, workability, compressive strength etc.
Corrosion resistance performance of fly ash blended cement concreteseSAT Publishing House
1) The document describes an experimental study on the corrosion resistance of reinforced concrete with different percentages of fly ash replacement.
2) An accelerated corrosion test method was used where concrete cylinders containing rebar were subjected to polarization in a sodium chloride solution. This simulated rebar corrosion in marine environments.
3) The test results showed that concretes with 30% fly ash replacement had the highest corrosion resistance, with initiation times of 54 and 63 days for M25 and M30 grade concrete, respectively.
4) Graphs of current over time showed changes in slope indicating the initiation time and time for cracking, which increased with higher percentages of fly ash replacement up to 30%.
This document summarizes a research study on the effect of using electrically precipitated fly ash (EPFA) as a partial replacement for cement in self-compacting concrete (SCC). The study tested SCC mixes with 0-30% EPFA replacement at 5% intervals. Tests were conducted on fresh properties, mechanical properties like compressive strength, and durability properties like rapid chloride permeability and water sorptivity. Results showed that 20% EPFA replacement provided better results than the control SCC mix, improving properties while also providing economic and environmental benefits through reduced cement usage.
This document summarizes a review on the properties of high-performance concrete. It discusses that high-performance concrete incorporates supplementary cementitious materials like fly ash and silica fume to improve strength and durability compared to regular concrete. It describes various supplementary materials used in high-performance concrete like silica fume, alccofine, metakaolin, rice husk ash, and bamboo leaf ash and how they improve properties. It also discusses the effects of aggregates, fibers, and other ingredients on high-performance concrete characteristics. The purpose is to provide information on developing high-performance concrete mixtures with optimized properties.
Design of High Compressive Strength Concrete Mix without AdditivesIJERA Editor
In this paper, the crashed Basalt and uncrushed granite is used in concrete mixes as coarse aggregate. The selected materials, with high specification using special production techniques, the properties ,the mix design procedure and mix proportion of the high strength concrete (HSC) were discussed. Different proportions of Ordinary Portland cement (410,430 and 450) kg/m3 with different crashed Basalt and uncrushed Granite coarse aggregate amount (1120 and 1050) kg/m3 and fine aggregate with fine modulus of 3.65 were used. Eight concrete mixes were prepared: two as control mix for crashed Basalt and uncrushed Granite, three with crashed Basalt and three with uncrushed Granite coarse aggregate with mix amount(410:680:1120,430:610:1050 and 450:550:1050) kg/m3,(cement: fine aggregate: coarse aggregate)respectively. The study showed that the use of granite coarse aggregate in concrete mixes has a clear effect in mix proportion. The compressive strength of concrete was measured at ages of 7, 28 and 56 days and it was found that the granite (Mix3) of (450:550:1050) kg/m3 with w/c of 0.46 give the highest of strength in 28 and 56 days among the abovementioned mixes its 56 and 64 N/mm2 respectively. The paper shows that good results of compressive strength and workability of concrete were obtained when using granite coarse aggregate.
This document summarizes a study that assessed the fresh and hardened properties of self-consolidating concrete (SCC) containing steel, polypropylene, and hybrid fibers at various high temperatures. Four SCC mixtures were tested: a control without fibers, one with 1% polypropylene fibers, one with 1% steel fibers, and one with 0.5% of each steel and polypropylene fibers. All mixtures met standards for workability and passing ability. The inclusion of fibers slightly reduced workability. Mechanical properties generally increased with temperature up to 200°C then decreased at higher temperatures. Fiber-reinforced SCC exhibited improved spalling resistance compared to plain SCC.
This document reviews the development and use of supplementary cementitious materials (SCMs) in self-compacting concrete (SCC). It summarizes past literature on how various calcium-rich and silica-rich SCMs have been used to improve the properties of SCC. The review focuses on the effects of ultra-fine fly ash (UFFA) on the plastic and hardened properties of SCC. It notes that prior studies have examined the use of SCMs like fly ash, slag, and silica fume to enhance workability and strength but that no comprehensive study has looked at the impact of UFFA specifically. The review proposes that future work should examine how UFFA influences SCC properties using an artificial
This document evaluates the strength parameters of self-compacting concrete incorporated with carbon and glass fibres. It discusses how the concrete was made with various percentages of micro silica and fibres as a replacement for cement. The compressive, tensile, and flexural strength of the concrete mixtures were tested at 7 and 28 days. The results showed that the concrete achieved the highest strength at 0.6% addition of carbon or glass fibres, with carbon fibres performing slightly better. In conclusion, the compressive strength increased by 12% for carbon fibre and 8% for glass fibre mixtures at the 0.6% fibre level.
This document discusses the effect of rheological active additives on the properties of self-compacting concrete. Stone powders from local mountain rocks were used to increase the rheological matrix and fluidity of self-compacting concrete mixtures. Plasticizers were used to regulate the properties of cement-based mixtures. The flow rate of cement suspensions and spread of mortars and concretes were evaluated with different testing methods. Results showed that limestone powder was more effective than other stone powders at improving compressive strength when added at 40% to concrete mixtures. The optimal quantities of rheological additives and plasticizers were identified to produce high-strength self-compacting concrete.
This document is the proceedings of the 2nd International Professional Doctorate and Postgraduate Symposium held at Universiti Teknologi Malaysia on September 25, 2021. It contains abstracts from various papers presented at the symposium covering topics such as machine learning, architecture, occupational health and safety, education, supply chain management, and more. The proceedings were organized by the School of Graduate Studies and Postgraduate Student Society of Universiti Teknologi Malaysia.
This study investigates the synergistic effects of combining fly ash and silica fume to produce high-strength self-compacting cementitious composites. Seven mixtures were prepared with varying amounts of fly ash (17.5-25%) and silica fume (1.25-7.5%) as a replacement for ordinary portland cement. The mixtures were tested for rheological properties in the fresh state and mechanical properties like compressive strength and ultrasonic pulse velocity in the hardened state. The results showed that a combination of 80% fly ash and 20% silica fume produced the highest flowability. For superior mechanical properties, the optimum mixture contained 80% cement, 17.5% fly ash and 2
View of Synergetic Effect of Met kaolin for Developing Fast Setting Early Str...Muthumari Ganesan
The document discusses the benefits of exercise for mental health. Regular physical activity can help reduce anxiety and depression and improve mood and cognitive functioning. Exercise causes chemical changes in the brain that may help protect against mental illness and improve symptoms.
The document discusses the use of copper slag as a supplementary cementitious material in high strength self-compacting concrete. Twelve concrete mixes were prepared with 0-20% fly ash replacement of cement and 10-100% copper slag replacement of fine aggregate. The fresh and mechanical properties of the mixes were evaluated up to 180 days. The results showed that workability improved with increasing copper slag content due to its glassy texture. The 40% copper slag mix achieved the maximum compressive strength. Copper slag also reduced chloride penetration and improved concrete quality according to tests. However, sulfate immersion increased weight but reduced strength over time. Overall, the study found that copper slag can be used as a sustainable material to develop high performance self-
The document summarizes research into developing sustainable high-performance self-compacting concrete using ladle slag as a cement replacement. Ladle slag, a steel industry waste material, was used to replace cement at levels of 5%, 10%, 15% and 25% in self-compacting concrete mixtures. The fresh properties, mechanical properties such as compressive and splitting tensile strength, and simple durability properties of the mixtures were evaluated based on standard tests and compared to a control mixture without ladle slag. The results generally showed improvements in properties for replacements up to 15% ladle slag compared to the control mixture. The research aims to evaluate the performance of ladle slag as a supplementary cementitious material in producing sustainable high-performance
This document discusses a research study on developing high-strength self-compacting concrete using supplementary cementitious materials. The study aims to produce self-compacting concrete with high compressive strength using silica fume and fly ash as partial replacements for cement. The laboratory tests evaluated the fresh and hardened properties of self-compacting concrete mixes with binary and ternary combinations of silica fume and fly ash at different replacement levels. The results showed that both the fresh and hardened properties depended on the use of supplementary cementitious materials. Compressive, split tensile and flexural strengths significantly increased for mixes containing supplementary cementitious materials. The optimum replacement levels for high strength self-compacting concrete were found to be 10%
বাংলাদেশের অর্থনৈতিক সমীক্ষা ২০২৪ [Bangladesh Economic Review 2024 Bangla.pdf] কম্পিউটার , ট্যাব ও স্মার্ট ফোন ভার্সন সহ সম্পূর্ণ বাংলা ই-বুক বা pdf বই " সুচিপত্র ...বুকমার্ক মেনু 🔖 ও হাইপার লিংক মেনু 📝👆 যুক্ত ..
আমাদের সবার জন্য খুব খুব গুরুত্বপূর্ণ একটি বই ..বিসিএস, ব্যাংক, ইউনিভার্সিটি ভর্তি ও যে কোন প্রতিযোগিতা মূলক পরীক্ষার জন্য এর খুব ইম্পরট্যান্ট একটি বিষয় ...তাছাড়া বাংলাদেশের সাম্প্রতিক যে কোন ডাটা বা তথ্য এই বইতে পাবেন ...
তাই একজন নাগরিক হিসাবে এই তথ্য গুলো আপনার জানা প্রয়োজন ...।
বিসিএস ও ব্যাংক এর লিখিত পরীক্ষা ...+এছাড়া মাধ্যমিক ও উচ্চমাধ্যমিকের স্টুডেন্টদের জন্য অনেক কাজে আসবে ...
The simplified electron and muon model, Oscillating Spacetime: The Foundation...RitikBhardwaj56
Discover the Simplified Electron and Muon Model: A New Wave-Based Approach to Understanding Particles delves into a groundbreaking theory that presents electrons and muons as rotating soliton waves within oscillating spacetime. Geared towards students, researchers, and science buffs, this book breaks down complex ideas into simple explanations. It covers topics such as electron waves, temporal dynamics, and the implications of this model on particle physics. With clear illustrations and easy-to-follow explanations, readers will gain a new outlook on the universe's fundamental nature.
Macroeconomics- Movie Location
This will be used as part of your Personal Professional Portfolio once graded.
Objective:
Prepare a presentation or a paper using research, basic comparative analysis, data organization and application of economic information. You will make an informed assessment of an economic climate outside of the United States to accomplish an entertainment industry objective.
Physiology and chemistry of skin and pigmentation, hairs, scalp, lips and nail, Cleansing cream, Lotions, Face powders, Face packs, Lipsticks, Bath products, soaps and baby product,
Preparation and standardization of the following : Tonic, Bleaches, Dentifrices and Mouth washes & Tooth Pastes, Cosmetics for Nails.
A Strategic Approach: GenAI in EducationPeter Windle
Artificial Intelligence (AI) technologies such as Generative AI, Image Generators and Large Language Models have had a dramatic impact on teaching, learning and assessment over the past 18 months. The most immediate threat AI posed was to Academic Integrity with Higher Education Institutes (HEIs) focusing their efforts on combating the use of GenAI in assessment. Guidelines were developed for staff and students, policies put in place too. Innovative educators have forged paths in the use of Generative AI for teaching, learning and assessments leading to pockets of transformation springing up across HEIs, often with little or no top-down guidance, support or direction.
