CERAMIC BASED COATING MATERIALS
APPLICABLE WITHOUT REMOVAL OF RUST
HARDENING BY ABSORBING HUMIDITY OF ATMOSPHERE
ADHESIVE ON THE WOOD, CONCREATE , GLASS FIBER, ETC.
It cures by reacting to moisture in the air.
It can be applied to metal, concrete, masonry, wood, etc.
Provides a superior adhesion to the substrates
Properties:
Can be applied directly over the rust or toxic paints
- Resistant to most chemical solvents and salt water
- Surface tensile strength:6,780psi(475kgs/㎠)
- Water-proof, insulation(10¹² )
Indoor temperature differences of Waterproof coating± 5°C,
Floor Crack Sealing & Coating
Excellent impact Resistance
- UV resistance
- 15-20 year-long lasting coating
bbn@bbnworld.com
3. CERAMIC BASED COATING MATERIALS
APPLICABLE WITHOUT REMOVAL OF RUST
HARDENING BY ABSORBING HUMIDITY OF ATMOSPHERE
ADHESIVE ON THE WOOD, CONCREATE , GLASS FIBER, ETC.
It cures by reacting to moisture in the air.
It can be applied to metal, concrete, masonry, wood, etc.
Provides a superior adhesion to the substrates
- 3 -
1. PRODUCT
CONCEPT
NT-100 & NT-200
4. NT-100 Anti-Corrosion Coating for Metal
General Information :
It can be applied directly over the rusty metal without removing the existing rust.
It cures by reacting to moisture in the air. It can be applied to metal, concrete, masonry,
wood, etc and provides a superior adhesion to the substrates.
Properties:
Can be applied directly over the rust or toxic paints
- Resistant to most chemical solvents and salt water
- Surface tensile strength:6,780psi(475kgs/㎠)
- Water-proof, insulation(10¹² )
-Indoor temperature differences of Waterproof coating± 5°C,
-Floor Crack Sealing & Coating
-Excellent impact Resistance
- UV resistance
- 15-20 year-long lasting coating
5. NT-100 Anti-Corrosion Coating for Metal
Typical Uses:
- Basecoat
- Anti-corrosion coating on rusty metal
- Protection coating for metal or concrete from acid
- Interior/exterior coating for acid/solvent/oil tank
- Coating for pipe line over/under ground
- Anti-corrosion coating on water circulation tank or refrigerator
-An encapsulant for lead-based paints and other bio-hazardous materials
Description :
- Color : silver gray
-Thickness : non-rusty surface : 40 ~ 50μ. rusty surface : 50 ~ 100μ
- Temperature : -30 ~ 160℃(possible 500℃, Option)
- Applying methods : Brush, roller, Spray
- Coating surface area : 6㎡/ℓ
- Hardening time : 7~9 days
- Intervals : 4 hours
- Cleaner : MEK
6. NT-100 Anti-Corrosion Coating for Underwater
Underwater paint Properties :
1. NT- 100 Directly applied over a rust
2. Protection against salt water or acid (hydrochloric acid , acetic acid)
3. Major 6 heavy metals free (Refer to “Test result”)
4. Indoor temperature differences of Waterproof coating ±5°C, Floor sealing
5. Electric insulation : 1012
6. Coating area: 6~10㎡, Iron frame: 20㎡
7. Replacement of Hot-dip Galvanizing
8. Excellent adhesion strength of 11.3MPa Abrasion resistance of 4mg (Refer to
“Test result”)
9. Applicable to wood, plastics, bricks, etc.
7. NT-200 Anti-Corrosion Coating for Underwater
General Information :
Underwater anti-corrosion coating in water and humidity environment
Can be applied as a lining coat for drinking water tanks.
Adhere tenaciously to a variety of substrates
Can be used successfully in DTM(direct to metal) applications
The coating has been fortified with a very efficient, non-toxic rust inhibitor.
