- Centrifugal casting uses centrifugal force to infiltrate molten metal into fibrous preforms to produce metal matrix composites. There are three main cases of infiltration depending on the shape and size of the preform.
- The minimum rotational speed required for infiltration to begin depends on the threshold pressure needed to overcome surface tension, which is determined by factors like fiber diameter and contact angle.
- Darcy's law and the continuity equation can be used to model infiltration, relating the pressure, velocity, and position of the infiltration front over time. Numerical integration is typically required to solve the resulting differential equations.
fatigue of 400 series martensitic stainless steel that called WELDCLAD 3HT is producing by COREIWRE have been evaluated in the temperature of 100-600 °C in comparison with ss 316L that normally use in ROT
fatigue of 400 series martensitic stainless steel that called WELDCLAD 3HT is producing by COREIWRE have been evaluated in the temperature of 100-600 °C in comparison with ss 316L that normally use in ROT
Forming operations are those in which the shape of a metal piece is changed by plastic deformation; for example, forging, rolling, extrusion, and drawing are common forming techniques.
A Permanent Magnet BLDC motor is designed for reduction in cogging torque and flux per pole. The cogging torque causes direct impact in permanent magnet BLDC motor performance by causing torque ripple problems. This paper proposes a new method for reducing cogging torque by adapting to U-clamped magnetic poles. Finite Element Analysis (FEA) is used to calculate the cogging torque and the flux per pole for different shapes of magnetic pole. It can be shown that the cogging torque could be greatly reduced by adapting to U-clamped magnetic poles. At the same time it is found that the flux per pole is also considerably reduced. The effectiveness of the proposed method is verified by comparing the cogging torque and flux per pole for various designs available in the literature.
Study the Magnetic Properties of Invar Alloys by Using High Pressure Mössbaur...IJERA Editor
High pressure 57F MÖssbaur spectroscopy measurement ( up to 42 Gpa ) at room temperature have been carried
out for investigation the magnetic properties of Ɣ(f.c.c) Fe78Ni22 alloys using diamond anvil cell (DAC)
technique. The mÖssbaur spectrum at 0 Gpa shows a six line magnetic pattern with broad outer peaks and an
average hyperfine field of ~32T characteristic of a disordered alloys. In the pressure rang (2<p><20 Gpa) we
observe MÖssbaur spectra with additional low heperfine field component resembling spectra of Ɣ(f.c.c) Fe-Ni
Invar alloys (25-35 at % Ni). Our data indicate a pressure induced invar effect for Fe78Ni22 alloy at ~7-12 Gpa.
Above 20 Gpa the hyperfine field break down and the alloy becomes non-magnetic showing only a single line
MÖsbauer spectrum.
Forming operations are those in which the shape of a metal piece is changed by plastic deformation; for example, forging, rolling, extrusion, and drawing are common forming techniques.
A Permanent Magnet BLDC motor is designed for reduction in cogging torque and flux per pole. The cogging torque causes direct impact in permanent magnet BLDC motor performance by causing torque ripple problems. This paper proposes a new method for reducing cogging torque by adapting to U-clamped magnetic poles. Finite Element Analysis (FEA) is used to calculate the cogging torque and the flux per pole for different shapes of magnetic pole. It can be shown that the cogging torque could be greatly reduced by adapting to U-clamped magnetic poles. At the same time it is found that the flux per pole is also considerably reduced. The effectiveness of the proposed method is verified by comparing the cogging torque and flux per pole for various designs available in the literature.
Study the Magnetic Properties of Invar Alloys by Using High Pressure Mössbaur...IJERA Editor
High pressure 57F MÖssbaur spectroscopy measurement ( up to 42 Gpa ) at room temperature have been carried
out for investigation the magnetic properties of Ɣ(f.c.c) Fe78Ni22 alloys using diamond anvil cell (DAC)
technique. The mÖssbaur spectrum at 0 Gpa shows a six line magnetic pattern with broad outer peaks and an
average hyperfine field of ~32T characteristic of a disordered alloys. In the pressure rang (2<p><20 Gpa) we
observe MÖssbaur spectra with additional low heperfine field component resembling spectra of Ɣ(f.c.c) Fe-Ni
Invar alloys (25-35 at % Ni). Our data indicate a pressure induced invar effect for Fe78Ni22 alloy at ~7-12 Gpa.
Above 20 Gpa the hyperfine field break down and the alloy becomes non-magnetic showing only a single line
MÖsbauer spectrum.
Similar to Introduction to metal matrix composites (20)
What are the main advantages of using HR recruiter services.pdfHumanResourceDimensi1
HR recruiter services offer top talents to companies according to their specific needs. They handle all recruitment tasks from job posting to onboarding and help companies concentrate on their business growth. With their expertise and years of experience, they streamline the hiring process and save time and resources for the company.
India Orthopedic Devices Market: Unlocking Growth Secrets, Trends and Develop...Kumar Satyam
According to TechSci Research report, “India Orthopedic Devices Market -Industry Size, Share, Trends, Competition Forecast & Opportunities, 2030”, the India Orthopedic Devices Market stood at USD 1,280.54 Million in 2024 and is anticipated to grow with a CAGR of 7.84% in the forecast period, 2026-2030F. The India Orthopedic Devices Market is being driven by several factors. The most prominent ones include an increase in the elderly population, who are more prone to orthopedic conditions such as osteoporosis and arthritis. Moreover, the rise in sports injuries and road accidents are also contributing to the demand for orthopedic devices. Advances in technology and the introduction of innovative implants and prosthetics have further propelled the market growth. Additionally, government initiatives aimed at improving healthcare infrastructure and the increasing prevalence of lifestyle diseases have led to an upward trend in orthopedic surgeries, thereby fueling the market demand for these devices.
As a business owner in Delaware, staying on top of your tax obligations is paramount, especially with the annual deadline for Delaware Franchise Tax looming on March 1. One such obligation is the annual Delaware Franchise Tax, which serves as a crucial requirement for maintaining your company’s legal standing within the state. While the prospect of handling tax matters may seem daunting, rest assured that the process can be straightforward with the right guidance. In this comprehensive guide, we’ll walk you through the steps of filing your Delaware Franchise Tax and provide insights to help you navigate the process effectively.