This Gasta posits a strategic approach to integrating AI into HEIs to prepare staff, students and the curriculum for an evolving world and workplace. We will highlight the advantages of working with these technologies beyond the realm of teaching, learning and assessment by considering prompt engineering skills, industry impact, curriculum changes, and the need for staff upskilling. In contrast, not engaging strategically with Generative AI poses risks, including falling behind peers, missed opportunities and failing to ensure our graduates remain employable. The rapid evolution of AI technologies necessitates a proactive and strategic approach if we are to remain relevant.
A workshop hosted by the South African Journal of Science aimed at postgraduate students and early career researchers with little or no experience in writing and publishing journal articles.
Thinking of getting a dog? Be aware that breeds like Pit Bulls, Rottweilers, and German Shepherds can be loyal and dangerous. Proper training and socialization are crucial to preventing aggressive behaviors. Ensure safety by understanding their needs and always supervising interactions. Stay safe, and enjoy your furry friends!
Executive Directors Chat Leveraging AI for Diversity, Equity, and InclusionTechSoup
Let’s explore the intersection of technology and equity in the final session of our DEI series. Discover how AI tools, like ChatGPT, can be used to support and enhance your nonprofit's DEI initiatives. Participants will gain insights into practical AI applications and get tips for leveraging technology to advance their DEI goals.
Main Java[All of the Base Concepts}.docxadhitya5119
This is part 1 of my Java Learning Journey. This Contains Custom methods, classes, constructors, packages, multithreading , try- catch block, finally block and more.
2. Materials 2022, 15, 2222 2 of 24
Compared to normal vibrated concrete, self-compacting concrete (SCC) contains
a much higher amount/volume of fine particles (≤0.125 mm) needed to achieve mix
stability or cohesion. A high percentage of fine particles in SCC is usually achieved by
using mineral additives (pozzolanic and non-pozzolanic) such as fly ash, slag, silica fume,
limestone, metakaolin, etc., since the use of cement alone as fines results in high production
costs [7–9]. While the addition of mineral additives usually results in high quality and dense
microstructure, which has a positive effect on mechanical properties and durability, this
compact microstructure results in adverse effects in the concrete at elevated temperatures,
as permeability is reduced so that moisture cannot escape as easily, and high stresses are
generated [10–12].
Extensive research has been carried out to study the effects of the different mineral
additives on the mechanical properties of normal and high strength mortar and concrete
at and after high temperature exposure [3,13]. In recent years, some studies have been
conducted on the effect of different mineral additives, both pozzolanic [14–16] and non-
pozzolanic [17,18], on the residual properties of SCC. Although fly ash is known to have
a positive effect on the residual properties of normal concrete [19], contradictory results
have been obtained in the available literature for the use of fly ash in SCC. Abed et al. [14]
replaced cement mass by fly ash in amounts of 15% and 30% and concluded that the
optimum amount of fly ash that does not affect the 15% fire resistance of concrete for
temperatures up to 800 ◦C. Anand et al. [20] obtained significantly lower residual strengths
of SCC with fly ash after heating to 900 ◦C and attributed this to the extremely high
fly ash content (40% per cement mass). Uysal and Tanyildizi [21] studied the effects of
various mineral additive after heating to 800 ◦C, including fly ash up to 35% of the cement
replacement and limestone filler up to 30% on the residual compressive strength at the age
of 56 days. The results showed a decrease in compressive strength of up to 20% and 24%
for fly ash and limestone filler, respectively, compared to the control mix.
Data on the residual properties of SCC containing metakaolin are scarce in the available
literature. Anand et al. [22] tested SCC with the addition of silica fume, fly ash and
metakaolin heated to 900 ◦C and cooled with air or water. They found that mixes with
metakaolin exhibited the densest structure and, consequently, the highest strength reduction
of up to 73% when cooled in air. In contrast, Abdelmelek et al. [23] studied the effect of high
temperature up to 800 ◦C on high strength concrete (HSC) in which cement was replaced
with 6 and 9% metakaolin. Among the tested concretes, the concrete mix with higher
metakaolin content showed the best behavior in terms of residual compressive strength.
Although SCC has been used in practice for more than 30 years [24], a literature
review has shown that only limited and conflicting data are available on the effect of high
temperatures on high strength SCC concretes with different mineral additives. Therefore,
the main objective of this work is to contribute to a better understanding on the effect of
different mineral additives on the compressive behaviour of SCC after high temperature
exposure. For this purpose, 10 mixes, i.e., one reference and nine mixes divided into
three groups, depending on mineral additive used, were prepared and tested: metakaolin
(5–15% by cement weight), fly ash (10–30% by cement weight) and limestone (5–15% by
cement weight). Microstructural analysis, stress–strain relationships, compressive strength,
modulus of elasticity and strain at peak stress were tested at room temperature and after
high temperature exposure. To exclude the influence of aggregate decomposition on the
residual properties, a Thermogravimetry/Differential Thermal Analysis (TG/DTA) of the
dolomite aggregate was performed to determine the decomposition temperature. Based
on the results of TG/DTA, a temperature range up to 600 ◦C was chosen. This paper
summarizes the findings of the tests performed.
2. Materials and Methods
2.1. Constituent Materials
The constituent materials for concrete production included the following:
3. Materials 2022, 15, 2222 3 of 24
1. Binder materials:
– Portland cement CEM I 42.5R according to EN 197-1 [25] and dolomite powder
were used in all mixes. The compressive strength of cement, tested according to
the standard EN 196-1 [26], was 61 MPa after 28 days.
– Mineral additives used (metakaolin, fly ash and limestone) are available on the
Croatian market. Table 1 summarizes the properties of the Portland cement and
mineral additives used in the studied mixes, while Figure 1a shows the particle
size distribution obtained by the laser diffraction method.
2. Natural, crushed dolomite aggregate (0/4, 4/8 and 8/16 mm) with a particle size
distribution is shown in Figure 1b.
3. A superplasticizer based on modified polycarboxylic ether polymers, with a rela-
tive density of 1100 kg/m3, and a viscosity modifying agent (VMA) based on high-
molecular weight synthetic copolymer with a relative density of 1009 kg/m3, were
added during concrete production to set the workability of the tested mixes.
4. Tap water was obtained from the general municipal drinking-water supply, which
contained a negligible amount of chloride substances.
Materials 2022, 15, x FOR PEER REVIEW 4 of 26
(a) (b)
Figure 1. Granulometry of the (a) binder materials and dolomite filer, (b) aggregate.
The dolomite aggregates and the dolomite powder used in the concrete mixes came
from the same quarry. TG/DTA analyses were performed on the dolomite aggregate to
determine the temperature at which the decomposition of the dolomite occurs. The results
of the analysis, presented in Figure 2, showed that their decomposition started at a tem-
perature of 762.8 °C. After 864.5 °C, the dolomite’s mass decreased by more than 47%.
Figure 1. Granulometry of the (a) binder materials and dolomite filer, (b) aggregate.
Table 1. Properties of binder materials.
Property/Components Portland Cement
Dolomite
Filler
Metakaolin Fly Ash Limestone
Chemical analysis, %
CaO 60.23 30.38 0.55 4.21 54.05
SiO2 19.81 0.00 53.53 51.87 0.66
Fe2O3 2.71 0.18 1.17 9.22 0.12
Al2O3 5.38 0.31 41.18 24.46 0.15
MgO 2.87 21.84 0.36 1.83 1.01
Na2O 0.8 0.05 0.08 0.23 0.08
K2O 0.77 0.02 0.83 1.14 0.02
SO3 3.07 0.05 0.08 0.56 0.09
Loss of ignition, LOI 4.47 47.58 1.36 0.54 43.87
Physical properties
Specific gravity, g/cm3 3.05 2.86 2.68 2.34 2.63
Blaine fineness, cm2/g 3290 1630 10,260 3070 8948
4. Materials 2022, 15, 2222 4 of 24
The dolomite aggregates and the dolomite powder used in the concrete mixes came
from the same quarry. TG/DTA analyses were performed on the dolomite aggregate
to determine the temperature at which the decomposition of the dolomite occurs. The
results of the analysis, presented in Figure 2, showed that their decomposition started at a
temperature of 762.8 ◦C. After 864.5 ◦C, the dolomite’s mass decreased by more than 47%.
Figure 1. Granulometry of the (a) binder materials and dolomite filer, (b) aggregate
The dolomite aggregates and the dolomite powder used in the concre
from the same quarry. TG/DTA analyses were performed on the dolomite
determine the temperature at which the decomposition of the dolomite occu
of the analysis, presented in Figure 2, showed that their decomposition sta
perature of 762.8 °C. After 864.5 °C, the dolomite’s mass decreased by more
Figure 2. TG/DTA graph of dolomite aggregates.
2.2. Concrete Mix Design and Specimen Dimensions
The details of the studied concrete mixes are provided in Table 2. CEM
used as the binder in the reference mix, M2. In the other nine mixes, M3–M1
additives, metakaolin (MK), fly ash (FA) and limestone filler (LF) were u
replacement for cement by weight. All concrete mixes were designed to ac
flow of 700 ± 50 mm. Other fresh concrete properties required for SCC m
tested to ensure good flowability, workability and segregation resistance
mixes and are also listed in Table 2. All mixes met the requirements for SCC
EFNARC [27] and EN 206-9 [28].
Figure 2. TG/DTA graph of dolomite aggregates.
2.2. Concrete Mix Design and Specimen Dimensions
The details of the studied concrete mixes are provided in Table 2. CEM I 42.5 R was
used as the binder in the reference mix, M2. In the other nine mixes, M3–M11, the mineral
additives, metakaolin (MK), fly ash (FA) and limestone filler (LF) were used as partial
replacement for cement by weight. All concrete mixes were designed to achieve a slump
flow of 700 ± 50 mm. Other fresh concrete properties required for SCC mixes were also
tested to ensure good flowability, workability and segregation resistance of the tested
mixes and are also listed in Table 2. All mixes met the requirements for SCC according to
EFNARC [27] and EN 206-9 [28].
An analysis of the fresh properties of the tested mixes can be found in Jelcic
Rukavina et al. [29]. All concrete specimens intended for testing were cast without com-
paction and vibration. After casting, the specimens were kept covered in the laboratory
for 24 h until demolding to prevent the evaporation of water. Then, the specimens were
placed in a curing chamber at 20 ± 2 ◦C and RH ≥ 95% for the next 27 days. After 28 days
of curing, the specimens were kept in the laboratory (T = 15–25 ◦C; RH = 50–70%) until
the age of one year, when heating and subsequent testing took place. In order to study the
effects of high temperatures on the change in mechanical properties of SCC, the cylinders
with dimensions Ø/L = 75/225 mm (i.e., with the required slenderness of 3) were prepared
according to the recommendations of RILEM TC 200 HTC [30,31].
5. Materials 2022, 15, 2222 5 of 24
Table 2. Mix design and properties of studied SCC mixes.
