This document provides an introduction and overview of Laser Shock Processing (LSP). It discusses how LSP works by using high-intensity laser pulses to generate shock waves that induce deep compressive residual stresses in metals, increasing fatigue strength. It describes how LSP can be applied to both external and internal surfaces to strengthen areas prone to fatigue failure. The document also outlines the basic LSP method and process, including how parts are prepared and treated with the laser system.
Laser shock peening produces a compressive residual stress in the surface of metallic materials, which significantly increases fatigue life in applications where failure is caused by surface-initi ated cracks. Laser shock peening is applied by using a high energy pulsed laser to create a high amplitude stress wave or shock wave on the surface to be treated. This stress wave propagates into the material, causing the surface layer to yield and plastically deform, and thereby, develop a residual compressive stress. Where comparisons have been made to shot peening, the magnitude of the residual stresses at the surface are similar, but the compressive stresses from laser peening extend much deeper below the surface than those from shot peening. The resulting fatigue life enhancement is often greater for laser peering than it is for shot peening. In addition to fatigue strength improvement, laser peering can also locally strain harden thin sections of parts or strain harden a surface
Laser Shock Peening of Bulk Metallic GlassesDeepak Rajput
Final report on Laser Shock Peening of Bulk Metallic Glasses submitted by Deepak Rajput at the University of Tennessee at Knoxville.
This experiment was not so fruitful. Also, there is a mistake in the concept of "overlap". However, this was the first ever attempt on laser shock processing of bulk metallic glasses.
Laser shock peening produces a compressive residual stress in the surface of metallic materials, which significantly increases fatigue life in applications where failure is caused by surface-initi ated cracks. Laser shock peening is applied by using a high energy pulsed laser to create a high amplitude stress wave or shock wave on the surface to be treated. This stress wave propagates into the material, causing the surface layer to yield and plastically deform, and thereby, develop a residual compressive stress. Where comparisons have been made to shot peening, the magnitude of the residual stresses at the surface are similar, but the compressive stresses from laser peening extend much deeper below the surface than those from shot peening. The resulting fatigue life enhancement is often greater for laser peering than it is for shot peening. In addition to fatigue strength improvement, laser peering can also locally strain harden thin sections of parts or strain harden a surface
Laser Shock Peening of Bulk Metallic GlassesDeepak Rajput
Final report on Laser Shock Peening of Bulk Metallic Glasses submitted by Deepak Rajput at the University of Tennessee at Knoxville.
This experiment was not so fruitful. Also, there is a mistake in the concept of "overlap". However, this was the first ever attempt on laser shock processing of bulk metallic glasses.
Laser Beam Machining and it's full Criteria.
By- Engr. Md Abu Bakar Siddique
Industrial and Production Engineer,
Rajshahi University of Engineering and Technology,
Bangladesh
Autogenous laser welding of the AA6082-T651 aluminium alloy was investigated with 3 lasers, namely a pulsed laser of 300W, a disk laser of 4kW and a laser marker of 70W. First, the hot cracking susceptibility was studied with two conventional laser welding equipment, without using filler material or heat treatment. Additionally, an attempt was made to weld with a laser marking equipment. Most of the welds made were laser seam welds but, some continuous and laser spot welds were also tested. As each laser was operated with different parameters, more than 400 welds were obtained with a wide range of parameters. Selected welds were studied with visual inspection, dye penetrant inspection (DPI), optical microscopy and scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS). Results indicated that welds with pulse laser beam tend to develop hot cracking, due to the segregation of silicon-rich low melting point eutectics to the grain boundaries and the development of contraction stresses during solidification. On the other hand, positive results were found with continuous welding since this process results in much longer solidification times and lower stresses. Finally, promising results were obtained with the laser marking machine, which produced high aspect ratio laser seam welds without hot cracking and a penetration of 1 mm using 99.9% of overlap factor. These welds were crack free due to their small weld pool, avoiding segregation effects, and to the heat build-up of successive spots, what had similar effect to solidification in continuous welding.
Microstructure and Mechanical Properties of Nano Alumina Particulate Reinforc...IJERA Editor
A356, which is much lighter than steel, is an attractive replacement material. Therefore, it is of great interest to
enhance its properties. There is strong evidence that the microstructure and mechanical properties can be
considerably improved if nano particles are used as reinforcement to form metal-matrix- nano-composite
(MMNC). In this thesis, a detailed analysis of alumina i.e.., 60µm is reduced to 32nm by high energy ball
milling. For every 5hrs alumina powder is taken and calculating the crystallite size by X-Ray Diffraction. In this
thesis, a detailed analysis of the microstructure and mechanical properties is provided for an A356 alloy
enhanced with alumina nano particles via ultrasonic processing. Each type of the nano particles was inserted
into the A356 molten metal and dispersed by ultrasonic cavitation and acoustic streaming technology (UST) to
avoid agglomeration or coalescence. The results showed that Microstructures and hardness studies increased
significantly. SEM and EDS analyses were also performed to analyze the dispersion of micro and nano particles
of Alumina.
LASER BEAM MACHINING - NON TRADITIONAL MACHININGSajal Tiwari
Laser Beam Machining or more broadly laser material processing deals with machining and material processing like heat treatment, allowing, cladding, sheet metal bending etc. Such processing is carried out utilizing the energy of coherent photons or laser beam, which is mostly converted into thermal energy upon interaction with most of the materials. Nowadays, the laser is also finding application in regenerative machining or rapid prototyping as in processes like stereolithography, selective laser sintering etc. Laser stands for light amplification by stimulated emission of radiation. The underline working principle of a laser was first put forward by Albert Einstein in
1917 through the first industrial laser for experimentation was developed around the 1960s. The laser beam can very easily be focused using optical lenses as their wavelength ranges from half a micron to around 70 microns. The focused laser beam as indicated earlier can have power density in excess of 1 MW/mm2 . As laser interacts with the material, the energy of the photon are absorbed by the work material leading to a rapid substantial rise in local temperature. This, in turn, results in melting and vaporization of the work material and finally material removal.
Laser Beam Machining and it's full Criteria.
By- Engr. Md Abu Bakar Siddique
Industrial and Production Engineer,
Rajshahi University of Engineering and Technology,
Bangladesh
Autogenous laser welding of the AA6082-T651 aluminium alloy was investigated with 3 lasers, namely a pulsed laser of 300W, a disk laser of 4kW and a laser marker of 70W. First, the hot cracking susceptibility was studied with two conventional laser welding equipment, without using filler material or heat treatment. Additionally, an attempt was made to weld with a laser marking equipment. Most of the welds made were laser seam welds but, some continuous and laser spot welds were also tested. As each laser was operated with different parameters, more than 400 welds were obtained with a wide range of parameters. Selected welds were studied with visual inspection, dye penetrant inspection (DPI), optical microscopy and scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS). Results indicated that welds with pulse laser beam tend to develop hot cracking, due to the segregation of silicon-rich low melting point eutectics to the grain boundaries and the development of contraction stresses during solidification. On the other hand, positive results were found with continuous welding since this process results in much longer solidification times and lower stresses. Finally, promising results were obtained with the laser marking machine, which produced high aspect ratio laser seam welds without hot cracking and a penetration of 1 mm using 99.9% of overlap factor. These welds were crack free due to their small weld pool, avoiding segregation effects, and to the heat build-up of successive spots, what had similar effect to solidification in continuous welding.
