This document provides background information and test results for developing a 3D printed child ankle foot orthosis (AFO) for Shriners Hospital. The project team tested 5 materials - PLA, carbon fiber PLA, 3D printed polypropylene, PETG, and nylon - to identify the optimal material. PLA scored highest overall due to its strength, fatigue resistance, printability and cost. However, concerns about its brittleness and degradation led the team to also consider PETG as a strong, flexible alternative to current polypropylene designs. Ultimately no single material met all requirements, so material selection balanced mechanical properties with long-term viability and patient comfort.
Low-cost 3D-printed transtibial prosthetic sockets in a rural area of Sierra ...MerelVanderStelt1
Graduation presentation for my Technical Medicine study at the University of Twente. In cooperation with the Masanga Hospital research department and 3D-lab RadboudUMC.
The document describes a pilot project to evaluate the viability of using digital design and 3D printing to fabricate CBCT/radiographic templates for dental implant planning. Traditional methods for creating these templates require 4 appointments, whereas the digital method developed takes only 3 appointments. Dental casts and rims were digitized to arrange teeth virtually and design the templates. 3D printed templates were then tested on 15 patients and found to reduce appointments for 12 patients, while 3 patients required minor adjustments. The digital method shows potential to improve efficiency but future development is needed to account for dynamic occlusion.
This document discusses CAD CAM dentistry and digital impressions. It begins by comparing traditional dentistry and CAD CAM dentistry, noting advantages of digital impressions like decreased turnaround time, improved accuracy and fewer remakes. It then reviews several studies showing digital impressions are more accurate and comfortable for patients. The document outlines the basic components of CAD CAM systems including scanners, design software and milling machines. It discusses open vs closed architecture systems and chairside vs lab-based production. Recent advances in digital impression technology like powder-free scanning and continuous color imaging are also summarized.
Dentistry in the digital age
Digital dentistry refers to the use of dental technologies or devices to carry out dental procedures rather than using mechanical or electrical tools. The use of digital dentistry can make carrying out dental procedures more efficient than using mechanical tools, both for restorative as diagnostic purposes. 'Godfather' of Digital Dentistry is the French professor François Duret, who invented dental CAD/CAM in 1973.
For more information, you can book an appointment at
Dr Sachdeva's Dental Aesthetic And Implant Institute,
I 101, Ashok Vihar Phase 1, Delhi- 110052
Contact us at
• Phone : +919818894041,01142464041
• Our Websites:
• www.sachdevadentalcare.com
• www.dentalclinicindelhi.com
• www.dentalimplantindia.co.in
• www.dentalcoursesdelhi.com
• www.facialaestheticsdelhi.com
• Google+ link: https://goo.gl/vqAmvr
• Facebook link: https://goo.gl/tui98A
• Youtube link: https://goo.gl/mk7jfm
• Linkedin link: https://goo.gl/PrPgpB
• Slideshare link : http://goo.gl/0HY6ep
• Twitter Page : https://goo.gl/tohkcI
• Instagram page : https://goo.gl/OOGVig
Evaluation of removable partial denture frameworks fabricatedNAMITHA ANAND
The document summarizes three studies that evaluated the accuracy of removable partial denture (RPD) frameworks fabricated using different techniques:
1) A study compared digital, analog, and analog-digital techniques and found the digital technique produced significantly more accurate frameworks than the other techniques.
2) A second study evaluated the accuracy of a digital RPD fabricated by 3D printing and casting a pattern, finding it an accurate method.
3) A third study used replica techniques to analyze the internal fit of 10 digital RPDs, measuring 348 points and finding acceptable internal fit.
This document provides a summary of an editorial and articles from the CAD/CAM international magazine of digital dentistry. The editorial discusses the benefits of integrating chairside CAD/CAM dentistry and cone-beam CT technology into a dental practice. It allows dentists to provide same-day restorations and surgical guidance without outsourcing work. Upcoming software may combine intraoral scans and CBCT data to enable restorative-driven implant planning. Articles discuss CAD/CAM techniques for complex cases, CBCT applications, and industry news on digital dentistry events and products.
This document provides an overview of CAD/CAM technology in dentistry. It defines CAD/CAM and discusses the evolution of digital impressions from the early 1980s. It describes the key components of CAD/CAM systems including scanners, design software, and milling devices. It outlines different production concepts for chairside, laboratory, and centralized production. It also discusses the various materials that can be milled like metals, ceramics, and zirconia as well as future technologies like laser sintering. Finally, it highlights the significance of CAD/CAM for dentists and important preparation considerations.
Digital impressions in prosthodontics are emerging as an alternative to traditional elastomeric impressions. Various digital impression systems like CEREC, E4D, iTero, and Lava COS use intraoral scanners with blue or red lasers to optically capture 3D images of the teeth and produce digital models. This eliminates the need for physical impressions and allows for viewing of the occlusion digitally. The digital files can be used to directly mill restorations chairside or be sent to a lab for fabrication. Benefits include accuracy, reduced errors and cross-contamination control compared to conventional impressions. However, the equipment has high costs and requires trained personnel. Overall, digital impressions are expected to become more common
Low-cost 3D-printed transtibial prosthetic sockets in a rural area of Sierra ...MerelVanderStelt1
Graduation presentation for my Technical Medicine study at the University of Twente. In cooperation with the Masanga Hospital research department and 3D-lab RadboudUMC.