Properties:
Lead and Chromate free
Excellent Impact Resistance
Excellent tensile strength
Excellent protection against chemical solvents
Excellent adhesion strength
Can be applied directly over wet, rusted surface without loss of adhesion
8. NT-200 Anti-Corrosion Coating for Underwater
Typical Uses:
Lower part of river infrastructure (bridge, a pedestrian crossing bridge)
Lower part of a ship vessel, power line tower
Lower part of iron structure (coastal, marine)
Lining coat for storage tank (drinking water, industrial water, oil, chemistry wastes)
An oil prospecting ship
Description :
Color : White( possible for variety of color, Option)
Thickness : 150μ(2 times)
Surface treatment : remove Oil and remnants
Coating surface area : 6㎡/ℓ
Applying methods : Brush, roller, Spray
Hardening time : 10 days
Shelf life : 6 ~ 8 hours
Temperature : -30 ~ 160℃(possible 500℃, Option)
Intervals : 4 hours ~ 2weeks
Mixed ratio : 5:1(Main : Hardener)
9. Ⅱ. Properties and Specification
NO. Item Unit Testing Method Measured Value
1 Color - - Silver Grey
2 Adhesive KS D-6711 100/100
3 Insulation 2.8193×10¹²
4 Heat Resisting 500℃×1 Hr(Bubble & Crack) Test All Right
5 Wear Resistance KSL-1001 0.00
6 Tensile Strength - 475kg/ ㎠
7 Viscosity cps KSM-5000 320
8 Specific Gravity g/㎠ KSM-5000 1.1
9 Temperature C KSM-5000 °Celsius -30~163°C
10 Main Components - KSM-5000 Special Metal and Ceramic Compound
11 Vehicle Type - KSM-5000 Aromatic Polyurethane
12 Pigment Type - KSM-5000 Aluminum
13 V.O.C g/liter KSM-5000 425
14 Applicable Area - - 12㎡/liter
10. Ⅲ. Product Advantage
1. Coating after simple cleaning of the surface without removal of rust save
expenses and time
2. Strong Adhesion to glass, wood, concrete structure, plastic and etc.
3. Not easy to be dusted and easy to clean
4. Very good durability due to no Color Change by Ultraviolet Rays
and no Loss of Glossy
5. Coating works is possible in High Temperature due to high heat resistance
6. Working effectiveness is maximized due to single liquid solution
7. Eco-Friendly Coating Materials composed of major Ceramic components
11. Eco-Friendly
Pure Natural Inorganic Materials
does not cause pollution
- 11 -
Durability
No Color Change by Ultraviolet
Ray, Almost No Loss of Glossy
Superior Insulation
Characteristics
Dust and Dirt are not stickable and
Easy to clean by water
Nonflammable, Non-Toxic. Non-
VOC and No emission of
poisonous gas
Superior Protective against
Alkali and Acid
Heat Resistance
Anti-Contaminant
Chemical Resistance
Heat Insulation
11
Feature
Ⅳ. Product Feature
12. Environment
Waste Water and Waste
Treatment Place
- 12 -
Factory
Piping and Valve, Furnace,
Boiler, Chimney, Electric
Transmission Tower
Ships, Sea Shore and Ocean
structure and construction
Heat Insulation, Water
Proofing, Internal and
Interior and Exterior
Painting
Storage Tank of Oil, Gas,
Chemicals
Construction
Power Generation Chemicals
Marine
Piping, Tank, Untilities
12
APPLICATION
Ⅴ. Application Area
13. Ⅴ-1. Coating Works on the Rusted Wall and Pipe of Water Tank Inside
Before Coating After Coating
14. Ⅴ-2. Lining Works Inside of Pure Water Tank
Lining works on Inside of Pure Water Tank in Power Plant 2nd & 3rd Coating on the Inside of Pure Water Tank
15. Ⅴ-3. Coating Works on Factory Floor
Natural Touch Natural Touch
Before Coating First Coating by NT-100
Natural Touch Natural Touch
2nd Coating by NT-200 After Coating
16. Partial Before Coating Mortar Resin Works
NT-100 Coating Works NT-200 Coating Works
After Coating
Ⅴ-4. Water Proof Works of Factory Roof
17. Ⅴ-5. Pipe Line & Dock
Heat Resistant and Anti-Corrosion Works Corrosion Protection Works at Dock
18. Ⅴ-6. Sea Wind Corrosion Protection Works for Steel Structure
19.
