This study compared the etching patterns of enamel and dentin surfaces produced by Er,Cr:YSGG laser etching and conventional acid etching using 37% phosphoric acid. 40 extracted human teeth were sectioned to produce enamel and dentin specimens, which were divided into control, acid-etched, and laser-etched groups. The specimens were analyzed using environmental scanning electron microscopy. For enamel, both methods largely removed the smear layer without significant difference. Acid etching produced predominantly Type I etching patterns while laser etching resulted in Type III patterns. For dentin, both methods mostly removed the smear layer without difference. However, laser etching opened dentinal tubules to a significantly smaller diameter than acid etching. This study thus evaluated the micro
Micro-computed tomographic assessment of dentinal microcrack formation in str...DR.AJAY BABU GUTTI M.D.S
Micro-computed tomographic assessment of
dentinal microcrack formation in straight and
curved root canals in extracted teeth prepared
with hand, rotary and reciprocating instruments IEJ 2021
Comparative evaluation of treatment of noncarious cervical hypersensitivity b...DR.AJAY BABU GUTTI M.D.S
Comparative evaluation of treatment of noncarious
cervical hypersensitivity by a fluoride varnish, a
dentin bonding agent, and Er, Cr:YSGG laser: An
in vivo study JCD 2020
Comparison of root microcrack formation after root canal preparation using tw...iosrjce
IOSR Journal of Dental and Medical Sciences is one of the speciality Journal in Dental Science and Medical Science published by International Organization of Scientific Research (IOSR). The Journal publishes papers of the highest scientific merit and widest possible scope work in all areas related to medical and dental science. The Journal welcome review articles, leading medical and clinical research articles, technical notes, case reports and others.
Investigation of the Remineralization Effect Tnrough Scanning Electron Micros...IJERA Editor
Background: Local fluoride varnishes have been widely used as a method of non-operative treatment and for
caries preventive interventions for more than three decades.
Purpose: Evaluation of the remineralization effect by means of electron microscopy of mineralization varnish -
Clinpro ™ White Varnish with TCP (Tri-Calcium phosphate) (3M).
Materials and Methods: The material used is from 20 temporary intact teeth, extracted due to physiological
change with permanent teeth, with a completely preserved structure and anatomy of crowns and fully
physiologically resorbed roots. For the purposes of the study a scanning electron microscope JEOL JSM 6390 is
used with an attachment for element analysis (EDS INCA of Oxford). Prepared samples are pre-coated with
gold (cathode sputtering with apparatus JEOL JFC – 1200) to obtain a better contrast of the SEM image of early
carious lesions on the smooth surfaces of the temporary teeth, with predilection for development of caries with a
d1 threshold. For this purpose the two processes were monitored occurring continuously on the enamel surfacede-
and remineralization. Performed was computer processing of the digital images.
Results: There is presence of certain minerals deposited in the embossed enamel prisms after of
remineralization. The chemical analysis established the presence of calcium (Ca2 +
), around the organic matrix.
Demineralised surface has pores present of around 1%, which is visible through the enamel on the surface of the
deciduous teeth looking like filled and pores looking like partially covered, filled with newly formed and
growing crystals. The crystals, which are hydroxylapatite, fluorapatite or fluorhydroxiapatite gradually connect,
growing and forming mineral structure filling the microscopi defects and the pores from the demineralisation in
the surface enamel prismless layer.
Micro-computed tomographic assessment of dentinal microcrack formation in str...DR.AJAY BABU GUTTI M.D.S
Micro-computed tomographic assessment of
dentinal microcrack formation in straight and
curved root canals in extracted teeth prepared
with hand, rotary and reciprocating instruments IEJ 2021
Comparative evaluation of treatment of noncarious cervical hypersensitivity b...DR.AJAY BABU GUTTI M.D.S
Comparative evaluation of treatment of noncarious
cervical hypersensitivity by a fluoride varnish, a
dentin bonding agent, and Er, Cr:YSGG laser: An
in vivo study JCD 2020
Comparison of root microcrack formation after root canal preparation using tw...iosrjce
IOSR Journal of Dental and Medical Sciences is one of the speciality Journal in Dental Science and Medical Science published by International Organization of Scientific Research (IOSR). The Journal publishes papers of the highest scientific merit and widest possible scope work in all areas related to medical and dental science. The Journal welcome review articles, leading medical and clinical research articles, technical notes, case reports and others.
Investigation of the Remineralization Effect Tnrough Scanning Electron Micros...IJERA Editor
Background: Local fluoride varnishes have been widely used as a method of non-operative treatment and for
caries preventive interventions for more than three decades.
Purpose: Evaluation of the remineralization effect by means of electron microscopy of mineralization varnish -
Clinpro ™ White Varnish with TCP (Tri-Calcium phosphate) (3M).
Materials and Methods: The material used is from 20 temporary intact teeth, extracted due to physiological
change with permanent teeth, with a completely preserved structure and anatomy of crowns and fully
physiologically resorbed roots. For the purposes of the study a scanning electron microscope JEOL JSM 6390 is
used with an attachment for element analysis (EDS INCA of Oxford). Prepared samples are pre-coated with
gold (cathode sputtering with apparatus JEOL JFC – 1200) to obtain a better contrast of the SEM image of early
carious lesions on the smooth surfaces of the temporary teeth, with predilection for development of caries with a
d1 threshold. For this purpose the two processes were monitored occurring continuously on the enamel surfacede-
and remineralization. Performed was computer processing of the digital images.