The document describes a pilot project to evaluate the viability of using digital design and 3D printing to fabricate CBCT/radiographic templates for dental implant planning. Traditional methods for creating these templates require 4 appointments, whereas the digital method developed takes only 3 appointments. Dental casts and rims were digitized to arrange teeth virtually and design the templates. 3D printed templates were then tested on 15 patients and found to reduce appointments for 12 patients, while 3 patients required minor adjustments. The digital method shows potential to improve efficiency but future development is needed to account for dynamic occlusion.
This document discusses CAD CAM dentistry and digital impressions. It begins by comparing traditional dentistry and CAD CAM dentistry, noting advantages of digital impressions like decreased turnaround time, improved accuracy and fewer remakes. It then reviews several studies showing digital impressions are more accurate and comfortable for patients. The document outlines the basic components of CAD CAM systems including scanners, design software and milling machines. It discusses open vs closed architecture systems and chairside vs lab-based production. Recent advances in digital impression technology like powder-free scanning and continuous color imaging are also summarized.
Dentistry in the digital age
Digital dentistry refers to the use of dental technologies or devices to carry out dental procedures rather than using mechanical or electrical tools. The use of digital dentistry can make carrying out dental procedures more efficient than using mechanical tools, both for restorative as diagnostic purposes. 'Godfather' of Digital Dentistry is the French professor François Duret, who invented dental CAD/CAM in 1973.
For more information, you can book an appointment at
Dr Sachdeva's Dental Aesthetic And Implant Institute,
I 101, Ashok Vihar Phase 1, Delhi- 110052
Contact us at
• Phone : +919818894041,01142464041
• Our Websites:
• www.sachdevadentalcare.com
• www.dentalclinicindelhi.com
• www.dentalimplantindia.co.in
• www.dentalcoursesdelhi.com
• www.facialaestheticsdelhi.com
• Google+ link: https://goo.gl/vqAmvr
• Facebook link: https://goo.gl/tui98A
• Youtube link: https://goo.gl/mk7jfm
• Linkedin link: https://goo.gl/PrPgpB
• Slideshare link : http://goo.gl/0HY6ep
• Twitter Page : https://goo.gl/tohkcI
• Instagram page : https://goo.gl/OOGVig
Evaluation of removable partial denture frameworks fabricatedNAMITHA ANAND
The document summarizes three studies that evaluated the accuracy of removable partial denture (RPD) frameworks fabricated using different techniques:
1) A study compared digital, analog, and analog-digital techniques and found the digital technique produced significantly more accurate frameworks than the other techniques.
2) A second study evaluated the accuracy of a digital RPD fabricated by 3D printing and casting a pattern, finding it an accurate method.
3) A third study used replica techniques to analyze the internal fit of 10 digital RPDs, measuring 348 points and finding acceptable internal fit.
This document provides a summary of an editorial and articles from the CAD/CAM international magazine of digital dentistry. The editorial discusses the benefits of integrating chairside CAD/CAM dentistry and cone-beam CT technology into a dental practice. It allows dentists to provide same-day restorations and surgical guidance without outsourcing work. Upcoming software may combine intraoral scans and CBCT data to enable restorative-driven implant planning. Articles discuss CAD/CAM techniques for complex cases, CBCT applications, and industry news on digital dentistry events and products.
This document provides an overview of CAD/CAM technology in dentistry. It defines CAD/CAM and discusses the evolution of digital impressions from the early 1980s. It describes the key components of CAD/CAM systems including scanners, design software, and milling devices. It outlines different production concepts for chairside, laboratory, and centralized production. It also discusses the various materials that can be milled like metals, ceramics, and zirconia as well as future technologies like laser sintering. Finally, it highlights the significance of CAD/CAM for dentists and important preparation considerations.
Digital impressions in prosthodontics are emerging as an alternative to traditional elastomeric impressions. Various digital impression systems like CEREC, E4D, iTero, and Lava COS use intraoral scanners with blue or red lasers to optically capture 3D images of the teeth and produce digital models. This eliminates the need for physical impressions and allows for viewing of the occlusion digitally. The digital files can be used to directly mill restorations chairside or be sent to a lab for fabrication. Benefits include accuracy, reduced errors and cross-contamination control compared to conventional impressions. However, the equipment has high costs and requires trained personnel. Overall, digital impressions are expected to become more common
The document provides information on Neobiotech's Cameleon CAD/CAM system, an integrated digital solution for dentistry. It describes the TRIOS intraoral scanner, 3Shape model scanners including the D700, CAD and CAM software, milling machines, and dental materials compatible with the system. The Cameleon system aims to streamline workflows, improve communication, and provide accurate, esthetic restorations using innovative technology and materials.
EnvisionTEC 3D printers are known for accuracy, surface finish, reliability and speed. They can print multiple materials on the same machine and are used to create dental models, castables, restorations and appliances. The document discusses the various printer models from EnvisionTEC suitable for dental labs, dentists and orthodontists, with details on their build sizes, resolutions and applications.
CAD/CAM systems use computer-aided design (CAD) and computer-aided manufacturing (CAM) for digital dentistry workflows. CAD is used to design restorations digitally, while CAM techniques like subtractive milling and additive 3D printing are used for manufacturing. The main 3D printing techniques for dentistry include stereolithography (SLA), digital light processing (DLP), polyjet, and selective laser sintering (SLS). SLA and DLP use UV lasers or projectors to cure liquid resin layer-by-layer, while SLS melts or sinters powder materials with a laser. 3D printers offer advantages like low waste and easy customization, but CNC
digital applications in advanced implant dentistryDoaa Jamal
Digital dentistry utilizes 3D scanning, CAD/CAM software, 3D printing and other digital technologies to improve dental implant treatment planning and placement. Key benefits include increased accuracy, reduced errors and surgery time, and improved patient experience. The document discusses digital workflows for implant planning, the use of 3D printing to create surgical guides for precise implant placement, and the future of digital dentistry.
