This document provides an overview of dental composites, including their chemistry, materials, filler types, bonding agents, curing methods, classifications, and clinical applications and techniques. Key points include:
- Dental composites consist of a resin matrix and filler materials, along with coupling agents to bond resin to fillers. They are polymerized through heat, chemical, or photochemical initiation.
- Fillers improve physical properties but characteristics depend on filler type, size, shape, and load. Larger and smaller filler particles reduce shrinkage.
- Bonding agents like silanes chemically coat fillers to improve strength, but can degrade with moisture.
- Composites are classified by initiation method
There have been several changes since inception in the field of dental ceramics. Need for newer materials with improved aesthetics, flexural strength and optical properties made it necessary for introduction of advanced technology in fabrication of dental ceramics.
This presentation tells everything about composite resin from history to composition to usage protocols. A must read for all dental students before practicals and exams.
A powerpoint presentation focusing mainly on the material aspects of composite resins. The second part of this presentation deals with the clinical aspects
There have been several changes since inception in the field of dental ceramics. Need for newer materials with improved aesthetics, flexural strength and optical properties made it necessary for introduction of advanced technology in fabrication of dental ceramics.
This presentation tells everything about composite resin from history to composition to usage protocols. A must read for all dental students before practicals and exams.
A powerpoint presentation focusing mainly on the material aspects of composite resins. The second part of this presentation deals with the clinical aspects
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Colour and Shade Selection in dental practiseSNEHA RATNANI
Shade selection is an extremely important aspect of aesthetic dentistry.One must have thorough knowledge of colour and shade selection before carrying out any restorative procedures in patients mouth. A brief seminar on colour and shade selection has been penned down here. Hope it helps u fetch some information regarding shade selection and colour in dentistry.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Colour and Shade Selection in dental practiseSNEHA RATNANI
Shade selection is an extremely important aspect of aesthetic dentistry.One must have thorough knowledge of colour and shade selection before carrying out any restorative procedures in patients mouth. A brief seminar on colour and shade selection has been penned down here. Hope it helps u fetch some information regarding shade selection and colour in dentistry.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Composites in dentistry /certified fixed orthodontic courses by Indian denta...Indian dental academy
Welcome to Indian Dental Academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy has a unique training program & curriculum that provides students with exceptional clinical skills and enabling them to return to their office with high level confidence and start treating patients
State of the art comprehensive training-Faculty of world wide repute &Very affordable.
Dental composite /certified fixed orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
this presentation includes details about composite resins which are tooth colored filling materials used in dentistry. it also includes various recent advances in this field.
Orthodontic resin /certified fixed orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Composite dental restorations represent a unique class of biomaterials with severe restrictions on biocompatibility, curing behaviour, aesthetics, and ultimate material properties. These materials are presently limited by shrinkage and polymerization-induced shrinkage stress, limited toughness, the presence of unreacted monomer that remains following the polymerization, and several other factors. Fortunately, these materials have been the focus of a great deal of research in recent years with the goal of improving restoration performance by changing the initiation system, monomers, and fillers and their coupling agents, and by developing novel polymerization strategies.
Orthodontic resins /certified fixed orthodontic courses by Indian dental acad...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
Acrylic resin was introduced to dentistry in 1936 and received a great response from the dental professionals such that by 1946, 98% of all denture were made with methyl methacrylate polymer or copolymer.
Prior to 1940 vulcanite was the most widely used denture base resin. This is highly cross linked natural rubber which was difficult to pigment and tended to become unhygienic due to the uptake of saliva.
This presentation provides an in-depth analysis of the application and biomechanical properties of dental composites, critically examining their role in restorative dentistry. Explore the molecular structure, mechanical characteristics, and clinical performance metrics that make composites the material of choice for a variety of dental applications. Through case studies and recent research findings, the presentation aims to elucidate the material science innovations driving advancements in this field. Recommended for dental practitioners, postgraduate students, and researchers focusing on dental materials and technologies
Implicitly or explicitly all competing businesses employ a strategy to select a mix
of marketing resources. Formulating such competitive strategies fundamentally
involves recognizing relationships between elements of the marketing mix (e.g.,
price and product quality), as well as assessing competitive and market conditions
(i.e., industry structure in the language of economics).
An introduction to the cryptocurrency investment platform Binance Savings.Any kyc Account
Learn how to use Binance Savings to expand your bitcoin holdings. Discover how to maximize your earnings on one of the most reliable cryptocurrency exchange platforms, as well as how to earn interest on your cryptocurrency holdings and the various savings choices available.
[Note: This is a partial preview. To download this presentation, visit:
https://www.oeconsulting.com.sg/training-presentations]
Sustainability has become an increasingly critical topic as the world recognizes the need to protect our planet and its resources for future generations. Sustainability means meeting our current needs without compromising the ability of future generations to meet theirs. It involves long-term planning and consideration of the consequences of our actions. The goal is to create strategies that ensure the long-term viability of People, Planet, and Profit.
