BÜFA®-Firestop S 570 is a pre-accelerated, thixotropic laminating resin made from unsaturated polyester resin dissolved in styrene and MMA with aluminium hydroxide as a fire retardant. It is used to produce molded parts with fire protection properties. The resin has a density of 1.5 g/ml, viscosity of 700-1500 mPas, and cures in 25-35 minutes at 20-30°C reaching maximum temperature of 100-130°C. The cured resin has a heat deflection temperature of 90°C and glass transition temperature of 115°C.
Portfolio assignment (mock portfolio for a 6Ruth Dapkus
This mock portfolio summarizes work from a hypothetical 6-year-old ELL student named Alyx from September 2014 to February 2015. It includes samples of the student's art projects, worksheets, writing assignments, and observations from class activities covering topics like science, math, reading, and language arts. The portfolio is intended to involve both the student and parents and assess the child's holistic learning and development over time through incorporating work samples, parent surveys, teacher observations, and utilizing the portfolio as an ongoing archive of the student's work and progress.
The document describes the far-field approach for calculating mean drift forces on a body in water. It establishes a control volume around the body and uses the rate of change of linear momentum, Euler's equation, and conservation of mass to derive an expression for the mean drift force. This involves calculating the potential at infinite distance from the body using Green's theorem and approximating the Green's function. The potential is then related to fluid velocities and pressure using Bernoulli's equation to arrive at an expression showing the mean drift force is proportional to the square of the wave amplitude.
Приклади реалізації алгоритмів управління в середовищі UNITY PROПупена Александр
Приклади реалізації алгоритмів управління в середовищі UNITY PRO Викладений нижче матеріал являється частиною навчального посібника "Програмування промислових контролерів у середовищі Unity Pro." Навч. посібник., — К.: Видавництво Ліра-К. — 2013. — с. Тв.
Barrier 80 is a two-part zinc rich epoxy primer that complies with standards for corrosion protection. It contains a high amount of zinc and is used as a primer on blast cleaned steel to improve corrosion resistance when combined with advanced coating systems. Barrier 80 is applied by airless spray or brush at a dry film thickness of 40-90 microns and has excellent water resistance, abrasion resistance, and solvent resistance. It requires surface preparation of blast cleaning steel substrates to a minimum standard and provides corrosion protection when used in a full coating system.
This document provides product information for Mipa Ziehspachtel PL10, a two-component long-term paste filler based on unsaturated polyester resins. It is suitable for repairing larger body areas on vehicles and machinery. The putty has a fine grain and can be applied in thin layers. It has a long pot life and is heat resistant up to 180°C. The document describes the product's applications, mixing instructions, drying times, and safety precautions.
Portfolio assignment (mock portfolio for a 6Ruth Dapkus
This mock portfolio summarizes work from a hypothetical 6-year-old ELL student named Alyx from September 2014 to February 2015. It includes samples of the student's art projects, worksheets, writing assignments, and observations from class activities covering topics like science, math, reading, and language arts. The portfolio is intended to involve both the student and parents and assess the child's holistic learning and development over time through incorporating work samples, parent surveys, teacher observations, and utilizing the portfolio as an ongoing archive of the student's work and progress.
The document describes the far-field approach for calculating mean drift forces on a body in water. It establishes a control volume around the body and uses the rate of change of linear momentum, Euler's equation, and conservation of mass to derive an expression for the mean drift force. This involves calculating the potential at infinite distance from the body using Green's theorem and approximating the Green's function. The potential is then related to fluid velocities and pressure using Bernoulli's equation to arrive at an expression showing the mean drift force is proportional to the square of the wave amplitude.
Приклади реалізації алгоритмів управління в середовищі UNITY PROПупена Александр
Приклади реалізації алгоритмів управління в середовищі UNITY PRO Викладений нижче матеріал являється частиною навчального посібника "Програмування промислових контролерів у середовищі Unity Pro." Навч. посібник., — К.: Видавництво Ліра-К. — 2013. — с. Тв.