Remote sensing and monitoring are changing the mining industry for the better. These are providing innovative solutions to long-standing challenges. Those related to exploration, extraction, and overall environmental management by mining technology companies Odisha. These technologies make use of satellite imaging, aerial photography and sensors to collect data that might be inaccessible or from hazardous locations. With the use of this technology, mining operations are becoming increasingly efficient. Let us gain more insight into the key aspects associated with remote sensing and monitoring when it comes to mining.
Taurus Zodiac Sign_ Personality Traits and Sign Dates.pptxmy Pandit
Explore the world of the Taurus zodiac sign. Learn about their stability, determination, and appreciation for beauty. Discover how Taureans' grounded nature and hardworking mindset define their unique personality.
Improving profitability for small businessBen Wann
In this comprehensive presentation, we will explore strategies and practical tips for enhancing profitability in small businesses. Tailored to meet the unique challenges faced by small enterprises, this session covers various aspects that directly impact the bottom line. Attendees will learn how to optimize operational efficiency, manage expenses, and increase revenue through innovative marketing and customer engagement techniques.
The world of search engine optimization (SEO) is buzzing with discussions after Google confirmed that around 2,500 leaked internal documents related to its Search feature are indeed authentic. The revelation has sparked significant concerns within the SEO community. The leaked documents were initially reported by SEO experts Rand Fishkin and Mike King, igniting widespread analysis and discourse. For More Info:- https://news.arihantwebtech.com/search-disrupted-googles-leaked-documents-rock-the-seo-world/
RMD24 | Debunking the non-endemic revenue myth Marvin Vacquier Droop | First ...BBPMedia1
Marvin neemt je in deze presentatie mee in de voordelen van non-endemic advertising op retail media netwerken. Hij brengt ook de uitdagingen in beeld die de markt op dit moment heeft op het gebied van retail media voor niet-leveranciers.
Retail media wordt gezien als het nieuwe advertising-medium en ook mediabureaus richten massaal retail media-afdelingen op. Merken die niet in de betreffende winkel liggen staan ook nog niet in de rij om op de retail media netwerken te adverteren. Marvin belicht de uitdagingen die er zijn om echt aansluiting te vinden op die markt van non-endemic advertising.
"𝑩𝑬𝑮𝑼𝑵 𝑾𝑰𝑻𝑯 𝑻𝑱 𝑰𝑺 𝑯𝑨𝑳𝑭 𝑫𝑶𝑵𝑬"
𝐓𝐉 𝐂𝐨𝐦𝐬 (𝐓𝐉 𝐂𝐨𝐦𝐦𝐮𝐧𝐢𝐜𝐚𝐭𝐢𝐨𝐧𝐬) is a professional event agency that includes experts in the event-organizing market in Vietnam, Korea, and ASEAN countries. We provide unlimited types of events from Music concerts, Fan meetings, and Culture festivals to Corporate events, Internal company events, Golf tournaments, MICE events, and Exhibitions.
𝐓𝐉 𝐂𝐨𝐦𝐬 provides unlimited package services including such as Event organizing, Event planning, Event production, Manpower, PR marketing, Design 2D/3D, VIP protocols, Interpreter agency, etc.
Sports events - Golf competitions/billiards competitions/company sports events: dynamic and challenging
⭐ 𝐅𝐞𝐚𝐭𝐮𝐫𝐞𝐝 𝐩𝐫𝐨𝐣𝐞𝐜𝐭𝐬:
➢ 2024 BAEKHYUN [Lonsdaleite] IN HO CHI MINH
➢ SUPER JUNIOR-L.S.S. THE SHOW : Th3ee Guys in HO CHI MINH
➢FreenBecky 1st Fan Meeting in Vietnam
➢CHILDREN ART EXHIBITION 2024: BEYOND BARRIERS
➢ WOW K-Music Festival 2023
➢ Winner [CROSS] Tour in HCM
➢ Super Show 9 in HCM with Super Junior
➢ HCMC - Gyeongsangbuk-do Culture and Tourism Festival
➢ Korean Vietnam Partnership - Fair with LG
➢ Korean President visits Samsung Electronics R&D Center
➢ Vietnam Food Expo with Lotte Wellfood
"𝐄𝐯𝐞𝐫𝐲 𝐞𝐯𝐞𝐧𝐭 𝐢𝐬 𝐚 𝐬𝐭𝐨𝐫𝐲, 𝐚 𝐬𝐩𝐞𝐜𝐢𝐚𝐥 𝐣𝐨𝐮𝐫𝐧𝐞𝐲. 𝐖𝐞 𝐚𝐥𝐰𝐚𝐲𝐬 𝐛𝐞𝐥𝐢𝐞𝐯𝐞 𝐭𝐡𝐚𝐭 𝐬𝐡𝐨𝐫𝐭𝐥𝐲 𝐲𝐨𝐮 𝐰𝐢𝐥𝐥 𝐛𝐞 𝐚 𝐩𝐚𝐫𝐭 𝐨𝐟 𝐨𝐮𝐫 𝐬𝐭𝐨𝐫𝐢𝐞𝐬."
Putting the SPARK into Virtual Training.pptxCynthia Clay
This 60-minute webinar, sponsored by Adobe, was delivered for the Training Mag Network. It explored the five elements of SPARK: Storytelling, Purpose, Action, Relationships, and Kudos. Knowing how to tell a well-structured story is key to building long-term memory. Stating a clear purpose that doesn't take away from the discovery learning process is critical. Ensuring that people move from theory to practical application is imperative. Creating strong social learning is the key to commitment and engagement. Validating and affirming participants' comments is the way to create a positive learning environment.
Business Valuation Principles for EntrepreneursBen Wann
This insightful presentation is designed to equip entrepreneurs with the essential knowledge and tools needed to accurately value their businesses. Understanding business valuation is crucial for making informed decisions, whether you're seeking investment, planning to sell, or simply want to gauge your company's worth.