Metakaolin Fly Ash Limestone
Mix ID M2
M3
(MK5)
M4
(MK10)
M5
(MK15)
M6
(FA20)
M7
(FA30)
M8
(FA40)
M9
(LF5)
M10
(LF10)
M11
(LF15)
Cement, kg 450 427.5 405 382.5 360 315 270 427.5 405 382.5
MK
% c.w. - 5 10 15 - - - - - -
kg - 22.5 45 67.5 - - - - - -
FA
% c.w. - - - - 20 30 40 - - -
kg - - - - 90 135 180 - - -
LF
% c.w. - - - - - - - 5 10 15
kg - - - - - - - 22.5 45 67.5
Dolomite filer, kg 220
Water, L 180
v/c 0.40 0.42 0.44 0.47 0.50 0.57 0.67 0.42 0.44 0.47
Fine aggregate, kg 862 862 862 862 862 862 862 862 862 862
Coarse aggregate, kg 696 696 696 696 696 696 696 696 696 696
Superplasticizer, L 5.6 4.5 5.2 6.3 4.1 3.6 3.4 5.0 4.1 3.9
WMA, L 0.7 1.0
Fresh concrete properties
Density in fresh state,
kg/m3 2499 2485 2482 2488 2462 2438 2419 2489 2486 2480
Air content, % 1.9 2.1 2.4 2.1 2.3 2.0 2.3 2.1 2.2 2.2
Slump flow 732 720 725 727 720 723 725 720 718 717
Slump flow time (t500), s 2.08 2.35 2.19 2.10 1.66 1.47 1.40 1.38 1.49 1.65
L-box (h2/h1), - 0.94 0.93 0.82 0.82 0.84 0.87 0.92 0.94 0.91 0.85
Segregation resistance 5 8 10 10 5 5 8 7 4 3
2.3. Heat Treatment
Heat treatment was also performed according to the recommendations of RILEM TC
200 HTC [30,31]. The specimens of all mixes were exposed to three different temperature
cycles with target temperatures of 200 ◦C, 400◦ C and 600 ◦C in an electric furnace (capable
of heating up to 1350 ◦C), while the specimens of reference mix, M2, were exposed to an
additional cycle with a target temperature of 800 ◦C to investigate the effect of dolomite
(aggregate and filler) decomposition on the mechanical properties of the tested mix.
Each temperature cycle consisted of 3 stages (Figure 3a):
5. First stage: heating at a rate ∆T/∆t of 2 ◦C/min (in the furnace) up to the target temperature;
6. Second stage: keeping the target temperature constant until steady-state thermal
conditions throughout the specimens were ensured, ∆t;
7. Third stage: slow natural cooling to ambient temperature in a closed furnace to avoid
thermal shock.
Materials 2022, 15, x FOR PEER REVIEW 6 of 26
6. Second stage: keeping the target temperature constant until steady-state thermal con-
ditions throughout the specimens were ensured, Δt;
7. Third stage: slow natural cooling to ambient temperature in a closed furnace to avoid
thermal shock.
Temperature distribution in the specimens was monitored with 4 Ni-Cr thermocou-
ples embedded in one specimen during each temperature cycle: three on the specimen
surface at mid-height with equal spacing and one in the centre, all embedded during cast-
ing, Figure 3b, as proposed by recommendations of RILEM TC 200 HTC [31]. To achieve
steady-state thermal conditions through the specimens, a preliminary analysis of the heat-
ing regimes was performed, and the time of the second stage (Δt) was determined for each
target temperature. Figure A1 in Appendix A shows the monitored temperatures
achieved through specimens for mix M11. A very similar temperature development was
observed in the specimens from other mixes.
After cooling, the specimens were stored under standard laboratory conditions until
testing, which occurred 7 days after cooling to ambient temperature, when the lowest val-
ues of residual mechanical properties were expected [32].
(a) (b)
Figure 3. (a) Schematic representation of temperature cycle; (b) position of NiCr thermocouples in
the specimens.
The reference mix was heated to 800 °C to evaluate the effect of dolomite decompo-
sition on post-cooling behaviour. In accordance with the TG/TDA analysis shown in Fig-
ure 2, the decomposition of the dolomite occurred at 763 °C. After cooling to room tem-
perature, the specimens, although exhibiting a high degree of cracking, remained “in one
Figure 3. (a) Schematic representation of temperature cycle; (b) position of NiCr thermocouples in
the specimens.
6. Materials 2022, 15, 2222 6 of 24
Temperature distribution in the specimens was monitored with 4 Ni-Cr thermocouples
embedded in one specimen during each temperature cycle: three on the specimen surface
at mid-height with equal spacing and one in the centre, all embedded during casting,
Figure 3b, as proposed by recommendations of RILEM TC 200 HTC [31]. To achieve steady-
state thermal conditions through the specimens, a preliminary analysis of the heating
regimes was performed, and the time of the second stage (∆t) was determined for each
target temperature. Figure A1 in Appendix A shows the monitored temperatures achieved
through specimens for mix M11. A very similar temperature development was observed in
the specimens from other mixes.
After cooling, the specimens were stored under standard laboratory conditions until
testing, which occurred 7 days after cooling to ambient temperature, when the lowest
values of residual mechanical properties were expected [32].
The reference mix was heated to 800 ◦C to evaluate the effect of dolomite decomposi-
tion on post-cooling behaviour. In accordance with the TG/TDA analysis shown in Figure 2,
the decomposition of the dolomite occurred at 763 ◦C. After cooling to room temperature,
the specimens, although exhibiting a high degree of cracking, remained “in one piece”
(see Figure A2 in Appendix B). However, the extent of damage that developed within the
next 7 days prevented further testing. According to Liu et al. [33], this type of degradation
can be regarded as post-cooling spalling after exposure to very high temperatures. Upon
heating, lime, (CaO), is formed from the dehydration of portlandite, (Ca(OH)2), from
cement matrix at temperatures between 400 and 600 ◦C or, in this case, from the thermal
decomposition of the dolomite aggregate and dolomite filler at a temperature of 763 ◦C.
After the specimens cooled, moisture from the air was absorbed by the heated concrete
and gradually penetrated deep into the exposed specimens. The absorbed moisture caused
the rehydration of the lime, which was accompanied by a volume increase of 44% [34],
resulting in severe cracking and falling of parts of the concrete specimens. Therefore, a
maximum temperature of 600 ◦C was chosen to study the influence of binders on the
properties after cooling.
2.4. Microstructural Analysis
The morphology and microstructure before and after heat treatments of the specimens
were analyzed with an electron scanning microscope (SEM, JEOL Ltd., Tokyo, Japan),
type JEOL 5500 LV, connected to a spectrometer-Oxford energy dispersion spectrometer
(EDS, Oxford Instruments NanoAnalysis Asylum Research, High Wycombe, UK), using
backscattered electrons and low vacuum. The parameters for the microscopic analyses
were as follows: acceleration of 20 kV, working distance of 18–22 mm and working pressure
of 17–28 Pa. The specimens were cut out from the central part of the specimen at a
height of 5 cm. The specimens were further sawed to 1 cm and polished in the transverse
direction. After sawing, the specimens were stored in isopropanol until analysis. The
analysis was conducted on specimens taken from the reference mix and on one mix per
group of mineral additives.
2.5. Compressive Stress–Strain Behaviour
The uniaxial compression tests were performed using a universal testing machine
with a capacity of 3000 kN (Figure 4). The tests were performed at a constant displacement
rate of 0.02 ‰/s. To monitor deformations during the test, LVDT gauges (Spring d.o.o.,
Zagreb, Croatia) with a measuring length of 10 cm were attached to the central part of
the specimens. Data acquisition was performed using HBM’s MGCplus data acquisition
system (MGCplus, Hottinger Brüel Kjaer GmbH, Darmstadt, Germany). The Catman
computer programme from the same manufacturer was used to process and graphically
display the data. Prior to testing, additional rubber bands were attached to each specimen
to hold the displacement gauges in place after the cracks appeared, since the untreated
specimens and those treated at 200 ◦C sometimes burst explosively when the peak stress
was reached (Figure 5b).
7. Materials 2022, 15, 2222 7 of 24
tem (MGCplus, Hottinger Brüel Kjaer GmbH, Darmstadt, Germany). The Catman co
puter programme from the same manufacturer was used to process and graphically d
play the data. Prior to testing, additional rubber bands were attached to each specimen
hold the displacement gauges in place after the cracks appeared, since the untreated sp
imens and those treated at 200 °C sometimes burst explosively when the peak stress w
reached (Figure 5b).
Figure 4. Experimental setup—test machine and electronic equipment for compressive stress–st
monitoring.
Figure 4. Experimental setup—test machine and electronic equipment for compressive stress–
strain monitoring.
Materials 2022, 15, x FOR PEER REVIEW 8 of 26
(a) (b)
Figure 5. Appearance of the tested specimens (a) prior and (b) after mechanical loading.
Three specimens of each concrete mix were tested per target temperature. Unheated
specimens were also tested to determine the effect of heating temperature on the studied
properties. The compressive strength, fc, corresponded to the peak stress (σmax) reached in
the material during the test. The modulus of elasticity was calculated from the obtained
stress–strain curves in the range from 10% to 1/3 of the peak stress.
3. Results
3.1. Spalling Occurrence during Heating
Although the present study referred to concrete with high strength and dense micro-
structure, of all the specimens that were subjected to thermal treatment, explosive spalling
occurred only in two specimens during heating to 400 °C (Figure 6a) and 600 °C, (Figure
6b), respectively. The fact that explosive spalling did not occur in the other specimens can
be explained by the low moisture content, since the test was performed when the speci-
mens were already more than a year old. In addition, residual moisture in the specimens
had the possibility to evaporate not only due to the relatively small specimen dimensions
but also due to the slow increase in furnace temperature of 2 °C/min. Since explosive spall-
ing is not the subject of the present work, no further analyses of the spalled specimens
were performed.
Figure 5. Appearance of the tested specimens (a) prior and (b) after mechanical loading.
Three specimens of each concrete mix were tested per target temperature. Unheated
specimens were also tested to determine the effect of heating temperature on the studied
properties. The compressive strength, fc, corresponded to the peak stress (σmax) reached in
the material during the test. The modulus of elasticity was calculated from the obtained
stress–strain curves in the range from 10% to 1/3 of the peak stress.
3. Results
3.1. Spalling Occurrence during Heating
Although the present study referred to concrete with high strength and dense mi-
crostructure, of all the specimens that were subjected to thermal treatment, explosive
spalling occurred only in two specimens during heating to 400 ◦C (Figure 6a) and
600 ◦C, (Figure 6b), respectively. The fact that explosive spalling did not occur in the
other specimens can be explained by the low moisture content, since the test was per-
formed when the specimens were already more than a year old. In addition, residual
moisture in the specimens had the possibility to evaporate not only due to the relatively
small specimen dimensions but also due to the slow increase in furnace temperature of
8. Materials 2022, 15, 2222 8 of 24
2 ◦C/min. Since explosive spalling is not the subject of the present work, no further
analyses of the spalled specimens were performed.
erials 2022, 15, x FOR PEER REVIEW 9 of
(a) (b)
Figure 6. Specimens in the furnace that explosively spalled during heating to (a) 400 °C; (b) 600 °
3.2. Microstructural Analysis
In heated concrete, the cement matrix expands slightly at temperatures between
°C and 100 °C, followed by significant shrinkage at higher temperatures. In contrast, t
aggregate expands and forms large differential thermal stresses that can result in seve
microcracking in the interfacial transition zone (ITZ) [32,34]. Since ITZ is considered
the weakest part of concrete and each mineral additive used has a different effect on
density, Figure 7 shows SEM images of the ITZ from one specimen of each group analyz
for temperatures of 20 °C, 400 °C and 600 °C.