The CS 3800 gives you a whole new experience in acquiring impressions: Freedom. Freedom from cables; freedom to pursue your preferred workflow; freedom to pay only for what you use; and freedom to interact with partners, how you prefer, when you prefer. Plus, as the result of a renewed collaboration with Studio F. A. Porsche, the CS 3800 displays a timeless, ergonomic design that ensures a high- performance scanning experience.
• High-performance wireless intraoral scanner for optimal mobility
• One of the lightest and most compact intraoral scanners on the market
• Fast and smooth scanning thanks to a large and deep field of view
• Easier for you and end-to-end workflows provide a seamless user experience
Neobiotech introduces its Cameleon CAD/CAM system as an integrated digital solution for dentistry. The system provides precise 3D scanning, CAD modeling and design tools, and accurate milling and sintering. It offers benefits like improved communication, innovative material applications, guaranteed scan tools, precise and economical milling, and convenient and effective use. The system includes the TRIOS intraoral scanner, model scanners, CAD software, milling machines, and sintering furnaces.
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
This presentation gives a brief overview of the current intra oral scanner market as of October 2018. Comparisons of accuracy and a brief overview of some of the software packages available to allow you to go to guide.
360 Visualise: Last year 360 Visualise sold more CBCT in the UK than any other company. Our first scanning centre in Ilkley was the first independent CBCT referral centre outside of London and we now scan over 3000 patients each year. This experience gives us a unique insight into the clinical needs and processes of the dental profession and what can be achieved with new software packages.
New processes are quickly developing enabling implant dentists to quickly scan, plan and print implant drilling guides using third-party applications such as SMoP & BlueSkyBio. The price of these services has reduced dramatically over the past year and with increased competition is set to continue to improve and become more accurate and efficient.
Working with so many dentists and labs, 360 Visualise are in a unique position to support you and your 3D scanner as this incredible technology continues to evolve over the coming years.
Brief introduction to the latest innovations that are used at dentistry, where equipment used are fully digitized and computerized, with the differences between using conventional methods and digital equipment in dentistry.
Main equipment to be discussed are dental imaging systems and CAD/CAM systems
The presentation gives you an overview of the digital impression as well as intraoral scanners. Trios 3 of 3Shape was specifically discussed in the presentation.
1. Removable partial dentures (RPDs) are still commonly used to restore partial edentulism despite the availability of dental implants. New trends include using thermoplastic materials and additive manufacturing techniques for RPD frameworks to improve esthetics and mechanical properties over conventional metal frameworks and acrylic denture bases.
2. Digital technologies now allow for computer-aided design and 3D printing of RPD frameworks, reducing fabrication time and costs compared to conventional casting methods. However, challenges remain with casting precision and long-term performance of 3D printed frameworks.
3. Promising new materials for RPD frameworks include titanium, zirconia, and carbon-fiber reinforced polymers which have better biocomp
Intraoral scanners for digital impressions aren't what they used to be. In fact, they' re becoming the standard of care. If you're thinking of purchasing one, here are the factors you'll need to consider.
For more information, you can book an appointment at
Dr Sachdeva's Dental Aesthetic And Implant Institute,
I 101, Ashok Vihar Phase 1, Delhi- 110052
Contact us at
• Phone : +919818894041,01142464041
• Our Websites:
• www.sachdevadentalcare.com
• www.dentalclinicindelhi.com
• www.dentalimplantindia.co.in
• www.dentalcoursesdelhi.com
• www.facialaestheticsdelhi.com
• Google+ link: https://goo.gl/vqAmvr
• Facebook link: https://goo.gl/tui98A
• Youtube link: https://goo.gl/mk7jfm
• Linkedin link: https://goo.gl/PrPgpB
• Slideshare link : http://goo.gl/0HY6ep
• Twitter Page : https://goo.gl/tohkcI
• Instagram page : https://goo.gl/OOGVig
The student team conducted research to determine if 3D printing could improve the manufacturing process of child ankle-foot orthosis (AFOs). They tested various materials for strength and fatigue resistance and found PETG to have the best balance of properties. While PLA and PETG may work for prototypes or temporary use, long-term viability is uncertain. The team concluded 3D printing could save significant time over traditional methods but recommended further testing to identify materials suitable for patient needs.
15 Online Experts for Boosting Your Plastics BusinessHerwig Juster
Everybody wants to turn daily business operations in polymer engineering more effective and efficient! Using mobile apps instead of old design guides and large excel calculation tables to quickly calculate daily needed engineering parameters such as clamping force or residence time may be a way to follow. Another way is to use free online sources. These eliminate the need of having several apps on your mobile phone.
This document provides an overview of 3D printing including its definition, history, materials used, mechanism, applications in dentistry, and comparisons to CAD/CAM. It discusses the development of 3D printing from its origins in 1984 to current uses like dental modeling and surgical guides. Applications in maxillofacial surgery, orthodontics, prosthodontics and endodontics are also covered. The document concludes by discussing emerging technologies like bioprinting, where living cells are used as "bioinks" to print tissues, and 4D printing, where printed objects can change shape over time in response to environmental conditions.
