This document discusses the influence of slag composition on copper losses in the slag-cleaning furnace at Konkola Copper Mines in Zambia. It finds through linear regression analysis that the major components of slag (Fe3O4, SiO2, Al2O3, MgO, CaO) influence copper losses, as slag composition affects liquidus temperature and fluidity. The composition of flash smelting furnace slag supplied to the slag-cleaning furnace has varied over two years of data analyzed, presenting operational challenges. Copper losses occur through dissolved oxides and entrained metal prills, and are affected by reduction reactions with coke, slag viscosity influencing droplet settling rates, and bath ag
Low grade iron ores are often contaminated with relatively high percentage of different
impurity gangue minerals. The iron ores contaminated with manganese oxide and silica are hardly reducible
and consume more energy in the integrated steel plant. Therefore it is important to estimate and predict the
influence of manganese oxide, silica and temperature on the reduction yield of iron oxide using mathematical
model approach. In the current study, a 23
(three-parameters, two-levels)factorial design is applied on the
gaseous reduction experimental data of mixed oxides (Fe2O3-MnO2-SiO2) to build a linear regression model.
The calculations have been performed using Matlab program. The developed mathematical model indicated that
SiO2 and temperature have positive effect on the reduction yield of iron oxide. On the other hand, MnO2
exhibited the highest negative impact on the reduction yield of iron oxide followed by the interaction coefficient
of MnO2, SiO2 and temperature. The results of the developed mathematical model are fitted to the experimental
reduction data of mixed oxides.
IJERA (International journal of Engineering Research and Applications) is International online, ... peer reviewed journal. For more detail or submit your article, please visit www.ijera.com
Simulation of non metallic inclusions formation during liquid steel reoxidizingAlexander Alexeenko
Processes of inclusions formation during steel reoxidizing were investigated by computer simulation and SEM analysis of oxide inclusions in steel samples. The thermodynamic-based model of interaction between oxide inclusions and liquid metal in the line of equilibrium state and program for computation of inclusions transformation are developed. For Al- and Si-killed steels trajectories of change of inclusions chemical composition from initial FexO phase formed during reoxidation to final inclusions oxide phases were computed. Those finals phases are: heterogeneous inclusions (grains of hard spinals solution |MnO.Al2O3,FeO.Al2O3| + interlayers from phase based on MnO–SiO2–Al2O3 system, and Al2O3 cover) in LCAK-steel with Si content 0.01 wt. pct; hard inclusions based on Al2O3–MnO–SiO2 system in LCAK-steel with Si content 0.2 wt. pct, manganese silicates in medium carbon Si-killed steel. Computer simulation of inclusion transformation in LCAK-steel showed that Si significantly increases a time of transformation from initial liquid phase FexO to hard phases. It explains the well-known fact that LCAK-steels with Si > 0.1 wt. pct has better castability than low silicon ones.
Low grade iron ores are often contaminated with relatively high percentage of different
impurity gangue minerals. The iron ores contaminated with manganese oxide and silica are hardly reducible
and consume more energy in the integrated steel plant. Therefore it is important to estimate and predict the
influence of manganese oxide, silica and temperature on the reduction yield of iron oxide using mathematical
model approach. In the current study, a 23
(three-parameters, two-levels)factorial design is applied on the
gaseous reduction experimental data of mixed oxides (Fe2O3-MnO2-SiO2) to build a linear regression model.
The calculations have been performed using Matlab program. The developed mathematical model indicated that
SiO2 and temperature have positive effect on the reduction yield of iron oxide. On the other hand, MnO2
exhibited the highest negative impact on the reduction yield of iron oxide followed by the interaction coefficient
of MnO2, SiO2 and temperature. The results of the developed mathematical model are fitted to the experimental
reduction data of mixed oxides.
IJERA (International journal of Engineering Research and Applications) is International online, ... peer reviewed journal. For more detail or submit your article, please visit www.ijera.com
Simulation of non metallic inclusions formation during liquid steel reoxidizingAlexander Alexeenko
Processes of inclusions formation during steel reoxidizing were investigated by computer simulation and SEM analysis of oxide inclusions in steel samples. The thermodynamic-based model of interaction between oxide inclusions and liquid metal in the line of equilibrium state and program for computation of inclusions transformation are developed. For Al- and Si-killed steels trajectories of change of inclusions chemical composition from initial FexO phase formed during reoxidation to final inclusions oxide phases were computed. Those finals phases are: heterogeneous inclusions (grains of hard spinals solution |MnO.Al2O3,FeO.Al2O3| + interlayers from phase based on MnO–SiO2–Al2O3 system, and Al2O3 cover) in LCAK-steel with Si content 0.01 wt. pct; hard inclusions based on Al2O3–MnO–SiO2 system in LCAK-steel with Si content 0.2 wt. pct, manganese silicates in medium carbon Si-killed steel. Computer simulation of inclusion transformation in LCAK-steel showed that Si significantly increases a time of transformation from initial liquid phase FexO to hard phases. It explains the well-known fact that LCAK-steels with Si > 0.1 wt. pct has better castability than low silicon ones.
Ferrosilicon productiion and submerged arc furnace (1)Nasser Harby
Ferroalloys, by definition, are alloys of two or more metals, of which one is Iron. The U.S. Bureau of Mines defines ferroalloy as an alloy of iron with at least one other element except for carbon.
