This document summarizes a study that assessed the fresh and hardened properties of self-consolidating concrete (SCC) containing steel, polypropylene, and hybrid fibers at various high temperatures. Four SCC mixtures were tested: a control without fibers, one with 1% polypropylene fibers, one with 1% steel fibers, and one with 0.5% of each steel and polypropylene fibers. All mixtures met standards for workability and passing ability. The inclusion of fibers slightly reduced workability. Mechanical properties generally increased with temperature up to 200°C then decreased at higher temperatures. Fiber-reinforced SCC exhibited improved spalling resistance compared to plain SCC.
Impact and Performance of Linen Fiber Reinforced Concrete in Slender ColumnsAJSERJournal
This study was consisted of two phases, revealed the behavior of Self-Compacting Concrete (SCC)
specimens of small-diameter slender column to achieve high quality concrete properties without using concrete
vibrator. The first phase investigated the effect of linen fiber on the rheological properties of SCC using two mixes types:
type I mix: without lime powder, and type II mix: with 20% lime as a replacement of cement content. The linen fiber was
contented of 0, 2, and 4 Kg/m³. In the second phase, the type II mix was used to cast three columns; one with plain SCC
and the other two with 2 and 4 Kg/m³ fiber contents. These columns were cured and cut in a certain manner to obtain 7
cylinders 150 × 300 mm and 8 slices 20 mm thickness. The cylinders were used to measure the distribution of unit
weight, compressive strength, and ultrasonic pulse velocity (UPV) along the column height. The rheological properties
of SCC were reduced with the additives of fibers to the mix constituents, but the properties of Fiber reinforced SelfCompacted Concrete (FSCC) were tested at 4 Kg/m³ fiber content. The distribution of unit weight, compressive strength,
and UPV provided good compaction of concrete. Also, the distribution of coarse aggregate at bottom, middle and top
sections of columns were uniformly distributed.
The document summarizes a literature review on self-compacting concrete (SCC). It lists 16 research papers on SCC, providing the title, authors, year published, journal/publisher, methodology used, and main outcomes for each. The majority of the papers studied the fresh and hardened properties of SCC mixtures containing supplementary cementitious materials like fly ash, slag, or mineral admixtures. Common tests included measuring flowability, passing ability, and compressive strength. Most found that partial replacement of cement with these materials can improve the properties of SCC, though higher replacement rates may negatively impact strength.
This document summarizes a research study on the effect of using electrically precipitated fly ash (EPFA) as a partial replacement for cement in self-compacting concrete (SCC). The study tested SCC mixes with 0-30% EPFA replacement at 5% intervals. Tests were conducted on fresh properties, mechanical properties like compressive strength, and durability properties like rapid chloride permeability and water sorptivity. Results showed that 20% EPFA replacement provided better results than the control SCC mix, improving properties while also providing economic and environmental benefits through reduced cement usage.
Experimental Study on Durability Characteristics of High Performance Concrete...theijes
High performance concrete (HPC) is developed gradually over the last 15 years with respect to production of concrete with higher and higher strength. To enhance the properties such as durability, strength, workability, economy has increased due to the usage of mineral admixtures in making high performance concrete. The scope of the present study is to investigate the effect of mineral admixtures and by-products towards the performance of HPC. An effort has been made to concentrate on the mineral admixture of silica fume towards their pozzolanic reaction and industrial by-product of bottom ash and steel slag towards their hydration reaction can be contributed towards their strength and durability properties. The strength characteristics such as compressive strength, tensile strength and flexural strength were investigated to find the optimum replacement of mineral admixture and by-product admixture. HPC with mineral admixture of silica fume at the replacement levels of 0%, 5%, 10%, 15% & 20% were studied at the age of 28 days and industrial by-products of bottom ash and steel slag aggregate at the replacement level of 10%, 20%, 30%, 40% & 50% were studied at the age of 28 days. There were a total of 15 mixes created with different material contents. Out of 14 were HPC mixes and 1 were conventional concrete mixes. Finally strength has enhanced with the mix of silica fume can replaced by cement with 5% and bottom ash and steel slag can replaced by fine and coarse aggregate with 10% can be achieved higher strength when compared with other percentage of mixes. The combination mixes can be classified as binary and ternary mixes. Binary mixes involved combinations of silica fume and bottom ash (SF+BA), silica fume and steel slag aggregate (SF+SSA), bottom ash and steel slag aggregate (BA+SSA) and Ternary mixes involved combination of three materials such as silica fume, bottom ash and steel slag aggregate (SF+BA+SSA) in High performance concrete. The investigation revealed that the combined use of silica fume, bottom ash and steel slag aggregate improved the mechanical properties of HPC and thus there 3 materials may use as a partial replacement material in making HPC. The durability studies such as acid resistance, salt resistance, sulphate resistance & water absorption were conducted. From the experimental investigation, it was observed that mineral admixture of silica fume and industrial by-products of bottom ash & steel slag aggregate plays a vital role in improving the strength and durability parameter itself.
To Study the Properties of Self-Compacting Concrete Using Recycled Aggregate ...paperpublications3
Abstract: This paper investigates the study of workability and durability characteristics of Self-Compacting Concrete (SCC) with Viscosity Modifying Admixture (VMA), and containing fly ash. The mix design for SCC was arrived as per the Guidelines of European Federation of National Associations Representing for Concrete (EFNARC). In this investigation, SCC was made by usual ingredients such as cement, fine aggregate, coarse aggregate, water, mineral admixture fly ash and demolished concrete at various replacement levels (5%, 10%, 15%, and 20%). To enhance the property of SCC made with the use of demolish concrete and fly ash, glass fiber has been added to the mix. Glass fiber in various % (i.e. 0.15%, 0.20% 0.30%, of Wt. of cement) has been added in the mix which contain demolish concrete and gave highest strength i.e. (10% demolish concrete).
Strength and durability studies on silica fume modified high volume fly ash c...IAEME Publication
This document discusses a study on the strength and durability of silica fume modified high-volume fly ash concrete. Five concrete mixes were tested: a control mix and four mixes where 50% of cement was replaced with fly ash and additional replacement of cement with 5%, 10%, and 15% silica fume. Testing included compressive strength at various ages, rapid chloride permeability, chloride ion diffusion, and carbonation resistance. The addition of silica fume to high-volume fly ash concrete was found to improve mechanical properties and durability compared to fly ash concrete without silica fume.
. effect of different types of cement on fresh and mechanical properties of c...ENGJiidhe
The document reviews several studies that investigated the effect of different cement types on the fresh and mechanical properties of concrete. The cement types investigated included ordinary Portland cement, fly ash-based cement, slag cement, and cement with supplementary materials like silica fume, metakaolin, and polyethylene therephthalate. The studies found that workability generally decreased with the addition of supplementary materials but mechanical properties like compressive strength and durability increased. The performance of concrete depended on factors like water-cement ratio, curing conditions, and the replacement levels of supplementary materials. Overall, the studies emphasized that choosing the appropriate cement type and optimizing the mix design can improve the properties of concrete for different applications.
Performance of Self Compacting High Strength Fiber Reinforced Concrete (SCHSFRC)IOSR Journals
In this experimental study the changes on some mechanical properties of self compacting concrete
specimen produced by silica fume, metakaolin, fly ash and steel fibers were investigated. The main objective of
this is to obtain ductile Self Compacting High Strength Concrete (SCHSC) which flows under its own weight
and homogeneity while completely filling any formwork and passing around congested reinforcement. The Self
Compacting High Strength Concrete produced by using silica fume, metakaolin, fly ash, steel fibers and
Polycarboxylatether base superplasticizer. Three types of steel fibers were used in the experiments and volume
fractions of steel fiber were 0.5% to 4.0 %. Addition of silica fume, metakaolin and fly ash into the concrete
were 2.5 %, 2.5 % and 10 % by weight of cement content respectively. Water/cement ratio was 0.29.
Compressive strength and split tensile strength tests were made on hardened concrete specimens.
Impact and Performance of Linen Fiber Reinforced Concrete in Slender ColumnsAJSERJournal
This study was consisted of two phases, revealed the behavior of Self-Compacting Concrete (SCC)
specimens of small-diameter slender column to achieve high quality concrete properties without using concrete
vibrator. The first phase investigated the effect of linen fiber on the rheological properties of SCC using two mixes types:
type I mix: without lime powder, and type II mix: with 20% lime as a replacement of cement content. The linen fiber was
contented of 0, 2, and 4 Kg/m³. In the second phase, the type II mix was used to cast three columns; one with plain SCC
and the other two with 2 and 4 Kg/m³ fiber contents. These columns were cured and cut in a certain manner to obtain 7
cylinders 150 × 300 mm and 8 slices 20 mm thickness. The cylinders were used to measure the distribution of unit
weight, compressive strength, and ultrasonic pulse velocity (UPV) along the column height. The rheological properties
of SCC were reduced with the additives of fibers to the mix constituents, but the properties of Fiber reinforced SelfCompacted Concrete (FSCC) were tested at 4 Kg/m³ fiber content. The distribution of unit weight, compressive strength,
and UPV provided good compaction of concrete. Also, the distribution of coarse aggregate at bottom, middle and top
sections of columns were uniformly distributed.
The document summarizes a literature review on self-compacting concrete (SCC). It lists 16 research papers on SCC, providing the title, authors, year published, journal/publisher, methodology used, and main outcomes for each. The majority of the papers studied the fresh and hardened properties of SCC mixtures containing supplementary cementitious materials like fly ash, slag, or mineral admixtures. Common tests included measuring flowability, passing ability, and compressive strength. Most found that partial replacement of cement with these materials can improve the properties of SCC, though higher replacement rates may negatively impact strength.
This document summarizes a research study on the effect of using electrically precipitated fly ash (EPFA) as a partial replacement for cement in self-compacting concrete (SCC). The study tested SCC mixes with 0-30% EPFA replacement at 5% intervals. Tests were conducted on fresh properties, mechanical properties like compressive strength, and durability properties like rapid chloride permeability and water sorptivity. Results showed that 20% EPFA replacement provided better results than the control SCC mix, improving properties while also providing economic and environmental benefits through reduced cement usage.
Experimental Study on Durability Characteristics of High Performance Concrete...theijes
High performance concrete (HPC) is developed gradually over the last 15 years with respect to production of concrete with higher and higher strength. To enhance the properties such as durability, strength, workability, economy has increased due to the usage of mineral admixtures in making high performance concrete. The scope of the present study is to investigate the effect of mineral admixtures and by-products towards the performance of HPC. An effort has been made to concentrate on the mineral admixture of silica fume towards their pozzolanic reaction and industrial by-product of bottom ash and steel slag towards their hydration reaction can be contributed towards their strength and durability properties. The strength characteristics such as compressive strength, tensile strength and flexural strength were investigated to find the optimum replacement of mineral admixture and by-product admixture. HPC with mineral admixture of silica fume at the replacement levels of 0%, 5%, 10%, 15% & 20% were studied at the age of 28 days and industrial by-products of bottom ash and steel slag aggregate at the replacement level of 10%, 20%, 30%, 40% & 50% were studied at the age of 28 days. There were a total of 15 mixes created with different material contents. Out of 14 were HPC mixes and 1 were conventional concrete mixes. Finally strength has enhanced with the mix of silica fume can replaced by cement with 5% and bottom ash and steel slag can replaced by fine and coarse aggregate with 10% can be achieved higher strength when compared with other percentage of mixes. The combination mixes can be classified as binary and ternary mixes. Binary mixes involved combinations of silica fume and bottom ash (SF+BA), silica fume and steel slag aggregate (SF+SSA), bottom ash and steel slag aggregate (BA+SSA) and Ternary mixes involved combination of three materials such as silica fume, bottom ash and steel slag aggregate (SF+BA+SSA) in High performance concrete. The investigation revealed that the combined use of silica fume, bottom ash and steel slag aggregate improved the mechanical properties of HPC and thus there 3 materials may use as a partial replacement material in making HPC. The durability studies such as acid resistance, salt resistance, sulphate resistance & water absorption were conducted. From the experimental investigation, it was observed that mineral admixture of silica fume and industrial by-products of bottom ash & steel slag aggregate plays a vital role in improving the strength and durability parameter itself.