Barrier 80 is a two-part zinc rich epoxy primer that complies with standards for corrosion protection. It contains a high amount of zinc and is used as a primer on blast cleaned steel to improve corrosion resistance when combined with advanced coating systems. Barrier 80 is applied by airless spray or brush at a dry film thickness of 40-90 microns and has excellent water resistance, abrasion resistance, and solvent resistance. It requires surface preparation of blast cleaning steel substrates to a minimum standard and provides corrosion protection when used in a full coating system.
This document provides product information for Mipa Ziehspachtel PL10, a two-component long-term paste filler based on unsaturated polyester resins. It is suitable for repairing larger body areas on vehicles and machinery. The putty has a fine grain and can be applied in thin layers. It has a long pot life and is heat resistant up to 180°C. The document describes the product's applications, mixing instructions, drying times, and safety precautions.
This is a different chemistry of powder coatings which offers excellent outdoor durability with better chemical resistance. We have three different grades on the basis of application –
1. Anti-Graffiti Powder
2. Architectural Powder
3. Wood Coat Powder
Visit: https://rapidcoat.com/products/thermosetting/polyurethane-powders.aspx
Call/Whatsapp: +91-9654292971 | email: exports@rapidcoat.com
Zipcoat is a two-part, multi-monomer polyester glassflake coating that provides corrosion protection in aggressive environments. It has excellent application properties and can be applied in single coats with good edge coverage when spray applied. Zipcoat dries quickly, including at sub-freezing temperatures, and is suitable for protecting structural steel, bridges, ships, and pipelines. It requires specialized cleaning solvents and has limitations for some chemical and high-temperature environments.
Here is a “Polymer Product Technical Datasheet Template“. TDSmaker offer you free Datasheet/ Specsheet/ Techsheet. Visit to ( https://www.tdsmaker.com ) to get start with free template.
Our industrial polyester ranges of shades are capable of offering high resistance to extreme weather and consistency in the shade and the gloss level. For more information visit http://rapidcoat.com/products/thermosetting/pure-polyester-powders/industrial-grade.aspx or Call/WhatsApp: +91-9654292970, +91-7290035860 | email: exports@rapidcoat.com
This document provides information on various gasket materials produced by Donit Tesnit including Grafilit, Doniflon, Micalit, and Doniflex. Grafilit is an expanded natural graphite material with excellent chemical and thermal resistance. It is available in different compositions for varying operating pressures and temperatures. Doniflon is an expanded PTFE material suitable for most media across a wide pH range. Micalit contains mica flakes and resin for high thermal and chemical resistance. Doniflex materials have aramid fibers, graphite, and binders for good chemical and mechanical properties at elevated temperatures. Each material is designed for specific industries and has distinct properties, composition, and technical data.
This document provides information on Kl bertop TP 41 N A-B, a two-component bonded coating for metal components. It has benefits such as a long component life expectancy from -40 to 230°C due to its flexible bonded coating of up to 70 μm thickness. It reduces friction and wear on metal and plastic pairings and provides lifetime lubrication and high resistance to wear. The document describes the product's composition, applications, instructions for mixing the two components, application process, and drying and hardening times.
This 4-page document provides information on a two-component, high build micaceous iron oxide pigmented polyamide cured recoatable epoxy coating. The coating is suitable for protecting steel and concrete structures exposed to atmospheric, land, or marine conditions. It has good adhesion, flexibility, chemical and heat resistance, and can be applied by airless spray or brush. The document provides details on product specifications, application instructions, and safety precautions.
This document provides information on Corroglass 600 Laminating Resin, including its suggested uses, limitations, surface preparation requirements, application details, curing times, and some physical properties. It is a two-part cold cured vinyl ester resin intended for use in constructing glass reinforced laminates and for repairing severely corroded areas, and should be applied by trained personnel according to the product data sheet and health and safety documentation. Full cure is obtained within 4-6 days.
Corrocoat Armagel is an abrasion resistant vinyl ester coating containing glass flake and silicon carbide. It is suitable for immersed environments where chemical resistance and abrasion resistance are required, such as pipes, chutes, and process tanks. Armagel is normally applied at 750-2500 microns as a coating over a 500 micron Polyglass VE primer. It has a pot life of around 50 minutes at 20°C and requires a minimum of 3-4 days for full cure.