Microstructure and Mechanical Properties of Nano Alumina Particulate Reinforc...IJERA Editor
A356, which is much lighter than steel, is an attractive replacement material. Therefore, it is of great interest to
enhance its properties. There is strong evidence that the microstructure and mechanical properties can be
considerably improved if nano particles are used as reinforcement to form metal-matrix- nano-composite
(MMNC). In this thesis, a detailed analysis of alumina i.e.., 60µm is reduced to 32nm by high energy ball
milling. For every 5hrs alumina powder is taken and calculating the crystallite size by X-Ray Diffraction. In this
thesis, a detailed analysis of the microstructure and mechanical properties is provided for an A356 alloy
enhanced with alumina nano particles via ultrasonic processing. Each type of the nano particles was inserted
into the A356 molten metal and dispersed by ultrasonic cavitation and acoustic streaming technology (UST) to
avoid agglomeration or coalescence. The results showed that Microstructures and hardness studies increased
significantly. SEM and EDS analyses were also performed to analyze the dispersion of micro and nano particles
of Alumina.
LASER BEAM MACHINING - NON TRADITIONAL MACHININGSajal Tiwari
Laser Beam Machining or more broadly laser material processing deals with machining and material processing like heat treatment, allowing, cladding, sheet metal bending etc. Such processing is carried out utilizing the energy of coherent photons or laser beam, which is mostly converted into thermal energy upon interaction with most of the materials. Nowadays, the laser is also finding application in regenerative machining or rapid prototyping as in processes like stereolithography, selective laser sintering etc. Laser stands for light amplification by stimulated emission of radiation. The underline working principle of a laser was first put forward by Albert Einstein in
1917 through the first industrial laser for experimentation was developed around the 1960s. The laser beam can very easily be focused using optical lenses as their wavelength ranges from half a micron to around 70 microns. The focused laser beam as indicated earlier can have power density in excess of 1 MW/mm2 . As laser interacts with the material, the energy of the photon are absorbed by the work material leading to a rapid substantial rise in local temperature. This, in turn, results in melting and vaporization of the work material and finally material removal.
Under GTU course of Allied Manufacturing Techniques; Laser Beam Machining & Laser Beam Welding is prime methods used in todays technical era in industries
Observability Concepts EVERY Developer Should Know -- DeveloperWeek Europe.pdfPaige Cruz
Monitoring and observability aren’t traditionally found in software curriculums and many of us cobble this knowledge together from whatever vendor or ecosystem we were first introduced to and whatever is a part of your current company’s observability stack.
While the dev and ops silo continues to crumble….many organizations still relegate monitoring & observability as the purview of ops, infra and SRE teams. This is a mistake - achieving a highly observable system requires collaboration up and down the stack.
I, a former op, would like to extend an invitation to all application developers to join the observability party will share these foundational concepts to build on:
Communications Mining Series - Zero to Hero - Session 1DianaGray10
This session provides introduction to UiPath Communication Mining, importance and platform overview. You will acquire a good understand of the phases in Communication Mining as we go over the platform with you. Topics covered:
• Communication Mining Overview
• Why is it important?
• How can it help today’s business and the benefits
• Phases in Communication Mining
• Demo on Platform overview
• Q/A
Unlocking Productivity: Leveraging the Potential of Copilot in Microsoft 365, a presentation by Christoforos Vlachos, Senior Solutions Manager – Modern Workplace, Uni Systems
Sudheer Mechineni, Head of Application Frameworks, Standard Chartered Bank
Discover how Standard Chartered Bank harnessed the power of Neo4j to transform complex data access challenges into a dynamic, scalable graph database solution. This keynote will cover their journey from initial adoption to deploying a fully automated, enterprise-grade causal cluster, highlighting key strategies for modelling organisational changes and ensuring robust disaster recovery. Learn how these innovations have not only enhanced Standard Chartered Bank’s data infrastructure but also positioned them as pioneers in the banking sector’s adoption of graph technology.
State of ICS and IoT Cyber Threat Landscape Report 2024 previewPrayukth K V
The IoT and OT threat landscape report has been prepared by the Threat Research Team at Sectrio using data from Sectrio, cyber threat intelligence farming facilities spread across over 85 cities around the world. In addition, Sectrio also runs AI-based advanced threat and payload engagement facilities that serve as sinks to attract and engage sophisticated threat actors, and newer malware including new variants and latent threats that are at an earlier stage of development.
The latest edition of the OT/ICS and IoT security Threat Landscape Report 2024 also covers:
State of global ICS asset and network exposure
Sectoral targets and attacks as well as the cost of ransom
Global APT activity, AI usage, actor and tactic profiles, and implications
Rise in volumes of AI-powered cyberattacks
Major cyber events in 2024
Malware and malicious payload trends
Cyberattack types and targets
Vulnerability exploit attempts on CVEs
Attacks on counties – USA
Expansion of bot farms – how, where, and why
In-depth analysis of the cyber threat landscape across North America, South America, Europe, APAC, and the Middle East
Why are attacks on smart factories rising?
Cyber risk predictions
Axis of attacks – Europe
Systemic attacks in the Middle East
Download the full report from here:
https://sectrio.com/resources/ot-threat-landscape-reports/sectrio-releases-ot-ics-and-iot-security-threat-landscape-report-2024/
Essentials of Automations: The Art of Triggers and Actions in FMESafe Software
In this second installment of our Essentials of Automations webinar series, we’ll explore the landscape of triggers and actions, guiding you through the nuances of authoring and adapting workspaces for seamless automations. Gain an understanding of the full spectrum of triggers and actions available in FME, empowering you to enhance your workspaces for efficient automation.
We’ll kick things off by showcasing the most commonly used event-based triggers, introducing you to various automation workflows like manual triggers, schedules, directory watchers, and more. Plus, see how these elements play out in real scenarios.
Whether you’re tweaking your current setup or building from the ground up, this session will arm you with the tools and insights needed to transform your FME usage into a powerhouse of productivity. Join us to discover effective strategies that simplify complex processes, enhancing your productivity and transforming your data management practices with FME. Let’s turn complexity into clarity and make your workspaces work wonders!
UiPath Test Automation using UiPath Test Suite series, part 4DianaGray10
Welcome to UiPath Test Automation using UiPath Test Suite series part 4. In this session, we will cover Test Manager overview along with SAP heatmap.
The UiPath Test Manager overview with SAP heatmap webinar offers a concise yet comprehensive exploration of the role of a Test Manager within SAP environments, coupled with the utilization of heatmaps for effective testing strategies.
Participants will gain insights into the responsibilities, challenges, and best practices associated with test management in SAP projects. Additionally, the webinar delves into the significance of heatmaps as a visual aid for identifying testing priorities, areas of risk, and resource allocation within SAP landscapes. Through this session, attendees can expect to enhance their understanding of test management principles while learning practical approaches to optimize testing processes in SAP environments using heatmap visualization techniques
What will you get from this session?