Leading companies such as Nike, Toyota, and Siemens are prioritizing sustainable innovation in their business models, setting an example for others to follow. In this Sustainability training presentation, you will learn key concepts, principles, and practices of sustainability applicable across industries. This training aims to create awareness and educate employees, senior executives, consultants, and other key stakeholders, including investors, policymakers, and supply chain partners, on the importance and implementation of sustainability.
LEARNING OBJECTIVES
1. Develop a comprehensive understanding of the fundamental principles and concepts that form the foundation of sustainability within corporate environments.
2. Explore the sustainability implementation model, focusing on effective measures and reporting strategies to track and communicate sustainability efforts.
3. Identify and define best practices and critical success factors essential for achieving sustainability goals within organizations.
CONTENTS
1. Introduction and Key Concepts of Sustainability
2. Principles and Practices of Sustainability
3. Measures and Reporting in Sustainability
4. Sustainability Implementation & Best Practices
To download the complete presentation, visit: https://www.oeconsulting.com.sg/training-presentations
"𝑩𝑬𝑮𝑼𝑵 𝑾𝑰𝑻𝑯 𝑻𝑱 𝑰𝑺 𝑯𝑨𝑳𝑭 𝑫𝑶𝑵𝑬"
𝐓𝐉 𝐂𝐨𝐦𝐬 (𝐓𝐉 𝐂𝐨𝐦𝐦𝐮𝐧𝐢𝐜𝐚𝐭𝐢𝐨𝐧𝐬) is a professional event agency that includes experts in the event-organizing market in Vietnam, Korea, and ASEAN countries. We provide unlimited types of events from Music concerts, Fan meetings, and Culture festivals to Corporate events, Internal company events, Golf tournaments, MICE events, and Exhibitions.
𝐓𝐉 𝐂𝐨𝐦𝐬 provides unlimited package services including such as Event organizing, Event planning, Event production, Manpower, PR marketing, Design 2D/3D, VIP protocols, Interpreter agency, etc.
Sports events - Golf competitions/billiards competitions/company sports events: dynamic and challenging
⭐ 𝐅𝐞𝐚𝐭𝐮𝐫𝐞𝐝 𝐩𝐫𝐨𝐣𝐞𝐜𝐭𝐬:
➢ 2024 BAEKHYUN [Lonsdaleite] IN HO CHI MINH
➢ SUPER JUNIOR-L.S.S. THE SHOW : Th3ee Guys in HO CHI MINH
➢FreenBecky 1st Fan Meeting in Vietnam
➢CHILDREN ART EXHIBITION 2024: BEYOND BARRIERS
➢ WOW K-Music Festival 2023
➢ Winner [CROSS] Tour in HCM
➢ Super Show 9 in HCM with Super Junior
➢ HCMC - Gyeongsangbuk-do Culture and Tourism Festival
➢ Korean Vietnam Partnership - Fair with LG
➢ Korean President visits Samsung Electronics R&D Center
➢ Vietnam Food Expo with Lotte Wellfood
"𝐄𝐯𝐞𝐫𝐲 𝐞𝐯𝐞𝐧𝐭 𝐢𝐬 𝐚 𝐬𝐭𝐨𝐫𝐲, 𝐚 𝐬𝐩𝐞𝐜𝐢𝐚𝐥 𝐣𝐨𝐮𝐫𝐧𝐞𝐲. 𝐖𝐞 𝐚𝐥𝐰𝐚𝐲𝐬 𝐛𝐞𝐥𝐢𝐞𝐯𝐞 𝐭𝐡𝐚𝐭 𝐬𝐡𝐨𝐫𝐭𝐥𝐲 𝐲𝐨𝐮 𝐰𝐢𝐥𝐥 𝐛𝐞 𝐚 𝐩𝐚𝐫𝐭 𝐨𝐟 𝐨𝐮𝐫 𝐬𝐭𝐨𝐫𝐢𝐞𝐬."
VAT Registration Outlined In UAE: Benefits and Requirementsuae taxgpt
Vat Registration is a legal obligation for businesses meeting the threshold requirement, helping companies avoid fines and ramifications. Contact now!
https://viralsocialtrends.com/vat-registration-outlined-in-uae/
LA HUG - Video Testimonials with Chynna Morgan - June 2024Lital Barkan
Have you ever heard that user-generated content or video testimonials can take your brand to the next level? We will explore how you can effectively use video testimonials to leverage and boost your sales, content strategy, and increase your CRM data.🤯
We will dig deeper into:
1. How to capture video testimonials that convert from your audience 🎥
2. How to leverage your testimonials to boost your sales 💲
3. How you can capture more CRM data to understand your audience better through video testimonials. 📊
Personal Brand Statement:
As an Army veteran dedicated to lifelong learning, I bring a disciplined, strategic mindset to my pursuits. I am constantly expanding my knowledge to innovate and lead effectively. My journey is driven by a commitment to excellence, and to make a meaningful impact in the world.