To Study the Properties of Self-Compacting Concrete Using Recycled Aggregate ...paperpublications3
Abstract: This paper investigates the study of workability and durability characteristics of Self-Compacting Concrete (SCC) with Viscosity Modifying Admixture (VMA), and containing fly ash. The mix design for SCC was arrived as per the Guidelines of European Federation of National Associations Representing for Concrete (EFNARC). In this investigation, SCC was made by usual ingredients such as cement, fine aggregate, coarse aggregate, water, mineral admixture fly ash and demolished concrete at various replacement levels (5%, 10%, 15%, and 20%). To enhance the property of SCC made with the use of demolish concrete and fly ash, glass fiber has been added to the mix. Glass fiber in various % (i.e. 0.15%, 0.20% 0.30%, of Wt. of cement) has been added in the mix which contain demolish concrete and gave highest strength i.e. (10% demolish concrete).
Strength and durability studies on silica fume modified high volume fly ash c...IAEME Publication
This document discusses a study on the strength and durability of silica fume modified high-volume fly ash concrete. Five concrete mixes were tested: a control mix and four mixes where 50% of cement was replaced with fly ash and additional replacement of cement with 5%, 10%, and 15% silica fume. Testing included compressive strength at various ages, rapid chloride permeability, chloride ion diffusion, and carbonation resistance. The addition of silica fume to high-volume fly ash concrete was found to improve mechanical properties and durability compared to fly ash concrete without silica fume.
. effect of different types of cement on fresh and mechanical properties of c...ENGJiidhe
The document reviews several studies that investigated the effect of different cement types on the fresh and mechanical properties of concrete. The cement types investigated included ordinary Portland cement, fly ash-based cement, slag cement, and cement with supplementary materials like silica fume, metakaolin, and polyethylene therephthalate. The studies found that workability generally decreased with the addition of supplementary materials but mechanical properties like compressive strength and durability increased. The performance of concrete depended on factors like water-cement ratio, curing conditions, and the replacement levels of supplementary materials. Overall, the studies emphasized that choosing the appropriate cement type and optimizing the mix design can improve the properties of concrete for different applications.
Performance of Self Compacting High Strength Fiber Reinforced Concrete (SCHSFRC)IOSR Journals
In this experimental study the changes on some mechanical properties of self compacting concrete
specimen produced by silica fume, metakaolin, fly ash and steel fibers were investigated. The main objective of
this is to obtain ductile Self Compacting High Strength Concrete (SCHSC) which flows under its own weight
and homogeneity while completely filling any formwork and passing around congested reinforcement. The Self
Compacting High Strength Concrete produced by using silica fume, metakaolin, fly ash, steel fibers and
Polycarboxylatether base superplasticizer. Three types of steel fibers were used in the experiments and volume
fractions of steel fiber were 0.5% to 4.0 %. Addition of silica fume, metakaolin and fly ash into the concrete
were 2.5 %, 2.5 % and 10 % by weight of cement content respectively. Water/cement ratio was 0.29.
Compressive strength and split tensile strength tests were made on hardened concrete specimens.
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
The document describes an experimental study that evaluated the flexural behavior of steel fiber reinforced high strength self-compacting concrete slabs. Six concrete slabs were tested with varying concrete types (ordinary, self-compacting, high strength self-compacting) and steel fiber volume fractions (0%, 0.75%, 1.5%). Test results found that using self-compacting concrete and adding steel fibers improved flexural resistance and led to more ductile failure. The high strength self-compacting concrete slab with 1.5% steel fibers showed the highest ultimate load capacity, an 18.8% increase over the non-fiber slab. A finite element analysis was able to reasonably model the slab test results.
This study examined the effects of different proportions of light weight expanded clay aggregates on the compressive and flexural strength of concrete. Concrete mixtures were prepared with 0%, 25%, 50%, 75%, and 100% replacement of coarse aggregates with expanded clay aggregates. The mixtures also included 10% silica fume and 1.6% polyvinyl alcohol to replace cement and water. Test results found that compressive and flexural strength decreased as the expanded clay aggregate content increased. However, the densities of the concretes were significantly lower than conventional concrete, indicating light weight concrete is suitable when self-weight needs to be reduced.
This study investigated the effects of using different percentages of expanded clay aggregates (ECA) as a replacement for normal coarse aggregates in concrete. Concrete mixtures were prepared with 0%, 25%, 50%, 75%, and 100% replacement of ECA and tested for compressive strength and flexural strength after 28 days of curing. The results showed that as the percentage of ECA increased, the density and strengths of the concrete decreased. Concretes with higher ECA content achieved lower compressive strengths but still met the requirements for structural lightweight concrete. The study concluded that this lightweight concrete can be used in places where external forces are minimal as its strength is only sufficient to support its own weight.
To Study the Properties of Latex Modified Steel Fibre Reinforced Concretepaperpublications3
Abstract: This journal documents the effects of using steel fibres in Styrene Butadiene Rubber (SBR) latex modified concrete. The study was carried out to record the different properties of steel fibre reinforced latex modified concrete such as compressive strength, split tensile strength and flexural strength. Latex modified concrete is defined as Portland cement and aggregate combined at the time of mixing with polymers that are dispersed in water. This dispersion is called as latex. Polymer when used as an admixture can improve properties like higher strength and lower water permeability than the conventional concrete. Since, concrete is weak in tension, steel fibres have been added to concrete, to improve its characteristics in tension. The polymer concrete specimens with and without fibres and latex were cast and tested to watch the improvement of certain mechanical and physical properties like compressive strengths, tensile strengths, flexural strengths and workability. Styrene Butadiene Rubber Latex polymer and hooked end steel fibres have been used for our study. The percentage of steel fibre used were 0%,0.5%,0.75%,1%,1.25% at an interval of 0.25%. The fraction of steel fibre which gave the best result was taken and latex was varied in percentage 5%, 10%, 15% to obtain maximum strength. In all total 24 specimen cubes (150mm X 150 mm X 150 mm), 24 beam (500mm X 100mm X 100mm) and 24 cylinder specimens (150 mm X 300 mm) were made. The hardened properties of concrete were tested at 28th days.
IRJET- Experimental Investigation on the Behaviour of Strength and Durability...IRJET Journal
This document presents the results of an experimental investigation on the strength and durability of concrete when using a combination of steel fiber, glass fiber, and fly ash. Various concrete mixes were prepared by replacing cement with different percentages (0-30%) of fly ash and adding different volumes (0-1.5%) of steel and glass fibers. The compressive strength, split tensile strength, flexural strength, and workability of the mixes were then tested. The results showed that compressive strength reached its highest when cement was replaced with 10% fly ash and 1.5% fibers were added. Split tensile strength was maximized with 10% fly ash and 1.2% fibers. Flexural strength increased the most with
Development of mix design for high strength Concrete with AdmixturesIOSR Journals
This paper presents the result of mix design developed for high strength concrete with silica fume
and High range water reducing admixture (HRWR). It involves the process of determining experimentally the
most suitable concrete mixes in order to achieve the targeted mean strength. In this research work 53 grade
ordinary Portland cement, the locally available river sand, 10 mm graded coarse aggregate were selected based
on ASTM C 127 standard for determining the relative quantities and proportions for the grade of concrete M60.
For this design ACI 211.4R-93 guidelines were followed. Totally Five mixes were designed one mix was treated
as basic mix with HRWR - 0.5% without silica fume, Four mixes were designed with Micro silica quantities
varied from 5 to 9 percent weight of cementitious materials and HRWR varies between 0.6% to 0.9% with
increment of 0.1% . Each mix 2 numbers of 150mm x 300 mm cylinders were cast then kept in curing tank after
24 hours of time period. After 28 days of curing the specimens were tested and the appropriate mix proportions
were obtained.
IRJET - A Review Paper on Comparative Study of Lightweight Concrete and Reinf...IRJET Journal
This document provides a review of lightweight concrete and compares it to reinforced concrete. It discusses that lightweight concrete has a lower density than conventional concrete, which reduces dead load and transportation costs. The main types of lightweight concrete are no-fines concrete, lightweight aggregate concrete, and aerated concrete. The document summarizes several studies that found lightweight concrete to have lower compressive strength but adequate properties for structural use. It provides information on the density, modulus of elasticity, flexural strength, and other properties of lightweight concrete. The conclusion is that lightweight concrete is an economical alternative to normal weight concrete for construction.
This document discusses a study on the effect of using Sudanese aggregates and supplementary cementitious materials like silica fume and fly ash to produce high strength concrete. Hundreds of concrete specimens with different mixtures of local materials, silica fume, fly ash, and water-cement ratios were tested to determine compressive strength and workability. The results showed that local Sudanese materials can be used to successfully produce concrete with a compressive strength of 80 MPa when combined with supplementary cementitious materials. Water-cement ratio had an inverse relationship with compressive strength. Silica fume improved short and long-term concrete properties while fly ash inversely affected 28-day strength. The study aims to provide insights for producing
Improving the Properties of Self-compacted Concrete with Using Combined Silic...Pouyan Fakharian
The viscosity is the main property of self- compacted concrete (SCC) and using of pozzolan material such as metakaolin (MK) and Silica fume (SF) can help to achieve that goal. The effect of simultaneous substitution of MK and SF instead of cement on the rheological and mechanical properties of self-compacted concrete was experimentally investigated in this paper. Seventeen mix designs were cast with a substitution weight percentage (5, 10, 15, 20 %) in water to adhesive material ratio equal 0.32. All mixes were examined by compressive, tensile strengths and water absorption tests with an appropriate fluidity, without having signs of segregation or instability. The test results were indicated that the SCC mixes containing MK and SF had higher compressive and tensile strengths in comparison with no-pozzolan concrete. The comparison of linear multiple regression techniques (LMRT) and nonlinear multiple regression technique outputs with experimental results showed an appropriate similarity.
IRJET- Effect of Glass Fiber Volume and Mineral Admixture Contents on the Beh...IRJET Journal
This document summarizes research on the effect of glass fiber volume and mineral admixtures on the behavior of high performance fiber reinforced concrete (HPFRC). It discusses how HPFRC was produced using fly ash, metakaolin, and superplasticizer to improve mechanical and durability properties. The mechanical properties tested included compressive, split tensile, and flexural strength at various ages. Durability properties like water absorption, chloride penetration, and acid resistance were also evaluated. The results showed that HPFRC with optimal fiber and mineral admixture contents can achieve high strength and satisfy durability requirements for classification as a high performance cementitious composite.
The Study of Self Healing Properties with High Strength Concreteijtsrd
This document summarizes a study on developing high-strength concrete with self-healing properties. It begins by discussing the use of mineral admixtures and superplasticizers to develop a mix design for high-strength concrete. It then discusses the challenges of cracks in concrete and environmental impacts of cement production. The document proposes using bacteria that can precipitate calcium carbonate to fill cracks and enable self-healing. It outlines experiment methodology including isolating alkali-resistant bacteria from concrete samples and testing their ability to precipitate calcium carbonate. The results of tests on the urease activity of isolated bacteria strains are also summarized.
The International Journal of Engineering & Science is aimed at providing a platform for researchers, engineers, scientists, or educators to publish their original research results, to exchange new ideas, to disseminate information in innovative designs, engineering experiences and technological skills. It is also the Journal's objective to promote engineering and technology education. All papers submitted to the Journal will be blind peer-reviewed. Only original articles will be published.
The papers for publication in The International Journal of Engineering& Science are selected through rigorous peer reviews to ensure originality, timeliness, relevance, and readability.
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
The document summarizes an experimental study on the mechanical behavior of high strength fibre reinforced concrete (HSFRC). Concrete mixes were produced by adding two types of hooked end steel fibres at volume fractions ranging from 0.5% to 4% to a base high strength concrete of grade M80. A total of 147 specimens of cubes, cylinders and prisms were tested to determine the compressive strength, split tensile strength, and flexural strength of the HSFRC mixes. The results indicated that the addition of steel fibres led to significant improvements in the mechanical properties of the high strength concrete. The compressive strength, split tensile strength and flexural strength all increased with the addition of fibres up to an optimal volume
IRJET- Experimental Investigation of Steel Fiber Reinforced Concrete with Par...IRJET Journal
This document discusses an experimental investigation into steel fiber reinforced concrete with partial replacement of coarse aggregate by cupola slag. The following key points are discussed:
1. Steel fibers were added to concrete to improve properties like strength and ductility. Cupola slag, a byproduct from cast iron manufacturing, was used to partially replace coarse aggregate.