Results: There is presence of certain minerals deposited in the embossed enamel prisms after of
remineralization. The chemical analysis established the presence of calcium (Ca2 +
), around the organic matrix.
Demineralised surface has pores present of around 1%, which is visible through the enamel on the surface of the
deciduous teeth looking like filled and pores looking like partially covered, filled with newly formed and
growing crystals. The crystals, which are hydroxylapatite, fluorapatite or fluorhydroxiapatite gradually connect,
growing and forming mineral structure filling the microscopi defects and the pores from the demineralisation in
the surface enamel prismless layer.
Root repair materials in Dentistry is evolving like never before with the advent of bioactive materials.lets have quick look at the products that have become history to the recent advances .
The bond strength of endodontic sealers to root /prosthodontic coursesIndian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Recent advances in prosthodontics / crown & bridge courses by indian dental a...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
This presentation will look at both employment and wages by sector. The presentation will give you good idea of the pay scales by sector including wage growth.
Root repair materials in Dentistry is evolving like never before with the advent of bioactive materials.lets have quick look at the products that have become history to the recent advances .
The bond strength of endodontic sealers to root /prosthodontic coursesIndian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.
Recent advances in prosthodontics / crown & bridge courses by indian dental a...Indian dental academy
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and offering a wide range of dental certified courses in different formats.
Indian dental academy provides dental crown & Bridge,rotary endodontics,fixed orthodontics,
Dental implants courses.for details pls visit www.indiandentalacademy.com ,or call
0091-9248678078
This presentation will look at both employment and wages by sector. The presentation will give you good idea of the pay scales by sector including wage growth.
What is happiness? How space could effect us? These slides shows the initial data collection of phase# 1 while designing a landscape to reflect happiness.
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all
aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
The Indian Dental Academy is the Leader in continuing dental education , training dentists in all aspects of dentistry and
offering a wide range of dental certified courses in different formats.for more details please visit
www.indiandentalacademy.com
Class on "Porcelain layering on zirconia coping"
Presentation by Prof. Dr. Marco Ferrari MD, DMD, PhD.
http://www.dentalevo.it/dentistry-materials/porcelain-layering-zirconia-coping/
Die space to be maintained for the proper application of the spacer to maintain the contour and anatomy. in vitro studies were conducted to manage before applying in the patients study group. To attain axial,buccal, lingual and mesio-distal contours of the preparing tooth.
smear layer in endodontics/ rotary endodontic courses by indian dental academyIndian dental academy
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
Comparison and Optimization of Wear Rates of Two Types of Dental Composites O...inventionjournals
International Journal of Engineering and Science Invention (IJESI) is an international journal intended for professionals and researchers in all fields of computer science and electronics. IJESI publishes research articles and reviews within the whole field Engineering Science and Technology, new teaching methods, assessment, validation and the impact of new technologies and it will continue to provide information on the latest trends and developments in this ever-expanding subject. The publications of papers are selected through double peer reviewed to ensure originality, relevance, and readability. The articles published in our journal can be accessed online.
Article presentation: enamel repair with amorphous ceramicsDr. Ritu Gupta
this presentation simplifies and explains the mentioned article which describes newer technology for enamel repair, with this method regenerating enamel stronger and better than before
Erosive cola-based drinks affect the bonding to enamel surface: an in vitro s...AD Dental
Erosive cola-based drinks affect the bonding to enamel surface: an in vitro study
Leslie Caroll CASAS-APAYCO, Vanessa Manzini DREIBI, Ana Carolina HIPÓLITO, Márcia Sirlene Zardin GRAEFF, Daniela RIOS, Ana Carolina MAGALHÃES, Marília Afonso Rabelo BUZALAF, Linda WANG
J Appl Oral Sci. http://dx.doi.org/10.1590/1678-775720130468
Abstract
Objective: This study aimed to assess the impact of in vitro erosion provoked by different cola-based drinks (Coke types), associated or not with toothbrushing, to bonding to enamel. Material and methods: Forty-six bovine enamel specimens were prepared and randomly assigned into seven groups (N=8): C- Control (neither eroded nor abraded), ERO-RC: 3x/1-minute immersion in Regular Coke (RC), ERO-LC: 3x/1-minute immersion in Light Coke (LC), ERO-ZC: 3x/1-minute immersion in Zero Coke (ZC) and three other eroded groups, subsequently abraded for 1-minute toothbrushing (EROAB-RC, EROAB-LC and EROAB-ZC, respectively). After challenges, they were stored overnight in artificial saliva for a total of 24 hours and restored with Adper Single Bond 2/Filtek Z350. Buildup coronal surfaces were cut in 1 mm2-specimens and subjected to a microtensile test. Data were statistically analyzed by two-way ANOVA/Bonferroni tests (a=0.05). Failure modes were assessed by optical microscopy (X40). The Interface of the restorations were observed using Confocal Laser Scanning Microscopy (CLSM). Results: All tested cola-based drinks significantly reduced the bond strength, which was also observed in the analyses of interfaces. Toothbrushing did not have any impact on the bond strength. CLSM showed that except for Zero Coke, all eroded specimens resulted in irregular hybrid layer formation.
