heat treatment process to improves the mechanical properties of metal

1. Annealing
 Makes a metal as soft as
possible
 Hypoeutectoid steels (less
than 0.83% carbon) are
heated above upper critical
temp., soaked and cooled
slowly.
 Hypereutecoid (above
0.83%) are heated above
lower critical temp., soaked
and allowed to cool slowly.

2.  Process Annealing.
Low carbon steels may
harden through cold
working. They can be
heated to around 100
degrees below lower
critical temp., soaked
and allowed to cool in
air.
 Spheroidising. High
carbon steels may be
annealed just below the
lower critical temp. to
improve machinability.

3.  Normalising. Internal stresses caused by
rolling and rolling or forging are removed.
Steels are heated above upper critical temp.,
soaked and cooled in air. The cooling rate is
faster than annealing giving a smaller grain
structure.
 Stress relieving. The component is reheated
and held at temperature for a period of time
and cooled slowly.

4. Hardening
 Medium and High carbon steels (0.4 – 1.2%)
can be heated until red hot and then
quenched in water producing a very hard and
brittle metal. At 723 degrees, the BCC ferrite
changes into Austenite with a FCC structure.

5. Hardening 0.6% carbon steel
 The metal is heated to over 780
degrees, which allows the
carbon to dissolve into the FCC
Austenite.
 Quenching the metal quickly in
water prevents the structure
from changing back into BCC.
 A different structure, Body
Centre Tectragonal (BCT) is
formed. It is called Martensite
and is extremely hard and
brittle with a needle-like
microstructure.

6. Tempering
 To remove some of the brittleness from
hardened steels, tempering is used. The
metal is heated to the range of 220-300
degrees and cooled.
 Tempering colours are an indicator of
temperature on polished metals. Colours
range from yellow to brown to violet and blue.

7. Heat Treatments
 A – Normalising
 B – Annealing or
Hardening
 C – Spheroidising or
Process Annealing
 D - Tempering

8. Quenching media
 Brine (water and salt solution)
 Water
 Oil
 Air
 Turn off furnace

9. Case hardening
 Low carbon steels cannot be hardened by
heating due to the small amounts of carbon
present.
 Case hardening seeks to give a hard outer
skin over a softer core on the metal.
 The addition of carbon to the outer skin is
known as carburising.

10. Pack carburising
 The component is packed
surrounded by a carbon-rich
compound and placed in the
furnace at 900 degrees.
 Over a period of time carbon
will diffuse into the surface of
the metal.
 The longer left in the furnace,
the greater the depth of hard
carbon skin. Grain refining is
necessary in order to prevent
cracking.

11.  Salt bath carburising. A molten salt bath (sodium
cyanide, sodium carbonate and sodium chloride) has
the object immersed at 900 degrees for an hour giving
a thin carbon case when quenched.
 Gas carburising. The object is placed in a sealed
furnace with carbon monoxide allowing for fine control
of the process.
 Nitriding. Nitrides are formed on a metal surface in a
furnace with ammonia gas circulating at 500 degrees
over a long period of time (100 hours). It is used for
finished components.

12. Induction hardening
 Induced eddy currents
heat the surface of the
steel very quickly and is
quickly followed by jets
of water to quench the
component.
 A hard outer layer is
created with a soft core.
The slideways on a
lathe are induction
hardened.

13. Flame hardening
 Gas flames raise the
temperature of the
outer surface above the
upper critical temp. The
core will heat by
conduction.
 Water jets quench the
component.

14. Age hardening
 Hardening over a period of time
 Also known as precipitation hardening
 Occurs in duraluminium which is an
aluminium alloy that contains 4% copper.
This makes this alloy very useful as it is light
yet reasonably hard and strong, it is used in
the space industry.
 The metal is heated and soaked (solution
treatment) then cooled and left.