2. Tests were conducted to study the effect of adding hooked steel fibers and varying amounts of cupola slag on the mechanical properties of concrete, including compressive strength, split tensile strength, and flexural strength.
3. A literature review presented research on the use of steel fibers to enhance concrete properties and studies investigating the use of cupola slag as a partial replacement for
International Journal of Computational Engineering Research(IJCER) is an intentional online Journal in English monthly publishing journal. This Journal publish original research work that contributes significantly to further the scientific knowledge in engineering and Technology
This document discusses the performance of steel fiber reinforced concrete under elevated temperatures. It begins with an introduction to how elevated temperatures affect the mechanical and physical properties of concrete. The addition of steel fibers is shown to improve the toughness, tensile strength, and cracking behavior of concrete. A literature review found that steel fibers can reduce plastic shrinkage cracking and spalling when concrete is subjected to high temperatures. The document then describes an experimental study that used Box-Behnken design to evaluate the effects of steel fiber percentage (0%, 0.5%, 1%), water-cement ratio (0.35, 0.4, 0.45), and temperature (27°C, 200°C, 400°C) on the
This document reviews the development and use of supplementary cementitious materials (SCMs) in self-compacting concrete (SCC). It summarizes past literature on how various calcium-rich and silica-rich SCMs have been used to improve the properties of SCC. The review focuses on the effects of ultra-fine fly ash (UFFA) on the plastic and hardened properties of SCC. It notes that prior studies have examined the use of SCMs like fly ash, slag, and silica fume to enhance workability and strength but that no comprehensive study has looked at the impact of UFFA specifically. The review proposes that future work should examine how UFFA influences SCC properties using an artificial
This document evaluates the strength parameters of self-compacting concrete incorporated with carbon and glass fibres. It discusses how the concrete was made with various percentages of micro silica and fibres as a replacement for cement. The compressive, tensile, and flexural strength of the concrete mixtures were tested at 7 and 28 days. The results showed that the concrete achieved the highest strength at 0.6% addition of carbon or glass fibres, with carbon fibres performing slightly better. In conclusion, the compressive strength increased by 12% for carbon fibre and 8% for glass fibre mixtures at the 0.6% fibre level.
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
The document describes an experimental study that evaluated the flexural behavior of steel fiber reinforced high strength self-compacting concrete slabs. Six concrete slabs were tested with varying concrete types (ordinary, self-compacting, high strength self-compacting) and steel fiber volume fractions (0%, 0.75%, 1.5%). Test results found that using self-compacting concrete and adding steel fibers improved flexural resistance and led to more ductile failure. The high strength self-compacting concrete slab with 1.5% steel fibers showed the highest ultimate load capacity, an 18.8% increase over the non-fiber slab. A finite element analysis was able to reasonably model the slab test results.
This study examined the effects of different proportions of light weight expanded clay aggregates on the compressive and flexural strength of concrete. Concrete mixtures were prepared with 0%, 25%, 50%, 75%, and 100% replacement of coarse aggregates with expanded clay aggregates. The mixtures also included 10% silica fume and 1.6% polyvinyl alcohol to replace cement and water. Test results found that compressive and flexural strength decreased as the expanded clay aggregate content increased. However, the densities of the concretes were significantly lower than conventional concrete, indicating light weight concrete is suitable when self-weight needs to be reduced.
This study investigated the effects of using different percentages of expanded clay aggregates (ECA) as a replacement for normal coarse aggregates in concrete. Concrete mixtures were prepared with 0%, 25%, 50%, 75%, and 100% replacement of ECA and tested for compressive strength and flexural strength after 28 days of curing. The results showed that as the percentage of ECA increased, the density and strengths of the concrete decreased. Concretes with higher ECA content achieved lower compressive strengths but still met the requirements for structural lightweight concrete. The study concluded that this lightweight concrete can be used in places where external forces are minimal as its strength is only sufficient to support its own weight.
To Study the Properties of Latex Modified Steel Fibre Reinforced Concretepaperpublications3
Abstract: This journal documents the effects of using steel fibres in Styrene Butadiene Rubber (SBR) latex modified concrete. The study was carried out to record the different properties of steel fibre reinforced latex modified concrete such as compressive strength, split tensile strength and flexural strength. Latex modified concrete is defined as Portland cement and aggregate combined at the time of mixing with polymers that are dispersed in water. This dispersion is called as latex. Polymer when used as an admixture can improve properties like higher strength and lower water permeability than the conventional concrete. Since, concrete is weak in tension, steel fibres have been added to concrete, to improve its characteristics in tension. The polymer concrete specimens with and without fibres and latex were cast and tested to watch the improvement of certain mechanical and physical properties like compressive strengths, tensile strengths, flexural strengths and workability. Styrene Butadiene Rubber Latex polymer and hooked end steel fibres have been used for our study. The percentage of steel fibre used were 0%,0.5%,0.75%,1%,1.25% at an interval of 0.25%. The fraction of steel fibre which gave the best result was taken and latex was varied in percentage 5%, 10%, 15% to obtain maximum strength. In all total 24 specimen cubes (150mm X 150 mm X 150 mm), 24 beam (500mm X 100mm X 100mm) and 24 cylinder specimens (150 mm X 300 mm) were made. The hardened properties of concrete were tested at 28th days.
IRJET- Experimental Investigation on the Behaviour of Strength and Durability...IRJET Journal
This document presents the results of an experimental investigation on the strength and durability of concrete when using a combination of steel fiber, glass fiber, and fly ash. Various concrete mixes were prepared by replacing cement with different percentages (0-30%) of fly ash and adding different volumes (0-1.5%) of steel and glass fibers. The compressive strength, split tensile strength, flexural strength, and workability of the mixes were then tested. The results showed that compressive strength reached its highest when cement was replaced with 10% fly ash and 1.5% fibers were added. Split tensile strength was maximized with 10% fly ash and 1.2% fibers. Flexural strength increased the most with
Development of mix design for high strength Concrete with AdmixturesIOSR Journals
This paper presents the result of mix design developed for high strength concrete with silica fume
and High range water reducing admixture (HRWR). It involves the process of determining experimentally the
most suitable concrete mixes in order to achieve the targeted mean strength. In this research work 53 grade
ordinary Portland cement, the locally available river sand, 10 mm graded coarse aggregate were selected based
on ASTM C 127 standard for determining the relative quantities and proportions for the grade of concrete M60.
For this design ACI 211.4R-93 guidelines were followed. Totally Five mixes were designed one mix was treated
as basic mix with HRWR - 0.5% without silica fume, Four mixes were designed with Micro silica quantities
varied from 5 to 9 percent weight of cementitious materials and HRWR varies between 0.6% to 0.9% with
increment of 0.1% . Each mix 2 numbers of 150mm x 300 mm cylinders were cast then kept in curing tank after
24 hours of time period. After 28 days of curing the specimens were tested and the appropriate mix proportions
were obtained.
IRJET - A Review Paper on Comparative Study of Lightweight Concrete and Reinf...IRJET Journal
This document provides a review of lightweight concrete and compares it to reinforced concrete. It discusses that lightweight concrete has a lower density than conventional concrete, which reduces dead load and transportation costs. The main types of lightweight concrete are no-fines concrete, lightweight aggregate concrete, and aerated concrete. The document summarizes several studies that found lightweight concrete to have lower compressive strength but adequate properties for structural use. It provides information on the density, modulus of elasticity, flexural strength, and other properties of lightweight concrete. The conclusion is that lightweight concrete is an economical alternative to normal weight concrete for construction.
This document discusses a study on the effect of using Sudanese aggregates and supplementary cementitious materials like silica fume and fly ash to produce high strength concrete. Hundreds of concrete specimens with different mixtures of local materials, silica fume, fly ash, and water-cement ratios were tested to determine compressive strength and workability. The results showed that local Sudanese materials can be used to successfully produce concrete with a compressive strength of 80 MPa when combined with supplementary cementitious materials. Water-cement ratio had an inverse relationship with compressive strength. Silica fume improved short and long-term concrete properties while fly ash inversely affected 28-day strength. The study aims to provide insights for producing
Improving the Properties of Self-compacted Concrete with Using Combined Silic...Pouyan Fakharian
The viscosity is the main property of self- compacted concrete (SCC) and using of pozzolan material such as metakaolin (MK) and Silica fume (SF) can help to achieve that goal. The effect of simultaneous substitution of MK and SF instead of cement on the rheological and mechanical properties of self-compacted concrete was experimentally investigated in this paper. Seventeen mix designs were cast with a substitution weight percentage (5, 10, 15, 20 %) in water to adhesive material ratio equal 0.32. All mixes were examined by compressive, tensile strengths and water absorption tests with an appropriate fluidity, without having signs of segregation or instability. The test results were indicated that the SCC mixes containing MK and SF had higher compressive and tensile strengths in comparison with no-pozzolan concrete. The comparison of linear multiple regression techniques (LMRT) and nonlinear multiple regression technique outputs with experimental results showed an appropriate similarity.
IRJET- Effect of Glass Fiber Volume and Mineral Admixture Contents on the Beh...IRJET Journal
This document summarizes research on the effect of glass fiber volume and mineral admixtures on the behavior of high performance fiber reinforced concrete (HPFRC). It discusses how HPFRC was produced using fly ash, metakaolin, and superplasticizer to improve mechanical and durability properties. The mechanical properties tested included compressive, split tensile, and flexural strength at various ages. Durability properties like water absorption, chloride penetration, and acid resistance were also evaluated. The results showed that HPFRC with optimal fiber and mineral admixture contents can achieve high strength and satisfy durability requirements for classification as a high performance cementitious composite.
The Study of Self Healing Properties with High Strength Concreteijtsrd
This document summarizes a study on developing high-strength concrete with self-healing properties. It begins by discussing the use of mineral admixtures and superplasticizers to develop a mix design for high-strength concrete. It then discusses the challenges of cracks in concrete and environmental impacts of cement production. The document proposes using bacteria that can precipitate calcium carbonate to fill cracks and enable self-healing. It outlines experiment methodology including isolating alkali-resistant bacteria from concrete samples and testing their ability to precipitate calcium carbonate. The results of tests on the urease activity of isolated bacteria strains are also summarized.
The International Journal of Engineering & Science is aimed at providing a platform for researchers, engineers, scientists, or educators to publish their original research results, to exchange new ideas, to disseminate information in innovative designs, engineering experiences and technological skills. It is also the Journal's objective to promote engineering and technology education. All papers submitted to the Journal will be blind peer-reviewed. Only original articles will be published.
The papers for publication in The International Journal of Engineering& Science are selected through rigorous peer reviews to ensure originality, timeliness, relevance, and readability.
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
The document summarizes an experimental study on the mechanical behavior of high strength fibre reinforced concrete (HSFRC). Concrete mixes were produced by adding two types of hooked end steel fibres at volume fractions ranging from 0.5% to 4% to a base high strength concrete of grade M80. A total of 147 specimens of cubes, cylinders and prisms were tested to determine the compressive strength, split tensile strength, and flexural strength of the HSFRC mixes. The results indicated that the addition of steel fibres led to significant improvements in the mechanical properties of the high strength concrete. The compressive strength, split tensile strength and flexural strength all increased with the addition of fibres up to an optimal volume
IRJET- Experimental Investigation of Steel Fiber Reinforced Concrete with Par...IRJET Journal
This document discusses an experimental investigation into steel fiber reinforced concrete with partial replacement of coarse aggregate by cupola slag. The following key points are discussed:
1. Steel fibers were added to concrete to improve properties like strength and ductility. Cupola slag, a byproduct from cast iron manufacturing, was used to partially replace coarse aggregate.
2. Tests were conducted to study the effect of adding hooked steel fibers and varying amounts of cupola slag on the mechanical properties of concrete, including compressive strength, split tensile strength, and flexural strength.