Enterprise Excellence is Inclusive Excellence.pdfKaiNexus
Enterprise excellence and inclusive excellence are closely linked, and real-world challenges have shown that both are essential to the success of any organization. To achieve enterprise excellence, organizations must focus on improving their operations and processes while creating an inclusive environment that engages everyone. In this interactive session, the facilitator will highlight commonly established business practices and how they limit our ability to engage everyone every day. More importantly, though, participants will likely gain increased awareness of what we can do differently to maximize enterprise excellence through deliberate inclusion.
What is Enterprise Excellence?
Enterprise Excellence is a holistic approach that's aimed at achieving world-class performance across all aspects of the organization.
What might I learn?
A way to engage all in creating Inclusive Excellence. Lessons from the US military and their parallels to the story of Harry Potter. How belt systems and CI teams can destroy inclusive practices. How leadership language invites people to the party. There are three things leaders can do to engage everyone every day: maximizing psychological safety to create environments where folks learn, contribute, and challenge the status quo.
Who might benefit? Anyone and everyone leading folks from the shop floor to top floor.
Dr. William Harvey is a seasoned Operations Leader with extensive experience in chemical processing, manufacturing, and operations management. At Michelman, he currently oversees multiple sites, leading teams in strategic planning and coaching/practicing continuous improvement. William is set to start his eighth year of teaching at the University of Cincinnati where he teaches marketing, finance, and management. William holds various certifications in change management, quality, leadership, operational excellence, team building, and DiSC, among others.
Event Report - SAP Sapphire 2024 Orlando - lots of innovation and old challengesHolger Mueller
Holger Mueller of Constellation Research shares his key takeaways from SAP's Sapphire confernece, held in Orlando, June 3rd till 5th 2024, in the Orange Convention Center.
3. COMPOSITE CHEMISTRY
• Dental composite is composed of a resin matrix and filler materials.
• Coupling agents are used to improve adherence of resin to filler
surfaces.
• Activation systems including heat, chemical and photochemical
initiate polymerization.
• Plasticizers are solvents that contain catalysts for mixture into resin.
• Monomer, a single molecule, is joined together to form a polymer, a
long chain of monomers.
• Physical characteristics improve by combining more than one type
of monomer and are referred to as a copolymer.
• Cross linking monomers join long chain polymers together along the
chain and improve strength.
4. RESIN MATERIALS
• BIS-GMA resin is the base for composite. In the late 1950's, Bowen
mixed bisphenol A and glycidylmethacrylate thinned with TEGDMA
(triethylene glycol dimethacrylate) to form the first BIS-GMA resin.
Diluents are added to increase flow and handling characteristics or
provide cross linking for improved strength. Common examples are:
• RESIN:- BIS-GMA bisphenol glycidylmethacrylate
• DILUENTS:- MMA methylmethacrylate
BIS-DMA bisphenol dimethacrylate
UDMA urethane dimethacrylate
• CROSS LINK DILUENTS
TEGDMA triethylene glycol dimethacrylate
EGDMA ethylene glycol dimethacrylate
5. COUPLING AGENTS
• Coupling agents are used to improve adherence of resin to filler
surfaces.
• Coupling agents chemically coat filler surfaces and increase
strength.
• Silanes have been used to coat fillers for over fifty years in industrial
plastics and later in dental fillers. Today, they are still state of the
art.
• Silanes have disadvantages. They age quickly in a bottle and
become ineffective. Silanes are sensitive to water so the silane filler
bond breaks down with moisture.
• Water absorbed into composites results in hydrolysis of the silane
bond and eventual filler loss.
• Common silane agents are:
vinyl triethoxysilane
methacryloxypropyltrimethoxysilane
6. HEAT CATALYST
• Polymerization of resin requires initiation by a free radical.
• Initiation starts propagation or continued joining of molecules at
double bonds until termination is reached.
• Heat applied to initiators breaks down chemical structure to produce
free radicals, however, monomers may polymerize when heat is
applied even without initiators.
• Resins require stabilizers to avoid spontaneous polymerization.
Stabilizers are also used to control the reaction of activators and
resin mixtures.
• Hydroquinone is most commonly used as a stabilizer.
• Common heat based initiators are peroxides such as
benzoylperoxide
t-butylperoxide
t-cumythydroxyperoxide
7. PHOTOCHEMICAL CATALYST
• Early photochemical systems used were benzoin methyl ether which
is sensitive to UV wavelengths at 365 nm. UV systems had limited
use as depth of cure was limited. Visible light activation of
diketones is the preferred photochemical systems. Diketones
activate by visible, blue light to produce slow reactions. Amines are
added to accelerate curing time.
• Presently, different composites use different photochemical
systems. These systems are activated by different wavelengths of
light. In addition, different curing lights produce various ranges of
wavelengths that might not match composite activation
wavelengths. This can result in no cure or partial cure. Composite
materials must be matched to curing lights.
