This study assessed the effect of combining wood ash and lime on the engineering properties of expansive soil from Awgu, Nigeria. Natural soil samples had high plasticity and shrink-swell potential. Addition of wood ash alone improved soil properties up to an optimum of 78% soil and 18% wood ash. Further addition of lime up to an optimum of 78% soil, 18% wood ash and 4% lime further reduced plasticity, shrinkage, and swell potential while improving compaction and strength. Curing treated soil samples for 28 days led to further strength gains. The study concluded that combining wood ash and lime can successfully stabilize expansive soils to improve their use in construction while providing an environmentally-friendly use for wood ash
Soil is a peculiar material. Some waste materials such Fly Ash, rice husk ash, pond ash may use to
make the soil to be stable. Addition of such materials will increase the physical as well as chemical properties of
the soil. Some expecting properties to be improved are CBR value, shear strength, liquidity index, plasticity
index, unconfined compressive strength and bearing capacity etc. The objective of this study was to evaluate the
effect of Fly Ash derived from combustion of sub-bituminous coal at electric power plants in stabilization of soft
fine-grained red soils. California bearing ratio (CBR) and other strength property tests were conducted on soil.
The soil is in range of plasticity, with plasticity indices ranging between 25 and 30. Tests were conducted on
soils and soil–Fly Ash mixtures prepared at optimum water content of 9% .Addition of Fly Ash resulted in
appreciable increases in the CBR of the soil. For water contents 9% wet of optimum, CBRs of the soils are
found in varying percentage such that 3,5,6and 9.We will found optimum CBR value of the soil is 6%.Increment
of CBR value is used to reduce the thickness of the pavement. And increasing the bearing capacity of soil.
Strength Behaviour of Expansive Soil Treated with Tile WasteIJERD Editor
The amount of wastes has increased year by year and the disposal becomes a serious problem. This
paper presents the effects of tile waste on, liquid limit, plastic limit, compaction characteristics, California
Bearing Ratio and swelling pressure of an expansive soil. The expansive soil collected locally was mixed with
tile waste from 0 to 30% at an increment of 10%. From the analysis of test results it was found that, liquid limit,
plastic limit, optimum moisture content, and swelling pressure are decreased, maximum dry density and
California bearing ratio are increased with an increase in tile waste.
EXPERIMENTAL INVESTIGATION ON CALIFORNIA BEARING RATIO FOR MECHANICALLY STABI...IAEME Publication
Soil stabilization is any process which improves the physical properties of soil, such as increasing shear strength, bearing capacity etc. which can be done by use of controlled compaction or addition of suitable admixtures like cement, lime and waste materials like phosphogypsum,etc. The cost of introducing these additives has also increased in recent yearswhich opened the door widely for the development of other kinds of soil additives such as plastics, bamboo, fly ash etc. This new technique of soil stabilization can be effectively used to meet the challenges of society, to reduce the quantities of waste, producing useful material from non-useful waste materials.
Stabilization of soft soil with granulated blast furnace slag and fly asheSAT Publishing House
IJRET : International Journal of Research in Engineering and Technology is an international peer reviewed, online journal published by eSAT Publishing House for the enhancement of research in various disciplines of Engineering and Technology. The aim and scope of the journal is to provide an academic medium and an important reference for the advancement and dissemination of research results that support high-level learning, teaching and research in the fields of Engineering and Technology. We bring together Scientists, Academician, Field Engineers, Scholars and Students of related fields of Engineering and Technology.
Stabilisation of clay subgrade using sawdust Ash and concrete debrisDKarthik SK
This project is done in Highway Research Station,Guindy ,Chennai.
We use concrete debris and sawdust ash as stabilizer for subgrade to increase CBR strength and reduce pavement thickness.
For details contact : skconnectme7@gmail.com
Soil is a peculiar material. Some waste materials such Fly Ash, rice husk ash, pond ash may use to
make the soil to be stable. Addition of such materials will increase the physical as well as chemical properties of
the soil. Some expecting properties to be improved are CBR value, shear strength, liquidity index, plasticity
index, unconfined compressive strength and bearing capacity etc. The objective of this study was to evaluate the
effect of Fly Ash derived from combustion of sub-bituminous coal at electric power plants in stabilization of soft
fine-grained red soils. California bearing ratio (CBR) and other strength property tests were conducted on soil.
The soil is in range of plasticity, with plasticity indices ranging between 25 and 30. Tests were conducted on
soils and soil–Fly Ash mixtures prepared at optimum water content of 9% .Addition of Fly Ash resulted in
appreciable increases in the CBR of the soil. For water contents 9% wet of optimum, CBRs of the soils are
found in varying percentage such that 3,5,6and 9.We will found optimum CBR value of the soil is 6%.Increment
of CBR value is used to reduce the thickness of the pavement. And increasing the bearing capacity of soil.
Strength Behaviour of Expansive Soil Treated with Tile WasteIJERD Editor
The amount of wastes has increased year by year and the disposal becomes a serious problem. This
paper presents the effects of tile waste on, liquid limit, plastic limit, compaction characteristics, California
Bearing Ratio and swelling pressure of an expansive soil. The expansive soil collected locally was mixed with
tile waste from 0 to 30% at an increment of 10%. From the analysis of test results it was found that, liquid limit,
plastic limit, optimum moisture content, and swelling pressure are decreased, maximum dry density and
California bearing ratio are increased with an increase in tile waste.
EXPERIMENTAL INVESTIGATION ON CALIFORNIA BEARING RATIO FOR MECHANICALLY STABI...IAEME Publication
Soil stabilization is any process which improves the physical properties of soil, such as increasing shear strength, bearing capacity etc. which can be done by use of controlled compaction or addition of suitable admixtures like cement, lime and waste materials like phosphogypsum,etc. The cost of introducing these additives has also increased in recent yearswhich opened the door widely for the development of other kinds of soil additives such as plastics, bamboo, fly ash etc. This new technique of soil stabilization can be effectively used to meet the challenges of society, to reduce the quantities of waste, producing useful material from non-useful waste materials.
Stabilization of soft soil with granulated blast furnace slag and fly asheSAT Publishing House
IJRET : International Journal of Research in Engineering and Technology is an international peer reviewed, online journal published by eSAT Publishing House for the enhancement of research in various disciplines of Engineering and Technology. The aim and scope of the journal is to provide an academic medium and an important reference for the advancement and dissemination of research results that support high-level learning, teaching and research in the fields of Engineering and Technology. We bring together Scientists, Academician, Field Engineers, Scholars and Students of related fields of Engineering and Technology.
Stabilisation of clay subgrade using sawdust Ash and concrete debrisDKarthik SK
This project is done in Highway Research Station,Guindy ,Chennai.
We use concrete debris and sawdust ash as stabilizer for subgrade to increase CBR strength and reduce pavement thickness.
For details contact : skconnectme7@gmail.com
Stabilisation of Black cotton Soils by Using Groundnut Shell AshIJSRD
Due to rapid increase in the world’s population there is increased demand for food, and this has resulted in the production of different types of crops and consequently large amounts of agricultural wastes are generated. Hence it is necessary to dispose these agricultural wastes safely on to the environment. On other hand BC soils expands and contracts due to changes in the moisture content of the soil, causing structural problems through differential movement of the structure. This isolated movement of sections of the structure can cause damage to building foundations and cracking in the exterior or interior wall covering leads to uneven floors etc. Also cause severe cracking in pavements, swimming pools, pipelines, sidewalks, highways etc. Hence there is need to stabilize expansive soil. From these discussion we should find out the solution for the above two problems. After studying several research papers it is concluded that agricultural wastes can be used effectively in stabilization of BC soils. This project presents stabilization of BC soils using groundnut shell ash since its production increased to large extent. On addition of groundnut shell ash in increment of 15% from 0to 60% to BC soils different experiments on plasticity characteristics, compaction characteristics, shear strength characteristics are conducted .And found gradual improvement in geotechnical properties of black cotton soils.
introduction to soil stabilization and introduction to geo textiles and synth...husna004
Stabilization is the process of blending and mixing materials with a soil to improve certain properties of the soil. The process may include the blending of soils to achieve a desired gradation or the mixing of commercially available additives that may alter the gradation, texture or plasticity, or act as a binder for cementation of the soil.