3. A literature review presented research on the use of steel fibers to enhance concrete properties and studies investigating the use of cupola slag as a partial replacement for
International Journal of Computational Engineering Research(IJCER) is an intentional online Journal in English monthly publishing journal. This Journal publish original research work that contributes significantly to further the scientific knowledge in engineering and Technology
This document discusses the performance of steel fiber reinforced concrete under elevated temperatures. It begins with an introduction to how elevated temperatures affect the mechanical and physical properties of concrete. The addition of steel fibers is shown to improve the toughness, tensile strength, and cracking behavior of concrete. A literature review found that steel fibers can reduce plastic shrinkage cracking and spalling when concrete is subjected to high temperatures. The document then describes an experimental study that used Box-Behnken design to evaluate the effects of steel fiber percentage (0%, 0.5%, 1%), water-cement ratio (0.35, 0.4, 0.45), and temperature (27°C, 200°C, 400°C) on the
This document reviews the development and use of supplementary cementitious materials (SCMs) in self-compacting concrete (SCC). It summarizes past literature on how various calcium-rich and silica-rich SCMs have been used to improve the properties of SCC. The review focuses on the effects of ultra-fine fly ash (UFFA) on the plastic and hardened properties of SCC. It notes that prior studies have examined the use of SCMs like fly ash, slag, and silica fume to enhance workability and strength but that no comprehensive study has looked at the impact of UFFA specifically. The review proposes that future work should examine how UFFA influences SCC properties using an artificial
This document evaluates the strength parameters of self-compacting concrete incorporated with carbon and glass fibres. It discusses how the concrete was made with various percentages of micro silica and fibres as a replacement for cement. The compressive, tensile, and flexural strength of the concrete mixtures were tested at 7 and 28 days. The results showed that the concrete achieved the highest strength at 0.6% addition of carbon or glass fibres, with carbon fibres performing slightly better. In conclusion, the compressive strength increased by 12% for carbon fibre and 8% for glass fibre mixtures at the 0.6% fibre level.
This document discusses the effect of rheological active additives on the properties of self-compacting concrete. Stone powders from local mountain rocks were used to increase the rheological matrix and fluidity of self-compacting concrete mixtures. Plasticizers were used to regulate the properties of cement-based mixtures. The flow rate of cement suspensions and spread of mortars and concretes were evaluated with different testing methods. Results showed that limestone powder was more effective than other stone powders at improving compressive strength when added at 40% to concrete mixtures. The optimal quantities of rheological additives and plasticizers were identified to produce high-strength self-compacting concrete.
This document is the proceedings of the 2nd International Professional Doctorate and Postgraduate Symposium held at Universiti Teknologi Malaysia on September 25, 2021. It contains abstracts from various papers presented at the symposium covering topics such as machine learning, architecture, occupational health and safety, education, supply chain management, and more. The proceedings were organized by the School of Graduate Studies and Postgraduate Student Society of Universiti Teknologi Malaysia.
This study investigates the synergistic effects of combining fly ash and silica fume to produce high-strength self-compacting cementitious composites. Seven mixtures were prepared with varying amounts of fly ash (17.5-25%) and silica fume (1.25-7.5%) as a replacement for ordinary portland cement. The mixtures were tested for rheological properties in the fresh state and mechanical properties like compressive strength and ultrasonic pulse velocity in the hardened state. The results showed that a combination of 80% fly ash and 20% silica fume produced the highest flowability. For superior mechanical properties, the optimum mixture contained 80% cement, 17.5% fly ash and 2
View of Synergetic Effect of Met kaolin for Developing Fast Setting Early Str...Muthumari Ganesan
The document discusses the benefits of exercise for mental health. Regular physical activity can help reduce anxiety and depression and improve mood and cognitive functioning. Exercise causes chemical changes in the brain that may help protect against mental illness and improve symptoms.
The document discusses the use of copper slag as a supplementary cementitious material in high strength self-compacting concrete. Twelve concrete mixes were prepared with 0-20% fly ash replacement of cement and 10-100% copper slag replacement of fine aggregate. The fresh and mechanical properties of the mixes were evaluated up to 180 days. The results showed that workability improved with increasing copper slag content due to its glassy texture. The 40% copper slag mix achieved the maximum compressive strength. Copper slag also reduced chloride penetration and improved concrete quality according to tests. However, sulfate immersion increased weight but reduced strength over time. Overall, the study found that copper slag can be used as a sustainable material to develop high performance self-
The document presents an experimental study that evaluated the residual compressive behavior of self-compacting concrete (SCC) mixes exposed to high temperatures up to 600°C. Ten SCC mixes were tested that varied the type and amount of mineral additives used as partial replacements for cement by weight, including metakaolin (5-15%), fly ash (20-30%), and limestone (5-15%). Testing of the mixes included compressive strength, stress-strain behavior, modulus of elasticity, and strain at peak stress at room temperature and after high temperature exposure. The results showed a significant decrease in mechanical properties for all mixes after 200°C, with the mineral additives affecting the variations in residual strength by 24%
The document summarizes research into developing sustainable high-performance self-compacting concrete using ladle slag as a cement replacement. Ladle slag, a steel industry waste material, was used to replace cement at levels of 5%, 10%, 15% and 25% in self-compacting concrete mixtures. The fresh properties, mechanical properties such as compressive and splitting tensile strength, and simple durability properties of the mixtures were evaluated based on standard tests and compared to a control mixture without ladle slag. The results generally showed improvements in properties for replacements up to 15% ladle slag compared to the control mixture. The research aims to evaluate the performance of ladle slag as a supplementary cementitious material in producing sustainable high-performance
This document discusses a research study on developing high-strength self-compacting concrete using supplementary cementitious materials. The study aims to produce self-compacting concrete with high compressive strength using silica fume and fly ash as partial replacements for cement. The laboratory tests evaluated the fresh and hardened properties of self-compacting concrete mixes with binary and ternary combinations of silica fume and fly ash at different replacement levels. The results showed that both the fresh and hardened properties depended on the use of supplementary cementitious materials. Compressive, split tensile and flexural strengths significantly increased for mixes containing supplementary cementitious materials. The optimum replacement levels for high strength self-compacting concrete were found to be 10%
Architectural and constructions management experience since 2003 including 18 years located in UAE.
Coordinate and oversee all technical activities relating to architectural and construction projects,
including directing the design team, reviewing drafts and computer models, and approving design
changes.
Organize and typically develop, and review building plans, ensuring that a project meets all safety and
environmental standards.
Prepare feasibility studies, construction contracts, and tender documents with specifications and
tender analyses.
Consulting with clients, work on formulating equipment and labor cost estimates, ensuring a project
meets environmental, safety, structural, zoning, and aesthetic standards.
Monitoring the progress of a project to assess whether or not it is in compliance with building plans
and project deadlines.
Attention to detail, exceptional time management, and strong problem-solving and communication
skills are required for this role.
Decormart Studio is widely recognized as one of the best interior designers in Bangalore, known for their exceptional design expertise and ability to create stunning, functional spaces. With a strong focus on client preferences and timely project delivery, Decormart Studio has built a solid reputation for their innovative and personalized approach to interior design.
Explore the essential graphic design tools and software that can elevate your creative projects. Discover industry favorites and innovative solutions for stunning design results.
Visual Style and Aesthetics: Basics of Visual Design
Visual Design for Enterprise Applications
Range of Visual Styles.
Mobile Interfaces:
Challenges and Opportunities of Mobile Design
Approach to Mobile Design
Patterns
Connect Conference 2022: Passive House - Economic and Environmental Solution...TE Studio
Passive House: The Economic and Environmental Solution for Sustainable Real Estate. Lecture by Tim Eian of TE Studio Passive House Design in November 2022 in Minneapolis.
- The Built Environment
- Let's imagine the perfect building
- The Passive House standard
- Why Passive House targets
- Clean Energy Plans?!
- How does Passive House compare and fit in?
- The business case for Passive House real estate
- Tools to quantify the value of Passive House
- What can I do?
- Resources
Fonts play a crucial role in both User Interface (UI) and User Experience (UX) design. They affect readability, accessibility, aesthetics, and overall user perception.
Practical eLearning Makeovers for EveryoneBianca Woods
Welcome to Practical eLearning Makeovers for Everyone. In this presentation, we’ll take a look at a bunch of easy-to-use visual design tips and tricks. And we’ll do this by using them to spruce up some eLearning screens that are in dire need of a new look.
PDF SubmissionDigital Marketing Institute in NoidaPoojaSaini954651
https://www.safalta.com/online-digital-marketing/advance-digital-marketing-training-in-noidaTop Digital Marketing Institute in Noida: Boost Your Career Fast
[3:29 am, 30/05/2024] +91 83818 43552: Safalta Digital Marketing Institute in Noida also provides advanced classes for individuals seeking to develop their expertise and skills in this field. These classes, led by industry experts with vast experience, focus on specific aspects of digital marketing such as advanced SEO strategies, sophisticated content creation techniques, and data-driven analytics.
2. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2084
Various types of filler have been frequently employed in SCC as a partial cement substitute in recent years. SCC
could become a more sustainable material as a result of this substitution [4]. SCC's high flow and resistance to
segregation can be accomplished by using a considerable amount of super-plasticizer and filler materials. Though a
variety of filler materials have been utilized in SCC production, the most typically used fillers include fly ash, silica
fume, iron slag etc. [5]. As a partial substitute for cement, SCC produced with micro-fillers and mineral admixtures
becomes cost effective [6]. Several studies have studied the influence of mineral additives on the fresh and hardening
properties of SCC [7-10]. When compared to ordinary concrete created with vibrators, SCC is typically made with a
lower water cement ratio, resulting in higher strength, lower permeability, and greater durability. The inclusion of
fibers improves SCC's characteristics even more. The fibers act as crack arresters, bridging cracks and preventing
crack growth [11]. Due to the addition of fibers, FR-SCC combines the benefits of SCC in the fresh state with
increased performance in the hardened state [12-14]. With the inclusion of fibers, however, the workability of SCC
decreases, and this decrease is depending on the type, shape, size, and dosage of fibers utilized [15]. Researchers [16,
17] added steel fibers to SCC and found that, although having a lower shear strength than conventional concrete, SCC
with fibers achieved resistance values comparable to traditional vibrated concrete.
However, in dense concrete mixes, such as high strength concrete, or if the concrete is exposed to extremely high
temperatures, the pore pressure created can be extremely damaging to the concrete matrix, resulting in material failure
through spalling [18]. Adding PP and steel fibers to concrete lessens these negative impacts while also improving its
mechanical properties at high temperatures [19-21].
Furthermore, because SCC has a tiny pore structure, it is susceptible to substantial degradation and violent spalling
when exposed to high temperatures [22]. The influence of higher temperature has primarily been examined on vibrated
and high-performance concretes to date. The limited investigations on SCC exposed to high temperatures indicate a
loss in strength as well as an increased danger of spalling [23-27], or behavior identical to vibrated concrete [28].
Despite the significant uncertainties and the growing usage of SCC in a variety of applications, the temperature
behavior of SCC has not been adequately researched, and the processes involved are not completely understood.
The goal of this research is to assess the fresh and hardened properties of SCC made from locally available
materials. This research also considers the effects of steel, PP, and hybrid fibers on the same properties. In addition,
the mechanical properties of SCC specimens (with and without fibers) at high temperatures up to 800 ° C for one hour,
including compressive, tensile, and flexural strengths, are the focus of this research.
In this work, section 2 refers to the experimental program used (materials and methods and Mixing, moulding and
curing) to produce SCC. Section 3 refers to the results obtained from this study for fresh concrete (slump flow and
T50 slump flow time, L-box test and screen stability (GTM)) and hardened concrete (residual Compressive Strength,
spalling, splitting Tensile Strength, flexural strength, ratio for mass losses and velocity of ultrasonic pulses (UPV))
under the influence of room temperature and high temperatures and discussion these results. The fourth part refers to
the conclusions summarized from this study.
2. Materials and Methods
Ordinary Portland cement, silica fume (SF), aggregate (fine and coarse), water, super-plasticizer, and fibers (steel
or polypropylene) are the mixture components. Table 1 describes the proportions of the SCC mix, the components of
the SCC mix and their amounts. Natural sand with a maximum size of 4 mm and broken dolomite with a maximum
size of 9.5 mm are used as coarse aggregates. The fine and coarse aggregate grain size distributions are depicted in
Figure 1. A 25 per cent proportion of silica fume were added by cement weight. Silica fumes, specific gravity 2.1,
specific area 172000 cm2
/ g (production data sheets). Figure 2 shows the particle size distribution of silica fume. In
this study, a locally developed third generation super-plasticizer called Visco-Crete 3425 was used to help improve
concrete workability without water added and to help fine particles occupy the pore space and minimize the amount of
mixing water. This is a modified polycarboxylate aqueous solution, with a specific gravity of 1.08. It is ASTM C494
compliant type G and F [29]. Steel fibers with a hooked end, 25 mm length, 80 μm diameter, and 7.85 g/cm3
density,
and polypropylene fibers with a 12 mm length, 18 μm diameter, and 0.91 g / cm3
density, were employed. In this case,
tap water converted into used during mixing and curing phases for the concrete.