The analysis of the microstructure of the unheated specimens (20 °C) showed that t
ITZ of each specimen can be related to the particle size of a particular mineral additive
the mix, given as Blaine fineness in Table 1. The largest Blaine fineness of the particles
MK (10260 cm2/g) compared to other the binders used (8948 and 3290 cm2/g for LF an
FA, respectively) resulted in the densest ITZ. This dense interface in the MK specim
resulted in more severe damage compared to specimens with FA and LF after temperatu
treatment at 400 °C. In addition to a wide crack in the ITZ, two cracks in the cement matr
can also be observed in the MK specimen. The specimen with FA, on the other han
showed no visible cracks after treatment at 400 °C. After 600 °C, all specimens showed
similar appearance, with cracks appearing in both the cement matrix and the aggregate
20 °C 400 °C 600 °C
reference
mix
Figure 6. Specimens in the furnace that explosively spalled during heating to (a) 400 ◦C; (b) 600 ◦C.
3.2. Microstructural Analysis
In heated concrete, the cement matrix expands slightly at temperatures between
80 ◦C and 100 ◦C, followed by significant shrinkage at higher temperatures. In contrast,
the aggregate expands and forms large differential thermal stresses that can result in severe
microcracking in the interfacial transition zone (ITZ) [32,34]. Since ITZ is considered as
the weakest part of concrete and each mineral additive used has a different effect on its
density, Figure 7 shows SEM images of the ITZ from one specimen of each group analyzed
for temperatures of 20 ◦C, 400 ◦C and 600 ◦C.
The analysis of the microstructure of the unheated specimens (20 ◦C) showed that the
ITZ of each specimen can be related to the particle size of a particular mineral additive
in the mix, given as Blaine fineness in Table 1. The largest Blaine fineness of the particles
of MK (10,260 cm2/g) compared to other the binders used (8948 and 3290 cm2/g for LF
and FA, respectively) resulted in the densest ITZ. This dense interface in the MK specimen
resulted in more severe damage compared to specimens with FA and LF after temperature
treatment at 400 ◦C. In addition to a wide crack in the ITZ, two cracks in the cement matrix
can also be observed in the MK specimen. The specimen with FA, on the other hand,
showed no visible cracks after treatment at 400 ◦C. After 600 ◦C, all specimens showed a
similar appearance, with cracks appearing in both the cement matrix and the aggregate.
Materials 2022, 15, x FOR PEER REVIEW 9 of 26
(a) (b)
Figure 6. Specimens in the furnace that explosively spalled during heating to (a) 400 °C; (b) 600 °C.
3.2. Microstructural Analysis
In heated concrete, the cement matrix expands slightly at temperatures between 80
°C and 100 °C, followed by significant shrinkage at higher temperatures. In contrast, the
aggregate expands and forms large differential thermal stresses that can result in severe
microcracking in the interfacial transition zone (ITZ) [32,34]. Since ITZ is considered as
the weakest part of concrete and each mineral additive used has a different effect on its
density, Figure 7 shows SEM images of the ITZ from one specimen of each group analyzed
for temperatures of 20 °C, 400 °C and 600 °C.
The analysis of the microstructure of the unheated specimens (20 °C) showed that the
ITZ of each specimen can be related to the particle size of a particular mineral additive in
the mix, given as Blaine fineness in Table 1. The largest Blaine fineness of the particles of
MK (10260 cm2/g) compared to other the binders used (8948 and 3290 cm2/g for LF and
FA, respectively) resulted in the densest ITZ. This dense interface in the MK specimen
resulted in more severe damage compared to specimens with FA and LF after temperature
treatment at 400 °C. In addition to a wide crack in the ITZ, two cracks in the cement matrix
can also be observed in the MK specimen. The specimen with FA, on the other hand,
showed no visible cracks after treatment at 400 °C. After 600 °C, all specimens showed a
similar appearance, with cracks appearing in both the cement matrix and the aggregate.
20 °C 400 °C 600 °C
(a)
reference
mix
Figure 7. Cont.
9. Materials 2022, 15, 2222 9 of 24
Materials 2022, 15, x FOR PEER REVIEW 10 of 26
(b)
MK
(c)
FA
(d)
LF
Figure 7. SEM images of tested mix at room temperature and after fire exposure to 400 and 600 °C
for (a) reference mix, (b) mix with MK, (c) mix with FA and (d) mix with LF
3.3. Compressive Stress–Strain Relationship
Figure 8 shows normalized stress–strain curves as a function of temperature for each
target temperature. Separate stress–strain curves for each tested specimen are provided
in Figure A3 in Appendix C.
(a)
Figure 7. SEM images of tested mix at room temperature and after fire exposure to 400 and 600 ◦C
for (a) reference mix, (b) mix with MK, (c) mix with FA and (d) mix with LF.
3.3. Compressive Stress–Strain Relationship
Figure 8 shows normalized stress–strain curves as a function of temperature for each
target temperature. Separate stress–strain curves for each tested specimen are provided in
Figure A3 in Appendix C.
b)
MK
c)
FA
d)
LF
Figure 7. SEM images of tested mix at room temperature and after fire exposure to 400 and 600 °C
for (a) reference mix, (b) mix with MK, (c) mix with FA and (d) mix with LF
3.3. Compressive Stress–Strain Relationship
Figure 8 shows normalized stress–strain curves as a function of temperature for each
target temperature. Separate stress–strain curves for each tested specimen are provided
in Figure A3 in Appendix C.
(a)
Figure 8. Cont.
10. Materials 2022, 15, 2222 10 of 24
als 2022, 15, x FOR PEER REVIEW 11 of 26
(b)
(c)
Figure 8. Normalised stress–strain curves for (a) metakaolin based (M3–M5), (b) fly-ash based (M6–
M8) and (c) limestone based (M9–M11) in relation to the reference mixture (M2) as a function of
temperature.
The curves shown include an ascending branch up to the peak stress. The descending
portion of the σ-ε curve was not recorded during the test because the rate of displacement
was controlled by the piston movement of the test machine.
As observed from the curves given in Figure A3 in Appendix C, good reproducibility
of the results was achieved after they were exposed to the respective target temperature.
Due to the more homogeneous microstructure compared to conventional concrete, the
stress–strain curves of the tested concrete are rather linear compared to conventional vi-
brated concrete. In addition, the shape of the curves was strongly influenced by tempera-
ture. As temperature increased, the curve became smoother, with lower maximum stress
and higher deformation at peak stress. This can be applied for all mixes except those with
fly ash after exposure to 200 °C, where the curves of the heated specimens were very close
to those of the unheated ones (Figure 8b).
Comparing the stress–strain curves shown in Figure 8 within each tested group, it
can be observed that the different amounts of FA (mixes M6–M8) and limestone (M9–
M11) in the concrete mixes resulted in similar behaviours, while the mixes with different
MK content (M3–M5) showed larger variations after all target temperatures.
Figure 8. Normalised stress–strain curves for (a) metakaolin based (M3–M5), (b) fly-ash based
(M6–M8) and (c) limestone based (M9–M11) in relation to the reference mixture (M2) as a function
of temperature.
The curves shown include an ascending branch up to the peak stress. The descending
portion of the σ-ε curve was not recorded during the test because the rate of displacement
was controlled by the piston movement of the test machine.
As observed from the curves given in Figure A3 in Appendix C, good reproducibility of
the results was achieved after they were exposed to the respective target temperature. Due
to the more homogeneous microstructure compared to conventional concrete, the stress–
strain curves of the tested concrete are rather linear compared to conventional vibrated
concrete. In addition, the shape of the curves was strongly influenced by temperature. As
temperature increased, the curve became smoother, with lower maximum stress and higher
deformation at peak stress. This can be applied for all mixes except those with fly ash after
exposure to 200 ◦C, where the curves of the heated specimens were very close to those of
the unheated ones (Figure 8b).
Comparing the stress–strain curves shown in Figure 8 within each tested group, it
can be observed that the different amounts of FA (mixes M6–M8) and limestone (M9–M11)
11. Materials 2022, 15, 2222 11 of 24
in the concrete mixes resulted in similar behaviours, while the mixes with different MK
content (M3–M5) showed larger variations after all target temperatures.
As mentioned above, the compressive strength (peak stress), static modulus of elastic-
ity and strain at peak stress were determined from the stress–strain curves and analyzed in
the next sections.
3.4. Peak Stress—Compressive Strength
Figure 9 shows the peak stress or compressive strength, of unheated SCC specimens
(20 ◦C) and specimens heated to all target temperatures (200 ◦C, 400◦C and 600 ◦C). The
initial compressive strength ranged from 71.8 MPa for M2 to 96.5 MPa for M5, i.e., the
difference is up to 34%.
Materials 2022, 15, x FOR PEER REVIEW 12 of 26
3.4. Peak Stress—Compressive Strength
Figure 9 shows the peak stress or compressive strength, of unheated SCC specimens
(20 °C) and specimens heated to all target temperatures (200°C, 400°C and 600 °C). The
initial compressive strength ranged from 71.8 MPa for M2 to 96.5 MPa for M5, i.e., the
difference is up to 34%.
Figure 9. Compressive strength vs. temperature of tested mixes.
It can be observed from the figure that all the mineral additives used (both pozzolanic
and non-pozzolanic) had a positive effect on the compressive strength of the unheated
specimens. The highest values after one year of curing were obtained for SCC concrete
mixes in which cement was replaced by metakaolin (mixes M3–M5). Compared to the
reference mix, the compressive strength of the mixes with MK increased with an increase
in the content of MK up to 34%. The FA mixes increased the compressive strength of the
reference mix by up to 9.3%, and the addition of limestone filler increased it up to 14%.
The positive effect of MK and FA on the development of strength, especially at later ages,
can be attributed to the effect of the filler in combination with the acceleration of cement
hydration and the pozzolanic reaction with calcium hydroxide [35].
To illustrate the effect of high temperatures on the change in compressive strength,
Figure 10 shows the relative values that clearly indicate the influence of the specific min-
eral additive on the residual compressive strength of the tested mixes. The deviations be-
tween all the mixes at the defined target temperatures were up to 24% depending on the
additive used.
Figure 9. Compressive strength vs. temperature of tested mixes.
It can be observed from the figure that all the mineral additives used (both pozzolanic
and non-pozzolanic) had a positive effect on the compressive strength of the unheated
specimens. The highest values after one year of curing were obtained for SCC concrete
mixes in which cement was replaced by metakaolin (mixes M3–M5). Compared to the
reference mix, the compressive strength of the mixes with MK increased with an increase
in the content of MK up to 34%. The FA mixes increased the compressive strength of the
reference mix by up to 9.3%, and the addition of limestone filler increased it up to 14%.
The positive effect of MK and FA on the development of strength, especially at later ages,
can be attributed to the effect of the filler in combination with the acceleration of cement
hydration and the pozzolanic reaction with calcium hydroxide [35].
