This document provides a 14-page overview of the metallurgical principles of mechanical working and forming of aluminum shapes. It outlines the objectives of describing the processes, prerequisites for understanding, and covers topics like how mechanical working produces changes in shape and microstructure, the role of dislocations in deformation, strengthening mechanisms, and specific forming processes like rolling, extrusion, and forging. It includes 14 figures to illustrate the concepts discussed.
TALAT Lecture 1205: Introduction to Mechanical Properties, Casting, Forming, ...CORE-Materials
This lecture provides background, basic information on mechanical properties and testing, solidification and casting, joining and corrosion of aluminium and its alloys. Basic knowledge of physics and chemistry and some familiarity with lectures 1201 and 1203 is assumed.
Study of behaviour of composite beams with truss type shear connectoreSAT Journals
Abstract
Composite action of two concrete members is achieved by the interface shear transfer between the two members; this mechanism is of great significance. The interface shear carrying capacity is dependent on the surface properties and shear connectors provided. In the current research ATENA is used, it is FEM based software in which the interface properties between materials can be modeled to a great level of detail. In the present study the influence of angle of inclination, size and the depth of embedment of truss connector on the load carrying behavior is studied with the help of a beam model. The angles of inclination varied are 30o, 45o, 60o and 75o with varying bar diameters of 8mm, 10mm and 12mm. Angles between 60o to 75o are found most efficient with no significant changes when diameters are varied. The ultimate load for a given connector is found to be independent of the depth of embedment. Composite beams are also modeled to study the influence of cohesion and friction coefficient, and are compared with behavior of solid and non-composite beams.
Keywords: Truss shear connector, Composite slab, ATENA, Slab flexure test, Interface shear capacity
TALAT Lecture 1205: Introduction to Mechanical Properties, Casting, Forming, ...CORE-Materials
This lecture provides background, basic information on mechanical properties and testing, solidification and casting, joining and corrosion of aluminium and its alloys. Basic knowledge of physics and chemistry and some familiarity with lectures 1201 and 1203 is assumed.
Study of behaviour of composite beams with truss type shear connectoreSAT Journals
Abstract
Composite action of two concrete members is achieved by the interface shear transfer between the two members; this mechanism is of great significance. The interface shear carrying capacity is dependent on the surface properties and shear connectors provided. In the current research ATENA is used, it is FEM based software in which the interface properties between materials can be modeled to a great level of detail. In the present study the influence of angle of inclination, size and the depth of embedment of truss connector on the load carrying behavior is studied with the help of a beam model. The angles of inclination varied are 30o, 45o, 60o and 75o with varying bar diameters of 8mm, 10mm and 12mm. Angles between 60o to 75o are found most efficient with no significant changes when diameters are varied. The ultimate load for a given connector is found to be independent of the depth of embedment. Composite beams are also modeled to study the influence of cohesion and friction coefficient, and are compared with behavior of solid and non-composite beams.
Keywords: Truss shear connector, Composite slab, ATENA, Slab flexure test, Interface shear capacity
Seminar Report on Brittle Fracture of ShipsVISHAL SHARMA
This study investigates the sinking of the Titanic from the theory of Brittle Fracture and
Engineering Failures. This study offers a subjectivist perspective of mental inertia to
understand the Titanic Disaster. Specifically, this study argue that the fall of the Titanic was
mainly due to Brittle Fracture of Rivets and the Hull Steel. Metallurgical and Mechanical
Analysis were performed on steel and rivet samples recovered from the wreck of the RMS
Titanic. It is found that the steel possessed a ductile-to-brittle transition temperature that was
very high with respect to the service temperature, making the material very brittle at ice-water
temperatures. This had been attributed to both chemical and microstructural factors. It is also
been found that the wrought iron rivets used in the construction of Titanic contained an elevated
amount of incorporated slag, and that the orientation of the slag within the rivets may hold an
explanation for how the ship accumulated damage during its encounter with the iceberg.