Four forms of mixture concrete have been designed: control mix (SCC) has been made without adding fibers,
mixture contains 1% polypropylene fibers (SCC-PPF), mixture contains 1% steel fibers (SCC-StF), and mixture contains
hybrid fibers 0.5% for both steel and polypropylene fibers (SCC-StF & PPF) by concrete volume. Figure 3 summarizes
the testing program used to meet the goals of this research.
All mixtures were made with generic Portland cement weighing 420 kg/m3
and containing 25, 1, and 45 percent
silica fume, super-plasticizer, and water by weight, respectively.
3. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2085
Figure 1. Grading curve of a) fine aggregate, b) coarse aggregate
Figure 2. Particle size distribution of silica fume (source: from supplier)
Table 1. The constituents of the mixture are per kg/m3
Mix No. Cement
Silica
fume
Aggregate
Water
Super-
Plasticizer
Fibers
Coarse Fine Steel PPF
SCC 420 105 810.58 810.58 189 4.2 0 0
SCC- PPF 420 105 755.56 755.56 189 4.2 0 0.91
SCC-SF 420 105 797.48 797.48 189 4.2 78.5 0
SCC-SF & PPF 420 105 776.7 776.7 189 4.2 40 0.45
3. Mixing, Moulding and Curing
In dry conditions, Portland cement, aggregate and silica fumes were mixed, then water and super-plasticizer were
added. Fibers were introduced to dry materials before water, and additives were applied in the case of FR-SCC. For
compressive testing, a (10×10×10) cm volume cube, a 10 cm diameter cylinder and a 20 cm height cylinder for
tension test, as well as a (10×10×30) cm bending strength prism were applied. The slump-flow experiment, L-box,
time series T50 and stability of the GTM screen were measured to investigate the fresh characteristics of SCC (filling
strength, passing capacity and segregation resistance).
Flow-chart describing the SCC study methodology.
0
10
20
30
40
50
60
70
80
90
100
0.1 1 10
Passing
percentage
%
a) Sieve size (mm)
ASTM Max Limits for coares sand
ASTM Min Limits for coares sand
Used sand 0
10
20
30
40
50
60
70
80
90
100
1 10 100
passing
percentage
%
b) Sieve size (mm)
4. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2086
Figure 3. Overview of the Experimental Program
4. Results and Discussion
4.1. Fresh Properties of SCC
The behavior of SCC in its fresh condition is defined, categorised, and determined. The stated principles mentioned
in standards such as EFNARC are one approach to identify the behavior of concrete and determine whether it fits
certain specific requirements for its use or not. For all mixtures in this investigation, the slump flow, T50, L-box test,
and Screen stability (GTM) were utilized, as shown in Table 2, which is based on the results of the four tests and the
limits of EFNARC listed [30]. The values of (D) represent the greatest spread (slump flow ultimate diameter) in
Figures 4–7, whereas T50 values represent the time necessary for the concrete flow to reach a circle with a diameter of
50 cm. The blocking ratio is represented by (H2/H1). In Figures 1 and 3, D and (H2/H1) are plotted in descending order,
while T50 is plotted in ascending order in Figure 2.
Verify Performance of concrete in Laboratory
Evaluate alternative
Materials
Design and adjust Mix Composition
Verify or adjust performance in Laboratory
Producing SCC
Mix design procedure
Set required Performance
Select Materials (from site)
Experimental Program
Not ok
Fresh Properties of SCC
T50 cm (second)
Slump-flow (mm)
L-box (H2/H1)
GTM (%)
Hardening
properties of SCC
Residual Compressive strength at:
25, 200, 400, 600 and 800 °C
Flexural strength at:
25, 200, 400, 600 and 800 °C
Splitting strength at:
25, 200, 400, 600 and 800 °C
1) Compressive strength
2) Mass loss ratio
3) Ultrasonic pulses Velocity (UPV)
1) Splitting strength
2) Mass loss ratio
3) Ultrasonic pulses Velocity (UPV)
1) Flexural strength
2) Mass loss ratio
3) Ultrasonic pulses Velocity (UPV)
Spalling
5. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2087
The ability of the SCC to flow unrestrictedly to fill the mold with its full volume, based solely on the influence of
its weight, is referred as filling ability (unconstrained flowability). Passing ability (confined flowability) is defined as
the ability of concrete to flow and pass through a narrow space, similar to the normal situation during casting, as well
as the influence of reinforcing steel and its ratios through the mold and the space left behind, allowing concrete to flow
uninterrupted. Segregation resistance (stability) is measured by the amount of time it takes to keep concrete uniform
and homogeneous throughout transit and casting.
Table 2. Results of fresh SCC properties
Mix No. Slump-flow (mm) T50 cm second L-box (H2/H1) GTM (%)
SCC 780 2.3 0.96 11.1
SCC-PPF 690 3.6 0.83 9.0
SCC-StF 710 3.3 0.90 9.1
SCC-StF & PPF 700 4.0 0.82 8.6
Limit of EFNARC (2005) [30] 650-800 2-5 0.8-1.0 ≤ 15
Figure 4. Slump Flow Diameter (mm) Figure 5. Time Required Passing (50 cm Dia.) Circle (T50)
Figure 6. Fiber content impact on blocking ratio Figure 7. Fiber content impact on segregation ratio
The viscosity of SCC can be calculated using the T50 time or estimated using the V-funnel flow time. The time
amount collected does not calculate the viscosity of SCC, but it is associated with it by defining the flow rate.
Concrete with a medium viscosity should flow quickly at first and then halt. Concrete with a high viscosity may
proceed to creep forward over a lengthy period of time. It is obvious from Figures 4 to 7 that:
All of the mixtures meet the SCC standards outlined in the EFNARC specifications. As a result, all of the
mixtures are deemed to have high consistency and workability in terms of filling and passing ability.
It is obvious that the SCC mix (without fibers) is a low viscosity concrete, but the mix containing steel fibers is a
high viscosity concrete. This behavior can be attributed to increased friction between fibers and aggregates
particles in addition to the increased viscosity resulting from the addition of fibers [31].
There is no segregation or bleeding when the flow is flowing or when the flow is stopped.
It is clear from Table 2 and Figures 4 to7 that adding PP, steel, and hybrid PP and steel fibers with 1, 1 and 0.5 %
decreases the slump flow by 11.5, 9 and 10%, increases T50 by 56.5, 43, and 74 %, reduces L-box by 13.5, 6 and
640
660
680
700
720
740
760
780
800
SCC SCC-PPF SCC-StF SCC-StF & PPF
Slump
flow
cm
Mix No.
0
0.5
1
1.5
2
2.5
3
3.5
4
4.5
SCC SCC-PPF SCC-StF SCC-StF & PPF
T50
cm
second
Mix No.
0.75
0.8
0.85
0.9
0.95
1
SCC SCC-PPF SCC-StF SCC-StF & PPF
L-box
(H
2
/H
1
)
Mix No.
0
2
4
6
8
10
12
SCC SCC-PPF SCC-StF SCC-StF & PPF
GMT
%
Mix No.
6. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2088
14.6 %, and reduces GTM by 19, 18 and 22.5 %. This loss of workability is caused by the presence of steel or PP
fibers, which act as a barrier to the movement of mix components. The properties of the concrete are listed I
Table 2, and it can only be classed and represented as an SCC if it fits all of the standards. These results are in
accordance with those of other researchers [32, 33].
4.2. Test Procedure
Both mass and velocity of the ultra-sonic pulse were determined after the end of the sample processing time and
before heating in the electrical furnace. Samples were heated at 5 °C per minute up to 200, 400, 600 and 800 °C using
an electric oven. The temperature was then kept constant for an hour to guarantee that the specimens were all at the
same temperature (Figure 8).
Figure 8. The electric oven used for heating the specimens
The final stage of the cycles involved a cooling down to room temperature. Figure 8 depicts the electric oven that
was used to heat the specimens. The samples were removed from the oven and then tested for ultrasonic wave
frequency, mass loss, compressive, tensile and flexural strengths.
4.3. Hardened Properties
4.3.1. Residual Compressive Strength
For all (100 mm) cubes, the compressive strength test was performed in accordance with ASTM C109-20 [34]. The
compressive strength of each mix at each stage of heating was determined using three cubes. The following points can
be noted from the test results shown in Table 3 and Figures 9 and 10:
Behavior of unheated SCC: The compressive strength of SCC specimens containing PP fibers reduced at room
temperature. When compared to reference mixtures without fibers, the strength loss is roughly 2.7 %. This could
be attributed to the high air content and big volume of voids percentage in the mixes as a result of adding a high
volume fraction of PP fibers. However, when compared to reference mixes without fibers, the compressive
strength of SCC containing steel fibers and hybrid PP and steel fibers increased by about 15% and 2%,
respectively, by the total volume. Steel fibers were a powerful material due to their higher stiffness, which
improved compressive strength. As a result, steel fibers can withstand a higher load, have a higher carrying
capacity, and provide better performance for SCC mixes. The enhanced interface between the aggregate and
paste due to the absence of vibration may also account for the increased compressive strength of SCC. These
results are consistent with those of other researchers [35, 36]. The failure of SCC specimens containing fibers
proceeded gradually, and the fibers connected the segments together. In SCC specimens lacking fibers, however,
failure occurs rapidly, and the cube splits into numerous fragments. The shape of failure is depicted in Figure 11.
Behavior of SCC/FR-SCC specimens after heating: The compressive strength of SCC without fibers, SCC with
steel fibers, and SCC with hybrid fibers improved by 1.8, 3.8, and 4.3 %, respectively, when the temperature was
increased to 200 °C. As the temperature climbs to 200 °C, increasing cement hydration could be the main cause
of enhanced compressive strength. However, SCC incorporating PP fibers had a 13.6 % reduction in
compressive strength. Above 300 °C, the mechanical and physical characteristics of the SCC and FR-SCC
specimens rapidly deteriorated. Mechanical properties were related with physical properties in specimens heated
to 600 °C (appearance of cracking). The strength diminished as the temperature rose. When the furnace
temperature is (400, 600, and 800) °C, the compressive strength of SCC specimens (without fibers) decreases by
about (38, 73.5, 86.7) %, SCC specimens with PP fibers decrease by about (45.5, 68, 87.5) %, SCC specimens
with steel fibers decrease by about (23, 54, 84.8) %, and SCC specimens with hybrid fibers decrease by about
(43, 65, 85) %. The breakdown of the interfacial link caused by incompatible volume changes between cement
paste and aggregate during heating and cooling is blamed for the loss in concrete's compressive strength. When
the temperature rises over (400°C), the calcium hydroxide dehydrates, causing the cement paste to shrink. At
around (600°C), many quartz-like aggregates undergo a crystalline transition, causing significant expansion and
fracture of the concrete [12].
7. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2089
The drop in compressive strength in specimens containing 1.0 % PP fibers is greater than in SCC specimens
(without fibers). When the heating temperature is (200, 400, 600, and 800) °C, this reduction is roughly (21,
16.7, 9.1) % when compared to SCC specimens (without fibers). This could be due to the combined effect of the
high temperature, which alters the structure of concrete as shown in point above, and the melting point of PP
fibers (particularly at 400 and 600 °C), which results in a significant number of weak places between concrete
materials. These findings are consistent with those of other researchers [37, 38].
When the heating temperature is (200, 400, 600, and 800) °C, the compressive strength of specimens having 1.0
% steel fibers and specimens containing hybrid (0.5% steel + 0.5% PP) fibers is more than that of SCC
specimens (without fibers). This increase is approximately (15, 42.8, 100, 33) % and (4.3, 7.6, 33.3, 16.7) %,
respectively. Steel fibers improve the load-carrying capacity of the SCC matrix when exposed to tensile stresses,
which explains the improvement in mechanical properties of SCC. Steel fibers play a function in preventing
cracking and reducing the severe damage caused by high temperatures, which can influence all mechanical
properties of concrete. The fibers perform well until the concrete reaches 700°C, after which it becomes brittle,
crumbly, and loses its bonding strength with the fibers. Concrete expansion during heating, vapor pressure from
water gel and holes, and the decomposition of cement-hydrating components are all elements that contribute to
the formation of fractures [39].