• Common photochemical initiators are:
Camphoroquinone
Acenaphthene quinone
Benzyl
8. LIGHT CURING
• Light curing can be accomplished with:-
1) Quartz-Tungsten-Halogen
2) Plasma Arc Curing
3) Light Emitting Diode
9. CHEMICAL CATALYST
• Chemical activation of peroxides produces free radicals. Chemical
accelerators are often not color stable and have been improved for
this reason.
• The term self cure or dual cure (when combined with photo chemical
initiation) describes chemical cure materials.
• Chemical composites mix a base paste and a catalyst paste for self
cure.
• Bonding agents mix two liquids.
• Mixing two pastes incorporates air into the composite.
• Oxygen inhibits curing resulting in a weaker restoration.
• Chemical accelerators include:
Dimethyl p-toludine
N,N-bis(hydroxy-lower-alkyl)-3,5-xylidine
10. COMPOSITE FILLERS
• Fillers are placed in dental composites to reduce shrinkage upon
curing.
• Physical properties of composite are improved by fillers, however,
composite characteristics change based on filler material, surface,
size, load, shape, surface modifiers, optical index, filler load and
size distribution.
• Materials such as strontium glass, barium glass, quartz, borosilicate
glass, ceramic, silica, prepolymerized resin, or the like are used.
11. • Fillers are classified by material, shape and size.
• Fillers are irregular or spherical in shape depending on the mode of
manufacture.
• Spherical particles are easier to incorporate into a resin mix and to
fill more space leaving less resin.
• One size spherical particle occupies a certain space.
• Adding smaller particles fills the space between the larger particles
to take up more space.
• There is less resin remaining and therefore, less shrinkage on
curing the more size particles used in proper distribution.
FILLERS CLASSIFICATION
12. • Classification According to Size:-
MACROFILLERS ---- 10 TO 100 um
MIDIFILLERS ----- 1 TO 10 um
MINIFILLERS ----- 0.1 TO 1 um
MICROFILLERS ----- 0.01 TO 0.1 um
NANOFILLERS ----- 0.005 TO 0.01 um
FILLERS CLASSIFICATION
13. PLASTICIZERS
• Dental composite is composed of a resin matrix and filler materials.
• Coupling agents are used to improve adherence of resin to filler
surfaces.
• Plasticizers are solvents that contain catalysts for mixture into resin.
• They need to be non reactive to the catalyst & resin.
14. Physical Characteristics
• Following are the imp physical properties:-
• 1) Linear coefficient of thermal expansion (LCTE)
• 2) Water Absorption
• 3) Wear resistance
• 4) Surface texture
• 5) Radiopacity
• 6) Modulus of elasticity
• 7) Solubility
15. C- FACTOR
• It is the ratio of the bonded surfaces to the unbonded or free
surfaces in a tooth preparation.
• The higher the C-Factor, greater is the potential for bond disruption
from polymerisation effects.
16. INTERNAL STRESSES
• Internal stresses can be reduced by,
1) ‘Self start’ Polymerisation
2) Incremental placement
3) Use of stress breaking liners such as:-
a)Filled Dentinal Adhesives
b)RMGI.
17. COMPOSITE CLASSIFICATION
• Composite is classified by initiation techniques, filler size, and
viscosity.
• Laboratory heat process fillings are processed under nitrogen and
pressure to produce a more thorough cure.
• Core build up materials are commonly self cure.
• Dual cure composite is commonly used as a cementing medium
under crowns.
• Viscosity determines flow characteristics during placement. A
flowable composite flows like liquid or a loose gel. A packable
composite is firm and hard to displace.
18. Composite is classified by initiation
techniques, filler size, and viscosity
• Heat cured composites are polymerized by application of heat.
• Self cured composite means chemical initiation converting monomer
to polymer takes place.
• Light cured composite means photochemical initiation causes
polymerization
• Dual cure means chemical initiation is used and combined with
photochemical initiation so either and both techniques polymerize
composite.
19. Radiospacity
• One of the requirements of using a composite as a posterior
restorative is that it should be radiopaque.
• In order for a material to be described as being radiopaque, the
International Standard Organization (ISO) specifies that it should
have radiopacity equivalent to 1 mm of aluminium, which is
approximately equal to natural tooth dentine.
• However, there has been a move to increase the radiopacity to be
equivalent to 2 mm of aluminium, which is approximately equal to
natural tooth enamel.
• A majority of the composites described as all-purpose or universal
have levels of radiopacity greater than 2 mm of aluminium
20. INDICATIONS
• 1) Class-I, II, III, IV, V & VI restorations.
• 2) Foundations or core buildups.
• 3) Sealant & Preventive resin restorations.
• 4) Esthetic enhancement procedures.
• 5) Luting
• 6) Temporary restorations
• 7) Periodontal splinting.
21. CONTRAINDICATIONS
• 1) Inability to isolate the site.
• 2) Excessive masticatory forces.