The main indicator of the quality of a ferroalloy is its chemical composition and, above all, the content of the leading element. It is important to have Consistency in alloying element amounts in ferroalloys from heat to heat, allowing the manufacture of standard products
The smelting of ferroalloys is commonly performed in electric arc furnaces.
Although ferromanganese can be produced in a blast furnace in a manner similar to iron, the reduction of chromium and silicon from their oxides requires higher Process temperatures and lower oxygen potentials than can be achieved in a blast furnace
Raw materials are perhaps the most important factor for obtaining good furnace operation the first step towards improvements is to reduce the variations
The aim of this course is to present the basic principles for the production of ferrosilicon alloys processes, and a simple preview for submerged arc furnaces.
It is attended for Engineers working in this field, and students or metallurgists maybe find answers for their questions, because at the end of this course you will figure out that you have a preview for this manufacture and the main problems and solutions for the ferrosilicon production process. And having an overview for submerged arc furnaces design and operations.
.
Effect Of CaO, FeO, MgO, SiO2 and Al2O3 Content of Slag on Dephosphorization ...karun19
Phosphorus has atomic number 15 and it can give up all 5 electrons from its outermost shell to become P5+ or accept 3 electrons to become P3- to attain stable configuration.
This means that phosphorus can be removed both under oxidizing as well as reducing conditions.
But removal of phosphorus under reducing conditions is not practical since its removal is highly hazardous.
Thus P removal is practised mostly under oxidizing conditions(i.e. in Basic Oxygen Furnace).
Effects of thermo mechanical simulation on the corrosion of steelJaideep Adusumelli
Performed numerous stress-strain elasticity tests along with impact test under controlled temperature and stress factors.
then the corrosion properties were studied based on the microstructures and corrosion current graphs.
This lecture provides an introduction to the metallurgy of precipitation hardening, with a presentation of the fundamental mechanisms involved and illustrations from alloys which form the basis for engineering alloys. The Al-Mg<sub>2</sub>Si system is discussed in some detail because of its commercial importance. The microstructural aspects of precipitation hardening are illustrated by examples, many of which were obtained by electron microscopy; an outline of the background to electron microscopy is given in an appendix. Familiarity with the subject matter covered in earlier lectures 1201, 1202 and 1203 is assumed.
Direct alloying of steel a review of studies at lab and industrial scaleJorge Madias
The direct alloying of the steel is attractive as it minimizes alloying cost, total energy consumption and CO2 emissions, compared with ferroalloys. This allying technique is in use for high alloyed (stainless), low alloyed and carbon steel. The elements reviewed include chromium, nickel, molybdenum, vanadium and manganese. Raw materials used to this purpose are lump ores, ore fines, special slags, self-reducing briquettes and others. For the development of this technique, tools like thermodynamic modelling, testing in induction furnaces of several scales and industrial tests have been instrumental. This paper summarizes the fundamental and industrial efforts carried out to develop and employ direct alloying in Japan, Russia, China and other steelmaking countries
FellowBuddy.com is an innovative platform that brings students together to share notes, exam papers, study guides, project reports and presentation for upcoming exams.
We connect Students who have an understanding of course material with Students who need help.
Benefits:-
# Students can catch up on notes they missed because of an absence.
# Underachievers can find peer developed notes that break down lecture and study material in a way that they can understand
# Students can earn better grades, save time and study effectively
Our Vision & Mission – Simplifying Students Life
Our Belief – “The great breakthrough in your life comes when you realize it, that you can learn anything you need to learn; to accomplish any goal that you have set for yourself. This means there are no limits on what you can be, have or do.”
Like Us - https://www.facebook.com/FellowBuddycom
Ferrosilicon productiion and submerged arc furnace (1)Nasser Harby
Ferroalloys, by definition, are alloys of two or more metals, of which one is Iron. The U.S. Bureau of Mines defines ferroalloy as an alloy of iron with at least one other element except for carbon.
The main indicator of the quality of a ferroalloy is its chemical composition and, above all, the content of the leading element. It is important to have Consistency in alloying element amounts in ferroalloys from heat to heat, allowing the manufacture of standard products
The smelting of ferroalloys is commonly performed in electric arc furnaces.
Although ferromanganese can be produced in a blast furnace in a manner similar to iron, the reduction of chromium and silicon from their oxides requires higher Process temperatures and lower oxygen potentials than can be achieved in a blast furnace
Raw materials are perhaps the most important factor for obtaining good furnace operation the first step towards improvements is to reduce the variations
The aim of this course is to present the basic principles for the production of ferrosilicon alloys processes, and a simple preview for submerged arc furnaces.
It is attended for Engineers working in this field, and students or metallurgists maybe find answers for their questions, because at the end of this course you will figure out that you have a preview for this manufacture and the main problems and solutions for the ferrosilicon production process. And having an overview for submerged arc furnaces design and operations.
.
Effect Of CaO, FeO, MgO, SiO2 and Al2O3 Content of Slag on Dephosphorization ...karun19
Phosphorus has atomic number 15 and it can give up all 5 electrons from its outermost shell to become P5+ or accept 3 electrons to become P3- to attain stable configuration.
This means that phosphorus can be removed both under oxidizing as well as reducing conditions.
But removal of phosphorus under reducing conditions is not practical since its removal is highly hazardous.
Thus P removal is practised mostly under oxidizing conditions(i.e. in Basic Oxygen Furnace).