Overview of Soil Stabilization :Cement / Lime :PPTAniket Pateriya
Soil-cement is frequently used as a construction material for pipe bedding, slope protection, and road construction as a sub-base layer reinforcing and protecting the subgrade. It has good compressive and shear strength, but is brittle and has low tensile strength, so it is prone to forming cracks.
Lime can be used to treat soils to varying degrees, depending upon the objective. The least amount of treatment is used to dry and temporarily modify soils. Such treatment produces a working platform for construction or temporary roads. A greater degree of treatment supported by testing, design, and proper construction techniques--produces permanent structural stabilization of soils.
Soil stabilization with cement, bitumen, lime, chemical stabilization,geotextile, grouting etc. are discussed. It is a method of improving soil properties by blending and mixing other materials.
Effect of Lime Stabilisation on the Strength and Microstructure of ClayIOSR Journals
Abstract:Lime stabilization is one of the techniques that can be used for improving the engineering properties,
particularly the strength, of soft clays. This paper aims to investigate the effect of hydrated lime on the strength
and microstructure of lime treated clays. In order to illustrate such effect, a series of laboratory tests were
conducted. Atterberg limits, compaction tests, unconfined compressive strength tests and scanning electron
microscope (SEM) were carried out on kaolin clay mixed with 5% hydrated lime. The results indicated that the
addition of lime resulted in a reduction in the plasticity of kaolin and an improvement in compaction properties.
The unconfined compressive strength (UCS) of stabilized clay experienced an increase with lime addition. Two
variables influencing the amount of strength developed were studied. These variables included curing time and
water content. Curing time contributed to an increase in the UCS, from 183 kPa to 390 kPa, that is
approximately twice of the strength of untreated kaolin. SEM analysis showed the presence of the cementious
products in the kaolin clay resulted from lime-clay reaction.
Key words:Lime, Stabilisation, Soft clay, Pozzolanic reaction, Mineralogy
STABILIZATION OF BLACK COTTON SOIL WITH SAND AND CEMENT AS A SUBGRADE PAVEMENTIAEME Publication
The present work is done in stabilizing the black cotton soil by using cement and sand. the tests conducted for this work were atterberg limits, specific gravity , standard proctor test , unconfined compression test , California bearing ratio.
All construction should rest on the soil. So, the soil bearing capacity plays a vital role in constructions. All soils will not have good strength and bearing capacity. So there is a need to increase the soil strength and bearing capacity. The black cotton soils pose many problems in construction. So in this present work, the black soil collected from chintakommadinne mandal has been stabilized by using sand and cement.
A Study on Stabilzation of Black Cotton Soil Using Ferric ChlorideIOSR Journals
Expansive soils such as black cotton soil are very susceptible to detrimental volume changes, with changes in moisture. This behavior of soil is attributed to the presence of mineral Montmorillonite which has expanding lattice; Expansive soils because of their specific physical & chemical make are subjected to volume changes. In many countries including India, these soils are so extensive that alteration of highway route to avoid the material is virtually impossible. Various remedial measures like soil replacement, prewetting, moisture control, lime stabilization etc have been practiced with varied degree of success. Extensive research is going on to find the solutions to black cotton soils. Recent investigations on chemical stabilization revealed that strong electrolytes like potassium chloride, Ferric chloride can be used in place of conventionally used lime due to their ready dissolvability in water and supply of adequate cations for ready cation exchange. In the present work experimentation is carried out to investigate efficacy of ferric chloride and fly ash in improving the properties of black cotton soil.
Soil Stabilization using Fly Ash and Cotton Fiberijtsrd
Mixing of fiber for ground improvement has been practiced for recent years. Many researches has shown the expected results. This paper mainly deals with the ground improvement technique using both Fly Ash and cotton fiber. The combination of them gives a satisfactory value of its practical application. Both Fly Ash and Cotton fiber are treated as waste materials in our country in spite of having its engineering significances. Here all the tests were performed accepting the Fly Ash percent is 10 for maximum bearing capacity of soil. Three types of sample were prepared as per 0.3%, 0.5%, 0.7% of cotton fiber. For instances, it deliberately increases the Dry Density of soil up to 48.05 KN/m3 where as normal unreinforced soil sample gives about 22 KN/m3. The Ultimate bearing capacity increases up to 80.65 Kpa whereas the unreinforced soil sample gives for 35 Kpa. The result of California Bearing Ratio (CBR) test gives desired value (23%) than unreinforced soil (17%). The CBR test is performed only for 0.7% of cotton fiber where maximum stress is found. The most significant part in this study is to show the variation on cotton fiber for ground improvement technique at different ratio. This paper shows the gradual increase in Deviator stress for UCS tests for the increase in the percent of cotton fiber mixing with Fly Ash. This research may meet the need of ground having low strength at important sites. Tonmoy Kumar Brahmachary "Soil Stabilization using Fly Ash and Cotton Fiber " Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-1 | Issue-6 , October 2017, URL: http://www.ijtsrd.com/papers/ijtsrd2493.pdf http://www.ijtsrd.com/engineering/civil-engineering/2493/soil-stabilization-using-fly-ash-and-cotton-fiber-/tonmoy-kumar-brahmachary-
A Study on Stabilization of Black Cotton Soil by Use of Fly Ash, Ferric Chlor...inventy
Research Inventy : International Journal of Engineering and Science is published by the group of young academic and industrial researchers with 12 Issues per year. It is an online as well as print version open access journal that provides rapid publication (monthly) of articles in all areas of the subject such as: civil, mechanical, chemical, electronic and computer engineering as well as production and information technology. The Journal welcomes the submission of manuscripts that meet the general criteria of significance and scientific excellence. Papers will be published by rapid process within 20 days after acceptance and peer review process takes only 7 days. All articles published in Research Inventy will be peer-reviewed.
Stabilisation of Black cotton Soils by Using Groundnut Shell AshIJSRD
Due to rapid increase in the world’s population there is increased demand for food, and this has resulted in the production of different types of crops and consequently large amounts of agricultural wastes are generated. Hence it is necessary to dispose these agricultural wastes safely on to the environment. On other hand BC soils expands and contracts due to changes in the moisture content of the soil, causing structural problems through differential movement of the structure. This isolated movement of sections of the structure can cause damage to building foundations and cracking in the exterior or interior wall covering leads to uneven floors etc. Also cause severe cracking in pavements, swimming pools, pipelines, sidewalks, highways etc. Hence there is need to stabilize expansive soil. From these discussion we should find out the solution for the above two problems. After studying several research papers it is concluded that agricultural wastes can be used effectively in stabilization of BC soils. This project presents stabilization of BC soils using groundnut shell ash since its production increased to large extent. On addition of groundnut shell ash in increment of 15% from 0to 60% to BC soils different experiments on plasticity characteristics, compaction characteristics, shear strength characteristics are conducted .And found gradual improvement in geotechnical properties of black cotton soils.
introduction to soil stabilization and introduction to geo textiles and synth...husna004
Stabilization is the process of blending and mixing materials with a soil to improve certain properties of the soil. The process may include the blending of soils to achieve a desired gradation or the mixing of commercially available additives that may alter the gradation, texture or plasticity, or act as a binder for cementation of the soil.
