Heat treating is a process used to alter the properties of metals by heating and cooling. There are four main types of heat treatment: annealing, normalizing, hardening, and tempering. Annealing makes metals softer and more ductile, normalizing removes internal stresses, hardening increases hardness and strength but reduces ductility, and tempering relieves internal stresses induced by hardening. The three stages of heat treatment are heating, soaking at a controlled temperature, and cooling. Proper control of heating, temperature, time, and cooling rates is required to achieve the desired material properties.
This document provides definitions for common heat treatment terminology used in the steel industry. It defines terms related to annealing, aging, hardening, quenching, tempering, and transformation temperatures. Key terms defined include annealing, austempering, austenitizing, carburizing, hardening, normalizing, quenching, tempering, and transformation ranges.
Welding theory & application definitions أحمد دعبس
This document provides definitions for welding and metalworking terms. It defines over 100 terms in detail, including types of welding processes like arc welding, gas welding, and brazing. It also defines metal alloys, joint configurations, welding defects, and other technical terms related to welding theory, equipment, and applications. Key terms defined include arc, electrode, filler metal, flux, joint preparation, and weld bead.
The document discusses various aspects of hardening hypoeutectoid and hypereutectoid steels. It explains that hardening involves heating steel to the appropriate temperature, holding, and then rapidly quenching to form martensite. Factors like chemical composition, part size/shape, heating/cooling rates, and quenchant properties influence the hardening process and final properties. Different hardening methods like direct, stage, and self-tempering quenching are also summarized.
Metallurgy is the process of extracting pure metals from their ores. Ores contain unwanted impurities and the required metal. The process involves both physical and chemical steps to separate the metal from impurities. One such process is the Parke's process for extracting silver, which involves heating an alloy of lead and silver to melt it, mixing it with molten zinc where the silver dissolves and separates from the lead due to different solubilities. Ellingham diagrams graphically show the thermodynamic stability of metal oxides and their variation with temperature, indicating the spontaneity of oxidation reactions. Iron is extracted from its ore, haematite, using a blast furnace where coke and limestone are added and hot
The document discusses different methods for heat treating steels to alter their properties, including quenching and slow cooling. Quenching involves heating steel above its critical temperature and then rapidly cooling to transform austenite into martensite, hardening the steel. Slow cooling processes like normalizing, annealing, and spheroidizing involve heating steel and then allowing it to cool slowly to produce different microstructures like pearlite.
The document defines various heat treatment terms and processes. It provides multiple definitions for some terms to highlight subtle differences. Key terms defined include annealing, austempering, austenite, bainite, hardening, and aging. Annealing involves heating and cooling to soften metals and modify properties or microstructure. Austempering and hardening involve controlled cooling after heating to achieve specific microstructures like bainite that impart strength.
The document discusses various heat treatment processes including annealing, normalizing, quenching, and martensitic transformation. It provides details on the purposes, methods, and applications of each process. Annealing involves heating and slow cooling to relieve stresses and modify properties. Normalizing heats above the transformation temperature and air cools to produce a fine grain structure. Quenching rapidly cools steel above the transformation temperature to form very hard martensite. Martensitic transformation is the formation of acicular needlelike structures during rapid cooling of austenite.
This document provides definitions for common heat treatment terminology used in the steel industry. It defines terms related to annealing, aging, hardening, quenching, tempering, and transformation temperatures. Key terms defined include annealing, austempering, austenitizing, carburizing, hardening, normalizing, quenching, tempering, and transformation ranges.
Welding theory & application definitions أحمد دعبس
This document provides definitions for welding and metalworking terms. It defines over 100 terms in detail, including types of welding processes like arc welding, gas welding, and brazing. It also defines metal alloys, joint configurations, welding defects, and other technical terms related to welding theory, equipment, and applications. Key terms defined include arc, electrode, filler metal, flux, joint preparation, and weld bead.
The document discusses various aspects of hardening hypoeutectoid and hypereutectoid steels. It explains that hardening involves heating steel to the appropriate temperature, holding, and then rapidly quenching to form martensite. Factors like chemical composition, part size/shape, heating/cooling rates, and quenchant properties influence the hardening process and final properties. Different hardening methods like direct, stage, and self-tempering quenching are also summarized.
Metallurgy is the process of extracting pure metals from their ores. Ores contain unwanted impurities and the required metal. The process involves both physical and chemical steps to separate the metal from impurities. One such process is the Parke's process for extracting silver, which involves heating an alloy of lead and silver to melt it, mixing it with molten zinc where the silver dissolves and separates from the lead due to different solubilities. Ellingham diagrams graphically show the thermodynamic stability of metal oxides and their variation with temperature, indicating the spontaneity of oxidation reactions. Iron is extracted from its ore, haematite, using a blast furnace where coke and limestone are added and hot
The document discusses different methods for heat treating steels to alter their properties, including quenching and slow cooling. Quenching involves heating steel above its critical temperature and then rapidly cooling to transform austenite into martensite, hardening the steel. Slow cooling processes like normalizing, annealing, and spheroidizing involve heating steel and then allowing it to cool slowly to produce different microstructures like pearlite.
The document defines various heat treatment terms and processes. It provides multiple definitions for some terms to highlight subtle differences. Key terms defined include annealing, austempering, austenite, bainite, hardening, and aging. Annealing involves heating and cooling to soften metals and modify properties or microstructure. Austempering and hardening involve controlled cooling after heating to achieve specific microstructures like bainite that impart strength.
The document discusses various heat treatment processes including annealing, normalizing, quenching, and martensitic transformation. It provides details on the purposes, methods, and applications of each process. Annealing involves heating and slow cooling to relieve stresses and modify properties. Normalizing heats above the transformation temperature and air cools to produce a fine grain structure. Quenching rapidly cools steel above the transformation temperature to form very hard martensite. Martensitic transformation is the formation of acicular needlelike structures during rapid cooling of austenite.
Study and Analysis on Heat Treatment Process and Microstructure of Low Carbon...IJARTES
The document summarizes a study on the heat treatment process and microstructure of low carbon steel. It describes various heat treatment processes like annealing, normalizing, hardening, austempering, and tempering. Experimental details are provided on specimen preparation, heat treatment processes, hardness and tensile testing, and microstructure analysis. Results show that hardness decreases and ductility increases with higher tempering temperature and longer time. Austempering provides an optimal combination of properties. Microstructure analysis found that martensite fraction increases with higher annealing temperature. In conclusion, mechanical properties vary by heat treatment process, and austempering yields the best balance of properties for many applications.
Quenching is a vital part of the heat treating process in manufacturing. Polymer quenchants are one option for quenching operations, and knowing which one to choose is key to successful heat treating applications. Scott Mackenzie, PhD, FASM, from Houghton International shares what you need to know when selecting quenching oils for your heat treating operations.
Heat treatment is a group of industrial processes used to alter the physical properties of materials by controlled heating and cooling. There are several common heat treatment methods including annealing, normalizing, hardening, and tempering. The goal of heat treatment is to achieve desired properties such as increased strength, hardness, ductility or corrosion resistance by changing the material's microstructure and relieving internal stresses.
This presentation provides an introduction into the basics of heat treating, primarily steel alloys. Heat treat processes for strengthening steel, or through hardening, using quench and temper, martempering, and austempering will be introduced and explained using the iron-carbon phase diagram and time-temperature-transformation diagrams to help understand the transformations occurring.
Precipitation hardening techniques will be introduced, which apply to one group of stainless steels, aluminum alloys and high performance materials. Common surface hardening techniques such as case hardening and carburizing will also be discussed. Various processes for reducing strength, or softening steel, will be presented. Preheat and post-heat treatments applied during welding will also be briefly discussed.
Evaluation of Structural Behavior of Structural Steel Joints at Elevated Temp...IRJET Journal
This document discusses the evaluation of the structural behavior of structural steel joints at elevated temperatures. It begins with an abstract that outlines the investigation of the mechanical properties of high-strength and mild structural steels at elevated temperatures, which is important for fire-resistant design. It then provides background on fire outbreaks and structural response, current fire design approaches, and the objectives of studying the behavior of structural steel joints and their critical elements under high temperatures. The document also reviews literature on standard fire tests and full-scale tests, and investigates the behavior of steel connections in fires. It examines the stress-strain behavior and degradation of steel properties at elevated temperatures. Finally, it describes the structural configuration of the steel joint being analyzed.
This presentation gives a brief introduction to chemical heat treatment of steels and surface hardening techniques
Keywords: Carburising, Nitriding, Carbonitriding, Flame hardening, Laser hardening, Induction hardening
This document provides an overview of metal heat treating presented by various individuals. It discusses what metal heat treating is, where it is used, why and how it is done, common heat treating processes and equipment. Specific details covered include commonly heat treated metals, types of heat treating furnaces, importance of protective atmospheres, and different heat treating processes like annealing. The document is intended to educate about key aspects of industrial metal heat treating.
This document discusses various heat treatments that can be used on steels, including:
- Annealing treatments like full annealing, recrystallization annealing, stress relief annealing, and spheroidization annealing.
- Normalizing to refine grain structure, harden slightly, and reduce segregation.
- Hardening by heating above the transformation temperatures and quenching to form martensite, followed by tempering.
- Factors that influence the severity of quenching and hardenability of steels, such as the quenching medium, agitation level, and alloying elements. Microstructures can vary from surface to interior based on cooling rate.