1. Insights into SAP testing best practices
2. Heatmap utilization for testing
3. Optimization of testing processes
4. Demo
Topics covered:
Execution from the test manager
Orchestrator execution result
Defect reporting
SAP heatmap example with demo
Speaker:
Deepak Rai, Automation Practice Lead, Boundaryless Group and UiPath MVP
Generative AI Deep Dive: Advancing from Proof of Concept to ProductionAggregage
Join Maher Hanafi, VP of Engineering at Betterworks, in this new session where he'll share a practical framework to transform Gen AI prototypes into impactful products! He'll delve into the complexities of data collection and management, model selection and optimization, and ensuring security, scalability, and responsible use.
Why You Should Replace Windows 11 with Nitrux Linux 3.5.0 for enhanced perfor...SOFTTECHHUB
The choice of an operating system plays a pivotal role in shaping our computing experience. For decades, Microsoft's Windows has dominated the market, offering a familiar and widely adopted platform for personal and professional use. However, as technological advancements continue to push the boundaries of innovation, alternative operating systems have emerged, challenging the status quo and offering users a fresh perspective on computing.
One such alternative that has garnered significant attention and acclaim is Nitrux Linux 3.5.0, a sleek, powerful, and user-friendly Linux distribution that promises to redefine the way we interact with our devices. With its focus on performance, security, and customization, Nitrux Linux presents a compelling case for those seeking to break free from the constraints of proprietary software and embrace the freedom and flexibility of open-source computing.
GraphSummit Singapore | The Future of Agility: Supercharging Digital Transfor...Neo4j
Leonard Jayamohan, Partner & Generative AI Lead, Deloitte
This keynote will reveal how Deloitte leverages Neo4j’s graph power for groundbreaking digital twin solutions, achieving a staggering 100x performance boost. Discover the essential role knowledge graphs play in successful generative AI implementations. Plus, get an exclusive look at an innovative Neo4j + Generative AI solution Deloitte is developing in-house.
Epistemic Interaction - tuning interfaces to provide information for AI supportAlan Dix
Paper presented at SYNERGY workshop at AVI 2024, Genoa, Italy. 3rd June 2024
https://alandix.com/academic/papers/synergy2024-epistemic/
As machine learning integrates deeper into human-computer interactions, the concept of epistemic interaction emerges, aiming to refine these interactions to enhance system adaptability. This approach encourages minor, intentional adjustments in user behaviour to enrich the data available for system learning. This paper introduces epistemic interaction within the context of human-system communication, illustrating how deliberate interaction design can improve system understanding and adaptation. Through concrete examples, we demonstrate the potential of epistemic interaction to significantly advance human-computer interaction by leveraging intuitive human communication strategies to inform system design and functionality, offering a novel pathway for enriching user-system engagements.
Climate Impact of Software Testing at Nordic Testing DaysKari Kakkonen
My slides at Nordic Testing Days 6.6.2024
Climate impact / sustainability of software testing discussed on the talk. ICT and testing must carry their part of global responsibility to help with the climat warming. We can minimize the carbon footprint but we can also have a carbon handprint, a positive impact on the climate. Quality characteristics can be added with sustainability, and then measured continuously. Test environments can be used less, and in smaller scale and on demand. Test techniques can be used in optimizing or minimizing number of tests. Test automation can be used to speed up testing.
GraphSummit Singapore | The Art of the Possible with Graph - Q2 2024Neo4j
Neha Bajwa, Vice President of Product Marketing, Neo4j
Join us as we explore breakthrough innovations enabled by interconnected data and AI. Discover firsthand how organizations use relationships in data to uncover contextual insights and solve our most pressing challenges – from optimizing supply chains, detecting fraud, and improving customer experiences to accelerating drug discoveries.
Removing Uninteresting Bytes in Software FuzzingAftab Hussain
Imagine a world where software fuzzing, the process of mutating bytes in test seeds to uncover hidden and erroneous program behaviors, becomes faster and more effective. A lot depends on the initial seeds, which can significantly dictate the trajectory of a fuzzing campaign, particularly in terms of how long it takes to uncover interesting behaviour in your code. We introduce DIAR, a technique designed to speedup fuzzing campaigns by pinpointing and eliminating those uninteresting bytes in the seeds. Picture this: instead of wasting valuable resources on meaningless mutations in large, bloated seeds, DIAR removes the unnecessary bytes, streamlining the entire process.
In this work, we equipped AFL, a popular fuzzer, with DIAR and examined two critical Linux libraries -- Libxml's xmllint, a tool for parsing xml documents, and Binutil's readelf, an essential debugging and security analysis command-line tool used to display detailed information about ELF (Executable and Linkable Format). Our preliminary results show that AFL+DIAR does not only discover new paths more quickly but also achieves higher coverage overall. This work thus showcases how starting with lean and optimized seeds can lead to faster, more comprehensive fuzzing campaigns -- and DIAR helps you find such seeds.
- These are slides of the talk given at IEEE International Conference on Software Testing Verification and Validation Workshop, ICSTW 2022.
In his public lecture, Christian Timmerer provides insights into the fascinating history of video streaming, starting from its humble beginnings before YouTube to the groundbreaking technologies that now dominate platforms like Netflix and ORF ON. Timmerer also presents provocative contributions of his own that have significantly influenced the industry. He concludes by looking at future challenges and invites the audience to join in a discussion.
1. LSP Technologies, Inc.
Laser Shock Processing
Technical Bulletin No. 1
Introduction
What Does It Do?
Laser Shock Processing (LSP) produces a number of beneficial effects in metals and
alloys. Foremost among these is increasing the resistance of materials to surface-related
failures, such as fatigue, fretting fatigue and stress corrosion cracking. It does this by
driving compressive residual stresses deep into metals and alloys. Much deeper than shot
peening. For these applications the process is referred to as laser shock peening.
There are a number of other reasons to use LSP besides increasing fatigue strength and
fatigue life; it can be used to strengthen thin sections, work-harden surfaces, shape or
straighten parts, break up hard materials, possibly to consolidate or compact powdered
metals, and still others remaining to be discovered.
Applying LSP
LSP can often be applied to the finished surface of a part, or just prior to the final
finishing step. In machine components, tooling and other parts, application to external
surfaces and internal surfaces with line-of-sight access is straightforward. Application to
internal surfaces without line-of-sight access is quite possible, but the method used is
application specific and requires some development for each application.
LSP works by exerting a mechanical force on the part surface; the surface is not affected
thermally. However, process options can be selected which have a limited thermal effect
and offer potential cost benefits. The effects of the mechanical force on the surface itself
are minimal. In softer alloys, a very shallow surface depression occurs, which decreases
in depth in harder materials. For example, in aluminum alloys, the depression is about
250 minches (6 mm) deep, but on machined surfaces of harder alloys, it is difficult to see
where the surface was laser shocked. The depth of the depression does increase with
increasing intensity of shock peening.
With LSP, treating just the fatigue critical area(s) on a part without masking the area
around it is easily accomplished. This enables localized treatment around holes, and in
and along notches, keyways, fillets, splines, welds, and other highly stressed regions.
The intensity of LSP can be easily controlled and monitored, allowing the process to be
tailored to the specific service and manufacturing requirements demanded by the part.
The flexible nature of the process accommodates a wide range of part geometries and
2. 2
sizes. It can also be used in combination with other treatments, e.g., shot peening or
coatings, to achieve the most beneficial property and cost advantages for each part.