Improving Prosthetic Patient Care Through 3D Technology1Jessica Zistatsis
This document discusses using 3D technology to improve the process of fabricating prosthetic devices. Currently, fabrication is a manual multi-week process. The author proposes using 3D scanning and carving to decrease fabrication time from weeks to days, lower costs, increase reproducibility, and improve patient safety and comfort by eliminating plaster casting. Research identified several 3D scanning and carving systems that could scan the residual limb in under a minute and carve a test socket within 10 minutes, allowing same-day fittings. This proposed process is estimated to reduce labor costs by $614 per socket while improving quality and patient experience.
applications of 3d printing in dental prosthodonticsahmedgamal968279
applications of 3d printing in dental prosthodontics including the history of 3d printers and types of 3d printers and different applications of 3d printers in dentistry and different and recent martials used with this technique
The document summarizes a research proposal for designing an automatic plastic bottle trimming machine. It discusses the need for such a machine in the plastic manufacturing industry and related works that have tried to address bottle trimming. The proposed design will utilize pneumatic systems and an automatic feeding mechanism to trim bottles, collecting trimmed pieces for recycling rather than waste. This addresses sustainability and cost concerns of previous solutions. The research plan involves studying differences from existing designs, material availability, testing functionality, impacts on industry productivity, and advantages over current trimming methods.
This document summarizes an experiment conducted to determine the significant parameters affecting the shear strength of hot-air welds between polypropylene rod material and twintex composite material. The experiment tested different welding temperatures, feed rates, and fan speeds using a designed experiment approach. Samples were tested and data was analyzed to make recommendations for further testing.
The document discusses the creation and comparison of 3D-printed and finite element analysis (FEA) models of a porcine lumbar vertebra created using various open source software packages. Key findings include:
- 3D-printed models created with 3D-Slicer and MIMICS software were measured and found to be geometrically similar, with minor differences attributed to smoothing and measurement errors.
- FEA models were significantly stiffer than actual test results and published data. The model using equations from Morgan et al. was closest but still stiffer.
- Customizing material properties in the FEA model improved results, but equations require further validation.
- The study demonstrated a process for creating
The document provides information on Neobiotech's Cameleon CAD/CAM system, an integrated digital solution for dentistry. It describes the TRIOS intraoral scanner, 3Shape model scanners including the D700, CAD and CAM software, milling machines, and dental materials compatible with the system. The Cameleon system aims to streamline workflows, improve communication, and provide accurate, esthetic restorations using innovative technology and materials.
EnvisionTEC 3D printers are known for accuracy, surface finish, reliability and speed. They can print multiple materials on the same machine and are used to create dental models, castables, restorations and appliances. The document discusses the various printer models from EnvisionTEC suitable for dental labs, dentists and orthodontists, with details on their build sizes, resolutions and applications.
CAD/CAM systems use computer-aided design (CAD) and computer-aided manufacturing (CAM) for digital dentistry workflows. CAD is used to design restorations digitally, while CAM techniques like subtractive milling and additive 3D printing are used for manufacturing. The main 3D printing techniques for dentistry include stereolithography (SLA), digital light processing (DLP), polyjet, and selective laser sintering (SLS). SLA and DLP use UV lasers or projectors to cure liquid resin layer-by-layer, while SLS melts or sinters powder materials with a laser. 3D printers offer advantages like low waste and easy customization, but CNC
digital applications in advanced implant dentistryDoaa Jamal
Digital dentistry utilizes 3D scanning, CAD/CAM software, 3D printing and other digital technologies to improve dental implant treatment planning and placement. Key benefits include increased accuracy, reduced errors and surgery time, and improved patient experience. The document discusses digital workflows for implant planning, the use of 3D printing to create surgical guides for precise implant placement, and the future of digital dentistry.
The CS 3800 gives you a whole new experience in acquiring impressions: Freedom. Freedom from cables; freedom to pursue your preferred workflow; freedom to pay only for what you use; and freedom to interact with partners, how you prefer, when you prefer. Plus, as the result of a renewed collaboration with Studio F. A. Porsche, the CS 3800 displays a timeless, ergonomic design that ensures a high- performance scanning experience.
• High-performance wireless intraoral scanner for optimal mobility
• One of the lightest and most compact intraoral scanners on the market
• Fast and smooth scanning thanks to a large and deep field of view
• Easier for you and end-to-end workflows provide a seamless user experience
Neobiotech introduces its Cameleon CAD/CAM system as an integrated digital solution for dentistry. The system provides precise 3D scanning, CAD modeling and design tools, and accurate milling and sintering. It offers benefits like improved communication, innovative material applications, guaranteed scan tools, precise and economical milling, and convenient and effective use. The system includes the TRIOS intraoral scanner, model scanners, CAD software, milling machines, and sintering furnaces.
Indian Dental Academy: will be one of the most relevant and exciting training center with best faculty and flexible training programs for dental professionals who wish to advance in their dental practice,Offers certified courses in Dental implants,Orthodontics,Endodontics,Cosmetic Dentistry, Prosthetic Dentistry, Periodontics and General Dentistry.
This presentation gives a brief overview of the current intra oral scanner market as of October 2018. Comparisons of accuracy and a brief overview of some of the software packages available to allow you to go to guide.
360 Visualise: Last year 360 Visualise sold more CBCT in the UK than any other company. Our first scanning centre in Ilkley was the first independent CBCT referral centre outside of London and we now scan over 3000 patients each year. This experience gives us a unique insight into the clinical needs and processes of the dental profession and what can be achieved with new software packages.