Overview of Soil Stabilization :Cement / Lime :PPTAniket Pateriya
Soil-cement is frequently used as a construction material for pipe bedding, slope protection, and road construction as a sub-base layer reinforcing and protecting the subgrade. It has good compressive and shear strength, but is brittle and has low tensile strength, so it is prone to forming cracks.
Lime can be used to treat soils to varying degrees, depending upon the objective. The least amount of treatment is used to dry and temporarily modify soils. Such treatment produces a working platform for construction or temporary roads. A greater degree of treatment supported by testing, design, and proper construction techniques--produces permanent structural stabilization of soils.
Soil stabilization with cement, bitumen, lime, chemical stabilization,geotextile, grouting etc. are discussed. It is a method of improving soil properties by blending and mixing other materials.
Effect of Lime Stabilisation on the Strength and Microstructure of ClayIOSR Journals
Abstract:Lime stabilization is one of the techniques that can be used for improving the engineering properties,
particularly the strength, of soft clays. This paper aims to investigate the effect of hydrated lime on the strength
and microstructure of lime treated clays. In order to illustrate such effect, a series of laboratory tests were
conducted. Atterberg limits, compaction tests, unconfined compressive strength tests and scanning electron
microscope (SEM) were carried out on kaolin clay mixed with 5% hydrated lime. The results indicated that the
addition of lime resulted in a reduction in the plasticity of kaolin and an improvement in compaction properties.
The unconfined compressive strength (UCS) of stabilized clay experienced an increase with lime addition. Two
variables influencing the amount of strength developed were studied. These variables included curing time and
water content. Curing time contributed to an increase in the UCS, from 183 kPa to 390 kPa, that is
approximately twice of the strength of untreated kaolin. SEM analysis showed the presence of the cementious
products in the kaolin clay resulted from lime-clay reaction.
Key words:Lime, Stabilisation, Soft clay, Pozzolanic reaction, Mineralogy
STABILIZATION OF BLACK COTTON SOIL WITH SAND AND CEMENT AS A SUBGRADE PAVEMENTIAEME Publication
The present work is done in stabilizing the black cotton soil by using cement and sand. the tests conducted for this work were atterberg limits, specific gravity , standard proctor test , unconfined compression test , California bearing ratio.
All construction should rest on the soil. So, the soil bearing capacity plays a vital role in constructions. All soils will not have good strength and bearing capacity. So there is a need to increase the soil strength and bearing capacity. The black cotton soils pose many problems in construction. So in this present work, the black soil collected from chintakommadinne mandal has been stabilized by using sand and cement.
A Study on Stabilzation of Black Cotton Soil Using Ferric ChlorideIOSR Journals
Expansive soils such as black cotton soil are very susceptible to detrimental volume changes, with changes in moisture. This behavior of soil is attributed to the presence of mineral Montmorillonite which has expanding lattice; Expansive soils because of their specific physical & chemical make are subjected to volume changes. In many countries including India, these soils are so extensive that alteration of highway route to avoid the material is virtually impossible. Various remedial measures like soil replacement, prewetting, moisture control, lime stabilization etc have been practiced with varied degree of success. Extensive research is going on to find the solutions to black cotton soils. Recent investigations on chemical stabilization revealed that strong electrolytes like potassium chloride, Ferric chloride can be used in place of conventionally used lime due to their ready dissolvability in water and supply of adequate cations for ready cation exchange. In the present work experimentation is carried out to investigate efficacy of ferric chloride and fly ash in improving the properties of black cotton soil.
Soil Stabilization using Fly Ash and Cotton Fiberijtsrd
Mixing of fiber for ground improvement has been practiced for recent years. Many researches has shown the expected results. This paper mainly deals with the ground improvement technique using both Fly Ash and cotton fiber. The combination of them gives a satisfactory value of its practical application. Both Fly Ash and Cotton fiber are treated as waste materials in our country in spite of having its engineering significances. Here all the tests were performed accepting the Fly Ash percent is 10 for maximum bearing capacity of soil. Three types of sample were prepared as per 0.3%, 0.5%, 0.7% of cotton fiber. For instances, it deliberately increases the Dry Density of soil up to 48.05 KN/m3 where as normal unreinforced soil sample gives about 22 KN/m3. The Ultimate bearing capacity increases up to 80.65 Kpa whereas the unreinforced soil sample gives for 35 Kpa. The result of California Bearing Ratio (CBR) test gives desired value (23%) than unreinforced soil (17%). The CBR test is performed only for 0.7% of cotton fiber where maximum stress is found. The most significant part in this study is to show the variation on cotton fiber for ground improvement technique at different ratio. This paper shows the gradual increase in Deviator stress for UCS tests for the increase in the percent of cotton fiber mixing with Fly Ash. This research may meet the need of ground having low strength at important sites. Tonmoy Kumar Brahmachary "Soil Stabilization using Fly Ash and Cotton Fiber " Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-1 | Issue-6 , October 2017, URL: http://www.ijtsrd.com/papers/ijtsrd2493.pdf http://www.ijtsrd.com/engineering/civil-engineering/2493/soil-stabilization-using-fly-ash-and-cotton-fiber-/tonmoy-kumar-brahmachary-
A Study on Stabilization of Black Cotton Soil by Use of Fly Ash, Ferric Chlor...inventy
Research Inventy : International Journal of Engineering and Science is published by the group of young academic and industrial researchers with 12 Issues per year. It is an online as well as print version open access journal that provides rapid publication (monthly) of articles in all areas of the subject such as: civil, mechanical, chemical, electronic and computer engineering as well as production and information technology. The Journal welcomes the submission of manuscripts that meet the general criteria of significance and scientific excellence. Papers will be published by rapid process within 20 days after acceptance and peer review process takes only 7 days. All articles published in Research Inventy will be peer-reviewed.
A Comparative Study of using Fly Ash and Rice Husk Ash in Soil Stabilizationijtsrd
Soils are generally stabilized to increase their strength and durability or to prevent erosion and dust formation in soils. The main aim is the creation of a soil material or system that will hold under the design use conditions and for the designed life of the engineering project. In this study, Stabilization of soil using solid wastes like Rice husk Ash and Fly ash which reduces the cost of chemical stabilization a review is made on Rice husk ash and Fly ash. RHA has rich amount of silica and FA believed to be one of the best pozzolans which may be used as chemical stabilizers for soil stabilization. The rice husk ash and fly ash is mixed in various proportions with soil like 5 , 10 , 15 and 20 . Various tests were also conducted on these mixes in order to find optimum proportions. Alok Kumar Chaudhary | Puspendra Kushwaha "A Comparative Study of using Fly Ash and Rice Husk Ash in Soil Stabilization" Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-6 | Issue-6 , October 2022, URL: https://www.ijtsrd.com/papers/ijtsrd52005.pdf Paper URL: https://www.ijtsrd.com/engineering/civil-engineering/52005/a-comparative-study-of-using-fly-ash-and-rice-husk-ash-in-soil-stabilization/alok-kumar-chaudhary
The International Journal of Engineering & Science is aimed at providing a platform for researchers, engineers, scientists, or educators to publish their original research results, to exchange new ideas, to disseminate information in innovative designs, engineering experiences and technological skills. It is also the Journal's objective to promote engineering and technology education. All papers submitted to the Journal will be blind peer-reviewed. Only original articles will be published.
The papers for publication in The International Journal of Engineering& Science are selected through rigorous peer reviews to ensure originality, timeliness, relevance, and readability.