LSP can also be used in manufacturing processes requiring a high, controllable,
mechanical impact over a defined area, where mechanical punches are limited in how
they can be adapted to the task. The impact area could have a variety of shapes.
The first production application of laser shock peening began in 1997 on a military gas
turbine engine blade. More production applications will begin in 1998.
Benefits
The use of LSP to obtain increased strength and resistance to failure offers several
advantages. After applying LSP to failure-prone areas on troublesome parts, the service
life of the parts and the maintenance intervals of machinery can be increased and
downtime decreased, without changing the design. Alternatively, a part or machine can
be redesigned to make them lighter, easier to manufacture, or less expensive, using LSP
to upgrade the properties to meet the original design performance requirements.
It is a new manufacturing tool that could offer more control, flexibility or unique effects
for upgrading current products or developing new ones than other methods.
LSP Technologies, Inc.
LSP Technologies, Inc. provides commercial laser shock processing services and
equipment. We are the only company providing LaserPeenTM laser peening services to
industry, and building LaserPeenTM equipment specifically for laser shock processing
applications. In 2000 we will be introducing our new RapidPeenTM process and
associated RapidPeenTM equipment for increased throughput and lower cost. In 2001 we
will introduce a factory-floor ready laser shock peening system.
LSP Technologies’ key management and staff have many years of experience in the
development and use of laser-generated shock waves for a wide variety of applications.
Our staff’s experience dates back to the early 1970’s, when we began developing the
technology at Battelle Memorial Institute in Columbus, Ohio.
The company is located in Dublin, Ohio, a suburb of Columbus, in new facilities for
production processing of parts and development of new applications. The facility has two
laser shock peening systems that provide flexibility for processing a wide variety of parts.
The Laser Shock Process
The Laser Shock Process is a mechanical process for treating materials, not a thermal
process. The laser is a high-energy, pulsed Neodymium-glass laser, producing a very
short pulse, 15 to 30 nanoseconds long, having a wavelength of 1.06 mm, with an energy
3. 3
per pulse of 50 joules or more. The laser beam is directed from the laser through an
optical chain of mirrors and lenses onto the surface of the part being treated.
Description of the Process
A schematic of how the process works is shown in Figure 1. The area to be treated on a
part is locally covered with two types of overlays: an opaque overlay, opaque to the laser
beam directly on the surface of the part, and over this a transparent overlay, transparent to
the laser beam (Figure 1a). The opaque overlay can be any material opaque to the laser
beam; a black coating is commonly used. The transparent overlay can be any material
transparent to the laser beam; water is commonly used.
When the laser beam is directed onto the surface to be treated, it passes through the
transparent overlay and strikes the opaque overlay. As shown in Figure 1b, when the
laser beam strikes the surface of the opaque overlay, it immediately vaporizes a thin
surface layer of the overlay. This vapor then absorbs the incoming laser energy, rapidly
heating and expanding against the surfaces of the workpiece and the transparent overlay.
a. Surface area to be laser shocked, showing the laser beam and overlays.
b. Effect of laser beam at the overlay-workpiece interface.
Figure 1. Schematics of how the laser shock process works.
4. 4
The transparent overlay acts to trap the thermally expanding vapor against the surface of
the workpiece, and consequently causes the pressure to rise much higher than it would
if the transparent overlay were absent. The sudden, high pressure against the surface of
the workpiece causes a shock wave to propagate into the material. If the peak stress of
this shock wave is above the dynamic yield strength of the material, the material yields
and plastically deforms. As the stress wave propagates deeper into the material, the peak
stress of the wave decreases, but deformation of the material continues until the peak
stress falls below its dynamic yield strength. This plastic deformation caused by the
shock wave gives rise to the compressive residual stresses at the surface of the workpiece
(Figure 1b). This is one of the most useful effects caused by LSP.
The shape of the laser treated spots is generally round, but other shapes can be used, if
necessary, to provide the most efficient and effective processing conditions. The size of
the area treated in one pulse depends on a number of material, laser and processing
factors. The spot size can range from about 1 inch (25 mm) to about 0.1 inch (2.5mm) in
diameter. A typical spot size for the development laser is about 0.25 inches (6 mm) to
0.35 inches (9 mm) or larger.
Processing Parts
In practice, the laser is located next to a work station in which the parts are held and
manipulated during processing. A part is placed in the work station by loading it into a
fixture, then the part and fixture are moved into the proper position for processing. After
positioning the part, the laser beam is directed into the work station, treating the desired
spot on the part. The part is then either moved to the next position for the following shot,
or is removed from the work station and replaced with the next part. For a high-rate
production run, each of the work station steps: part pick-up, positioning, processing and
removal, would be performed automatically. With the current developmental laser-work
station arrangement some of these steps are being performed manually.
Parts are set up for laser shock processing in either of two ways. For thicker sections,
nominally 0.5 inches (12 mm) thick or more, a single beam enters the work station and is
directed onto the area being treated. To minimize distortion of the part in thinner sections
the laser beam is usually split into two beams of equal intensity, and these beams strike
the part on opposite surfaces simultaneously. Thin sections can be treated from one side
only, if necessary, by using a back up support.
The size of the area to be treated depends on the part design and service conditions.
Sometimes, a part requires that only a small area be treated and a single treated spot will
suffice, e.g., around small oil, pin or bolt holes, or at the root of a notch in the side of a
thin section. In other instances, the areas requiring treatment will be larger, e.g., an area
on a turbine blade, crankshaft fillet, or gear. In these cases, successive spots are
overlapped until the desired region is completely covered.
Laser Shock Peening
5. 5
When laser shock processing is used to increase fatigue life, straighten or shape parts,
increase stress corrosion cracking resistance, or for other applications where surface
compressive residual stresses are used to provide the desired result, it is referred to as
laser shock peening instead of laser shock processing (although both will be referred to as
LSP). In these applications it acts in much the same way as shot peening, except that LSP
drives the compressive stresses and work hardening deeper into the material without
significantly degrading the surface.
All past experience indicates that LSP can be used for any material and application for
which shot peening has been used. It is not expected that laser peening will replace shot
peening for large area coverage. Indeed, in some cases it may be best to combine the two
processes, laser shock peening the fatigue critical areas and shot peening the rest of the
part surface.
Properties of Laser Shock Peened Materials
A number of metals and alloys have been treated by LSP, including steels, aluminum
alloys, titanium alloys, nickel-base superalloys, cast irons and a powder metallurgy iron
alloy. In most cases, these investigations did not include both residual stresses and
fatigue results in the same study, or directly compare LSP and shot peening. However,
the information presented here clearly illustrates the residual stress distribution, fatigue,
strength and hardness changes representative of LSP in a variety of alloys. It should be
emphasized that none of the results shown here represent the optimum or maximum
benefit condition for the particular material or application.
The nature of the residual stresses will be shown first, followed by fatigue, then strength
and hardness properties.
Residual Stresses
All residual stresses were measured using x-ray diffraction. The existence of residual
stresses at the surface of a crystalline material creates elastic strains in the crystal lattice
that alters the spacing between the lattice planes, i.e., tension increases the spacing and
compression decreases the spacing. The x-ray diffraction technique measures the spacing
of the crystallographic lattice planes at the surface of the part. The difference in the
measured lattice spacing at the surface of the part from that of an unstressed crystal lattice
of the same material is due to the presence of the elastic strains at the surface of the part.
