Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Precious metal alloys /orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Indian Dental Academy: will be one of the most relevant and exciting
training center with best faculty and flexible training programs
for dental professionals who wish to advance in their dental
practice,Offers certified courses in Dental
implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic
Dentistry, Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training
center with best faculty and flexible training programs for dental
professionals who wish to advance in their dental practice,Offers certified
courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry,
Prosthetic Dentistry, Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training
center with best faculty and flexible training programs for dental
professionals who wish to advance in their dental practice,Offers certified
courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry,
Prosthetic Dentistry, Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Precious metal alloys /orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Indian Dental Academy: will be one of the most relevant and exciting
training center with best faculty and flexible training programs
for dental professionals who wish to advance in their dental
practice,Offers certified courses in Dental
implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic
Dentistry, Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training
center with best faculty and flexible training programs for dental
professionals who wish to advance in their dental practice,Offers certified
courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry,
Prosthetic Dentistry, Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training
center with best faculty and flexible training programs for dental
professionals who wish to advance in their dental practice,Offers certified
courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry,
Prosthetic Dentistry, Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Description :
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Metals in dentistry /certified fixed orthodontic courses by Indian dental aca...Indian dental academy
Dental Courses by Indian Dental Academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Metals and alloys for prosthodontics/ dental crown & bridge coursesIndian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Metals in prosthodontics/dental crown &bridge course by Indian dental academyIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
metals and alloys for prosthodontics / academy of fixed orthodonticsIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
1.Introduction
2.Historical perspective
3.Classification
4.Desirable properties
5.Functional mechanical properties
6.Alloys for
A]. All Metal Prosthesis
B]. Resin – Veneered Metal Restoration
7. High noble and noble alloys for Metal- Ceramic Prosthesis
8. Alternative Technologies for fabricating prosthesis
Biological Hazards and precautions – risks of dental laboratory
technician
10. Guidelines for selection and use of base metals for crown and
bridge applications.
11. Partial denture alloys and guidelines for selection
12. Alternatives technologies for fabricating prosthesis
13. Recent advancements
Base Metal Casting Alloys in Dentistry by Dr Rashid HassanDr Rashid Hassan
A comprehensive lecture on Base Metal Casting Alloys in Dentistry By Dr Rashid Hassan. Covering all the aspects from the very basics to the clinical applications. For video lectures on Dental Materials by Dr Rashid like end follow dmbydrrashid on Facebook.
Dentalcasting alloys/certified fixed orthodontic courses by Indian dental aca...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Wholesale Silver Jewelry New York : Silver Alloys are in High Demandpandkjewelry
Nowadays, silver based alloys are being specially developed for improving upon tarnish resistance in case of multi-layer stacks. Generally, these alloys have 80-95% silver and employ platinum or gold group metals for stabilizing the properties of silver; especially when used in mildly acidic environments or exposed to moisture. It is easy to find lower cost alloys that showcase a favorable balance between performance and cost. More and more alloys are being experimented with, and they are more complex than standard binary / ternary alloys that are currently in use. These alloys can also be manufactured by using readily available equipment for production.
Metals in dentistry /certified fixed orthodontic courses by Indian dental aca...Indian dental academy
Dental Courses by Indian Dental Academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Metals and alloys for prosthodontics/ dental crown & bridge coursesIndian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Metals in prosthodontics/dental crown &bridge course by Indian dental academyIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
metals and alloys for prosthodontics / academy of fixed orthodonticsIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
1.Introduction
2.Historical perspective
3.Classification
4.Desirable properties
5.Functional mechanical properties
6.Alloys for
A]. All Metal Prosthesis
B]. Resin – Veneered Metal Restoration
7. High noble and noble alloys for Metal- Ceramic Prosthesis
8. Alternative Technologies for fabricating prosthesis
Biological Hazards and precautions – risks of dental laboratory
technician
10. Guidelines for selection and use of base metals for crown and
bridge applications.
11. Partial denture alloys and guidelines for selection
12. Alternatives technologies for fabricating prosthesis
13. Recent advancements
Base Metal Casting Alloys in Dentistry by Dr Rashid HassanDr Rashid Hassan
A comprehensive lecture on Base Metal Casting Alloys in Dentistry By Dr Rashid Hassan. Covering all the aspects from the very basics to the clinical applications. For video lectures on Dental Materials by Dr Rashid like end follow dmbydrrashid on Facebook.
Dentalcasting alloys/certified fixed orthodontic courses by Indian dental aca...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Wholesale Silver Jewelry New York : Silver Alloys are in High Demandpandkjewelry
Nowadays, silver based alloys are being specially developed for improving upon tarnish resistance in case of multi-layer stacks. Generally, these alloys have 80-95% silver and employ platinum or gold group metals for stabilizing the properties of silver; especially when used in mildly acidic environments or exposed to moisture. It is easy to find lower cost alloys that showcase a favorable balance between performance and cost. More and more alloys are being experimented with, and they are more complex than standard binary / ternary alloys that are currently in use. These alloys can also be manufactured by using readily available equipment for production.
