This document provides information on Carbothane 133 HB, an aliphatic acrylic-polyester polyurethane coating. It has excellent resistance to corrosion, chemicals and abrasion. It can be applied by spray, brush or roller and provides very good weathering performance in a broad range of colors. The document outlines the product features, specifications, surface preparation requirements, application details, performance test results and curing times.
TinSil® 70-Series Silicone Elastomers are two-component,
room temperature curing mold rubbers. TinSil silicone elastomers are
condensation-cure, tin-catalyzed systems that cure to flexible rubbers.
TinSil molds have high tear strength, excellent chemical resistance,
good release properties and resistance to high temperatures. These
molds are a great choice for casting polyesters, epoxy and polyurethane
resins, polyurethane foams, plaster, waxes and many other materials.
TinSil® 70-Series Silicone Elastomers are two-component,
room temperature curing mold rubbers. TinSil silicone elastomers are
condensation-cure, tin-catalyzed systems that cure to flexible rubbers.
TinSil molds have high tear strength, excellent chemical resistance,
good release properties and resistance to high temperatures. These
molds are a great choice for casting polyesters, epoxy and polyurethane
resins, polyurethane foams, plaster, waxes and many other materials.
TinSil® 70-Series Silicone Elastomers are two-component,
room temperature curing mold rubbers. TinSil silicone elastomers are
condensation-cure, tin-catalyzed systems that cure to flexible rubbers.
TinSil molds have high tear strength, excellent chemical resistance,
good release properties and resistance to high temperatures. These
molds are a great choice for casting polyesters, epoxy and polyurethane
resins, polyurethane foams, plaster, waxes and many other materials.
TinSil® 70-Series Silicone Elastomers are two-component,
room temperature curing mold rubbers. TinSil silicone elastomers are
condensation-cure, tin-catalyzed systems that cure to flexible rubbers.
TinSil molds have high tear strength, excellent chemical resistance,
good release properties and resistance to high temperatures. These
molds are a great choice for casting polyesters, epoxy and polyurethane
resins, polyurethane foams, plaster, waxes and many other materials.
Poly 74-Series Polyurethane Rubbers consist of two
parts (A and B), which, after mixing, cure at room temperature to
flexible, high-strength, mold rubbers. Poly 74-Series Rubbers make
durable, easy-releasing molds for casting plasters and waxes without
release agents. When Poly 74-Series molds are properly prepared, they
are also excellent for casting concrete and various resins, such as epoxy,
polyester, polyurethane and acrylic
How to reduce hot forging costs through innovative techniques?Srikar Shenoy
This presentation gives successful industrial case studies of cost reduction in hot forging by the use of:
1. Anti-scale protective coatings to prevent rejections due to scaling, reduce or eliminate shot blasting, reduce decarburization in heat treatment, hot rolling and hot forging.
2. Environment friendly die lubricants that eliminate pollution and increase die life.
3. Zero maintenance die lubricant spraying systems that ensure maximum uptime and no unplanned downtime during hot forging.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Momentive has launched two new products, ECC3011 and ECC3051S conformal coatings that can withstand harsh operating conditions, helping to prevent the occurrence of corrosion on vital PCB components and surfaces.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses
in different formats.
Dental waxes/certified fixed orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
Dental waxes are among the routine laboratory materials used in dentistry. For successful lab procedures it is necessary to amplify the material knowledge.
Poly 74-Series Polyurethane Rubbers consist of two
parts (A and B), which, after mixing, cure at room temperature to
flexible, high-strength, mold rubbers. Poly 74-Series Rubbers make
durable, easy-releasing molds for casting plasters and waxes without
release agents. When Poly 74-Series molds are properly prepared, they
are also excellent for casting concrete and various resins, such as epoxy,
polyester, polyurethane and acrylic
How to reduce hot forging costs through innovative techniques?Srikar Shenoy
This presentation gives successful industrial case studies of cost reduction in hot forging by the use of:
1. Anti-scale protective coatings to prevent rejections due to scaling, reduce or eliminate shot blasting, reduce decarburization in heat treatment, hot rolling and hot forging.