Table 3. Compressive strength values after 28 days of cure for all SCC mixtures (MPa)
Mix No.
Compressive strength at high temperature (MPa)
25°C 200°C 400°C 600°C 800°C
SCC 45.2 (1) 46 (1.02) 28 (0.62) 12 (0.27) 6 (0.13)
SCC-PPF 44 (1) 38 (0.86) 24 (0.55) 14 (0.32) 5.5 (0.13)
SCC-StF 52 (1) 54 (1.04) 40 (0.77) 24 (0.46) 8 (0.15)
SCC-StF & PPF 46 (1) 48 (1.04) 26 (0.57) 16 (0.35) 7 (0.15)
Note: Bracket results for the different SCC mixes indicate the relative compressive strength
Figure 9. Results of compressive strength of different SCC
mixes after high temperature exposure
Figure 10. Effect of fiber type on the compressive strength for
different types of SCC mixes
Specimens without fiber Specimens with fiber
Figure 11. Modes of Failure
Figures 12 to 14 show a scanning electron microscope (SEM) micrographs of several SCC samples at high
temperatures. SCC samples decomposed at temperatures beyond 800 ℃. SEM pictures of SCC (without fibers) mix at
20, 200 and 400 °C are shown in Figure 12. SEM micrographs of SCC with PP fibers samples at 200, 400 and 600 °C
are shown in Figures 13a, b and c. When heated to 200°C, the rigid structure of polypropylene fibers was lost. Figure
13c shows SEM observations of samples that were subjected to 600 °C. Polypropylene fibers melt and volatilize easily
at this temperature, resulting in more holes and narrow channels in the mortar. Figure 14a demonstrates SEM analysis
of fracture surface for the distribution of steel and PP fibres in the SCC matrix (samples with hybrid fibers) after the
test at room temperature. The failure pattern of steel fibre is mainly pulled out from the matrix (Figure 14b), PP fibres
are partly pulled out and partly broken down (Figure 14c).
0
10
20
30
40
50
60
25 200 400 600 800
Compressive
strength,
MPa
Temperatur °C
SCC
SCC-PPF
SCC-StF
SCC-StF & PPF
40
42
44
46
48
50
52
54
SCC SCC-PPF SCC-StF SCC-StF & PPF
Compressive
strength,
MPa
Mix No.
8. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2090
(a) (b) (c)
Figure 12. SEM pictures of SCC samples, (a) at 20 °C, (b) at 200 °C and (c) at 400 °C
(a) (b) (c)
Figure 13. SEM pictures of samples of SCC with PP fibers (a) at 200° C, (b) at 400 ° C, (c) at 600 ° C
(a) (b) (c)
Figure 14. SEM pictures of samples SCC matrix contain hybrid fibers (a) at room temp. and (b) failure pattern of steel and
(c) failure pattern of PP fibers at 200°C
Spalling
After being exposed to high temperatures, the specimens were submitted to a comprehensive visual examination to
assess visible symptoms of cracking and spalling on their surfaces. There was no noticeable cracking or breakage in
specimens with temperatures between 200-400 °C. At high temperatures, Figure 15 depicts the surface feature of SCC
specimens with and without fibres. At around 600 °C, hairline cracks started to form in large numbers. Just a little
degree of spalling was apparent on the corners and edges of certain specimens at 600 °C. Whenever the furnace
temperature is between 425 and 475 °C, explosive spalling occurs in SCC samples and this observation agrees with
Kanema [40]. Low permeability is linked to a dense microstructure in concrete, which inhibits water vapors from
dissipating due to heat, resulting in greater pore pressure.
Figure 15 shows that SCC samples with steel fibers suffers far less damage and spalling than SCC mixture. At
elevated temperatures, silica fume can limit the development of cracks and bridge thermal cracks by mitigating
concrete expansion owing to fast temperature changes and reducing wide temperature gradients due to the increased
heat transfer coefficient [41]. In the SCC with PP fibers samples, the polypropylene fibers minimized the potential of
explosive spalling. This could be because the PP fibers melt and evaporate during the rapid temperature increase
procedure, causing micro channels to emerge in the concrete. As a result, capillary vapor tension can be reduced and
discharged, that could explain why the SSC with PP fibers did not burst. At 800 °C, all of the samples displayed
evident spalling at the corners and edges. The concretes containing steel fibers experienced no extensive cracking and
spalling. Steel fiber-enhanced concrete did not crack or spall as much as other concretes.
9. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2091
Figure 15. Surface behavior of SCC samples in 200, 400, 600 and 800 °C with and without fibres
4.3.2. Splitting Tensile Strength
The tensile strength test was carried out according to ASTM C496 [42], for all (10×20 mm) cylinders. Because
concrete isn't usually built to withstand direct stress, knowing its tensile strength might help you estimate the load that
will cause cracking. The absence of cracks is critical for maintaining a concrete structure's continuity and, in many
situations, preventing corrosion [43]. Tensile strength is an essential factor in the creation of cracks and, as a
consequence, in the prediction of concrete durability. Table 5 and Figures 16 and 17 show the test results of tensile
strength of all SCC specimens. From the results, the following points are observed:
Behavior of unheated SCC: Tensile strength increased by roughly 10, 40, 15% in SCC specimens including (PP,
steel, hybrid PP and steel) fibers, while compressive strength increased by 2.7, 15, 1.8% in comparison to
reference mixes without fibers. Better homogeneity from vibration-free production may also contribute to
increased splitting tensile strength. These results are consistent with those of other researchers [22, 36]. Fibers
help hold the cylinder parts together after they fail in specimens containing fibers, preserving the entire member
and connection integrity. The failure shape is depicted in Figure 11.
Behavior of SCC/FR-SCC specimens after heating: When the temperature was raised to 200 °C, the tensile
strength of SCC without fibers, SCC with steel fibers, and SCC with hybrid fibers improved by about 5, 0.0,
7.1, and 4.3%, respectively. As the temperature climbs to 200 °C, increasing cement hydration may be the
primary cause of higher tensile strength. In specimens exposed to high temperatures, there is a decrease in
tensile strength. As the furnace temperature is 200, 400, and 600 °C, the tensile strength of SCC specimens
(without fibers) decreases by around 5, 40, 89.5%, and SCC specimens with PP fibers decreases by about 0, 41,
91% when compared to specimens still at room temperature. In SCC specimens with steel fibers, the tensile
strength decreases by around 7.1, 67.9% at 400 and 600 °C, and by about 13, 67.4% in SCC specimens with
hybrid fibers, compared to specimens still at ambient temperature. The difference in thermal expansion between
the cement paste and the aggregates, as well as the dryness of the cement paste and aggregate disintegration,
may all play a role in the loss of strength [44].
It is observed that the increase in tensile strength is higher in specimens containing 1.0 % PP fibers, 1.0 % steel
fibers, and (0.5% steel + 0.5% PP) hybrid fibers by total volume than in SCC specimens (without fibers). As the
furnace temperature is 200, 400, and 600 °C, this increase is approximately (4.8, 8.3, 4.8) %, (42.9, 117, 329)
%, and (14.3, 66.7, 257) %, respectively, when compared to specimens without fibers. This could be due to the
effect of the fibers, which alters the structure of concrete as shown in compressive strength [39].
Table 4. Tensile strength values after 28 days of cure for all SCC mixtures (MPa)
Mix
Tensile strength at elevated temperature (MPa)
25°C 200°C 400°C 600°C
SCC 4.0 4.20 2.40 0.42
SCC-PPF 4.40 4.40 2.60 0.40
SCC-StF 5.60 6.00 5.20 1.8
SCC-StF & PPF 4.60 4.80 4.0 1.5
10. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2092
Figure 16. Values of tensile strength for all Mixes (MPa) at
different temperatures
Figure 17. Values of tensile strength for all Mixes (MPa)
4.3.3. Flexural Strength
The flexural strength test was carried out according to ASTM C293 [45]. A simple concrete prisms was subjected
to flexural testing in this study. Prisms measuring 10×10×30 mm were used to measure flexural strength. The cracks
begins in the tension surface within the middle third of the span length in all specimens using the following
relationship:
R=PL/bd2
(1)
Table 5 and Figures 18 and 19 show the test results of flexural strength of all SCC specimens. From the results, the
following points are observed:
Behavior of unheated SCC: As compressive strength increased by 2.7, 15, 1.8 % at room temperature in SCC
specimens having (PP, steel, hybrid PP and steel) fibers, flexural strength increased by roughly 17.3, 42, 32.2
%, respectively, when compared to reference mixes without fibers. The restricting of cracks by fibers may
account for the increase in flexural strength of SCC. These findings are consistent with those of other
researchers [22, 35]. Fibers aid to hold prism elements together after they fail in specimens containing fibers,
preserving the entire member and connection integrity. The failure shape is depicted in Figure 11.
Behavior of SCC/FR-SCC specimens after heating: When the temperature was raised to 200 °C, the flexural
strength of SCC with steel fibers and SCC with hybrid fibers improved by around 8.5 and 5.9%, respectively.
As the temperature climbs to 200 °C, increasing cement hydration may be the primary cause of enhanced
flexural strength. When specimens are exposed to high temperatures, they lose flexural strength. As the furnace
temperature is (200, 400, and 600) °C, the flexural strength of SCC specimens (without fibers) decreases by
about (2, 36.6, 94.4) %, and SCC specimens with PP fibers decreases by around (12, 49, 96.4) % when
compared to specimens still at room temperature. In SCC specimens with steel fibers, the decrement in flexural
strength is around (25.2, 81.3) %, and in SCC specimens with hybrid fibers, it is about (30.4, 88) % at (400 and
600) °C, compared to specimens still at ambient temperature. This could be due to the influence of the high
temperature on the concrete construction. When the temperature rises over (400°C), the calcium hydroxide
dehydrates, causing the cement paste to shrink. Because of the thermal incompatibility between cement in the
past and aggregates, many micro and macro cracks appeared in the samples, reducing flexural strength. At 25
°C, steel fibers enhanced flexural strength and polypropylene fibers raised it marginally, but when the
temperature rose, steel fibers also improved flexural and compressive strength, while polypropylene fibers
caused some flexural strength reduction during curing before elevated temperatures exposures. A melting of PP
fiber, which leads in the development of specific pores in the matrix, could explain this behavior [46].
Table 5. Flexural strength values after 28 days of cure for all SCC mixtures (MPa)
Mix
Relative flexural strength at elevated temperature
25°C 200°C 400°C 600°C
SCC 7.16 7.02 4.54 0.40
SCC-PPF 8.40 7.40 4.28 0.30
SCC-StF 10.16 11.02 7.60 1.90
SCC-StF & PPF 9.54 10.10 6.64 1.14
0
1
2
3
4
5
6
7
25 200 400 600
Tensile
strength,
MPa
Temperatur °C
SCC SCC-PPF SCC-StF SCC-StF & PPF
0
1
2
3
4
5
6
SCC SCC-PPF SCC-StF SCC-StF & PPF
Tensile
strength,
MPa
Mix No.
11. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2093
The increase in flexural strength is higher in specimens with 1.0 %t PP fibers, 1.0 % steel fibers, and (0.5 % steel +
0.5 % PP) hybrid fibers by total volume than in SCC specimens (without fibers). As the furnace temperature is (200,
400, and 600) °C, the increase is around (5.4, 6, 25) %, (57, 67.4, 375) %, and (43.8, 46, 185) %, respectively, when
compared to specimens still without fibers. This could be due to the effect of the fibers, which alters the structure of
concrete as shown in compressive strength [39].
