This document discusses the optimization of polysulfone-based ultrafiltration membranes prepared through phase inversion. It examines how various preparation parameters, such as the concentration of the polysulfone dope solution, the solvent used, temperature, and pressure, affect the properties of the resulting membranes, including water flux and pore size. The key findings are that increasing the concentration of the dope solution or the temperature used decreases water flux by reducing pore size and porosity, while increasing pressure leads to higher water flux linearly according to Fick's law. Bubble point tests also indicate that higher dope solution concentrations produce membranes with smaller pore sizes. Overall, the study shows how preparation parameters can be optimized to control membrane properties for various separation applications.
Episode 65 : Membrane separation processes
Membrane separation consists of different process operating on a variety of physical
principles and applicable to a wide range of separations of miscible components
These methods yield only a more concentrated liquid stream than feed. Membrane
separation processes have several advantages. These include :
Low energy alternative to evaporation in concentrating a dilute feed, particularly when the desired material is thermally labile or when the desired component is a clear liquid
The chemical and mechanical stresses on the product are minimal and since no phase change is involve the energy requirement is modest
Product concentration and purification can be achieved in a single step and the
selectivity towards the desired product is good
The method can easily be scaled up
In bioprocess industry, membrane separation is widely used because of the mild operating conditions and low energy requirements in the recovery of lactose from whey, separation of immiscible components such extracellular products (
e.g. proteins, enzymes etc) and biomass.
Membrane separation process cannot be used for feeds containing a high concentration of low molecular weight components because of high osmotic pressure or when the feed has high solid content(>25% w/v) because of pumping problems
SAJJAD KHUDHUR ABBAS
Ceo , Founder & Head of SHacademy
Chemical Engineering , Al-Muthanna University, Iraq
Oil & Gas Safety and Health Professional – OSHACADEMY
Trainer of Trainers (TOT) - Canadian Center of Human
Development
MICROSPONGE: A NOVEL APPROACH IN GASTRO-RETENTION DRUG DELIVERY SYSTEM (GRDDS)Snehal Patel
Oral controlled release dosage forms face several physiological restriction like inability to retain and position the controlled drug delivery system within the targeted region of the gastrointestinal tract (GIT) due to fluctuation in gastric emptying. This results in non‑uniform absorption pattern, inadequate medication release and shorter residence time of the dosage form in the stomach. As the fallout of this episode there is inadequate absorption of the drug having absorption window predominantly, in the upper area of GIT. These contemplations have provoked to the development of oral controlled release dosage forms with gastroretentive properties. Microsponge hold certification as one of the potential approaches for gastric retention. Microsponge are porous spherical empty particles without core and can remain in the gastric region for delayed periods. They significantly increase the gastric residence time of medication, thereby enhance bioavailability, improves patient compliance by reducing dosing frequency, lessen the medication waste, enhance retention of medication which solubilize only in stomach, enhance solubility for medications that are less soluble at a higher pH environment. In the present review method of preparation, characterization, advantages, disadvantages and applications of floating microsponge are discussed. Please cite
Episode 65 : Membrane separation processes
Membrane separation consists of different process operating on a variety of physical
principles and applicable to a wide range of separations of miscible components
These methods yield only a more concentrated liquid stream than feed. Membrane
separation processes have several advantages. These include :
Low energy alternative to evaporation in concentrating a dilute feed, particularly when the desired material is thermally labile or when the desired component is a clear liquid
The chemical and mechanical stresses on the product are minimal and since no phase change is involve the energy requirement is modest
Product concentration and purification can be achieved in a single step and the
selectivity towards the desired product is good
The method can easily be scaled up
In bioprocess industry, membrane separation is widely used because of the mild operating conditions and low energy requirements in the recovery of lactose from whey, separation of immiscible components such extracellular products (
e.g. proteins, enzymes etc) and biomass.
