Ringkasan dari dokumen tersebut adalah:
1. Dokumen tersebut membahas penggunaan Differencial Scanning Calorimetry (DSC) untuk mengkarakterisasi Shape Memory Alloy (SMA).
2. DSC digunakan untuk mengukur dan menganalisis puncak pembentukan dan penyerapan panas selama transformasi fasa SMA untuk mengetahui suhu transformasi seperti Ms, Mf, As, dan Af.
3. Beberapa penelitian yang diringkas menggun
Tugas presentasi kimia mengenai materi golongan alkali tanah untuk kelas 12 IPA semester 1. Menyebutkan berbagai unsur pada golongan alkali tanah berikut juga dengan sifat-sifat alkali tanah. Selain itu terdapat pula kegunaan/manfaat dan berbagai macam reaksi yang ditimbulkan dari alkali tanah/. Memahami karakteristik unsur-unsur, kegunaan dan eksistensinya di alam
Differential thermal analysis: Pengembangan Alat Differential Thermal Analys...Universitas Gadjah Mada
Differentiall Thermal Analysis merupakan teknik analisis termal dimana perubahan material diukur sebagai fungsi temperatur.
Bahan presentasi ini membahas mengenai pengembangan alat Differential Thermal Analysis untuk analisa termal material Ca(OH)2
presentasi ini menjelas tentang Perbedaan Prinsip XRD, XRF.
apa itu XRD dan XRF?
XRD (X-Ray Diffraction), salah satu teknik analisa untuk stuktur suatumineral, garam, logam, bahkan senyawaan organik seperti DNA, vitamin, dll
XRF (X-ray fluorescence spectrometry) merupakan teknik analisa non-destruktif yang digunakan untuk identifikasi serta penentuan konsentrasi elemen yang ada pada padatan, bubuk ataupun sample cair. XRF mampu mengukur elemen dari berilium (Be) hingga Uranium pada level trace element, bahkan dibawah level ppm. Secara umum, XRF spektrometer mengukur panjang gelombang komponen material secara individu dari emisi flourosensi yang dihasilkan sampel saat diradiasi dengan sinar-X
nb: disarankan membuka ppt dengan microsoft office 2016
Tugas presentasi kimia mengenai materi golongan alkali tanah untuk kelas 12 IPA semester 1. Menyebutkan berbagai unsur pada golongan alkali tanah berikut juga dengan sifat-sifat alkali tanah. Selain itu terdapat pula kegunaan/manfaat dan berbagai macam reaksi yang ditimbulkan dari alkali tanah/. Memahami karakteristik unsur-unsur, kegunaan dan eksistensinya di alam
Differential thermal analysis: Pengembangan Alat Differential Thermal Analys...Universitas Gadjah Mada
Differentiall Thermal Analysis merupakan teknik analisis termal dimana perubahan material diukur sebagai fungsi temperatur.
Bahan presentasi ini membahas mengenai pengembangan alat Differential Thermal Analysis untuk analisa termal material Ca(OH)2
presentasi ini menjelas tentang Perbedaan Prinsip XRD, XRF.
apa itu XRD dan XRF?