New processes are quickly developing enabling implant dentists to quickly scan, plan and print implant drilling guides using third-party applications such as SMoP & BlueSkyBio. The price of these services has reduced dramatically over the past year and with increased competition is set to continue to improve and become more accurate and efficient.
Working with so many dentists and labs, 360 Visualise are in a unique position to support you and your 3D scanner as this incredible technology continues to evolve over the coming years.
Brief introduction to the latest innovations that are used at dentistry, where equipment used are fully digitized and computerized, with the differences between using conventional methods and digital equipment in dentistry.
Main equipment to be discussed are dental imaging systems and CAD/CAM systems
The presentation gives you an overview of the digital impression as well as intraoral scanners. Trios 3 of 3Shape was specifically discussed in the presentation.
1. Removable partial dentures (RPDs) are still commonly used to restore partial edentulism despite the availability of dental implants. New trends include using thermoplastic materials and additive manufacturing techniques for RPD frameworks to improve esthetics and mechanical properties over conventional metal frameworks and acrylic denture bases.
2. Digital technologies now allow for computer-aided design and 3D printing of RPD frameworks, reducing fabrication time and costs compared to conventional casting methods. However, challenges remain with casting precision and long-term performance of 3D printed frameworks.
3. Promising new materials for RPD frameworks include titanium, zirconia, and carbon-fiber reinforced polymers which have better biocomp
Intraoral scanners for digital impressions aren't what they used to be. In fact, they' re becoming the standard of care. If you're thinking of purchasing one, here are the factors you'll need to consider.
For more information, you can book an appointment at
Dr Sachdeva's Dental Aesthetic And Implant Institute,
I 101, Ashok Vihar Phase 1, Delhi- 110052
Contact us at
• Phone : +919818894041,01142464041
• Our Websites:
• www.sachdevadentalcare.com
• www.dentalclinicindelhi.com
• www.dentalimplantindia.co.in
• www.dentalcoursesdelhi.com
• www.facialaestheticsdelhi.com
• Google+ link: https://goo.gl/vqAmvr
• Facebook link: https://goo.gl/tui98A
• Youtube link: https://goo.gl/mk7jfm
• Linkedin link: https://goo.gl/PrPgpB
• Slideshare link : http://goo.gl/0HY6ep
• Twitter Page : https://goo.gl/tohkcI
• Instagram page : https://goo.gl/OOGVig
The student team conducted research to determine if 3D printing could improve the manufacturing process of child ankle-foot orthosis (AFOs). They tested various materials for strength and fatigue resistance and found PETG to have the best balance of properties. While PLA and PETG may work for prototypes or temporary use, long-term viability is uncertain. The team concluded 3D printing could save significant time over traditional methods but recommended further testing to identify materials suitable for patient needs.
15 Online Experts for Boosting Your Plastics BusinessHerwig Juster
Everybody wants to turn daily business operations in polymer engineering more effective and efficient! Using mobile apps instead of old design guides and large excel calculation tables to quickly calculate daily needed engineering parameters such as clamping force or residence time may be a way to follow. Another way is to use free online sources. These eliminate the need of having several apps on your mobile phone.
This document provides an overview of 3D printing including its definition, history, materials used, mechanism, applications in dentistry, and comparisons to CAD/CAM. It discusses the development of 3D printing from its origins in 1984 to current uses like dental modeling and surgical guides. Applications in maxillofacial surgery, orthodontics, prosthodontics and endodontics are also covered. The document concludes by discussing emerging technologies like bioprinting, where living cells are used as "bioinks" to print tissues, and 4D printing, where printed objects can change shape over time in response to environmental conditions.
Improving Prosthetic Patient Care Through 3D Technology1Jessica Zistatsis
This document discusses using 3D technology to improve the process of fabricating prosthetic devices. Currently, fabrication is a manual multi-week process. The author proposes using 3D scanning and carving to decrease fabrication time from weeks to days, lower costs, increase reproducibility, and improve patient safety and comfort by eliminating plaster casting. Research identified several 3D scanning and carving systems that could scan the residual limb in under a minute and carve a test socket within 10 minutes, allowing same-day fittings. This proposed process is estimated to reduce labor costs by $614 per socket while improving quality and patient experience.
applications of 3d printing in dental prosthodonticsahmedgamal968279
applications of 3d printing in dental prosthodontics including the history of 3d printers and types of 3d printers and different applications of 3d printers in dentistry and different and recent martials used with this technique
The document summarizes a research proposal for designing an automatic plastic bottle trimming machine. It discusses the need for such a machine in the plastic manufacturing industry and related works that have tried to address bottle trimming. The proposed design will utilize pneumatic systems and an automatic feeding mechanism to trim bottles, collecting trimmed pieces for recycling rather than waste. This addresses sustainability and cost concerns of previous solutions. The research plan involves studying differences from existing designs, material availability, testing functionality, impacts on industry productivity, and advantages over current trimming methods.
This document summarizes an experiment conducted to determine the significant parameters affecting the shear strength of hot-air welds between polypropylene rod material and twintex composite material. The experiment tested different welding temperatures, feed rates, and fan speeds using a designed experiment approach. Samples were tested and data was analyzed to make recommendations for further testing.
The document discusses the creation and comparison of 3D-printed and finite element analysis (FEA) models of a porcine lumbar vertebra created using various open source software packages. Key findings include:
- 3D-printed models created with 3D-Slicer and MIMICS software were measured and found to be geometrically similar, with minor differences attributed to smoothing and measurement errors.