Keywords- Brittle fracture, Rivets, Hull Steel, Metallurgical Failure, Titanic Disaster.
System shear connector digunakan sebagai aplikasi dalam konstruksi bangunan untuk menghasilkan kekuatan coran beton lebih kuat dan stabil sesuai dengan perhitungan engineering civil. Dalam hal ini ada 2 hal perhitungan kekuatan secara umum yaitu kekuatan kelengketan stud pada batang baja sesudah dilas. Dan yang kedua adalah kekuatan stud bolt yang digunakan.
Seminar Report on Brittle Fracture of ShipsVISHAL SHARMA
This study investigates the sinking of the Titanic from the theory of Brittle Fracture and
Engineering Failures. This study offers a subjectivist perspective of mental inertia to
understand the Titanic Disaster. Specifically, this study argue that the fall of the Titanic was
mainly due to Brittle Fracture of Rivets and the Hull Steel. Metallurgical and Mechanical
Analysis were performed on steel and rivet samples recovered from the wreck of the RMS
Titanic. It is found that the steel possessed a ductile-to-brittle transition temperature that was
very high with respect to the service temperature, making the material very brittle at ice-water
temperatures. This had been attributed to both chemical and microstructural factors. It is also
been found that the wrought iron rivets used in the construction of Titanic contained an elevated
amount of incorporated slag, and that the orientation of the slag within the rivets may hold an
explanation for how the ship accumulated damage during its encounter with the iceberg.
Keywords- Brittle fracture, Rivets, Hull Steel, Metallurgical Failure, Titanic Disaster.
System shear connector digunakan sebagai aplikasi dalam konstruksi bangunan untuk menghasilkan kekuatan coran beton lebih kuat dan stabil sesuai dengan perhitungan engineering civil. Dalam hal ini ada 2 hal perhitungan kekuatan secara umum yaitu kekuatan kelengketan stud pada batang baja sesudah dilas. Dan yang kedua adalah kekuatan stud bolt yang digunakan.
Dislocations & Materials Classes , and strenthning mechanismsonadiaKhan
In brittle materials, failure in the film occurs when the stress exceeds a critical stress defined by the intrinsic atomic strength of the material and the nature of any critical defects. If the strength of the material can be increased or the size (or sharpness) of the defects decreased, then the film will be able to withstand higher levels of stress. It is important to emphasize that this approach will not reduce the stress in the system; so, bending and other detrimental effects will still occur.
The strength of the material can be increased by adding second-phase reinforcements that can be either permanent (e.g. fibers) or temporary (long-chain polymers). The size of critical defects can be modified through appropriate processing (either selection of route or control of processing) to ensure that the samples are free of critical defects. Large pores, introduced due to contamination, and poor powder packing or large grains are common strength-limiting defects in powder-based thick films – the use of fine grains and ensuring well-homogenized powders with no contaminants are therefore critical, as is high-quality deposition processing (Chapter 3).
Such strengthening mechanisms can play an important role, as there is a significant change in the mechanical properties of thick films during processing due to the rapidly evolving microstructure and chemistry of the system. Often, stresses in the system will increase before the strength of the material increases, leading to situations where the film is at a higher risk of failing mid-way through processing.
Overcoming Challenges of Integration
Reduce temperature
Reducing the temperature used for processing is by far the most effective way to overcome the challenges. It alleviates all the thermally induced issues, reduces (or even eliminates) chemical reactions, and reduces differential strains caused by reactions and temperature.
Separate reactants
Two reactive materials can be separated either by removing one material completely or by placing a barrier between the two materials. Protective atmospheres and barrier layers are frequently used.
Reduce differential strains
Select materials with comparable thermal expansions, those that do not undergo volume changes due to reactions or phase changes, or reduce the need to consolidate materials during processing.
Reduce film thickness
Building up multiple thin layers can allow much thicker films to be created, as each single layer is better able to withstand relative shrinkage during processing.