PRESENTATION ON GOLD ALLOYS USED IN DENTISTRY. USEFUL FORALLBRANCHES OF DENTISTRY SPECIALLY PROSTHODONTICS AND CONSERVATIVE DENTISTRY. INCLUDES VARIOUS CATEGORIES OF ALLOYS AND THEIR ADVANTAGES, DISADVANTAGES, USES ETC.
Materials used in restorations/ orthodontic course by indian dental academyIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Base-Metal-Alloys used in dentistry..pptxKalpanaNunia1
Dentists should be aware of the corrosion properties and biocompatibility of any alloy they use.
In the absence of detailed data on corrosion for an alloy, use of high-noble and noble alloys of single-phase microstructure will minimize biologic risk.
Patients with Ni allergy may have sensitivity for cobalt. Such patients should be tested to rule out allergy before giving Co-Cr restoration.
Opportunity for Dentists (BDS/MDS )to relocate to United kingdom -Register as a DENTAL HYGIENIST/ DENTAL THERAPIST without Board exams and after approval you can register in GDC as a DH/DT and start working as a DH/DT Immediately and get paid.
You can complete the whole process in 3-4 months.Salary range for DH/DT is around 2500-3500 Pounds per month.
Eligibility / requirements-
1. An International English Language Testing System (IELTS) certificate
at the appropriate level.(Within 2 yrs of application date )
2: A recent primary dental qualification that has been taught and examined in English..(Within 2 yrs of application date )
3: A recent pass in a language test for registration with a regulatory authority in a country where the first language is English.
If you are interested Please contact us for more details.
1ST, 2ND AND 3RD ORDER BENDS IN STANDARD EDGEWISE APPLIANCE SYSTEM /Fixed ort...Indian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals
who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry,
Periodontics and General Dentistry.
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
I –Aligners are made with FDA approved transparent thermoplastic materials using 3D scanning, 3D Printing and finally Trays with Pressure vacuum formers.
Dear Doctor,
Indian Dental Academy Now offers comprehensive online Orthodontics course.
Course includes:
1.whiteboard lecture presentations
2.Case Discussions
3.with hundreds of pictures.
4.Demo on Models
5.Demo on Patients
6. subtitles in your own language
12 months unlimited access and support @350 USD only.
For Demo please visit :www.idalectures.com/preview/
For more details visit: www.idalectures.com
Please contact us for any clarifications:
idalectures@gmail.com
indiandentalacademy@gmail.com
Thanks & Regards
Indian Dental Academy
--
Indian Dental Academy
Leader in continuing dental education
www.indiandentalacademy.com
skype:indiandentalacademy
+919248678078
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Cytotoxicity of silicone materials used in maxillofacial prosthesis / dental ...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Diagnosis and treatment planning in completely endntulous arches/dental coursesIndian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Properties of Denture base materials /rotary endodontic coursesIndian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Use of modified tooth forms in complete denture occlusion / dental implant...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
2024.06.01 Introducing a competency framework for languag learning materials ...Sandy Millin
http://sandymillin.wordpress.com/iateflwebinar2024
Published classroom materials form the basis of syllabuses, drive teacher professional development, and have a potentially huge influence on learners, teachers and education systems. All teachers also create their own materials, whether a few sentences on a blackboard, a highly-structured fully-realised online course, or anything in between. Despite this, the knowledge and skills needed to create effective language learning materials are rarely part of teacher training, and are mostly learnt by trial and error.
Knowledge and skills frameworks, generally called competency frameworks, for ELT teachers, trainers and managers have existed for a few years now. However, until I created one for my MA dissertation, there wasn’t one drawing together what we need to know and do to be able to effectively produce language learning materials.
This webinar will introduce you to my framework, highlighting the key competencies I identified from my research. It will also show how anybody involved in language teaching (any language, not just English!), teacher training, managing schools or developing language learning materials can benefit from using the framework.
Ethnobotany and Ethnopharmacology:
Ethnobotany in herbal drug evaluation,
Impact of Ethnobotany in traditional medicine,
New development in herbals,
Bio-prospecting tools for drug discovery,
Role of Ethnopharmacology in drug evaluation,
Reverse Pharmacology.
The Roman Empire A Historical Colossus.pdfkaushalkr1407
The Roman Empire, a vast and enduring power, stands as one of history's most remarkable civilizations, leaving an indelible imprint on the world. It emerged from the Roman Republic, transitioning into an imperial powerhouse under the leadership of Augustus Caesar in 27 BCE. This transformation marked the beginning of an era defined by unprecedented territorial expansion, architectural marvels, and profound cultural influence.
The empire's roots lie in the city of Rome, founded, according to legend, by Romulus in 753 BCE. Over centuries, Rome evolved from a small settlement to a formidable republic, characterized by a complex political system with elected officials and checks on power. However, internal strife, class conflicts, and military ambitions paved the way for the end of the Republic. Julius Caesar’s dictatorship and subsequent assassination in 44 BCE created a power vacuum, leading to a civil war. Octavian, later Augustus, emerged victorious, heralding the Roman Empire’s birth.
Under Augustus, the empire experienced the Pax Romana, a 200-year period of relative peace and stability. Augustus reformed the military, established efficient administrative systems, and initiated grand construction projects. The empire's borders expanded, encompassing territories from Britain to Egypt and from Spain to the Euphrates. Roman legions, renowned for their discipline and engineering prowess, secured and maintained these vast territories, building roads, fortifications, and cities that facilitated control and integration.