XRD (X-Ray Diffraction), salah satu teknik analisa untuk stuktur suatumineral, garam, logam, bahkan senyawaan organik seperti DNA, vitamin, dll
XRF (X-ray fluorescence spectrometry) merupakan teknik analisa non-destruktif yang digunakan untuk identifikasi serta penentuan konsentrasi elemen yang ada pada padatan, bubuk ataupun sample cair. XRF mampu mengukur elemen dari berilium (Be) hingga Uranium pada level trace element, bahkan dibawah level ppm. Secara umum, XRF spektrometer mengukur panjang gelombang komponen material secara individu dari emisi flourosensi yang dihasilkan sampel saat diradiasi dengan sinar-X
nb: disarankan membuka ppt dengan microsoft office 2016
Metode BET (Brunaur, Emmett and Teller) pertama kali ditemukan oleh Stephen Brunauer, Paul Hugh Emmett, and Edward Teller pada tahun 1938. Metode ini digunakan untuk permukaan yang datar (tidak ada lekukan) dan tidak ada batas dalam setiap layer yang dapat digunakan dalam menjelaskan luas permukaan. Metode ini digunakan berdasarkan asumsi bahwa pada setiap permukaan mempunyai tingkat energi yang homogen (energi adsorpsi tidak mengalami perubahan dengan adanya adsorpsi di layer yang sama) dan tidak ada interaksi selama molekul teradsorpsi
Differential Thermal Analysis adalah salah satu pengujian tak rusak (non-destructive test). Pengujian ini berguna untuk mengidentifikasi dan enganalisis secara kuantitatif komoposisi suatu zat dengan melihat perilakunya terhadap temperatur. Di dalam presentasi ini akan dibahas seputar dasar teori, faktor yang mempengaruhi perubahan suhu baiks ecara fisika maupun kimia, standar sampel, standar kalibrasi, instrumen, dan sistem DTA nya
Metode BET (Brunaur, Emmett and Teller) pertama kali ditemukan oleh Stephen Brunauer, Paul Hugh Emmett, and Edward Teller pada tahun 1938. Metode ini digunakan untuk permukaan yang datar (tidak ada lekukan) dan tidak ada batas dalam setiap layer yang dapat digunakan dalam menjelaskan luas permukaan. Metode ini digunakan berdasarkan asumsi bahwa pada setiap permukaan mempunyai tingkat energi yang homogen (energi adsorpsi tidak mengalami perubahan dengan adanya adsorpsi di layer yang sama) dan tidak ada interaksi selama molekul teradsorpsi
Differential Thermal Analysis adalah salah satu pengujian tak rusak (non-destructive test). Pengujian ini berguna untuk mengidentifikasi dan enganalisis secara kuantitatif komoposisi suatu zat dengan melihat perilakunya terhadap temperatur. Di dalam presentasi ini akan dibahas seputar dasar teori, faktor yang mempengaruhi perubahan suhu baiks ecara fisika maupun kimia, standar sampel, standar kalibrasi, instrumen, dan sistem DTA nya
In this study, impressed
current cathodic protection using MMO-Ti conductive concrete anode was conducted in the new reinforced bar
(rebar) concrete submerged in the seawater on the various protecting current. The aim of this study was to
investigate performance of protecting current to reduce aggressive environment in the interface of new rebar
cocncrete and also to evaluate new rebar concrete after application of protecting current. This technique was
conducted on the various protecting current of 100, 150 and 200 mA/m² by surface area of rebar. NACE SP0290
was used as standard criteria of cathodic protection. Examinations were arried to observe the influent of
to record corrosion potential, polarisation resistant, corrosion rate at initial and after application of protecting
current. Cyclic polarisation test was performed to know susceptibility of pitting corrosion on the rebar concrete.
The result showed that this technique have been successfully applied and have been meet standard criteria of
NACE SP02090. Their corrosion potential of rebar concrete obtaine lower as well
as corrosion rate compared to sample without protecting current (PPC 1) during 30 days submerged in the
seawater. Pitting corrosion not found in the all of samples.
Analisis kritis jurnal ini diperoleh dari hasil membaca dan membandingkan jurnal yang berjudul "The Philosophy of Existensialism: Individual Awareness in Indonesian Education" dan "Peranan Filsafat dan Bahasa sebagai Media Komunikasi"
Analisis kritis jurnal ini membahas peran filsafat pendidikan dalam pembentukan moralitas siswa, mengkaji hubungan antara bahasa dan filsafat dalam konteks filsafat bahasa, serta menyoroti pentingnya pendidikan karakter yang melibatkan peran aktif orang tua dan guru. Artikel ini juga menekankan kompleksitas bahasa sebagai sistem simbol yang memengaruhi persepsi kita tentang realitas, serta pentingnya analisis kritis terhadap bahasa dalam memahami konsep-konsep filosofis.
Analsis kritis jurnal ini diperoleh dari hasil membaca dan membandingkan jurnal yang berjudul Filsafat Pendidikan Dalam Pengembangan Sains
Berbasis Kearifan Lokal dan Manajemen kurikulum bahasa arab di madrasah: kajian problematika
Apakah program Sekolah Alkitab Liburan ada di gereja Anda? Perlukah diprogramkan? Jika sudah ada, apa-apa saja yang perlu dipertimbangkan lagi? Pak Igrea Siswanto dari organisasi Life Kids Indonesia membagikannya untuk kita semua.