Strengthening
Modifying the materials to increase strength or interface strength of system can be used to prevent mechanical failure.
Read more
Creep of Intermetallics
M.-T. Perez-Prado, M.E. Kassner, in Fundamentals of Creep in Metals and Alloys (Third Edition), 2015
4.2.3 Strengthening Mechanisms
Several strengthening mechanisms have been utilized in order to improve the creep strength of NiAl alloys. Solid solution of Fe, Nb, Ta, Ti, and Zr produced only
This lecture provides an introduction to the metallurgy of precipitation hardening, with a presentation of the fundamental mechanisms involved and illustrations from alloys which form the basis for engineering alloys. The Al-Mg<sub>2</sub>Si system is discussed in some detail because of its commercial importance. The microstructural aspects of precipitation hardening are illustrated by examples, many of which were obtained by electron microscopy; an outline of the background to electron microscopy is given in an appendix. Familiarity with the subject matter covered in earlier lectures 1201, 1202 and 1203 is assumed.
This lecture describes the most significant correlation among foundry processes, microstructures and defects of castings and fatigue behaviour of Al casting alloys. No prior knowledge is strictly necessary; however, the basic concepts developed in TALAT lectures 2400 and 3200 are very useful for the comprehension of this lecture.
Research Inventy : International Journal of Engineering and Scienceresearchinventy
Research Inventy : International Journal of Engineering and Science is published by the group of young academic and industrial researchers with 12 Issues per year. It is an online as well as print version open access journal that provides rapid publication (monthly) of articles in all areas of the subject such as: civil, mechanical, chemical, electronic and computer engineering as well as production and information technology. The Journal welcomes the submission of manuscripts that meet the general criteria of significance and scientific excellence. Papers will be published by rapid process within 20 days after acceptance and peer review process takes only 7 days. All articles published in Research Inventy will be peer-reviewed.
Due to dislocations, it is no longer necessary to break all bonds between two atomic planes at once in order to shear off a lattice planes.
Rather, it is enough to overcome only one binding series at a time.
The dislocation line jumps step-by-step from atomic row to atomic row with little effort and finally emerges as a slip step on the surface of the material.
Case Study 7- A Bold Step into the Modern Economy & A Remote Solution for a G...
Mechanical Working and Forming of Shapes
1. TALAT Lecture 1251
Mechanical Working and Forming of Shapes
14 pages, 14 Figures
Advanced level
prepared by M H Jacobs
Interdisciplinary Research Centre in Materials
The University of Birmingham, UK
Objectives:
Outline of the metallurgical principles of mechanical working and forming of shapes
from aluminium.
Prerequisites:
Basic knowledge of physics and chemistry. Familiarity with the contents of TALAT
lectures 1201 through 1205.
Date of Issue: 1999
EAA - European Aluminium Association
2. 1251 Mechanical Working and Forming of Shapes
Contents (14 Figures)
1251 Mechanical Working and Forming of Shapes ________________________2
1251.01 Background to Mechanical Working and Forming______________________ 3
1251.01.01 Change of Shape ____________________________________________________3
1251.01.02 Change of Microstructure and Mechanical Properties ________________________4
1251.02 Forming Processes_______________________________________________ 12
1251.02.01 Flat Rolling _________________________________________________________12
1251.02.02 Extrusion _________________________________________________________12
1251.02.03 Forging___________________________________________________________13
1251.02.04 Sheet Metal Forming Processes ________________________________________13
1251.03 References ______________________________________________________ 14
1251.04 List of Figures ___________________________________________________ 14
TALAT 1251 2
3. 1251.01 Background to Mechanical Working and Forming
This involves the conversion of a cast ingot to a wrought product by processes which
are carried out at high temperatures or at room temperature and which might involve
reheating the material to restore ductility.
Two main aspects must be considered, which are (1) change of shape, and (2) change
of microstructure and mechanical properties. We will deal with these in turn.