The measured elastic strain is then related to the residual stress through the elastic moduli
of the material, allowing the residual stress to be calculated from the x-ray measurements
of the lattice strain.
The distribution of the residual stress below the material surface was determined by
successively removing a thin layer from the surface by electropolishing, then making x-
ray measurements on the new surface. Electropolishing does not introduce stresses into
the surface as would machining or grinding. This incremental process was continued
6. 6
down to the maximum depth of interest, usually 0.020 to 0.050 inches (0.5 to 1.2 mm)
deep. An analytical technique was then used to calculate the stress distribution below the
surface as it existed before disturbing it by removing the layers. This analytical technique
accounts for both the stress relaxation occurring as material is removed, and for the depth
of penetration of the x-rays into the stress gradient.
Surface Distribution of Residual Stresses
It is important to have relatively uniform residual stresses across the treated area on a
part, and LSP provides this. The surface stress distribution along the radius of a laser
shock peened spot is shown in Figure 2 for an aluminum alloy. This is typical for all
other alloys where surface distributions were determined. The stress distribution is
essentially uniform except for a slight dip in the center of the spot. There has been no
evidence that this dip has affected fatigue behavior. In the next section, it will be seen
that the dip extends only a few thousandths of an inch below the surface.
In Figure 2, the residual stresses in both the tangential and radial directions are shown.
These stresses are nominally equal in the interior of the laser treated spot, but at the spot’s
outside edge, they tend to differ. Immediately outside the treated spot a surface tensile
residual stress forms tangentially to compensate for the compressive stresses inside the
spot, whereas in the radial direction this effect is often absent. To avoid having this
peripheral tensile residual stress affect the post-processed properties, the treated area must
be large enough to move this stress outside the fatigue-critical area.
40
Radial Stress
20 Tangential Stress
Residual Stress, ksi
0
Laser Shocked Region
-20
7075-T6
-40
-60
-80
-100
0 1 2 3 4 5 6
Distance from Center of Laser Spot, mm
Figure 2. Uniform surface residual stress distribution from the center to the outside
of a laser shock peened spot in 7075-T6 aluminum.
Larger areas are laser peened with overlapping spots. Extensive measurements have
shown that there is no tensile residual stress around the edges of the spots either on the
surface, or in the subsurface compressive stress layer within the overlapped area. The
7. 7
residual stresses within the laser peened areas created by overlapping spots is uniform
across the group of spots.
In addition to laying out a treatment pattern consisting of multiple spots, specially tailored
spot shapes can be used to provide different surface and in-depth distributions of the
residual stress. Figure 3a shows an example of an annular-shaped spot around a hole,
a. Layout of annular-shaped laser shock peened region around a hole.
60
Surface 2024-T351
40 -0.0035 inches
-0.0125 inches
Residual Stress, ksi
20
Laser Shocked Zone
0
Drilled Hole
-20
-40
-60
-80
0.00 0.05 0.10 0.15 0.20 0.25 0.30 0.35
Distance from center of annulus, inches
b. Residual stress profiles along the path shown in a. above.
Figure 3. Residual stress profiles along the radius across an annular-shaped spot,
including the surface and two levels below the surface.
with the inside diameter of the laser shocked region slightly larger than the diameter of
the hole. Figure 3b shows the resulting residual stress distributions along a radius
8. 8
through the annular spot at the surface and at depths of 0.0035 and 0.0125 inches (0.09
and 0.31 mm) below the surface. At 0.012 inches and more below the surface, the stress
is reduced more rapidly around the edges of the annulus than in the middle. This is
caused by the peak pressure being decreased by release shock waves traveling in from the
edges of the shock wave.
It is noteworthy that the compressive residual stress is increased between the inside
diameter of the annular shocked region and the hole, even though this area was not
shocked (the unshocked surface residual stress is about -8 ksi). The hole was drilled
before LSP.
Increasing the intensity of laser shock peening increases the magnitude of the surface
compressive residual stresses. This effect is demonstrated in the next section where the
effects of laser peening intensity is shown for both the surface and in-depth residual
stresses.
In-Depth Residual Stress Distribution
The distribution of the residual stresses below the surface is usually much deeper for LSP
than it is for shot peening. The actual depths of the LSP-induced stresses will vary
depending on the type and intensity of the processing conditions chosen and the material
properties, but in general the depths will range from 0.020 to 0.040 inches (0.5 to 1 mm)
deep or more. For comparison, the depths from shot peening will generally be under
0.010 inches (0.025 mm) deep. Achieving deeper stresses with shot peening often causes
a degradation of the surface caused by the severe impact conditions of the shot. In
addition, LSP seldom produces the “hook” in the compressive residual stress profile just
below the surface that is observed after shot peening, i.e., the compressive residual stress
increases with increasing depth for a short distance below the surface to a maximum, then
decreases with increasing depth. After LSP, the residual stress is usually highest at the
surface and decreases gradually with distance below the surface.
The deep penetration of the compressive residual stresses produced by laser shock
peening is illustrated for 2024-T351 aluminum in Figure 4, where the residual stresses are
still high 0.040 inches (1 mm) below the surface. Figure 4 also shows that the in-depth
stress uniformity across the shock peened spot is good. The stress measurements were
made at two points within the laser shocked peened spot, one in the center and one at the
mid-radius. The good agreement between these results demonstrates that the surface dip
in the residual stress in the center of the spot extends to no more than between 0.003 to
0.008 inches (0.075 to 0.2 mm) deep, and more importantly, that the in-depth stress
distribution is uniform to at least the mid-radius of the spots.
9. 9
10
0
Residual Stress, ksi
-10
-20
-30
-40 2024-T351
-50 Not Laser Shock Peened
Center of Laser Spot
-60 Mid-radius of Laser Spot
-70
0.000 0.010 0.020 0.030 0.040 0.050
Depth, inches
Figure 4. In-depth residual stress profiles are deep and consistent from the center to at
least the mid-radius of the laser shock peened spot.
Increasing the laser shock peening intensity drives the compressive stresses deeper below
the surface. Figure 5 shows this for a titanium alloy laser peened as 0.5 inch-thick plate.
Lower intensity shock peening produces both a lower surface compressive stress and a
shallower depth. The compressive stress extends to only about 0.010 inches (0.25 mm)
below the surface. An intermediate intensity shock peening creates a higher surface
compressive stress and this stress extends down to about 0.020 inches (0.5 mm). After a
higher intensity peening, the compressive stresses extend down to about 0.030 to 0.040
inches (0.75 to 1 mm). The stresses after LSP generally lie in the range of -100 to -120
ksi (689 to 827 MPa) for this alloy, although higher surface stresses have been observed.
Figure 5 is also representative of the response of other titanium alloys and titanium to
LSP, recognizing that depending on the particular alloy properties and processing
conditions, the stresses may be somewhat higher or lower, and could extend deeper below
the surface.
The compressive residual stresses also extend far into the nickel-base superalloy, IN718,
as shown in Figure 6 for 0.5 inch-thick plate. Steels also respond well to LSP. Figure 7
shows the residual stresses in a steel used for aircraft landing gear. The compressive
residual stresses extend for a significant distance below the surface.