Conclusions: All cola-based drinks reduced the bond strength. Different patterns of hybrid layers were obtained revealing their impact, except for ZC.
Local Advanced Lung Cancer: Artificial Intelligence, Synergetics, Complex Sys...Oleg Kshivets
Overall life span (LS) was 1671.7±1721.6 days and cumulative 5YS reached 62.4%, 10 years – 50.4%, 20 years – 44.6%. 94 LCP lived more than 5 years without cancer (LS=2958.6±1723.6 days), 22 – more than 10 years (LS=5571±1841.8 days). 67 LCP died because of LC (LS=471.9±344 days). AT significantly improved 5YS (68% vs. 53.7%) (P=0.028 by log-rank test). Cox modeling displayed that 5YS of LCP significantly depended on: N0-N12, T3-4, blood cell circuit, cell ratio factors (ratio between cancer cells-CC and blood cells subpopulations), LC cell dynamics, recalcification time, heparin tolerance, prothrombin index, protein, AT, procedure type (P=0.000-0.031). Neural networks, genetic algorithm selection and bootstrap simulation revealed relationships between 5YS and N0-12 (rank=1), thrombocytes/CC (rank=2), segmented neutrophils/CC (3), eosinophils/CC (4), erythrocytes/CC (5), healthy cells/CC (6), lymphocytes/CC (7), stick neutrophils/CC (8), leucocytes/CC (9), monocytes/CC (10). Correct prediction of 5YS was 100% by neural networks computing (error=0.000; area under ROC curve=1.0).
Basavarajeeyam is a Sreshta Sangraha grantha (Compiled book ), written by Neelkanta kotturu Basavaraja Virachita. It contains 25 Prakaranas, First 24 Chapters related to Rogas& 25th to Rasadravyas.
Antimicrobial stewardship to prevent antimicrobial resistanceGovindRankawat1
India is among the nations with the highest burden of bacterial infections.
India is one of the largest consumers of antibiotics worldwide.
India carries one of the largest burdens of drug‑resistant pathogens worldwide.
Highest burden of multidrug‑resistant tuberculosis,
Alarmingly high resistance among Gram‑negative and Gram‑positive bacteria even to newer antimicrobials such as carbapenems.
NDM‑1 ( New Delhi Metallo Beta lactamase 1, an enzyme which inactivates majority of Beta lactam antibiotics including carbapenems) was reported in 2008
These lecture slides, by Dr Sidra Arshad, offer a quick overview of the physiological basis of a normal electrocardiogram.
Learning objectives:
1. Define an electrocardiogram (ECG) and electrocardiography
2. Describe how dipoles generated by the heart produce the waveforms of the ECG
3. Describe the components of a normal electrocardiogram of a typical bipolar lead (limb II)
4. Differentiate between intervals and segments
5. Enlist some common indications for obtaining an ECG
6. Describe the flow of current around the heart during the cardiac cycle
7. Discuss the placement and polarity of the leads of electrocardiograph
8. Describe the normal electrocardiograms recorded from the limb leads and explain the physiological basis of the different records that are obtained
9. Define mean electrical vector (axis) of the heart and give the normal range
10. Define the mean QRS vector
11. Describe the axes of leads (hexagonal reference system)
12. Comprehend the vectorial analysis of the normal ECG
13. Determine the mean electrical axis of the ventricular QRS and appreciate the mean axis deviation
14. Explain the concepts of current of injury, J point, and their significance
Study Resources:
1. Chapter 11, Guyton and Hall Textbook of Medical Physiology, 14th edition
2. Chapter 9, Human Physiology - From Cells to Systems, Lauralee Sherwood, 9th edition
3. Chapter 29, Ganong’s Review of Medical Physiology, 26th edition
4. Electrocardiogram, StatPearls - https://www.ncbi.nlm.nih.gov/books/NBK549803/
5. ECG in Medical Practice by ABM Abdullah, 4th edition
6. Chapter 3, Cardiology Explained, https://www.ncbi.nlm.nih.gov/books/NBK2214/
7. ECG Basics, http://www.nataliescasebook.com/tag/e-c-g-basics
share - Lions, tigers, AI and health misinformation, oh my!.pptxTina Purnat
• Pitfalls and pivots needed to use AI effectively in public health
• Evidence-based strategies to address health misinformation effectively
• Building trust with communities online and offline
• Equipping health professionals to address questions, concerns and health misinformation
• Assessing risk and mitigating harm from adverse health narratives in communities, health workforce and health system
micro teaching on communication m.sc nursing.pdfAnurag Sharma
Microteaching is a unique model of practice teaching. It is a viable instrument for the. desired change in the teaching behavior or the behavior potential which, in specified types of real. classroom situations, tends to facilitate the achievement of specified types of objectives.
Comparative evaluation of the etching patter of er.cr and acid etching on extracter teeth
1. Journal of Clinical and Diagnostic Research. 2016 May, Vol-10(5): ZC01-ZC05 11
DOI: 10.7860/JCDR/2016/19739.7705
Original Article
Introduction
Etching of enamel and dentin produces surface irregularities
and helps forming microtags & macrotags which aids in
micromechanical bonding to composite resins. Sazak et al.,
quoted many drawbacks of acid etching like damage to the tooth
structure, multiple clinical steps making the procedure technique
sensitive and time consuming and hybridization deficit [1].