This document provides information about gas welding and cutting. It discusses oxy-fuel welding, which uses oxygen and acetylene gases to produce a flame over 5700°F that can melt metals. Cutting uses the flame to preheat and then pure oxygen to burn away metal. The document describes the equipment used, including oxygen and acetylene cylinders, regulators, hoses, and torches. It explains the chemical reactions that produce the high temperature flame and discusses properties of acetylene such as its heat output. Advantages and limitations of oxy-fuel welding are also outlined.
Microstructual Analysis Of Heat Treated EN8 SteelSourav Mahato
The document discusses heat treatment processes including quenching, annealing, normalizing, and tempering that are performed on EN-8 steel. Specifically, it describes treating EN-8 steel samples via quenching, annealing, and normalizing, followed by single tempering. The treated samples are then tested for tensile strength using a universal testing machine and hardness is compared. Microstructures of samples after different heat treatments are also examined.
This document discusses various heat treatment processes for steels including annealing, normalizing, hardening, tempering, and case hardening. It explains that annealing involves heating metals above or below critical temperatures and slowly cooling to make the metal soft. Hardening involves heating steel above its critical temperature then quenching in water to form martensite and make the metal very hard. Tempering is used after hardening to reduce brittleness by reheating to 220-300 degrees C. Case hardening, such as carburizing or nitriding, adds carbon or nitrogen to the surface layer to harden low-carbon steels. Methods of measuring temperature in furnaces like pyrometers and Seger cones are also summarized
The document discusses various heat treatment processes used in engineering:
1) Annealing makes metals softer by heating above critical temperatures and slowly cooling. Normalizing removes internal stresses by heating above critical temperatures and air cooling faster than annealing.
2) Hardening involves heating steel above critical temperatures, quenching quickly in water to form martensite, and making the metal very hard. Tempering then removes some brittleness by reheating to 220-300 degrees.
3) Case hardening methods like pack carburizing, salt bath carburizing, and gas carburizing add carbon to the surface to create a hard outer case over a softer core. Induction and flame hardening also
The document provides information about heat treatment processes. It defines heat treatment as a process of heating and cooling metals and alloys in the solid state to change their properties. Heat treatment is done to change properties like strength, hardness, toughness etc. of steels. The key heat treatment processes described are annealing, normalizing, hardening and tempering. Annealing involves heating steel above or below its critical temperature, holding, and slow cooling to soften it and relieve stresses. The goals, processes, and effects of various annealing types like full annealing and spheroidizing annealing are explained.
STUDY OF MICRO STRUCTURE OF HEAT TREATED EN8 STEELAkhil Raj U R
The document discusses heat treatment processes used to alter the physical and chemical properties of materials like metals. It focuses on the heat treatment of EN8 steel and describes how processes like annealing, normalizing, and quenching can be used to manipulate a metal's microstructure and properties. The key points are:
- Heat treatment involves heating metals to alter properties like hardness, strength and toughness. It controls diffusion and the rate of cooling to manipulate grain size and composition.
- The microstructure, allotropes, and composition of metals determine how they respond to heat treatments. Hypoeutectoid, eutectoid, and hypereutectoid alloys form different microstructures like ferrite or
Quenching is a vital part of the heat treating process in manufacturing. This presentation by Houghton International will show you how to master the process for the most efficient quenching and heat treating operations.
This document describes a project to test flame hardening on low carbon steels. It discusses low carbon steels, their properties and applications. It then describes the process of flame hardening and how it was used in this project to selectively harden the surface of steel samples. Brinell hardness tests were conducted on the samples to analyze the hardness at the surface (case) versus the core after flame hardening. The results and conclusions from this analysis are presented.
This document discusses post weld heat treatment (PWHT). It describes how welding causes residual stresses and microstructural changes in the heat affected zone (HAZ) that can lead to cracking. PWHT involves controlled heating and cooling to relieve residual stresses and improve properties. The key aspects covered include:
- PWHT relieves residual stresses and improves toughness by altering the HAZ microstructure.
- Preheating the metal prior to welding reduces cooling rates and residual stresses. The required preheat temperature depends on material thickness and carbon content.
- Thermal stress relief involves heating to just below the recrystallization temperature to allow stress relaxation. Proper heating and cooling rates are important.
This document discusses various heat treatment processes including annealing, hardening, and tempering. Annealing involves heating metals to specific temperatures to soften them and make them easier to shape. Hardening involves heating steel above its critical temperature then quenching to form martensite, making the steel very hard but brittle. Tempering is then used to reduce brittleness by reheating hardened steel to lower temperatures. The document provides details on the purposes and procedures for various annealing, hardening, and tempering techniques.
This document provides information on various heat treatment processes including annealing, normalizing, hardening, and tempering. It defines heat treatment as any process of heating and cooling metals to alter their properties. Annealing aims to relieve stresses and refine grains, while normalizing also improves properties. Hardening involves heating steel to form austenite and then quenching to form martensite. Tempering reduces brittleness caused by hardening. Specific methods like flame hardening and induction hardening selectively harden surfaces. Case hardening diffuses carbon or nitrogen into surfaces to create a hard case over a tough core.
Relazione annuale inerente al censimento dei funghi eduli nella zona dell'ospedale "S. Maria degli Angeli" di Sacile, relativa all'anno 2013.
[NB]: La reale visualizzazione delle slide non è a scorrimento, ma tramite i link presenti in fondo alle diapositive. Scaricare la presentazione per una visione ottimale.
This document provides an overview of Maven, including:
1. It describes how to install Maven and configure user-specific settings and repositories.
2. It explains the basic components of a Maven project including the pom.xml file, dependencies, and packaging.
3. It outlines Maven's build lifecycle of compiling, testing, packaging, and deploying a project as well as how to define dependencies and repositories.
Study and Analysis on Heat Treatment Process and Microstructure of Low Carbon...IJARTES
The document summarizes a study on the heat treatment process and microstructure of low carbon steel. It describes various heat treatment processes like annealing, normalizing, hardening, austempering, and tempering. Experimental details are provided on specimen preparation, heat treatment processes, hardness and tensile testing, and microstructure analysis. Results show that hardness decreases and ductility increases with higher tempering temperature and longer time. Austempering provides an optimal combination of properties. Microstructure analysis found that martensite fraction increases with higher annealing temperature. In conclusion, mechanical properties vary by heat treatment process, and austempering yields the best balance of properties for many applications.
Quenching is a vital part of the heat treating process in manufacturing. Polymer quenchants are one option for quenching operations, and knowing which one to choose is key to successful heat treating applications. Scott Mackenzie, PhD, FASM, from Houghton International shares what you need to know when selecting quenching oils for your heat treating operations.
Heat treatment is a group of industrial processes used to alter the physical properties of materials by controlled heating and cooling. There are several common heat treatment methods including annealing, normalizing, hardening, and tempering. The goal of heat treatment is to achieve desired properties such as increased strength, hardness, ductility or corrosion resistance by changing the material's microstructure and relieving internal stresses.
This presentation provides an introduction into the basics of heat treating, primarily steel alloys. Heat treat processes for strengthening steel, or through hardening, using quench and temper, martempering, and austempering will be introduced and explained using the iron-carbon phase diagram and time-temperature-transformation diagrams to help understand the transformations occurring.
Precipitation hardening techniques will be introduced, which apply to one group of stainless steels, aluminum alloys and high performance materials. Common surface hardening techniques such as case hardening and carburizing will also be discussed. Various processes for reducing strength, or softening steel, will be presented. Preheat and post-heat treatments applied during welding will also be briefly discussed.
Evaluation of Structural Behavior of Structural Steel Joints at Elevated Temp...IRJET Journal
This document discusses the evaluation of the structural behavior of structural steel joints at elevated temperatures. It begins with an abstract that outlines the investigation of the mechanical properties of high-strength and mild structural steels at elevated temperatures, which is important for fire-resistant design. It then provides background on fire outbreaks and structural response, current fire design approaches, and the objectives of studying the behavior of structural steel joints and their critical elements under high temperatures. The document also reviews literature on standard fire tests and full-scale tests, and investigates the behavior of steel connections in fires. It examines the stress-strain behavior and degradation of steel properties at elevated temperatures. Finally, it describes the structural configuration of the steel joint being analyzed.
This presentation gives a brief introduction to chemical heat treatment of steels and surface hardening techniques
Keywords: Carburising, Nitriding, Carbonitriding, Flame hardening, Laser hardening, Induction hardening
This document provides an overview of metal heat treating presented by various individuals. It discusses what metal heat treating is, where it is used, why and how it is done, common heat treating processes and equipment. Specific details covered include commonly heat treated metals, types of heat treating furnaces, importance of protective atmospheres, and different heat treating processes like annealing. The document is intended to educate about key aspects of industrial metal heat treating.
This document discusses various heat treatments that can be used on steels, including:
- Annealing treatments like full annealing, recrystallization annealing, stress relief annealing, and spheroidization annealing.
- Normalizing to refine grain structure, harden slightly, and reduce segregation.
- Hardening by heating above the transformation temperatures and quenching to form martensite, followed by tempering.
- Factors that influence the severity of quenching and hardenability of steels, such as the quenching medium, agitation level, and alloying elements. Microstructures can vary from surface to interior based on cooling rate.