1. Chapter 5
Centrifugal Casting of Metal Matrix Composites
Abstract There are three major types of centrifugal casting used for the infiltration
of molten metal into fibrous preforms. In this chapter, the infiltration of molten
metal into fibrous preforms using centrifugal force is discussed theoretically and the
predictions of the theory are compared with experimental results. We discuss
the rotational speed necessary for infiltration to start, the pressure distribution in
the preforms, the velocity of the infiltration front and other important parameters.
When the volume fraction of fibers is not high, the pressure necessary for the
infiltration of molten metal is low. This process is suitable for fabricating products
which are symmetrical around a rotational axis, and uses simple and economical
casting equipment. In addition to discussion of fibrous preforms, centrifugal casting
of molten metal including ceramic particles is also discussed, focusing on the
theory of the behavior of a ceramic particle in molten metal in the centrifugal
force field.
5.1 Infiltration of Molten Metal Using Centrifugal Force
If molten metal is rotated, centrifugal force will act on the molten metal. The force
increases radially from zero at the rotation center. This force generates pressure in
the molten metal, and the pressure increases with distance along the radius. This
pressure can be used to infiltrate molten metal into a porous preform made of
ceramic fibers or particles and thus produce composites [1–4].
In this process, when the volume fraction Vf of the preform is relatively low, the
pressure needed for infiltration is not high. The apparatus is simple and economical,
although the process is only suitable for the symmetrical products. However, when
Vf of the preform is high, a high rotation number is needed, and the apparatus
required to produce the rate will be large.
Y. Nishida, Introduction to Metal Matrix Composites: Fabrication and Recycling,
DOI 10.1007/978-4-431-54237-7_5, # Springer Japan 2013
91
2. 5.1.1 Pressure Generated at the Surface of Preform
There are three cases for the production of composites using centrifugal force as
shown in Fig. 5.1. In Case 1, the preform is shaped like a pipe. Infiltration begins
from the inner surface of the pipe. The infiltration front spreads to the outer surface
of the pipe along the rotation radius. In Case 2, the volume of the preform is very
small compared with the total volume of molten metal, and therefore the displace-
ment of the inner surface of molten metal is negligible during infiltration. This
means that the pressure generated on the inner surface of the preform is almost
constant throughout infiltration. In addition, as the cross-section of the preform in
Case 2 is constant, it is possible to apply a one-dimensional infiltration model to this
case. In Case 3, the hatched area outside the fan-shaped molten metal also presses
the preform, which means that the pressure generated in Case 3 is higher than in the
other two cases. Therefore, the pressure which acts on the preform surface depends
on the type of infiltration.
A good starting point to develop the theory of centrifugal casting is to consider
the infiltration of molten metal in the small angle a at the rotation center during
preform
preform
preform
container
container
container
molten metal
molten metal
molten metal
rotation center
rotation
center
rotation
center
A
a
b
c
Fig. 5.1 Three major cases
for the infiltration of molten
metal by centrifugal casting
92 5 Centrifugal Casting of Metal Matrix Composites
3. Case 1, as shown in Fig. 5.1a. The mass of this part is rmAdr and its acceleration is
o2
r. The centrifugal force, dFc, which acts on the region r to r + dr shown in
Fig. 5.1a, is given by:
dFc ¼ rmAo2
rdr; (5.1)
where rm is the density of the molten metal, A is the cross-sectional area of the fan-
shaped molten metal with small angle a, and o is the angular velocity (¼ 2pN,
where N is the number of revolutions per second or revolution number).
5.1.1.1 Case 1
Case 1 corresponds to Fig. 5.1a. By integration of Eq. (5.1) between r0 and r1, the
force, Fc, is obtained as:
Fc ¼
1
3
rmao2
ðr3
1 À r3
0Þ; (5.2)
where r0 and r1 are the locations of the inner surfaces of the molten metal and the
preform during rotation. The pressure P1, which acts on the inner surface of the
preform, is obtained by dividing Fc by the preform inner surface area ar1 at r ¼ r1.
When the infiltration of molten metal into the preform starts, the location of the
inner surface of the molten metal, rs(t), moves as shown in Fig. 5.2 and time-
dependent P1(t) during infiltration is given by:
P1ðtÞ ¼
1
3r1
rmo2
ðr3
1 À ðrsðtÞÞ3
Þ: (5.3)
We suppose that solidification of the molten metal does not occur during
infiltration and that the molten metal is an incompressible liquid. When the location
of the infiltration front in the preform once infiltration starts is rf (t), rs(t) is given by:
rsðtÞ ¼
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
r2
0 þ f ðrf ðtÞÞ2
À r2
1
n or
; (5.4)
preform
front
container
molten metal
rotation
center
Fig. 5.2 Locations of the
infiltration front and inner
surface of molten metal
during infiltration
5.1 Infiltration of Molten Metal Using Centrifugal Force 93
4. where f is the porosity of the preform (¼ 1 À Vf). Substitution of Eq. (5.4) into
Eq. (5.3) yields:
P1ðtÞ ¼
rmo2
3r1
r3
1 À fr2
0 þ fððrf ðtÞÞ2
À r2
1Þg
3=2
h i
: (5.5)
This is the pressure which is applied to the inner surface of the preform during
infiltration.