2. Environment friendly die lubricants that eliminate pollution and increase die life.
3. Zero maintenance die lubricant spraying systems that ensure maximum uptime and no unplanned downtime during hot forging.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Momentive has launched two new products, ECC3011 and ECC3051S conformal coatings that can withstand harsh operating conditions, helping to prevent the occurrence of corrosion on vital PCB components and surfaces.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses
in different formats.
Dental waxes/certified fixed orthodontic courses by Indian dental academy Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
Dental waxes are among the routine laboratory materials used in dentistry. For successful lab procedures it is necessary to amplify the material knowledge.
Antala Distribuidor oficial de Molykote, líder mundial en tecnología de lubricación.
http://www.antala.com/product/MOLYKOTE
La gama de lubricantes especiales MOLYKOTE® es líder mundial en tecnología de lubricación con más de 60 años de experiencia, pioneros en incorporar el bisulfuro de molibdeno puro (MoS2) en los lubricantes, nació la tecnología de la lubricación inteligente, Smart Lubrication™ Technology, creando productos específicos para soportar cargas elevadas, altas y bajas temperaturas de trabajo, suciedad y polvo, ambientes químicos agresivos y velocidades extremas.
Estas soluciones de lubricación ayudan al control de la fricción y el desgaste aumentando la fiabilidad de los equipos, generando ahorros de energía y costes, reduciendo las emisiones de CO2 y prolongando los intervalos de lubricación en los ciclos de mantenimiento.
Pastas Lubricantes: Alta concentración de lubricantes sólidos dispensados en aceite
Grasas Industriales: Dispersión de un agente espesante en un alto porcentaje de aceite
Compounds: Lubricante de silicona con poder sellante
Aceites Especiales: aceite de base sintética
Dispersiones: Porcentage bajo de sólido lubricante en aceite
Recubrimientos anti-fricción AFC: Barníz con partículas de sólido lubricante micronizado
http://www.antala.com/product/MOLYKOTE
PT Flex products are two-component, fast-setting
polyurethane rubbers that cure at room temperature (RTV). Available
in a variety of hardnesses, these products are excellent for prototyping
and model making applications and for the casting of production parts,
props, tools, and more.
Car Park Flooring - Maris Polymers - Maripur 7100Orfeas Aggelou
Car park coating is very important. Car Parking otherwise called car park is a challenging surfacing job. Car park coating in car parks must provide a highly durable, abrasion resistant, hard-elastic, anti skid and esthetic surface, capable of withstanding long term vehicular traffic.
The MARIPUR® SYSTEM is the technologically advanced, premium liquid polyurethane car park coating system that offers easy application, high durability, quick curing times and most importantly guaranteed long lasting results. Read more about parking flooring.
StarCompliance is a leading firm specializing in the recovery of stolen cryptocurrency. Our comprehensive services are designed to assist individuals and organizations in navigating the complex process of fraud reporting, investigation, and fund recovery. We combine cutting-edge technology with expert legal support to provide a robust solution for victims of crypto theft.
Our Services Include:
Reporting to Tracking Authorities:
We immediately notify all relevant centralized exchanges (CEX), decentralized exchanges (DEX), and wallet providers about the stolen cryptocurrency. This ensures that the stolen assets are flagged as scam transactions, making it impossible for the thief to use them.
Assistance with Filing Police Reports:
We guide you through the process of filing a valid police report. Our support team provides detailed instructions on which police department to contact and helps you complete the necessary paperwork within the critical 72-hour window.
Launching the Refund Process:
Our team of experienced lawyers can initiate lawsuits on your behalf and represent you in various jurisdictions around the world. They work diligently to recover your stolen funds and ensure that justice is served.
At StarCompliance, we understand the urgency and stress involved in dealing with cryptocurrency theft. Our dedicated team works quickly and efficiently to provide you with the support and expertise needed to recover your assets. Trust us to be your partner in navigating the complexities of the crypto world and safeguarding your investments.
1. Carbothane
®
133 HB
July 2015 0840
To the best of our knowledge the technical data contained herein is true and accurate on the date of publication and is subject to change without prior notice. User must contact Carboline Company
to verify correctness before specifying or ordering. No guarantee of accuracy is given or implied. We guarantee our products to conform to Carboline quality control. We assume no responsibility for
coverage, performance or injuries resulting from use. Liability, if any, is limited to replacement of products. NO OTHER WARRANTY OR GUARANTEE OF ANY KIND IS MADE BY CARBOLINE,
EXPRESS OR IMPLIED, STATUTORY, BY OPERATION OF LAW, OR OTHERWISE, INCLUDING MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE. Carboline® and Carboguard®
are registered trademarks of Carboline Company.