Strength Improvement of Mud Houses Through Stabilization of the Lateritic Mat...theijes
This paper reports an experimental investigation of the compressive strength of laterite stabilized with cement (CSL), lime (LSL) and rice straw (RSL) respectively. The laterites were collected from borrow pit used by locals in Bauchi, Nigeria to build mud houses. Unfortunately the mud houses experienced massive failures by through wall collapses over the years during the flooding cycles of the rainy seasons. An attempt is made to stabilize the lateritic soil materials used for the mud house walls in order to strengthen them against rains and flood erosions. Briefly discussed are factors that affect performance and strength, this include mix proportions, compaction, characteristics of the lateritic soil, mix procedure and curing. The results showed that the lateritic soils in the investigated area were relatively high on sand and lower on clay thereby promoting cement as the best stabilizer for strength. It increased the compressive strength by 661% from 0.61 N/mm2 at zero stabilization (ZSL) to 4.64 N/mm2 at 8% cement content after 28 days of curing. LSL and RSL at the same contents had strengths of 1.21 N/mm2 (98.4% increase) and 0.71 N/mm2 (16.4% increase) respectively. At 6% contents strength values were 4.33 N/mm2 , 1.16 N/mm2 and 0.66 N/mm2 respectively. The values reduced at 4% contents reporting 3.14N/mm2 , 0.82N/mm2 and 0.44N/mm2 respectively. While CSL increased non-linearly in density with increase in cement content, LSL and RSL decreased with increase of the respective contents. The results show that with cement as the stabilizer, mud house walls constructed with CSL bricks will resist collapse failures due to the perennial flooding in the area. Moreover by their relatively high compressive strengths they can be used for load bearing walls as much as sandcrete blocks
Partial replacement of wood ash and quarry dust with cement and sand to study
Expansive soil stabilization
1. Full Terms & Conditions of access and use can be found at
http://www.tandfonline.com/action/journalInformation?journalCode=yjge20
Download by: [ogbonnaya igwe] Date: 30 January 2016, At: 05:24
International Journal of Geotechnical Engineering
ISSN: 1938-6362 (Print) 1939-7879 (Online) Journal homepage: http://www.tandfonline.com/loi/yjge20
The combined effect of wood ash and lime on the
engineering properties of expansive soils
Chukwuebuka Emeh & Ogbonnaya Igwe
To cite this article: Chukwuebuka Emeh & Ogbonnaya Igwe (2016): The combined effect of
wood ash and lime on the engineering properties of expansive soils, International Journal of
Geotechnical Engineering
To link to this article: http://dx.doi.org/10.1080/19386362.2015.1125412
Published online: 06 Jan 2016.
Submit your article to this journal
Article views: 5
View related articles
3. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
International Journal of Geotechnical Engineering 2016 VOL. XX NO. X2
expansive soil stabilized with rice husk ash, while Okagbue
(2007) reported an improvement in the gradation, reduction
in the plasticity and MDD of an expansive soil stabilized
with wood ash (wood combustion by-product). Authors like
Ene and Okagbue (2009) used pyroclastic dust, while Cokca
(2001), Kumar and Sharma (2004), Ji-ru and Xing (2002) and
Wong (2015) used fly ash (byproduct of coal power plant) to
also improve the engineering properties of expansive soil and
each got result quiet similar to the cases earlier stated.
Some researchers also assessed the effect of two stabiliz-
ers (conventional and unconventional stabilizer) and discov-
ered that such combinations are better stabilizers than only
one material. For example, Rao et al. (2012) used rice husk
ash and lime to stabilize marine clay and discovered that on
the addition of 25% rice husk ash, the plasticity index (PI),
optimum moisture content (OMC), and differential free swell
(DFS) decreased by 30, 18.5 and 72.8%, respectively while
the MDD) and California bearing ratio (CBR) increased by
17 and 282%, respectively. Their work further revealed that
on addition of the two 25% rice husk ash and 9% lime, the PI,
OMC, and DFS decreased by 56.4, 42.6, and 77.2%, respec-
tively while the MDD and CBR increased by 12 and 449%,
respectively. Other authors like Ismaiel (2006) and Malhotra
and Naval (2013) combined lime and fly ash, while Amu et al.
(2005) used cement and fly ash also got higher improvement
in the geotechnical property of the soil than using only one
stabilizer. However, no author has yet combined a conventional
stabilizer and wood ash irrespective that Kersten et al. (1998)
and Babayemi and Dauda (2009) have shown that enormous
wood ash is regularly generated and improperly disposed into
the environment from bakeries, restaurants, and homes of some
countries like Nigeria, and the environmental and health impli-
cations associated with indiscriminate dumping of wood ash
to the environment have been highlighted by Pitman (2006),
Risto et al. (2005), and Pasquini (2006).
This work assesses the effect of combined wood ash and
lime (CaO) on the engineering properties of soils and their best
admixture ratio in stabilizing expansive soil.
Study methodology
Field observations and sampling
The observations that led to this study were performed atAwgu
town of southeastern Nigeria where it was observed that most of
the civil engineering structures like roads and residential build-
ings develop cracks shortly after their construction, and in some
cases lead to heaving or total failure of the structure. Reddish
brown soil underlying the area that showed highest structural
damage was collected at 30 cm depth, air-dried for two weeks
to attain complete drying, and preserved for analyses.
The lime (calcium oxide) used was obtained from an indus-
trially grade chemical store while the wood ash (the residue
powder left after the combustion of wood) was obtained from
the furnace of a wood-fired oven of a bread bakery. Following
Okagbue (2007), the wood ash was left undisturbed for 1 h
to cool to ambient temperature after it was removed from the
bakery furnace, passed through BS sieve of 63 μm to obtain
the size needed for ash clay reaction, and preserved in an air-
tight bag to eliminate its possible reaction with the atmospheric
carbon dioxide.
Analyses procedure
The wood ash was subjected to X-ray fluorescence analysis to
determine its chemical composition and to specific gravity test
following BS 1377 (1975) standard to determine its specific
gravity. The pH of the wood ash was determined following
ASTM C25-93a (1993) standard while the chemical composi-
tion and physical properties of the lime have already been given
on the container of the lime by the producing industry (specialty
mineral incorporated, 2009). The soil sample was subjected
to X-ray diffraction (XRD) analysis using Shimadzu X-ray
diffractometer (XRD-6000) to determine its dominant miner-
alogical composition. It was further subjected to sieve analy-
sis, Atterberg limits, specific gravity, free swell index (FSI),
linear shrinkage (LS), compaction, and unconfined compres-
sive strength (UCS) tests. The sieve analysis/Atterberg limits,
UCS, and FSI test were carried out according toASTM D2487
(2011), ASTM D2166/D2166M-13 (2013) and IS: 2720-XL
(1985) standards, respectively, while the specific gravity and
compaction test were performed following BS 1377 (1975)
standard.
About 940 g of the soil and 60 g of the wood ash (corre-
sponding to 94% soil and 6% wood ash) were thoroughly mixed
with a hand trowel and the wood ash–soil admixture divided
into five portions. The five portions were subjected toAtterberg
limits, FSI, LS, compaction, and UCS tests, respectively, in
order to determine the effect of wood ash on the geotechnical
properties of the soil sample. The mixing, dividing, and geo-
technical tests were repeated for three more times using 88%
soil and 12% wood ash; 82% soil and 18% wood ash; 76%
soil and 24% wood ash. For each of the geotechnical tests, the
soil–wood ash admixture that gave the best (optimum) geo-
technical property was selected and mixed with lime (calcium
oxide) in the ratio of 49:1 (i.e. 2% lime and 98% soil-wood ash
admixture). The wood ash-soil-lime admixture was also divided
into five portions and subjected to Atterberg limits, FSI, LS,
compaction, and UCS tests in order to ascertain if the addi-
tion of lime will improve or depreciate the tested geotechnical
properties of the soil. The mixing, dividing, and geotechnical
testing were repeated three more times using 4% lime and 96%
soil–wood ash admixture; 6% lime and 94% soil–wood ash
admixture; and 8% lime and 92% soil–wood ash admixture.
In each case, the geotechnical tests were done following the
earlier stated standards.