Informasi lebih lanjut: 0821-3313-3315 (MLC)
#SABDAYLSA #SABDAEvent #ylsa #yayasanlembagasabda #SABDAAlkitab #Alkitab #SABDAMLC #ministrylearningcenter #digital #sekolahAlkitabliburan #gereja #SAL
2. 3 minutes 5 minutes
2
CONTENT
Introduction SMA Preparasi Sampel
Review Paper
5 minutes
1 minutes
Prinsip DSC
3. Shape Memory Alloy
Material yang mampu mengingat kembali bentuk awalnya setelah
diberikan deformasi dan dipanaskan diatas suhu transformasi
Shape Memory alloy
Transformasi
nondifusi
Transformasi dari
fasa induk
austenit ke fasa
martensit
Fenomena mengingat bentuk
SMA dikenal sebagai SME
Temperatur Transisi
Ms As
Mf Af
Needle likeV-type
4. Aplikasi SMA
Sampai saat ini, terdapat 20 paduan
SMA yang dikembangkan
Shape Memory Alloy memiliki aplikasi
yang sangat luas
Aktuator
Kesehatansensor
Aerospace
Ag-Cd
Au-Cd
Cu-Al-Ni
Cu-Al-Mn
Cu-Au-Zn
Cu-Sn
Cu-Au-Sn
Cu-Zn
Cu-Zn-Al
Cu-Zn-Sn
Zu-Zn-Ga
Cu-Zn-Si
In-Ti
Ni-Al
Ni-Ti
Cu-Al
Fe-Mn
Fe-Si
Dalam paduan bentuk-memori, struktur kristal berubah pada titik
transformasi disertai dengan pembentukan panas dan penyerapan.
Diperlukannya pemahamanan transfiormasi lebih dalam dengan
mengukur dan menganalisis puncak pembentukan dan
penyerapan panas menggunakan
Differencial Scanning Calorimetry (DSC)
5. Prinsip DSC
DSC merupakan salah satu instrumen analisis termal. Prinsip
kerja dari DSC adalah ketika sampel mengalami transformasi
fisik seperti transisi fase, perubahan panas diperlukan untuk
mengalir dari referensi dan sampel untuk mempertahankan
keduanya pada suhu yang sama. Panas yang dibutuhkan
kurang atau lebih yang harus mengalir ke sampel tergantung
pada apakah proses ini eksotermik atau endotermik dan akan
direpresentasikan melalui sebuah grafik.
6. Preparasi Sampel DSC
Preparasi sampel sebesar 3-5 mg (sampel
dipersiapkan sekecil dan setipis mungkin)
Sampel dipanaskan diatas titik transformasi
dibawah atmosfir Nitrogen dan didinginkan
pada suhu tertentu (eksotermik)
Setelah reaksi transformasi eksotermik selesai ,
sampel di dinginkan dan dipanaskan (endotermik)
Setelah reaksi transformasi eksotermik selesai ,
sampel di dinginkan dan dipanaskan (endotermik)
Suhu dimana sampel memulai reaksi eksotermik
selama pendinginan disebut suhu Ms (martensit start)
Suhu dimana sampel menyelesaikan reaksi enotermik
disebut Austenit Finish
7. Hasil Pengujian SMA dengan DSC
Effects of Composition and Thermal Treatment of Cu-Al-Zn Alloys with Low Content of Al on their Shape-memory Properties, Zorica
Zorica et al melakukan pengujian paduan
Cu-25Zn-4Al dan Cu-30Zn-4Al dan
diberikan perlakuan variasi metodde
quenching untuk pembentukan martensit
yang terjadi melalui transformasi non
difusi. Melalui pengujian menggunakan
DSC didapatkan suhu Ms, Mf, As dan Af
dari masing-masing sampel dan entalpi saat
transformasi terjadi. Pada pengujian ini
sampel berupa logam paduan
8. Hasil Pengujian SMA dengan DSC
On the influence of austenitization on the morphology of -phase in tempered Cu–Zn–Al shape memory alloys, Leandru
Leandru et al Selain untuk mempelajari
transformasi fasa guna mengetahui
suhu As, Af, Ms dan Mf , pada
penelitian ini Leandru memprediksi
adanya fassa Bainit yang muncul
melalui analisa DSC. Pada pengujian
ini sampel berupa logam paduan
9. Hasil Pengujian SMA dengan DSC
Marforming and martempering of a Cu–Zn–Al shape memory alloy, Spielfield
Spielfield et al Dengan menggunakan
DSC, Spielfield menganalisa padduan
shape memory alloy berbasis Cu-Zn-Al
untuk mengetahui setiap tahapan
trasnformasi fasa yang terjadi. Pada
pengujian ini sampel berupa logam
paduan