Effects of thermo mechanical simulation on the corrosion of steelJaideep Adusumelli
Performed numerous stress-strain elasticity tests along with impact test under controlled temperature and stress factors.
then the corrosion properties were studied based on the microstructures and corrosion current graphs.
This lecture provides an introduction to the metallurgy of precipitation hardening, with a presentation of the fundamental mechanisms involved and illustrations from alloys which form the basis for engineering alloys. The Al-Mg<sub>2</sub>Si system is discussed in some detail because of its commercial importance. The microstructural aspects of precipitation hardening are illustrated by examples, many of which were obtained by electron microscopy; an outline of the background to electron microscopy is given in an appendix. Familiarity with the subject matter covered in earlier lectures 1201, 1202 and 1203 is assumed.
Direct alloying of steel a review of studies at lab and industrial scaleJorge Madias
The direct alloying of the steel is attractive as it minimizes alloying cost, total energy consumption and CO2 emissions, compared with ferroalloys. This allying technique is in use for high alloyed (stainless), low alloyed and carbon steel. The elements reviewed include chromium, nickel, molybdenum, vanadium and manganese. Raw materials used to this purpose are lump ores, ore fines, special slags, self-reducing briquettes and others. For the development of this technique, tools like thermodynamic modelling, testing in induction furnaces of several scales and industrial tests have been instrumental. This paper summarizes the fundamental and industrial efforts carried out to develop and employ direct alloying in Japan, Russia, China and other steelmaking countries
FellowBuddy.com is an innovative platform that brings students together to share notes, exam papers, study guides, project reports and presentation for upcoming exams.
We connect Students who have an understanding of course material with Students who need help.
Benefits:-
# Students can catch up on notes they missed because of an absence.
# Underachievers can find peer developed notes that break down lecture and study material in a way that they can understand
# Students can earn better grades, save time and study effectively
Our Vision & Mission – Simplifying Students Life
Our Belief – “The great breakthrough in your life comes when you realize it, that you can learn anything you need to learn; to accomplish any goal that you have set for yourself. This means there are no limits on what you can be, have or do.”
Like Us - https://www.facebook.com/FellowBuddycom
Along with being a lifelong connoisseur of RAS, I also have the pleasure of being wrapped in a layer of skin that does not respond favorably to the sun. That’s a more eloquent way of saying that I’m a lily-assed white guy.
Somo - Creating compelling Mobile Strategies (US content specific) Ross Sleight
Presentation on developing mobile strategies presented at Mobile Squared event in NYC December 2011
US Content specific (stats)
Presented by Ross Sleight, Chief Strategy Officer, Somo.
Somo are a global full service mobile marketing agency. To find out more please visit http://www.somoagency.com
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
This briefing note focuses on the pyro-metallurgical recycling of copper squirrel cage rotors used in electrical motors (Copper Rotor Motors or CRM). Like conventional electrical motors, after adequate sorting of the different metals, they can be easily recycled with existing technologies. This can achieve an almost 100% recovery of copper in a highly purified state and the formation of a valuable iron-silicon slag suitable for a variety of applications after granulation, including materials suitable for infrastructure construction. The same technology holds also for other copper/steel and copper/stainless steel composites. Indeed, in the latter, a large fraction of the nickel contained in the steel is recoverable separately.
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
IJERA (International journal of Engineering Research and Applications) is International online, ... peer reviewed journal. For more detail or submit your article, please visit www.ijera.com
Steel industry can be characterized by a significant amount of by-products
including fine dust (up to 1.5% of heat size). Dust of gas cleaners, containing above
0.5% Zn and 50% Fe, cannot be directly returned to basic melting facilities due to high
contents of zinc that destroys its lining. High consumption of reducing agent, furnace
lining corrosion, final product of high impurities content made difficult use of
hydrometallurgical processing. Use of hydrometallurgy technologies is held back by
zinc in dust, primarily, as ferrites that cannot be opened using alkali, while acids make
iron transfer into solution. As a result, major part of smelters stockpiles the dust.
Secondary deposits of zinc-containing steelmaking dust can be involved into processing
thus expand the feedstock of zinc industry, increase efficiency of steel making and
reduce negative impact on environment.
The paper contains chemical and mineralogical analysis of steel dust sample from
PAO Severstal and study results on hydrometallurgical extraction of zinc from dust
using salt solution. It has been established that ammonium chloride leaching of zinc
The Effect of Bed Thickness and Cooling Time on the Rate of Copper Slag Cooli...CrimsonPublishersAMMS
The Effect of Bed Thickness and Cooling Time
on the Rate of Copper Slag Cooling, Case Study:Khatoonabad Copper Smelter Plant by Esmaeil Rahimi and Neda Mohaghegh in Aspects in Mining & Mineral Science
International Refereed Journal of Engineering and Science (IRJES)irjes
International Refereed Journal of Engineering and Science (IRJES)
Ad hoc & sensor networks, Adaptive applications, Aeronautical Engineering, Aerospace Engineering
Agricultural Engineering, AI and Image Recognition, Allied engineering materials, Applied mechanics,
Architecture & Planning, Artificial intelligence, Audio Engineering, Automation and Mobile Robots
Automotive Engineering….