This document provides information about gas welding and cutting. It discusses oxy-fuel welding, which uses oxygen and acetylene gases to produce a flame over 5700°F that can melt metals. Cutting uses the flame to preheat and then pure oxygen to burn away metal. The document describes the equipment used, including oxygen and acetylene cylinders, regulators, hoses, and torches. It explains the chemical reactions that produce the high temperature flame and discusses properties of acetylene such as its heat output. Advantages and limitations of oxy-fuel welding are also outlined.
Microstructual Analysis Of Heat Treated EN8 SteelSourav Mahato
The document discusses heat treatment processes including quenching, annealing, normalizing, and tempering that are performed on EN-8 steel. Specifically, it describes treating EN-8 steel samples via quenching, annealing, and normalizing, followed by single tempering. The treated samples are then tested for tensile strength using a universal testing machine and hardness is compared. Microstructures of samples after different heat treatments are also examined.
This document discusses various heat treatment processes for steels including annealing, normalizing, hardening, tempering, and case hardening. It explains that annealing involves heating metals above or below critical temperatures and slowly cooling to make the metal soft. Hardening involves heating steel above its critical temperature then quenching in water to form martensite and make the metal very hard. Tempering is used after hardening to reduce brittleness by reheating to 220-300 degrees C. Case hardening, such as carburizing or nitriding, adds carbon or nitrogen to the surface layer to harden low-carbon steels. Methods of measuring temperature in furnaces like pyrometers and Seger cones are also summarized
The document discusses various heat treatment processes used in engineering:
1) Annealing makes metals softer by heating above critical temperatures and slowly cooling. Normalizing removes internal stresses by heating above critical temperatures and air cooling faster than annealing.
2) Hardening involves heating steel above critical temperatures, quenching quickly in water to form martensite, and making the metal very hard. Tempering then removes some brittleness by reheating to 220-300 degrees.
3) Case hardening methods like pack carburizing, salt bath carburizing, and gas carburizing add carbon to the surface to create a hard outer case over a softer core. Induction and flame hardening also
The document provides information about heat treatment processes. It defines heat treatment as a process of heating and cooling metals and alloys in the solid state to change their properties. Heat treatment is done to change properties like strength, hardness, toughness etc. of steels. The key heat treatment processes described are annealing, normalizing, hardening and tempering. Annealing involves heating steel above or below its critical temperature, holding, and slow cooling to soften it and relieve stresses. The goals, processes, and effects of various annealing types like full annealing and spheroidizing annealing are explained.
STUDY OF MICRO STRUCTURE OF HEAT TREATED EN8 STEELAkhil Raj U R
The document discusses heat treatment processes used to alter the physical and chemical properties of materials like metals. It focuses on the heat treatment of EN8 steel and describes how processes like annealing, normalizing, and quenching can be used to manipulate a metal's microstructure and properties. The key points are:
- Heat treatment involves heating metals to alter properties like hardness, strength and toughness. It controls diffusion and the rate of cooling to manipulate grain size and composition.
- The microstructure, allotropes, and composition of metals determine how they respond to heat treatments. Hypoeutectoid, eutectoid, and hypereutectoid alloys form different microstructures like ferrite or
Quenching is a vital part of the heat treating process in manufacturing. This presentation by Houghton International will show you how to master the process for the most efficient quenching and heat treating operations.
This document describes a project to test flame hardening on low carbon steels. It discusses low carbon steels, their properties and applications. It then describes the process of flame hardening and how it was used in this project to selectively harden the surface of steel samples. Brinell hardness tests were conducted on the samples to analyze the hardness at the surface (case) versus the core after flame hardening. The results and conclusions from this analysis are presented.
This document discusses post weld heat treatment (PWHT). It describes how welding causes residual stresses and microstructural changes in the heat affected zone (HAZ) that can lead to cracking. PWHT involves controlled heating and cooling to relieve residual stresses and improve properties. The key aspects covered include:
- PWHT relieves residual stresses and improves toughness by altering the HAZ microstructure.
- Preheating the metal prior to welding reduces cooling rates and residual stresses. The required preheat temperature depends on material thickness and carbon content.
- Thermal stress relief involves heating to just below the recrystallization temperature to allow stress relaxation. Proper heating and cooling rates are important.
This document discusses various heat treatment processes including annealing, hardening, and tempering. Annealing involves heating metals to specific temperatures to soften them and make them easier to shape. Hardening involves heating steel above its critical temperature then quenching to form martensite, making the steel very hard but brittle. Tempering is then used to reduce brittleness by reheating hardened steel to lower temperatures. The document provides details on the purposes and procedures for various annealing, hardening, and tempering techniques.
This document provides information on various heat treatment processes including annealing, normalizing, hardening, and tempering. It defines heat treatment as any process of heating and cooling metals to alter their properties. Annealing aims to relieve stresses and refine grains, while normalizing also improves properties. Hardening involves heating steel to form austenite and then quenching to form martensite. Tempering reduces brittleness caused by hardening. Specific methods like flame hardening and induction hardening selectively harden surfaces. Case hardening diffuses carbon or nitrogen into surfaces to create a hard case over a tough core.
Relazione annuale inerente al censimento dei funghi eduli nella zona dell'ospedale "S. Maria degli Angeli" di Sacile, relativa all'anno 2013.
[NB]: La reale visualizzazione delle slide non è a scorrimento, ma tramite i link presenti in fondo alle diapositive. Scaricare la presentazione per una visione ottimale.
This document provides an overview of Maven, including:
1. It describes how to install Maven and configure user-specific settings and repositories.
2. It explains the basic components of a Maven project including the pom.xml file, dependencies, and packaging.
3. It outlines Maven's build lifecycle of compiling, testing, packaging, and deploying a project as well as how to define dependencies and repositories.
This document is a letter from Indigo Marketing Group promoting their direct mail services to Ford BPN dealers. It emphasizes that their direct mail campaigns can effectively reach over 10,000 potential commercial truck customers annually for as little as $4,800, with 50% of production costs reimbursed through Ford's co-op advertising program. Indigo also claims to handle all necessary paperwork and have access to Ford's newest products, artwork, and incentives.
Spring, web service, web server, eclipse by a introduction sandesh sharmaSandesh Sharma
This document discusses Spring, a Java framework for building web applications. It describes key Spring concepts like dependency injection, inversion of control, and beans. It explains how Spring uses dependency injection to reduce coupling between objects. It also covers Spring annotations like @Component, @Controller, and @Repository that can be used to define beans. The document provides an example XML configuration file for configuring a Spring application context. It briefly mentions Tomcat as a web server that can run Spring web applications and the Eclipse IDE for developing Spring applications.
El documento define clases para representar personas, estudiantes, profesores, departamentos, cursos y calificaciones en una universidad. Las clases Persona, Estudiante y Profesor tienen atributos como nombre, fecha de nacimiento y dirección. Profesor extiende de Persona y añade atributos como categoría y salario. Estudiante extiende de Persona y añade titulación. Se definen relaciones entre las clases como que un profesor trabaja en un departamento o que un estudiante cursa asignaturas. El documento también inclu
Morte de chávez e a volta da autonomia petrolífera dos euaSilva Gomes
1) A morte de Hugo Chávez deixa a Venezuela vulnerável em meio à crescente autonomia de petróleo dos EUA;
2) A produção de petróleo da Venezuela caiu 30% sob o governo Chávez, enquanto a produção dos EUA se aproxima da Arábia Saudita;
3) A ascensão dos EUA como grande produtor de petróleo e gás terá grandes implicações geopolíticas e econômicas.
OOP and java by a introduction sandesh sharmaSandesh Sharma
This document provides an overview of object-oriented programming concepts in Java including objects and classes, encapsulation, inheritance, polymorphism, and language basics. It discusses key OOP concepts like access modifiers, constructors, interfaces, nested classes, anonymous classes, method overloading. It also covers polymorphism through examples. Finally, it lists some important methods like clone, equals, finalize and language features like final, abstract keywords and exception handling.
This document discusses automated code review processes and available tools. It describes Gerrit and SONAR as tools that can integrate with continuous integration environments to automatically check code for potential bugs, design issues, coding standards, and more. Gerrit allows for collaborative peer code reviews through a commit-to-deploy pipeline. It notifies developers and provides dashboards. SONAR provides a wider range of quality checks through plugins and generates interactive reports on issues. Both tools can integrate with version control and build systems like SVN, Maven, and Ant.
This document provides an introduction to service-oriented architecture (SOA). It discusses key concepts of SOA including loose coupling, implementation neutrality, and granularity. It explains that a service is an autonomous unit of automated business logic that is accessible to other systems. A SOA is a collection of services that are classified into types and layers and governed by architectural patterns and policies. The document outlines several principles for designing services, such as abstraction, reusability, composability, and autonomy.
Levi Strauss arrived in San Francisco in 1853 and opened a wholesale dry goods business. In 1873, Levi Strauss & Jacob Davis were granted a patent for riveting pants. Today, Levi's sells denim pants, non-denim pants, shirts, jackets and other apparel worldwide under brands like Levi's, Dockers, Denizen. The company focuses on quality, fit, fabric, features and targets various market segments with different product lines and pricing. Levi's uses advertising, promotions, and brand ambassadors like Bollywood stars to promote their jeans and apparel.
Core java by a introduction sandesh sharmaSandesh Sharma
This document provides an overview of core Java concepts including primitive types, wrappers, static methods and blocks, strings, abstract classes and interfaces, collections, equals and hashcode methods, and threads. It defines each concept, provides examples of usage, and notes key behaviors and properties. The document serves as a reference for fundamental Java programming concepts.