Membrane separation process cannot be used for feeds containing a high concentration of low molecular weight components because of high osmotic pressure or when the feed has high solid content(>25% w/v) because of pumping problems
SAJJAD KHUDHUR ABBAS
Ceo , Founder & Head of SHacademy
Chemical Engineering , Al-Muthanna University, Iraq
Oil & Gas Safety and Health Professional – OSHACADEMY
Trainer of Trainers (TOT) - Canadian Center of Human
Development
MICROSPONGE: A NOVEL APPROACH IN GASTRO-RETENTION DRUG DELIVERY SYSTEM (GRDDS)Snehal Patel
Oral controlled release dosage forms face several physiological restriction like inability to retain and position the controlled drug delivery system within the targeted region of the gastrointestinal tract (GIT) due to fluctuation in gastric emptying. This results in non‑uniform absorption pattern, inadequate medication release and shorter residence time of the dosage form in the stomach. As the fallout of this episode there is inadequate absorption of the drug having absorption window predominantly, in the upper area of GIT. These contemplations have provoked to the development of oral controlled release dosage forms with gastroretentive properties. Microsponge hold certification as one of the potential approaches for gastric retention. Microsponge are porous spherical empty particles without core and can remain in the gastric region for delayed periods. They significantly increase the gastric residence time of medication, thereby enhance bioavailability, improves patient compliance by reducing dosing frequency, lessen the medication waste, enhance retention of medication which solubilize only in stomach, enhance solubility for medications that are less soluble at a higher pH environment. In the present review method of preparation, characterization, advantages, disadvantages and applications of floating microsponge are discussed. Please cite
Dissolution Enhancement of BCS Class 4 Dssrugs Using Quality by Design Approa...inventionjournals
Solid dispersion is one of the vastly accepted and practically economical processes in bioavailability enhancement study. The present investigation deals mostly with increase in solubility and dissolution rate of BCS class 4 drugs for enhancement of oral bioavailability. For the same solid dispersion were prepared and analyzed for appropriate concentration of drug polymer ratio by phase solubility analysis. The solvent evaporation study widely accepted due to its efficient solid dispersion in lesser efforts. The study designs were prepared with specific concentration of drug and polymer ratio with the help of high throughput model i.e. Central Composite Design (by Design Expert trial copy) by specific design of experiment with full factorial design (DOE). The fixed variables were concentration of polymers and dependant variables were dissolution and permeability across bio-membrane in in-vitro model. The prepared dispersion investigated for dissolution and permeability improvement using USP Type II apparatus and modified everted gut sac model which leads to improvement of quality of whole formulation with Quality by design efficiently.
microencapsulation is the part of an pharmaceutics, in that the method of preperation is giving. and all related thing about microencapsulation is given.
thanks you.
Dissolution Enhancement of BCS Class 4 Dssrugs Using Quality by Design Approa...inventionjournals
Solid dispersion is one of the vastly accepted and practically economical processes in bioavailability enhancement study. The present investigation deals mostly with increase in solubility and dissolution rate of BCS class 4 drugs for enhancement of oral bioavailability. For the same solid dispersion were prepared and analyzed for appropriate concentration of drug polymer ratio by phase solubility analysis. The solvent evaporation study widely accepted due to its efficient solid dispersion in lesser efforts. The study designs were prepared with specific concentration of drug and polymer ratio with the help of high throughput model i.e. Central Composite Design (by Design Expert trial copy) by specific design of experiment with full factorial design (DOE). The fixed variables were concentration of polymers and dependant variables were dissolution and permeability across bio-membrane in in-vitro model. The prepared dispersion investigated for dissolution and permeability improvement using USP Type II apparatus and modified everted gut sac model which leads to improvement of quality of whole formulation with Quality by design efficiently.
microencapsulation is the part of an pharmaceutics, in that the method of preperation is giving. and all related thing about microencapsulation is given.
thanks you.
Presentazione Reflex - Convegno Viessmann, Lodi 23 aprile 2015Viessmann Italia
Reflex è partner di Viessmann per la realizzazione di impianti efficienti e di qualità.
Le soluzioni Reflex: vasi di espansione, sistemi di degasazione e separazione, serbatoi, sistemi di trattamento acqua.
Synthesis, Evaluation, Modeling and Simulation of Nano-Pore NAA Zeolite Membr...antjjournal
ABSTRACT
Zeolite membranes have uniform and molecular-sized pores that separate molecules based on the differences in the molecules’ adsorption and diffusion properties. Strong electrostatic interaction between ionic sites and water molecules (due to its highly polar nature) makes the zeolite NaA membrane very hydrophilic. Zeolite NaA membranes are thus well suited for the separation of liquid-phase mixtures by
pervaporation. In this study, experiments were conducted with various Ethanol–water mixtures (1–20 wt. %) at 25 °C. Total flux for Ethanol–water mixtures was found to vary from 0.331 to 0.229 kg/m2 .h with increasing Ethanol concentration from 1 to 20 wt.%. Ionic sites of the NaA zeolite matrix play a very important role in water transport through the membrane. These sites act both as water sorption and transport sites. Surface diffusion of water occurs in an activated fashion through these sites. The precise Nano-porous structure of the zeolite cage helps in a partial molecular sieving of the large solvent
molecules leading to high separation factors. A comparison between experimental flux and calculated flux using Stephan Maxwell (S.M.) correlation was made and a linear trend was found to exist for water flux through the membrane with Ethanol concentration. A comprehensive model also was proposed for the Ethanol/water pervaporation (PV) by Finite Element Method (FEM). The 2D model was masterfully capable of predicting water concentration distribution within both the membrane and the feed side of the pervaporation membrane module.