Figure 18. Values of flexural strength for all Mixes (MPa) at
different temperatures
Figure 19. Values of flexural strength for all Mixes (MPa)
4.3.4. Ratio for Mass Losses
The mass loss ratio is calculated by dividing the difference between the weight at room temperature and the weight
at a given temperature by the weight of various RPC specimens at room temperature. The ratio between the weight at
25°C and the weight at a particular temperature to the weight at 25°C is known as the mass loss ratio. Each specimen's
mass was evaluated at 25°C and after being exposed to extreme temperatures. For the four concretes investigated, the
weight loss vs. temperature was relatively similar. The mass loss ratio ranged from 2.96 to 18%, at temperature
increasing from 200 to 800°C. It demonstrates that SCC had higher mass loss ratios than FR-SCC. Table 6 illustrates
the mass losses of SCC mixes as a percentage of total mass as temperature rises. Figure 20 demonstrates that weight
losses were smaller for SCC samples containing polypropylene and steel fibers than for those that did not. Weight loss
following high-temperature concrete contact can be caused by a variety of factors. The main causes of weight loss are
chunk expulsions or concrete spalling from the surface layers [46]. Small explosive spalling or chunks being ejected
were seen during this test. The loss of weight at low temperatures could be owing to the escape of free water from
capillary pores. The evaporation of bonded water, according to Rami et al. [47], causes weight loss among 150 – 300
°C. The fundamental explanation for this was that when the SCC samples were heated, the melted polypropylene
fibers generated micro channels within the SCC samples that allowed the vapour to escape.
Table 6. Ratio of mass losses for all mixes
Mix
Mass loss ratio at elevated temperature (%)
25°C 200°C 400°C 600°C 800°C
SCC 0 5.16 7.58 11.24 18.00
SCC-PPF 0 3.60 6.82 8.82 14.72
SCC-StF 0 2.96 6.52 8.50 13.54
SCC-StF & PPF 0 4.64 7.16 9.06 15.44
Figure 20. The relationship between the temperature and mass loss ratio
0
2
4
6
8
10
12
25 200 400 600
flexural
strength,
MPa
Temperatur °C
SCC
SCC-PPF
SCC-StF
SCC-StF & PPF
0
2
4
6
8
10
12
SCC SCC-PPF SCC-StF SCC-StF & PPF
flexural
strength,
MPa
Mix No.
0
5
10
15
20
25 200 400 600 800
Mass
loss
at
elevatfd
(%)
Temperatures °C
SCC
SCC-PF
SCC-SF
SCC-SF & PF
12. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2094
4.3.5. Velocity of Ultrasonic Pulses (UPV)
Ultrasonic pulse velocity was performed using ASTM C597 [48] Standard Method Test. A UPV test was
conducted to assess the degree of damage to the SCC sample after it was exposed to high temperatures. The UPV test
was carried out by sending an ultrasonic pulse through the cube samples and recording the time it took for the pulse to
pass through. The greater the speeds, the better the concrete quality and consistency, as well as the lesser cracks and
cavities. The UPV was computed by dividing the structure's breadth by the pulse's travel duration. The range of
concrete samples' quality is shown in Table 7.
Table 7. Concrete quality assessment criterion based on speed [49]
Pulse velocity (km/s) Concrete quality grading
Above 4.5 Excellent
3.5–4.5 Good
3.0–3.5 Medium
Below 3.0 Doubtful
The UPV findings of all of the SCC samples exposed to various elevated temperatures are shown in Table 8 and
Figure 21. Each data point is the result of averaging three different SCC cubes samples tests. SCC-Stf had slightly
higher UPV values than other SCC mixes at ambient temperature. The heated SCC specimens' UPV values declined as
the temperature climbed, as seen in the figure. Plain SCC, SCC- PPF, SCC- StF, and SCC-StF & PPF samples' UPV values
have dropped by 19.3 percent, 22.2 percent, 16.6 percent, 8.1 percent, and 18.9 percent, respectively, at 200 °C. At
400 °C, all SCC specimens' UPV values indicated a continuous decrease. At this temperature, the SCC- PPF and plain
SCC samples had the least UPV values. It's possible that the fall in UPV values for SCC- PPF and plain SCC samples is
due to the high temperature, which causes full physical breakdown in SCC samples. In comparison to the samples at
200 and 400 °C, the frequency of micro-cracks rose and the concrete quality decreased at 600 ° C, resulting in a larger
reduction in UPV values. All SCC samples kept their physical shape as the temperature was raised from 25 to 800 °C
to measure UPV, which ranged from good to dubious. Due to melting polypropylene fibers, cracks and pores emerge
in the SCC- StF & PPF and SCC-PPF samples, resulting in physico-chemical variations in cement paste and thermal
mismatch between aggregate and cement paste, which is assumed to be the cause of mechanical property degradation
[47, 50]. Because fewer fractures form inside the SCC after evaporation, the UPV readings for SCC-StF & PPF are greater
at 600 and 800 °C than for SCC-PPF, as shown in Figure 21. The amount of micro-cracks in the SCC-PPF samples tends
to be higher, leading in a steeper decrease in UPV readings than in the SCC-StF & PPF samples.
Table 8. Result of ultrasonic pulse velocity for all mixes
Mix
Ultrasonic pulse velocity at elevated temperature (km/sec)
25°C 200°C 400°C 600°C 800°C
SCC 4.46 3.6 2.34 1.12 0.84
SCC-PPF 4.40 3.42 2.24 1.10 0.50
SCC-StF 4.42 4.06 2.62 1.06 0.44
SCC-StF & PPF 4.34 3.52 2.42 1.56 0.84
Figure 21. Relation of the ratio of mass loss to temperature
0
0.5
1
1.5
2
2.5
3
3.5
4
4.5
25°C 200°C 400°C 600°C 800°C
Ultrasonic
pulse
velocity
(Km/sec)
Temperatures
SCC
SCC-PPF
SCC-StF
SCC-StF & PPF
13. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2095
The micro-cracking of concrete has a significant impact on the transmission of pulse waves through it. As a result,
decreasing pulse velocity as temperature rises is a sensitive indicator of material cracking. Fissures in the concrete can
form as a result of high temperatures, thermal expansion, and dryness. The pulse velocity of the SCC samples is
increased by the cracks or micro-pathways that generate rising cracks. As a result, microcracks slow down the pulse
and cause low UPV levels [48].
5. Conclusions
A series of experiments were carried out throughout this study to evaluate changes in mechanical characteristics on
SCC sample was subjected to considerable temperatures between 25 and 800 ° C, as well as to investigate the impact
of incorporating steel fibers, polypropylene fibers, and hybrid fibers on mechanical properties. Based on the findings
of this research, the following conclusions can be drawn:
Slump flow, L-Box tests, and GMT results show that all of the mixes meet the SCC standards outlined in the
EFNARC guidelines. As a result, all of the mixtures are deemed to have high consistency and workability in
terms of filling and passing ability.
Fibers can be used in SCC, and the characteristics of FR-SCC are within acceptable limits. In addition, the
addition of fibers results in a more uniform and cohesive mix with just a minor reduction in workability.
There is no segregation or bleeding when the flow is flowing or when the flow is stopped.
When comparing reference mixes without fibers to mixes containing PP, steel, and hybrid PP and steel fibers,
T50 increases by about 56.5, 43, and 74 percent, while slump flow diameter decreases by about (11.5, 9 and 10)
percent, L-box decreases by 13.5, 6 and 14.6 percent, and GTM decreases by 19, 18 and 22.5 percent. As a
result, substantial doses of superplasticizer are used in these mixtures to retain workability.
The addition of steel fibers resulted in a significant increase in mechanical strength. The effect of fibers, which
effectively inhibits the spread of crack due to the existence of a strong link between the matrix and steel fibers,
can be attributed to this increase in mechanical characteristics. This improved the SCC mechanical strength by
increasing the concrete's ability to absorb energy. Furthermore, steel fibers can bridge micro/macro cracks,
limiting the growth of main cracks and changing the failure mode from brittle to ductile.
The mechanical characteristics of SCC with steel fibers increased to 200 °C and the loses over 400 °C. Whilst
the mechanical properties for SCC with PP fiber declined to 200 °C.
In specimens exposed to high temperatures, there is a decrease in compressive, tensile, and flexural strengths.
The better mechanical characteristics were provided by concrete mixtures which include steel fibers as well as
hybrid fibres.
The inclusion of steel fibers and polypropylene fibers minimized the possibility of explosion spilling in the self-
compacting concrete.
When the temperature is between 425 and 475 ℃, spalling happens in SCC samples.
With the temperature rise the mass loss ratio increased.
Using steel fibers and polyethylene fibres lowered the mass-loss ratio.
With rising temperature, all SCC mixes showed increasing mass loss and decreasing UPV until samples spalled
(as in plain SCC and SCC with steel fibers) or were suspect (as in samples of RPC with PP fibers and RPC
contain hybrid fibers).
5.1. Recommendation for Future Work
On the effect of elevated temperature on FR-SCC, the following points should be researched.
The effects of steel fibers, polypropylene fibers, and hybrid fibers on the mechanical and thermal properties of
SCC exposed to varying periods of high temperatures.
The effect of adding carbon fibers to SCC that has been exposed to high temperatures on mechanical and thermal
properties.
6. Nomenclature
SCC Self-Compacting Concrete FR-SCC Fiber Reinforced Self-Compacting Concrete
SCC-PPF Mixture contains 1% polypropylene fibres SCC-StF Mixture contains 1% steel fibres
SCC-StF & PPF
Mixture contains hybrid fibres, 0.5% steel and
polypropylene fibres
PP fibers Polypropylene fibers
14. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2096
7. Declarations
7.1. Author Contributions
Conceptualization, H.H.Y.A. and H.K.S.; methodology, S.D.; software, H.H.Y.A.; validation, H.H.Y.A., S.D. and
H.K.S.; formal analysis, H.H.Y.A.; investigation, H.H.Y.A.; resources, H.H.Y.A.; data curation, H.H.Y.A. and
H.K.S.; writing—original draft preparation, H.H.Y.A. and H.K.S.; writing—review and editing, H.H.Y.A. and H.K.S.;
visualization, H.K.S.; supervision, S.D.; project administration, S.D.; funding acquisition, H.H.Y.A. All authors have
read and agreed to the published version of the manuscript.
7.2. Data Availability Statement
The data presented in this study are available on request from the corresponding author.
7.3. Funding
The authors received no financial support for the research, authorship, and/or publication of this article.
7.4. Conflicts of Interest
The authors declare no conflict of interest.
8. References
[1] Ozawa, Kazumasa, Koichi Maekawa, and Hajime Okamura. "Development of high performance concrete." Journal of the
Faculty of Engineering, University of Tokyo, Series B;(Japan) 41, no. 3 (1992).
[2] Geiker, M., and Jacobsen, S., “Self-compacting concrete (SCC).” In: MINDESS, S. Developments in the formulation and
reinforcement of concrete. 2. ed. Vancouver: Woodhead, cap. 10, (2019): 229-256.
[3] Nis, Anil. “Mechanical Properties of Steel Fiber Reinforced Self-Compacting Concrete.” International Journal of Engineering
Technologies IJET 4, no. 1 (August 2, 2018): 33–40. doi:10.19072/ijet.340259.
[4] Coppola, L., T. Cerulli, and D. Salvioni. “Sustainable Development and Durability of Self-Compacting Concretes.” In
American Concrete Institute, ACI Special Publication, SP-221: (2004): 29–50.
[5] Aggarwal, Paratibha, Rafat Siddique, Yogesh Aggarwal, and Surinder M. Gupta. “Self-Compacting Concrete - Procedure for
Mix Design.” Leonardo Electronic Journal of Practices and Technologies 7, no. 12 (2008): 15–24.
[6] Nehdi, M., M. Pardhan, and S. Koshowski. “Durability of Self-Consolidating Concrete Incorporating High-Volume
Replacement Composite Cements.” Cement and Concrete Research 34, no. 11 (2004): 2103–12.
doi:10.1016/j.cemconres.2004.03.018.
[7] Jalal, Mostafa, Alireza Pouladkhan, Omid Fasihi Harandi, and Davoud Jafari. “Comparative Study on Effects of Class F Fly
Ash, Nano Silica and Silica Fume on Properties of High Performance Self Compacting Concrete.” Construction and Building
Materials 94, no. 2015 (2015): 90–104. doi:10.1016/j.conbuildmat.2015.07.001.
[8] Frazão, Cristina, Aires Camões, Joaquim Barros, and Delfina Gonçalves. “Durability of Steel Fiber Reinforced Self-
Compacting Concrete.” Construction and Building Materials 80 (April 2015): 155–166.
doi:10.1016/j.conbuildmat.2015.01.061.
[9] Vivek, S. S., and G. Dhinakaran. “Fresh and Hardened Properties of Binary Blend High Strength Self Compacting Concrete.”
Engineering Science and Technology, an International Journal 20, no. 3 (2017): 1173–79. doi:10.1016/j.jestch.2017.05.003.