To illustrate the effect of high temperatures on the change in compressive strength,
Figure 10 shows the relative values that clearly indicate the influence of the specific min-
eral additive on the residual compressive strength of the tested mixes. The deviations
between all the mixes at the defined target temperatures were up to 24% depending on the
additive used.
The negative effect of the addition of MK is evident at all treatment temperatures. The
higher the percentage of MK in the concrete mix, the lower the relative residual compressive
strength. For the M5 mix, the strength loss after a temperature of 200 ◦C, 400 ◦C and 600 ◦C
was about 21%, 51% and 66%, respectively. Compared to the reference mix, the decrease
in compressive strength was higher by 13–15%. As mentioned above, the negative effect
of MK addition on the residual strength is a result of the denser microstructure shown
in Figure 7, especially in ITZ, where pronounced cracks appeared at temperatures after
heating to 400 ◦C. When HSC was tested with 5%, 10% and 20% of MK, Poon at al. [34]
obtained a different pattern, i.e., an increase in concrete strength of 2–8% was observed
after heating to 200 ◦C, while a slight decrease of 5–8% occurred after 400 ◦C, which is
similar to results obtained by Abdelmelek et al. [23] who tested SCC with MK.
12. Materials 2022, 15, 2222 12 of 24
Materials 2022, 15, x FOR PEER REVIEW
Figure 10. Normalized values of compressive strength vs. temperature.
The negative effect of the addition of MK is evident at all treatment temp
The higher the percentage of MK in the concrete mix, the lower the relative resid
pressive strength. For the M5 mix, the strength loss after a temperature of 200 °C
and 600 °C was about 21%, 51% and 66%, respectively. Compared to the refere
the decrease in compressive strength was higher by 13–15%. As mentioned ab
negative effect of MK addition on the residual strength is a result of the dense
structure shown in Figure 7, especially in ITZ, where pronounced cracks appeare
peratures after heating to 400 °C. When HSC was tested with 5%, 10% and 20%
Poon at al. [34] obtained a different pattern, i.e., an increase in concrete strength
was observed after heating to 200 °C, while a slight decrease of 5–8% occurred
°C, which is similar to results obtained by Abdelmelek et al. [23] who tested S
MK.
The replacement of cement with FA in an amount of 20–40% had a positive
the residual compressive strength. After exposure to 200 °C, a slight increase (u
in compressive strength was observed in mixes with FA compared to their stren
°C. In addition, the relative compressive strength of the mixes with FA was 13%
compared to the reference mix. This can be explained by the subsequent hydrati
unhydrated cement particles due to internal steam curing due to the hot steam
internal autoclave condition or the subsequent pozzolanic reaction of fly ash and
hydroxide due to the free movement of moisture in the material due to the high t
ture [36]. In addition, microstructural analysis showed that the ITZ of FA mixes
as dense as that of MK (Figure 7b).
Mixes with limestone (as a non-pozzolanic material) showed comparable be
to the reference mix over the entire temperature range, with variations within 5%
In accordance with Abed et al. [17], the residual compressive strength with in
temperature can be divided into five main stages: (1) room temperature at 50 °C
terized by a moderate decrease in compressive strength due to the loss of free w
150–300 °C, characterized by a constant or slightly increased compressive stren
Figure 10. Normalized values of compressive strength vs. temperature.
The replacement of cement with FA in an amount of 20–40% had a positive effect
on the residual compressive strength. After exposure to 200 ◦C, a slight increase (up to
4%) in compressive strength was observed in mixes with FA compared to their strength
at 20 ◦C. In addition, the relative compressive strength of the mixes with FA was 13%
higher compared to the reference mix. This can be explained by the subsequent hydration
of the unhydrated cement particles due to internal steam curing due to the hot steam
from the internal autoclave condition or the subsequent pozzolanic reaction of fly ash and
calcium hydroxide due to the free movement of moisture in the material due to the high
temperature [36]. In addition, microstructural analysis showed that the ITZ of FA mixes
was not as dense as that of MK (Figure 7b).
Mixes with limestone (as a non-pozzolanic material) showed comparable behaviour
to the reference mix over the entire temperature range, with variations within 5%.
In accordance with Abed et al. [17], the residual compressive strength with increasing
temperature can be divided into five main stages: (1) room temperature at 50 ◦C, char-
acterized by a moderate decrease in compressive strength due to the loss of free water;
(2) 150–300 ◦C, characterized by a constant or slightly increased compressive strength as a
result of C-S-H rehydration; (3) 300–400 ◦C, characterized by an approximately constant or
slightly decreased compressive strength due to the breakup of the chemically bound water;
(4) 400–800 ◦C, characterized by a drastic decrease in compressive strength; (5) 800 ◦C,
characterized by the complete loss of concrete strength. Although different temperature
increments were chosen in this study, the obtained results showed that major strength loss
occurred earlier up to a temperature of 400 ◦C.
The recommended values provided in Eurocodes EC2 [5] and EC4 [6] for the reduction
in concrete compressive strength due to exposure to high temperatures for both normal
strength and high strength concretes are shown in Figure 11 and compared with the results
obtained in this work (gray shadow area in Figure 11).
13. Materials 2022, 15, 2222 13 of 24
concrete. Mixes M3–M11 could be classified in strength class C70/85 or h
to their 1-year strength; thus, it can be observed from Figure 11 that EC2
mate the strength reduction for these mixes at a temperature of 200 °C. M
of metakaolin meets the requirements of strength class C90/105, and it c
Figure 11 that EC2 also overestimates strength reduction due to the high
Figure 11. Normalized values of compressive strength compared to results of oth
and EC 4.
Figure 11 also makes comparisons with studies on high strength
Persson [37] and Bamonte et al. [38]. These studies were chosen since th
of tested concrete mixes are similar, although different aggregate, natu
gravel and crushed gneiss and gravel, respectively, were used, which m
sults. As observed from the figure, their results agree well with the comp
obtained with the mixes with MK.
With the exception of MK, the obtained results after 200 and 600 °C
the results of Uysal et al. [39] but differ after treatment at 400 °C. Any dis
results obtained may be due to different curing and heating durations.
3.5. Modulus of Elasticity
High temperatures have a negative effect on the elastic properties of
due to the decomposition of hydrated cement products and the breakin
microstructure [40]. Figures 12 and 13 show the effects of high temperatu
ual modulus of elasticity of the SCC concretes tested, both in absolute an
Figure 11. Normalized values of compressive strength compared to results of other studies and EC2
and EC 4.
EC2 [5] recognizes that a greater reduction in strength is required for high strength
concrete. Mixes M3–M11 could be classified in strength class C70/85 or higher, according to
their 1-year strength; thus, it can be observed from Figure 11 that EC2 would overestimate
the strength reduction for these mixes at a temperature of 200 ◦C. Mix M5 with 15% of
metakaolin meets the requirements of strength class C90/105, and it can be seen from
Figure 11 that EC2 also overestimates strength reduction due to the high temperature.
Figure 11 also makes comparisons with studies on high strength SCC concrete by
Persson [37] and Bamonte et al. [38]. These studies were chosen since the initial strength of
tested concrete mixes are similar, although different aggregate, natural, round river gravel
and crushed gneiss and gravel, respectively, were used, which may affect the results. As
observed from the figure, their results agree well with the compressive strengths obtained
with the mixes with MK.
With the exception of MK, the obtained results after 200 and 600 ◦C agree well with
the results of Uysal et al. [39] but differ after treatment at 400 ◦C. Any discrepancies in the
results obtained may be due to different curing and heating durations.
3.5. Modulus of Elasticity
High temperatures have a negative effect on the elastic properties of concrete, mainly
due to the decomposition of hydrated cement products and the breaking of bonds in the
microstructure [40]. Figures 12 and 13 show the effects of high temperatures on the residual
modulus of elasticity of the SCC concretes tested, both in absolute and relative values.
14. Materials 2022, 15, 2222 14 of 24
Materials 2022, 15, x FOR PEER REVIEW 15 of 26
Figure 12. Modulus of elasticity vs. temperature of tested mixes.
Figure 13. Relative values of modulus of elasticity with increasing temperature.
The initial values of modulus of elasticity ranged from 45.1 GPa for M8 to 51.7 GPa
for the M2 mix (i.e., the difference is around 14%) and decreased almost linearly with
temperature.
As expected, a greater effect of elevated temperatures was observed on the modulus
of elasticity compared to the compressive strength, but in this case, the differences be-
tween the studied mixes were smaller. The highest difference in relative modulus of elas-
ticity between the studied mixes is 14% after 200 °C and continues to decrease with in-
creasing temperature. After 600 °C, the difference between mixes was 6%.
Considering the different groups of studied mixes, a very similar pattern as for com-
pressive strength was obtained—the lowest relative values after 400 °C and 600 °C were
obtained within MK-based mixes, i.e., the initial modulus of elasticity of M5 mix de-
creased for 75% and 88%, respectively. After 200 °C, the reference mix had negligibly
lower values compared to MK mixes—decrease was around 38%. FA and LF had a bene-
ficial effect on the residual modulus of elasticity compared to reference mix. As with the
compressive strength, there was a strong loss of the modulus of elasticity up to 400 °C in
all tested mixes.
Figure 12. Modulus of elasticity vs. temperature of tested mixes.
Materials 2022, 15, x FOR PEER REVIEW 15 of 26
Figure 12. Modulus of elasticity vs. temperature of tested mixes.
Figure 13. Relative values of modulus of elasticity with increasing temperature.
The initial values of modulus of elasticity ranged from 45.1 GPa for M8 to 51.7 GPa
for the M2 mix (i.e., the difference is around 14%) and decreased almost linearly with
temperature.
As expected, a greater effect of elevated temperatures was observed on the modulus
of elasticity compared to the compressive strength, but in this case, the differences be-
tween the studied mixes were smaller. The highest difference in relative modulus of elas-
ticity between the studied mixes is 14% after 200 °C and continues to decrease with in-
creasing temperature. After 600 °C, the difference between mixes was 6%.
Considering the different groups of studied mixes, a very similar pattern as for com-
pressive strength was obtained—the lowest relative values after 400 °C and 600 °C were
obtained within MK-based mixes, i.e., the initial modulus of elasticity of M5 mix de-
creased for 75% and 88%, respectively. After 200 °C, the reference mix had negligibly
lower values compared to MK mixes—decrease was around 38%. FA and LF had a bene-
ficial effect on the residual modulus of elasticity compared to reference mix. As with the
compressive strength, there was a strong loss of the modulus of elasticity up to 400 °C in
all tested mixes.
Figure 13. Relative values of modulus of elasticity with increasing temperature.
The initial values of modulus of elasticity ranged from 45.1 GPa for M8 to 51.7 GPa for
the M2 mix (i.e., the difference is around 14%) and decreased almost linearly with temperature.
As expected, a greater effect of elevated temperatures was observed on the modulus
of elasticity compared to the compressive strength, but in this case, the differences between
the studied mixes were smaller. The highest difference in relative modulus of elasticity
between the studied mixes is 14% after 200 ◦C and continues to decrease with increasing
temperature. After 600 ◦C, the difference between mixes was 6%.
