General Structural Welding Fabrication of Cylinders and vessels Long Seam and Cir Seam Welding of Pipes General Description : Agglomerated Flux Aluminate- Rutile Type Flux Acidic Flux having Basicity Index of 0.6 Active Flux with moderate Si and Mn pick-up For Single and Multi-pass Butt and fillet welding (With EM12K Wire restrict to 15mm thickness for multi-pass) For Carbon Steels Suitable for Single Wire & Tandem System Suitable for Welding Speeds of 0.35 –0.60 m/min Grain Size – 0.25-2.00mm Type of Current – DCEP / AC 800A Wall Neutrality Number with EL8 Wire is 56

1. C-Mn STEEL (Special Purpose)
SILOX Fe LH
Hydrogen Controlled Electrode for Welding of Hot Dip Galvanizing Baths
KEY FEATURES :
• Basic type heavy coated
Controlled Hydrogen content•
Deposit pure iron with low impurities•
• Low Silicon content
Strong & ductile weld•
Weld metal is resistant to corrosion•
by molten Zinc & Lead
WELDING POSITION :
TYPICAL APPLICATIONS :
• Welding and repairing of hot dip galvanizing baths
C Mn Si S P
Typical
Specification
0.05 0.5 0.03 0.02 0.02
0.08 max 0.3-0.8 0.04 max 0.03 max 0.03 max.
Ø x L, mm Amperage, A
Approx.
Pcs/Carton
Carton/Box
Approx. wt. of 1000
pcs, Kg.
4.0 x 450 140-180 82 4 61
5.0 x 450 51 4 98
AC (70 OCV)/ DCEP
180-220
3.15 x 450 90-130 128 4 39
Condition UTS, MPa EL%
CVN Impact
at 27°C, J
Typical
As Welded
475 400 25 64
Specification 440-520 350-445 22-27 50-80
O
REDRYING CONDITION : 250-300 C for minimum 1 hr.
YS at 0.2%
offset, MPa
PARAMETERS - PACKING DATA :
MECHANICAL PROPERTIES OF ALL WELD METAL :
CHEMICAL COMPOSITION OF UNDILUTED WELD METAL, Wt % :