• 3) Restorations extending to the root surfaces.
• 4) Other operator errors.
23. DISADVANTAGES
• 1) May result in gap formation when restoration extends to the root
surface.
• 2) Technique sensitive.
• 3) Expensive
• 4) May exhibit more occlusal wear in areas of higher stresses.
• 5) Higher linear coefficient of thermal expansion.
24. STEPS IN COMPOSITE
RESTORATION
• 1) Local anaesthesia.
• 2) Preparation of the operating site.
• 3) Shade selection
• 4) Isolation of the operating site.
• 5) Tooth preparation.
• 6) preliminary steps of enamel and dentin bonding.
• 7) Matrix placement.
• 8) Inserting the composite.
• 9) Contouring the composite.
• 10) polishing the composite.
25. PRINCIPLES OF ANTERIOR
COMPOSITE RESTORATION
• 1. Smile Design
• 2. Color and Color Analysis
• 3. Tooth Color
• 4. Tooth Shape
• 5. Tooth Position
• 6. Esthetic Goals
• 7. Composite Selection
• 8. Tooth Preparation
• 9. Bonding Techniques
• 10. Composite Placement
• 11. Composite Sculpture and
• 12. Composite Polishing to properly restore anterior teeth with
composite:
26. 1. SMILE DESIGN
• A dentist must understand proper smile design so composite
restoration can achieve a beautiful smile. This is true for extensive
veneering and small restorations.
• Factors which are considered in smile design include:-
A. Smile Form which includes size in relation to the face, size of one
tooth to another, gingival contours to the upper lip line, incisal edges
overall to the lower lip line, arch position, teeth shape and size,
perspective, and midline.
B. Teeth Form which includes understanding long axis, incisal edge,
surface contours, line angles, contact areas, embrasure form, height
of contour, surface texture, characterization, and tissue contours
within an overall smile design.
C. Tooth Color of gingival, middle, incisal, and interproximal areas
and the intricacies of characterization within an overall smile design.
27. 2. COLOUR AND COLOUR
ANALYSIS
• Colour is a study in and of itself. In dentistry, the effect of enamel
rods, surface contours, surface textures, dentinal light absorption,
etc. on light transmission and reflection is difficult to understand and
even more difficult replicate.
• The intricacies of understanding matching and replicating hue,
chroma, value, translucency, florescence; light transmission,
reflection and refraction to that of a natural tooth under various light
sources is essential but far beyond the scope of this article.
28. 3. TOOTH COLOUR
• Analysis of colour variation within teeth is improved by an
understanding of how teeth produce color variation.
• Enamel is prismatic and translucent which results in a blue gray
color on the incisal edge, interproximal areas and areas of
increased thickness at the junction of lobe formations.
• The gingival third of a tooth appears darker as enamel thins and
dentin shows through.
• Color deviation, such as craze lines or hypocalcifications, within
dentin or enamel can cause further color variation.
• Aging has a profound effect on color caused by internal or external
staining, enamel wear and cracking, caries, acute trauma and
dentistry.
29. 4. TOOTH SHAPE
• Understanding tooth shape requires studying dental anatomy.
• Studying anatomy of teeth requires recognition of general form,
detail anatomy and internal anatomy.
• It is important to know ideal anatomy and anatomy as a result of
aging, disease, trauma and wear.
• Knowledge of anatomy allows a dentist to reproduce natural teeth.
For example, a craze line is not a straight line as often is produced
by a dentist, but is a more irregular form guided by enamel rods.
30. 5. TOOTH POSITION
• Knowledge of normal position and axial tilt of teeth within a head,
lips, and arches allows reproduction of natural beautiful smiles.
• Understanding the goals of an ideal smile and compromises from
limitations of treatment allows realistic expectations of a dentist and
patient.
• Often, learning about tooth position is easily done through denture
esthetics.
• Ideal and normal variations of tooth position is emphasized in
removable prosthetics so a denture look does not occur.
31. 6. ESTHETIC GOALS
• The results of esthetic dentistry are limited by limitations of ideals
and limitations of treatment.
• Ideals of the golden proportion have been replaced by preconceived
perceptions.
• Limitations of ideals are based on physical, environmental and
psychological factors.
• Limitations of treatment are base on physical, financial and
psychological factors.
32. 7. COMPOSITE SELECTION
• Esthetic dentistry is an art form. There are different levels of
appreciation so individual dentists evaluate results of esthetic
dentistry differently. Artistically dentists select composites based on
their level of appreciation, artistic ability and knowledge of specific
materials. Factors which influence composite selection include
• A- Restoration Strength,
• B- Wear
• C- Restoration Color
• D- Placement characteristics.
• E- Ability to use and combine opaquers and tints.
• F- Ease of shaping.
• G- Polishing characteristics.
• H- Polish and colour stability
33. 8. TOOTH PREPARATION
• Tooth preparation often defines restoration strength.