Page 1 of 3
Selection & Specification Data
Generic Type Aliphatic Acrylic-Polyester Polyurethane
Description High build, low sheen finish that has excellent
resistance to corrosion, chemicals and abrasion.
Suitable for application over a number of Carboline
primers and intermediates, this material provides very
good weathering performance in a broad range of
colors.
Features • Outstanding performance properties in both mild
and aggressive environments
• High build; suitable for many two-coat systems
• Suitable for application direct to inorganic zincs
• Application by spray, brush or roller
• Indefinite recoatability
• VOC compliant to current AIM regulations
Color Refer to Carboline Color Guide. Certain colors may
require multiple coats to hide.
Finish Satin
Primer Refer to Substrates & Surface Preparation.
Topcoat with Carbothane® Clear Coat when required.
Dry Film
Thickness
3.0 - 5.0 mils (76 - 127 microns) per coat
Dry film thickness in excess of 7 mils (175 microns) per coat is not
recommended.
Solids Content By Volume 57% +/- 2%
Theoretical
Coverage Rate
914 ft
2
at 1.0 mils (22.4 m
2
/l at 25 microns)
305 ft
2
at 3.0 mils (7.5 m
2
/l at 75 microns)
183 ft
2
at 5.0 mils (4.5 m
2
/l at 125 microns)
Allow for loss in mixing and application.
VOC Values Thinner 214 3.3 lbs/gal (403 g/l)
Thinner 241 3.5 lbs/gal (423 g/l)
Thinner 25 11 oz/gal: 3.5 lbs./gal (420 g/l)
Thinner 25 18 oz/gal: 3.7 lbs./gal (449 g/l)
As Supplied 3.2 lbs./gal (383 g/l)
1.5 oz/gal of Additive 101 adds 0.08 lbs/gal (10 g/l). These are nominal
values and may vary slightly with color.
Dry Temp.
Resistance
Continuous: 200 °F (93 °C)
Non-Continuous: 250 °F (121 °C)
Discoloration and loss of gloss is observed above 200°F (93°C)
Limitations *The alignment of aluminum flakes in aluminum-
filled finishes is very dependent on application
conditions and techniques. Care must be taken to
keep conditions as constant as possible to reduce
variations in final appearance. It is also advisable to
work from a single batch of material since variations
can occur from batch to batch.
Substrates & Surface Preparation
General Surfaces must be clean and dry. Employ adequate
methods to remove dirt, dust, oil and all other
contaminants that could interfere with adhesion of
the coating. Refer to the specific primer’s Product
Data Sheet for detailed requirements of the specified
primer.
Steel SSPC-SP6 with a 1.5-2.5 mil (37.5-62.5 micron)
surface profile for maximum protection. SSPCSP2
or SP3 as minimum requirement. Prime with specific
Carboline primers as recommended by your Carboline
sales representative.
Galvanized Steel Prime with specific Carboline primers as
recommended by your Carboline Sales
Representative. Refer to the specific primer’s Product
Data Sheet for substrate preparation requirements.
Aluminum SSPC-SP1 and prime with appropriate Carboline
primer as recommended by your Carboline sales
representative.
Previously Painted
Surfaces
Lightly sand or abrade to roughen and degloss the
surface. Existing paint must attain a minimum 3A
rating in accordance with ASTM D3359 “XScribe”
adhesion test. Prime with specific Carboline
primers as recommended by your Carboline sales
representative.
2. Carbothane
®
133 HB
July 2015 0840
To the best of our knowledge the technical data contained herein is true and accurate on the date of publication and is subject to change without prior notice. User must contact Carboline Company
to verify correctness before specifying or ordering. No guarantee of accuracy is given or implied. We guarantee our products to conform to Carboline quality control. We assume no responsibility for
coverage, performance or injuries resulting from use. Liability, if any, is limited to replacement of products. NO OTHER WARRANTY OR GUARANTEE OF ANY KIND IS MADE BY CARBOLINE,
EXPRESS OR IMPLIED, STATUTORY, BY OPERATION OF LAW, OR OTHERWISE, INCLUDING MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE. Carboline® and Carboguard®
are registered trademarks of Carboline Company.