5.1.1.2 Case 2
Case 2 is shown in Fig. 5.1b. The volume of the preform is so small compared with
the whole volume of the molten metal that the volume change of molten metal is
negligible during infiltration. In this case, the location of the inner surface of the
molten metal does not move during infiltration. Therefore, the pressure P1(t) in
Eq. (5.3) is constant throughout infiltration, and by putting rs(t) ¼ r0 in Eq. (5.3),
P1(t) becomes:
P1ðtÞ ¼
1
3r1
rmo2
ðr3
1 À r3
0Þ: (5.6)
5.1.1.3 Case 3
This case is shown in Fig. 5.1c. The cross-section of the molten metal column is
constant and does not change with increasing r. In other words, as well as the fan-
shaped metal with angle a, the hatched part of the molten metal also presses against
the inner surface of the preform. By putting A ¼ constant in Eq. (5.1), the force
which acts on the inner surface of the preform is given by:
Fc ¼
1
2
rmAo2
ðr2
1 À r2
0Þ: (5.7)
In this case, as infiltration proceeds, the location of the inner surface of the liquid
column moves. When the location is rs(t), the time-dependent P1(t) is given by:
P1ðtÞ ¼
1
2
rmo2
fr2
1 À ðrsðtÞÞ2
g; (5.8)
and
rsðtÞ ¼ r0 þ fðrf ðtÞ À r1Þ: (5.9)
94 5 Centrifugal Casting of Metal Matrix Composites
5. Substituting Eq. (5.9) into Eq. (5.8), we obtain:
P1ðtÞ ¼
1
2
rmo2
½r2
1 À fr0 þ fðrf ðtÞ À r1Þg2
Š: (5.10)
5.1.2 Infiltration Start Pressure
The contact angle of a ceramic fiber with molten aluminum is usually higher than
90
. A certain pressure must be applied to the molten metal to induce infiltration. The
pressure is called the “threshold pressure”, and was discussed in detail in Chap. 3.
When the distribution of fibers is random, the threshold pressure Pc is given by:
Pc ¼ À
4Vf g cos y
df ð1 À Vf Þ
; (5.11)
where g is the surface energy of the molten metal, y is the contact angle and df is the
diameter of fibers. When P1(t) is smaller than Pc, infiltration cannot begin. The
minimum revolution number necessary for infiltration is given by Eqs. (5.12) and
(5.13):
N !
1
2p
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
3r1Pc
rmðr3
1 À r3
0Þ
s
ðfor Case 1 and Case 2Þ (5.12)
N !
1
2p
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
2Pc
rmðr2
1 À r2
0Þ
s
ðfor Case 3Þ (5.13)
5.1.3 Infiltration of Molten Metal into the Preform
Ignoring fluid inertial contributions and preform compression, the flow of the fluid
(molten metal) in the preform in the radial direction is governed by Darcy’s law in a
centrifugal force field [5, 6]:
@pðr; tÞ
@r
¼ À
mmuðr; tÞ
K
þ rmo2
r; (5.14)
5.1 Infiltration of Molten Metal Using Centrifugal Force 95
6. where p(r, t) is the pressure in the preform, mm is the viscosity of the molten metal, K
is the permeability, and u(r, t) is the radial superficial velocity which is the mass of
molten metal which flows into the preform per unit time and unit area.
5.1.3.1 Case 1
The continuity equation for the radial direction in cylindrical coordinates is given by:
rm
r
@fruðr; tÞg
@r
¼ 0: (5.15)
From Eq. (5.15), we obtain the following relationship:
ruðr; tÞ ¼ CðtÞ ði:e:; it is a function of time onlyÞ: (5.16)
Using Eq. (5.16), Eq. (5.14) is rewritten as:
@pðr; tÞ
@r
¼ À
mm
K
CðtÞ
r
þ rmo2
r: (5.17)
At a fixed time, it is possible to regard Eq. (5.17) as an ordinary differential
equation with respect to r. Then, we can obtain the following solution:
pðr; tÞ À P1ðtÞ ¼ À
fmmCðtÞ
K
ln
r
r1
þ
1
2
rmo2
ðr2
À r2
1Þ; (5.18)
where P1(t) is the pressure at r ¼ r1. As the pressure at r ¼ rf (t) (infiltration front)
is Pc (the threshold pressure):
Pc À P1ðtÞ ¼ À
fmmCðtÞ
K
ln
rf ðtÞ
r1
þ
1
2
rmo2
fðrf ðtÞÞ2
À r2
1g: (5.19)
Alternatively, we have the following relationship between infiltration front rf (t)
and the superficial velocity uf (t) at the front:
drf ðtÞ
dt
¼
uf ðtÞ
f
: (5.20)
If mm, K, rm and f are independent of t, substitution of Eqs. (5.16) and (5.19) into
Eq. (5.20) yields the following ordinary differential equation:
t ¼
ðrf ðtÞ
r1
mmf2
rf ðtÞ lnðrf ðtÞ=r1Þ
K½P1ðtÞ À Pc þ ð1=2Þrmo2fðrf ðtÞÞ2
À r2
1gŠ
drf ðtÞ: (5.21)
96 5 Centrifugal Casting of Metal Matrix Composites
7. It is difficult to obtain an analytical solution of this differential equation, but
numerical integration can be used.
The pressure distribution in the infiltrated region is obtained by substitution of C
(t) from Eq. (5.18) into Eq. (5.19):
pðr; tÞ ¼ P1ðtÞ À P1ðtÞ À Pc þ
1
2
rmo2
fðrf ðtÞÞ2
À r2
1g
lnðr=r1Þ
lnðrf ðtÞ=r1Þ
þ
1
2
rmo2
ðr2
À r2
1Þ (5.22)
Equation (5.22) gives the pressure distribution in the infiltrated region when the
infiltration front is located at position rf(t). This relationship shows that the pressure
is independent of f and K except for the threshold pressure Pc which depends on f.
When this process is applied industrially, the thickness of the preform is finite.
When the infiltration front reaches the outer surface of the preform (r ¼ rt), the
infiltration stops and the pressure distribution in the infiltrated region changes
instantaneously. Supposing that the framework of the fibrous preform is sufficiently
rigid and does not deform in the infiltrated region, the centrifugal force, dFc, which
acts on the metal of the region r to r + dr in the preform, is given by:
dFc ¼ frmAo2
rdr: (5.23)
When the preform thickness is L (¼ rt À r1), the pressure in the preform p(r) at r
(r1 r rt) is given by:
pðrÞ ¼
1
3r1
rmo2
½r3
1 À fr2
0 þ fðr2
t À r2
1Þg3=2
Š þ
1
3r
frmo2
ðr3
À r3
1Þ: (5.24)
When the amount of molten metal is small and all molten metal enters the
preform before the infiltration front arrives at the outer surface of the preform, the
pressure curve is given only by the second term of Eq. (5.24).