KEYWORDS
Nano pores; Pervaporation; Ethanol separation; Zeolite NaA membrane; FEM simulation
SYNTHESIS, EVALUATION, MODELING AND SIMULATION OF NANO-PORE NAA ZEOLITE MEMBR...antjjournal
Zeolite membranes have uniform and molecular-sized pores that separate molecules based on the
differences in the molecules’ adsorption and diffusion properties. Strong electrostatic interaction between
ionic sites and water molecules (due to its highly polar nature) makes the zeolite NaA membrane very
hydrophilic. Zeolite NaA membranes are thus well suited for the separation of liquid-phase mixtures by
pervaporation. In this study, experiments were conducted with various Ethanol–water mixtures (1–20 wt.
%) at 25 °C. Total flux for Ethanol–water mixtures was found to vary from 0.331 to 0.229 kg/m2
.h with
increasing Ethanol concentration from 1 to 20 wt.%. Ionic sites of the NaA zeolite matrix play a very
important role in water transport through the membrane. These sites act both as water sorption and
transport sites. Surface diffusion of water occurs in an activated fashion through these sites. The precise
Nano-porous structure of the zeolite cage helps in a partial molecular sieving of the large solvent
molecules leading to high separation factors. A comparison between experimental flux and calculated flux
using Stephan Maxwell (S.M.) correlation was made and a linear trend was found to exist for water flux
through the membrane with Ethanol concentration. A comprehensive model also was proposed for the
Ethanol/water pervaporation (PV) by Finite Element Method (FEM). The 2D model was masterfully
capable of predicting water concentration distribution within both the membrane and the feed side of the
pervaporation membrane module.
OPTUM® Technology an innovative barrier solution for polypropylene-based mate...José Luis Feijoo
Ferro, a leading supplier of specialty plastics, has recently developed OPTUM® Barrier masterbatch for a wide range of polymers. This can be incorporated by melt processing in most of the manufacturing processes involved in the developing of single and multi-layer structures in flexible and rigid packaging. In particular this is suitable for food packaging applications in order to increase product protection and shelf-life. Barrier applications can be found, however, in other in market segments such as cosmetics, industrial containers and agricultural films, where barrier to oxygen and other gases is also critical.
IJERA (International journal of Engineering Research and Applications) is International online, ... peer reviewed journal. For more detail or submit your article, please visit www.ijera.com
We present a micro fluidic device that allows rapid and defined delivery of discrete and homogeneous reagents or samples to allow kinetic studies of surface-tethered biomolecules. We developed an Electro Osmotic Flow (EOF) based device consisting of an asymmetric Y-junction with an incorporated fast, pressure driven valve, two embedded measurement electrodes and reservoirs. The EOF is used to circumvent kinetic limitations on reagent transport to the surface of these tethered biomolecules due to the slow diffusion across parabolic concentration gradients in conventional pressure-driven flow devices. Using Fluorescein isothiocyanate (FITC) as the pH sensitive surface-immobilized biomolecules, we show that the reagent solution can be repeatedly exchanged within milliseconds, and that by using a synchronized triggering scheme we can monitor the reaction of our sensor biomolecules to the change of the environment on a time scale of 10ms.
This presentation discusses the measurement of PFCs in drinking and tap water using LC-MS/MS. As contaminants of emerging concern, research on PFCs is ongoing to determine the impacts of these materials on human health and the environment. Perfluorinated compounds can be effectively and quickly measured directly from surface and drinking water using a modified configuration of the LCMS-8050. For more information, go to ssi.shimadzu.com and follow Shimadzu on Twitter @ShimadzuSSI. Thanks for viewing.
Foam fractionation as a means to recover and fractionate bioactiveseSAT Journals
Abstract In this research, the optimum conditions for the separation of polyphenols from apple juice (AJ) and the separation of BSA from a BSA/water solution were found by looking at the enrichment ratio (ER) and recovery. A mixture of the AJ and BSA was also studied to see how the different conditions affect separation of either compound. For AJ only, maximum ER was achieved at a feed concentration of 0.00184mg/mL of polyphenols (10.9˚Brix), air flowrate of 10mL/min, pH of 6.03 and temperature of 4.1˚C. For the BSA only solution, maximum ER was achieved at a feed concentration of 2.5g/L, air flowrate of 7mL/min, pH of 5-6 and temperature either above or below 20˚C. For the mixture, maximum polyphenol ER was at a feed polyphenol concentration of 0.0018mg/mL, feed BSA concentration of 5g/L and a pH of 3.7. Whereas maximum BSA ER was achieved when the feed polyphenol concentration was again 0.00184mg/mL, but a minimum was seen at 5g/L BSA feed concentration and pH of 3.7. These results show that there are interactions between the polyphenol and proteins that affects the separation of compounds. The bubble size distribution and gas hold-up of the AJ and BSA solutions were then compared and the BSA solution had larger bubbles present and a greater gas hold-up, which is attributed to the greater surface activity of BSA protein. Finally basic modelling – linear regression, was performed to link the ER to the different conditions tested. The models were judged by comparing R2 values, the F-statistic and the p-value and all showed weak relationships between the ER and the independent variables. Further data is required to improve the model as from previous literatures these variables have been seen to contribute to adsorption, which in turn affects the ER.