Study on hardening mechanisms in aluminium alloysIJERA Editor
The Al-Zn-Mg alloys are most commonly used age-hardenable aluminium alloys. The hardening mechanism is
further enhanced in addition of Sc. Sc additions to aluminium alloys are more promising. Due to the
heterogeneous distribution of nano-sized Al3Sc precipitates hardening effect can be accelerated. Mainly,
highlight on hardening mechanism in Al-Zn-Mg alloys with Sc effect is to study. In addition, several
characterisations have been done to age-hardening measurements at elevated temperatures from 120oC to 180
oC. The ageing kinetics has also been calculated from Arrhenius equation. Furthermore, friction stir processing
(FSP) can be introduced to surface modification process and hardened the cast aluminium alloys. In this study,
hardening mechanism can be evaluated by Vicker’s hardness measurement and mechanical testing is present
task.
Study on hardening mechanisms in aluminium alloysIJERA Editor
The Al-Zn-Mg alloys are most commonly used age-hardenable aluminium alloys. The hardening mechanism is
further enhanced in addition of Sc. Sc additions to aluminium alloys are more promising. Due to the
heterogeneous distribution of nano-sized Al3Sc precipitates hardening effect can be accelerated. Mainly,
highlight on hardening mechanism in Al-Zn-Mg alloys with Sc effect is to study. In addition, several
characterisations have been done to age-hardening measurements at elevated temperatures from 120oC to 180
oC. The ageing kinetics has also been calculated from Arrhenius equation. Furthermore, friction stir processing
(FSP) can be introduced to surface modification process and hardened the cast aluminium alloys. In this study,
hardening mechanism can be evaluated by Vicker’s hardness measurement and mechanical testing is present
task.
Plasma Technique for Quickest IronmakingZohaib Akbar
The production of Liquid Iron by Orbitting plasma technique in a few micro seconds using fine ore such as Taconite(Fe3O4) Concentrates coupled with other technological advancement is a significant breakthrough for quality and cost-effective production of Ironmaking.
RAUTOMEAD TECHNOLOGY FOR CONTINUOUS CASTING OF OXYGEN-FREE COPPER, COPPER-MA...Rautomead Limited
Rautomead Chairman, Sir Michael Nairn, presented a paper at the ICDC seminar in Mumbai on 30 November 2014. Sir Michael talked about “Rautomead Technology for Continuous Casting of Oxygen Free Copper, Copper Magnesium & Other Copper Conductor Alloys” and reflected on the development and evolution of Rautomead continuous casting technology during its 35 year history.
RAUTOMEAD TECHNOLOGY FOR CONTINUOUS CASTING OF OXYGEN-FREE COPPER, COPPER-MA...
185-Chikashi
1. Southern African Pyrometallurgy 2011, Edited by R.T. Jones & P. den Hoed,
Southern African Institute of Mining and Metallurgy, Johannesburg, 6–9 March 2011
185
Influence of slag composition on reduction
control and operations of the slag-cleaning
furnace at KCM, Zambia
H.M. Chikashi
Konkola Copper Mines plc, Chingola, Zambia
Keywords: Pyrometallurgy, furnace, bath agitation, regression analysis, entrainment
Abstract – This paper presents the results of linear regression analysis of the
influence that each component of slag has on the losses of copper in slag-cleaning-
furnace slag. Data used for the analysis are actual plant data collected over the
past two years of operation. Facts obtained from the study will be helpful for
smelter management to control these components in the flash smelting furnace
feed and slag, to levels which will enable better control of copper in slag, and
smoother operation of the KCM slag-cleaning furnace.
INTRODUCTION
Konkola Copper Mines plc of the Vedanta group (KCM) operates a 112 t/h
Outotec direct-to-blister copper smelter at its Chingola operations in Zambia.
Sulphide copper concentrates are oxidized by a concentrate burner at 75% air
enrichment to produce blister containing up to 99.4% copper, which is tapped
to anode furnaces for fire refining. The environment in the flash smelting
furnace (FSF) is highly oxidizing; recovery of sulphur to the gas phase is high,
but the slag contains high amounts of copper, both as dissolved oxide and
mechanically entrained metallic prills (18 to 21%). The gases are channelled to
the boiler and ESP for energy- and dust-recovery before final cleaning in the
gas-cleaning plant for sulphuric acid preparation. Slag is cleaned in two stages,
by carbothermic reduction, in the electric slag-cleaning furnaces (ESCF). In the
first electric furnace (20 MVA), called the SCF (slag-cleaning furnace), copper
oxide is reduced to produce blister copper (98.25% Cu) and slag containing 3 to
5% Cu, 0.78% Co. The slag from the first furnace is transferred to the second
electric furnace, called the CRF (cobalt-recovery furnace). The CRF (15 MVA)
offers a more reducing environment for the recovery of Cu and Co, together
with Fe, forming a product known as cobalt alloy, and a slag containing as low
as 0.45% Cu and 0.32% Co. Because of the high Fe content, the alloy has a high
melting point; to lower the liquidus temperature, sulphur is introduced to the
alloy by injection of FSF feed mixture to the bath1. The two-stage process of
slag cleaning employed at KCM, where copper oxide is first partially reduced in
one electric furnace and more comprehensively in a second furnace, results in
very high recovery of both copper and cobalt2.
2. 186
SLAG-CLEANING OPERATIONS AT NCHANGA SMELTER
Slag is tapped every 4 hours from the FSF to the SCF via water-cooled copper
launders at 1290ºC. A typical slag analysis from the FSF is shown in Table I.