• Small tooth defects which receive minimal force require minimal
tooth preparation because only bond strength is required to provide
retention and resistance.
• In larger tooth defects where maximum forces are applied,
mechanical retention and resistance with increased bond area can
be required to provide adequate strength.
34. 9. BONDING TECHNIQUES
• Understanding techniques to bond composite to dentin and enamel
provide strength, elimination of sensitivity and prevention of micro-
leakage.
• Enamel bonding is a well understood science. Dentinal bonding,
however, is constantly changing as more research is being done
and requires constant periodic review.
• Micro-etching combined with composite bonding techniques to old
composite, porcelain, and metal must be understood to do anterior
composite repairs.
35. 10. COMPOSITE PLACEMENT
TECHNIQUE
• Understanding techniques which allow ease of placement, minimize
effects of shrinkage, eliminate air entrapment and prevent material
from pulling back from tooth structure during instrumentation
determine ultimate success or failure of a restoration.
• It is important to incorporate proper instrumentation to allow ease of
shaping tooth anatomy and provide color variation prior to curing
composite.
• In addition, a dentist must understand placement of various
composite layers with varying opacities and color to replicate normal
tooth structure.
36. 11. COMPOSITE SCULPTURE
• Composite sculpture of cured composite is properly done if
appropriate use of polishing strips, burs, cups, wheels and points is
understood.
• In addition, proper use of instrumentation maximizes esthetics and
allows minimal heat or vibrational trauma to composite resulting in a
long lasting restoration.
37. 12. COMPOSITE POLISHING
• Polishing composite to allow a smooth or textured surface shiny
produces realistic, natural restorations.
• Proper use of polishing strips, burs, cups, wheels and points with
water or polish pastes as required minimizes heat generation and
vibration trauma to composite material for a long lasting restoration.
38. DIRECT POSTERIOR
COMPOSITES
• Composites are indicated for Class 1, class 2 and class 5 defects on
premolars and molars. Ideally, an isthmus width of less than one
third the intercuspal distance is required.
• This requirement is balanced against forces created on remaining
tooth structure and composite material. Forces are analyzed by
direction, frequency, duration and intensity. High force occurs with
low angle cases, in molar areas, with strong muscles, point contacts
and parafunctional forces such as grinding and biting finger nails.
• Composite is strongest in compressive strength and weakest in
shear, tensile and modulus of elasticity strengths. Controlling forces
by preparation design and occlusal contacts can be critical to
restorative success.
• Failure of a restoration occurs if composite fractures, tooth fractures,
composite debonds from tooth structure or micro-leakage and
subsequent caries occurs. A common area of failure is direct point
contact by sharp opposing cusps. Enameloplasty that creates a
three point contact in fossa or flat contacts is often indicated.
39.
40. • Tooth preparation requires adequate access to remove caries,
removal of caries, elimination of weak tooth structure that could
fracture, beveling of enamel to maximize enamel bond strength, and
extension into defective areas such as stained grooves and
decalcified areas.
• Matrix systems are placed to contain materials within the tooth and
form proper interproximal contours and contacts. Selection of a
matrix system should vary depending on the situation (see web
pages contacts and contours in this section).
• Enamel and dentin bonding is completed. Composite shrinks when
cured so large areas must be layered to minimize negative forces.
• Generally, any area thicker than two millimeters requires layering.
In addition, cavity preparation produces multiple wall defects.
• Composite curing when touching multiple walls creates dramatic
stress and should be avoided.
41.
42. • Composite built in layers replicate tooth structure by placing dentin
layers first and then enamel layers.
• Final contouring with hand instruments is ideal to minimize the
trauma of shaping with burs.
• Matrix systems are removed and refined shaping and occlusal
adjustment done with a 245 bur and a flame shaped finishing bur.
Interproximal buccal and lingual areas are trimmed of excess with a
flame shaped finishing bur.
• Final polish is achieved with polishing cups, points, sandpaper
disks, and polishing paste.
43.
44. INDIRECT POSTERIOR
COMPOSITES
• Indirect laboratory composite is indicated on teeth that required
large restorations but have a significant amount of tooth remaining.
It is used when a tooth defect is larger than indicated for direct
composite and smaller than indicated for a crown. A common
situation is fracture of a single cusp on a molar or a thin cusp on a
bicuspid. Force analysis is critical to success as high force will
fracture composite, tooth structure or separate bonded interfaces.
High force is indicated on teeth furthest back in the mouth for
example, a second molar receives five times more force than a
bicuspid. Orthodontic low angle cases and large masseter muscles
generate high force. Sharp point contacts from opposing teeth
create immense force and are often altered with enameloplasty.
• Indirect composite restorations are processed in a laboratory under
heat, pressure and nitrogen to produce a more thorough composite
cure. Pressure and heat increase cure while nitrogen eliminates
oxygen that inhibits cure. Increased cure results in stronger
restorations. Strength of laboratory processed composite is
between composite and crown strength and requires adequate tooth
support.