Foam fractionation as a means to recover and fractionate bioactives
ART201673
1. International Journal of Science and Research (IJSR)
ISSN (Online): 2319-7064
Index Copernicus Value (2013): 6.14 | Impact Factor (2015): 6.391
Volume 5 Issue 6, June 2016
www.ijsr.net
Licensed Under Creative Commons Attribution CC BY
Polysulfone based Ultrafiltration Membrane
Preparation by Phase Inversion: Parameter
Optimization
*Jayant S. Phale1
, Dr. Yogesh J. Chendake2
1, 2
Department of Chemical Engineering, Bharati Vidyapeeth University, College of Engineering, Pune, India – 411043
Abstract: Polysulfone based ultrafiltration (UF) membranes are contemplated to be one of the most important separation material
with large benefits of hydrolytic stability, chemical resistance, high strength, creep resistance etc. Due to these benefits it can be applied
in diversified applications of gas separation, food and beverage processing, electro paint recovery, etc. PSF membranes are applicable
in wide range of filtration spectra from microfiltration (MF) to reverse osmosis (RO). Optimization of membrane porosity and pore size
are very difficult due to unstable solutions. Hence optimization of PSF membrane formation based upon effect of affecting parameters
during phase inversion based membrane preparation is done. The concentration of dope solution, solvent of preparation of dope
solution and other operating parameters such as humidity, temperature, pressure, etc. strongly affect membrane properties. The
decreasing trend of concentration of doped solution is witnessed with the increase in the water flux. Additionally, the parabolic relation
between the temperature and water flux through the membrane is noted to the extent of 60°C where is starts shrinking. A linear
increase in bubble point with increase in concentration of dope solution used for preparation of membranes shows that membrane pore
size and porosity reduces with increasing solution concentrations. The study shows various parameters affecting PSF based UF
membrane preparation parameters, with wide range of separation applications with distinctive features.
Keywords: Polysulfone membrane, casting parameters, solution concentration, solvent, phase inversion, water flux
1. Introduction
Over the last three decades, the use of porous polymer
membranes has achieved a significant position in separation
operations [1]
. Phase inversion is one of the most substantial
techniques for synthesizing porous polymer membrane [2]
.
Numerous parameters such as mechanical strength, water
flux, pH resistance etc. are observed to be the influencing
factors in membrane properties and applicability [4]
. There is
always a tradeoff between selectivity and transport rate. An
increase in pore size would lead to increase in the flux but
molecular weight cut off of the porous membrane would be
higher [5]
. This would lead to passage of undesired molecules
and thus affecting desired selectivity. There is need of careful
optimization of porosity and pore size for desired transport
properties. Pore size and porosity are important factor in any
membrane, pore size related to separation and porosity
governs the flux through membrane [6]
. Pore size and porosity
vary according to casting condition of membrane. Casting
condition, non solvent, polymer solution, solvent plays an
important role in membrane preparation.
Polysulfone is the paramount material for synthesis of porous
polymer membrane. Polysulfone are amorphous
thermoplastics consist of aromatic units (phenylenes)
subtended with Sulfone, isopropylidene or ether moieties[7],
[8]
. It has exemplary hydrolytic stability, chemical resistance,
high strength and generous agency certifications make these
polymers congruous for membranes used in stringent end-use
environments [9]
. Conventional application areas involve
pharmaceutical production, water purification, wastewater
treatment, and blood purification along with a range of
industrial process separations, such as electro paint recovery,
food and beverage processing, and gas separation [9],[10]
.