Page 2 of 3
Performance Data
Test Method System Results
ASTM B117 Salt Fog Blasted Steel 1 ct.
IOZ 1 ct. 133 HB
No rusting, or
blistering on plane or
scribe 2,000 hours
ASTM B117 Salt Fog Blasted Steel 1 ct.
OZ 1 ct. 133 HB
No rusting, or
blistering on plane or
scribe 4,000 hours
ASTM D1735 Water Fog Blasted Steel 1 ct.
Epoxy 1 ct. 133 HB
No rusting or blistering
after 8600 hours.
ASTM D4213
Scrub Resistance
1 ct. 133 HB .0027 microliters
erosion rate after
100 cycles with
abrasive scrub medium.
ASTM D4585 Humidity Blasted Steel 1 ct.
IOZ 1 ct. 133 HB
No rusting or blistering
after 3000 hours.
ASTM D5894
QUV A Prohesion
1 ct. 133 HB No effect on plane area
and 78% gloss retention
after 1008 hours of
wet/dry salt fog cycle
ASTM G26
Weatherometer
Blasted Steel 1 ct
IOZ 1 ct. 133 HB
No blistering,
rusting or cracking
after 3500 hours
ASTM G53 QUV (2500
hours w/ UVA 340 bulb)
Blasted Steel 1 ct.
Epoxy 1 ct. 133 HB
Color change less
than 2 McAdam units;
no blistering, rusting,
cracking or chalking.
Graffiti Resistance Blasted Steel 1 ct.
Epoxy 1 ct. 133 HB
All markings and stains
removed by solvent
after exposure to:
shoe polish,Sharpie
marker, crayon, l
Test reports and additional data available upon request.
Mixing & Thinning
Mixing Power mix Part A separately, then combine with Part
B and power mix. DO NOT MIX PARTIAL KITS.
Thinning Spray: Up to 11 oz/gal (9%) w/ Thinner 25.
Roller: Up to 18 oz/gal (14%) w/ Thinner 25.
Use of thinners other than those supplied or
recommended by Carboline may adversely affect
product performance and void product warranty,
whether expressed or implied. Thinner 214 may also
be used, up to 6 oz/gal, for either spray or brush/roller
application. Carboline Thinner 236E may also be used
to minimize HAP and VOC emissions.
Ratio 6:1 Ratio (A to B)
.88 Gal. Kit
Part A: 1 gal. can (partial filled)
UC 133: 1 pint
5.0 Gal. Kit
Part A: 5 gal. can (partial filled)
UC 133: 1 gallon can (partial filled)
Pot Life 4 Hours at 75°F (24°C) and less at higher
temperatures. Pot life ends when coating becomes too
viscous to use. MOISTURE CONTAMINATION WILL
SHORTEN POT LIFE AND CAUSE GELLATION.
Application Equipment Guidelines
Listed below are general equipment guidelines for the application of this product. Job site conditions
may require modifications to these guidelines to achieve the desired results.
Conventional
Spray
Pressure pot equipped with dual regulators
3/8” I.D. minimum material hose
.070” I.D. fluid tip and appropriate air cap
Airless Spray Pump Ratio: 30:1 (min.)*
GPM Output: 3.0 (min.)
Material Hose: 3/8” I.D. (min.)
Tip Size: .013-.015”
Output PSI: 2100-2300
Filter Size: 60 mesh
*Teflon packings are recommended and available from
the pump manufacturer.
Brush & Roller
(General)
Multiple coats may be required to obtain desired
appearance, recommended dry film thickness and
adequate hiding. Avoid excessive re-brushing or
rerolling. For best results, tie-in within 10 minutes at
75°F (24°C).
Brush Recommended for touch-up only. Use a medium,
natural bristle brush.
Roller Use a medium-nap synthetic roller cover with phenolic
core.
Spray Application
(General)
This is a high solids coating and may require
adjustments in spray techniques. Wet film thickness
is easily and quickly achieved. The following spray
equipment has been found suitable and is available
from manufacturers such as Binks, DeVilbiss and
Graco.
