1. Introduction
 Applications of Magnetite Nanoparticles
4. Conclusion
 High Pressure Homogenizer
(HPH, Nano Disperser, ILSHIN AUTOCLAVE)
 We have synthesized uniform magnetite nanoparticles using the high
pressure homogenizer without dispersing agent and oxidant.
 The X-ray diffraction patterns showed that all the samples had the inverse
spinel structure of magnetite nanoparticles.
 The average particle size decreased with the number of passes, but after
reaching 3 passes the average particle size increased.
 The VSM measurements revealed superparamagnetism of the nanoparticles
for 1 and 3 passes at 1500 bar.
The uniform size, narrow distributions and superparamagnetism of these
magnetite nanoparticles demonstrated their suitability for use as an MRI
contrast agent, as magnetic fluids, and for targeting drug delivery systems.
Synthesis of Monodisperse Magnetite Nanoparticles
Using a High Pressure Homogenizer
Jun Hee Choa, Taeyoung Kima, Yun Hye Yeona, Sung Hwa Jia, Hyun Hyo Kima
aDepartment of Research & Development, ILSHINAUTOCLAVE CO. #835 Taplipdong, Yuseonggu, Daejeon 305-510,
Korea
2. Experimental & Results
 Experimental
3. Results & Discussion
Requirement
Superparamagnetic
Uniform Particle Size
Colloidal Suspension
 Objectives of This Study
 Nozzle Chamber
High
Energy
Pressure (bar) 500 1000 1500 2000 2500
Fluid velocity
(m/sec)
313 442 542 626 700
Inlet Shear &
Cavitation Zone
Impact
Zone Outlet
Inlet
Inlet
Outlet
Outlet
Impact
Zone
Shear &
Cavitation Zone
Shear &
Cavitation Zone
Impact
Zone
 Fluid Velocity (Sound Speed: 340 m/s)
 XRD Patterns
 TEM Images
• Shear Force
• Cavitation
• Impact Force
Inlet
High Pressure
Pump
Pressure
Gauge Nozzle
Chamber
 VSM
Magnetic Fluid Cell Separation Magnetic Memory
MRI Imaging Hyperthermia Drug Delivery
- Synthesis of uniform magnetite nanoparticles using a high pressure homogenizer
without any dispersing agent.
- Control of the size of the magnetite nanoparticles.
- Synthesis of superparamagnetic magnetite nanoparticles
- High pressure homogenization in a solution during the chemical
reaction may accelerate the rate of the reaction and the crystallization
may be possible at low temperature.
0.85 M NaOH (30 ml, 0.0255 mol)
H S
((( )))
Magnetite
Nanoparticles
0.1 M FeCl2∙4H2O
(100 ml, 0.01 mol)
High Energy
(Nucleation &
Crystal Growth)
Filtration &
drying
Nano Disperser
1500 bar - 1, 3, 5 Passes
＊ Optimum conditions:
- Reaction Temp.: R.T
- Stirring Time: 5 min
• Cavitation
- the formation, growth, and implosive collapse of bubbles in a fluid
• Cavitational Collapse
- intense local heating(~5000 K)
- high pressures(~1000 atm)
- enormous heating and cooling rates(10-9 K/sec)
• Advantages
- Highly dispersion by high energy, Short process time
- Magnetite nanoparticles have received intensive interest in recent years due to their
potential applications in various fields, such as in magnetic memory devices, magnetic
fluids, magnetic refrigeration, magnetic resonance imaging and targeting drug delivery
systems
Outlet
20 30 40 50 60 70
Intensity(arb.unit)
2 Θ (degree)
(311)
(220)
(110)
(222)
(121)
(400)
(422)
(221)
(511)
(440)
Non-high pressure hpmpgemization
Red Line: FeOOH peaks
20 30 40 50 60 70
Intensity(arb.unit)
2 Θ (degree)
(220)
(311)
(222)
(400)
(422)
(511)
(440)
1 Pass
3 Passes
5 Passes
0 Pass FeOOH
Fe(OH)2
Ultrasonic
FeOOH
Average Particle Size
(nm)
Magnetic Property(b)
Phase
XRD(a) TEM
Magnetization
(emu/g)
Coercive
(Oe)
Retentivity
(emy/g)
0 Pass 26 - 64 125 17
FeOOH
Fe(OH)x
Fe3O4
1 Pass 21 20 72 - - Cubic Spinel
3 Passes 19 17 67 - - Cubic Spinel
5 Passes 23 22 76 82 19 Cubic Spinel
 Average particle sizes and magnetic properties of the prepared magnetite
nanoparticles
a The particle size was calculated from the values of FWHM at the diffraction peak of 35.4 °for Fe3O4.
b Magnetic properties were determined by VSM.
Fe2+ + 2NaOH → Fe(OH)2 ↓ + 2Na+
3Fe(OH)2 + H2O2 → Fe3O4 ↓ + 4H2O
-80
-60
-40
-20
0
20
40
60
80
-10000 -5000 0 5000 10000
Magnetization(emu/g)
Magnetic Field (Oe)
-80
-60
-40
-20
0
20
40
60
80
-10000 -5000 0 5000 10000
Magnetization(emu/g)
Magnetic Field (Oe)
-80
-60
-40
-20
0
20
40
60
80
-10000 -5000 0 5000 10000
Magnetization(emu/g)
Magnetic Field (Oe)
-90
-70
-50
-30
-10
10
30
50
70
90
-10000 -5000 0 5000 10000
Magnetization(emu/g)
Magnetic Field (Oe)
- The XRD pattern of the 0 pass sample showed diffraction peaks at 2 θ = 21.1 o, 40.3 o and 53.8 o from the FeOOH.
- All the peaks of 1, 3 and 5 passes samples were matched to the inverse spinel Fe3O4
H2O H + OH
H + H· H2
OH + OH H2O2
Nano Disperser
- The particles synthesized through the ultrasonic method and 0 pass sample are spherical, through square
and rod shapes could also be observed.
- Spherical magnetite nanoparticles were obtained for 1 to 5 passes at 1500 bar.
0 Pass 1 Pass
3 Passes 5 Passes