The Roman Empire’s society was hierarchical, with a rigid class system. At the top were the patricians, wealthy elites who held significant political power. Below them were the plebeians, free citizens with limited political influence, and the vast numbers of slaves who formed the backbone of the economy. The family unit was central, governed by the paterfamilias, the male head who held absolute authority.
Culturally, the Romans were eclectic, absorbing and adapting elements from the civilizations they encountered, particularly the Greeks. Roman art, literature, and philosophy reflected this synthesis, creating a rich cultural tapestry. Latin, the Roman language, became the lingua franca of the Western world, influencing numerous modern languages.
Roman architecture and engineering achievements were monumental. They perfected the arch, vault, and dome, constructing enduring structures like the Colosseum, Pantheon, and aqueducts. These engineering marvels not only showcased Roman ingenuity but also served practical purposes, from public entertainment to water supply.
Palestine last event orientationfvgnh .pptxRaedMohamed3
An EFL lesson about the current events in Palestine. It is intended to be for intermediate students who wish to increase their listening skills through a short lesson in power point.
How to Split Bills in the Odoo 17 POS ModuleCeline George
Bills have a main role in point of sale procedure. It will help to track sales, handling payments and giving receipts to customers. Bill splitting also has an important role in POS. For example, If some friends come together for dinner and if they want to divide the bill then it is possible by POS bill splitting. This slide will show how to split bills in odoo 17 POS.
We all have good and bad thoughts from time to time and situation to situation. We are bombarded daily with spiraling thoughts(both negative and positive) creating all-consuming feel , making us difficult to manage with associated suffering. Good thoughts are like our Mob Signal (Positive thought) amidst noise(negative thought) in the atmosphere. Negative thoughts like noise outweigh positive thoughts. These thoughts often create unwanted confusion, trouble, stress and frustration in our mind as well as chaos in our physical world. Negative thoughts are also known as “distorted thinking”.
The Art Pastor's Guide to Sabbath | Steve ThomasonSteve Thomason
What is the purpose of the Sabbath Law in the Torah. It is interesting to compare how the context of the law shifts from Exodus to Deuteronomy. Who gets to rest, and why?
Read| The latest issue of The Challenger is here! We are thrilled to announce that our school paper has qualified for the NATIONAL SCHOOLS PRESS CONFERENCE (NSPC) 2024. Thank you for your unwavering support and trust. Dive into the stories that made us stand out!
The Indian economy is classified into different sectors to simplify the analysis and understanding of economic activities. For Class 10, it's essential to grasp the sectors of the Indian economy, understand their characteristics, and recognize their importance. This guide will provide detailed notes on the Sectors of the Indian Economy Class 10, using specific long-tail keywords to enhance comprehension.
For more information, visit-www.vavaclasses.com
Synthetic Fiber Construction in lab .pptxPavel ( NSTU)
Synthetic fiber production is a fascinating and complex field that blends chemistry, engineering, and environmental science. By understanding these aspects, students can gain a comprehensive view of synthetic fiber production, its impact on society and the environment, and the potential for future innovations. Synthetic fibers play a crucial role in modern society, impacting various aspects of daily life, industry, and the environment. ynthetic fibers are integral to modern life, offering a range of benefits from cost-effectiveness and versatility to innovative applications and performance characteristics. While they pose environmental challenges, ongoing research and development aim to create more sustainable and eco-friendly alternatives. Understanding the importance of synthetic fibers helps in appreciating their role in the economy, industry, and daily life, while also emphasizing the need for sustainable practices and innovation.
6. These are called noble metals as they do not form
oxides.
Gold and palladium do not oxidise at any
tempratures
www.indiandentalacademy.com
7. Rhodium has a very good resistance to oxidation
at all temps.
Osmium and ruthenium forms volatile oxides,
and palladium and iridium form oxides in
temperatures ranges from 400 to 600 to 1000
degrees centigrade respectively
www.indiandentalacademy.com
9. In 1971 the gold came into market and due to the
increasing price of that gold made it to be
replaced with palladium after that base metal
alloys had replaced these noble metal alloys
completely.
The use of palladium in cars as a catalyst
increased its cost and demand.
www.indiandentalacademy.com
10. ALLOYS
. The alloys are compounded to produce
properties most acceptable for their intended
dental applications, such as simple inlays,
bridges, removable cast restorations, solders, (or)
wrought wire forms
www.indiandentalacademy.com
11. HISTORICAL PERSPECTIVE ON DENTAL
CASTING ALLOYS
The history of dental casting alloys has been
influenced by 3 major factors:
1.The technologic changes of dental prosthesis.
2.Metallurgic advancements; and
3.Price changes of the noble metals since 1968.
www.indiandentalacademy.com
12. Taggart’s presentation to the New York
odontological group in 1907 on the fabrication of
cast inlay restorations often has been
acknowledged as the first reported application of
the lost wax technique in dentistry
The inlay technique described by Taggart was an
instant success.
www.indiandentalacademy.com
13. It soon led to the casting of complex inlays such
as onlays, crowns, FPD, and RPD frame works.