The residual stresses in the preceding Figures were measured in relatively thick sections,
0.25 to 0.5 inches (6.3 to 12.7 mm) thick. In thinner sections, laser shock peened with a
split beam from both sides, the depth of the residual stresses will be affected by the
interaction of the shock waves from opposite surfaces. This is shown in Figure 8 for
0.060-inch (1.5-mm) thick 4340 steel sheet hardened to 54 RC. In this case, a higher
intensity treatment does not necessarily drive the compressive residual stresses deeper
into the material (since the thickness limits this), but it does increase their magnitude. It is
10. 10
20
0
Residual Stress, ksi
-20
-40
-60 Ti-6Al-4V
Low Intensity LSP
-80
Intermediate Intensity LSP
-100 High Intensity LSP
Not Laser Shocked
-120
0.000 0.010 0.020 0.030 0.040 0.050
Depth, inches
Figure 5. In-depth residual stresses in Ti-6Al-4V at three different laser shock
peening intensity levels.
50
0
Residual Stress, ksi
-50
-100
IN718
-150 Not Laser Peened
High Intensity LSP
-200
0.000 0.010 0.020 0.030 0.040 0.050
Depth, inches
Figure 6. In-depth residual stress in nickel-base superalloy IN718.
11. 11
40
Residual Stress, ksi 0
-40
-80
AF 1410 Steel
-120 Not Shocked
Laser Shock Peened
-160
0.000 0.010 0.020 0.030 0.040
Depth, inches
Figure 7. Residual stresses in AF 1410 steel.
50
0
Residual Stress, ksi
-50
4340 Steel
-100 54 R
C
Not Shocked
-150 1 shot, LSP
5 shots, LSP
-200
0.000 0.005 0.010 0.015 0.020 0.025 0.030
Depth, inches
Figure 8. Residual stress profiles in 4340 steel sheet. Mid-thickness of the sheet is
0.030 inches (0.75 mm).
likely that the residual stress profile shown is symmetrical around the mid-thickness at
0.030 inches (0.75 mm).
Thermal Stability of Residual Stresses
In service conditions involving elevated temperatures, the thermal stability of the residual
stresses becomes an important issue. To retain the benefits of the residual stresses at
higher service temperatures, the residual stresses must be resistant to thermal recovery. A
titanium alloy, Ti-8Al-1V-1Mo , was laser peened, then held at elevated temperatures in
the service temperature range of interest, for four hours(1). After these anneals, the
12. 12
residual stress profiles were measured. The results, in Figure 9, show that after four
hours there is no recovery of the residual stress.
40
20
Residual stress, ksi
0
-20
-40
-60 Ti-8Al-1V-1Mo
-80 LSP, Not Annealed
LSP, Annealed 450F, 4 hr
-100
LSP, Annealed 750F, 4 hr
-120
0.000 0.010 0.020 0.030 0.040 0.050
Depth, inches
Figure 9. In-depth residual stress profiles after annealing Ti-8Al-1V-1Mo for 4
hours at elevated temperatures(1).
Fatigue
Fatigue tests have been made on several metals and alloys, some of which relate to the
residual stress Figures shown earlier.
A significant application of LSP will be the protection of fan blades in aircraft gas turbine
engines against failure from foreign object damage (FOD). The Air Force recently
completed a study of the comparison between laser shock processing and shot peening of
F101 fan blades(2). These blades are fabricated from the Ti-8Al-1V-1Mo titanium alloy.
The laser shock peened blades were treated with one LSP intensity. The shot peened
blades were treated at two different intensity levels; one a typical dual-intensity peening
procedure using glass beads followed by shot at an intensity of 0.014A, and the other a
high intensity peening procedure consisting of peening a narrow, 0.25-inch (6.3-mm)
wide strip at the leading edge of the blade to 0.012C and a 0.5-inch (12.7-mm) wide strip
behind it to 0.018C. These are shown in Figure 10 The latter shot peening condition was
intended to provide a deep residual stress distribution comparable to that of LSP. With
both methods, the blades were not treated over the entire surface, but rather over a patch
1.5 inches (38 mm) long by 0.75 inches (19 mm) wide along the leading edge of the
airfoil in the region where the blades are most sensitive to FOD damage.
To simulate FOD, after the LSP and shot peening treatments, either a 0.25-inch (6.3-mm)
deep notch made with a chisel, or a 0.125-inch (3.1-mm) deep notch made by electrical
13. 13
LSP Dual Intensity SP High Intensity SP
First Pass = 14A 18C ½“
Second Pass = ¾“
Low Intensity Glass Bead 12C ¼“
Chisel Notch 1 ¾“
Figure 10. The configuration of the treated areas on the leading edge of F101 First
Stage fan blades(2).
discharge machining was introduced into the leading edge of the blades. These notches
were located in the center of the treated region as shown on the left in Figure 10.
Before fatigue testing, the blades were heated to 400 F and held for 24 hours to
accommodate any stress relief which might occur under this condition in service. After
the stress relief, the blades were tested in a siren testing device. The test procedure was to
begin testing at a low stress amplitude level, then increase the stress amplitude by 10 ksi
after every 106 fatigue cycles. The results are shown in Figure 11. It is striking that LSP
was able to retain a fatigue life at least equivalent to that of the undamaged, peened blade,
even in the presence of the severe damage. Shot peening also increased the fatigue life of
the damaged blades compared to blades that received no peening treatment at all.
Siren Testing Device
Heated 24 hr at 400F before
100 testing at Room Temperature
10 Cycles at Indicated Stress, Ksi
90
80
6
70 10 Cycles
60
50
40
6
30
20
Type and Depth No Chisel EDM Chisel EDM Chisel EDM Chisel EDM
of Notch: Damage 0.25" 0.125" 0.25" 0.125" 0.25" 0.125" 0.25" 0.125"
Surface Dual Intensity Baseline Dual Intensity High Intensity Laser Shock
Treatment: Shot Peened None Shot Peened Shot Peened Peened
Figure 11. Comparison of laser shock peening and shot peening for foreign object
damage resistance in F101 fan blades(2).
Several different aspects of laser shock processing and fatigue conditions have been
investigated in aluminum alloys. One comparison made in 2024-T351 aluminum alloy
14. 14
plate concerned fatigue crack propagation from a fastener hole, Figure 12. The fatigue
specimens were large: 0.25-inch (6.3-mm) thick, with a gauge section 4 inches (101.6
mm) wide by 10 inches (254 mm) long. The fatigue behavior was determined by
measuring the fatigue crack length, a, vs. the number of cycles, N, for the non-shocked
condition and two laser shock peened conditions. For one of the LSP conditions, the hole
was in the center of a solid treated spot. In the other condition, the hole was surrounded
by an annular-shaped spot as previously shown in Figure 3a. The specimens were tested
in tension-tension, R = 0.1, at 15 ksi maximum stress amplitude. Considering the fatigue
life to be nominally the point where the crack length curves become nearly vertical, the
LSP condition with the solid spot had a fatigue life about 40 times longer than the non-
shocked condition, whereas the condition with the annular spot had a life about 3 times
longer than the non-shocked condition.