This document discusses different types of stitches and seams. It begins by defining what a stitch is according to British standards. It then describes various stitch properties like length, width, depth, tension and consistency. It classifies stitches into 6 main classes based on their structure and method of interlacing. These include single thread chain stitch, hand stitch, lock stitch, multi thread chain stitch, overlock stitch and covering chain stitch. Each class has various sub-classes that are used for specific purposes. The document also defines seams and classifies them into 4 main types - plain seam, lapped seam, bound seam and flat seam based on their structure and use.
This document discusses metallurgical concepts related to welding, including:
1) Welding affects the mechanical properties of metals through metallurgical transformations in the heat-affected zone. Finer microstructures improve properties like strength and toughness.
2) Alloying and heat treatments can change microstructures and properties. Quenching produces martensite to increase hardness and strength. Tempering relieves stresses in martensite.
3) Preheating and controlling cooling rates in welding prevents cracking by allowing formation of microstructures besides martensite like ferrite and pearlite.
The document discusses heat treatment and metal fabrication processes. It begins by defining heat treatment as a method to alter the physical and chemical properties of a material through heating and cooling. It then describes various metal fabrication techniques like forging, rolling, extrusion, and casting. The remainder of the document discusses heat treatment processes for steel like annealing, normalizing, and stress relief annealing. It explains how these processes are used to achieve desired microstructures and properties without changing the shape of the material.
The document discusses the heat treatment process of annealing. It begins by defining heat treatment as heating a metal to a specified temperature, keeping it at that temperature for a period of time, then cooling at a specified rate. Annealing is described as a heat treatment that involves heating metal above its recrystallization temperature, holding for some time, then slowly cooling to develop an equilibrium structure with increased ductility. The document outlines the stages of annealing as recovery, recrystallization, and grain growth.
This document provides information on various heat treatment processes for steel, including annealing, normalizing, hardening, and tempering. It describes the purposes and procedures for each process. Key points include:
- Annealing involves heating steel above the upper critical temperature, then slow cooling to relieve stresses and improve ductility.
- Normalizing also involves heating above the upper critical temperature, but the steel is air cooled to refine grain size while retaining some strength.
- Hardening greatly increases strength by heating steel to the austenitizing temperature then quenching in water or oil to form martensite.
- Tempering is then used to reduce brittleness by reheating hardened steel to lower temperatures.
The document discusses various heat treatment processes. It defines heat treatment as operations involving heating and cooling of metals/alloys in their solid state to obtain desirable properties. It describes the stages of heat treatment as heating, soaking, and cooling. It then discusses various heat treatment processes like annealing, normalizing, hardening, and tempering in detail including their purposes, methods, and effects on material properties.
In order for metal workpiece to have required working properties, a heat treatment process is often necessary. Heat treatment process generally includes three processes of heating, heat preservation and cooling. It is divided into quenching, tempering, normalizing, annealing, etc. depending on process. Can you distinguish it?
The document provides an outline on heat treatment processes. It defines heat treatment and its purposes, discusses heat treatment theory and the stages of heat treatment including heating, soaking, and cooling. It describes various heat treatment processes like annealing, normalizing, hardening, and tempering. It also discusses case hardening techniques like carburizing, cyaniding, and nitriding. Finally, it introduces the TTT diagram and the microstructures obtained from different cooling rates.
This document discusses various heat treatment processes and their effects on carbon steel properties. It describes the main heat treatment types of annealing, normalizing, hardening, carburizing, and tempering. For each it provides details on the heating temperatures, soaking times, cooling methods and their purposes such as relieving stresses, improving machinability, or inducing hardness. Hardening is described as heating steel above its critical temperature then quenching to form martensite, while tempering removes brittleness. Case hardening through carburizing and methods like pack, salt bath, and gas carburizing are also summarized.
Material Engineering,
Heat treating (or heat treatment) is a group of industrial and metalworking processes used to alter the physical, and sometimes chemical, properties of a material. The most common application is metallurgical. Heat treatments are also used in the manufacture of many other materials, such as glass. Heat treatment involves the use of heating or chilling, normally to extreme temperatures, to achieve a desired result such as hardening or softening of a material. Heat treatment techniques include annealing, case hardening, precipitation strengthening, tempering, carburizing, normalizing and quenching
Heat treatment involves altering the physical and mechanical properties of metals through heating and cooling processes. There are several stages and types of heat treatment, including annealing, normalizing, hardening, carburizing, and tempering. Annealing involves slowly cooling heated metal to make it more machinable and reduce internal stresses. Hardening rapidly cools heated metal to increase its hardness and strength. Tempering reheats hardened metal to make it less brittle while maintaining hardness. Heat treatment is used to modify properties like hardness, strength, toughness, and wear resistance of metals including steel.
Heat treatment of Steel by Prof Altafhussain G MominMr.Momin (M.Tech)
This document discusses various heat treatment processes for steel, including annealing, normalizing, stress relieving, hardening, tempering, case hardening, and age hardening. Annealing makes steel soft by heating and slow cooling. Normalizing removes internal stresses by heating and faster cooling. Hardening involves heating steel above its critical temperature and quenching to form martensite, making the steel very hard. Tempering is then used to reduce brittleness by reheating the hardened steel. Case hardening techniques like carburizing add carbon to the surface to create a hard exterior. Measurement of furnace temperatures involves techniques like using Seger cones or pyrometers.
This document describes various heat treatment processes and their purposes. It explains processes like tempering, annealing, normalizing and hardening. Quenching involves rapidly cooling steel above its transformation temperature to produce martensite and increase hardness. Tempering reduces brittleness and stresses caused by quenching. Annealing softens metals by slowly cooling after heating. Normalizing heats steel to a higher temperature than annealing before air cooling to reduce stresses. The document provides examples of applying hardening and case hardening processes and recommends heat treatments for different steel types based on required properties.
Heat treatment is a process of heating and cooling metals and alloys to achieve desired properties. There are various heat treatment processes classified based on temperature, phase transformation or purpose. Common processes include annealing, normalizing, hardening, and tempering. Annealing relieves stresses and improves ductility while normalizing produces harder and stronger steel. Hardening involves rapid cooling from an elevated temperature to produce a hard surface. Tempering is used to reduce brittleness caused by hardening.
The document discusses various heat treatment processes used to alter the properties of metals and alloys. It describes processes like annealing, normalizing, hardening, and tempering. Annealing is used to relieve stress, soften metals, and refine grain size. Normalizing produces a uniform structure and relieves stresses. Hardening involves heating metal and rapidly cooling to produce martensite for hardness. Tempering is then used to reduce brittleness caused by hardening. The document also discusses diagrams like TTT and CCT that are used to determine the effects of different cooling rates on microstructure formation.
The document discusses heat treatment processes used to alter the properties of metals and alloys. It describes various heat treatment methods like annealing, normalizing, hardening, and tempering. Annealing is used to relieve stress, induce softness, refine grain size, and remove gases. Normalizing involves heating above the critical temperature and air cooling to refine grain size and relieve stress. Hardening involves heating and quenching to produce martensite for hardness. Tempering is used after hardening to reduce brittleness by reheating and slow cooling. The document provides details on the purposes, procedures, and applications of different heat treatment techniques.
The document discusses various heat treatment processes used to alter the properties of metals and alloys. It describes processes like annealing, normalizing, hardening, and tempering. Annealing is used to relieve stress, soften metals, and refine grain size. Normalizing produces a uniform structure and relieves stresses. Hardening involves heating metal and rapidly cooling to produce martensite for hardness. Tempering is then used to reduce brittleness caused by hardening. The document also discusses diagrams like TTT and CCT that are used to determine the effects of different cooling rates on microstructure formation.
The document discusses various heat treatment processes used to alter the properties of metals and alloys. It describes processes like annealing, normalizing, hardening, and tempering. Annealing is used to relieve stress and induce softness. Normalizing increases strength and achieves a uniform structure. Hardening through quenching improves hardness but causes brittleness, which tempering relieves by controlled reheating. The Jominy end quench test measures a steel's hardenability or ability to harden uniformly during quenching.
This document discusses various heat treatment processes for altering the properties of metals including annealing, hardening, tempering, and case hardening. It explains that annealing is used to soften metals by slowly cooling after heating. Hardening involves heating metals above critical temperatures and quenching in water to produce very hard but brittle materials. Tempering is then used to reduce brittleness by reheating hardened metals. Case hardening techniques like carburizing add carbon to the surface to create a hard outer case over a soft core. The document also covers methods of measuring temperature in furnaces like using Seger cones or thermoelectric pyrometers.
it describes the bony anatomy including the femoral head , acetabulum, labrum . also discusses the capsule , ligaments . muscle that act on the hip joint and the range of motion are outlined. factors affecting hip joint stability and weight transmission through the joint are summarized.
বাংলাদেশের অর্থনৈতিক সমীক্ষা ২০২৪ [Bangladesh Economic Review 2024 Bangla.pdf] কম্পিউটার , ট্যাব ও স্মার্ট ফোন ভার্সন সহ সম্পূর্ণ বাংলা ই-বুক বা pdf বই " সুচিপত্র ...বুকমার্ক মেনু 🔖 ও হাইপার লিংক মেনু 📝👆 যুক্ত ..