Mipa A 40 1K-Acrylspachtel is an acrylic-based filler for levelling minor irregularities, scratches and pores on primer or filler surfaces. It can also be used on fiberglass and old coatings. It applies in thin layers and can be recoated with most paint systems. The document provides product information on the filler including its color, application methods, drying times, and VOC content which is below the EC limiting value. It also notes application and processing conditions and states the product should be disposed of according to environmental regulations.
PPA is a peroxide catalyzed glass flake polyester primer suggested for use as a holding primer on ferrous substrates prior to applying Polyglass or Polyglass VE coatings. It can also be used for adhesion promotion between existing Corroglass/Polyglass and repairs, or a new topcoat. PPA is applied by airless sprayer at 60-120 microns wet film thickness and cures partially by air drying. It has a pot life of approximately 2 hours at 100C or 1 hour at 200C and requires overcoating within 28 days at 200C with good ventilation.
Mipa P 70 is a two-component polyester filling putty used to fill irregularities and cavities in mechanical engineering and car repairs. It adheres well to iron, steel, aluminum and other substrates. It has a high stability, elasticity and sandability. The putty has a silver-gray metallic color and contains 83-86% solid content by weight. It requires a mixing ratio of 2% hardener and has a pot life of 4-5 minutes at 20°C before sanding. Proper ventilation and protective equipment is required when using the putty.
Corroglass AR VEILCOAT has been specially formulated to offer the best resistance to base environments, e.g. Sodium Hydroxide and Sodium Hypochlorite, the resin and cure system having been modified to impart the optimum resistance to these environments. Corroglass AR Veilcoat is to be used as a surface veil in certain applications where the glass present in the AR4 may be attacked by the environment.
The document discusses a door hinge gasket product called TESNIT that provides a waterproof seal for door hinges. TESNIT prevents door hinges from slipping and protects glass doors from damage, enabling reliable long-lasting use of all types of door hinges and fittings. It is made of cellulose fibers, inorganic fillers and NBR binder, giving it good mechanical and sealing properties for use in applications like the water supply industry up to temperatures of 180°C.
Here is a “Polyurethane Datasheet Template “. TDSmaker offer you free Datasheet/ Specsheet/ Techsheet. Visit to ( https://www.tdsmaker.com ) to get start with free template.
Huntsman Advanced Materials provides materials for the wind turbine industry, including composites, adhesives, and repair solutions. They have over 20 years of experience partnering with wind turbine manufacturers to develop reliable and cost-effective materials. Their product portfolio includes resins, hardeners, and adhesives for various composite manufacturing processes and turbine component bonding and repair. Huntsman supports customers through technical expertise, custom product development, and helping optimize manufacturing processes.
Kl bertop TP 03-111 is a thermosetting bonded coating that provides cost savings and component performance benefits. It reduces friction and wear in metal/metal or metal/plastic contacts through its low friction coefficient and excellent resistance to chemicals, oils, and corrosion. The coating can be applied by immersion, spraying or brushing and once cured at 160C for 60 minutes, it achieves a long-lasting protective film between 7-15 micrometers thick.
Here is a “Polyurethane Foam Datasheet Template“. TDSmaker offer you free Datasheet/ Specsheet/ Techsheet. Visit to ( https://www.tdsmaker.com ) to get start with free template.
Similar to 716-0570 Firestop S570 - ATH filled-approved for new EU standart (20)
716-0570 Firestop S570 - ATH filled-approved for new EU standart
1. Technical Data Sheet
Product description BÜFA®-Firestop S 570 is a pre-accelerated, highly thixotropic laminating
resin that is also moderately reactive with low viscosity. It is made from a
special, unsaturated polyester resin dissolved in styrene and MMA. The
resin is halogen-free and contains aluminium hydroxide as a fire
retardant. A skin-forming agent has been added to reduce the emission of
styrene.
Applications BÜFA®-Firestop S 570 is used for the production of moulded parts that
have fire protection properties.