When the areas around holes in sheet materials are laser shock peened with a solid spot
around a hole, the crack tends to initiate on the hole surface at mid-thickness, and then
tunnels down the mid-thickness of the sheet between the compressive surface layers
before it breaks through to the surface beyond the laser shocked region. While the crack
propagation rate is slowed considerably by this behavior, (Figure 14, solid spot), and
fatigue life is significantly increased, the crack itself is not easily detected. This is
sometimes a concern in failure-sensitive applications.
Figure 12. Fatigue crack propagation in non-shocked and laser shock peened 2024-
T351 aluminum. The crack length, a, is shown vs. the number of cycles,
N.
15. 15
The annular spot was chosen to demonstrate that a crack could be initiated and detected at
a fastener hole, and then be significantly slowed when it reaches the laser shocked region.
This would allow ample time for the detection and monitoring of cracks originating from
holes before failure.
LSP is also effective in arresting pre-existing cracks. Large specimens similar to that
described above were pre-fatigued to create cracks 0.020 inches (0.5 mm) long, coming
out each side of the fastener hole. The region ahead of each crack was then laser shock
peened, and the specimens re-tested. The results are shown in Figure 13. The unshocked
condition had a fatigue life of about 145,000 cycles, and the laser shocked condition
without a pre-crack had a lives of 700,000 to 1,000,000 cycles. After pre-cracking and
laser shocking, the fatigue lives were in the same range as those of the laser shocked
material tested without a precrack.
Precracking Cycles
Not Laser 2024-T351
Shocked
Laser Shock
Peened
Precracked,
Laser Shock
Peened
5 5 5 5 6 6
0 2 10 4 10 6 10 8 10 1 10 1.2 10
Number of Cycles to Failure, N
f
Figure 13. The effect of laser shock peening on precracked specimens of 2024-T351
aluminum.
The fatigue life of weldments can also be extended by LSP. Plates of 5456 aluminum
alloy 0.25 inches (6.3 mm) thick were butt-welded together, the weld bead machined off,
and the weld and heat-affected-zones laser shocked with overlapping spots. Test
specimens machined from this plate were then tested in tensile fatigue, R=0, in both the
as-welded and laser shock peened conditions, Figure 14. At a stress amplitude of 20 ksi,
the fatigue life was increased by at least an order of magnitude. More significantly, at 23
ksi the fatigue life was increased from less than 50,000 cycles to more than 3 to 6 million
cycles without failure after LSP.
Laser shock peening is also effective against fretting fatigue. Dog-bone specimens and
pads of 7075-T6 aluminum were laser treated around a simulated fastener hole in
each piece (Figure 15a), then fastened together through the hole with a manufactured
16. 16
20 ksi
5456 Al
Not Shocked
Laser Shocked
23 ksi
Not Shocked
Laser Shocked
4 5 6 7 8
10 10 10 10 10
Cycles to Failure, N
f
Figure 14. Fatigue life increased in welded 5456 aluminum after laser shock
peening.
(CSK) fastener. This combination was then fatigue tested in tension at R = 0.1. The
stress differential between the larger cross-section of the pad and the smaller cross-
section of the dog-bone created an elongation differential between the two pieces during
each cycle, leading to fretting around the fastener hole. The results are shown in Figure
15b. The tests were initially conducted at 14 ksi. When a long life was reached, the
stress was raised in 10 percent increments until failure occurred within few hundred
thousand cycles. Even at 16.4 ksi, the fretting fatigue life is increased by LSP.
Fatigue improvement after laser shock peening thin sections was demonstrated in steel
sheet. 4340 steel sheet, 0.060 inches (1.5 mm) thick, heat treated to RC 54 hardness, was
laser shock peened and tested in tensile fatigue in the specimen configuration shown in
Figure 16a. The roots of both notches were laser shocked with one spot, using a split
beam as shown. The fatigue tests were conducted at R = 0.1 with the results shown in
Figure 16b. The run-out stress of the unshocked condition was taken from a handbook.
The specimen numbers are attached to the individual data points. Specimens 2, 3, and 4
were stepped up in stress after reaching well over a million cycles. Laser shock peening
produced a large increase in the run-out stress, from about 85 ksi (586 MPa) to 140 to 150
ksi (965 to 1034 MPa).
In thicker pieces, a notch would be treated by laser shock peening directly into the notch.
To demonstrate the effectiveness of LSP in this case, a beam specimen of 4340 steel,
hardened to 54 RC, 0.25 inches (6.3 mm) thick, 0.75 inches (19 mm) deep and 8 inches
(203.2 mm) long, had a notch having a KT @ 1.7 machined into the upper surface. The
notch was shocked from one side only, directly into the notch. The beams were fatigue
tested in 4-point bending with tensile loads at the notched surface. Without LSP the
specimens failed in the notch after 40,000 cycles. After LSP at intermediate and high
17. 17
a. Fretting fatigue specimen configuration
b. Fretting fatigue results
Figure 15. Increased resistance to fretting fatigue around fastener holes after laser
shock peening 7075-T6 aluminum.
18. 18
a. Specimen and laser shock peening configuration. Dimensions in inches.
b. Tensile fatigue results.
Figure 16. The tensile fatigue strength of 4340 steel sheet increased significantly by
laser shock peening.
intensities, no fatigue failures were observed originating in the notch. Instead, after the
bending load was increased to a level about 25 percent higher than the unshocked run-out
stress, the specimens began failing under the loading pins. How much higher the notch
failure load was raised could not be determined with this test configuration.
A part made from 1026 steel was failing at 30,000 cycles from the formation of cracks at
the locations shown in Figure 17a. Just these regions were laser shock peened as shown
19. 19
in Figure 17b, with two overlapping spots. After treatment, the fatigue life was tripled
from 33,000 cycles to 92,000 cycles.
a. Untreated, Nf = 33,000 cycles. b. Laser shocked, Nf = 92,000 cycles.
Figure 17. A 1026 steel part, locally laser shock peened to triple its fatigue life.
Fatigue-limited metals, including pearlitic and ferritic malleable cast irons, and iron
powder metallurgy materials show fatigue life improvements after laser shock peening.
A comparison between LSP and shot peening is shown in Figure 18. This was performed
on AF 1410 steel cylindrical test bars fatigue tested under flight spectrum loading. The
LSP bar’s fatigue life was 56 percent longer than that of the unshocked bars, and 25
percent longer than that of the shot peened bars.
Laser Shock
Peened
Shot peened
As-machined
AF 1410 Steel
4
0 2000 4000 6000 8000 1 10
Spectrum Flight Hrs to Failure
Figure 18. Fatigue of AF 1410 Steel tested under Flight Spectrum loading
conditions comparing shot peening and laser shock peening.
Strength and Hardness
By essentially cold working the surface of metals and alloys, LSP strain hardens the
surface layer. An example of the surface hardness profile across a laser shocked spot is
shown in Figure 19 for 2024-T351 aluminum.
20. 20
180
2024-T351
170
Hardness, DPH500
160
150
Baseline
140 Laser Shocked Region Hardness
130
0 0.2 0.4 0.6 0.8 1 1.2
Distance, inches
Figure 19. Surface hardening across a laser shock peened spot in 2024-T351
aluminum.