আমাদের সবার জন্য খুব খুব গুরুত্বপূর্ণ একটি বই ..বিসিএস, ব্যাংক, ইউনিভার্সিটি ভর্তি ও যে কোন প্রতিযোগিতা মূলক পরীক্ষার জন্য এর খুব ইম্পরট্যান্ট একটি বিষয় ...তাছাড়া বাংলাদেশের সাম্প্রতিক যে কোন ডাটা বা তথ্য এই বইতে পাবেন ...
তাই একজন নাগরিক হিসাবে এই তথ্য গুলো আপনার জানা প্রয়োজন ...।
বিসিএস ও ব্যাংক এর লিখিত পরীক্ষা ...+এছাড়া মাধ্যমিক ও উচ্চমাধ্যমিকের স্টুডেন্টদের জন্য অনেক কাজে আসবে ...
Main Java[All of the Base Concepts}.docxadhitya5119
This is part 1 of my Java Learning Journey. This Contains Custom methods, classes, constructors, packages, multithreading , try- catch block, finally block and more.
Walmart Business+ and Spark Good for Nonprofits.pdfTechSoup
"Learn about all the ways Walmart supports nonprofit organizations.
You will hear from Liz Willett, the Head of Nonprofits, and hear about what Walmart is doing to help nonprofits, including Walmart Business and Spark Good. Walmart Business+ is a new offer for nonprofits that offers discounts and also streamlines nonprofits order and expense tracking, saving time and money.
The webinar may also give some examples on how nonprofits can best leverage Walmart Business+.
The event will cover the following::
Walmart Business + (https://business.walmart.com/plus) is a new shopping experience for nonprofits, schools, and local business customers that connects an exclusive online shopping experience to stores. Benefits include free delivery and shipping, a 'Spend Analytics” feature, special discounts, deals and tax-exempt shopping.
Special TechSoup offer for a free 180 days membership, and up to $150 in discounts on eligible orders.
Spark Good (walmart.com/sparkgood) is a charitable platform that enables nonprofits to receive donations directly from customers and associates.
Answers about how you can do more with Walmart!"
How to Make a Field Mandatory in Odoo 17Celine George
In Odoo, making a field required can be done through both Python code and XML views. When you set the required attribute to True in Python code, it makes the field required across all views where it's used. Conversely, when you set the required attribute in XML views, it makes the field required only in the context of that particular view.
Chapter wise All Notes of First year Basic Civil Engineering.pptxDenish Jangid
Chapter wise All Notes of First year Basic Civil Engineering
Syllabus
Chapter-1
Introduction to objective, scope and outcome the subject
Chapter 2
Introduction: Scope and Specialization of Civil Engineering, Role of civil Engineer in Society, Impact of infrastructural development on economy of country.
Chapter 3
Surveying: Object Principles & Types of Surveying; Site Plans, Plans & Maps; Scales & Unit of different Measurements.
Linear Measurements: Instruments used. Linear Measurement by Tape, Ranging out Survey Lines and overcoming Obstructions; Measurements on sloping ground; Tape corrections, conventional symbols. Angular Measurements: Instruments used; Introduction to Compass Surveying, Bearings and Longitude & Latitude of a Line, Introduction to total station.
Levelling: Instrument used Object of levelling, Methods of levelling in brief, and Contour maps.
Chapter 4
Buildings: Selection of site for Buildings, Layout of Building Plan, Types of buildings, Plinth area, carpet area, floor space index, Introduction to building byelaws, concept of sun light & ventilation. Components of Buildings & their functions, Basic concept of R.C.C., Introduction to types of foundation
Chapter 5
Transportation: Introduction to Transportation Engineering; Traffic and Road Safety: Types and Characteristics of Various Modes of Transportation; Various Road Traffic Signs, Causes of Accidents and Road Safety Measures.
Chapter 6
Environmental Engineering: Environmental Pollution, Environmental Acts and Regulations, Functional Concepts of Ecology, Basics of Species, Biodiversity, Ecosystem, Hydrological Cycle; Chemical Cycles: Carbon, Nitrogen & Phosphorus; Energy Flow in Ecosystems.
Water Pollution: Water Quality standards, Introduction to Treatment & Disposal of Waste Water. Reuse and Saving of Water, Rain Water Harvesting. Solid Waste Management: Classification of Solid Waste, Collection, Transportation and Disposal of Solid. Recycling of Solid Waste: Energy Recovery, Sanitary Landfill, On-Site Sanitation. Air & Noise Pollution: Primary and Secondary air pollutants, Harmful effects of Air Pollution, Control of Air Pollution. . Noise Pollution Harmful Effects of noise pollution, control of noise pollution, Global warming & Climate Change, Ozone depletion, Greenhouse effect
Text Books:
1. Palancharmy, Basic Civil Engineering, McGraw Hill publishers.
2. Satheesh Gopi, Basic Civil Engineering, Pearson Publishers.
3. Ketki Rangwala Dalal, Essentials of Civil Engineering, Charotar Publishing House.
4. BCP, Surveying volume 1
This presentation was provided by Steph Pollock of The American Psychological Association’s Journals Program, and Damita Snow, of The American Society of Civil Engineers (ASCE), for the initial session of NISO's 2024 Training Series "DEIA in the Scholarly Landscape." Session One: 'Setting Expectations: a DEIA Primer,' was held June 6, 2024.
A workshop hosted by the South African Journal of Science aimed at postgraduate students and early career researchers with little or no experience in writing and publishing journal articles.
South African Journal of Science: Writing with integrity workshop (2024)
14250 ch2
1. CHAPTER 2
BASIC HEAT TREATMENT
As Steelworkers, we are interested in the heat treat- water vapor, and other various hydrocarbons. Fuel-fired
ment of metals, because we have to know what effects furnaces can provide three distinct atmospheres when
the heat produced by welding or cutting has on metal. you vary the proportions of air and fuel. They are called
We also need to know the methods used to restore metal oxidizing, reducing, and neutral.
to its original condition. The process of heat treating is
the method by which metals are heated and cooled in a
STAGES OF HEAT TREATMENT
series of specific operations that never allow the metal
to reach the molten state. The purpose of heat treating is Heat treating is accomplished in three major stages:
to make a metal more useful by changing or restoring
l Stage l—Heating the metal slowly to ensure a
its mechanical properties. Through heat treating, we can
make a metal harder, stronger, and more resistant to uniform temperature
impact. Also, heat treating can make a metal softer and l Stage 2—Soaking (holding) the metal at a given
more ductile. The one disadvantage is that no heat-treat- temperature for a given time and cooling the
ing procedure can produce all of these characteristics in metal to room temperature
one operation. Some properties are improved at the
expense of others; for example, hardening a metal may l Stage 3—Cooling the metal to room temperature
make it brittle.
HEATING STAGE
HEAT-TREATING THEORY The primary objective in the heating stage is to
maintain uniform temperatures. If uneven heating oc-
The various types of heat-treating processes are
curs, one section of a part can expand faster than another
similar because they all involve the heating and cooling
and result in distortion or cracking. Uniform tempera-
of metals; they differ in the heating temperatures and the tures are attained by slow heating.
cooling rates used and the final results. The usual meth-
ods of heat-treating ferrous metals (metals with iron) are The heating rate of a part depends on several factors.
annealing, normalizing, hardening, and tempering. One important factor is the heat conductivity of the
Most nonferrous metals can be annealed, but never metal. A metal with a high-heat conductivity heats at a
tempered, normalized, or case-hardened. faster rate than one with a low conductivity. Also, the
condition of the metal determines the rate at which it
Successful heat treatment requires close control
may be heated. The heating rate for hardened tools and
over all factors affecting the heating and cooling of a
parts should be slower than unstressed or untreated
metal. This control is possible only when the proper
metals. Finally, size and cross section figure into the
equipment is available. The furnace must be of the heating rate. Parts with a large cross section require
proper size and type and controlled, so the temperatures slower heating rates to allow the interior temperature to
are kept within the prescribed limits for each operation. remain close to the surface temperature that prevents
Even the furnace atmosphere affects the condition of the
warping or cracking. Parts with uneven cross sections
metal being heat-treated.
experience uneven heating; however, such parts are less
The furnace atmosphere consists of the gases that apt to be cracked or excessively warped when the heat-
circulate throughout the heating chamber and surround ing rate is kept slow.
the metal, as it is being heated. In an electric furnace,
the atmosphere is either air or a controlled mixture of SOAKING STAGE
gases. In a fuel-fired furnace, the atmosphere is the
mixture of gases that comes from the combination of the After the metal is heated to the proper temperature,
air and the gases released by the fuel during combustion. it is held at that temperature until the desired internal
These gases contain various proportions of carbon mon- structural changes take place. This process is called
oxide, carbon dioxide, hydrogen, nitrogen, oxygen, SOAKING. The length of time held at the proper
2-1
2. temperature is called the SOAKING PERIOD. The is used for metals that require a rapid cooling rate, and
soaking period depends on the chemical analysis of the oil mixtures are more suitable for metals that need a
metal and the mass of the part. When steel parts are slower rate of cooling. Generally, carbon steels are
uneven in cross section, the soaking period is deter- water-hardened and alloy steels are oil-hardened. Non-
mined by the largest section. ferrous metals are normally quenched in water.
During the soaking stage, the temperature of the
metal is rarely brought from room temperature to the
HEAT COLORS FOR STEEL
final temperature in one operation; instead, the steel is
slowly heated to a temperature just below the point at You are probably familiar with the term red-hot as
which the change takes place and then it is held at that applied to steel. Actually, steel takes on several colors
temperature until the heat is equalized throughout the and shades from the time it turns a dull red until it
metal. We call this process PREHEATING. Following reaches a white heat. These colors and the correspond-
preheat, the metal is quickly heated to the final required ing temperatures are listed in table 2-1.
temperature.