5.1.3.2 Case 2
This is the case where P1(t) is constant (¼ P0). The cross section of the preform is
independent of r and constant. Therefore, the superficial velocity u(r, t) in
Eq. (5.14) is also independent of r and expressed by u(t). The one-dimensional
form of the continuity equation, which applies in this situation, is:
@uðtÞ
@r
¼ 0: (5.25)
At a fixed time, it is also possible to regard Eq. (5.14) as an ordinary differential
equation with respect to r. Then, we can obtain the following solution:
5.1 Infiltration of Molten Metal Using Centrifugal Force 97
8. pðr; tÞ ¼ P0 À
mmuðtÞ
K
ðr À r1Þ þ
1
2
rmo2
ðr2
À r2
1Þ: (5.26)
As the pressure at the infiltration front r ¼ rf (t) is Pc, we obtain:
P0 ¼
mmuðtÞ
K
ðrf ðtÞ À r1Þ À
1
2
rmo2
fðrf ðtÞÞ2
À r2
1g þ Pc: (5.27)
Alternatively, the velocity of the infiltration front is given by:
drf ðtÞ
dt
¼
uðtÞ
f
: (5.28)
Substitution of u(t) from Eq. (5.28) into Eq. (5.27) yields an ordinary differential
equation:
m3 þ m4rf ðtÞ
m1 þ m2frf ðtÞg2
drf ðtÞ ¼ dt; (5.29)
where
m1 ¼ K P0 À Pc À
rmo2
r2
1
2
; m2 ¼
Krmo2
2
; m3 ¼ Àmmfr1; m4 ¼ mmf:
The solution of Eq. (5.29) depends on the sign (negative or positive) of m1.
However, since we know P0 from Eq. (5.6), m1 is always negative. Then, the
following solution is obtained:
t ¼ n1 lnfðrf ðtÞÞ2
À n2
3g þ n2 ln
rf ðtÞ À n3
rf ðtÞ þ n3
þ n4; (5.30)
where
n1 ¼
m4
2m2
; n2 ¼
m3
2
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
Àm2m1
p ; n3 ¼
ffiffiffiffiffiffiffiffiffiffi
À
m1
m2
r
; and
n4 ¼ Àn1 lnðr2
1 À n2
3Þ À n2 ln
r1 À n3
r1 þ n3
:
By substituting uðtÞ from Eq. (5.26) into Eq. (5.27), we obtain:
pðr; tÞ ¼
rf ðtÞ À r
rf ðtÞ À r1
P0 þ
1
2
rmo2
ðr À r1Þðr À rf ðtÞÞ þ Pc
r À r1
rf ðtÞ À r1
: (5.31)
This equation gives the pressure distribution in the infiltrated region when the
infiltration front is specified. The characteristic features of this equation are that the
equation does not include f, and that the pressure distribution pattern is
98 5 Centrifugal Casting of Metal Matrix Composites
9. independent of the volume fraction of fibers in the preform except for the depen-
dence of the threshold pressure, Pc, on f.
When the preform thickness is L, the pressure p(r) in the infiltrated region after
the infiltration front reaches the outer surface of the preform is given by:
pðrÞ ¼ P0 þ
1
2
frmo2
ðr2
À r2
1Þ; ðr1 r rtÞ: (5.32)
5.1.3.3 Case 3
This is the case shown in Fig. 5.1c. Since cross sectional variations can be neglected
because of the cylindrical configuration, the superficial velocity u(r, t) in Eq. (5.14)
is actually u(t) and the continuity equation in the one-dimensional form, Eq. (5.25),
should also be valid in this case. At a fixed time, it is possible to regard Eq. (5.14) as
an ordinary differential equation with respect to r, if mm, K and rm are independent
of r. Then, we can get the following solution:
pðr; tÞ ¼ P1ðtÞ À
mmuðtÞ
K
ðr À r1Þ þ
1
2
rmo2
ðr2
À r2
1Þ; (5.33)
where P1(t) is the pressure at r ¼ r1. As the pressure p(r, t) at r ¼ rf (t) in Eq. (5.33)
is the threshold pressure Pc, we obtain:
P1ðtÞ ¼
mmuðtÞ
K
ðrf ðtÞ À r1Þ À
1
2
rmo2
ððrf ðtÞÞ2
À r2
1Þ þ Pc: (5.34)
Substitution of Eqs. (5.10) and (5.28) into Eq. (5.34) provides an ordinary
differential equation, if mm, K, rm and f are independent of t. The solution is:
t ¼
1
2m3
ln fðrf ðtÞÞ2
þ m1rf ðtÞ þ m2g
rf ðtÞ þ m6
rf ðtÞ þ m5
m4
þ m7; (5.35)
where
m1 ¼
2fðfr1 À r0Þ
1 À f2
; m2 ¼
Àr2
0 À f2
r2
1 þ 2fr0r1 À 2Pc=ðrmo2
Þ
1 À f2
;
m3 ¼
rmo2
Kð1 À f2
Þ
2mmf
; m4 ¼
m1 þ 2r1
2
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
m2
1=4 À m2
p ; m5 ¼
1
2
m1 À
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
m2
1
4
À m2
r
;
m6 ¼
1
2
m1 þ
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
m2
1
4
À m2
r
; and m7 ¼ À
1
2m3
ln ðr2
1 þ m1r1 þ m2Þ
r1 þ m6
r1 þ m5
m4
5.1 Infiltration of Molten Metal Using Centrifugal Force 99
10. Equation (5.35) gives the relationship between the location of the infiltration
front rf (t) and time t.