1251.01.01 Change of Shape
As an example, consider the production of flat rolled products. If we start with a cast
ingot of a suitable alloy which is 5m long and 300mm thick, this slab can be
converted to foil which may be 7µm (.007mm) thick. Neglecting any change in width
that occurs, the length of foil produced from this ingot is about 200km. The change of
shape is expressed by measurement of strain. In the particular example, the total
reduction in thickness can be expressed as
Original thickness - Final thickness x 100 % = 99.998
Original thickness
This is called nominal strain or engineering strain.
Another way of expressing the thickness strain is
logn Original thickness = 10.7
Final thickness
This is called true strain.
Such large strains cannot be achieved in a single operation. The usual route is to start
with hot working processes followed by cold working and annealing,
Figure 1251.01.01.
TALAT 1251 3
4. 1251.01.02 Change of Microstructure and Mechanical Properties
The ability to undergo large plastic deformation is one of the most useful attributes of
metals. Metals with a face-centred cubic (fcc) crystal structure usually exhibit good,
isotropic ductility as a direct consequence of three sets of active slip planes. In this
respect, aluminium and its many alloys are excellent examples of a material that is
readily formed into complex shapes.
Metals usually consist of large numbers of individual grains or crystals; that is, they
are polycrystalline, see TALAT lecture 1201. A typical grain or crystal after hot
working, plus cold working and annealing will be of diameter, say, 40µm thus
contains many millions of unit cells, see Figure 1251.01.02.
In the cast condition, the initial crystals grow from the liquid phase and the resultant
microstructure is usually coarse, see TALAT lecture 1201. When the metal is
deformed, each grain deforms by the movement of line defects in the crystal lattice;
deformation is by slip on slip planes along the shear direction, see
Figure 1251.01.03. These defects are known as dislocations, Figure 1251.01.04.
The dislocations move on certain crystallographic planes in the crystals (close-packed
planes) which are known as slip planes, see again TALAT lecture 1201. The
movement of a single dislocation produces a shear strain and the combined motion of
hundreds of thousands of dislocations produces the total strain.
TALAT 1251 4
5. Figure 1251.01.05 lists four points that emphasise the importance of dislocations and
the ease with which they slip under the influence of an applied stress:
Metals, especially those with a cubic crystal structure, are ductile and tough
because dislocations can move through the crystal lattice with relative ease.
Large single crystals of a pure metal are very WEAK because the dislocations
present can move easily without encountering obstacles.
Very small single crystals (METAL WHISKERS) are very strong because there
is insufficient crystal volume for them to deform by the movement of
dislocations.
TALAT 1251 5
6. Commercial metals and alloys are strengthened by various types of
OBSTACLES to the movement of dislocations.
Obstacles to dislocation movement, Figure 1251.01.06, include one or more of the
following:
(1) Grain boundaries
(2) Other dislocations (work hardening)
(3) Solute atoms (solution hardening)
(4) Precipitated GP zones (precipitation hardening)
(5) Dispersed particles (dispersoid hardening).
Some or all of these may contribute to the strength of a metal or alloy,
Figure 1251.01.07:
TALAT 1251 6
7. σy = σo + σd + σs + σp + kd-0.5 (1)
where
σy = overall yield stress
σo = stress due to basic lattice
σd = stress due to dislocations interactions
σs = stress due to resistance to dislocation movement caused by
solute atoms (size effect)
σp = stress due to obstacles resented as precipitate particles and
dispersoid particles
The effect of grain size is given by the Hall-Petch relationship
σ = Constant + kd-0.5 , where d is the grain size (mean diameter).