The wood ash–soil and wood ash-soil-lime admixtures
were each further compacted at the OMC and specimen was
molded using the split mold of dimension 38 mm in diameter
and 76 mm in height. The molded samples were each carefully
extruded and divided into four portions. Each of the 4 portions
was cured moist (storing in polythene bags at 98% humidity
and 25 °C) for 7, 14, 21, and 28 days, respectively. The cured
samples were thereafter subjected to UCS test to determine
their possible strength gain/lose.
Results and discussion
The index properties and dominant mineralogy of the expansive
soil are shown in Table 1 and 2, respectively. The physical and
chemical properties of the wood ash are shown in Table 3, while
those of lime are shown in Table 4.
Downloadedby[ogbonnayaigwe]at05:2430January2016
4. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
3International Journal of Geotechnical Engineering 2016 VOL. XX NO. X
From Table 1, the soil was classified as high plasticity inor-
ganic clay (CH) with high expansivity. Based on findings done
by Prakash and Sridhara (2004), the free swell ratio of the soil
showed that the soil contains both swelling and non-swelling
clays, which corresponds with its (soil) montmorillonite and
illite content shown in Table 2. Table 3 reveals that the wood
ash contains over 13 oxide compounds. Chemical composition
of wood ash varies greatly because there are many factors that
determine it such as the type and burn process (Campbell, 1990;
Etiégni and Campbell, 1991; Hakkila, 1989; Someshwar, 1996),
Table 1 Index properties and classification of the natural soil
Property Numerical value
Specific gravity (g/cm3
) 2.43
Liquid limit (%) 57.00
Plastic limit (%) 26.84
Linear shrinkage (%) 16.51
Plasticity index 30.17
Sand (%) 49.00
Silt (%) 36.00
Clay (%) 15.00
Soil classification (USCS) CH
Free swell ratio 1.23
Activity 2.00
Swell potential 8.80
Table 2 Dominant mineralogy of the expansive soil
Mineral present Percentage abundance
Na-montmorillonite 6.21
Illites 33.01
Kaolinites 12.14
Sepiolite 18.69
Sanidine 8.97
Table 3 Chemical and physical properties of the wood ash
Compounds/property Concentration unit
P2
O5
3.40%
SO3
1.82%
K2
O 15.1%
CaO 71.58%
TiO2
0.46%
Cr2
O3
0.02%
V2
O5
0.091%
MnO 2.37%
Fe2
O3
2.30%
CuO 0.070%
ZnO 0.17%
Ag2
O 2.10%
BaO 0.40%
Re2
O7
0.2%
LOI 20.01%
pH 12–13
Specific gravity 2.81
Table 4 Chemical and physical properties of the lime (after specialty minerals Inc., 2009)
Compounds Concentration unit
CaO 96%
Mg 0.8%
Fe2O3
0.1%
LOI 0.1%
pH 13–14
Percent fines (%) 98
Bulk density 1.12 g/cm3
Downloadedby[ogbonnayaigwe]at05:2430January2016
5. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
International Journal of Geotechnical Engineering 2016 VOL. XX NO. X4
For the case of Atterberg limits, the addition of 6% wood ash
resulted in a 12% increase in liquid limit and 12.2% increase
in plastic limit, while an addition of 18% wood ash resulted
in a 3% increase in liquid limit and 22.2% increase in plas-
tic limit. This higher increase in plastic limit than in liquid
limit resulted to the lowest decrease (19%) in the PI on addi-
tion of 18% wood ash. The lowest decrease of 9.5% was
also recorded in the LS on addition of 18% wood ash. These
results agree with those of Bhuvaneshwari et al. (2005) and
Ismaiel (2006) and Okagbue (2007) who used fly ash and
wood ash to stabilize expansive soil. Terzaghi and Peck (1996)
and Nalbantoglu and Gucbilmez (2001) explained that the
reduction in plasticity of the soil was due to the decrease in
the thickness of the double layer of the clay particles as a
result of cation exchange reaction which causes increase in the
attraction force therefore leading to the flocculation of the par-
ticles. Similarly, the lowest decrease (2.15%) in FSI was also
recorded on addition of 18% wood ash. However, the trend of
the FSI was more fluctuating than others (see Fig. 1(a)). This
fluctuation is probably due to the variation in the mineralog-
ical composition of the natural soil as the reaction between
clay and lime depends on the cation exchange capacity of the
the tree components (Hakkila, 1989; Waring and Schlesinger,
1985), the species of tree (Ayininuola and Oyedemi, 2013;
Misra et al., 1993; Someshwar, 1996), and the burn tempera-
ture (Etiégni and Campbell, 1991; Misra et al., 1993). There
is high percentage amount of CaO in this wood ash and this
should make it a good additive for expansive soil stabiliza-
tion because it will not only increase the alkalinity of the soil
to promote solubility of silica and alumina (Okagbue, 2007),
but also provides enough calcium ion for the cation exchange
reaction. Table 3 also revealed the presence of some heavy
metals like Zn, Cr, and Cu, but their concentrations are within
the permissible limit of most environmental regulatory bodies
(Pitman, 2006).
Effect of the additives on the
geotechnical properties of the soil
Atterberg limits, shrinkage limits, and free swell
index
Figure 1(a) shows the variation of Atterberg limits, LS, and
FSI of the expansive soil with varying quantities of wood ash.
1a Variation in Atterberg limits, LS, and free swell index with varying percentages of wood ash
1b Variation in Atterberg limits, LS, and free swell index with 18% wood ash and varying percentages of lime
Downloadedby[ogbonnayaigwe]at05:2430January2016
6. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
5International Journal of Geotechnical Engineering 2016 VOL. XX NO. X
Maximum dry density and optimum moisture
content of the soil
The OMC and MDD with varying quantities of wood ash are
shown in Figs. 2(a) and 2(b) while the variation in the OMC and
MDD at their optimum wood ash (18%) with varying quantities
of lime are shown in Fig. 2(c) and 2(d). The compaction curves
of the soil, soil–wood ash, and soil-wood ash-lime admixtures
are shown in Fig. 2(e).
Figures 2(a) and 2(b) show that there is an initial sharp
decrease in the MDD from 1.49 to 1.46 mg/m3
and a corre-
sponding 4.5% increase in OMC upon addition of 6% wood
ash to the natural soil. There was then gradual increase to the
highest MDD (1.48 mg/m3
) and a corresponding decrease to
the lowest OMC (3.5%) on the addition of 18% wood ash.
The initial sharp decrease was also observed and explained by
Okagbue and Yakubu (2000) to have been caused by floccu-
lation and agglomeration of the clay particles but their reason
for the subsequent gradual drop did not agree with the result
obtained in the present work. An explanation for the gradual
drop in the MDD may be that the lime content in the 6% wood
ash added was enough only for the initial flocculation and
agglomeration reaction and thus an increase in the quantity of
wood ash resulted in a slower reaction rate. Generally, as the
amount of wood ash increases, the OMC and MDD fluctuate
in which case none of the wood ash-soil OMC decreased up
to that of the natural soil and none of the wood ash-soil MDD
increased up to that of the natural soil.
Figures 2(c) and 2(d) reveal a general progressive increase
in OMC and decrease in MDD as lime is added to the OWSA.
The OMC increased by 12.5% while the MDD decreased by
0.15 mg/m3
upon addition of 8% lime to the OWSA. Okagbue
(2007) explained that the decrease in the MDD is due to floc-
culation and agglomeration of the clay particles (caused by
cation exchange reaction) resulting in increase in void vol-
ume consequential reduction in the weight–volume ratio. The
increase in the OMC is because of the hydration of quick lime
(reaction of quick lime and water to form calcium hydroxide).
An exothermic reaction that normally leads to the drying of
soil and thus requires more water for the subsequent reaction,
which is disassociation of the calcium hydroxide into Ca2+
minerals present and the concentration of lime (Bell, 1996).