Sulfone polymers endeavor a unique combination of
characteristics for membrane filtration applications. They can
endure a variety of sterilization techniques, including gamma,
steam, e-beam, and ethylene oxide. They can be readily
transformed into UF and MF hollow fiber and flat sheet
membranes with extraordinarily controllable pore size
distribution. Additionally, they evince very high creep
resistance, mechanical strength and stable at pH levels from
3–13, outstanding biocompatibility, good resistance to
moderate concentrations of chlorine, outstanding hydrolytic
stability and caustic resistance, low levels of extractable and
insoluble materials, and global agency approvals [9]
. Phase
inversion is the mechanism by which PSF membrane can be
synthesized using solvent Dimethylacetamide,
methylpyrrolidone, dimethylformamide; with water as non
solvent [11], [12]
. The usually used solvent was
dimethylformamide [13], [14], [15]
. PSF has its own shortcoming
such as it is hydrophobic in nature which causes the fouling.
In PSF polymeric membranes, there is need of increasing
rejection, transport rate, and reducing the molecular weight
cut off [16].
In the presented work we plan to optimize the PSF membrane
casting parameter to enhance permeation properties. Casting
parameter such as humidity, temperature, concentration,
pressure, polymer solution, use of non solvent would be
varied to optimize membrane properties for application in
waste water treatment, water purification, and purification of
component.
2. Experimentation
2.1 Materials
PSF polymer synthesis grade (average molecular weight
30000Da) material in pallet purchased from Otto Chemei
Paper ID: ART201673 2569
2. International Journal of Science and Research (IJSR)
ISSN (Online): 2319-7064
Index Copernicus Value (2013): 6.14 | Impact Factor (2015): 6.391
Volume 5 Issue 6, June 2016
www.ijsr.net
Licensed Under Creative Commons Attribution CC BY
Pvt. Ltd. India. Dimethylacetamide (DMAc) (synthesis
grade) obtained from Loba Chemei Pvt Ltd India was used as
solvent for solution preparation. Water was used as non
solvent.
2.2 Solution Preparation
The dope solutions for membrane casting were prepared
using DMAc as solvent. Weighed quantity of vacuum dried
PSF was added to the solvent containing vessel under
constant stirring. The solution was stirred continuously for
more than 48 hr, to insure complete dissolution of DMAc
without containing any swollen particle. It was degassed
using probe Sonicator and used as dope solution for
membrane casting.
2.3 Membrane Casting
Flat sheet PSF membranes were prepared by automatic
membrane casting machine. Prepared solution was poured on
membrane casting plate. It was spread on flat glass sheet
surface by doctor knife. It was air dried for predetermine
time and dipped in water smoothly. The knife clearance,
knife speed and air dry time was maintained carefully by
using programmable casting setup. Obtained membranes
were preserved under formalin at 4°C, till further use. The
membranes were cut into circular coupons of 50 mm
diameter and used for further analysis.
2.4 Water flux analysis
The water flux of membranes was measured at one bar
pressure using distilled water in Amicon type dead end
stirring cell. Schematic of UF cell is given in figure (1). The
membranes were mounted on the base of cell filled with 150
ml of distilled water. Water flux was measured after passage
of 50 ml water at one bar pressure. The stirring speed as 300
rpm was maintained using magnetic stirrer with rpm
indicator. The variation in water flux with pressure was
analyzed from 0.5 bar to 3.0 bar at an interval of 0.5 bar each
show in the (figure 3)
Figure 1: Schematic Diagram for Ultrafiltration Cell
Figure 2: Actual Photograph of Ultrafiltration Cell
Figure 3: Effect of Pressure on Water Flux
2.4 Effect of Temperature
The effect of temperature on membrane morphology was
analyzed by treating the membranes with distilled water for
various temperatures from 30 – 60 °C. The membrane
coupons based on 21% PSF dope solutions were kept in the
distilled water at predetermined temperature for one hr and
then analyzed for water permeation (Figure 4).
Figure 4: Effect of Temperature on Water Flux
2.5 Effect of Concentration
The effect of dope solution concentration on water flux
through the membrane was analyzed by treating the different
concentration dope solution (15, 17, 19 and 21%) based
Paper ID: ART201673 2570
3. International Journal of Science and Research (IJSR)
ISSN (Online): 2319-7064
Index Copernicus Value (2013): 6.14 | Impact Factor (2015): 6.391
Volume 5 Issue 6, June 2016
www.ijsr.net
Licensed Under Creative Commons Attribution CC BY
membrane. These membranes were analyzed for water flux at
one bar pressure (Figure 5).
Figure 5: Effect of Dope Solution Concentration on
Permeate Water Flux
2.6 Bubble point analysis
The membrane coupons mounted in Amicon cell with little
water on surface. Air was used as second fluid. The air
pressure was increased at the rate 0.2 bar. After each pressure
increase a time of half hr was allowed to pass the air and then
pressure was increased. This was done up till constant air
flow rate was obtained.