- FEA models were significantly stiffer than actual test results and published data. The model using equations from Morgan et al. was closest but still stiffer.
- Customizing material properties in the FEA model improved results, but equations require further validation.
- The study demonstrated a process for creating
This document describes a study that used design of experiments to optimize the mechanical properties of parts made with fused deposition modeling (FDM) using polylactic acid (PLA) filament. The study evaluated the effects of various FDM process parameters like extrusion temperature, print orientation, layer thickness, and print speed on the mechanical properties of PLA parts, including yield strength, Young's modulus, and fracture toughness. Using a Taguchi design of experiments approach, the number of experiments needed was reduced from over 1,000 to just 144. Tensile and fracture test specimens were 3D printed and tested to determine how the process parameters affected the mechanical properties.
This document describes the development of a device capable of applying a polymer blend via blow spinning laparoscopically. The current method requires open surgery. The researchers designed a 5mm diameter, 20-30cm long device that can withstand pressures of 15mmHg and successfully deliver PLGA/PEG polymer nanofibers during testing. Future work includes animal studies and a trigger mechanism to control polymer release. The global market for laparoscopic devices is growing, indicating potential for this technology.
Design Evaluation and Development of Lumbar Cageijtsrd
Lumbar spinal fusion is advance method of surgery to permanently join or fuse two or more vertebrae in the human spine in order to eliminate the relative motion between them. It is currently considered as the most successful surgery in the patients with spinal deformity and degenerative spondylolisthesis. Its success critically depends on the geometric design of the interbody cages and the material properties of the material used. The main objective of this work is to design analyse and develop a 3D model of the intervertebrae disc for human lumbar spine based on anatomical reverse engineering techniques ARE techniques such as magnetic resonance imaging MRI scan. For this purpose, the sizes of L4 L5 which are the largest vertebrae of the human spine, were observed and modeled accordingly by using CREO with standard dimensions. The prototype was made with PLA plastic using an FDM 3D printer. The analytical tests were carried on ANSYS by applying various complex motions on the intervertebrae disc surface and the stress distributions were compared for the optimization of lumbar cage design. The compression force was applied on the prototype and observed till failure. Results obtained were compared for static position of the lumbar cage, of both analytical and physical outcomes. T. Venkataramana | E. Srinath Reddy | E. Pavan Kumar | B. Chenna Keshavulu ""Design Evaluation and Development of Lumbar Cage"" Published in International Journal of Trend in Scientific Research and Development (ijtsrd), ISSN: 2456-6470, Volume-4 | Issue-2 , February 2020,
URL: https://www.ijtsrd.com/papers/ijtsrd30136.pdf
Paper Url : https://www.ijtsrd.com/engineering/mechanical-engineering/30136/design-evaluation-and-development-of-lumbar-cage/t-venkataramana
3D printing technology builds objects layer by layer from digital models, opening new possibilities in design and customization. It is hailed as a versatile and disruptive technology that will transform sectors like healthcare, aerospace, education, and consumer goods. 3D printing works by building up layers of materials like plastic or metal to form objects. It is used to create models, prototypes, tools, spare parts, and more. The choice of materials depends on the type of 3D printing and the object's requirements, with common materials including plastics, metals, ceramics, and composites.
A prosthetic is a device that replaces any missing human body part visibly and functionally. Reverse engineering is a field of engineering wherein a model and further a prototype can be generated by extracting information from previous design or available model using the advanced tools of CAD/CAM. This paper aims at exploring the needs and advantages of connecting the prosthetic industry with reverse engineering in a developing country like India for patients with lower limb amputations under the brimming concept of “Make in India”.
MWest_5_22156_Tube_Thoracostomy_Airflow_Measurement_and_Management-1matthew west
The document describes a project to design a device called the Pleural Air Leak Measurement Device (PALMD) to accurately measure airflow from chest drain catheters. It provides background on chest drains and tube thoracostomy surgery. The research question aims to determine the optimal sized chest tube catheter by measuring and comparing the airflow rates of different sized catheters. The document outlines the project scope, design process, testing completed, and results which found that a smaller chest tube catheter can handle high airflow volumes as effectively as a larger catheter.
The life cycle analysis evaluated the environmental impact of a concrete masonry unit (CMU) block from extraction of raw materials to end of life. It found that while sand and aggregate make up most of a block's mass, cement production requires the most energy and has the highest global warming potential. Manufacturing the blocks, especially curing them in a kiln, also uses significant energy. The goal was to identify ways to reduce a block's environmental impact by examining each stage of its life cycle.
This document summarizes a study that used finite element analysis to analyze the stress distribution in transfemoral prosthetic sockets made of different materials and geometries. A 3D model of a prosthetic socket was developed and analyzed in Solidworks. Various materials were tested including PEEK, Perlon, and glass fiber. The results showed that a PEEK socket design provided the best results with 94.64% stress reduction compared to other materials. The study aims to identify optimal socket designs that improve comfort and reduce failure rates by better distributing stresses on the residual limb. Future work could involve analyzing different soft tissue and residual limb shapes to make the models and results more applicable.
PriMA is developing a lower-cost prosthetic arm using 3D printing and sensory feedback. The project is being conducted by interdisciplinary students at Florida Institute of Technology as part of their capstone design project. The goal is to create an affordable prosthetic arm option with high functionality. The team aims to eventually start a 3D printing technology company and bring innovation to the prosthetics industry.