Specifications /
technical data
Property Test method Value Unit
Density at 20 °C DIN 53 217/2 approx. 1,5 g/ml
Viscosity at 20 °C
Brookfield RV/DV-II
Spl 5 rpm 20
ISO 2555 700 -1.500 mPas
Monomer content 16 - 18 %
Flash point DIN 53 213 + 29 °C
Curing Reactivity:
BÜFA method in accordance with DIN 16 945 6.2.2.1
(100 g resin + 2 ml Butanox M-50)
20 - 30 °C 25 - 35 min
20 °C - Tmax 45 - 60 min
Tmax 100 - 130 °C
Attention!
The information given above refers exclusively to the use of the catalyst
named and the quantity specified. The use of different products or
differing quantities may yield different results.
BÜFA®-Firestop S 570
Fire protection Laminating Resin Prod. No. 716-0570
Rev. dated: 27.06.2013 Version: 3 Page 1
2. Mechanical Properties Property Test method Value
Tensile strength ISO 527-2 82 MPa
Tensile E-modulus ISO 527-2 8300 MPa
Flexural strength DIN 53 452 180 MPa
Flexural E-modulus DIN 53 457 8400 MPa
* measured on test plates with 30 % by weight glass content and conditioned for 8 hours
at + 80 °C.
Colouring The product has a blue shade of colour.
Properties of the cured
base resin
Property Test method Value
Heat deflection
temperature(HDT) ISO 75-A 90 °C
Glastransition
temperature (Tg) DIN 53765 115°C
Directions for use Working with glass fibre material
Due to its high thixotropic stabilisation, there is practically no settling out
of the filler. The storage viscosity for this product is between 3.000 - 4.000
mPas. Long stirring procedures should be avoided; the resin should be
gently stirred for a maximum of 0.5 h before using. "Gentle stirring" is
understood as stirring at low speed, just setting material at the edge of
the container in motion. Only a minimal "whirlpool" effect should take
place at the centre of the container. The best glass fibre material to use is
an open, emulsion-bound mat since this allows faster impregnation by the
resin.
BÜFA®-Firestop S 570
Fire protection Laminating Resin Prod. No. 716-0570
Rev. dated: 27.06.2013 Version: 3 Page 2
3. Note: To achieve optimal mechanical and fire protection properties, the
moulded parts should be post-cured for at least 8 hours at + 80 °C.
The thickness of the laminate and its construction as a whole, including
any top coats, varnishes, applications, sandwich inserts, etc. also have
considerable influence on fire behaviour. It should also be remembered
that individual component tests are prescribed for most applications.
Fire protection
properties
Evaluation according to DIN 5510 / part 2 tested on a 3 mm thick
random fibre laminate with 30 % glass content:
Flammability rating: S 4
Smoke development rating: SR 2
Drop-forming capacity rating: ST 2
The laminates were produced under ideal, controlled, laboratory
conditions. This information does not replace component tests by the
manufacturer.
Storage/Handling This product must be stored cool in closed containers, protected from
sunlight. Shelf-life is at least 2 months in unopened, original containers
stored up to a temperature of 20 °C. Gel and curing times may change
with increasing duration of storage.
Former product name 700-0570 BÜFA®-Firestop S 570
Note: The Information given above is based on our current state of knowledge and experience. In view of the many factors that may Influence working
conditions and the application of our products, the user is not relieved from carrying out his own tests and experiments. No legally binding warranty of
certain properties or suitability for a particular purpose can be derived from this information. It is the responsibility of the receiver or user of our products
to observe proprietary rights as well as existing laws and regulations. The latest version of the corresponding EU Safety Data Sheet must also be
observed.
BÜFA Composite Systems GmbH & Co. KG
Hohe Looge 2-8
26180 Rastede
GERMANY
Phone +49 4402 975-0
Fax +49 4402 975-300
compositesystems@buefa.de
www.buefa.de
www.buefacompositesystems.com
A member of the BÜFA-Group
BÜFA®-Firestop S 570
Fire protection Laminating Resin Prod. No. 716-0570
Rev. dated: 27.06.2013 Version: 3 Page 3