3. Result and Discussion
3.1 Selection of Materials
Polysulfone are amorphous thermoplastics comprised of
aromatic units (phenylenes) link with Sulfone, isopropylidene
or ether moieties [9]
. Polysulfone has the highest
concentration of Sulfone moieties in the polymer repeating
unit. The structure gives Polysulfone the highest water
absorption of all commercial Sulfone polymers, making it the
most hydrophilic Sulfone polymer [9]
.
Polysulfone offer a unique combination of features for
membrane filtration applications. They can withstand a
variety of sterilization techniques, including steam, gamma,
e-beam, and ethylene oxide [15]
. They can be readily formed
into MF and UF hollow fiber and flat sheet membranes with
highly controllable pore size distribution. They exhibit
following property such as very high mechanical strength and
creep resistance, Stable at pH levels from 3 – 13, outstanding
hydrolytic stability and caustic resistance, good resistance to
moderate concentrations of chlorine, low levels of extractable
and insoluble materials, outstanding biocompatibility and
global agency approvals.
It is soluble in polar solvents such as dimethylformamide
(DMF), Dimethylacetamide (DMAC) and N-methyl-2-
pyrrolidone (NMP) and water is non-solvent for the same [17]
.
This makes PSF as material of choice for preparation of
membranes.
Dimethylacetamide was used as solvent for membrane
preparation because it is easily available in major quantity,
possibility of using water as non-solvent. Though PSF
membranes were prepared with DMF as solvent [14]
, these
solutions were unstable nature at high concentration [17]
. This
inability of high solution concentration generated need for
alternative solvent which would allow high concentration
solution. Presence high concentration would lead to dense
surface layer and membranes with lower pore size. This
would lead to membranes with desired rejection analysis but
result in decrease of permeation flux, transport resistance and
increase in concentration of solution.
Effect of dope solution Concentration on permeates Water
Flux Selection of solvent plays an important consideration in
solution preparation. It is important to select a solvent with
high purity and minimal water content. When using a solvent
recovery system, monitor solvent purity regularly and ensure
that the recycling system is working properly. To optimize
solution viscosity, select the most appropriate molecular
weight polymer in order to tightly control the process
parameters. High molecular weight polymers lead to high
viscosity solutions and take longer to dissolve however; a
higher molecular weight may be required to ensure adequate
strength of the nascent membrane during processing as well
as the finished membrane during use.
During preparation of polymer solution, slowly add the
polymer to the solvent while agitating. Adding it too quickly
can lead to the formation of aggregates that will take longer
to dissolve. The geometry of the stirrer, the agitation rate,
and the temperature all affect the time needed to dissolve the
polymer.
It can be seen from the (Figure 5); the water flux was
decreased exponential with increase in dope solution. This
would be due to decrease in pore size and lower porosity of
membrane due to increase in solution concentration. This
lower pore size and porosity increases the resistance for
water transport through membrane [10]
.This increase in
resistance would result in lower permeate flux through the
membranes. Similar reduction in flux with increase in dope
solution concentration has been reported in literature [20]
. The
water flux reduced exponentially from 88 LMH to 7 LMH
for 15 and 21 % dope solution concentration, respectively.
The reduction in flux can be said to be a sign of reduction in
pore size and porosity depending upon dope solution
concentration. This lower pore size would reduce MWCO.
This interrelation between pore size and dope solution
concentration would be highly important while designing a
membrane for specific separation operation, where specific
pore size would help for better balance in membrane
rejection properties and permeate flux.
3.2 Effect of driving pressure on water transport rate
The real life application would require use of membranes for
treatment of process streams at different pressures. Use of
membranes at high pressures might damage the pores of
Paper ID: ART201673 2571
4. International Journal of Science and Research (IJSR)
ISSN (Online): 2319-7064
Index Copernicus Value (2013): 6.14 | Impact Factor (2015): 6.391
Volume 5 Issue 6, June 2016
www.ijsr.net
Licensed Under Creative Commons Attribution CC BY
membranes. This is known as compaction of membranes [17]
.
Hence the stability and effect of pressure on transport rate for
various membranes is used [18]
. The membranes prepared
with 15 % PSF dope solution were analyzed for effect of
pressure on permeate flux. The trans-membrane pressure was
increased from 0.5 bar to 3.0 bar. The permeate flux was
increased linearly from 89 LMH to 472 LMH. This linear
increase is according to Fick’s law, which states linear
variation in transport rate with driving force [20], [22]
. This
variation shows that membranes are stable without any
damage to pores. Thus membranes have excellent mechanical
stability and no compaction even at lower solution
concentration. With increase in dope solution concentration
the amount of polymer in solution would increase mechanical
support for the pores of membranes and thus the stability
would increase [23]
. This shows prepared membranes have
excellent mechanical stability.