45. TOOTH PREPARATION
• Tooth preparation requires removal of existing restorations and
caries. Thin cusps and enamel are removed in combination of
blocking out undercuts with composite, glass ionomer, flowable
composite or the like.
• Tooth preparation requires adequate wall divergence to bond and
cement the restoration and ideally, margins should finish in enamel.
The restoration floor is bonded and light cured.
• Bonding agent is light cured to stabilize collagen fibers and avoid
collapse during restoration placement. A base of glass ionomer or
composite is used if thermal sensitivity is anticipated.
• Restoration retention is judged by bonded surface area, number and
location of retentive walls, divergence of retentive walls, height to
width ratio and restoration internal and external shape.
• Resistance form, reduction of internal stress and conversion of
potential shear and tensile forces is accomplished by smoothing
sharp areas and creating flat floors as opposed to external angular
walls.
46. TOOTH PREPARATION
• Impressions are taken of prepared teeth, models poured and
composite restorations constructed at a laboratory. Temporaries
are placed and a second appointment made.
• At a second appointment, temporaries are removed and a rubber
dam placed. Restorations are tried on the teeth and
adjusted. Manufacturers directions are followed. In general,
bonding is completed on the tooth surfaces and bonding resin
precured.
• Matrix bands are placed prior to etching to contain etch within
prepared areas. Trimming of excess cement where no etching has
occurred is easier.
• Composite surfaces are silinated and dual cure resin cement
applied. Restorations are seated, excess resin cement is wiped
away with a brush and then facial and lingual surfaces are light
cured. Interproximal areas are flossed and then light cured. Excess
is trimmed with hand instruments and finishing flame shaped burs.
• The rubber dam is removed and occlusion adjusted. Surfaces are
finished and polished.
47. COMPOSITE WEAR
• There are several mechanisms of composite wear including
adhesive wear, abrasive wear, fatigue, and chemical wear.
• Adhesive wear is created by extremely small contacts and therefore
extremely high forces, of two opposing surfaces. When small forces
release, material is removed. All surfaces have microscopic
roughness which is where extremely small contacts occur between
opposing surfaces.
• Abrasive wear is when a rough material gouges out material on an
opposing surface. A harder surface gouges a softer surface.
Materials are not uniform so hard materials in a soft matrix, such as
filler in resin, gouge resin and opposing surfaces. Fatigue causes
wear. Constant repeated force causes substructure deterioration
and eventual loss of surface material. Chemical wear occurs when
environmental materials such s saliva, acids or like affect a surface.
48. COMPOSITE FRACTURE
• Dental composite is composed of a resin matrix and filler materials.
The resin filler interface is important for most physical properties.
• There are three causes of stress on this interface including: resin
shrinkage pulls on fillers, filler modulus of elasticity is higher than
resin, and filler thermo coefficient of expansion allows resin to
expand more with heat. When fracture occurs, a crack propagates
and strikes a filler particle. Resin pulls away from filler particle
surfaces during failure. This type of failure is more difficult with
larger particles as surface area is greater. A macrofill composite is
stronger than a microfill composite.
• Coupling agents are used to improve adherence of resin to filler
surfaces. Modification of filler physical structure on the surface or
aggregating filler particles create mechanical locking to improve
interface strength. Coupling agents chemically coat filler surfaces
and increase strength. Silanes have been used to coat fillers for
over fifty years in industrial plastics and later in dental fillers. Today,
they are still state of the art.
50. Multifunctional Composites and
Novel Microstructures
• Hierarchical microstructures
• - Dr H-X Peng
• The properties of composite materials can be tailored through
microstructural design at different lengthscales such as the micro-
and nano-structural level.
• At the micro-structural level, our novel approach creates
microstructures with controlled inhomogeneous reinforcement
distributions.
• These microstructures effectively contain more than one structural
hierarchy. This has the potential to create whole new classes of
composite materials with superior single properties and property
combinations.
• Research also involves tailoring the nano-structures of micro-
wires/ribbons for macro-composites.
51. Shaped fibres
• - Dr Ian Bond, Dr Paul Weaver
• Research has shown that shaped fibres can be an effective means
of improving the through thickness properties.
• A set of guidelines for fibre shape and a preferred ‘family’ of fibres
have been generated from qualitative analysis for the role of
reinforcing fibres in composites.
• Methods have also been developed to produce such shaped fibres
from glass in order to form reinforced laminates in sufficient quantity
for materials property testing using standard methods.
• Fibre shape has been shown to play a key role in contributing to the
bonding force between fibre and matrix, with significant increases in
fracture toughness possible. Results suggest that the shaped fibre
specimens have a greater throughthickness strength than the
circular fibre composites that are currently used.
52. Self healing
• - Dr Ian Bond
• Impact damage to composite structures can result in a drastic
reduction in mechanical properties. Bio-inspired approach is
adopted to effect selfhealing which can be described as mechanical,
thermal or chemically induced damage that is autonomically
repaired by materials already contained within the structure.