Alternatively, by substituting Eq. (5.34) into Eq. (5.33), we obtain the
pressure distribution in the infiltrated region when the infiltration front is specified
at rf (t):
pðr; tÞ ¼
ðrf ðtÞ À rÞP1ðtÞ þ ðr À r1ÞPc
rf ðtÞ À r1
þ
1
2
rmo2
ðr À r1Þðr À rf ðtÞÞ: (5.36)
When the preform thickness is L (¼ rt À r1), the pressure in the preform after
infiltration reaches the outer surface of the preform is:
pðrÞ ¼
1
2
rmo2
r2
1 À r0 þ fðrt À r1Þf g2
h i
þ
1
2
frmo2
ðr2
À r1
2
Þ: (5.37)
5.1.4 Example Calculations
The relationship between Vf and the permeability of the preform is needed for the
calculation of infiltration. There are many theoretical equations for the permeability
of porous media [7]. Among them, Langmuir’s equation [Eq. (5.38)] which applies
to flow parallel to the fiber alignment and Happel’s equation [Eq. (5.39)] which
applies to flow normal to fibers can be used to obtain the permeability of the
preform. Generally the permeability calculated using these equations agrees well
with experimental results. The equations are:
K
R2
¼
1
4Vf
À ln Vf À
3
2
þ 2Vf À
1
2
Vf
2
; (5.38)
and
K
R2
¼
1
8Vf
À ln Vf þ
V2
f À 1
V2
f þ 1
!
; (5.39)
where R is the radius of the fiber. As the fiber distribution we used was random, the
permeability of the preform was obtained by averaging the values of permeability
calculated for flows parallel and normal to the fiber alignment.
5.1.4.1 Case 1
The advance of the infiltration front of molten aluminum (without solidification)
calculated using Eq. (5.21) is shown in Fig. 5.3. The calculation was performed for
100 5 Centrifugal Casting of Metal Matrix Composites
11. a preform made from alumina short fibers. The following data were also used in this
calculation: r0 ¼ 0.07 m, r1 ¼ 0.12 m, f (¼ 1 À Vf) ¼ 0.87, rm ¼ 2.38 Â 103
kg/
m3
, R (¼ df/2) ¼ 1.85 Â 10À6
m, g ¼ 0.893 Pa m, y ¼ 160
and mm ¼ 0.984 Â 10
À3
Pa s. The minimum revolution number N for the infiltration is 19.74 rev/s, as
calculated from Eq. (5.12). Figure 5.3 shows that if the revolution rate is slightly
higher than the minimum value, infiltration will be continuous. The pressure
distribution in the infiltrated region obtained from Eq. (5.22) is shown in Fig. 5.4
for N ¼ 50 rev/s. The pressure distribution curves are convex towards lower
pressures, because the second derivative of Eq. (5.22) is always positive and
Fig. 5.3 Relationship between infiltrated distance and time for a range of rotational speeds for
Case 1
Fig. 5.4 Change with time of pressure distribution in the infiltrated region for Case 1 when
N ¼ 50 rev/s
5.1 Infiltration of Molten Metal Using Centrifugal Force 101
12. proportional to o2
. The preform surface pressure decreases quickly as the infiltra-
tion advances, and the intermediate part of the pressure distribution curve falls
below the threshold pressure. Nevertheless, infiltration continues, because the
threshold pressure is needed only to wet fibers with molten metal, and the pressure
at the infiltration front always remains constant at the threshold pressure. After
wetting, the molten metal does not separate from the preform, even if the pressure
becomes lower than the threshold pressure, unless enough work for the separation is
supplied to the molten metal/fiber interface.
When the preform thickness is L and the infiltration front reaches the location r
(t) (the outer surface of the preform), the pressure distribution curve shown in
Fig. 5.4 for N ¼ 50 rev/s is changed instantaneously to that of Fig. 5.5. Only the
preform surface pressure remains constant, and the pressure in the infiltrated region
rises quickly and becomes stable. In this calculation, in the cases of L ¼ 0.04 and
0.05 m, all liquid metal enters into the preform and a cavity is formed near the inner
surface of the preform, because of the lack of liquid metal.
5.1.4.2 Case 2
Figure 5.6 shows the relationship between time and the advance of the infiltration front
obtained from Eq. (5.30). The front advances faster than in Case 1, because the
preform surface pressure remains constant throughout the infiltration. The pressure
distribution curves are shown in Fig. 5.7 for N ¼ 50 rev/s. The pressure distribution
curves in this case are also convex toward lower pressure, because the second
derivative of Eq. (5.31) is also positive and proportional to o2
. The pressure distribu-
tion curves for finite preform thickness cases are shown in Fig. 5.8 for N ¼ 50 rev/s. In
Case 2, even if the preform thickness is different, the pressure distribution curve is the
same, and the curve depends only on the revolution number.
Fig. 5.5 Pressure distribution in the infiltrated region for Case 1 after the infiltration front reaches
the outer surface of the preform when N ¼ 50 rev/s
102 5 Centrifugal Casting of Metal Matrix Composites
13. 5.1.4.3 Case 3
Figure 5.9 shows the relationship between time and the advance of the infiltration
front obtained from Eq. (5.35) for Case 3. The front advances faster than in Case 1
and slower than in Case 2 for a particular revolution number. The pressure distri-
bution curves obtained from Eq. (5.36) are shown in Fig. 5.10 for N ¼ 50 rev/s.
These curves are also convex toward lower pressure. Regions having lower pressure
than the threshold pressure appeared at t ¼ 0.163 s in Fig. 5.10. The pressure
Fig. 5.6 Relationship between infiltrated distance and time for a range of rotational speeds for
Case 2
Fig. 5.7 Change with time of pressure distribution in the infiltrated region for Case 2 when
N ¼ 50 rev/s
5.1 Infiltration of Molten Metal Using Centrifugal Force 103
14. distribution curves obtained using Eq. (5.37) are shown in Fig. 5.11 for various
finite preform thickness at N ¼ 50 rev/s. Until the infiltration front arrives at the
outer surface of the preform, the preform surface pressure changes as given in
Fig. 5.10. When the front arrives at the preform outer surface, the change in the
preform surface pressure stops and the pressure distribution in the infiltrated region
becomes that shown in Fig. 5.11.