As a possible alternative to acid conditioning the use of laser therapy
has recently shown a promising front [2]. Er,Cr:YSGG(Erbium,
Chromium : Ytrium Scandium Gallium Garnet) laser, a hydrokinetic
laser system having a wavelength of 2780 nm was investigated by
Usumez et al., and was found to have ablating effect on enamel
and dentin [3].
The interest in the Erbium(Er) laser was based on the wavelength
it can emit i.e., 1.54µm and 2.7µm-2.9µm. The former coincides
with the absorption minimum of optical silica fibres, allowing long
range optical communication incorporating optical amplifiers. The
later wavelength coincides with the peak of water absorption.
Water is present in every biological tissue so efficient interaction
and dense optical energy deposition is guaranteed. In 1997 with
the FDA clearance of Er,Cr:YSGG in US, came approval for caries
removal, cavity preparation and conditioning of the tooth [4].
All the Er lasers have an affinity for the wavelengths to be highly
absorbed by water, hydroxyapatite and collagen, thus are the
target tissues. The highest peaks for the absorption of laser
energy in water are 3µm and 10µm. The proposed mechanisms
of ablation are cavitation bubbles, apatite crystal fragmentation
and an acceleration of water droplets by laser light called the
“hydrokinetic mechanism”. Laser etching is through a process of
continuous vaporization and micro explosions of water entrapped
in the hydroxyapatite matrix. The energy level basically depends
on the photon energy. The laser energy is absorbed by the water
molecules which expand. Therefore they need more space and
press and push the external microbulks of enamel towards the
axis of light [5].
In comparison to acid etching, laser etching, reduces chair side
time and can be used in moist conditions so is less technique
sensitive. The use of fine laser tips gives more control over the
area which needs to be precisely etched. Although cost has been
a major factor for the limited usage of hard tissue lasers but its
varied applications in other procedures, like tooth preparation, soft
tissue excision makes it economical over the time [3].
The specific objectives of the present study was to compare the
smear layer removal by Er,Cr:YSGG and acid etching on prepared
Keywords: Power density, Smear layer, Target tissues, Wavelength
DentistrySection
Comparative Evaluation of the Etching
Pattern of Er,Cr:YSGG & Acid Etching
on Extracted Human Teeth-An ESEM
Analysis
Rashmi Issar1
, Dibyendu Mazumdar2
, Shashi Ranjan3
, Naveen Kumar Krishna4
,
Ravindra Kole5
, Priyankar Singh6
, Deirimika Lakiang7
, Chiranjeevi Jayam8
ABSTRACT
Introduction: Etching of enamel and dentin surfaces increases
the surface area of the substrate for better bonding of the
tooth colored restorative materials. Acid etching is the most
commonly used method. Recently, hard tissue lasers have been
used for this purpose.
Aim: The aim of the present study was to evaluate and compare
the etching pattern of Er,Cr:YSGG and conventional etching on
extracted human enamel and dentin specimens.
Materials and Methods: Total 40 extracted non-diseased teeth
were selected, 20 anterior and 20 posterior teeth each for enamel
and dentin specimens respectively. The sectioned samples were
polished by 400 grit Silicon Carbide (SiC) paper to a thickness of
1.0 ± 0.5 mm. The enamel and dentin specimens were grouped
as: GrE1 & GrD1 as control specimens, GrE2 & GrD2 were
acid etched and GrE3 & GrD3 were lased. Acid etching was
done using Conditioner 36 (37 % phosphoric acid) according
to manufacturer instructions. Laser etching was done using
Er,Cr:YSGG (Erbium, Chromium : Ytrium Scandium Gallium
Garnet) at power settings of 3W, air 70% and water 20%.
After surface treatment with assigned agents the specimens
were analyzed under ESEM (Environmental Scanning Electron
Microscope) at X1000 and X5000 magnification.
Results: Chi Square and Student “t” statistical analysis was used
to compare smear layer removal and etching patterns between
GrE2-GrE3. GrD2 and GrD3 were compared for smear layer
removal and diameter of dentinal tubule opening using the same
statistical analysis. Chi-square test for removal of smear layer in
any of the treated surfaces i.e., GrE2-E3 and GrD2-D3 did not
differ significantly (p>0.05). While GrE2 showed predominantly
type I etching pattern (Chi-square=2.78, 0.05<p>0.10) and
GrE3 showed type III etching (Chi-square=4.50, p<0.05). The
tubule diameters were measured using GSA (Gesellschaft fur
Softwareentwicklung und Analytik, Germany) image analyzer
and the‘t’ value of student ‘t’ test was 18.10 which was a highly
significant result (p<.001). GrD2 had a mean dentinal tubule
diameter of 2.78µm and GrD3 of 1.09µm.
Conclusion: The present study revealed type I etching pattern
after acid etching, while type III etching pattern in enamel after
laser etching. The lased dentin showed preferential removal of
intertubular dentin while acid etching had more effect on the
peritubular dentin. No significant differences was observed
in removal of smear layer between the acid etched and lased
groups. Although diameter of the exposed dentinal tubules was
lesser after lased treatment in comparison to acid etching, further
long term in vivo studies are needed with different parameters
to establish the usage of Er,Cr:YSGG as a sole etching agent.