The objective of the SCF operation is to reduce copper in the FSF slag to 3–5%
by the addition of an appropriate amount of metallurgical coke, to ensure
minimal precipitation of iron and cobalt to the blister phase. Slag temperature
is maintained around 1350ºC, while blister temperature is kept above 1200ºC.
Table I: Typical analysis of Flash Smelting Furnace (FSF) slag, mass %
Cu Fe SiO2 CaO MgO Co S Al2O3 Fe3O4
19.46 22.52 25.69 5.89 2.46 0.64 0.29 3.94 20.79
Control of copper in the SCF slag within the 3 to 5% range has been a challenge,
due to changes in size and quality of metallurgical coke, and slag chemistry.
Table II shows the average composition of SCF slag from March 2009 to
December 2010.
Table I: Typical analysis of Slag Cleaning Furnace (SCF) slag, mass %
Cu Fe SiO2 CaO MgO Co S Al2O3 Fe3O4
5.48 27.03 30.93 8.09 3.242 0.76 0.38 6.39 14.02
Control of copper transferred to the CRF at between 3 to 5% has been very
important in recent months, as the LME copper price is estimated to reach
US $12 000 per ton in 2011. The idea is to send minimum copper to the alloy
phase in the CRF, because payables on copper in alloy are lower than in the
anodes that go to the refinery for copper cathode production.
Sampling of slag for chemical analysis
Three samples are collected from the SCF slag launders during transferring of
slag to the CRF, to make a composite sample for chemical analysis. Tapping
times depend on the number of tap-holes opened, the level of slag in the
furnace, and its viscosity. The samples are allowed to cool in air, and are then
sent to the laboratory for chemical analysis using an X-ray fluorescence (XRF)
method for components other than magnetite, which is determined by the
magnetic saturation method in the Satmagan analyser.
Control of copper in SCF slag
Metallurgical coke for reduction reactions in the SCF is charged from the roof of
the furnace to the surface of the slag. The amount of coke to charge to a slag
batch is calculated using a coke-addition model, which takes into account the
percentage of copper in the slag, the degree of copper reduction required, and
the amount of slag received. Figure 1 shows the degree of control of SCF
operations with respect to copper in slag.
3. 187
Figure 1: Control of copper in SCF slag within the desired range
Best control achieved was in April 2010, with 53.4% of the values being within
the desired range of 3–5%. September 2010 was the worst month, because
80.5% of the values were above the upper control limit.
EFFECT OF SLAG COMPOSITION ON CONTROL OF COPPER
IN SCF SLAG
Many investigations have shown that the composition of a particular slag
system has the major influence on control of copper losses to the slag3,5,8,9,10,11.
This is due to the effect that chemical composition has on the liquidus
temperature of the slag and its fluidity7. This paper uses simple linear
regression analysis to determine the impact that the major components (Fe3O4,
SiO2, Al2O3, MgO, and CaO) of the slag have on losses of copper to slag,
because it is the appropriate method for this kind of analysis2. Losses of copper
in the slag may be in the form of dissolved oxides or mechanically entrained
metal prills4. The data used in this investigation are actual plant data collected
over a period of two years. The temperature of SCF slag has varied from 1320
to 1400ºC over the period analysed in this paper.
Change in composition of FSF slag (KCM)
Due to changes in supply, mineralogy, and chemical composition of individual
concentrates, it has been very difficult to make FSF slag that has a composition
close to design values. SCF operations have likewise changed with the change
in FSF slag, and operational challenges have been different for each of these
changes. For example, Figure 1 shows that in the first six months of the period
under consideration, there were a significant number of ‘copper in SCF slag’
values below the low limit of 3%, and there were almost none in the last 10
months of 2010. This is due to the fact that, in the last part of the period
considered here, slag was more difficult to reduce because, as Figure 2 shows,
4. 188
the important components of slag which determine its ease to be reduced have
changed significantly.
Figure 2: Change in FSF slag composition over a period of two years
Carbothermic reduction chemistry, and mechanisms of copper losses in slag
When coke is charged to the surface of slag in the furnace, there is very rapid
direct reduction of copper oxide and magnetite by metallurgical coke8.
(Fe3O4) + C = (3FeO) + CO (g) [1]
(Cu2O) + C = 2Cu (l) + CO (g) [2]
Carbon monoxide from the above reactions forms a gas film between the coke
and the slag. From this point, oxides in the molten slag are reduced by carbon
monoxide, and the Boudouard reaction (Equation [3]) becomes the reaction-
rate-controlling factor8.
C + CO2 = 2 CO (g) [3]
Equations 1 and 2 take place at the same time; one cannot take place without
the other13. A dispersion of very fine copper droplets formed, from Equation 2,
coalesce to form bigger particles, which then settle to the bottom of the
furnace11. Mass transfer amongst fine copper droplets is therefore very
important for nucleation to take place12. In the slag-cleaning furnace, mixing of
small particles is intensified by the stirring action caused by the inflow of slag
during FSF-slag tapping. The biggest droplets of metallic copper are formed
during this time13. After FSF-slag tapping, there is less turbulence in the SCF;
5. 189
therefore reactions and droplet formation are slow13. Movement of slag in this
period is mainly by electromagnetic forces (magneto-hydrodynamics),
enhanced by high electrode-current-densities and temperatures12,13.