Considering the different groups of studied mixes, a very similar pattern as for com-
pressive strength was obtained—the lowest relative values after 400 ◦C and 600 ◦C were
obtained within MK-based mixes, i.e., the initial modulus of elasticity of M5 mix decreased
for 75% and 88%, respectively. After 200 ◦C, the reference mix had negligibly lower values
compared to MK mixes—decrease was around 38%. FA and LF had a beneficial effect on
the residual modulus of elasticity compared to reference mix. As with the compressive
strength, there was a strong loss of the modulus of elasticity up to 400 ◦C in all tested mixes.
3.6. Peak Strain
Figures 14 and 15 show the peak strain, which is the strain corresponding to the
ultimate stress applied for the studied concrete mixes with increasing temperature (200 ◦C,
400 ◦C and 600 ◦C) in both absolute and relative values. The initial peak strain of the tested
mixes varied from 1.90‰ for M7 up to 2.62‰ for M5.
15. Materials 2022, 15, 2222 15 of 24
3.6. Peak Strain
Figures 14 and 15 show the peak strain, which is the strain corresponding to the ulti-
mate stress applied for the studied concrete mixes with increasing temperature (200 °C,
400 °C and 600 °C) in both absolute and relative values. The initial peak strain of the tested
mixes varied from 1.90 ‰ for M7 up to 2.62‰ for M5.
Figure 14. Strain at peak stress vs. temperature of tested mixes.
Figure 15. Relative values of strain at peak stress with increasing temperature.
In accordance with the observations of Bamonte et al. [38] and Chang et al. [40], the
peak strain increases with temperature, indicating a higher ductility of concrete at ele-
vated temperatures. The highest increase after heating to 600 °C was obtained in FA mixes
with 30 and 40% cement replacement, which was up to 2.6 times. Opposed to compressive
strength and modulus of elasticity, peak strain seems to exhibit a higher degree of varia-
bility.
Figure 14. Strain at peak stress vs. temperature of tested mixes.
3.6. Peak Strain
Figures 14 and 15 show the peak strain, which is the strain corresponding to the ulti-
mate stress applied for the studied concrete mixes with increasing temperature (200 °C,
400 °C and 600 °C) in both absolute and relative values. The initial peak strain of the tested
mixes varied from 1.90 ‰ for M7 up to 2.62‰ for M5.
Figure 14. Strain at peak stress vs. temperature of tested mixes.
Figure 15. Relative values of strain at peak stress with increasing temperature.
In accordance with the observations of Bamonte et al. [38] and Chang et al. [40], the
peak strain increases with temperature, indicating a higher ductility of concrete at ele-
vated temperatures. The highest increase after heating to 600 °C was obtained in FA mixes
with 30 and 40% cement replacement, which was up to 2.6 times. Opposed to compressive
strength and modulus of elasticity, peak strain seems to exhibit a higher degree of varia-
bility.
Figure 15. Relative values of strain at peak stress with increasing temperature.
In accordance with the observations of Bamonte et al. [38] and Chang et al. [40], the
peak strain increases with temperature, indicating a higher ductility of concrete at elevated
temperatures. The highest increase after heating to 600 ◦C was obtained in FA mixes with
30 and 40% cement replacement, which was up to 2.6 times. Opposed to compressive
strength and modulus of elasticity, peak strain seems to exhibit a higher degree of variability.
4. Modelling of Stress–Strain Behaviour
The prediction of the stress–strain relationship of concrete subjected to uniaxial com-
pression at room temperature has been a topic of research papers for many decades [41–43].
Recently, several researchers performed experimental investigations of stress–strain rela-
tionships of concrete during or after exposure to fire [40,44,45]. Different equations have
been proposed to describe the stress–strain diagram of concrete. One of the simplest models
was proposed by Popovic (Equation (1)):
σ
σmax
=
ε
εmax
β
β − 1 +
ε
εmax
β
(1)
where σ is the compressive stress, σmax is the peak stress (equivalent to fc), ε is strain, εmax
is the strain at peak stress and β is parameter describing the curvature of the stress–strain
16. Materials 2022, 15, 2222 16 of 24
relationship [41,46]. It was found that the Popovics model can accurately describe the
stress–strain relation for concrete after being exposed to temperatures up to 500 ◦C while at
temperatures above 500 ◦C, the concave-up part of the stress–strain curve can form at low
stresses [40,45]. To provide a better fit to the experimental data, especially to the descending
branch of the stress–strain relationship, several modifications of Equation (1) have been
proposed by introducing additional correction coefficients into the equation [40,45,47].
As said previously, increasing temperature changes curvature of the stress–strain rela-
tionship. An example of the influence of high temperature treatment on the shape of stress–
strain relation in concrete is shown in Figure 16. As temperature increases stress–strain
relationship shifts from curved towards linear. This was confirmed on all mixes analyzed
within this research and is consistent with the data presented in the literature [40,44,45].
The shape of the stress–strain curves of concrete under uniaxial compression is explained
by progressive microcracking [46]. Up to about 50% of compressive strength microcrack-
ing is mainly concentrated at the ITZ between aggregate and cement matrix. A further
increase in stresses causes cracks to form in the matrix, which produces more pronounced
deviations of the stress–strain curve from linearity. In concrete exposed to elevated tem-
perature, cracks were already formed in the matrix and part of the aggregated before any
load was applied. SEM imaging shows that the amount of matrix and aggregate cracking
increases with temperature. These additional in-built cracks change the interaction be-
tween failure mechanisms under compressive loads, which is reflected on the shape of the
stress–strain curve.
max
where σ is the compressive stress, σmax is the peak stress (equivalent to fc), ε is strain, εmax
is the strain at peak stress and β is parameter describing the curvature of the stress–strain
relationship [41,46]. It was found that the Popovics model can accurately describe the
stress–strain relation for concrete after being exposed to temperatures up to 500 °C while
at temperatures above 500 °C, the concave-up part of the stress–strain curve can form at
low stresses [40,45]. To provide a better fit to the experimental data, especially to the de-
scending branch of the stress–strain relationship, several modifications of Equation (1)
have been proposed by introducing additional correction coefficients into the equation
[40,45,47].
As said previously, increasing temperature changes curvature of the stress–strain re-
lationship. An example of the influence of high temperature treatment on the shape of
stress–strain relation in concrete is shown in Figure 16. As temperature increases stress–
strain relationship shifts from curved towards linear. This was confirmed on all mixes
analyzed within this research and is consistent with the data presented in the literature
[40,44,45]. The shape of the stress–strain curves of concrete under uniaxial compression is
explained by progressive microcracking [46]. Up to about 50% of compressive strength
microcracking is mainly concentrated at the ITZ between aggregate and cement matrix. A
further increase in stresses causes cracks to form in the matrix, which produces more pro-
nounced deviations of the stress–strain curve from linearity. In concrete exposed to ele-
vated temperature, cracks were already formed in the matrix and part of the aggregated
before any load was applied. SEM imaging shows that the amount of matrix and aggre-
gate cracking increases with temperature. These additional in-built cracks change the in-
teraction between failure mechanisms under compressive loads, which is reflected on the
shape of the stress–strain curve.
0
0.2
0.4
0.6
0.8
1
1.2
0 0.2 0.4 0.6 0.8 1 1.2
Relative
compr.
stress,
σ/σ
max
(−)
Relative strain, ε/εmax (−)
M2-20°C
M2-200°C
M2-400°C
M2-600°C
Figure 16. Relative compressive stress vs. relative strain for mixture M2.
Nonlinear regression analysis using least squares method was applied to evaluate how
well the model from Equation (1) represents experimentally determined stress–strain curves.
Multiplying Equation (1) with peak stress (σmax) yields the stress–strain relationship in
absolute units. The differences between the values predicted by the model and the observed
values were evaluated by the root mean square error (S). The range of S for samples from
all mixes kept at 20 ◦C was 1.8–3.9 MPa. For specimens exposed 200 ◦C, 400 ◦C and 600 ◦C,
the range of S was 0.9–1.9 MPa, 0.2–1.3 MPa and 0.2–1.2 MPa, respectively. As an example,
a comparison between model and experimental values for specimens from mix M2 is
presented in Figure 17.
17. Materials 2022, 15, 2222 17 of 24
curves. Multiplying Equation (1) with peak stress (σmax) yields the stress–strain relation-
ship in absolute units. The differences between the values predicted by the model and the
observed values were evaluated by the root mean square error (S). The range of S for
samples from all mixes kept at 20 °C was 1.8–3.9 MPa. For specimens exposed 200 °C, 400
°C and 600 °C, the range of S was 0.9–1.9 MPa, 0.2–1.3 MPa and 0.2–1.2 MPa, respectively.
As an example, a comparison between model and experimental values for specimens from
mix M2 is presented in Figure 17.
Figure 17. Comparison between model and experimental values.
Equation (1) contains only one unknown parameter (β), which is determined by re-
gression analysis. Β represents the ratio E0/(E0 – Ep), where E0 is the initial tangent Youngs
modulus and Ep is secant Youngs modulus at peak stress [41]. Since an increase in tem-
perature shifts the stress–strain curve toward a linear shape, the difference E0 − Ep should
decrease and consequently β increase. This was confirmed by analyzing β for specimens
from mixes M2–M11. As temperature increases, parameter β increases, indicating that the
stress–strain curve approaches linear dependence. Figure 18 compares the average values
of β, and its standard deviations are compared between concrete mixes with different min-
eral additives. Increasing temperature also increased the dispersion of β.
It is important to emphasize that the variation of β has a significantly different effect
on the shape of the stress–strain curve for low and high values of β. One method of quan-
tifying the effect of β on the shape of a stress–strain curve is the use of the area under the
stress–strain curve, which represents the mechanical energy per unit volume. Equation
(1) represents relative stress (σ/σmax) expressed as a function of relative strain (ε/εmax). The
area under relative stress vs. relative strain curve is proportional to the mechanical energy
consumed by deforming the material. If β = 1, then Equation (1) produces σ/σmax = 1, which
represents perfectly plastic material; on the other hand, if β proceeds to infinity, Equation
(1) becomes σ/σmax = ε/εmax and represents linear elastic material. Integrating Equation (1)
in the range of relative strain between 0 and 1 provides an area of 1 for β = 1 and 0.5 for β
→ ∞. The values of β for concrete start at 1.3 or 1.4 [40,44]. By analyzing the dependence
of the area (A) under the relative stress–strain curve, the analysis shows that the area de-
creases with increasing β approximately according to A = 0.5 (β−k + 1), where k ≈ 1.095.
0
10
20
30
40
50
60
70
80
0 1 2 3 4 5 6 7
Compressive
stress,
σ
(MPa)
Strain, ε (mm/m)
experimental
model
20°C; β=2.9
S=2.3 MPa
200°C; β=3.7
S=1.4 MPa
400°C; β=8.2
S=1.1 MPa
600°C; β=13.9
S=0.4 MPa
Figure 17. Comparison between model and experimental values.
Equation (1) contains only one unknown parameter (β), which is determined by regres-
sion analysis. B represents the ratio E0/(E0 − Ep), where E0 is the initial tangent Youngs
modulus and Ep is secant Youngs modulus at peak stress [41]. Since an increase in tem-
perature shifts the stress–strain curve toward a linear shape, the difference E0 − Ep should
decrease and consequently β increase. This was confirmed by analyzing β for specimens
from mixes M2–M11. As temperature increases, parameter β increases, indicating that the
stress–strain curve approaches linear dependence. Figure 18 compares the average values
of β, and its standard deviations are compared between concrete mixes with different
mineral additives. Increasing temperature also increased the dispersion of β.