Another explanation is that the wood ash does not quickly
produce enough calcium ions (Ca2+
) that can favorably go
into cation exchange reaction since it (wood ash) contains
other high valence ions (like Fe3+
, Cr3+
, and Ti4+
) that may
mask the effect of Ca2+
.
Since the lowest PI, LS, and FSI were obtained on the
addition of 18% wood ash to 82% soil; this was taken as the
optimum wood ash–soil admixture (OWSA) and was added
varying percentages of lime. Figure 1(b) shows the variation
in the Atterberg limits, LS, and FSI at their OWSA with var-
ying percentage of lime. The figure shows that the addition
of 4% lime increases the liquid and plastic limits by 5 and
2%, respectively but an addition of 8% lime decreases the
liquid and plastic limits by 11 and 21%, respectively. The
result is that the PI showed a 6 and 10% increase on addition
of 4 and 8% lime, respectively. Similar progressive increase
shown by PI is also shown by the LS (see Fig. 1(b)). The
addition of 4 and 8% lime to the OWSA showed a 1.5 and
3.5% increase in the LS. Ismaiel (2006) also gave similar
report on stabilization of expansive soils with the combined
effect of fly ash and lime. It implies that the addition of lime
to the OWSA does not significantly improve the PI and LS
of the soil.
Figure 1(b) however reveals that an addition of 4 and 6%
lime to the OWSAcauses a further 18.66 and 18.44% decrease
in the FSI (i.e. relative to that of OWSA), respectively. It is
expected that the addition of 5% lime to the OWSAshall result
to the lowest decrease (19.13%) in the FSI. These results agree
with those of Buhler and Cerato (2007), Malhotra and Naval
(2013) in using fly ash and lime to stabilize soil and also that
of Rao et al. (2012) in using rice husk ash and lime to stabilize
soil. The reduction in the swell potential of the natural soil was
achieved by the initial reaction of lime which releases calcium
ion (Ca2+
) that migrates to the surface of the clay particles dis-
placing water and other ions thereby reducing the swell ten-
dency. A process regarded as flocculation and agglomeration
and it generally occurs in a matter of hours, though can sub-
stantially improve with time of curing and pozzolanic reaction
(Dempsey and Thompson, 1968; National Lime Association,
2004).
2a Variation in OMC with varying percentages of wood ash
Downloadedby[ogbonnayaigwe]at05:2430January2016
7. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
International Journal of Geotechnical Engineering 2016 VOL. XX NO. X6
Interestingly, the wood ash-lime-soil admixture mois-
ture–density curves (see Fig. 2(e)) showed a more flattened
and OH-
ions (National Lime Association, 2004; Okagbue and
Yakubu, 2000).
2b Variation in MDD with varying percentages of wood ash
2c Variation of OMC with 18% wood ash and varying percentages of lime
2d Variation in MDD with 18% wood ash and varying percentages of lime
Downloadedby[ogbonnayaigwe]at05:2430January2016
8. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
7International Journal of Geotechnical Engineering 2016 VOL. XX NO. X
natural soil, again this soil mixed with 18% wood ash taken as
the OWSAwas mixed with varying quantities of lime as shown
in Fig. 3(b). The result revealed that there was a significant
increase in the UCS. The UCS increased by 206.4 kpa upon
adding 2% lime to the OWSAand further increased by 181 kpa
upon the addition of 4% lime to the OWSA and decreased
upon the addition of more lime. Therefore, 4% lime and 96%
OWSA was taken as the optimum wood ash-soil-lime admix-
ture. However, Fig. 3(b) indicates that the highest UCS shall be
attained (about 400 kpa total increase) on the addition of about
4.5% lime to the optimum wood ash–soil. The OWSA (18%
wood ash content) and optimum wood ash-soil-lime admix-
ture (4% lime content) were selected and each cured for 7, 14,
21, and 28 days with the aim of determining the strength gain
of the admixtures with time, bearing in mind that pozzolanic
reaction is time dependent (Show et al., 2003), and this reaction
as shown below produces calcium silicate hydrate (CSH) and
calcium aluminate hydrate (CAH):
Ca2+
+ 2(OH)−
+ SiO2
(Clay Silica) → CSH
compaction curve than that of wood ash–soil admixture. This
was also observed by Sweeney et al. (1988) who explained that
the flattening is due to the short-term pre-compaction cemen-
tation reactions caused by the lime. This cementation mostly
concentrates between the inter-clay particles edges/faces offer-
ing greater resistance to compaction. Nicholson et al. (1994)
and Ismaiel (2006) further explained that the flattening of com-
paction curves makes it easier to achieve the required density
over a wider range of moisture contents thereby conserving
time, effort/energy, and hence reduction in the cost of operation.
Unconfined compressive strength and curing
From Fig. 3(a) it can be seen that, as in the case of OMC and
MDD, the UCS of the soil did not show significant increase
or decrease as wood ash is progressively added to it. The UCS
increased by only 7 kpa on the addition of 18% wood ash to the
soil. In order to determine if the increase in calcium oxide con-
tent of the wood ash will cause increase in strength value of the
2e Compaction curves of the natural soil and at varying proportions of additives
3a Variation in UCS with varying percentages of wood ash
Downloadedby[ogbonnayaigwe]at05:2430January2016
9. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
International Journal of Geotechnical Engineering 2016 VOL. XX NO. X8
3b Variation in UCS with 18% wood ash and varying percentages of lime
4a Effect of curing on the UCS
4b Stress–stain relationship of the natural soil, optimum wood ash admixture uncured and 28 days cured, and optimum lime–
wood ash admixture uncured and 28 days cured
Downloadedby[ogbonnayaigwe]at05:2430January2016
10. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
9International Journal of Geotechnical Engineering 2016 VOL. XX NO. X
seven days before significant strength gain could be observed.
However, pozzolanic reaction has been observed to last for
months even years as long as the pH of the soil remains above
10 (Biczysko, 1996; Ismaiel, 2006).
Conclusion
Table 5 shows the summary of the experiments and the results
obtained, and the following conclusions were drawn from this
work:
(1) The addition of wood ash into the studied expansive
soil reduced the PI and LS of the soil and thus generally
improved the workability of the soil. The mixing of 18%
wood ash and 82% soil (regarded as the OWSA) gave
the least reduction in PI (decreased by 19.00%) and LS
(decreased by 9.50%) of the soil. Addition of lime to
the OWSA did not show any significant improvement
in the PI and LS.
(2) The OWSA resulted in only 2.15% decrease in FSI of
the soil, while the addition of 4% lime to the OWSA
resulted in a further 18.66% decrease in the FSI.
(3) Addition of wood as to the soil has no significant effect
on its (soil) OMC and MDD but the addition of lime to
the OWSA resulted to a progressive increase in OMC
and progressive reduction in the MDD. Upon addition of
8% lime to the OWSA, the OMC increased by 12.50%
while the MDD decreased by 0.15mgm3
. Similarly,
the addition of wood ash to the soil has no immediate
significant effect on its UCS while the addition of 4%
lime to the OWSA resulted to 387.4 kpa increase in the
UCS of the soil. There is evidence that it will attain a
maximum increase (by 400 kpa) on the addition of 4.5%
lime to the OWSA.
(4) The strength of both wood ash–soil and wood ash-soil-
lime admixtures increases with curing duration. After
28 days curing at 98% humidity and a temperature of
25 °C, UCS of the wood ash–soil admixture increased
The calcium silicate gel formed initially coats and binds lumps
of clay together which, then in time, crystallizes to form an
interlocking structure which binds the soil particles together
thus, strength of the soils increases (Hadi et al., 2008; Terrel
et al., 1979).