Copper losses in slag can be divided between electrochemical losses (chemical
and physical) and mechanical losses (unsettled droplets) whose percentages
depend on the degree of oxidation or reduction, temperature, and composition
of the slag (which affects its viscosity)11. The effect of slag viscosity on the loss
of copper by entrainment (mechanical) is shown by the effect it has on the
settling rate of a metal droplet, as given by Stokes law (Equation 4)11.
[4]
where u = settling rate, m s-1
g = acceleration due to gravity, m s-2
d = diameter of copper droplet, m
ρCu, ρslag = density of copper and slag respectively, kg m-3
ηslag = viscosity of slag, Pa s
Equation 4 shows that the settling of copper droplets is very much dependent
on the viscosity of the slag. Slag viscosity plays a vital role in the formation of
copper droplets big enough to settle at the desired rates. The lower the
viscosity, the better the coalescence of fine blister particles to form bigger
particles, and, according to Equation 4, the faster the settling12.
Other mechanisms may be responsible for suspending copper particles in the
slag11. Gases formed during reactions may also transfer some metal droplets to
the slag zone11. In the SCF, bath agitation keeps copper droplets in suspension
in the slag, and, if this happens a few minutes before skimming, copper
mechanical losses to the SCF slag will be high.
The effects of Fe3O4 content in SCF slag on control of copper in SCF slag
Magnetite (Fe3O4) is formed in the flash smelting furnace by oxidation of iron in
the concentrates. Both the extent of oxidation and the amount of iron in the
concentrate has an influence on the amount of Fe3O4 in the FSF slag. It has been
found that losses of valuable metals (Cu, Co, and Ni) to slag increase with
increasing magnetite in the slag5. Figure 3 shows a strong dependency of
copper on the amount of Fe3O4 in SCF slag. Increasing the amount of Fe3O4 in
SCF slag will result in precipitation of Fe3O4 crystals, therefore increasing the
viscosity of the slag and the entrainment (mechanical losses) of molten copper
droplets in the slag3. As demonstrated by Stokes law above, this will result in
slow settling of molten copper droplets.
Over-heating of the slag decreases its viscosity, and accelerates reduction of
Fe3O4, and this liberates suspended copper droplets9,11. Operation of the SCF
has recently shown that, at high Fe3O4 levels in FSF slag, good control of Cu in
6. 190
SCF slag has been achieved, when the SCF slag temperature was kept above
1380ºC during FSF-slag tapping.
It is, therefore, important that Fe3O4 in FSF slag is controlled at levels that can
be reduced in the SCF within the design cycle time and plant feed rate to give
copper in SCF slag within the required range. For example, the data used in
this study show that, if Fe3O4 in FSF slag is kept below 18%, it is possible for the
SCF to reduce Fe3O4 to 10% within the design cycle time to produce slag with
4% Cu.
Figure 3: Influence of Fe3O4 on control of Cu in SCF slag
The effects of Fe3O4 in FSF slag on slag-cleaning operations
Apart from the above influence of Fe3O4 on SCF degree of reduction control,
Fe3O4 causes other operational issues. Firstly, precipitation of Fe3O4 at high
levels leads to formation of an intermediate layer (50 to 200 mm) between the
blister copper and slag phase during reduction. The intermediate phase
insulates the transfer of energy and Cu droplets to the blister phase.
Temperatures of blister copper in the SCF under such conditions drop below
1130ºC, making transfer of blister to the anode furnaces difficult, because of
poor flow, and the metal cools easily. Removal of solidified copper from blister
launders, and the repair of blister launders, also becomes frequent at low blister
tapping temperatures. This also increases the amount of scrap copper
generation that has to be re-melted in the anode furnaces.
To increase the transfer of energy from the slag phase to the blister, air agitation
of the bath is employed, using steel pipes to disturb the intermediate phase.
Use of agitation pipes is an extra cost, and the operation itself requires
additional manpower. An increase in the Fe3O4 content of the slag also results
7. 191
in increased metallurgical coke consumption, because Fe3O4 is also reduced by
copper during slag cleaning6.
Figure 4: Intermediate phase formation and entrainment of copper droplets
The pictures in Figure 4 were taken from the SCF furnace during the high Fe3O4
conditions. When the intermediate phase is too dense, the product elemental
copper will form a layer on top of this phase, and sometimes blister copper will
run out of the slag launders during skimming. This is not desirable, because
slag launders are made out of copper, and so blister copper will naturally stick
in the launders, and it is very difficult to remove, and may damage the
launders.
The influence of silica on control of copper in SCF slag
Silica content in the slag has an impact on the viscosity of slag10. An increase in
silica, as Figure 5 shows, increases the amount of copper in the SCF slag,
because of silica saturation at Fe/SiO2 ratios less than 1, which results in high
slag viscosity6. Because of the glassy nature of the high-silica slag, its porosity
to gases decreases, which adversely affects the reduction reaction rates at the
slag/gas interface5.
A new phenomenon was observed in September 2010 in SCF operations, when
the bath was expanding during slag tapping from the FSF, from gas evolution
that is highest in this phase of the cycle. For this reason, SCF slag volumes, as
calculated from level measurements, were about 150 t more than the FSF slag
calculation, leading to excess consumption of coke. This phenomenon was also
verified with mass-balance calculations.