Because pure gold did not have the physical
properties required of these dental restorations,
existing jewellery alloys were quickly adopted.
These gold alloys were further strengthened with
copper, silver (or) palladium
www.indiandentalacademy.com
14. In 1932, the dental materials group at the
National Bureau of Standards surveyed the alloys
being used and roughly classified them as Type 1,
2, 3 and 4.
www.indiandentalacademy.com
15. By 1948, the composition of Dental Noble metal
alloys for cast metal restorations had become
rather diverse, with these formulations, the
tarnishing tendency of the original alloys
apparently had disappeared. It is now known that
in gold alloys, palladium is added to counter act
the tarnish potential of silver.
www.indiandentalacademy.com
16. The base metal removable partial denture alloys
were introduced in the 1930s. Since that time,
both Nickel-chromium and cobalt-chromium
formulations have become increasingly popular
compared with conventional Type IV gold alloys
www.indiandentalacademy.com
17. by 1978, the price of gold was climbing so
rapidly the attention focused on the noble metal
alloys. To reduce the precious metal content yet
retain the advantages of the noble metals for
dental
www.indiandentalacademy.com
18. PROPERTIES OF NOBLE METALALLOYS
GOLD :
Pure gold is a soft, malleable, ductile metal that does
not oxidize under atmospheric conditions and is
attacked by only a few of the most powerful oxidizing
agents.
It has a rich yellow colour with a strong metallic
luster.
Although it is the most ductile and malleable of all
metals, it ranks much lower in strength.
www.indiandentalacademy.com
19. The pure metal fuses at 1063°C, which is only
20° below the melting point of copper (1083°C).
Small amounts of impurities have a pronounced effect
on the mechanical properties of gold and its alloys.
www.indiandentalacademy.com
20. The presence of less than 0.2% lead will cause
gold to be extremely brittle.
Mercury in small quantities also has a harmful
effect on its properties.
www.indiandentalacademy.com
21. Gold is nearly as soft as lead, with the result that in
dental alloys, coins, and articles of jewellery it must
be alloyed with copper, silver, platinum and other
metals to develop the necessary hardness, durability
and elasticity.
The specific gravity of pure gold is between 19.30 and
19.33, making it one of the heavy metal.
www.indiandentalacademy.com
22. Air (or) water at any temperature does not affect (or)
tarnish gold.
Gold is not soluble in sulfuric, nitric (or)
hydrochloric acids
www.indiandentalacademy.com
23. PALLADIUM
Palladium is not used in the pure state in
dentistry, but it is used in many dental alloys,
combined with either gold (or) silver.
It is cheaper than platinum and since it imparts
many of the properties of platinum to dental
alloys, it is often used as a replacement for
platinum.
www.indiandentalacademy.com
24. Palladium is a white metal some what darker than
platinum.
Its specific gravity is 11.4 (or) about half that of
platinum.
www.indiandentalacademy.com
25. It is a malleable and ductile metal with a melting
point of 1555°C, which is the lowest of the
platinum group of metals.
The metals has the quality of absorbing (or)
occluding large quantities of hydrogen gar when
heated. This can be an undesirable quality when
alloys containing palladium are heated with an
improperly adjusted gas air torch.
www.indiandentalacademy.com
26. IRIDIUM, RUTHENIUM, AND RHODIUM
Small amounts of iridium are some times present
in dental alloys, either as impurities combined
with platinum (or) as additions to modify the
properties.
As little as 0.005% (50 ppm) is effective in
refining the grain size of cast gold alloys.
www.indiandentalacademy.com
27. Ruthenium produces a similar effect.
Iridium is a hard metal that is quite brittle, white
with a high sp. Gravity of 22.42 and an
exceptionally high melting point estimated to be
about 2440'C
www.indiandentalacademy.com
28. SILVER
Silver is malleable and ductile, white, the best-
known conductor of heat and electricity, and
stronger and harder than gold but softer than
copper.
It melts at 960.5'C, which is below the melting
point of both gold and copper.
www.indiandentalacademy.com
29. It is unaltered in clean, dry air at any temperature
but combines with sulfur, chlorine and
phosphorous, (or) vapors containing these
elements (or) their compounds.
Foods containing sulfur compounds cause severe
tarnish on silver.
www.indiandentalacademy.com
30. Pure silver is seldom employed in dental
restorations because of the black sulfide
formation on the metal in the mouth, although it
is used extensively for small additions to many
gold alloys.
www.indiandentalacademy.com
31. Addition of small amounts of palladium to silver
containing alloys prevents the rapid corrosion of
such alloys in the oral environment.
www.indiandentalacademy.com
32. KARAT AND FINENESS OF GOLD
For many years the gold content of gold alloys
has been described on the basis of karat, (or) in
terms of fineness, rather than by weight %.
The term karat refers to the parts of pure gold
in 24 parts of an alloy.
www.indiandentalacademy.com
33. For many years the gold content of gold alloys
has been described on the basis of karat, (or) in
terms of fineness, rather than by weight %.
