1. Anti-Corrosion Coating for Metal(NT-100)
Typical Uses, Properties & Description
General Information :
It can be applied directly over the rusty metal without
removing the existing rust. It cures by reacting to moisture
in the air. It can be applied to metal, concrete, masonry,
wood, etc and provides a superior adhesion to the substrates.
Properties:
- Can be applied directly over the rust or toxic paints
- Resistant to most chemical solvents and salt water
Surface tensile strength:6,780psi(475kgs/㎠)
- Water-proof, insulation(10¹² )
- Indoor temperature differences of Waterproof coating± 5°C,
Floor sealing
- Excellent impact Resistance
- UV resistance
- 15-20 year-long lasting coating
Typical Uses:
- Basecoat for DHC-300
- Anti-corrosion coating on rusty metal
- Protection coating for metal or concrete from acid
- Interior/exterior coating for acid/solvent/oil tank
- Coating for pipe line over/under ground
- Anti-corrosion coating on water circulation tank or
refrigerator
- An encapsulant for lead-based paints and other bio-hazardous
materials
Description :
2. - Color : silver gray
- Thickness : non-rusty surface : 40 ~ 50μ
rusty surface : 50 ~ 100μ
- Temperature : -30 ~ 160℃(possible 500℃, Option)
- Applying methods : Brush, roller, Spray
- Coating surface area : 6㎡/ℓ
- Hardening time : 7~9 days
- Intervals : 4 hours
- Cleaner : MEK
* NT-100 Anti-corrosion coating for
metal and underwater plant
Properties
1. NT- 100 Directly applied over a rust
2. Protection against salt water or acid
(hydrochloric acid , acetic acid)
3. Major 6 heavy metals free (Refer to “Test result”)
4. Indoor temperature differences of Waterproof
coating ±5°C, Floor sealing
5. Electric insulation : 1012
3. 6. Coating area: 6~10㎡ ,Iron frame: 20㎡
7. Replacement of Hot-dip Galvanizing
8. Excellent adhesion strength of 11.3MPa Abrasion
resistance of 4mg (Refer to “Test result”)
9. Applicable to wood, plastics, bricks, etc.
Anti-Corrosion Coating for Underwater(NT-200)
Typical Uses, Properties & Description
General Information :
Underwater anti-corrosion coating outstanding water and
humidity environment. Can be applied as a lining coat for
drinking water tanks. Adhere tenaciously to a variety of
substrates and can be used successfully in DTM(directtometal)
applications as the coating has been fortified with a very
efficient, non-toxic rust inhibitor.
Properties:
- Lead and Chromate free
- Excellent Impact Resistance
- Excellent tensile strength
- Excellent protection against chemical solvents
- Excellent adhesion strength
4. - Can be applied directly over wet, rusted surface without
loss of adhesion
Typical Uses:
- Lower part of river infrastructure (bridge, a pedestrian
crossing bridge)
- Lower part of a ship vessel, power line tower
- Lower part of iron structure (coastal, marine)
- Lining coat for storage tank (drinking water, industrial
water, oil, chemistry wastes)
- An oil prospecting ship
Description :
- Color : White( possible to varity of color, Option)
- Thickness : 150μ(2 times)
- Surface treatment : remove Oil and remnants
- Coating surface area : 6㎡/ℓ
- Applying methods : Brush, roller, Spray
- Hardening time : 10 days
- Shelf life : 6 ~ 8 hours
- Temperature : -30 ~ 160℃(possible 500℃, Option)
- Intervals : 4 hours ~ 2weeks
- Mixed ratio : 5:1(Main : Hardener)