8. 192
Figure 5: Influence of SiO2 on control of Cu in SCF slag
SCF slag samples taken in September 2010 for mineralogical analysis also
indicated entrainment of both metallic copper droplets and Fe3O4 in the glassy
phase (as per lab report), as shown in Figure 6.
Figure 6: Grains of elemental copper (< 5 µm) with secondary magnetite in glass phase in SCF
slag
9. 193
The influence of alumina on control of copper in SCF slag
Alumina forms high-melting compounds with FeOx and SiO2, which are solid at
copper-smelting temperatures6. It has also been shown that an increase of
alumina in the calcium silicate slag enlarges the spinel (Fe3O4) saturation area
and this increases mechanical losses of copper as Figure 7 shows4.
Figure 7: Influence of Al2O3 on control of Cu in SCF slag
The influence of magnesia on control of copper in SCF slag
The MgO forms a thermally stable (solid) silicate called olivine (Mg2SiO4 –
Fe2SiO4) at concentrations greater than 3-4% in the KCM slag (FSF slag),
resulting in high-viscosity slags4,6, and its systems with FeOx or Fe2O3 are solid
at copper smelting temperatures6.
Figure 8 shows the influence MgO has on the amount of copper in SCF slag.
The coefficient of determination of 0.191 indicates that the influence of MgO on
copper in SCF slag is low at average concentrations seen in the period studied.
10. 194
Figure 8: Influence of MgO on control of Cu in SCF slag
Effect of lime on control of copper in SCF slag
Lime (CaO) is used as a flux in the flash smelting furnace to prevent the
formation of solid substances such as magnetite (Fe3O4) and olivine (Mg2SiO4 –
Fe2SiO4), and to flux the solid silica6. It has an influence on the viscosity of the
slag; the more the CaO, to a certain extent, the less the viscosity, and the easier
it becomes for copper droplets to settle. Variation of CaO in the SCF slag has,
however, had little impact on the control of copper levels in slag, as shown in
Figure 8.
Figure 9: Influence of CaO on Cu in SCF slag
11. 195
Linear regression analysis of the data collected for this study shows something
that is contrary to the common belief that CaO decreases losses of copper to
slag. It should be pointed out here that data given by ternary diagrams should
not be generalized, because it usually applies to a given set of conditions4. The
coefficient of determination for the CaO/Cu relationship is low, but shows that
an increase in CaO content of the SCF slag has slightly increased the content of
copper in SCF slag. The plant (SCF) experienced difficulties raising
temperatures when the lime suddenly increased in the FSF slag. CaO is
refractory, and, if present in more than required quantities, will increase the
liquidus temperatures of the slag and reverse the effect it has on copper losses
in slag.
Application of the R² for the Fe3O4 and Cu in the SCF slag relationship
The relationship between Fe3O4 and Cu in slag has come out very important for
every metallurgist working in the SCF because it has the highest coefficient of
determination (R2 = 0.605) of all components of slag considered in this study.
Magnetite, therefore, has the highest influence on copper in the slag that is
tapped to the cobalt recovery furnace (CRF). The significance here is not really
the value of R2 for the Fe3O4 – Cu relationship calculated in this study.
However, it is in the fact that in months where Fe3O4 had the major influence on
copper in SCF slag, values of R2 were very close to 0.6. The author concludes
that when Fe3O4 is the major controlling component of copper in SCF slag, R2
for the Fe3O4 – Cu relationship will be close to 0.6. This is valid for SCF (KCM)
operations only.
Figure 10 demonstrates how the R2 can be used to analyse the SCF slag-cleaning
operation. An important observation made from the data was that for months
which had other components of slag increase their influence on copper in SCF
slag the coefficient of determination R2 for the Fe3O4 – Cu relationship was less
than 0.6; for example, September 2010. In this month, the effect of SiO2 on
copper in SCF slag was amplified by the increased concentration of silica in the
slag, and the effect was weakening the strength of the correlation between
Fe3O4 and Cu in slag. For this reason, the September 2010 slag was tough to
clean, because both SiO2 and Fe3O4 had an influence on copper losses. Slag
with a coefficient of determination R2 above 0.6 tended to be easily reduced,
and cases of over-reduction were higher than for slags with a coefficient of
determination R2 value less than 0.6.
12. 196
Figure 10: Comparison of factors affecting Cu in SCF by comparing Fe3O4 – Cu R2 for slags
Therefore, if slag has an R2 value for the Fe3O4 – Cu relationship close to 0.6 (e.g.
the April 2010 slag), copper in the SCF slag will be effectively kept between 3
and 5%, if Fe3O4 in the slag is controlled between 8 and 10% under equilibrium
conditions, i.e. not adding too much coke to the slag resulting in rapid reduction
of Fe3O4 which increases Fe to the blister. This is only achievable if Fe3O4 in the
FSF slag is below 18%. The control of Fe3O4 formation in the FSF is outside of
the scope of this study.
Table III: Comparison of SCF slag composition between April 2010 and September 2010
Cu
%
Fe
%
SiO2
%
CaO
%
MgO
%
Co
%
S
%
Al2O3
%
Fe3O4
%
Fe/SiO2
Apr-10 4.84 31.34 28.58 9.11 3.11 0.79 0.13 6.10 13.01 1.10
Sep-10 5.95 24.31 34.52 7.49 2.93 0.68 0.08 7.71 14.61 0.70
To summarise the use and significance of the R2 for the Fe3O4 – Cu relationship
for SCF operation, the following will be important to a metallurgist’s analysis or
control of the slag-cleaning process in the SCF:
1. R2 (Fe3O4 vs Cu) > 0.6: slag has low viscosity and easier to clean but
over-reduction becomes easily possible.