[10] Shwalia, Ali Sabah Imran, Nabeel Hasan Ali Al-Salim, and Haider M. Al-Baghdadi. “Enhancement Punching Shear in Flat
Slab Using Mortar Infiltrated Fiber Concrete.” Civil Engineering Journal 6, no. 8 (August 1, 2020): 1457–1469.
doi:10.28991/cej-2020-03091560.
[11] Rando Junior, André Meneghel, Leonardo Guerra, and Gilson Morales. “Interferência Da Adição de Fibras de Polipropileno e
Finos de Basalto Na Resistência Mecânica de Micro-Concreto.” Semina: Ciências Exatas e Tecnológicas 40, no. 1 (June 27,
2019): 55. doi:10.5433/1679-0375.2019v40n1p55.
[12] Sadrmomtazi, Ali, Saeed Haghighat Gashti, and Behzad Tahmouresi. “Residual Strength and Microstructure of Fiber
Reinforced Self-Compacting Concrete Exposed to High Temperatures.” Construction and Building Materials 230 (2020):
116969. doi:10.1016/j.conbuildmat.2019.116969.
[13] Venkadachalam, Gokulnath, and M. Dileepkumar. “Behaviour of Self Compacted Concrete Produced with Steel Fiber, Glass
Fiber and Polypropylene Fiber Additives Subjected to High Temperature.” IOP Conference Series: Materials Science and
Engineering 981, no. 4 (2020): 42088. doi:10.1088/1757-899X/981/4/042088.
15. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2097
[14] Mansour, Sabria Malika. “New Generation of Fiber Self-Compacting Concrete Based on Pyrophyllite.” Emerging Materials
Research 10, no. 2 (2021): 194–205. doi:10.1680/jemmr.20.00137.
[15] El-Dieb, A. S., and M. M. Reda Taha. “Flow Characteristics and Acceptance Criteria of Fiber-Reinforced Self-Compacted
Concrete (FR-SCC).” Construction and Building Materials 27, no. 1 (2012): 585–96. doi:10.1016/j.conbuildmat.2011.07.004.
[16] Gali, Sahith, and Kolluru V.L. Subramaniam. “Improvements in Fracture Behavior and Shear Capacity of Fiber Reinforced
Normal and Self Consolidating Concrete: A Comparative Study.” Construction and Building Materials 189 (2018): 205–17.
doi:10.1016/j.conbuildmat.2018.08.194.
[17] Savaris, Gustavo, and Isabela de Gois Laufer. “Shear Strength of Steel Fiber Self-Compacting Concrete Beams.” Semina:
Ciências Exatas e Tecnológicas 42, no. 1 (2021): 45. doi:10.5433/1679-0375.2021v42n1p45.
[18] Cifuentes, Héctor, Fernando Medina, Carlos Leiva, and Constantino Fernández-Pereira. “Effects of Fibres and Rice Husk Ash
on Properties of Heated HSC.” Magazine of Concrete Research 64, no. 5 (2012): 457–70. doi:10.1680/macr.11.00087.
[19] Zuhair, Mohammad, and S. K. Deshmukh. “Effect of Different Fibers on Compressive Strength of Self-Compacting Concrete
at Elevated Temperature.” IOP Conference Series: Materials Science and Engineering 410, no. 1 (2018): 12007.
doi:10.1088/1757-899X/410/1/012007.
[20] Qasim, Ola Adel, and Hussein Kareem Sultan. “Experimental Investigation of Effect of Steel Fiber on Concrete Construction
Joints of Prism.” IOP Conference Series: Materials Science and Engineering 745, no. 1 (2020). doi:10.1088/1757-
899X/745/1/012170.
[21] Sultan, Hussein Kareem, and Isam Alyaseri. “Effects of Elevated Temperatures on Mechanical Properties of Reactive Powder
Concrete Elements.” Construction and Building Materials 261 (2020): 120555. doi:10.1016/j.conbuildmat.2020.120555.
[22] Kumar, P. Rathish, and K. Srikanth. “Mechanical Characteristics of Fiber Reinforced Self Compacting Mortars.” Asian
Journal of Civil Engineering 9, no. 6 (2008): 647–57.
[23] Ahmad, Subhan, and Arshad Umar. “Fibre-Reinforced Self-Compacting Concrete: A Review.” IOP Conference Series:
Materials Science and Engineering 377, no. 1 (2018): 12117. doi:10.1088/1757-899X/377/1/012117.
[24] Hawra Alradhawi. “Experimental Investigation of Use Polypropylene Fibers in Self-Compacting Concrete.” International
Journal of Engineering Trends and Technology 57, no. 1 (2018): 32–39. doi:10.14445/22315381/ijett-v57p207.
[25] Aslani, Farhad, and Jack Kelin. “Assessment and Development of High-Performance Fibre-Reinforced Lightweight Self-
Compacting Concrete Including Recycled Crumb Rubber Aggregates Exposed to Elevated Temperatures.” Journal of Cleaner
Production 200 (2018): 1009–25. doi:10.1016/j.jclepro.2018.07.323.
[26] Aslani, Farhad, Junbo Sun, and Guanqi Huang. “Mechanical Behavior of Fiber-Reinforced Self-Compacting Rubberized
Concrete Exposed to Elevated Temperatures.” Journal of Materials in Civil Engineering 31, no. 12 (2019): 04019302.
doi:10.1061/(asce)mt.1943-5533.0002942.
[27] Mahapatra, Chinmaya Kumar, and Sudhirkumar V. Barai. “Temperature Impact on Residual Properties of Self-Compacting
Based Hybrid Fiber Reinforced Concrete with Fly Ash and Colloidal Nano Silica.” Construction and Building Materials 198
(2019): 120–32. doi:10.1016/j.conbuildmat.2018.11.155.
[28] Okamura, Hajime, and Kazumasa Ozawa. "Mix design for self-compacting concrete." Concrete library of JSCE 25, no. 6
(1995): 107-120.
[29] ASTM C494/C494M−17. “Standard Specification for Chemical Admixtures for Concrete.” ASTM International C494, no.
February (2017): 1–10.
[30] EFNARC. “Specification and Guidelines for Self-Compacting Concrete.” Report from European Federation for Specialist
Construction Chemicals and Concrete 44, no. February (2002): 32.
[31] Mezzal, Saif K., Khalid B. Najim, and Zaid Al-Azzawi. “Residual Mechanical Properties of High Strength Self-Compacting
Concrete with Reused Steel Fibers at High Temperatures.” Journal of Green Engineering 10, no. 6 (2020): 3156–70.
[32] Qasim, Ola Adel, and Abdullah Sinan Ahmed. “High Temperature Effect on Shear Transfer Strength of Steel Fiber Reinforced
Self-Compacted Concrete.” ARPN Journal of Engineering and Applied Sciences 14, no. 10 (2019): 3158–74.
doi:10.36478/JEASCI.2019.3158.3174.
[33] Kumar, S L, V Manasa, and M Harish. “Evaluation of Workability Characteristics of Self-Compacting Concrete Creep
Behavior of Self-Compacting Concrete.” International Research Journal of Engineering and Technology, 5, no. 6 (2018).
[34] ASTM C 109/C 109M-02. “Standard Test Method for Compressive Strength of Hydraulic Cement Mortars.” Annual Book of
ASTM Standards. Conshohocken, PA, USA, 2005.
[35] Ahmad, Subhan, Arshad Umar, and Amjad Masood. “Properties of Normal Concrete, Self-Compacting Concrete and Glass
Fibre-Reinforced Self-Compacting Concrete: An Experimental Study.” Procedia Engineering 173 (2017): 807–813.
doi:10.1016/j.proeng.2016.12.106.
16. Civil Engineering Journal Vol. 7, No. 12, December, 2021
2098
[36] Aslani, Farhad, and Shami Nejadi. “Self-Compacting Concrete Incorporating Steel and Polypropylene Fibers: Compressive
and Tensile Strengths, Moduli of Elasticity and Rupture, Compressive Stress-Strain Curve, and Energy Dissipated under
Compression.” Composites Part B: Engineering 53 (2013): 121–33. doi:10.1016/j.compositesb.2013.04.044.
[37] Karatas, Mehmet, Murat Dener, Ahmet Benli, and Mehrzad Mohabbi. “High Temperature Effect on the Mechanical Behavior
of Steel Fiber Reinforced Self‐compacting Concrete Containing Ground Pumice Powder.” Structural Concrete 20, no. 5
(May 13, 2019): 1734–1749. doi:10.1002/suco.201900067.
[38] Ezziane, Mohammed, Tahar Kadri, Laurent Molez, Raoul Jauberthie, and Ali Belhacen. “High Temperature Behaviour of
Polypropylene Fibres Reinforced Mortars.” Fire Safety Journal 71 (2015): 324–31. doi:10.1016/j.firesaf.2014.11.022.
[39] Poon, C. S., Z. H. Shui, and L. Lam. “Compressive Behavior of Fiber Reinforced High-Performance Concrete Subjected to
Elevated Temperatures.” Cement and Concrete Research 34, no. 12 (2004): 2215–22. doi:10.1016/j.cemconres.2004.02.011.
[40] TSHIMANGA, Mulumba KANEMA. “Influence Des Paramètres de Formulation et Microstructuraux Sur Le Comportement à
Haute Température Des Bétons.” Revue Européenne de Génie Civil. Université de Cergy-Pontoise, 2006.
doi:10.1080/17747120.2006.9692891.
[41] Ding, Y., Y. Zhang, and A. Thomas. “The Investigation on Strength and Flexural Toughness of Fibre Cocktail Reinforced
Self-Compacting High Performance Concrete.” Construction and Building Materials 23, no. 1 (2009): 448–52.
doi:10.1016/j.conbuildmat.2007.11.006.
[42] American-Society. “American Society for Testing and Material Standard Test Method for Splitting Tensile Strength of
Cylindrical Concrete Specimens.” ASTM Standard C4996M-04, Philadelphia. Philadelphia, Pennsylvania, (2004).
[43] Behnood, Ali, and Masoud Ghandehari. “Comparison of Compressive and Splitting Tensile Strength of High-Strength
Concrete with and without Polypropylene Fibers Heated to High Temperatures.” Fire Safety Journal 44, no. 8 (2009): 1015–
22. doi:10.1016/j.firesaf.2009.07.001.
[44] Corinaldesi, Valeria, and Giacomo Moriconi. “Characterization of Self-Compacting Concretes Prepared with Different Fibers
and Mineral Additions.” Cement and Concrete Composites 33, no. 5 (2011): 596–601. doi:10.1016/j.cemconcomp.2011.03.007.
[45] ASTM C293, Standard test method for flexural strength of concrete (using simple beam with center point loading). West
Conshohocken, PA: ASTM International, (2016).
[46] Düğenci, Oğuz, Tefaruk Haktanir, and Fatih Altun. “Experimental Research for the Effect of High Temperature on the
Mechanical Properties of Steel Fiber-Reinforced Concrete.” Construction and Building Materials 75 (January 2015): 82–88.
doi:10.1016/j.conbuildmat.2014.11.005.
[47] Haddad, Rami H., Ruba A. Odeh, Hala A. Amawi, and Ayman N. Ababneh. “Thermal Performance of Self-Compacting
Concrete: Destructive and Nondestructive Evaluation.” Canadian Journal of Civil Engineering 40, no. 12 (2013): 1205–14.
doi:10.1139/cjce-2013-0037.
[48] ASTM C597. Standard Test Method for Pulse Velocity through Concrete. American Society for Testing and Materials, West
Conshohocken, PA, USA. West Conshohocken, PA, ASTM International, 2016. doi:10.1520/C0597-16.
[49] Indian Standard IS 13311-1, Method of Non-destructive testing of concrete, Part 1: Ultrasonic pulse velocity [CED 2: Cement
and Concrete], Bureau of Indian Standards Manak Bhavan, 9 Bahadur Shah Zafar Maro New Delhi 110002, (1992).
[50] Yang, Hsuanchih, Yiching Lin, Chiamen Hsiao, and Jian You Liu. “Evaluating Residual Compressive Strength of Concrete at
Elevated Temperatures Using Ultrasonic Pulse Velocity.” Fire Safety Journal 44, no. 1 (2009): 121–30.
doi:10.1016/j.firesaf.2008.05.003.