Materials 2022, 15, x FOR PEER REVIEW 19 of 26
Using this equation for A, it can be shown that a change in β within the range of 2–4 would
cause approximately the same change in the area as a variation in the range of 3–17.
Figure 18. Parameter β determined by regression analysis to experimentally determine stress–strain
relationships.
For normal concrete cured at room temperature, Popovics proposed that β can be
estimated from the compressive strength as 0.058fc + 1. In this work, for specimens stored
at 20 °C, the relation between fc and β determined by linear regression is 0.044fc +0.6. Both
equations have a similar slope and are compared in Figure 19. This implies that the order
in which microcracking evolves during loading in the high strength concrete tested in this
research is similar to that in normal strength concrete.
The relationship between fc and β for concrete exposed to elevated temperature does
not follow the same trend as for concrete stored at room temperature. The correlation be-
tween fc and β was analyzed for each mix separately using linear regression. It was found
that power law equation provided lower errors of estimation compared to the linear
model. Due to the wide dispersion of data, no significant differences between models for
mixes containing different mineral admixtures were found; thus, only overall regression
models based on the results of all tested samples are provided in Figure 19. The differences
between values predicted by model and the observed values are evaluated by root mean
0
5
10
15
20
25
30
M2-M11 M2 M3-M5 M6-M8 M9-M11
β
(−)
20
200
400
600
Figure 18. Parameter β determined by regression analysis to experimentally determine stress–
strain relationships.
It is important to emphasize that the variation of β has a significantly different effect
on the shape of the stress–strain curve for low and high values of β. One method of
quantifying the effect of β on the shape of a stress–strain curve is the use of the area
under the stress–strain curve, which represents the mechanical energy per unit volume.
Equation (1) represents relative stress (σ/σmax) expressed as a function of relative strain
(ε/εmax). The area under relative stress vs. relative strain curve is proportional to the
mechanical energy consumed by deforming the material. If β = 1, then Equation (1)
produces σ/σmax = 1, which represents perfectly plastic material; on the other hand, if β
18. Materials 2022, 15, 2222 18 of 24
proceeds to infinity, Equation (1) becomes σ/σmax = ε/εmax and represents linear elastic
material. Integrating Equation (1) in the range of relative strain between 0 and 1 provides
an area of 1 for β = 1 and 0.5 for β → ∞. The values of β for concrete start at 1.3 or 1.4 [40,44].
By analyzing the dependence of the area (A) under the relative stress–strain curve, the
analysis shows that the area decreases with increasing β approximately according to
A = 0.5 (β−k + 1), where k ≈ 1.095. Using this equation for A, it can be shown that a change
in β within the range of 2–4 would cause approximately the same change in the area as a
variation in the range of 3–17.
For normal concrete cured at room temperature, Popovics proposed that β can be
estimated from the compressive strength as 0.058fc + 1. In this work, for specimens stored
at 20 ◦C, the relation between fc and β determined by linear regression is 0.044fc + 0.6. Both
equations have a similar slope and are compared in Figure 19. This implies that the order
in which microcracking evolves during loading in the high strength concrete tested in this
research is similar to that in normal strength concrete.
Materials 2022, 15, x FOR PEER REVIEW
Figure 19. Correlation between parameter β and compressive strength for mixtures M2-M1
5. Conclusions
Previous studies on SCC have shown that the advantages of this type of con
room temperature over conventional concrete are its improved internal structure
is achieved by more effective particle packing. Compared to normal vibrated types
crete, a higher percentage of fines and, in most cases, mineral additives are used
study, new experimental results on mechanical properties were obtained by inves
the effects of elevated temperatures on the performance of high strength SCC w
common mineral additives, i.e., metakaolin, fly ash and limestone filler in differe
portions. Based on the results obtained, the following conclusions can be drawn:
8. By comparing the stress–strain curves within the mixes containing the same
additive, it can be observed that the different amounts of FA (20–40%) and lim
(5–15%) in the studied concrete mixes lead to a similar behaviour, while th
with different MK content (5–15%) show larger variations after all target te
tures.
9. The different mineral additives used in this study (MK, FA and LF) affected
velopment of different microstructures of the concrete, especially ITZ, which,
affected the variations in the residual compressive strength by 24% and th
strain by 38%, while the variation in the residual elastic modulus was 14%.
10. Contrary to the findings in the literature, which show that concrete retains
its strength up to 400 °C, in this study, a significant loss of mechanical pro
0
5
10
15
20
25
30
35
0 20 40 60 80 100 120
β
(−)
Compressive strength, fc (MPa)
20
200
400
600
Model
β = 1457.8fc
-1.32
S = 1.9 (20°C)
S = 2.0 (200°C)
S = 6.3 (400°C)
S = 7.3 (600°C)
β = 0.058fc+1
β = 0.044fc+0.6
Figure 19. Correlation between parameter β and compressive strength for mixtures M2–M11.
The relationship between fc and β for concrete exposed to elevated temperature does
not follow the same trend as for concrete stored at room temperature. The correlation
between fc and β was analyzed for each mix separately using linear regression. It was
found that power law equation provided lower errors of estimation compared to the linear
model. Due to the wide dispersion of data, no significant differences between models for
mixes containing different mineral admixtures were found; thus, only overall regression
models based on the results of all tested samples are provided in Figure 19. The differences
between values predicted by model and the observed values are evaluated by root mean
square error for each temperature of exposure and are also provided in Figure 19. Although
the variation of β increases with temperature, it can be shown that the effect of this variation
on the area under the relative stress–strain curve is the greatest at low temperatures.
5. Conclusions
Previous studies on SCC have shown that the advantages of this type of concrete at
room temperature over conventional concrete are its improved internal structure, which is
achieved by more effective particle packing. Compared to normal vibrated types of concrete,
a higher percentage of fines and, in most cases, mineral additives are used. In this study,
new experimental results on mechanical properties were obtained by investigating the
effects of elevated temperatures on the performance of high strength SCC with the common
mineral additives, i.e., metakaolin, fly ash and limestone filler in different proportions.
Based on the results obtained, the following conclusions can be drawn:
19. Materials 2022, 15, 2222 19 of 24
8. By comparing the stress–strain curves within the mixes containing the same mineral
additive, it can be observed that the different amounts of FA (20–40%) and limestone
(5–15%) in the studied concrete mixes lead to a similar behaviour, while the mixes
with different MK content (5–15%) show larger variations after all target temperatures.
9. The different mineral additives used in this study (MK, FA and LF) affected the
development of different microstructures of the concrete, especially ITZ, which, in
turn, affected the variations in the residual compressive strength by 24% and the peak
strain by 38%, while the variation in the residual elastic modulus was 14%.
10. Contrary to the findings in the literature, which show that concrete retains most of
its strength up to 400 ◦C, in this study, a significant loss of mechanical properties
(compressive strength and elastic modulus) and an increase in peak strain were
observed up to a temperature of 400 ◦C.
11. However, comparing the obtained results with the recommendations for compressive
strength given in EC 2 for HSC, it can be concluded that the strength loss of EC 2 in the
case of SCC with used mineral additives is too conservative in the lower temperature
range (400 ◦C), especially for mixes containing fly ash.
12. The Popovic model for the relationship between stress and strain, developed es-
sentially for conventional concrete, provided a good approximation relative to the
experimentally determined stress–strain curves at different temperatures.
In this study, one mineral additive was added to the mix. To increase the sustainability
of the concrete, the tests should be extended to binary and ternary mixes of mineral addi-
tives and their mutual interaction should be evaluated after exposure to high temperature.
Author Contributions: Conceptualization, methodology, formal analysis and investigation, M.J.R.,
I.G., I.N.G. and A.M.; writing—original draft preparation, M.J.R.; writing—review and editing, M.J.R.,
I.G. and I.N.G.; visualization, M.J.R. and I.G.; project administration and funding acquisition, M.J.R.,
A.M. All authors have read and agreed to the published version of the manuscript.
Funding: This research was funded by the Croatian Ministry of Science, Education and Sport; grant
number 082-0822161-2159.
Institutional Review Board Statement: Not applicable.
Informed Consent Statement: Not applicable.
Data Availability Statement: Not applicable.
Acknowledgments: Our special thanks are extended to Marija Ðuroković from IGH Institute dd for
performing chemical analysis of binders and Holcim Ltd for providing resources during research.
Conflicts of Interest: The authors declare no conflict of interest.
Appendix A. Monitored Temperatures in Concrete Specimens
Figure A1 presents temperature development within concrete specimens.
Materials 2022, 15, x FOR PEER REVIEW 22 of 27
(a)
(b)
Figure A1. Cont.
20. Materials 2022, 15, 2222 20 of 24
(a)
(b)
(c)
Figure A1. Temperature development for mix M11-LF15 during heating to target temperature of
(a) 200°C, (b) 400°C and (c) 600°C.
Appendix B. Dolomite Decomposition after Temperature of 800 °
C
In Figure A2., the degradation of specimens is presented with elapsed time up to 28
days after cooling.
Figure A1. Temperature development for mix M11-LF15 during heating to target temperature of
(a) 200 ◦C, (b) 400 ◦C and (c) 600 ◦C.
Appendix B. Dolomite Decomposition after Temperature of 800 ◦C
In Figure A2., the degradation of specimens is presented with elapsed time up to
28 days after cooling.
Materials 2022, 15, x FOR PEER REVIEW 22 of 26
Figure A1. Temperature development for mix M11-LF15 during heating to target temperature of
(a) 200°C, (b) 400°C and (c) 600°C.
Appendix B. Dolomite Decomposition after Temperature of 800 °
C
In Figure A2., the degradation of specimens is presented with elapsed time up to 28
days after cooling.
Figure A2. The post-cooling appearance of reference concrete specimens heated to 800 °C (a) after
cooling, (b) 7 days after cooling, (c) 21 days after cooling, (d) 28 days after cooling.
Appendix C. Stress–Strain Curves of Tested Mixes
Figure A3 presents stress–strain curves obtained on three specimens from each mix
and after each temperature cycle considered.
Figure A2. The post-cooling appearance of reference concrete specimens heated to 800 ◦C (a) after
cooling, (b) 7 days after cooling, (c) 21 days after cooling, (d) 28 days after cooling.
21. Materials 2022, 15, 2222 21 of 24
Appendix C. Stress–Strain Curves of Tested Mixes
Figure A3 presents stress–strain curves obtained on three specimens from each mix
and after each temperature cycle considered.
Materials 2022, 15, x FOR PEER REVIEW 23 of 26
(a)
(b) (c)
(d)
Figure A3. Cont.
22. Materials 2022, 15, 2222 22 of 24
Materials 2022, 15, x FOR PEER REVIEW 24 of 26
(e) (f)
(g)
(h) (i)
(j)
Figure A3. Stress–strain curves of the tested mixes: (a) reference mix; (b–d) mixes with metakaolin;
(e–g) mixes with fly ash; (h–j) mixes with limestone.
