Spray SP 30/4 is a formulated system for producing rigid polyurethane foam using R 141b blowing agent. It is suitable for insulating roofs, sheds, bays, farms, storage tanks, and pipes through spraying. The foam is flame retarded and classified as B3 under DIN 4102 standards. It has a recommended formulation of 100 parts by volume polyol and 100 parts by volume isocyanate. When processed at 20-22°C with a surface temperature of 35-45°C, it has a cream time of 6-8 seconds, gel time of 15-18 seconds, and rise time of 20-25 seconds, producing a free rise density of 28-33 kg/
The document has the information about Nitriding, Blackening, Cast Iron Blackening, Gas Carburizing & Heat Treatment Service offerings by Karbotherm. Please email at abhishek@karbotherm.com for any further details
A New Sustainable Polymeric Fire Safety Solution for Thermoplastics and Elast...Earthwise
A new generation of High Performance Polymeric flame-retardants has been developed at Albemarle Corporation. Designed for use in a broad
range of plastics, these products are made via a break-through technology. The flexibility of this technology allows the products to be tailored to offer a unique set of physical and flame retardant properties in a “single-package” solution.
Thanks to their non-bio accumulative, non-toxic and excellent recyclability these products are ideal for a polymer industry striving for more environmentally friendly and sustainable fire safety solutions.
The document has the information about Nitriding, Blackening, Cast Iron Blackening, Gas Carburizing & Heat Treatment Service offerings by Karbotherm. Please email at abhishek@karbotherm.com for any further details
A New Sustainable Polymeric Fire Safety Solution for Thermoplastics and Elast...Earthwise
A new generation of High Performance Polymeric flame-retardants has been developed at Albemarle Corporation. Designed for use in a broad
range of plastics, these products are made via a break-through technology. The flexibility of this technology allows the products to be tailored to offer a unique set of physical and flame retardant properties in a “single-package” solution.
Thanks to their non-bio accumulative, non-toxic and excellent recyclability these products are ideal for a polymer industry striving for more environmentally friendly and sustainable fire safety solutions.
Sparkler UK brochure
U.K.Office: Palmcroy House
387,London Road, Croydon
Surrey, CRO 3PB.
Phone: (+44) 020 8689 0863
Fax : (+44) 020 8689 6016
E-mail: info@sparkler-filters.co.uk
Brochure valid up to ~2009
In reality this was a cartridge from Parker
Sparkler UK brochure
U.K.Office: Palmcroy House
387,London Road, Croydon
Surrey, CRO 3PB.
Phone: (+44) 020 8689 0863
Fax : (+44) 020 8689 6016
E-mail: info@sparkler-filters.co.uk
Brochure valid up to ~2009
In reality this was a cartridge from Parker
Benefits of using GGBS cement in large concrete poursDavidOFlynn
This presentation explains the benefits of using GGBS cement in reducing the risk of thermal cracking, particularly in relation to wind turbine foundations
1. SPRAY SP 30/4 Provisional Product Information
Description
Spray SP 30/4 is a formulated system for the production of R 141b blown Rigid Polyurethane
Foam.
Spray SP 30/4 is suitable for the insulation of roofs, sheds, bays and farms, storage tanks and
pipes through spraying process. The foam is flame retarded and classified B3 as per DIN
4102. R 141b blowing agent is already mixed with Polyol.
Properties Polyrex® SP 30/4 Isorex® R 310/1
POLYOL MDI-ISOCYANATE
Viscosity at 20 ºC mPa.s 350 - 550 180 - 270
Specific Gravity at 20 ºC 1.16 1.17
Storage Temperature ºC 10 - 25 10 - 25
Stability months 6 6
Recommended Formulation
Polyrex SP 30/4 100 p.b.v
Isorex R 310/1 100 p.b.v
Processing Conditions
Material Temperature 20 - 22 ºC
Mixing Ratio Polyol / Iso 100/100 p.b.v
Surface Temperature 35 - 45 ºC
3
Molded Density 40 ± 2 Kg/m
Lab Reactivity Profile at 10 ºC
Cream Time 6-8 sec
Gel Time 15-18 sec
Rise Time 20-25 sec
3
Free Rise Density 28-33 Kg/m
Packaging
220 Kg net Polyrex 250 Kg net Isorex
2. SPRAY SP 30/4 Provisional Product Information
Physical Properties
3
Final Molded Density 40 ± 2 Kg/m DIN 53420
Final Molded Core 3
Density 36-38 Kg/m DIN 53420
Compression Strength @
10 % Deformation 2
Parallel to foam rise 0.16-0.21 N/mm ASTM C 165
2
perpendicular to foam rise 0.11-0.15 N/mm ASTM C 165
Dimensional Stability (
Volume change)
@ -20 °C <1 % Volume DIN 53431
@ +70 °C <1 % Volume DIN 53431
Closed Cell Content > 93 % ASTM 2856
Thermal
Conductivity(Initial
Lambda) 0.021 W/m°K DIN 52616
Fire Behavior B3 Class DIN 4102
This material manufactured in
the United Arab Emirates, which
is identical to the specifications
of SAB I.S .