During deformation at room temperature the number of dislocations increases and it
becomes increasingly difficult for dislocations to move through the lattice, i.e. the
metal work hardens or strain hardens. This means that higher loads are required to
continue deformation and the metal loses ductility, eventually leading to cracking and
failure. At the atomistic level the situation is complex and the theory of dislocations
has been developed to a high degree in order to understand the details of the
mechanisms involved [1]. During deformation, slip is very active and moving
dislocations on intersecting slip planes will give rise to jogs which, in themselves,
make only a small contribution to hindering dislocation movement and associated
work hardening; of move importance is the interaction between opposing strain fields
that surround dislocations, which gives rise to tangles or ‘forests’ of dislocations,
Figure 1251.01.07.
During work hardening in which dislocation forests are formed, the flow stress σ is
given by
σ = constant x √ (dislocation density) (2)
TALAT 1251 7
8. Dislocations may be removed by heating the cold worked metal to a moderately high
temperature (annealing) which causes the metal to soften and restores ductility. The
changes in microstructure which occur during annealing are referred to as recovery
and recrystallisation, see TALAT lecture 1201.
During deformation at elevated temperatures, restoration processes may occur. These
are called dynamic recovery or dynamic recrystallisation. In aluminium alloys, the
former is more likely to occur. As a result of these processes, the metal does not
strain harden as much as it does at room temperature and consequently lower loads
are required to deform the material. But, under these conditions, the speed of
deformation, or strain rate, becomes an important parameter of the process.
Several different techniques must be used to observe the microstructural features
referred to above. In order to observe dislocations, it is necessary to use transmission
electron microscopy (TEM) A thin foil of the material is prepared and inserted in an
electron microscope, and dislocations are revealed by diffraction contrast, see TALAT
lecture 1204, section 1204.05 Appendix. In aluminium alloys after a moderate
amount of deformation, the dislocations are not uniformly distributed but instead they
form cells, with walls of tangled dislocations and interior regions of low dislocation
density, see Figure 1251.01.08. Typically, these cells have a diameter of the order of
1µm. When recovery occurs, the cell walls become clean boundaries and the units are
then referred to as subgrains. However, when a large amount of cold work is
followed by annealing, new grains are formed by the process of recrystallisation,
Figure 1251.01.09.
TALAT 1251 8
9. The driving force for recrystallisation is the stored energy caused by the presence of
dislocations, Figure 1251.01.10.
The dislocation density can be expressed as the total length of dislocation lines in a
unit volume of the material. For annealed material this may be about 1010m-2 and for
heavily cold worked material the dislocation density rises to about 1015m-2.
TALAT 1251 9
10. The response of a metal to stress at constant temperature, Figure 1251.01.11 may be
expressed as:
σ = k εn εm (3)
where σ = stress
ε = strain
ε = strain rate
n = strain hardening exponent
m = strain rate sensitivity.
Figure 1251.01.12 and Figure 1251.01.13 show schematically the temperature
dependences of strain hardening and strain rate hardening in pure aluminium. These
figures show that the strain rate sensitivity of pure aluminium increases significantly
with temperature above 200°C. This reflects the importance of the dynamic recovery
at high temperatures.
TALAT 1251 10
11. Note that aluminium alloys that are formable by superplastic deformation have strain
rate sensitivities > 0.5. A stable, fine scale microstructure is required for superplastic
deformation, by which ductilities of several hundreds of percent are possible. This
requires special alloy compositions, containing Zirconium which provides particles
which pin grain boundaries, Figure 1251.01.14.
In heat treatable aluminium alloys, the effective hardening precipitates are very small
and it is necessary to use TEM to observe these directly, see TALAT lecture 1204 on
precipitation hardening. Also the small sub-micron dispersoid particles present in
some alloys are observable only by TEM.
Other features of the microstructure may be observed by optical microscopy – these
include the grain size, the degree of recrystallisation, the grain aspect ratio and
coarse intermetallic particles.