In 316 stainless steel the surface hardness was measured on spots given increasing
numbers of multiple shots. The hardness increased continuously with additional shots as
shown in Figure 20. Other alloys, such as 7075 aluminum and 2024-T8 aluminum did
not show surface hardening under the laser shocking conditions investigated. This
behavior reflects their relative strain hardening behavior and possibly dynamic yield
strength. Surface strain hardening will be greater in materials with a higher strain
hardening coefficient and lower dynamic yield strength.
450
400
Hardness, KHN
350
300
250
316 Stainless Steel
200
0 2 4 6 8 10 12
Number of Shots
Figure 20. Increasing surface hardness of 316 stainless steel with increasing laser
shock peening intensity.
21. 21
In thin sections, through-thickness hardening and over-all strengthening can be obtained
after shocking from both sides with the split beam arrangement. This arises from two
effects. One is the strain hardening of the surface layer and the other is hardening in the
mid-thickness of the section from the local superposition of the shock waves from
opposite surfaces. The last effect decreases with increasing thickness, becoming
inconsequential in sections thicker than about 0.25 inches (6.3 mm).
Two examples of this effect are shown in Figures 21 and 22. Figure 21 shows the
hardness through the thickness of a 0.1-inch (2.54 mm) thick sheet of 2024-T351 after
LSP. The base hardness was 140 VHN (Vickers hardness). The hardness gradually
decreased below each surface as the peak pressure of the shock wave decreased. The
bump in hardness in the mid-section where the shock waves traveling in opposite
directions super-imposed is clearly evident.
Figure 22 shows the increase in tensile yield strength of weld zones in two aluminum
alloys, a work-hardening alloy, 5086-H32, and an age-hardening alloy, 6061-T6, after
170
2024-T351
Hardness, DPH500
160
150
Baseline Hardness
140
0 0.2 0.4 0.6 0.8 1
Front Back
Surface
Distance, mm Surface
Figure 21. Through-thickness hardening in 2024-T351 aluminum after split-beam
laser shock peening from both sides simultaneously.
LSP of the weld and heat affected zones. The specimens were 0.120 inches (3 mm) thick
when laser shocked. After LSP the 5086 alloy regained its parent metal strength, as
would be expected in a work-hardening alloy. The 6061 alloy regained about half of the
strength lost by welding. In this age-hardening alloy, restoring the remainder of the
strength lost would require an aging heat treatment. From this response it is clear that
LSP could be used to provide localized strain hardening and strengthening in metallic
parts for selected applications.
22. 22
Parent Alloy
As Welded 5086-H32
Welded and LSP
Parent Alloy
As Welded 6061-T6
Welded and LSP
0 10 20 30 40 50
0.2% Yield Strength, ksi
Figure 22. The strengthening of weld and heat affected zones in aluminum alloys by
laser shock peening.
Stress Corrosion Cracking
There is limited evidence that laser shock peening should be beneficial in increasing
resistance to stress corrosion cracking. Since shot peening offers such improvement by
producing residual compressive stresses in the surface, LSP should offer similar or more
improvement due to the deeper compressive stresses.
Applications of Laser Shock Processing
Many of the potential applications of laser shock processing are based on laser shock
peening for increased fatigue resistance. The initial applications being implemented for
LSP are representative of those anticipated at this stage of development: processing high-
value-added parts for improved performance, or using LSP to replace a traditional process
or material to achieve a cost advantage. Applications which fall in these categories are
aircraft engine parts, aircraft structures, medical implants and prostheses, components of
power generation turbines and other turbines, specialized gears and parts in valves, and
other mechanism components having notches, holes and corners prone to fatigue failure.
With ongoing laser and process development, costs will continue to decrease rapidly,
opening the way to an ever-broader range of applications including automotive gears,
cams, rocker arms and connecting rods, tool bits, tooling and dies.
In considering applications of LSP, it should not be viewed as a competitor to shot
peening, but instead, as its complement. In many cases, LSP will be used alone where
shot peening is not suitable or cannot be used for various reasons. These reasons could
include better properties, treatment of difficult geometries, improved quality control,
smoother finished surface, or ease of processing, to name a few. In other cases LSP will
23. 23
be used along with shot peening, to provide additional protection in fatigue critical
regions.
In addition to laser shock peening, there are potential uses in a variety of applications
having nothing to do with fatigue, but instead based on the localized strain hardening or
shock impact characteristics of the process. For example, localized surface plastic strain
induced by shock impact could enhance diffusion bonding of small components, or
similarly, a coating. The shock wave may be used to locally densify porous coatings, or
to compact powders in unique situations. It may also be useful in unique metal forming
operations or connector attachments.
Quality Control
Quality control issues for laser shock peening can be addressed in numerous ways. For
example, a number of the laser beam parameters can be monitored and recorded for each
shot in real time. In addition, there are process parameters that can be monitored using
features on the material surface, measurement of material properties, or other
characteristics of the process. Periodic checks can be made by sampling the residual
stress distributions and property changes in processed parts.
Many of these process-related parameters can be measured and used to control the
process in real time. For these, acceptable limits of their values can be defined, and
corrections made immediately if they drift outside of these limits during processing.
References
1. C. Lykins, P. Prevey, and P. Mason, Laser Shock Peened Compressive Residual
Profile After Exposure to Temperature, AF Report WL-TR-95-2108, September,
1995, Wright Patterson AFB, OH.
2. C. O. Lykins, “Laser Shock Peening vs. Shot Peening, A Damage Tolerance
Investigation”, Proceedings Surface Treatment of Titanium Alloys, Cincinnati, OH,
October, 1996.
The rest of the information presented in this report has been taken from the following
papers and reports.
A. H. Clauer, B. P. Fairand and B. A. Wilcox, “Laser Shock hardening of weld Zones in
Aluminum Alloys”, Metallurgical Transactions A, 8A, 1871-1876 (December, 1977).
A. H. Clauer and B. P. Fairand, “Interaction of Laser-Induced Stress Waves With
Metals”, Applications of Lasers in Materials Processing, ed. by E. Metzbower, ASM,
Metals Park, OH (1979).
24. 24
A. H. Clauer, B. P. Fairand, and J. Holbrook, “Effects of Laser-Induced Shock Waves on
Metals”, Shock Waves and High Strain Rate Phenomena in Metals, ed. by M. A. Meyers
and L. E. Murr, Plenum Press, New York (1981), pp. 675-702.
A. H. Clauer, C. T. Walters, and S. C. Ford, “The Effects of Laser Shock Processing on
the Fatigue Properties of 2024-T3 Aluminum”, Lasers in Materials Processing, ASM,
Metals Park, OH (1983) pp. 7-22.
T. R. Tucker and A. H. Clauer, Laser Processing of Materials, Report MCIC-83-48,
Metals and Ceramics Information Center, Columbus, OH (November, 1983).
Laser Shock Processing Increases the Fatigue Life of Metal Parts, Materials and
Processing Report, 6, (6), 3 (September, 1991).
LSP Technologies, Inc. is interested in helping you with your fatigue
and other product problems that can be solved using laser shock
peening or laser shock processing.
Please Contact:
David W. Sokol
LSP Technologies, Inc.
6145 Scherers Place
Dublin, OH 43016-1284
Phone: (614) 718-3000 Ext. 14
Fax: (614) 718-3007
e-mail: dsokol@lspt.com