During hardening, normalizing, and annealing,
When apart has an intricate design, it may have to steel is heated to various temperatures that produce
be preheated at more than one temperature to prevent color changes. By observing these changes, you can
cracking and excessive warping. For example, assume determine the temperature of the steel. As an example,
an intricate part needs to be heated to 1500°F for hard- assume that you must harden a steel part at 1500°F. Heat
ening. This part could be slowly heated to 600°F, soaked the part slowly and evenly while watching it closely for
at this temperature, then heated slowly to 1200°F, and any change in color. Once the steel begins to turn red,
then soaked at that temperature. Following the final carefully note each change in shade. Continue the even
preheat, the part should then be heated quickly to the heating until the steel is bright red; then quench the part.
hardening temperature of 1500°F.
The success of a heat-treating operation depends
NOTE: Nonferrous metals are seldom preheated, largely on your judgment and the accuracy with which
because they usually do not require it, and preheating you identify each color with its corresponding tempera-
can cause an increase in the grain size in these metals. ture. From a study of table 2-1, you can see that close
observation is necessary. You must be able to tell the
COOLING STAGE difference between faint red and blood red and between
dark cherry and medium cherry. To add to the difficulty,
your conception of medium cherry may differ from that
After a metal has been soaked, it must be returned of the person who prepared the table. For an actual
to room temperature to complete the heat-treating proc- heat-treating operation, you should get a chart showing
ess. To cool the metal, you can place it in direct contact the actual colors of steel at various temperatures.
with a COOLING MEDIUM composed of a gas, liquid,
solid, or combination of these. The rate at which the
metal is cooled depends on the metal and the properties
TYPES OF HEAT TREATMENT
desired. The rate of cooling depends on the medium;
therefore, the choice of a cooling medium has an impor- Four basic types of heat treatment are used today.
tant influence on the properties desired. They are annealing, normalizing, hardening, and tem-
pering. The techniques used in each process and how
Quenching is the procedure used for cooling metal
they relate to Steelworkers are given in the following
rapidly in oil, water, brine, or some other medium.
paragraphs.
Because most metals are cooled rapidly during the hard-
ening process, quenching is usually associated with
ANNEALING
hardening; however, quenching does not always result
in an increase in hardness; for example, to anneal cop-
In general, annealing is the opposite of hardening,
per, you usually quench it in water. Other metals, such
You anneal metals to relieve internal stresses, soften
as air-hardened steels, are cooled at a relatively slow rate
them, make them more ductile, and refine their grain
for hardening.
structures. Annealing consists of heating a metal to a
Some metals crack easily or warp during quenching, specific temperature, holding it at that temperature for
and others suffer no ill effects; therefore, the quenching a set length of time, and then cooling the metal to room
medium must be chosen to fit the metal. Brine or water temperature. The cooling method depends on the
2-2
3. Table 2-1.—Heat Colors for Steel
Table 2-2.—Approximate Soaking Periods for Hardening, Annealing, and Normalizing Steel
metal and the properties desired. Some metals are Ferrous Metal
furnace-cooled, and others are cooled by burying them
To produce the maximum softness in steel, you heat
in ashes, lime, or other insulating materials.
the metal to its proper temperature, soak it, and then let
Welding produces areas that have molten metal next it cool very slowly. The cooling is done by burying the
to other areas that are at room temperature. As the weld hot part in an insulating material or by shutting off the
furnace and allowing the furnace and the part to cool
cools, internal stresses occur along with hard spots and
together. The soaking period depends on both the mass
brittleness. Welding can actually weaken the metal.
of the part and the type of metal. The approximate
Annealing is just one of the methods for correcting these soaking periods for annealing steel are given in tablc
problems. 2-2.
2-3
4. Steel with an extremely low-carbon content re- HARDENING
quires the highest annealing temperature. As the carbon
content increases, the annealing temperatures decrease. The hardening treatment for most steels consists of
heating the steel to a set temperature and then cooling it
rapidly by plunging it into oil, water, or brine. Most
Nonferrous Metal
steels require rapid cooling (quenching) for hardening
but a few can be air-cooled with the same results.
Copper becomes hard and brittle when mechani- Hardening increases the hardness and strength of the
cally worked; however, it can be made soft again by steel, but makes it less ductile. Generally, the harder the
annealing. The annealing temperature for copper is be- steel, the more brittle it becomes. To remove some of
tween 700°F and 900°F. Copper maybe cooled rapidly the brittleness, you should temper the steel after hard-
or slowly since the cooling rate has no effect on the heat ening.
treatment. The one drawback experienced in annealing
Many nonferrous metals can be hardened and their
copper is the phenomenon called “hot shortness.” At
strength increased by controlled heating and rapid cool-
about 900°F, copper loses its tensile strength, and if not
ing. In this case, the process is called heat treatment,
properly supported, it could fracture.
rather than hardening.
Aluminum reacts similar to copper when heat treat-
To harden steel, you cool the metal rapidly after
ing. It also has the characteristic of “hot shortness.” A
number of aluminum alloys exist and each requires thoroughly soaking it at a temperature slightly above its
special heat treatment to produce their best properties. upper critical point. The approximate soaking periods
for hardening steel are listed in table 2-2. The addition
of alloys to steel decreases the cooling rate required to
NORMALIZING produce hardness. A decrease in the cooling rate is an
advantage, since it lessens the danger of cracking and
warping.
Normalizing is a type of heat treatment applicable
to ferrous metals only. It differs from annealing in that Pure iron, wrought iron, and extremely low-carbon
the metal is heated to a higher temperature and then steels have very little hardening properties and are dif-
removed from the furnace for air cooling. ficult to harden by heat treatment. Cast iron has limited
The purpose of normalizing is to remove the internal capabilities for hardening. When you cool cast iron
stresses induced by heat treating, welding, casting, forg- rapidly, it forms white iron, which is hard and brittle.
ing, forming, or machining. Stress, if not controlled, And when you cool it slowly, it forms gray iron, which
leads to metal failure; therefore, before hardening steel, is soft but brittle under impact.
you should normalize it first to ensure the maximum In plain carbon steel, the maximum hardness ob-
desired results. Usually, low-carbon steels do not re- tained by heat treatment depends almost entirely on the
quire normalizing; however, if these steels are normal-
carbon content of the steel. As the carbon content in-
ized, no harmful effects result. Castings are usually
creases, the hardening ability of the steel increases;
annealed, rather than normalized; however, some cast-
however, this capability of hardening with an increase
ings require the normalizing treatment. Table 2-2 shows
in carbon content continues only to a certain point. In
the approximate soaking periods for normalizing steel.
Note that the soaking time varies with the thickness of practice, 0.80 percent carbon is required for maximum
the metal. hardness. When you increase the carbon content beyond
0.80 percent, there is no increase in hardness, but there
Normalized steels are harder and stronger than an- is an increase in wear resistance. This increase in wear
nealed steels. In the normalized condition, steel is much resistance is due to the formation of a substance called
tougher than in any other structural condition. Parts hard cementite.
subjected to impact and those that require maximum
toughness with resistance to external stress are usually When you alloy steel to increase its hardness, the
normalized. In normalizing, the mass of metal has an alloys make the carbon more effective in increasing
influence on the cooling rate and on the resulting struc- hardness and strength. Because of this, the carbon con-
ture. Thin pieces cool faster and are harder after normal- tent required to produce maximum hardness is lower
izing than thick ones. In annealing (furnace cooling), the than it is for plain carbon steels. Usually, alloy steels are
hardness of the two are about the same. superior to carbon steels.
2-4
5. Carbon steels are usually quenched in brine or heated in a furnace. To cool the parts, you can leave the
water, and alloy steels are generally quenched in oil. container in the furnace to cool or remove it and let it
When hardening carbon steel, remember that you must air cool. In both cases, the parts become annealed during
cool the steel to below 1000°F in less than 1 second. the slow cooling. The depth of the carbon penetration
When you add alloys to steel, the time limit for the depends on the length of the soaking period. With to-
temperature to drop below 1000°F increases above the day’s methods, carburizing is almost exclusively done
l-second limit, and a slower quenching medium can by gas atmospheres.
produce the desired hardness.
CYANIDING.— This process is a type of case
Quenching produces extremely high internal hardening that is fast and efficient. Preheated steel is
stresses in steel, and to relieve them, you can temper the dipped into a heated cyanide bath and allowed to soak.
steel just before it becomes cold. The part is removed Upon removal, it is quenched and then rinsed to remove
from the quenching bath at a temperature of about 200°F any residual cyanide. This process produces a thin, hard
and allowed to air-cool. The temperature range from shell that is harder than the one produced by carburizing
200°F down to room temperature is called the “cracking and can be completed in 20 to 30 minutes vice several
range” and you do not want the steel to pass through it. hours. The major drawback is that cyanide salts are a
In the following paragraphs, we discuss the differ- deadly poison.
ent methods of hardening that are commercially used.