20.
21. Ⅶ. Principle of Coating
Wet the rusted surface with coating liquid and it will be penetrated into porous air hole on
the rust and coated materials and then self-hardening . It forms internal bonding structure
between porous air hole and coating liquid.
Coating materials is specific Metallic Chemicals and becomes part of substrate on the
rusted surface of materials like electronic plating. This is not the same coating materials as
the general anti-corrosion coating materials
The polymer of coating liquid is penetrated into porous air hole of surface and then
absorb the humidity of atmosphere to generate gas and make micro expansion of porous air
hole . It is hardened and play role of bonding and locking between coating materials and
surface.
Metallic forms air encapsulation on the surface of coated materials and paint together
with polymer. It protects modification by ultraviolet ray
This can be used alone and independently or used as substrate coating. It can be applied
directly to the rusted surface and forms air encapsulation on the surface to protect rust
improvement or transferring
22. Ⅷ. Coating Method
1. Surface Treatment :
For the superior adhesion and getting rid of the coated defects, all rust scale, dust, dirt, oil
contaminants on the surface should be removed completely
The rust scale must be removed by scratching and surface of coating materials must be dried
If NT-100 is coated on the surface of water contained materials, the hardening of coating liquid can be
started before air encapsulation is started by penetrating into metal or porous air hole of surface, and the
adhesion power can be reduced.
2. Coating Condition:
Coating must be done over at 0℃ over and the optimum temperature for coating is 10℃~38℃
3. Mixing Rate :
This is single liquid type and can be used alone without hardening materials and
Bottom coating can be used independently without middle coating and upper coating.
4. Coating Method:
Airless Spray Gun, Bush, and roller
5. Diluting Solution
MEK, MIBK
23. Ⅷ-1. Coating Method
6. Paint and Coating Materials Preparation:
Metallic Components contained in NT-100 can be sink down at the bottom .
Fully shaking is needed before coating or use low speed stirrer
As NT-100 absorbs humidity of atmosphere and hardened, the lid should be closed after taking out quantity.
If the surface of NT-100 liquid in the used can is hardened, you can break the hardened surface and stir and
mix to use
7. Coating Procedures :
NT-100 needs always two times of coating to fill up micro hole generated after 1st coating and at the same
time, increase coating thickness for the endurance of coating
For the very high thickness of coating, the 2nd coating should be made by NT-100(HS)
2nd Coating should be made within 4-6 hours after 1st coating. 2nd Coating cannot be adhesive to the 1st
coating surface
8. Hardening Time :
If one hour is passed after coating, the paint is not wet on the hand but for the complete hardening, it takes 7-
10 days .
9. Keeping and Storage:
Lid of the can should be closed when the paint is not used. Never keep the lid open over 4 hours.
The can of 2 liters is recommendable to keep and store the paint on the shelf after opening the can
24. - 24 -
Ⅹ-8. Korea Institute of Construction Materials
Thermal Image Test before and after coating
25. Ⅹ-9. NT-100 Series for underwater Coating
The underwater coating works to recover and protect
- 25 -
the serious corrosion of underwater structure
26. Ⅹ-10. NT-100 Series of Products
Acid Resistance, Heat Resistance, For- 40℃
- 26 -
1. Acid Resistance
Hydrochloric Acid 35%
Sulfuric Acid 50~98%
2. Heat Resistance
700℃
3. Desulphurization: Acid Resistance at 350℃
4. Coating is possible at – 40℃