Olloclip Advances iPhone Camera Capabilities With 3D PrintingDesign World
olloclip advances iPhone camera capabilities with 3D printing. The company has used 3D printing throughout its product development process, printing prototypes on an Objet printer to validate designs. 3D printing has allowed olloclip to rapidly iterate on designs and shrink the time between development and production. The presentation discusses olloclip's history, product development workflow involving 3D printing, and its choice of the Objet printer for capabilities like high resolution and ability to print multiple materials.
This document discusses the motivation and origins for designing a system to measure footplate pressure on a rowing ergometer. The author aims to improve rowing technique and prevent injury by providing feedback on footplate pressure. Currently ergometers do not provide any data from the footplate, despite it being a key area for power transfer. The author proposes using sensors to measure footplate pressure and provide visual and audio feedback to users. The goal is to develop a low-cost, portable device that can benefit both rowers and the wider gym community by promoting better technique and reducing back injuries from improper ergometer use.
1. 1
Derrick,Horner,Le,Walters2016
Project Report
ENSC29: 3D Printed Child Ankle Foot Orthosis (AFO)
Updated 04/20/2016
Introduction:
Prosthetics and orthotics are oftentimes necessary for a variety of patients, but can also be very costly for
both patients and their hospitals. The manufacturing processes for some of these devices require a
significant amount of time and resources,which can be inconvenient for every party involved. Shriners
Hospital for Children has expressed a need to improve the process of designing and constructing child
orthotics, involving materials research and 3D printing design to minimize time, materials, and steps in
the fabricating process.
Objective:
The main goal for this project was to assist Shriners Hospital and its leading orthoptist, Dr. Peter
Springs, with providing high-quality orthoses to children within an optimized time-frame. The main
purpose of our project is to create a basic design of an Ankle Foot Orthosis (AFO) using materials that
meet the strength, flexibility, and durability requirements for patients. Creating a simple, easily printed
AFO with the best composition and geometry to meet strength and comfort requirements is our top
priority. To avoid the delays caused by trial and error, production, and shipping, 3D printed designs will
be developed to reduce testing and development time and to quickly enable use by patients. In addition,
severaltypes of printer filaments will be researched and an optimal material that meets strength and
functionality requirements while minimizing cost will be determined.
Background:
The current process for those in need of an AFO brace is a timely and costly manner due primarily to time
consuming stages of AFO fabrication. A 3D-printed rapid prototyping process for these braces is the next
step for reducing cost and time.
There are currently a couple major projects delivering 3D printed prosthetics to children, however there
are very few for braces,as these bring in less profit for large orthotic and prosthetic manufacturing
companies. The current process for Shriners Hospital to produce an AFO consists of severalinvolved
steps.
First the patient's leg and foot are scanned and the digital 3D model is edited by the orthotist. This model
is then sent to Portland, Oregon where a physical positive mold of the foot is carved out of foam. The
brace itself is then fabricated by vacuum forming a sheet of plastic (usually polypropylene or a copolymer
of such) over the positive mold. After fabrication is completed, it is sent back to Shriners Hospital in
Spokane or any other Shriners location around the country. The patient is then fitted with the brace,and
finishing touches such as trimming and flaring are added.
In total this process can take as many as three weeks,and cost as much as $2000 for the patient.
2. 2
Derrick,Horner,Le,Walters2016
Requirements:
These are a list of this project’s requirements, as instructed by Dr. Springs and the project advisor Patrick
Nowacki:
Customer:
Produce a children's leg brace via 3D printer that has equivalent or better specifications compared to the
current molded process.
Engineering:
1. Produced pieces must have consistently comparable strength to the current manufacturing
process,using Proteus NaturalCo-Polymer Polypropylene.
2. Produced pieces must be printable up to the size of the statistically tallest child that qualifies to
have an orthotic brace made by Shriners hospital, between 18 and 24 inches.
3. The thickness of the brace must be as thin as possible, preferably between 1.5 and 5
millimeters.
4. Lifespan of product must reach a maximum of three years under normal use.
5. Produce a comprehensive visual output of strength characteristics for simple comparison between
3D printed and current brace design.
Marketing:
6. Product must have equivalent design and strength characteristics to the current designs.
7. Product must be as thin and light as possible, for ease of use by the customer.
8. Production process must be simpler than the current process,and preferably of similar or lesser
price.
Constraints:
9. Must involve 3D printing
10. Recommended material of polypropylene
11. Constraints limited to printer available
Budget:
Funding for the AFO research project came from two sources. The largest portion of the funds was
granted from Gonzaga's Engineering Department due to the longevity of this research project. The printer
was purchased to be used by the university for years to come, as research and production will continue
after the preliminary project has finished. Gonzaga's funding equated to around $20,000 and the
remaining portion of funds of an undisclosed amount came from KEEN. This research project received
funding for the 3D printer, the associated printing materials, and any modifications made to the printer.
The project was budgeted to fit within the funding source but also to maximize the printer’s ability and
functionality for its intended purpose. Numerous printers had been considered in order to determine the
best printer for the task at hand.