Comparing Figs. 3(a) and 3(b) with 4(a), it can be seen that
the lower strength gained by the wood ash–soil admixture is due
to the calcium oxide in the wood ash is not readily available for
the pozzolanic reaction which is time dependent, noting that the
natural soil contains appreciable amount of Na-montmorillonite
(see Table 2) and excessive quantities of exchangeable sodium
affects the lime reactivity of soil (Mallela et al., 2004), therefore
at this point the wood ash has no pozzolanic value to the mix
but only as a filler (Abdullahi, 2006). This could be justified
by the increase in the strength value of the wood ash-soil-lime
admixture as compared with the one obtained with the optimum
wood ash admixture alone, that is from 200.6 kPa to 407 kPa
on addition of 2% lime which subsequently increases as more
lime is added, and also the surge up of the strength value after
7 days of curing from 200.6 kPa before curing to 1050 kPa and
to 1590 kPa after 28 days of curing, and at this point the wood
ash must have produced enough lime for Pozzolanic reaction.
This strength gain was also revealed in the stress–strain
curves of the natural soil, the optimum admixtures, and 28 days
cured optimum admixtures as shown in Fig. 4(b). The stress–
strain curves of the uncured samples showing plastic deforma-
tions compared to that of the cured samples that showed brittle
deformations. These behaviors are likely due to hardening of
the cured clay particles with time and agree with works of
Popescu et al. (1997) and Nasrizer et al. (2011). Curing of the
samples in this work did not only serve the purpose of deter-
mining the durability of the wood ash–-lime-stabilized soil, but
also revealed that the calcium oxide content in the wood ash
is not readily available or not adequate enough for pozzolanic
reaction within hours but has to last for a period of at least
Ca2+
+ 2(OH)−
+ Al2
O3
(Clay Alumina) → CAH
Table 5 Summary of the experiments and the results
Note: Where, W = wood ash, OWSA = optimum wood ash-soil admixture
S/No Admixture Consistency Limits Proctor com-
paction test
Free
Swell
Index
(%)
Unconfined compressive strength (kPa)
LL (%) PL (%) LS (%) PI (%) MDD
(mg/
m3
)
OMC
(%)
Curing period (days)
0 7 14 21 28
1 Soil sample
only (S)
57 26.84 16.51 30.17 1.49 19 23.08 193.7
2 S + 6% W 69 39 16 30 1.46 25.5 28.08 167.2
3 S + 12% W 60 49 11 11 1.47 21.5 26.32 170.5
4 S + 18% W 60 49 7.01 11 1.48 20 20.93 200.6 1050 1380 1490 1590
5 S + 24% W 61 49 7.5 12 1.47 21 26.32 195.1
Sample S + 18 % W = OWSA
6 OWSA + 2%
L
65 46 10.3 19 1.37 31 6.67 407
7 OWSA + 4%
L
65 47 9 18 1.38 30.5 2.27 588 1250 1690 2100 2500
8 OWSA + 6%
L
49 30 10.5 19 1.37 32 2.5 585
9 OWSA + 8%
L
49 28 11.04 21 1.33 32.5 6.38 507
Downloadedby[ogbonnayaigwe]at05:2430January2016
11. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
International Journal of Geotechnical Engineering 2016 VOL. XX NO. X10
Brooks, R. M. 2009. Soil stabilization with fly ash and rice husk ash, Int. J. Res.
Rev. Appl. Sci., 1, (3), 209–217.
British Standard Institute, BS 1377. 1975. Method of testing soils for civil
engineering purposes. British standards institution, London, 144 p.
Buhler, L. R. and Cerato, B. A. 2007. Stabilization of Oklahoma expansive
soil using lime and class C flyash. Problematic soils and rocks an insitu
characterization, ASCE Geotechnical special publication 162, 1–10.
Campbell, A. G. 1990. Recycling and disposing of wood ash TAPPI J., 73,
(9), 141–146.
Cokca, E. 2001. Use of class C fly ash for stabilization of expansive soil, J.
Geotech. Geoenviron. Eng., 127, (7), 568–573.
Dempsey, BJ and Thompson, MR. 1968 Durability properties of lime-soil
mixtures, Highway Research Record 235, National Research Council,
Washington, DC, 61–75.
Ene, E. and Okagbue, C. 2009. Some basic geotechnical properties of expansive
soil modified using pyroclastic dust, Eng. Geol., 107, 61–65.
Eskisar, T. 2015. Influence of cement treatment on unconfined compressive
strength and compressibility of lean clay with medium plasticity, Arabian
J. Sci. Eng., 40, (3), 763–772.
Etiégni, L. and Campbell, A. 1991. Physical and chemical characteristics of
wood ash, Bioresource. technol., 37, 173–178.
Hadi, N. A. R. A., Khoury, H. N., and Suliman, M. R. 2008. Utilization
of bituminous limestone ash from EL-LAJJUN area for engineering
applications, Acta Geotech., 3, (2), 139–151.
Hakkila, P. 1989. Utilisation of Residual Forest Biomass, Springer series in
Wood Science – Springer Verlag, Berlin, 568 p.
Holtz, W. G. 1983. The influence of vegetation on the swelling and shrinking of
clays in the United States of America, Géotechnique, 33, 159–163.
IS: 2720-XL. 1985. Indian standard methods for test of soils: determination of
free swell index of soil. Bureau of Indian Standards, New Delhi.
Ismaiel, H. A. H. 2006. Treatment and improvement of the geotechnical
properties of different soft fine grained soils using chemical stabilization,
PhD thesis, Institute of Geology, Martin Luther Halle-Wittenberg University,
Germany.
Ji-ru, Z. Xing, C. (2002). Stabilization of expansive soils by lime and fly ash.
J. Wuhan. Univ. Technol., 17(4), 73–78.
Kersten, I., Baumbach, G., Oluwole, A. F., Obioh, I. B. and Ogunsola, O. J.
1998. Urban and rural fuel wood situation in the tropical rain forest areas
of South-west Nigeria, J. Appl. Sci. Environ. Manage., 23, (10), 887–898.
Kumar, B. R. P. and Sharma, R. S. 2004. Effect of fly ash on engineering
properties of expansive soils, J. Geotech. Geoenviron. Eng., 130, (7),
764–767.
Malhotra, M. and Naval, S. 2013. Stabilization of expansive soils using low cost
materials, Int. J. Eng. Innovative Technol., 2, (11), 181–184.
Mallela, J., VonQuintus, H. and Smith, K. L. 2004. Consideration of lime
stabilized layers in mechanistic-empirical pavement design, The National
Lime Association, Arlington, Virginia.
Misra, M., Raglund, K., and Baker,A. 1993. Wood ash composition as a function
of furnace temperature, Biomass Bioenergy, 4, (2), 103–116.
Mitchell, J. K. and Soga, K. 2005. Fundamentals of soil behavior (3rd ed.). John
Wiley and Sons Inc., New York.
Nalbantoglu, Z. Gucbilmez, E. (2001). Improvement of calcareous expansive
soils in semi-arid environments. J. Arid. Environ., 47, 453–463.
Nasrizer, A. A., Mutlharam, M. and Llamparuthi, K. 2011. Characterization
of stress-strain response of thermally cured lime stabilized expansive
clay, Proceedings of the fifth international symposium of deformation
characteristics of geomaterial, Seoul, Korea, 434–438
National Lime Association. 2004. Lime-treated soil construction manual, lime
stabilization lime modification, National Lime Association, Bulletin 326,
1–41.Accessed 18 december 2014 https://lime.org/documents/publications/
free_downloads/construct-manual2004.pdf.
Nicholson, P., Kashyap, V. and Fuji, C. 1994. Lime and fly ash admixture
improvement of tropical Hawaiian soils, Transp. Res. Rec. 1440, 71–78.
Okagbue, C. O. and Onyeobi, T. U. S. 1999. Potential of marble dust to stabilise
red tropical soils for road construction, Eng. Geol., 53, 371–380.