• Efforts are undergoing to manufacture and incorporate
multifunctional hollow fibres to generate healing and vascular
networks within both composite laminates and sandwich structures.
• The release of repair agent from these embedded storage
reservoirs mimics the bleeding mechanism in biological organisms.
• Once cured, the healing resin provides crack arrest and recovery of
mechanical integrity.
• It is also possible to introduce UV fluorescent dye into the resin,
which will illuminate any damage/healing events that the structure
has undergone, thereby simplifying the inspection process for
subsequent permanent repair.
53. Fibre Reinforced Dental Resins
• - Dr Ian Bond and Professor Daryll Jagger
• The material most commonly used in the construction of dentures is
poly (methyl methacrylate) and although few would dispute that
satisfactory aesthetics can be achieved with this material, in terms
of mechanical properties it is still far from ideal.
• Over the years there have been various attempts to improve the
mechanical properties of the resin including the search for an
alternative material, such as nylon, the chemical modification of the
resin through the incorporation of butadiene styrene as in the "high
impact resins" and the incorporation of fibres such as carbon, glass
and polyethylene.
• The use of self-healing technology within dental resins is a novel
and exciting approach to solve the problems of the failing dental
resins.
• Methods are currently being developed to translate the self healing
resin technology into dental and biomaterials science.
54. Nanofibres and Nanocomposites
• - Dr Bo Su
• An electrospinning technique has been used to produce polymer,
ceramic and nanocomposite nanofibres for wound addressing,
tissue engineering and dental composites applications.
• The electrospun nanofibres have typical diameters of 100-500 nm.
Natural biopolymers, such as alginate, chitosan, gelatin and
collagen nanofibres, have been investigated.
• Novel nanocomposites, such as Ag nanoparticles doped alginate
nanofibres and alginate/chitosan core-shell nanofibres, have also
been investigated for antimicrobials and tissue engineering
scaffolds.
• Zirconia and silica nanofibre/epoxy composites are currently under
investigation for dental fillings and aesthetic orthodontic archwires.
55. Nanocomposites
• - Dr H-X Peng
• Carbon fibre composite components are susceptible to sand and
rain erosion as well as cutting by sharp objects.
• The use of nanomaterials in coating formulations can lead to wear-
resistant nanocomposite coatings.
• Work is developing novel fine-particle filled polymer coating systems
with a
• potential step-change in erosion resistance and exploring their
application to composite propellers and blades.
• These tailored materials also have potential applications in lightning
strike protection and de-icing.
• The nano-structure of magnetic micro-ribbons/wires is being
investigated and optimised to obtain the Giant Magneto-Impedance
(GMI) effect for high sensitivity magnetic sensor applications.
56. Composites with Magnetic
Function
• - Dr Ian Bond, Prof. Phil Mellor and Dr H-X Peng
• The main aim of this work is to examine methods ofincluding
magnetic materials within a composite whilst maintaining structural
performance.
• This has been achieved by filling hollow fibres with a suspension of
magnetic materials after manufacture of the composite component.
• Research is continuing to tailor the magnetic properties of the
composite to other applications.
• In another approach, magnetic microribbons and microwires are
being tailored and embedded into macrocomposite materials to
provide magnetic sensing functions.
57. Auxetics
• - Dr Fabrizio Scarpa
• Auxetic solids expand in all directions when pulled in only one,
therefore exhibiting a negative Poisson’s ratio.
• New concepts are being develope for composite materials, foams
and elastomers with auxetic characteristics for aerospace, maritime
and ergonomics applications.
• The use of smart material technologies and negative Poisson’s ratio
solids has also led to the development of smart auxetics for active
sound management, vibroacoustics and structural health
monitoring.
58. Diamond Fibre Composites
• - Dr Paul May and Professor Mike Ashfold
• Researchers in the CVD Diamond Film Lab based in the School of
Chemistry are investigating ways to make diamond fibre reinforced
composites.
• The diamond fibres are made by coating thin (100 mm diameter)
tungsten wires with a uniform coating of polycrystalline diamond
using hot filament chemical vapour deposition.
• The diamond-coated wires are extremely stiff and rigid, and can be
embedded into a matrix material (such as a metal or plastic) to
make a stiff but lightweight composite material with anisotropic
properties. Such materials may have applications in the aerospace
industry.
59. Novel Multifunctional Fibre
Composites
• - Professor Steve Mann
• New types of composites with a combination of strength, toughness
and functionality are being prepared by combining research in the
synthesis of inorganic non-particles with that in the synthesis of
organic polymers.
• This interdisciplinary approach has been used to produce flexible
fibres of magnetic spider silk as shown in the photograph (left). Silk
fibres are coated by a dipping procedure using dilute suspensions of
inorganic nano-particles that are prepared with specific surface
properties.
• Similar methods are being investigated with swellable polymer gels
and bacterial supercellular fibres to produce novel hybrid
composites.