Fig. 5.8 Pressure distribution in the infiltrated region for Case 2 after the infiltration front reaches
the outer surface of the preform when N ¼ 50 rev/s
Fig. 5.9 Relationship between infiltrated distance and time for a range of rotational speeds for
Case 3
104 5 Centrifugal Casting of Metal Matrix Composites
15. 5.1.5 Examples of Composites Fabricated Using
Centrifugal Force
In this section we summarize a previous study where the feasibility of centrifugal
force for the infiltration of molten metal into preforms was examined and the
composites obtained were characterized [8]. A schematic of the apparatus used is
Fig. 5.10 Change with time of pressure distribution in the infiltrated region for Case 3 when
N ¼ 50 rev/s
Fig. 5.11 Pressure distribution in the infiltrated region for Case 3 after the infiltration front
reaches the outer surface of the preform when N ¼ 50 rev/s
5.1 Infiltration of Molten Metal Using Centrifugal Force 105
16. shown in Fig. 5.12. A preheated graphite container with a uniform cross section was
used. The container was balanced by a counterweight. A preheated alumina short
fiber preform was set on the bottom of the container which was rotated. When the
rotational speed reached the target value, molten pure aluminum was poured into a
pouring device concentric with the rotation shaft and a composite was produced.
The experimentally obtained relationship between the rotational speed and the
infiltrated distance for different volume fractions of fiber and initial preform
thickness is shown in Fig. 5.13. The diameter for the preform was 24 mm, and
the initial thicknesses of the preforms were 20 mm for Vf ¼ 6 %, 19 mm for
Vf ¼ 9 %, and 18 mm for Vf ¼ 13 %. The infiltrated distances for Vf ¼ 6 % and
preform
graphite container
graphite pipe
pouring device
Fig. 5.12 Schematic of the apparatus used to generate centrifugal force for the infiltration of
aluminum
Fig. 5.13 Relationship between the pressure generated and infiltrated distance. The initial
thicknesses of the preforms are 20 mm for Vf ¼ 6 %, 19 mm for Vf ¼ 9 %, and 18 mm for
Vf ¼ 13 %. The compressive deformation of preforms is neglected
106 5 Centrifugal Casting of Metal Matrix Composites
17. 9 % were either zero or 100 %. That is, in the case of Vf ¼ 6 %, infiltration did not
advance at 65 kPa (N ¼ 10 rev/s) but fully advanced at 70 kPa (N ¼ 11 rev/s). For
Vf ¼ 9 %, infiltration did not take place at 70 kPa (N ¼ 16 rev/s), but occurred fully
at 85 kPa (N ¼ 17 rev/s). For Vf ¼ 13 %, the molten metal advanced a little and
then stopped at 160 kPa (N ¼ 26 rev/s), but advanced much further at 230 kPa
(N ¼ 32 rev/s). Since the preheat temperatures of the preform and graphite con-
tainer were 703 and 673 K, respectively, the infiltration velocity was slow in this
case and the metal solidified during infiltration. Pressure higher than 300 kPa was
needed for full infiltration for the Vf ¼ 13 % preform.
The structural characteristics of samples are presented in Figs. 5.14 and 5.15.
A partially infiltrated sample with Vf ¼ 13 % is also shown in Fig. 5.14. The
preform also contained many particles, because the quality of the alumina/silica
fibers was not high. The minimum pressures for the start of infiltration were
obtained from this experiment and are listed in Table 5.1, along with the threshold
pressure values calculated theoretically using Eq. (5.11). Both sets of values are in
agreement.
Fig. 5.14 Macrostructures of alumina/silica short fiber reinforced aluminum composite samples
fabricated using centrifugal force
5.1 Infiltration of Molten Metal Using Centrifugal Force 107
18. 5.2 Centrifugal Casting of Particle Dispersed Molten Metal
When molten metal which contains ceramic particles is cast in a centrifugal force
field, the particles tend to segregate because of the density difference between the
molten metal and the ceramic particles. Here, we discuss the movement of the
particles and the forces which act on the particles. To simplify the model, solidifi-
cation will be neglected.
A particle having density rp and radius Rp is present in molten metal having
density rm. The centrifugal force, which is proportional to the rotating radius r, is
acting on the particle. The equation for the force, Fc, which acts on the particle as a
result of the acceleration, o2
r is similar to Eq. (5.1):
Fc ¼
4
3
pR3
pðrp À rmÞo2
r: (5.40)
If the particle moves with very low velocity in the molten metal, as shown in
Fig. 5.16, Stokes’ drag formula will be applicable [9]. The viscous drag is given by:
Fv ¼ À6pmmRp
dr
dt
; (5.41)
where Fv acts on the particle in the opposite direction to the centrifugal force, and
has a negative sign. mm is the viscosity of the molten metal.
The fundamental expression of the movement of an object is: [force] ¼ [mass]
 [acceleration]. For the particle, the total force is Fc + Fv. Thus, we obtain the
following differential equation:
Fig. 5.15 Microstructure of alumina/silica short fiber reinforced aluminum composites fabricated
using centrifugal force
Table 5.1 Comparison of threshold pressures
Vf (%) Pc (kPa) (theoretical) Pc (kPa) (experimental)
6 57.9 66
9 89.7 81
13 135.6 156
108 5 Centrifugal Casting of Metal Matrix Composites
19. 4
3
pR3
pðrp À rmÞo2
r À 6pmmRp
dr
dt
¼
4
3
pR3
prp
d2
r
dt2
: (5.42)
Gravity is neglected, because the gravity is much smaller than the centrifugal force.
The solution of Eq. (5.42), i.e., the location of the particle as a function of time, is:
r ¼ r0 exp
À9mm þ
ffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffiffi
81m2
m þ 16ðrp À rmÞrpR4
po2
q
4Rprp
8
:
9
=
;
t
2
4
3
5; (5.43)
where r0 is the initial location of the particle. The solution is a simple exponential
function. If the particle goes far away from the rotating center, the velocity of the
particle will increase and Stokes’ drag formula (equation (5.41)) will be invalid,
because the formula is only valid when the Reynolds number around the particle is
less than 0.5.