TALAT 1251 11
12. Yet another aspect of the microstructure is concerned with the orientations of the
grains. During deformation involving crystallographic slip, rotations occur leading to
the lining up of crystals in preferred directions. The non-random distribution of
orientations is known as preferred orientation or crystallographic texture. The
preferred orientation developed during deformation is known as a deformation
texture and when the material is subsequently recrystallised, a new preferred
orientation is formed which is a recrystallisation texture. The presence of texture in
wrought products influences directionality of mechanical properties, an important
example in aluminium process technology being the control of earring in canstock
material used for the production of beverage cans.
Preferred orientation is usually measured by X-ray diffraction methods.
Another source of directionality, particularly in some of the strong aluminium alloys
in plate form, is associated with grain morphology. Flat, elongated grains account for
lower ductility, lower toughness and lower stress corrosion resistance in the short
transverse direction.
In the deformation and heat treatment of aluminium alloys, particles of intermetallic
compounds play an important role especially in relation to the recrystallisation
behaviour. Large particles, with diameters of the order of 1µm or more, create strain
concentrations during deformation and can act as nucleation sites for recrystallisation.
On the other hand, small particles (dispersoids) interact with moving grain boundaries
and can prevent grain growth.
The above considerations relate generally to deformation and we can now consider
briefly some specific working processes, flat rolling, extrusion, forging and sheet
metal forming processes.
1251.02 Forming Processes
1251.02.01 Flat Rolling
The first stage in the process is hot rolling. Slabs are pre-heated to a temperature of
up to ~500°C, depending on the alloy composition and the rolling to plate with a
thickness of ~7mm is often carried out without reheating, so that the temperature falls
during deformation.
A typical rolling mill for this stage is a large 4-high reversing mill, with work rolls of
about 1m diameter and back-up rolls of about 1.5m diameter.
Cold Rolling is carried out on a variety of mills depending on the alloy and the
dimensions of the strip - a single 4-high mill, tandem mill or cluster mill (Sendzimir)
can be used. In the case of very thin strip, the application of front and back tension is
important.
1251.02.02 Extrusion
TALAT 1251 12
13. The advantage of the extrusion process is that complicated cross section products can
be made in a single operation. It is a hot forming process carried out on large and
expensive extrusion presses. For large extruded sections, the loading capacity of the
press may be about 7000t.
1251.02.03 Forging
Forging of aluminium alloys is carried out at high temperatures in the region of
400°C. While the main outlet for aluminium forgings has been the aerospace
industry, commercial products now occupy a significant portion of the market.
Examples of commercial products are suspension units for trucks, wheels,
components for racing cars, etc.
1251.02.04 Sheet Metal Forming Processes
These are usually carried out at room temperature. The processes involved are
bending, stretch forming and deep drawing. The range of products is enormous,
ranging from aircraft fuselages to beer cans. Currently, efforts are being made to
introduce aluminium alloys into car bodies. The room temperature formability of
aluminium alloys is not as good as that of some competitive materials such as low-
carbon steels.
For the forming of complex shapes in a single operation, superplastic forming offers
possibilities. Aluminium alloys have been developed for superplastic forming
applications.
TALAT 1251 13
14. 1251.03 References
1. R E Smallman, Modern Physical Metallurgy, Fourth Edition, Butterworth
Heinemann, 1985.
1251.04 List of Figures
Figure No. Figure Title (Overhead)
1251.01.01 Processing of Aluminium Sheet from Ingot
1251.01.02 Grains and grain sizes
1251.01.03 Deformation by shear on slip planes
1251.01.04 Deformation by slip of a dislocation
1251.01.05 Deformation by slip of dislocations
1251.01.06 Obstacles to dislocation movement
1251.01.07 Modified Hall Petch Relationship
1251.01.08 Dislocations and work hardening
1251.01.09 Work hardening, recovery and recrystallisation
1251.01.10 Stored Energy
1251.01.11 Response of metals to stress
1251.01.12 Temperature dependence of strain hardening for pure aluminium
1251.01.13 Temperature dependence of strain rate hardening for pure aluminium
1251.01.14 Superplastic Forming – requires stable, fine microstructure
TALAT 1251 14