NITRIDING.— This case-hardening method pro-
In the Seabees, we use a rapid surface hardening com-
duces the hardest surface of any of the hardening proc-
pound called “Case” that can be ordered through the
esses. It differs from the other methods in that the
Navy supply system. Information on the use of “Case”
individual parts have been heat-treated and tempered
is located in the Welding Materials Handbook, P-433.
before nitriding. The parts are then heated in a furnace
that has an ammonia gas atmosphere. No quenching is
Case Hardening required so there is no worry about warping or other
types of distortion. This process is used to case harden
Case hardening produces a hard, wear-resistant sur- items, such as gears, cylinder sleeves, camshafts and
face or case over a strong, tough core. The principal other engine parts, that need to be wear resistant and
forms of casehardening are carburizing, cyaniding, and operate in high-heat areas.
nitriding. Only ferrous metals are case-hardened.
Case hardening is ideal for parts that require a Flame Hardening
wear-resistant surface and must be tough enough inter-
nally to withstand heavy loading. The steels best suited
Flame hardening is another procedure that is used
for case hardening are the low-carbon and low-alloy
to harden the surface of metal parts. When you use an
series. When high-carbon steels are case-hardened, the
oxyacetylene flame, a thin layer at the surface of the part
hardness penetrates the core and causes brittleness. In
is rapidly heated to its critical temperature and then
case hardening, you change the surface of the metal
immediately quenched by a combination of a water
chemically by introducing a high carbide or nitride
spray and the cold base metal. This process produces a
content. The core remains chemically unaffected. When
thin, hardened surface, and at the same time, the internal
heat-treated, the high-carbon surface responds to hard-
parts retain their original properties. Whether the proc-
ening, and the core toughens.
ess is manual or mechanical, a close watch must be
CARBURIZING.— Carburizing is a case-harden- maintained, since the torches heat the metal rapidly and
ing process by which carbon is added to the surface of the temperatures are usually determined visually.
low-carbon steel. This results in a carburized steel that
Flame hardening may be either manual or automat-
has a high-carbon surface and a low-carbon interior.
ic. Automatic equipment produces uniform results and
When the carburized steel is heat-treated, the case be-
is more desirable. Most automatic machines have vari-
comes hardened and the core remains soft and tough.
able travel speeds and can be adapted to parts of various
Two methods are used for carburizing steel. One sizes and shapes. The size and shape of the torch de-
method consists of heating the steel in a furnace con- pends on the part. The torch consists of a mixing head,
taining a carbon monoxide atmosphere. The other straight extension tube, 90-degree extension head, an
method has the steel placed in a container packed with adjustable yoke, and a water-cooled tip. Practically any
charcoal or some other carbon-rich material and then shape or size flame-hardening tip is available (fig. 2-1).
2-5
6. Figure 2-2.—Progressive hardening.
hardening produces a hard case that is highly resistant
Figure 2-1.—Progressive hardening torch tip. to wear and a core that retains its original properties.
Flame hardening can be divided into five general
Tips are produced that can be used for hardening flats, methods: stationary, circular band progressive, straight-
rounds, gears, cams, cylinders, and other regular or line progressive, spiral band progressive, and circular
irregular shapes. band spinning.
In hardening localized areas, you should heat the STATIONARY METHOD.— In this method the
metal with a standard hand-held welding torch. Adjust torch and the metal part are both held stationary.
the torch flame to neutral (see chapter 4) for normal CIRCULAR BAND PROGRESSIVE METHOD.—
heating; however, in corners and grooves, use a slightly This method is used for hardening outside surfaces of
oxidizing flame to keep the torch from sputtering. You round sections. Usually, the object is rotated in front of
also should particularly guard against overheating in a stationary torch at a surface speed of from 3 to 12
comers and grooves. If dark streaks appear on the metal inches per minute. The heating and quenching are done
surface, this is a sign of overheating, and you need to progressively, as the part rotates; therefore, when the
increase the distance between the flame and the metal. part has completed one rotation, a hardened band encir-
For the best heating results, hold the torch with the cles the part. The width of the hardened band depends
tip of the inner cone about an eighth of an inch from the upon the width of the torch tip. To harden the full length
surface and direct the flame at right angles to the metal. of a long section, you can move the torch and repeat the
Sometimes it is necessary to change this angle to obtain process over and over until the part is completely hard-
better results; however, you rarely find a deviation of ened. Each pass or path of the torch should overlap the
more than 30 degrees. Regulate the speed of torch travel previous one to prevent soft spots.
according to the type of metal, the mass and shape of the STRAIGHT-LINE PROGRESSIVE METHOD.—
part, and the depth of hardness desired. With the straight-line progressive method, the torch
In addition, you must select the steel according to travels along the surface, treating a strip that is about the
the properties desired. Select carbon steel when surface same width as the torch tip. To harden wider areas, you
hardness is the primary factor and alloy steel when the move the torch and repeat the process. Figure 2-2 is an
physical properties of the core are also factors. Plain example of progressive hardening.
carbon steels should contain more than 0.35% carbon SPIRAL BAND PROGRESSIVE METHOD.—
for good results inflame hardening. For water quench- For this technique a cylindrical part is mounted between
ing, the effective carbon range is from 0.40% to 0.70%. lathe centers, and a torch with an adjustable holder is
Parts with a carbon content of more than 0.70% are mounted on the lathe carriage. As the part rotates, the
likely to surface crack unless the heating and quenching torch moves parallel to the surface of the part. This travel
rate are carefully controlled. is synchronized with the parts rotary motion to produce
The surface hardness of a flame-hardened section is a continuous band of hardness. Heating and quenching
equal to a section that was hardened by furnace heating occur at the same time. The number of torches required
and quenching. The decrease in hardness between the depends on the diameter of the part, but seldom are more
case and the core is gradual. Since the core is not than two torches used.
affected by flame hardening, there is little danger of CIRCULAR BAND SPINNING METHOD.—
spalling or flaking while the part is in use. Thus flame The circular band spinning method provides the best
2-6
7. results for hardening cylindrical parts of small or me- is more than 1 inch thick, increase the time by 1 hour for
dium diameters. The part is mounted between lathe each additional inch of thickness.
centers and turned at a high rate of speed pasta station-
Normally, the rate of cooling from the tempering
ary torch. Enough torches are placed side by side to heat
temperature has no effect on the steel. Steel parts are
the entire part. The part can be quenched by water
usually cooled in still air after being removed from the
flowing from the torch tips or in a separate operation.
tempering furnace; however, there are a few types of
When you perform heating and quenching as sepa- steel that must be quenched from the tempering tem-
rate operations, the tips are water-cooled internally, but perature to prevent brittleness. These blue brittle steels
no water sprays onto the surface of the part. can become brittle if heated in certain temperature
In flame hardening, you should follow the same ranges and allowed to cool slowly. Some of the nickel
safety precautions that apply to welding (see chapter 3). chromium steels are subject to this temper brittleness.
In particular, guard against holding the flame too close Steel may be tempered after being normalized, pro-
to the surface and overheating the metal. In judging the viding there is any hardness to temper. Annealed steel is
temperature of the metal, remember that the flame impossible to temper. Tempering relieves quenching
makes the metal appear colder than it actually is. stresses and reduces hardness and brittleness. Actually,
the tensile strength of a hardened steel may increase as
TEMPERING the steel is tempered up to a temperature of about 450°F.
Above this temperature it starts to decrease. Tempering
increases softness, ductility, malleability, and impact
After the hardening treatment is applied, steel is resistance. Again, high-speed steel is an exception to the
often harder than needed and is too brittle for most rule. High-speed steel increases in hardness on temper-
practical uses. Also, severe internal stresses are set up ing, provided it is tempered at a high temperature (about
during the rapid cooling from the hardening tempera- 1550°F). Remember, all steel should be removed from
ture. To relieve the internal stresses and reduce brittle- the quenching bath and tempered before it is complete] y
ness, you should temper the steel after it is hardened. cold. Failure to temper correctly results in a quick failure
Tempering consists of heating the steel to a specific of the hardened part.
temperature (below its hardening temperature), holding
it at that temperature for the required length of time, and Permanent steel magnets are made of special alloys
then cooling it, usually instill air. The resultant strength, and are heat-treated by hardening and tempering. Hard-
hardness, and ductility depend on the temperature to ness and stability are the most important properties in
which the steel is heated during the tempering process. permanent magnets. Magnets are tempered at the mini-
mum tempering temperature of 212°F by placing them
The purpose of tempering is to reduce the brittleness in boiling water for 2 to 4 hours. Because of this low-
imparted by hardening and to produce definite physical tempering temperature, magnets are very hard.
properties within the steel. Tempering always follows,
never precedes, the hardening operation. Besides reduc- Case-hardened parts should not be tempered at too
ing brittleness, tempering softens the steel. That is un- high a temperature or they may loose some of their
avoidable, and the amount of hardness that is lost hardness. Usually, a temperature range from 212°F to
depends on the temperature that the steel is heated to 400°F is high enough to relieve quenching stresses.
during the tempering process. That is true of all steels Some metals require no tempering. The design of the
except high-speed steel. Tempering increases the hard- part helps determine the tempering temperature.
ness of high-speed steel. Color tempering is based on the oxide colors that
Tempering is always conducted at temperatures be- appear on the surface of steel, as it is heated. When you
low the low-critical point of the steel. In this respect, slowly heat a piece of polished hardened steel, you can
tempering differs from annealing, normalizing, and see the surface turn various colors as the temperature
hardening in which the temperatures are above the upper changes. These colors indicate structural changes are
critical point. When hardened steel is reheated, temper- taking place within the metal. Once the proper color
ing begins at 212°F and continues as the temperature appears, the part is rapidly quenched to prevent further
increases toward the low-critical point. By selecting a structural change. In color tempering, the surface of the
definite tempering temperature, you can predetermine steel must be smooth and free of oil. The part may be
the resulting hardness and strength. The minimum tem- heated by a torch, in a furnace, over a hot plate, or by
perature time for tempering should be 1 hour. If the part radiation.