3.2 Effect of Temperature on Water flux
The real life application would require use of membranes at
varying temperature. Exposure to such temperatures might
affect membrane properties. Hence the membranes prepared
with 21 % dope solution were analyzed for variation in
properties after exposure to temperature of 30, 40, 50 and 60
°C, respectively; for one hour. The temperatures were chosen
are room temperature in Indian conditions and above those.
These membranes showed linear increase in permeate flux
with increase in treatment temperature from 30 to 50 °C. This
might realign the polymer chains and change the pore size of
membranes. Such realign and increase in pore size would
increase the transport rate of membrane [13]
. Though this
realignment have positive effect on transport rate, but the
increase in pore size would increase the MWCO which is
unwanted while rejection properties are concerned.
Continuous exposure of the membranes to high temperature
would damage the membranes and have undesired effect on
their transport properties.
At temperature of 60°C, the membranes showed shrinking.
This makes them useless for application at this temperature.
This showed PSF based membranes should be used at
temperatures of 50°C or lesser. Damage to polymer
structures at high temperatures is well reported [20], [24], [25]
.
3.4 Bubble Point Test
The bubble point is analyzed to determine pore size or
presence of unusually large pores in membranes. The
analysis was carried out using air-water system. The wetted
membranes were mounted on cell and air flow rate was
measured. A linear increase in bubble point with increase in
dope solution concentration used for preparation of
membranes was observed. This variation shows formation of
proper membranes without any defect. The linear increase in
bubble point shows that the membranes are becoming tighter
or the maximum pore size of the membranes in decreasing
linearly with increase in dope solution concentration. This
resulted in higher bubble point. Such lower pore size would
result in lower MWCO, which is required for higher rejection
properties. This is supported by reduction in permeate flux.
Figure (7): Effect of Bubble Point Analysis on
Concentration
4. Conclusions
Various parameters affect formation of PSF membranes.
Major effect is solvent used for solution preparation. A
variation in solvent from DMF to DMAc makes the dope
solution stable at higher concentration. This also changes
gelation mechanism and varying its surface properties. In this
research, formation of PSF based UF membrane is made
possible with the phase inversion technique by casting
mechanism. The characterization of these membranes for
assorted parameters such as temperature, concentration,
water flux, bubble point and pressure stability, etc. has been
analyzed. Furthermore, the optimization of these process
parameters are observed for numerous treads among them. It,
therefore proposed that the PSF based UF membrane will
have an extensive scope for further research in future, by
varying the solvent for dope solution.
Acknowledgements
Authors are thankful to management of Bharti Vidyapeeth
University, College of Engineering, Pune (India) for their
support towards setting of membrane laboratory. Also we
would like to thank TEQIP-II for financing of Institute
Funded Research Project Scheme, under which we could
generate research facilities used for current project.
References
[1] Baker, R.W., “Membrane Technology and
Applications”, 2nd ed., John Wiley & Sons Ltd. (2004).
[2] Genn I., Kuypers S., Leysen R., “Effect of the addition
of ZrO2 to polysulfone based UF membranes”, J
Membr. Sci.113 (1996) 247-258.
[3] Vandezande, P., Li, X., Gevers, E.M.L. and
Vankelecom, F.J.I. “High throughput study of phase
inversion parameters for polyimide based SRNF
membranes”, J. Membr. Sci.330 (2009) 307 – 318.
[4] Ghosh A. K. and Hoek E.M.V., “Impacts of support
membrane structure and chemistry on polyamide-
polysulfone interfacial composite membranes”, J.
Membr. Sci. 336 (2009)140-8.
[5] Ma Y., Shi F., Ma J., Wu W., Zang J., Gao C., “Effect of
PEG additive on morphology and performance of
Paper ID: ART201673 2572
5. International Journal of Science and Research (IJSR)
ISSN (Online): 2319-7064
Index Copernicus Value (2013): 6.14 | Impact Factor (2015): 6.391
Volume 5 Issue 6, June 2016
www.ijsr.net
Licensed Under Creative Commons Attribution CC BY
Polysulfone ultrafiltration membrane”, Desalination. 272
(2011) 51-58.
[6] Xie-Quing X., “Additive for the preparation of
Polysulfone-based ultrafiltration membranes, especially
for hemodialysis and hemoosmometer”, Desalination. 48
(1983) 79-84
[7] Ghosh R., Wan Y.H. and Cui Z.F., “Parameter scanning
ultrafiltration: rapid optimization of protein separation”,
Biotechnol. Bioeng. 81 (2003) 673-682
[8] MoÈckel D., Staude E., Michael D. Guiver, “Static
protein adsorption, ultrafltration behavior and
cleanability of hydrophilized polysulfone membranes”,
J. Membr. Sci. 158 (1999) 63-75
[9] Kajekar A. J.,. Dodamani B.M , Isloor A. M, Karim A.