The term karat refers to the parts of pure gold
in 24 parts of an alloy.
www.indiandentalacademy.com
34. Fineness describes gold alloys by the number of
parts per 1000 of gold. For example, pure gold
has a fineness of 1000, and 650 fine alloy has a
gold content of 65%. Thus the fineness rating is
to timer the gold % in an alloy.
www.indiandentalacademy.com
35. CLASSIFICATION OF DENTAL CASTING
ALLOYS (OR) DENTAL GOLD ALLOYS
Type I
Type II
Type III and
Type IV
www.indiandentalacademy.com
36. Type I (Soft): These alloys are limited to use in
inlays that are subject only to slight stress during
mastication
www.indiandentalacademy.com
37. Type II (Medium): These medium alloys can be
used for all types of cast inlays and onlays.
www.indiandentalacademy.com
38. Type III (Hard): These alloys are most
acceptable for crowns, thin 3/4th crowns, and
anterior and posterior bridge abutments, which
should not be cast from the softer and weaker
Type I and Type II alloys.
www.indiandentalacademy.com
39. Type IV (Extra hard): These alloys are designed
to have sufficient strength and adequate
properties for cast removable partial dentures
with clasps, precision cast fixed bridges and ¾
crowns, which are not subjected to hard working
(or) burnishing operations.
www.indiandentalacademy.com
40. Composition:
The composition of the gold casting alloys
that meet the requirements of ADA Sp. No. 5 are
given in the Table below:
www.indiandentalacademy.com
41. TYPE GOLD PLATINUM PALLADIUM
I 81-83% - 0.2-4.5%
II 76-78% - 1-3%
III 73-77% - 2-4%
IV 71-74% 0-1% 2-5%
www.indiandentalacademy.com
43. It is apparent from the Table that there is some
reduction in gold content when a comparison is
made between Type I and IV alloys.
An increase in copper content is observed as
the gold content is decreased.
An increase in the zinc content also occurs in
Type IV alloys.
www.indiandentalacademy.com
44. Platinum is rarely added to Type 1 gold alloys,
but a small amount of palladium is always added
to all 4 types.
www.indiandentalacademy.com
45. PROPERTIES OF GOLD CASTING ALLOYS
Type
Vickers hardness number
(Kg/mm2) Softened
Yield strength, (0.1% Offset) MPa Elongation
Minimum Maximum
Softened
minimum
Hardened
minimum
Softened
minimum
Hardened
minimum (%)
I 50 90 None None 18 None
II 90 120 140 None 12 None
III 120 150 200 None 12 None
IV 150 None 340 500 10 2
www.indiandentalacademy.com
46. From the above table it may be seen that as the
hardness increases from Type I to Type IV, the
yield strength and tensile strength values are also
increased, and the elongation generally
decreased.
www.indiandentalacademy.com
47. Soft alloys have a higher degree of elongation
and a relatively greater quality of ductility than
the alloys of higher hardness values
www.indiandentalacademy.com
48. Melting range:
its between 920-960
The melting range of the alloy is important for
selecting the type of investment and type of heating
source needed
Density:
It indicates the number of dental castings made from
an unit weight of the metal.
Gold alloys are lighter than pure gold
www.indiandentalacademy.com
49. The Castability of the alloy is also effected by the
density
Hardness:
this indicates the ease of with which these alloys can
be cut , ground , and polished
Gold alloys are generally more user friendly
www.indiandentalacademy.com
50. Elongation:
it indicates the ductility of the material
Alloys with low elongation are brittle
www.indiandentalacademy.com
51. Modulus of elasticity:
It indicates the stiffness/ flexibility of the metal
Tarnish and corrosion resistance:
gold alloys are resistant to tarnish and corrosion
Casting shrinkage:
It is less than 1.25 and 1.65% when compared to base
metal alloys
www.indiandentalacademy.com
52. This shrinkage occurs in 3 stages
1. Thermal contraction of the liquid material
2. Contraction of the metal while changing from liquid
to solid state.
3. Thermal contraction of the solid metal as it reaches
room temperature
www.indiandentalacademy.com
53. Biocompatibility: def :ability of a material to
elicit an appropriate biological response in an
given application in a body
gold alloys are relatively compatible
Casting investment: gypsum bonded investments
are used for gold alloys because of their low
fusion temperature
www.indiandentalacademy.com
54. FUSION TEMPERATURES OF DENTAL
GOLD CASTING ALLOYS
METAL (or) ALLOY TYPICAL FUSION TEMPERATURE (°C)
Type I 1005-1070
Type II 900-970
Type III 875-1000
Type IV 875-1000
www.indiandentalacademy.com
55. The fusion temperatures are important factors in
choosing the type of investment to be used.
Alloys having fusion temperatures higher than
about 1100°C should not be cast into calcium
sulfate bonded investment
www.indiandentalacademy.com
56. In 1984 the ADA proposed a simple classification
of dental casting alloys.
ALLOY TYPE TOTAL NOBLE METAL CONTENT
High noble metal
Contains 40 wt% AV and 60% wt of the
noble metal elements (Au+Ir+OS+Pt+Rh+Ru).
Noble metal Contains 25% of the noble metal elements.