2-7
8. Table 2-3.—0xide Colors for Tempering Steel
Cold chisels and similar tools must have hard cut- cutting edge. When you have completed the above de-
ting edges and softer bodies and heads. The head must scribed process, the chisel will be hardened and tem-
be tough enough to prevent shattering when struck with pered and only needs grinding.
shammer.The cutting edge must be more than twice as During the tempering, the oxide color at which you
hard as the head, and the zone separating the two must quench the steel varies with the properties desired in the
be carefully blended to prevent a lineof demarcation. A part. Table 2-3 lists the different colors and their corre-
method of color tempering frequently used for chisels sponding temperatures. To see the colors clearly, you
and similar tools is one in which the cutting end is heated must turn the part from side to side and have good
by the residual heat of the opposite end of the same tool. lighting. While hand tempering produces the same result
To harden and tempera cold chisel by this method, you as furnace tempering, there is a greater possibility for
heat the tool to the proper hardening temperature and error. The slower the operation is performed, the more
then quench the cutting end only. Bob the chisel up and accurate are the results obtained.
down in the bath, always keeping the cutting edge below
the surface. This method air-cools the head while rapidly
quenching the cutting edge. The result is a tough head, QUENCHING MEDIA
fully hardened cutting edge, and a properly blended
structure. The cooling rate of an object depends on many
things. The size, composition, and initial temperature of
When the cutting end has cooled, remove the chisel the part and final properties are the deciding factors in
from the bath and quickly polish the cutting end with a selecting the quenching medium. A quenching medium
buff stick (emery). Watch the polished surface, as the must cool the metal at a rate rapid enough to produce
heat from the opposite end feeds back into the quenched the desired results.
end. As the temperature of the hardened end increases,
Mass affects quenching in that as the mass in-
oxide colors appear. These oxide colors progress from
creases, the time required for complete cooling also
pale yellow, to a straw color, and end in blue colors. As
increases. Even though parts are the same size, those
soon as the correct shade of blue appears, quench the
containing holes or recesses cool more rapidly than solid
entire chisel to prevent further softening of the cutting
objects. The composition of the metal determines the
edge. The metal is tempered as soon as the proper oxide
maximum cooling rate possible without the danger of
color appears and quenching merely prevents further
cracking or warping. This critical cooling rate, in turn,
tempering by freezing the process. This final quench has
influences the choice of the quenching medium.
no effect on the body and the head of the chisel, because
their temperature will have dropped below the critical The cooling rate of any quenching medium varies
point by the time the proper oxide color appears on the with its temperature; therefore, to get uniform results,
2-8
9. you must keep the temperature within prescribed limits.
The absorption of heat by the quenching medium also
depends, to a large extent, on the circulation of the
quenching medium or the movement of the part. Agita-
tion of the liquid or the part breaks up the gas that forms
an insulating blanket between the part and the liquid.
Normally, hardening takes place when you quench
a metal. The composition of the metal usually deter-
mines the type of quench to use to produce the desired
hardness. For example, shallow-hardened low-alloy and
carbon steels require severer quenching than deep-hard-
ened alloy steels that contain large quantities of nickel,
manganese, or other elements. Therefore, shallow-hard-
ening steels are usually quenched in water or brine, and Figure 2-3.—Portable quench tank.
the deep-hardening steels are quenched in oil. Some-
times it is necessary to use a combination quench,
starting with brine or water and finishing with oil. In
coils. Self-contained coolers are integral parts of large
addition to producing the desired hardness, the quench
quench tanks.
must keep cracking, warping, and soft spots to a mini-
mum. A typical portable quench tank is shown in figure
2-3. This type can be moved as needed to various parts
The volume of quenching liquid should be large
of the heat-treating shop. Some tanks may have one or
enough to absorb all the heat during a normal quenching more compartments. If one compartment contains oil
operation without the use of additional cooling. As more and the other water, the partition must be liquid-tight to
metals are quenched, the liquid absorbs the heat and this prevent mixing. Each compartment has a drain plug, a
temperature rise causes a decrease in the cooling rate. screen in the bottom to catch scale and other foreign
Since quenching liquids must be maintained within matter, and a mesh basket to hold the parts. A portable
definite temperature ranges, mechanical means are used electric pump can be attached to the rim of the tank to
to keep the temperature at prescribed levels during circulate the liquid. This mechanical agitation aids in
continuous operations. uniform cooling.
LIQUID QUENCHING Water
The two methods used for liquid quenching are Water can be used to quench some forms of steel,
called still-bath and flush quenching. but does not produce good results with tool or other alloy
steels. Water absorbs large quantities of atmospheric
Instill-bath quenching, you cool the metal in a tank
gases, and when a hot piece of metal is quenched, these
of liquid. The only movement of the liquid is that caused
gases have a tendency to form bubbles on the surface of
by the movement of the hot metal, as it is being the metal. These bubbles tend to collect in holes or
quenched. recesses and can cause soft spots that later lead to
For flush quenching, the liquid is sprayed onto the cracking or warping.
surface and into every cavity of the part at the same time The water in the quench tank should be changed
to ensure uniform cooling. Flush quenching is used for daily or more often if required. The quench tank should
parts having recesses or cavities that would not be be large enough to hold the part being treated and should
properly quenched by ordinary methods. That assures a have adequate circulation and temperature control. The
thorough and uniform quench and reduces the possibili- temperature of the water should not exceed 65°F.
ties of distortion.
When aluminum alloys and other nonferrous metals
Quenching liquids must be maintained at uniform require a liquid quench, you should quench them in
temperatures for satisfactory results. That is particularly clean water. The volume of water in the quench tank
true for oil. To keep the liquids at their proper tempera- should be large enough to prevent a temperature rise of
ture, they are usually circulated through water-cooled more than 20°F during a single quenching operation. For
2-9
10. Table 2-4.—Properties and Average Cooling Abilities of Quenching Media
heavy-sectioned parts, the temperature rise may exceed can cause cracking or stress in high-carbon or low-alloy
20°F, but should be kept as low as possible. For wrought steels that are uneven in cross section.
products, the temperature of the water should be about
Because of the corrosive action of salt on nonfer-
65°F and should never exceed 100°F before the piece
rous metals, these metals are not quenched in brine.
enters the liquid.
Oil
Brine
Oil is used to quench high-speed and oil-hardened
steels and is preferred for all other steels provided that
Brine is the result of dissolving common rock salt
the required hardness can be obtained. Practically any
in water. This mixture reduces the absorption of atmos-
type of quenching oil is obtainable, including the vari-
pheric gases that, in turn, reduces the amount of bubbles.
ous animal oils, fish oils, vegetable oils, and mineral
As a result, brine wets the metal surface and cools it
oils. Oil is classed as an intermediate quench. It has a
more rapidly than water. In addition to rapid and uni-
slower cooling rate than brine or water and a faster rate
form cooling, the brine removes a large percentage of
than air. The quenching oil temperature should be kept
any scale that may be present.
within a range of 80°F to 150°F. The properties and
The brine solution should contain from 7% to 10% average cooling powers of various quenching oils are
salt by weight or three-fourths pound of salt for each given in table 2-4.
gallon of water. The correct temperature range for a
Water usually collects in the bottom of oil tanks but
brine solution is 65°F to 100°F.
is not harmful in small amounts. In large quantities it
Low-alloy and carbon steels can be quenched in can interfere with the quenching operations; for exam-
brine solutions; however, the rapid cooling rate of brine ple, the end of a long piece may extend into the water at
2-10
11. the bottom of the tank and crack as a result of the more
rapid cooling.
Air quenching is used for cooling some highly
Nonferrous metals are not routinely quenched in oil
alloyed steels. When you use still air, each tool or part
unless specifications call for oil quenching.
should be placed on a suitable rack so the air can reach
all sections of the piece. Parts cooled with circulated air
Caustic Soda are placed in the same manner and arranged for uniform
cooling. Compressed air is used to concentrate the cool-
A solution of water and caustic soda, containing 10 ing on specific areas of a part. The airlines must be free
percent caustic soda by weight, has a higher cooling rate of moisture to prevent cracking of the metal.
than water. Caustic soda is used only for those types of Although nonferrous metals are usually quenched
steel that require extremely rapid cooling and is NEVER in water, pieces that are too large to fit into the quench
used as a quench for nonferrous metals. tank can be cooled with forced-air drafts; however, an
air quench should be used for nonferrous metal only
when the part will not be subjected to severe corrosion
WARNING
conditions and the required strength and other physical
properties can be developed by a mild quench.
CAUSTIC SODA REQUIRES SPECIAL
HANDLING BECAUSE OF ITS HARMFUL
Solids
EFFECTS ON SKIN AND CLOTHING.
The solids used for cooling steel parts include cast-
DRY QUENCHING iron chips, lime, sand, and ashes. Solids are generally
used to slow the rate of cooling; for example, a cast-iron
This type of quenching uses materials other than part can be placed in a lime box after welding to prevent
liquids. Inmost cases, this method is used only to slow cracking and warping. All solids must be free of mois-
the rate of cooling to prevent warping or cracking. ture to prevent uneven cooling.
2-11