Examples of calculations using Eq. (5.43) are shown in Figs. 5.17 and 5.18. In these
calculations, the particle is a spherical SiC particle with density rp ¼ 3.15 Â 103
kg/m3
; the density rm of the molten aluminum is 2.38 Â 103
kg/m3
and the viscosity
of the molten aluminum mm ¼ 0.948 Â 10À3
Pa s. Figure 5.16 shows the movement
with time of particles with different radii, Rp, when the revolution number N is 10 rev/s.
Equation(5.43)givesthedimensionlessdisplacementratioofthelocationoftheparticle
to its initial location r/r0, which represents the movement of the particle. When the
particle radius is 1 mm (i.e., the diameter is 2 mm), the particle quickly moves away
from the rotating center. However, when the particle radius is 0.1 mm, the particle will
move slowly. Figure 5.17 shows the displacement ratio, r/r0 of a particle of radius
0.1 mm, for different revolution numbers N. When N ¼ 5 rev/s, the particle essentially
remainsatitsinitiallocationfortheentire300s.However,whenNislargerthan15rev/s
(900 rpm), the particle moves quickly.
However, Eq. (5.43) is quite different to “Stokes’ law” which gives:
dz
dt
¼
2R2
pðrp À rLÞg
9mL
; (5.44)
Fc
Fv
Rp
particle
Fig. 5.16 Viscous drag, Fv,
and centrifugal force, Fc,
which act on a particle during
centrifugal casting of particle
reinforced molten metal
5.2 Centrifugal Casting of Particle Dispersed Molten Metal 109
20. where g is the gravitational acceleration, rL and mL are the density and viscosity of
the fluid, respectively. The z-axis is taken as the gravity direction. In this equation,
the acceleration is constant, although it is o2
r in the centrifugal force field.
In actual centrifugal casting, solidification of metal occurs along with the
movement of particles. The solidification in this case is very complicated and it is
very difficult to analytically calculate the behavior, because solidification depends
Fig. 5.18 Curves of displacement ratio r/r0 with time for various values of revolution number N;
particle radius is 0.1 mm
Fig. 5.17 Curves of displacement ratio r/r0 with time for various particle radii; revolution number
N is 10 rev/s
110 5 Centrifugal Casting of Metal Matrix Composites
21. on the shape of container (mold), the composition of the alloy and on other factors.
In addition, Eq. (5.43) is the model of the movement for a single particle only.
When the number of particles is large, we should consider the interaction between
particles. Then, the apparent viscosity mapp must be used instead of the real viscosity
of the molten metal; the apparent viscosity increases when the number of particles
increases, and is given by [10]:
mapp ¼ mmð1 þ
5
2
Vf þ 10:05V2
f Þ: (5.45)
This mapp can then be used instead of mm in Eq. (5.43).
Centrifugal casting with solidification in the presence of solid particles was
discussed numerically by Panda et al. [11]. They showed that the segregation of
particles in the alumina particles/aluminum or silicon carbide particles/aluminum
systems depends on the size of particle, rotational speed, heat transfer coefficient at
the casting/mold interface and volume fraction of particles.
Examples of the application of centrifugal casting to composites include copper
alloy/graphite particle composites, which were developed by Kim et al. to improve
tribological properties of the inner surfaces of products [12]. Functionally graded
composites were also developed in TiB2 or TiC particles/aluminum alloy systems
by Kumar et al. [13].
References
1. Sugishita, J.: Fabrication and properties of centrifugally cast surface composites based on
Al-11%Si alloy. J. Jpn. Foundry Eng. Soc. 57, 102–107 (1985)
2. Tsunekawa, Y., Okumiya, M., Niimi, I., Yoneyama, K.: Centrifugally cast aluminum matrix
composites containing segregated alumina fibers. J. Mater. Sci. Lett. 7, 830–832 (1988)
3. Tsunekawa, Y., Okumiya, M., Niimi, I., Maeda, T.: Improvement of bending strength in
aluminum alloy matrix composites containing short alumina fibers by centrifugal force.
J. Jpn. Inst. Light Met. 40, 7–12 (1990)
4. Nishida, Y., Ohira, G.: Modelling of infiltration of molten metal in fibrous preform by
centrifugal force. Acta Mater. 47, 841–852 (1999)
5. Geiger, G.H., Poirier, D.R.: Transport Phenomena in Metallurgy, p. 48. Addison-Wesley,
Reading (1980)
6. Collins, R.E.: Flow of Fluids Through Porous Materials. Reinhold Publishing Corp, New York
(1961)
7. Jackson, G.W., James, D.F.: The permeability of fibrous porous media. Can. J. Chem. Eng. 64,
364–374 (1986)
8. Nishida, Y., Shirayanagi, I., Sakai, Y.: Infiltration of fibrous preform by molten aluminum in a
centrifugal force field. Metall. Mater. Trans. 27A, 4163–4169 (1996)
9. Geiger, G.H., Poirier, D.R.: Transport Phenomena in Metallurgy, p. 71. Addison-Wesley,
Reading (1980)
10. Schowalter, W.R.: Mechanics of Non-Newtonian Fluids, p. 288. Pergamon, London (1978)
References 111
22. 11. Panda, E., Mehrotra, S.P., Mazumdar, D.: Mathematical modeling of particle segregation
during centrifugal casting of metal matrix composites. Metall. Mater. Trans. 37A,
1675–1687 (2006)
12. Kim, J.K., Kestursatya, M., Rohatgi, P.K.: Tribological properties of centrifugally cast copper
alloy-graphite particle composite. Metall. Mater. Trans. 31A, 1283–1293 (2000)
13. Kumar, S., Sarma, V.S., Murty, B.S.: Functionally graded alloy matrix in situ composites.
Metall. Mater. Trans. 41A, 242–254 (2010)
112 5 Centrifugal Casting of Metal Matrix Composites