Z, Cheer N.B,. Ismail A.F, Shilton S. J., “Preparation
and characterization of novel PSf/PVP/PANI-nanofiber
nanocomposite hollowfiber ultrafiltrationmembranes and
their possible applications for hazardous dye rejection”,
Desalination 365 (2015) 117–125
[10]Liu Z., Bai Y., Sun D, C., Xiao A., Zhang
Y.,“Preparation and Performance of Sulfonated
Polysulfone Flat Ultrafiltration Membranes”, Polym.
Eng. Sci. 55 (2014) 1003-1011.
[11]Witte P.V , Dijkstra P.J., van den Berg J.W.A., Feijen J,
“Phase separation processes in polymer solutions in
relation to membrane formation”, J. Membr. Sci. 117
(1996) 1-31
[12]Blanco, J. F., Sublet, J., Nguyen, Q T., Schaetzel, P.
“Formation and morphology studies of different
polysulfones-based membranes made by wet phase
inversion process”, J. Membr. Sci. 283(2006) 27–37.
[13]Chakrabarty B., Ghoshal A. K., Purkait M. K.,
“Preparation, characterization and performance studies
of Polysulfone membranes using PVP as an additive”, J.
Membr. Sci. 315 (2008) 36-47
[14]Idris A., Zain N. M., Noordin M.Y., “Synthesis,
characterization and performance of asymmetric
polyethersulfone (PES) ultrafiltration membranes with
polyethylene glycol of different molecular weights as
additives”, Desalination 207 (2007) 324–339
[15]Blanco, J. F., Sublet, J., Nguyen, Q T., Schaetzel, P.
“Formation and morphology studies of different
polysulfones-based membranes made by wet phase
inversion process”, J. Membr. Sci. 283 (2006) 27–37
[16]Aryanti P.T.P., Subagjo S., Ariono D., Wenten I.G.
,“Fouling and Rejection Characteristic of Humic
Substances in Polysulfone Ultrafiltration Membrane”, J.
Membr. Sci. 01 (2015) 41-45
[17]K. W. Lee, B. K. Seo, S. T. Nam and M. J. Han, “Trade-
off between thermodynamic enhancements and kinetic
hindrance during phase inversion in the preparation of
polysulfone membranes”, Desalination 207 (2007) 324–
339
[18]Eisen M.S., Semiat R, Vainrot N, “Polysulfone polymer
and membrane for reverse osmosis, nanofiltration and
ultrafiltration”, U.S.Patent, US 8,944,257 B2 feb (2015).
[19]H. Ohyal J.J. Kim, A. Chinch, M. Alihara, S.I.
Semonova, Y. Negishi, O. Moil and M. Yasuda, “Effect
of pore size on separation of microfiltration of oily water
using porous glass tubular membrane”, J. Membr. Sci.
145 (1998) 1-14.
[20]Toraj Moha.madi, Ashkan Esmaeelifar, “Wastewater
treatment using Ultrafiltration at a vegetable oil
factory”, Desalination.166 (2004) 329-337
[21]Sofiah Hamzah, Nora’aini Ali, Marinah Mohd Ariffin,
Asmadi Ali and Abdul Wahab Mohammad, “High
performance of Polysulfone Ultrafiltration
membrane:Effect of polymer concentration”, ARPN
Journal of Engineering and Applied Sciences, 9 (2014)
2543-2550.
[22]P.Abaticchio, A.Bottino, G.Camera Roda, G.Capannellp
and S.Munari, “Characterization of Ultrafiltration
Polymeric Membranes”, Desalination, 78 (1990) 235-
255.
[23]Panda S.R., S. De, “Preparation, characterization and
performance of ZnCl2 incorporated polysulfone
(PSF)/polyethylene glycol (PEG) blend low pressure
nanofiltration membranes”, Desalination 347 (2014) 52–
65.
[24]Kumar R., Isloor A.M., Ismail A.F., Matsuura T.,
“Synthesis and characterization of novel water soluble
derivative of chitosan as an additive for polysulfone
ultrafiltration membrane", J. Membr. Sci. 440 (2013)
140–147
[25]Ong C, Lau W., P. Goh P., B. Ng B., Ismail A,
“Preparation and characterization of PVDF– PVP–TiO2
composite hollow fiber membranes for oily wastewater
treatment using submerged membrane system”, Desalin.
Water Treat. (2013) 1–11.
Paper ID: ART201673 2573