Predominantly base metal Contains < 25 wt% of noble metal elements.
www.indiandentalacademy.com
57. Many manufacturers have adopted this
classification to simplify the communication
between dentists and dental laboratory
technologists.
www.indiandentalacademy.com
58. CLASSIFICATION OF ALLOYS FOR ALL
METAL RESTORATIONS METAL,
CERAMIC RESTORATIONS AND FRAME
WORKS FOR REMOVABLE PARTIAL
DENTURES
www.indiandentalacademy.com
59. Alloy Type All-Metal Metal-Ceramic Removable Partial Dentures
High noble
Au-Ag-Cu-Pd metal ceramic
alloys
Au-Pt-Pd
Au-Pd-Ag (5-12 wt% Ag)
Au-Pd-Ag (>wt 12% Ag)
Au-Pd (no Ag)
Au-Ag-Cu-Pd
Noble
Ag-Pd-Au-Cu
Ag-Pd
Metal ceramic alloys
Pd-Au (no Ag)
Pd-Au-Ag
Pd-Ag
Pd-Cu
Pd-Co
Pd-Ga-Ag
Ag-Pd-Au-Cu
Ag-Pd
www.indiandentalacademy.com
60. HEAT TREATMENT OF HIGH NOBLE AND
NOBLE METALALLOYS:
Gold alloys can be significantly hardened if the
alloy contains a sufficient amount of copper.
Types I and II alloys usually do not harden, (or)
harden to a lesser degree than do the types III and
IV alloys.
www.indiandentalacademy.com
61. The actual mechanism of hardening is probably
the result of several different solid - solid
transformations
www.indiandentalacademy.com
62. SOLUTION HEAT TREATMENT: Alloys that
can be hardened can of course, also be softened.
In metallurgical terminology the softening heat
treatment is referred as
AGE HARDENING: The hardening heat
treatment is termed so
www.indiandentalacademy.com
63. SOFTENING HEAT TREATMENT
The casting is placed in an electric furnace for 10
minutes at a temperature of 700°C (129°F) and
then it is quenched in water
The tensile strength, hardness and proportional
limit are reduced by such a treatment but the
ductility is increased
www.indiandentalacademy.com
64. The softening heat treatment is indicated for
structures that are to be ground, shaped (or)
otherwise cold worked, either in or out of the
mouth.
www.indiandentalacademy.com
65. HARDENING HEAT TREATMENT:
The age hardening of the dental alloys can be
accomplished 'in several ways. One of the most
practical hardening treatments is by "Soaking"
(or) aging the casting at a specific temperature for
a definite time, usually 15 to 30 minutes, before it
is water quenched.
www.indiandentalacademy.com
66. The aging temperature depends on the alloy
composition but is generally between 200°C and
450°C.
Ideally, before the alloy is given an age-hardening
treatment, it should be subjected to a softening
heat treatment to relieve all strain hardening
www.indiandentalacademy.com
67. The hardening heat treatment is indicated for
metallic partial dentures, bridges, and other
similar structures.
www.indiandentalacademy.com
68. CASTING SHRINKAGE:
Most metals and alloys, including gold and noble
metal alloys, shrink when they change from the
liquid to the solid state
The values for the casting shrinkage differ for the
various alloys presumably because of differences
in their composition
www.indiandentalacademy.com
69. Alloy Casting shrinkage (%)
Type I, Gold base 1.56%
Type II, Gold base 1.37%
Type III, Gold base 1.42%
Ni-Cr-Mo 2.3%
www.indiandentalacademy.com
70. SILVER PALLADIUM ALLOYS:
These alloys are white and predominantly silver
'm composition but have substantial amounts of
palladium (at least 25/o) that provide nobility and
promote the silver tarnish resistance. They may
(or) may not contain copper and a small amount
of gold.
www.indiandentalacademy.com
71. The copper (Cu) free Ag-Pd alloys may contain
70% to 72% silver and 25% palladium and may
have physical properties of a Type III gold alloy.
Other silver-based might contain roughly 60%
silver 25% palladium and as much as 15% or
more of copper and may have properties more
like a Type IV gold alloy.
www.indiandentalacademy.com
72. Because of the increasing interest in aesthetics by
dental patients, a decreased use of all metal
restorations has occurred during the past decade
The use of metal ceramic restorations in posterior
sites has increased relative to the use of all metal
crowns and onlays.
www.indiandentalacademy.com
73. HIGH NOBLE ALLOYS FOR METAL
CERAMIC RESTORATIONS
The original metal ceramic alloys contained 88%
gold and were much to soft for stress bearing
restorations such as FPD. Because there was no
evidence of a chemical bond between these alloys
and dental porcelain, mechanical retention and
undercuts were used to prevent detachment of the
ceramic veneer
www.indiandentalacademy.com
74. Using the stress bond test, it was found that the
bond strength of the porcelain to this type of alloy
was less than the cohesive strength of the
porcelain itself
This mean that if the failure occurred in the
metal-ceramic restoration, it would most probably
arise at the porcelain metal interface.
www.indiandentalacademy.com
75. By adding less than 1% of oxide forming
elements such as iron, indium, and tin to this high
gold content alloy, the porcelain metal bond
strength was improved by a factor of 3. Iron also
increase the proportional limit and strength of the
alloy.
www.indiandentalacademy.com
76. This 1% addition of base metals to the gold,
palladium and platinum alloy was all that was
necessary to produce a slight oxide film on the
surface of the substructure to achieve a porcelain-
metal bond strength level that surpassed the
cohesive strength of porcelain itself.
www.indiandentalacademy.com
77. THE HIGH NOBLE ALLOYS FOR METAL
CERAMIC RESTORATIONS ARE:
www.indiandentalacademy.com
78. GOLD-PLATINUM - PALLADIUM ALLOYS
These9alloys have a gold content ranging up to
88% with varying amounts of palladium,
platinum and small amounts of base metals.