References
1. Schneider, U. Concrete at high temperature. Fire Saf. J. 1988, 13, 55–68. https://doi.org/10.1016/0379-7112(88)90033-1.
2. Kodur, V. Properties of Concrete at Elevated Temperatures. Int. Sch. Res. Not. 2014, 68510. https://doi.org/10.1155/2014/468510.
3. Babalola, O.E.; Awoyera, P.O.; Le, D.-H.; Bendezú Romero, L.M. A review of residual strength properties of normal and high
strength concrete exposed to elevated temperatures: Impact of materials modification on behaviour of concrete composite. Con-
str. Build. Mater. 2021, 296, 123448. https://doi.org/10.1016/j.conbuildmat.2021.123448.
4. Anupama Krishna, D.; Priyadarsini, R.S.; Narayanan, S. High temperature effects on different grades of concrete. Sadhana 2021,
46, 31. https://doi.org/10.1007/s12046-020-01536-6.
Figure A3. Stress–strain curves of the tested mixes: (a) reference mix; (b–d) mixes with metakaolin;
(e–g) mixes with fly ash; (h–j) mixes with limestone.
References
1. Schneider, U. Concrete at high temperature. Fire Saf. J. 1988, 13, 55–68. [CrossRef]
2. Kodur, V. Properties of Concrete at Elevated Temperatures. Int. Sch. Res. Not. 2014, 68510. [CrossRef]
3. Babalola, O.E.; Awoyera, P.O.; Le, D.-H.; Bendezú Romero, L.M. A review of residual strength properties of normal and high
strength concrete exposed to elevated temperatures: Impact of materials modification on behaviour of concrete composite.
Constr. Build. Mater. 2021, 296, 123448. [CrossRef]
4. Anupama Krishna, D.; Priyadarsini, R.S.; Narayanan, S. High temperature effects on different grades of concrete. Sadhana 2021,
46, 31. [CrossRef]
5. EN 1992-1-2+AC; Eurocode 2: Design of Concrete Structures—Part 1–2: General Rules—Structural Fire Design. European
Committee for Standardization (CEN): Brussels, Belgium, 2008.
6. EN 1994-1-2+A1; Eurocode 4: Design of Composite Steel and Concrete Structures—Part 1–2: General Rules—Structural Fire
Design. European Committee for Standardization (CEN): Brussels, Belgium, 2014.
7. Dadsetan, S.; Bai, J. Mechanical and microstructural properties of self-compacting concrete blended with metakaolin, ground
granulated blast-furnace slag and fly ash. Constr. Build. Mater. 2017, 146, 658–667. [CrossRef]
23. Materials 2022, 15, 2222 23 of 24
8. Pang, L.; Liu, Z.; Wang, D.; An, M. Review on the Application of Supplementary Cementitious Materials in Self-Compacting
Concrete. Crystals 2022, 12, 180. [CrossRef]
9. Diniz, H.A.A.; dos Anjos, M.A.S.; Rocha, A.K.A.; Ferreira, R.L.S. Effects of the use of agricultural ashes, metakaolin and
hydrated-lime on the behavior of self-compacting concretes. Constr. Build. Mater. 2022, 319, 126087. [CrossRef]
10. Abed, M.; Nemes, R.; Lublóy, É. Performance of Self-Compacting High-Performance Concrete Produced with Waste Materials
after Exposure to Elevated Temperature. J. Mater. Civ. Eng. 2020, 32, 05019004. [CrossRef]
11. Hager, I.; Mróz, K. Role of Polypropylene Fibres in Concrete Spalling Risk Mitigation in Fire and Test Methods of Fibres
Effectiveness Evaluation. Materials 2019, 12, 3869. [CrossRef]
12. RILEM Technical Committee. Final report of RILEM TC 205-DSC: Durability of self-compacting concrete. Mater. Struct. 2007,
41, 225–233. [CrossRef]
13. Khazani, M.H.; Chai Lian, O.; Wee, L.S.; Md Zain, M.R.; Yahya, N.A. The Effect of Elevated Temperature on Engineered
Cementitious Composite Microstructural Behavior: An Overview. Pertanika J. Sci. Technol. 2022, 30, 433–449. [CrossRef]
14. Abed, M.; Nemes, R.; Nehme, S. Residual Modulus of Elasticity of Self-Compacting Concrete Incorporated Unprocessed Waste
Fly Ash after Expose to the Elevated Temperature. Int. J. Civ. Environ. Eng. 2019, 13, 559–564. [CrossRef]
15. Al-Lami, M.S. Effect of elevated temperature on compressive strength of self compacting concrete using viscocrete and silica
fume. Int. J. Civ. Eng. Technol. 2017, 8, 405–413.
16. Uysal, M.; Yilmaz, K.; Ipek, M. Properties and behavior of self-compacting concrete produced with GBFS and FA additives
subjected to high temperatures. Constr. Build. Mater. 2012, 28, 321–326. [CrossRef]
17. Abed, M.; de Brito, J. Evaluation of high-performance self-compacting concrete using alternative materials and exposed to
elevated temperatures by non-destructive testing. J. Build. Eng. 2020, 32, 101720. [CrossRef]
18. Anagnostopoulos, N.; Sideris, K.K.; Georgiadis, A. Mechanical characteristics of self-compacting concretes with different filler
materials, exposed to elevated temperatures. Mater. Struct. 2008, 42, 1393–1405. [CrossRef]
19. Xu, Y.; Wong, Y.; Poon, C.; Anson, M. Impact of high temperature on PFA concrete. Cem. Concr. Res. 2001, 31, 1065–1073.
[CrossRef]
20. Anand, N.; Prince Arulraj, G.; Aravindhan, C. Stress-strain behaviour of normal compacting and self compacting concrete under
elevated temperatures. J. Struct. Fire Eng. 2014, 5, 63–75. [CrossRef]
21. Uysal, M.; Tanyildizi, H. Estimation of compressive strength of self compacting concrete containing polypropylene fiber and
mineral additives exposed to high temperature using artificial neural networ. Constr. Build. Mater. 2012, 27, 404–414. [CrossRef]
22. Anand, N.; Godwin, I.A.; Prince Arulraj, P. Influence of mineral admixtures on mechanical properties of self-compacting concrete
under elevated temperature. Fire Mater. 2016, 40, 940–958. [CrossRef]
23. Abdelmelek, N.; Alimrani, N.S.; Krelias, N.; Lubloy, E. Effect of Elevated Temperatures on Microstructure of High Strength
Concrete Based-Metakaolin. J. King Saud Univ. Eng. Sci. 2021; in press. [CrossRef]
24. Okamura, H.; Ouchi, M. Self-compacting concrete. J. Adv. Concr. Technol. 2003, 1, 5–15. [CrossRef]
25. EN 197-1; Cement—Part 1: Composition, Specifications and Conformity Criteria for Common Cements. European Committee for
Standardization (CEN): Brussels, Belgium, 2011.
26. EN 196-1; Methods of Testing Cement—Part 1: Determination of Strength. European Committee for Standardization (CEN):
Brussels, Belgium, 2016.
27. EFNARC. The European Guidelines for Self-Compacting Concrete; Specification, Production and Use; European Federation of
Producers and Applicators of Specialist Products for Structures: Surrey, UK, 2005.
28. EN 206-9; Concrete—Part 9: Additional Rules for Self-Compacting Concrete (SCC). European Committee for Standardization
(CEN): Brussels, Belgium, 2010.
29. Jelčić Rukavina, M.; Gabrijel, I.; Bjegović, D. Modifications of dolomite-based self-compacting concrete properties using mineral
additives. Teh. Vjesn. Tech. Gaz. 2015, 22, 233–240. [CrossRef]
30. Recommendation of RILEM TC 200-HTC: Mechanical concrete properties at high temperatures—modelling and application,
Part 1: Introduction—General presentation. Mater. Struct. 2007, 40, 841–853. [CrossRef]
31. Recommendation of RILEM TC 200-HTC: Mechanical concrete properties at high temperatures—modelling and applications,
Part 2: Stress—Strain relation. Mater. Struct. 2007, 40, 855–864. [CrossRef]
32. Hertz, K.D. Concrete strength for fire safety design. Mag. Concr. Res. 2005, 57, 445–453. [CrossRef]
33. Liu, J.C.; Tan, K.H.; Yao, Y. A new perspective on nature of fire-induced spalling in concrete. Constr. Build. Mater. 2018,
184, 581–590. [CrossRef]
34. Fernandes, B.; Gil, A.M.; Bolina, F.L.; Tutikian, B.F. Microstructure of concrete subjected to elevated temperatures: Physico-
chemical changes and analysis techniques. Rev. IBRACON Estrut. Mater. 2017, 10, 838–863. [CrossRef]
35. Wild, S.; Khatib, J.M.; Jones, A. Relative strength, pozzolanic activity and cement hydration in superplasticised metakaolin
concrete. Cem. Concr. Res. 1996, 26, 1537–1544. [CrossRef]
36. Poon, C.; Azhar, S.; Anson, M.; Wong, Y. Performance of metakaolin concrete at elevated temperatures. Cem. Concr. Compos. 2003,
25, 83–89. [CrossRef]
37. Persson, B. Fire resistance of self-compacting concrete, SCC. Mater. Struct. 2004, 37, 575–584. [CrossRef]
38. Bamonte, P.; Gambarova, P.G. A study on the mechanical properties of self-compacting concrete at high temperature and after
cooling. Mater. Struct. 2012, 45, 1375–1387. [CrossRef]
24. Materials 2022, 15, 2222 24 of 24
39. Uysal, M. Self-compacting concrete incorporating filler additives: Performance at high temperatures. Constr. Build. Mater. 2012,
26, 701–706. [CrossRef]
40. Chang, Y.F.; Chen, Y.H.; Sheu, M.S.; Yao, G.C. Residual stress–strain relationship for concrete after exposure to high temperatures.
Cem. Concr. Res. 2006, 36, 1999–2005. [CrossRef]
41. Popovics, S. A numerical approach to the complete stress-strain curve of concrete. Cem. Concr. Res. 1973, 3, 583–599. [CrossRef]
42. Tsai, W.T. Uniaxial Compressional Stress-Strain Relation of Concrete. J. Struct. Eng. 1988, 114, 2133–2136. [CrossRef]
43. Shafiq, N.; Ayub, T.; Nuruddin, M.F. Predictive Stress-Strain Models for High Strength Concrete Subjected to Uniaxial Compres-
sion. Appl. Mech. Mater. 2014, 567, 476–481. [CrossRef]
44. Annerel, E.; Taerwe, L. Evolution of the strains of traditional and self-compacting concrete during and after fire. Mater. Struct.
Constr. 2011, 44, 1369–1380. [CrossRef]
45. Sharma, U.; Zaidi, K.; Bhandari, N. Residual Compressive Stress-Strain Relationship for Concrete Subjected to Elevated Tempera-
tures. J. Struct. Fire Eng. 2012, 3, 327–350. [CrossRef]
46. Carreira, D.J.; Chu, K.-H. Stress-Strain Relationship for plain concrete in compression. ACI J. 1985, 82, 797–804.
47. Stojković, N.; Perić, D.; Stojić, D.; Marković, N. New stress-strain model for concrete at high temperatures. Teh. Vjesn. Tech. Gaz.