2. Rashmi Issar et al., Evaluation of Etching on Extracted Human Teeth by Er,Cr:YSGG & Acid Etching -ESEM Analysis www.jcdr.net
Journal of Clinical and Diagnostic Research. 2016 May, Vol-10(5): ZC01-ZC0522
specimens of enamel and dentin. This study also evaluated the
type of etching pattern exhibited on enamel by both the methods
of etching. Lastly, the difference in the etching zones on dentin
(intertubular vs peritubular dentin) was also analyzed in this study
by both laser and conventional etching methods. This study also
measures and compares the diameter of dentinal tubules after the
different surface treatments.
Our null hypothesis was that surface modification of enamel and
dentin by Er,Cr:YSGG will result in better removal of smear layer as
compared to that of 37% phosphoric acid. We also hypothesized
that the diameter of the dentinal tubules was lesser after laser
etching as compared to acid etching.
aim
The aim of the present study was to compare and evaluate the
etching pattern of Er,Cr:YSGG and conventional etching on
prepared samples of human enamel and dentin by ESEM.
Materials and Methods
This in vitro study was conducted in the Department of Conservative
Dentistry & Endodontics, Dr, R. Ahmed Dental College & Hospital,
Kolkata. Forty extracted non-diseased human teeth stored
in normal saline after cleaning were taken as sample. Ethical
Committee clearance was taken from West Bengal University of
Health Sciences, Kolkata, India. Twenty anterior teeth for enamel
specimens and 20 posterior teeth for dentin specimens were used
[Table/Fig-1]. To obtain uniform thickness of samples anterior teeth
were selected for enamel specimens. Vertical sections of enamel
surfaces were prepared through middle third of the sample teeth by
double sided diamond disk at slow speed. Horizontal sections of
dentin surfaces were prepared through middle third of the sample
teeth by double sided diamond disk at slow speed [Table/Fig-2].
Each specimen was polished by 400 grit SiC paper for 30sec
to produce a smear layer. The thickness of each specimen was
1.0 mm ±0.5mm and was measured by a bur gauge of 0.1mm
sensitivity. 20 enamel & 20 dentin specimens were subdivided into
group: GrE1, GrD1 (two samples each) acting as control, GrE2,
GrD2 (nine samples each) acid etched and GrE3, GrD3 (nine
samples each) lased.
An acrylic resin platform was made and the specimens were
placed in it stabilized by elastomeric impression material during
the etching procedure. GrE2 and GrD2 were acid etched using
36% phosphoric acid gel (Conditioner 36, Dentsply) [Table/Fig-3].
The application time for enamel was 30sec and that for dentin was
15sec. The application time for enamel is longer due to the higher
inorganic content of enamel (85% by volume) as compared to that
of dentin (45% by volume). The specimens were then rinsed with
water for 30sec and dried by oil free compressed air for 15sec
[6].
Er,Cr:YSGG laser of 2.78 µm wavelength with the following settings
was used: power -3W, air- 70%, water- 20%. The beam for enamel
and dentin specimens was aligned perpendicular at 1mm distance
and moved in a sweeping fashion over the specimen for 15sec
[Table/Fig-4]. The specimens were then dried with an oil free air
source for 15sec.
The specimens were then observed under ESEM at X1000 &
X5000 magnification. Parameters studied for enamel specimens
were: 1) removal of smear layer; 2) type of etching pattern.
Parameters studied for dentin specimens were: 1) removal of
smear layer; 2) diameter of dentinal tubule opening measured by
GSA (Gesellschaft fur Softwareentwicklung und Analytik, Germany)
image analyser. The collected data values were subjected to the
Chi square & Student‘t’ test.
Results
In the present study Chi- square & Student‘t’ statistical comparison
between GrE2 & E3 for smear layer removal and predominant type
of etching pattern. While GrD2 & D3 were analyzed for smear layer
removal and diameter of dentinal tubules after surface treatment.
GrE2 showed absence of smear layer in seven (77.8%) specimens
where as two specimens showed presence of smear layer. Eight
(88.9%) specimen of GrE3 specimens showed absence of smear
layer where as one specimen showed presence of smear layer
[Table/Fig-5].
Chi-square test revealed that comparison of removal of smear layer
in the two groups viz E2 & E3, do not differ significantly (p>0.05).
However in GrE3, absence of smear layer is 88.9% which is
significant (χ2
= 5.44, p<0.05) at 5% level & in GrE2 (χ2
= 2.78) the
removal of smear layer is significant at 10% level (p<0.10). For the
two groups the absence of smear layer is 83.33% (15 out of 18)
and it is significant (z=2.80, p<0.01).
GrE2 showed type I etching pattern in seven (77.8%) specimens,
type II & type III etching patterns in one specimen each. GrE3
[Table/Fig-4]: Samples lased.
[Table/Fig-1]: Tooth samples & armamentarium for sectioning. [Table/Fig-2]: Tooth sample sectioned by diamond disc. [Table/Fig-3]: Samples acid etched.
3. www.jcdr.net Rashmi Issar et al., Evaluation of Etching on Extracted Human Teeth by Er,Cr:YSGG & Acid Etching -ESEM Analysis
Journal of Clinical and Diagnostic Research. 2016 May, Vol-10(5): ZC01-ZC05 33
showed distinguishable type I etching pattern in two specimens &
rest seven (77.8%) showed type III etching pattern [Table/Fig-6].