Some of these alloys are yellow in colour. Alloys
of this type are susceptible to sag deformation
and FPD's should be restricted to 3-unit spans,
anterior cantilevers (or) crowns
www.indiandentalacademy.com
79. Gold-Palladium-Silver Alloys:
These gold based alloys contain between 39%
and 77% upto 35% palladium and silver levels as
high as 22%.
The silver increases thermal contraction
coefficient but it also has a tendency to discolour
some porcelains
www.indiandentalacademy.com
80. Gold-Palladium Alloys:
A gold content ranging from 44% to 55% and a
palladium level of 35% to 45% is present in these
metal ceramic alloys, which have remained
popular despite their relatively high cost.
www.indiandentalacademy.com
81. The lack of silver results in a decreased thermal
contraction coefficient and the freedom from
silver discolouration of porcelain.
www.indiandentalacademy.com
82. Alloys of this type must be used with porcelains
that have low coefficients on to avoid the
development of axial and circumferential of
thermal contraction to avoid the development of
axial and circumferential tensile stresses in
Porcelain during the cooling part of the porcelain
firing cycle.
www.indiandentalacademy.com
83. NOBLE ALLOYS FOR METAL
CERAMIC RESTORATIONS
www.indiandentalacademy.com
85. PALLADIUM BASED ALLOYS
Noble palladium based alloys offer a compromise
between the high noble gold alloys and the
predominantly base metal alloys
The price per ounce of a palladium alloy is
generally one half to one third that of a gold
alloys.
www.indiandentalacademy.com
86. The density of a palladium based alloy is midway
between that of base metal and of high noble
alloys
www.indiandentalacademy.com
87. Palladium - Silver Alloys:
Pd-Ag alloys were introduced widely in the late
1970s. This alloy type was introduced to the U.S.
market in 1974 as the first gold free noble metal
available for metal ceramic restorations
www.indiandentalacademy.com
88. Pd-Ag alloys enjoyed wide spread popularity for
a few years after they were introduced, but their
popularity has declined some what in recent years
because of their tendency to discolour porcelain
during firing.
www.indiandentalacademy.com
89. The compositions of Pd-Ag alloys fall within a
narrow range: 53% to 61% palladium and 28% to
40% silver
Tin (or) Indium or both are usually added to
increase alloy hardness and to promote oxide
formation for adequate bonding of porcelain. In
some of these alloys, the formation of an internal
oxide rather than an external oxide has been
reported.
www.indiandentalacademy.com
90. Other palladium alloys contain 75% to 90%
palladium and no silver and were developed to
eliminate the greening problem some of the high
palladium alloys develop a layer of dark oxide on
their surface during cooling from the degassing
cycle, and this oxide layer has proven difficult to
mask by the opaque porcelain.
www.indiandentalacademy.com
91. Other high palladium alloys such as the Pd-Ga-
Ag-Au type seem not to be plagued by this
problem.
The replacement of gold by palladium raises the
melting range but lower the contraction
coefficient of an alloy. Increases the silver
content tends to lower the melting range and
raises the contraction coefficient
www.indiandentalacademy.com
92. Because of their high silver contents compared
with the gold based alloys, the silver
discoloration effect is most severe for these
alloys. Gold metal conditioners or ceramic
coating agents may minimize this effect.
www.indiandentalacademy.com
93. The low specific gravity of these alloys (10.7-
11.1) combined with their low intrinsic cost
makes these alloys attractive as economical
alternatives to the gold based alloys.
www.indiandentalacademy.com
94. PALLADIUM-COPPER ALLOYS:
This alloy is comparable in cost to the Pd-Ag
alloys
Because of their low melting range of
approximately 1170°C to 1190°C, these alloys are
expected to be susceptible to creep deformation
(Sag) at elevated firing temperatures
www.indiandentalacademy.com
95. These alloys contain between 74-80% palladium
and 9-15% copper
One should be aware of the potential effect on
aesthetics of the dark brown (or) black oxide
formed during oxidation and subsequent
porcelain firing cycles
www.indiandentalacademy.com
96. Care should be taken, to mask this oxide
completely with opaque porcelain and to
eliminate the un-aesthetic dark band that develops
at metals porcelain junctions.
The Pd-Cu alloy have yield strengths upto
1145MPa.
www.indiandentalacademy.com
97. Elongation values of 5% to 11% and hardness
values as high as some base metal alloys.
Thus, these alloys would appear to have a poor
potential for burnishing except when the marginal
areas are relatively thin.
www.indiandentalacademy.com
98. PALLADIUM-COBALT ALLOYS:
This alloy group is comparable in cost to the Pd-
Ag and Pd-Cu alloys. They are often advertised
as gold free, nickel-free, beryllium-free, and
silver-free alloys.