2. R2 (Fe3O4 vs Cu) = 0.6: Control of Fe3O4 in the SCF slag becomes the
limiting factor for controlling Cu in SCF slag.
3. R2 (Fe3O4 vs Cu) < 0.6: indicates influence of other components of slag,
such as SiO2, increases Cu losses to the slag in SCF.
13. 197
CONCLUSIONS
With a coefficient of determination of 0.605, Fe3O4 has the highest influence on
copper content in SCF slag. Therefore, success in achieving the objective of SCF
operation, in keeping copper in slag within the 3 to 5% range, will be realised if
Fe3O4 in both the FSF and SCF slag is kept within the limits recommended in
this paper. Reduced Fe3O4 in FSF slag will also result in improved control of
SCF blister temperatures and less metallurgical coke consumption. Magnetite
will be the determining factor of what should be the degree of reduction to get
the required copper in SCF slag, as is the practice in most smelters7. The trends
show that SiO2 is second in influencing the control of Cu in SCF slag. The
smelter should therefore control the amount of SiO2 in the feed mixture, so that
it is around 23.7% in slag. Amplified influence of SiO2 and other slag
components in the control of Cu in the SCF will be indicated by coefficients of
determination for the Fe3O4 – Cu relationship below 0.6. FSF slag containing
higher Fe3O4 than desired by SCF should be cleaned at higher than normal
temperature, to liberate the entrained metal prills. It is very important to
remember that this should be done during FSF slag tapping when the bath is
turbulent. This will favour the formation of large Cu prills that will settle very
fast, thereby minimizing copper entrainment in slag.
REFERENCES
1. R.T. Jones, D.A. Hayman, and G.M. Denton, Recovery of Cobalt, Nickel, and Copper from
slags, using DC-arc furnace technology, International Symposium on Challenges of Process
Intensification, 35th Annual Conference of Metallurgists, Montreal, Canada, 24–29 August
1996, pp.451-466.
2. J. Czernecki, Z. Smieszek, and Z. Miczkowski, A proposal for a two-stage process from
flash furnace for increase in efficiency of HM Glogow 2, Institute of non-ferrous metals,
Gliwice, Poland, 2009.
3. Z. Zivkovic, N. Mitevska, I. Mihajlovic, and D. Nikolic, The influence of the silicate slag
composition on copper losses during smelting of the sulphide concentrates, Journal of
Mining and metallurgy, 45 (1) B (2009), pp.23–24.
4. F. Kongoli, I. McBow, and A. Yazawa, Phase relations of ferrous calcium silicate slag and
its possible application in the industrial practice, Sohn International Symposium,
Advanced processing of metals and materials, Volume 8 – International symposium on
sulphide smelting , 2006.
5. E. P. El-Rassi and T.A. Utigard, Rate of slag reduction in a laboratory electric furnace –
Alternating vs Direct current, Metallurgical and materials transactions B, Volume 31 B, 2000.
6. P. Taskinen, KCM Slag training course handouts, Helsinki University of Technology, 2009.
7. Z. Jancikova and P. Svec, Prediction of chemical composition of refining slag with
exploitation of artificial neural networks, Department of automation and computer science
in metallurgy, Technical University of Ostrava, Czech Republic, 2006.
8. A. Moreno, G. Sanchez, A. Warczok, and G. Riveros, Development of Slag Cleaning
Process and Operation of electric furnaces in Las Vantanas smelter, COPPER 99-COBRE 99
international conference, 1999.
9. R. Degel, H. Oterdoom, J. Kunze, A. Warczok, and G. Riveros, Latest results of slag
cleaning reactor for copper recovery and its potential for the PGM industry, SMS Demag
AG, Universidad de Chile, Third international platinum conference, ‘Platinum in
transformation’, The Southern African Institute of Mining and Metallurgy, 2008.
10. R.R. Moskalyk and A.M. Alfantazi, Review of pyrometallurgical practice: today and
tomorrow, Minerals Engineering, 16 (2003), pp.893–919.
11. W.G. Davenport, M. King, A.K. Biswas, and M. Schlesinger, Extractive Metallurgy of
Copper, Fourth edition, Pergamon, 2002.
14. 198
12. R.H. Eric, Slag properties and design issues pertinent to matte smelting electric furnaces,
Journal of the South African Institute of Mining and Metallurgy, 2004.
13. J. Tuominen, Y. Anjala, and P. Bjorklund, Slag cleaning of Outokumpu direct-to-blister
smelting slag, Outokumpu Technology Oy, 2007.
Humphrey Chikashi
Process Engineer, Konkola Copper Mines plc
2003: Trainee Materials Engineer – Engineering material testing
(destructive and non-destructive) and failure investigation,
Alfred H. Knight, Kitwe, Zambia.
2005: Evaluation and optimization of sulphide ions removal from cobalt
advance electrolyte in carbon columns – Cobalt Plant, Mopani Copper mines,
Kitwe, Zambia.
2006: Bachelor of Engineering in Metallurgical Engineering – Copperbelt
University, Zambia.
2007: Process Engineer – Nchanga Smelter, Konkola Copper Mines plc,
Chingola, Zambia.