In Type I etching pattern, the proportion in GrE2 is higher and
significant at 10% level (χ2
=2.78, 0.05<p>0.10) as compared to
GrE3. In Type III etching pattern, the proportion in GrE3 is higher &
significant (χ2
= 4.50, p<0.05) as compared to GrE2.
GrD2 showed six (66.7%) specimen free of smear layer and three
specimens revealed presence of smear layer. Seven (77.8%) of
Group D3 specimens showed absence of smear layer where as
two specimens showed presence of smear layer [Table/Fig-7].
Chi-square test reveals that comparison of removal of smear layer
in the two groups viz D2 & D3, do not differ significantly (p>0.05).
Comparison between the groups reveals non- significant results
(chi-square=0.28, p>0.05). Absence of smear layer in two groups
combined is 13 out of 18(72.2%). SND test shows that z=1.89,
p=0.061; indicating significance at 10% level.
GrD2 & D3 showed dentinal tubule opening in all the samples. For
comparison of SEM impression between GrD2 & D3, the mean
diameter of tubules was tested for significance of their difference.
Student‘t’ test was applied and the‘t’ value with 16 df came
out to be 18.10 which is highly significant (p<0.001). The mean
tubule diameter in GrD2 was 2.78µm & in GrD3 was 1.09µm & the
comparison between the groups showed a highly significant result
[Table/Fig-8].
Discussion
Er,CR: YSGG laser etching has the advantage of no heat
production due to the use of water coolant and absence of
vibration. The laser can be easily handled making this treatment
highly attractive for routine clinical use [7]. Er,Cr:YSGG laser
irradiated surfaces exhibited microirregulaties and removal of
smear layer [8].
In this study 3W energy density was used so as to avoid any
cavity formation [1]. According to T. Dostalova et al., at 3 W power
settings it is possible to etch the tooth surface without removing the
enamel & dentin, the border is well defined & roughness is clearly
visible. Sun X et al., in their study showed that samples irradiated
with Er,Cr:YSGG laser, in the lower range of output power (0–4
W), showed increased surface roughness of the substrate [9]. The
higher air to water percentage 70% air & 20% water was used
to reduce the thermal effect of laser and increase the cleaning &
cooling of the substrate [10].
The laser beam was aligned perpendicular to all the specimens for
maximum cutting effectiveness of the laser beam. According to
Usumez et al., the advantage of aligning laser beam perpendicular
were clean surfaces of the substrate, absence of debris and open
dentinal tubules [3].
The control specimens of both enamel and dentin did not show
any obvious morphology and were covered by smear layer [Table/
Fig-9,10]. Almost all the specimens of treated enamel & dentin
surfaces showed the absence of smear layer in the present study
& no statistically significant difference was found between acid
etched & laser etched surface. Thus the hypothesis that smear layer
removal was better for Er,Cr:YSGG as compared to acid etching
was rejected. This observation concurs well with previous studies
by M. Hossain et al., Piyamart et al., G. Olivi et al., [11‑13].
ESEM observation showed that laser irradiation produces
recrystallized enamel & dentin surface [Table/Fig-11,12] which
was also reported in studies by Secilmis et al., Tachibana et al.,
[10,14].
On observation of SEM photos of lased enamel in the present
study the classic features of laser-treated enamel was seen:
grooves, flakes, shelves and sharp edges [Table/Fig-11]; all these
aspects were more indicative of microexplosion than of melting as
was seen by Olivi G et al., [10].
The predominant enamel etching pattern after laser etching seen
was Type III [Table/Fig-11,13] as compared to the Type I in case of
acid etching [Table/Fig-14] Lin et al., using Er:YAG observed the
same etching pattern [15]. However in a study by Patricia et al.,
typical honey comb pattern of etching (type I) was observed after
irradiation by Er laser [16].
[Table/Fig-6]: Comparison between GrE2 & E3 for type of etching pattern.
[Table/Fig-7]: Comparison of absence & presence of smear layer between group
D2 & D3.
[Table/Fig-8]: Comparison of tubule diameter between Group D2 & D3.
[Table/Fig-5]: Comparison of absence & presence of smear layer removal between
GrE2 & E3.
4. Rashmi Issar et al., Evaluation of Etching on Extracted Human Teeth by Er,Cr:YSGG & Acid Etching -ESEM Analysis www.jcdr.net
Journal of Clinical and Diagnostic Research. 2016 May, Vol-10(5): ZC01-ZC0544
There was evidence of minor surface cracking on the laser etched
enamel & dentin surfaces [Table/Fig-13,15] which may be attributed
to the 3 W power setting. These cracks were also evident in a
study by Sun X et al., were higher power settings of 5 W and 6 W
was used [9]. A probable explanation for this according to Keller
Hibst et al., may be that the cracking occurs as a result of local
thermal stresses induced during the irradiation process.
Surface cracking was also evident in studies conducted by
Usumez et al., Shuinn Lee et al., Tachibana et al., [3,14,17]. As
lower power setting was used in a study by Torun Ozer et al.,
no cracks were reported in their study [8]. A study by Lin et al.,
showed that occasional cracks enhances retention and is ideal for
resin penetration [15].