. The reference to nickel and beryllium indicates
that these alloys, as is true with the other noble
metals, are generally considered biocompatible.
www.indiandentalacademy.com
99. This Pd-Co group is the most sag resistant of all
noble metal alloys.
The noble metal content (based on palladium)
ranges from 78% to 88%.
The cobalt content ranges between 4 and 10wt%
over commercial alloy contains 8% gallium.
www.indiandentalacademy.com
100. An example of typical properties of a Pd-Co alloy
is as follows:
Hardness 250DPH
Yield strength 586MPa
Elongation 20% and
Modulus of elasticity 85.2Gpa
www.indiandentalacademy.com
101. Although these alloys are silver-free,
discolouration of porcelain can still result because
of the presence of cobalt
www.indiandentalacademy.com
102. PALLADIUM-GALLIUM-SILVER AND PALLADIUM-GALLIUM-SILVER-GOLD ALLOYS
These alloys are the most recent of the noble
metals. This group of alloys was introduced
because they tend to have a slightly lighter
coloured oxide than Pd-Cu (or) Pd-Co alloys and
they are thermally compatible with lower
expansion porcelains.
www.indiandentalacademy.com
103. The oxide that is required for bonding to
porcelain is relatively dark, but it is somewhat
lighter than those of the Pd-Cu and Pd-Co alloys
The silver content is relatively low (508 wt%)
and is usually inadequate to cause porcelain
“greening”.
www.indiandentalacademy.com
104. GREENING:
It is believed that the colloidal dispersion of the
silver atoms entering body and incisal porcelain
or the glazed surface from vapour transport or
surface diffusion may cause colour change
including green, yellow-green, yellow-orange,
orange, and brown hues
www.indiandentalacademy.com
105. . One theory that has been proposed for this
greenish yellow discoloration, popularly termed
"Selling" is that the silver vapour escapes from
the surface of these alloys during firing of the
porcelain, diffuses as ionic silver into the
porcelain and is reduced to form colloidal
metallic silver in the surface layer of porcelain.
www.indiandentalacademy.com
106. Porcelains with higher sodium contents are
believed to exhibit a more intense discoloration
because of more rapid silver diffusion in sodium
containing glass
This hypothesis is based on observations of
greater discoloration in lighter shades of
porcelain and in porcelain with lower opacifier
contents and higher sodium content.
www.indiandentalacademy.com
107. The intensity of discolouration ( chroma ) usually
increases in the cervical region because surface
diffusion of silver from marginal metal provides a
higher localised silver concentration.
www.indiandentalacademy.com
108. This greening is more in:
1.high silver content alloys
2.lighter shades multiple firing procedures
3. higher temperatures
4. body porcelain in direct contact with the alloys
vacuum firing cycles
5. and certain brands of porcelain
www.indiandentalacademy.com
109. Claire Manaranchea, Helga Hornbergerb.
“A proposal for the classification of
dental alloys according to their resistance
to corrosion”.
The purpose of this study was to establish a
method to compare and classify dental alloys in
relation to their resistance to corrosion
www.indiandentalacademy.com
110. Results.
High gold alloys had a similar polarization curve
than gold. The same effect was observed for Pd–
base alloys, their curves were similar to the one
of palladium.
The ions released during chemical corrosion
were non-precious metallic ions.
Thereby Ni–Cr alloys were found to release the
most ions.
www.indiandentalacademy.com
111. Au–Pt alloys showed the highest release of ions
compared with other precious alloys but low
compared with Ni–Cr.
Electrochemical corrosion was more aggressive
than chemical corrosion and every type of
elements was etched,
the higher the precious metal content, the higher
the resistance to corrosion of the alloy.
www.indiandentalacademy.com
112. N. Silikas a, P.L. Wincott b, D. Vaughanb,
D.C. Wattsa, G. Eliadesc,∗
“Surface characterization of precious
alloys treated with thione metal primers”
Objectives. To characterize the effect of two
thione metal primers with phosphate groups
on the surface morphology and composition
of two noble Prosthodontic alloys.
www.indiandentalacademy.com
113. Results.
After Alloy Primer treatment, Polarised Light
Microscopy revealed a crystalline phase
dispersed in an amorphous phase on both the
alloys tested.
MP demonstrated a fibrial arrangement with the
most dense structure found on the Hi–Pd alloy.
Fourier-transform infrared micro spectroscopy
failed to clearly resolve the presence of S H
peaks on alloy surfaces.
www.indiandentalacademy.com
114. Moreover, NH and P S peaks were identified
denoting the presence of original thione
tautomers.
In both primers, phosphates were detected in a
dissociative state ( PO3 2−).
www.indiandentalacademy.com
115. CONCLUSION
Though these noble metals are costlier than base
metal alloys their properties like biocompatibility
gained them a lot of importance in dentistry
So one should have a through knowledge of these
precious metal alloys
www.indiandentalacademy.com
117. 4. Claire Manaranchea, Helga
Hornbergerb. “A proposal for the
classification of dental alloys according
to their resistance to corrosion”.
5. N. Silikas a, P.L. Wincott b, D.
Vaughanb, D.C. Wattsa, G. Eliadesc,∗
“Surface characterization of precious
alloys treated with thione metal primers”
www.indiandentalacademy.com