Application Conditions
Condition Material Surface Ambient Humidity
Minimum 40 °F (4 °C) 40 °F (4 °C) 40 °F (4 °C) 0%
Maximum 100 °F (38 °C) 110 °F (43 °C) 110 °F (43 °C) 90%
Industry standards are for substrate temperatures to be 5°F (3°C) above the dew point. This product
simply requires the substrate temperature to be above the dew point.
Caution: This Product is moisture sensitive in the liquid stage and until cured. Protect from high
humidity, dew and direct moisture contact until cured. Application and/or curing in humidities
above maximum, or exposure to moisture from rain or dew may result in a loss of gloss and/or
microbubbling of the product.
Curing Schedule
Surface Temp.
& 50% Relative
Humidity
Dry to Handle Dry to Recoat Final Cure
General
40 °F (4 °C) 20 Hours 20 Hours 28 Days
50 °F (10 °C) 12 Hours 12 Hours 14 Days
75 °F (24 °C) 5 Hours 5 Hours 7 Days
90 °F (32 °C) 1 Hours 1 Hours 4 Days
These times are based on a 3.0-5.0 mil (75-125 micron) dry film thickness. Higher film thickness,
insufficient ventilation or cooler temperatures will require longer cure times and could result in
solvent entrapment and premature failure.
*Maximum recoat times are indefinite. Surface must be clean and dry. As part of good painting
practice it is recommended to test for adhesion by wiping the surface with Thinner 25. If the film
shows a slight "tack" the surface is suitable for recoating without extensive surface preparation such
as abrading.
Carboline Additive 101 can be used to accelerate the film forming process in this product for
conditions outside of the parameters of this data sheet. Carboline Additive 101 is added at a rate
of 1.0-2.0 oz per mixed gallon or a maximum of 6 oz per mixed five gallons. At this addition rate,
Additive 101 will accelerate the cure rate of the urethane product between 25-40% depending on the
substrate temperature range and reduce the pot life of the product by approximately 40-50% of that
stated on the product data sheet. With the use of Additive 101, this product will continue to cure at
temperatures as low as 20°F (-7°C).
3. Carbothane
®
133 HB
July 2015 0840
To the best of our knowledge the technical data contained herein is true and accurate on the date of publication and is subject to change without prior notice. User must contact Carboline Company
to verify correctness before specifying or ordering. No guarantee of accuracy is given or implied. We guarantee our products to conform to Carboline quality control. We assume no responsibility for
coverage, performance or injuries resulting from use. Liability, if any, is limited to replacement of products. NO OTHER WARRANTY OR GUARANTEE OF ANY KIND IS MADE BY CARBOLINE,
EXPRESS OR IMPLIED, STATUTORY, BY OPERATION OF LAW, OR OTHERWISE, INCLUDING MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE. Carboline® and Carboguard®
are registered trademarks of Carboline Company.
Page 3 of 3
Cleanup & Safety
Cleanup Use Thinner 2 or Acetone. In case of spillage, dispose
of in accordance with local applicable regulations.
Safety Read and follow all caution statements on this product
data sheet and on the MSDS for this product and use
personal protective equipment as directed.
Ventilation When used in enclosed areas, thorough air circulation
must be used during and after application until the
coating is cured. The ventilation system should be
capable of preventing the solvent vapor concentration
from reaching the lower explosion limit for the solvents
used. User should test and monitor exposure levels to
insure all personnel are below guidelines. If not able to
monitor levels, use MSHA/NIOSH approved supplied
air respirator.
Packaging, Handling & Storage
Shelf Life Part A: Min. 36 months at 75°F (24°C)
Part B: Min. 24 months at 75°F (24°C)
*Shelf Life: when kept at recommended storage conditions and in
original unopened containers.
Shipping Weight
(Approximate)
.875 Gallon Kit - 11 lbs. (5 kg)
5 Gallon Kit - 64 lbs. (29 kg)
Storage
Temperature &
Humidity
40° -110°F (4°-43°C)
0-90% Relative Humidity
Flash Point
(Setaflash)
Part A: 95°F (35°C)
Part B: 91°F (33°C)
Storage Store Indoors.
This product is solvent based and not affected by excursions below
these published storage temperatures, down to 10°F, for a duration of no
more than 14 days. Always inspect the product prior to use to make sure
it is smooth and homogeneous when properly mixed.