In the present study SEM observation of the lased dentin
specimens revealed absence of smear layer, open dentinal tubules,
microroughness, and crater-like appearance [Table/Fig-12,15].
Oznurhan et al., in their study confirmed this appearance of lased
dentin surfaces with opening of dentinal tubules [18].
Cuff-like appearance of peritubular dentin was evident in the SEM
images from the current study [Table/Fig-12] Goes et al., attributed
this cuff-like appearance to the preferential removal of water from
the organic tissue in the intertubular dentin region, leading to the
raised appearance of the peritubular region [19].
When an acid etchant is applied due to the higher inorganic
content of peritubular dentin it is preferentially etched, resulting in
funnel-shaped openings to the tubules [Table/Fig-16]. According
to Ozer et al. this shape of dentinal tubule leads to polymerization
shrinkage, pulling the tags away from the walls and thus leading
to microleakage [8].
Ontheotherhand,laserirradiationproduceslesserdemineralization
of peritubular dentin, and the dentinal tubules remain open,
parallel, with no widening. This might probably contribute to the
reduced microleakge after laser etching [8]. The dentinal tubules
after laser etching were, approximately 1µm in diameter (GSA
image analyser) [Table/Fig-12,15]. While the acid etched dentin
surface displayed patent dentine tubules of around 2.8 µm [Table/
Fig-16]. Thus our second hypothesis of lesser diameter of dentinal
tubules after laser etching was confirmed.
According to Dunn et al. the tubule diameter in the middle third of
coronal dentin normally ranges from 0.8 -1.2 µm. In the present
study the diameter of dentinal tubules after laser etching was
found to be an average of 1 µm which implies that Er, Cr:YSGG
laser had no effect on tubule diameter [20,21].
Widely open dentinal tubules as seen after acid etching permits
access of bacteria, it’s by- products & toxic chemicals like acids to
the pulp. This is a major cause for postoperative pain, sensitivity &
pulpal damage after bonding of tooth coloured restorations [22].
As Er,Cr:YSGG might have no effect on dentinal tubule diameter &
thus it may lead to reduction in hypersensitivity clinically.
The present study is a preliminary step towards incorporating laser
in routine dental practice for esthetic restorations and needs to
be further validated by other in vitro & long term clinical studies
at different power settings. Further studies including variables like
microleakage and bond strength is needed to prove the efficacy
of laser clinically.
Within the limitations of the present study it can be concluded that
laser in the near future Er,Cr:YSGG laser can be used as a reliable
[Table/Fig-9]: Enamel control. [Table/Fig-10]: Dentin control. [Table/Fig-11]: Enamel after laser etching at (X5000)-uneven ablation of prism cores & peripheries seen.
[Table/Fig-12]: Collared up appearance surface observed of dentinal tubules- depicting more removal of intertubular dentin (X5000) by laser etching. [Table/Fig-13]: Enamel
after laser etching (X1000)-Type III etching pattern seen & microcracks observed. [Table/Fig-14]: Enamel after acid etching- Type I pattern with signs of erosion seen (X1000).
[Table/Fig-15]: Dentin after laser etching –open dentinal tubules with ablated
surface(X1300). [Table/Fig-16]: Typical funneled appearance of dentinal tubules
after acid etching (X5000).
5. www.jcdr.net Rashmi Issar et al., Evaluation of Etching on Extracted Human Teeth by Er,Cr:YSGG & Acid Etching -ESEM Analysis
Journal of Clinical and Diagnostic Research. 2016 May, Vol-10(5): ZC01-ZC05 55
etching agent by providing a substrate which is free of smear layer
with microporosities for better long term bonding.
Conclusion
Within the limits of this in vitro study it can be concluded that both
conventional & laser etching showed smear layer removal & no
statistical difference was found for smear layer removal between
the two groups (p>0.05). After laser etching the dentinal tubule
diameter was 1µm and after acid etching it was 2.8µm, which was
a highly statistically significant result (p<0.001). Predominant type
III etching pattern observed after laser etching, while type I etching
pattern after acid etching.
References
Sazak H, Turkmen C, Gunday M. Effects of Nd:YAG laser, air-abrasion and acid-[1]
etching on human enamel and dentin. Operative Dentistry. 2001; 26: 476-81.
Parker S Introduction, history of lasers and laser light production.[2] BDJ. 2007;
1:21-31.
Usumez S, Orhan M, Usumez A. Laser etching of enamel for direct bonding[3]
with an Er,Cr:YSGG hydrokinetic laser system. Am J Dentofacial Orthop.
2002;122:649-56.
Beer F, Goharkhay K, Schoop U, Strassl M, Verheyen P, Walsh LJ, et al. Oral[4]
Laser Application. 1st
Ed. Berlin:Quintessence Publishing;2006.
Maziar M, Norbert G, Reinhart P, Leon V, Friedrich L. Visualizing the procedures[5]
in the influence of water on the ablation of dental hard tissue with Er,Cr:YSGG
laser pulses. Laser in Med. Sci. 2008:451-57.
Sasaki H, Lobo DC, Moriyama Y, Watanabe S, Villaverde A, Tanaka S, et al.[6]
Tensile bond strength and SEM analysis of enamel etched with Er:YAG laser and
phohsphoric acid: a comparative study In vitro. Braz Dent J. 2008;19: 1.