Okagbue, C. O. and Yakubu, J. A. 2000. Limestone ash waste as a substitute
for lime in soil improvement for engineering construction, Bull. Eng. Geol.
Environ., 58, (2), 107–113.
Okagbue, C. O. (2007). Stabilization of clay using woodash. J. Mater. Sci. Civ.
Eng., ASCE, 19, (1), 14–18.
Pasquini, M. W. 2006. The use of town refuse ash in urban agriculture around
Jos, Nigeria: health and environmental risks, Sci. Total Environ., 354, (1),
43–59.
by 1389 kpa while that of wood ash-soil-lime admixture
increased by 1912 kpa. Curing of the samples in this
work did not only serve the purpose of determining the
durability of the wood ash–lime-stabilized soil, but also
revealed that the calcium oxide content in the wood
ash is not readily available or not adequate enough for
pozzolanic reaction within hours but has to last for a
period of at least seven days before significant strength
gain could be observed.
(5) The addition of industrial CaO to wood ash in the right
proportion improves the stabilizing ability of the wood
ash.
(6) Since wood ash is regarded as a waste material and it
is cheap, using it as a stabilizing material for expansive
soils will reduce the cost of carrying out engineering
constructions on expansive soils and also reduce the
environmental problems associated with indiscriminate
disposal of wood ash.
Acknowledgment
Authors are grateful to Mr Ojo Johnson, and Mr Ganiyu of
National Steel Raw Materials ExplorationAgency, Kaduna, for
providing geotechnical services. They are also grateful to the
management of Ife-best bakeries for providing the wood ash
used in this work and to Chinenye for her financial supports.
References
Abdullahi, M. 2006. Characterestics of wood ash/OPC concrete, Leonardo
Electron. J. Pract. Technol., 8, 9–16.
Agrawal, V. and Gupta, M. 2011. Expansive soil stabilization using marble dust,
Int. J. Earth Sci. Eng., 4, (6), 59–62.
Al-Rawasa, A. A., Hagoa, A. W. and Al-Sarmi, H. 2005. Effect of lime, cement
and Sarooj (artificial pozzolan) on the swelling potential of an expansive soil
from Oman, Build. Sci., 40, 681–687.
American Society for Testing and Material, ASTM C25. 1993. Standard test
methods for chemical analysis of limestone, quicklime and hydrated lime.
Annual book of ASTM standards 4.01, 9–36.
American Society for Testing and Material, ASTM D2487-11. 2011. Standard
practice for classification of soils for Engineering purposes (Unified Soil
Classification System), ASTM international, West Conshohocken, PA, Vol.
04.08.
Amu, O.,Adewumi, I. K.,Ayodele,A. L., Mustapha, R.A. and Ola, O. O. 2005.
Analysis of California bearing ratio values of lime and wood ash stabilized
lateritic soil, J. Appl. Sci., 5, 1479–1483.
Anifowose, A. Y. B. 1989. The performance of some soils under stabilization
in Ondo state, Nigeria, Bull IAEG, 400, 79–183.
ASTM D2166/D2166M-13. 2013. Standard test method for unconfined
compressive strength of cohesive soil. ASTM international, West
Conshohocken, PA, Vol. 04.08.
Ayininuola, G. M. and Oyedemi, O. P. 2013. Impact of hardwood and softwood
ashes on soil geotechnical properties, Transnational J. Sci. Technol., 3, (10),
1–7.
Babayemi, J. O. and Dauda, K. T. 2009. Evaluation of solid waste generation,
categories and disposal options in developing countries: a case study of
Nigeria, J. Appl. Sci. Environ. Manage., 13, (3), 1–10.
Baser, O. 2009. Stabilization of expansive soils using waste marble dust. MSc
thesis, Department of civil engineering, Middle-East Technical University.
Bell, F. G. 1996. Lime stabilization of clay minerals and soils, Eng. Geol., 42,
(4), 223–237.
Bhuvaneshwari, S., Robinson, R. G. and Gandhi, S. R. 2005 Stabilization of
expansive soils using fly ash. Fly Ash Utilization Programme, (FAUP),
Technology Information Forecasting Assessment Council (TIFAC),
Department of Science and Technology (DST), New Delhi, India.
Biczysko, S. J. 1996. Long-term performance of lime stabilized road subgrade.
Lime stabilization, Thomas Telford Publisher, London.
Downloadedby[ogbonnayaigwe]at05:2430January2016
12. Emeh and Igwe The combined effect of wood ash and lime on the engineering properties of expansive soils
11International Journal of Geotechnical Engineering 2016 VOL. XX NO. X
Specialty mineral Inc. 2009. Quicklime chemical grade. www.mineralstech.com.
Sweeney, D. A., Wong, D. K. H. and Fredlund, D. G. 1988. Effect of lime
on highly plastic clay with special emphasis on aging, Transp. Res. Rec.
1190, 13–23.
Taylor, R. K. and Smith, T. J. 1986. The engineering geology of clay minerals:
swelling, shrinking and mudrock breakdown, Clay Miner., 21, 235–260.
Terrel, R. L., Epps, J.A., Barenberg, E. J., Mitchell, J. K. and Thompson, M. R.
1979. Soil stabilization in pavement structures: a user’s manual, Volumes I
and II, FHWA, Washington D.C.
Terzaghi, K., Peak, R. B., Mesri, G. (1996). Soil mechanics in engineering
practice (3rd ed.). New York, NY: John Wiley and Sons Inc.
Uduji, E. R., Okagbue, C. O. and Onyeobi, T. U. S. 1994. Geotechnical properties
of soils derived from theAgwu and Mamu Formations in theAgwu-Okigwe
area of South-eastern Nigeria and their relation to Engineering problems, J.
Min. Geol., 30, 177–123.
Waring, R. and Schlesinger, W. 1985. Forest ecosystems – concepts and
management, Academic Press, London, 340 p.
Wong, L. S. 2015. Formulation of an optimal mix design of stabilized peat
columns with fly ash as a pozzolan, Arabian J. Sci. Eng., 40, (4), 1015–1025.
Wray, W. K. and Mayer, K. T. 2004. Expansive clay soil: a widespread and
costly geohazard. geostrata, ASCE GeoInstitute, 5, 24–28.
Pitman, M. R. 2006. Wood ash use in forestry – a review of the environmental
impacts, Forestry, 79, (5), 565–588.
Popescu, M. E., Constantinescu, T., Ferrando, C. and Quintavalle, F. 1997.
Treatment of subgrade expansion soil at the extension of Bucharest-Otopeni
international airport, Eng. Geol. Environ., 1, 331–338.
Prakash, K. and Shidhara, A. 2004. Free swell ratio and clay mineralogy of
fine-grained soils, Geotech. Test. J., 27, (2), 1–6.
Rao, D. K., Rao, G. V. V. R. and Pranav, P. R. T. 2012. A laboratory study on
the affect of rice husk ash and lime on the properties of marine clay, Int. J.
Eng. Innovative Technol., 2, (1), 345–353.
Risto, P., Hannu, N., Pavoo, P., Toivo, K. and Iikka, V. 2005. Leachability of
metals in fly ash from a pulp and paper mill complex and environmental
risk characterization for eco- efficient utilization of the fly ash as a fertilizer,
Chem. Speciation Bioavailability, 17, 1–9.
Show, K. Y., Tay, J. H. and Goh, A. T. C. 2003. Reuse of incinerator fly ash in
soft soil stabilization, J. Mater. Civ. Eng., 15, (4), 335–343.
Sivapullaiah, P. V. 2006. Pozzolanic stabilization of expansive soil. In: Al-
RawasA.A. and Goosen M. F.A. (eds). Recent advances in characterization
and treatment, Technomic Publishing Company Inc., Lancaster, USA, pp.
419–434.
Someshwar, A. 1996. Wood and combination wood-fired boiler ash
characterization, J. Environ. Qual., 25, 962–972.