Brannstrom.M, Nordenvall KJ. The effects of acid etching on the pulpodentin[7]
complex. Operative Dentistry. 1977; 17: 229-42.
Ozer T, Basara G, Berk N. Laser etching of enamel for orthodontic bonding.[8] Am
J Dentofacial Orthop. 2008;134:193-97.
Sun X, Ban J, Sha X, Wang W, Jiao Y, Wang W, et al. Effect of Er,Cr:YSGG laser[9]
at different output powers on the, micromorphology and the bond property of
non-carious sclerotic dentin to resin composites. PLoS ONE. 2015; 10:11.
Secilmis A, Altintas S, Usumez A, Berk G. Evaluation of mineral content of dentin[10]
prepared by Er,Cr:YSGG. Laser in Med Sci. 2007;23:421-25.
Olivi G, Angiero F, Benedicent S. Use of the Er,Cr:YSGG on human enamel[11]
tissues. Influence of the air water spray on the laser tissue interaction: SEM
evaluations. Lasers Med Sci. 2010; 25:793-97.
Hossain M, Nakumura Y, Yamada Y, Suzuki N, Murakami Y, Matsumoto K.[12]
Analysis of surface roughness of enamel and dentin after Er,Cr:YSGG laser
irradiation. Journal of Clinical Laser Medicine & Surgery. 2001;19: 297-303.
Piyanart E, Sharanbir KS, John FM. Effect of different power parameters of[13]
Er,Cr:YSGG laser on human dentin. Lasers in Med. Sci. 2007;22:175-82.
Tachibana A, Marques M, Soler J, Matos A. Er,Cr:YSGG laser for caries removal[14]
: influence on bonding of a self etching adhesive system. Lasers Med Sci.
2008;23:435-41.
Lin S, Caputo A, Eversole L, Rizoiu I. Topographical characteristics and shear[15]
bond strength of tooth surfaces cut with a laser-powered hydrokinetic system.
Journal of Prosthetic Dentistry. 1999; 82:451-45.
Patricia T, Joao CF, Sofia AO, Alvaro FA, Walter RD, Paulo RM. Shear bond[16]
strength and SEM morphology evaluation of different dental adhesives to enamel
prepared with Er:YAG laser. Contemp Cl Dent. 2013;4:20-26.
Lee B, Hsieh T, Lee Y. Bond strengths of orthodontic bracket after acid etched,[17]
Er:YAG laser irradiated & combined treatment on enamel surface. The Angle
Orthodontist. 2002;73:565-70.
Oznurhan F, Buldur B, Ozturk C. Influence of erbium: yttrium-aluminum-garnet[18]
laser, potassium titanyl phosphate laser irradiation, and acid etch on microtensile
bond strength of adhesives. J Pediatr Dent. 2015;3:46-51.
Goes M, Coelho M, Simnoides. Morphological effect of type, concentration[19]
& etching time of acid solutions on enamel & dentin surfaces. Braz Dent J.
1998;9(1):3-10.
Dunn W, Davis J, Bush A.Shear bond strength and SEM evaluation of composite[20]
bonded to Er:YAG laser-prepared dentin and enamel. Dental Materials.
2005;21:616-24.
Ramos R, Chimello D, Chinelatti M. Effect of Er:YAG laser on bond strength to[21]
dentin of a self etching primer & two single bottle adhesive systems. Lasers Med
Sci. 2002;31:164-70.
Hossain M, Yamada Y, Nakamura Y. A study on surface roughness & microleakage[22]
test in cavities prepared by Er:YAG laser irradiation & etched bur cavities. Lasers
Med Sci. 2003;18:25-31.
PARTICULARS OF CONTRIBUTORS:
1. Reader, Department of Conservative Dentistry & Endodontics, Buddha Institute of Dental Sciences and Hospital, Patna, Bihar, India.
2. Professor, Department of Conservative Dentistry & Endodontics, R. Ahmed Dental College and Hospital, Kolkata, West Bengal, India.
3. Reader, Department of Oral & Maxillofacial Pathology, Buddha Institute of Dental Sciences and Hospital, Patna, Bihar, India.
4. Professor, Department of Orthodontics, KGF College of Dental Sciences, Karnataka, India.
5. Senior Lecturer, Department of Conservative Dentistry and Endodontics, Bharati Vidyapeeth Deemed University, Sangli, Maharashtra, India.
6. Senior Resident, Department of Oral Surgery, Indira Gandhi Institute of Medical Sciences,Patna, India.
7. Senior Lecturer, Department of Conservative Dentistry and Endodontics, Dental College, Azamgarh (UP), India.
8. Senior Lecturer, Department of Pedodontics and Preventive Dentistry, Himachal Pradesh Govt. Dental College, Shimla, India.
NAME, ADDRESS, E-MAIL ID OF THE CORRESPONDING AUTHOR:
Dr. Rashmi Issar,
6-M.I.G, Lohia Nagar, Kankarbagh Colony, Patna-800020, Bihar, India.
E-mail: drrashmiissar@gmail.com
Financial OR OTHER COMPETING INTERESTS: None.
Date of Submission: Feb 23, 2016
Date of Peer Review: Mar 03, 2016
Date of Acceptance: Mar 16, 2016
Date of Publishing: May 01, 2016