3DP1000 Large Format 3D Printer with Second Head for Dual Head Print
~$23,000
purchased for school use, funded by engineering departments
Materials
3kg Polypropylene filament: $50/kg $150
3. 3
Derrick,Horner,Le,Walters2016
3kg Carbon Fiber PLA: $66/kg $198
3kg PLA: $27/kg $81
3kg PETG: $48/kg $144
2lbs PCTPE Nylon: $38/lb $76
Other
20 pieces of polypropylene Water-Jet cut $40
Total Material Budget Requested: $689
Liaison Collaboration:
There were severalinstances in which face-to-face collaboration between this group and Dr. Springs was
necessary. Two visits to Shriners Hospital consisted of witnessing how Dr. Springs’ Spectra 3D Scanner,
which is manufactured by Vorum, as well as taking a tour of the space where he modifies his patients’
AFOs by hand. Samples of both copolymer and homopolymer polypropylene to use in comparison to
current materials were also received during these visits. Dr. Springs took severaltrips to Gonzaga
University as well, mainly to discuss updated designs and the overall progress of the project – specifically
on the software side – as well as to discuss the crucial forces an AFO experiences during normal use.
3D Printing Procedure:
From 3D scan to the final print, the process is pretty simple but required constant monitoring at first.
After receiving the 3D scan from Dr. Springs which was created from a cast of the patient’s foot, the scan
is uploaded into MeshMixer, a free AutoDesk 3D modeling software. The reason MeshMixer was used as
opposed to SolidWorks was because 3D scans generate numerous faces on the 3D model to the order of
104
which requires heavy computational power to render, power that exceeds the limits of SolidWorks.
In MeshMixer, the scan is received as a 2D surface that must be extruded to a specified thickness that
creates the 3D model for the printer. The newly-created 3D model is exported to Simplify, a 3D modeling
software used specifically in conjunction with 3D printers such as the 3DP100. The model can be literally
be dropped into a 3D generated print bed displayed in the program and then shifted or moved for ease of
access during the print.
Within the specific settings of Simplify, the nozzle and bed temperatures can be set to best print the
designated material. Other features such as a raft and support material can also be adjusted in order to
support the odd shape of the bottom of the leg brace. A full infill of the model is used so that the leg brace
is a solid plastic part. After finalizing the print settings, the file is converted to a .gcode file that can be
read by the 3D printer.
Once the print is initialized and the nozzle and bed are set to the correct temperature,a small skirt is
printed around the model to help the 3D print technician determine if the print head needs to be minutely
lowered or raised to create the best bead and adhesion to the bed. This concludes the print technician's
involvement as the next step is to wait for the print to be completed (~14-16 hours depending on print
speed).
Settings such as temperatures,raft,support material and skirt within Simplify can be preset after
determining the best settings for the desired material to reduce labor and overall print time.
4. 4
Derrick,Horner,Le,Walters2016
Material Testing:
Specifics:
Our project consisted of testing and/or printing with five different materials: polylactic acid (PLA),
carbon fiber reinforced PLA (CFPLA),3D printed polypropylene (3DP PP),polyethylene terephthalate
glycol (PETG), and plasticized copolyamide thermoplastic elastomer (PCTPE) nylon.
Two different experiments were completed for most of these materials. These tests were a tensile strength
test using an MTS Model 45 Electromechanical Monotonic Load Frame tester,and a bending fatigue test.
For the tensile strength tests,ten sample specimens of each material were printed, each about 110 mm ×
5.5 mm × 4 mm. Ten solid polypropylene samples of the same size were also tested, and were water-jet
cut from a sheet of material that was received from Dr. Springs. Test rates for PLA and PETG were 0.008
in/min. For both solid polypropylene and 3DP PP,the test rate was 0.02 in/min, and for CFPLA,the test
rate was 0.012 in/min.
The machine used to test bending fatigue was able to count the number cycles it applied to a sample of
material until failure. The settings used for these tests were 0.9 witness and a threshold of 90%. This
meant the machine would stop once the sample reached 90% of its original strength.
Data Analysis:
Each tensile test gave us the length that each sample was elongated in millimeters, along with the
corresponding force in Newtons that was applied to the sample. Data was taken every second until the
sample failed, at which point the test was stopped. Using this raw data, the associated stress and strain
values for each data point was found for every test. From here least squares regression analysis was
applied and using Excel’s solver add-in, the estimate of Young’s Modulus for each test was calculated.
Averaging these estimates gave an overall value for modulus for each material. Maximum tensile
strengths were also calculated and averaged for every material tested.
Comparison of Results:
At the beginning of our project, it was stated that our goal was to find a 3D-printer filament with material
properties within ± 5% of the corresponding properties for solid polypropylene. This objective was
changed for three reasons: incomparable data,printability of certain materials, and time constraints.
As the following table shows, none of the properties of our selected materials reached the stated goal of ±
5%. This necessitated a rating system in which each material was scored according to their average values
in five categories: Young's Modulus, tensile strength, fatigue results (number of cycles until failure),
printability and repeatability, and cost per kilogram. Each category had a highest possible score of 5, and
each material was ranked based on the order in which their numbers fell.
5. 5
Derrick,Horner,Le,Walters2016
Table 1: Material ratings based on five critical categories.
It can be seen from Table 1 that PLA achieved the highest overall score,followed by PETG, CFPLA,
nylon, and 3DP PP,respectively. PLA scored at least a 4 in each category,and objectively it was by far
the best material tested. However,this table did not take into consideration severalsubjective categories
that were equally important, and therefore the decision on PLA as the one and only material choice could
not be easily made.
It can also be seen that no fatigue tests were completed for 3DP PP and nylon. While this affected the
final scores of these materials, it did not change which ones were either ruled out or recommended. 3DP
PP was ruled out because of its inability to be reliably printed using our printer, and so its material
properties could be deemed irrelevant. Nylon was ruled out because of extreme flexibility and low
modulus.
Figure 0: Fatigue Testing Comparison
Material Modulus (MPa) Score Tensile Strength (MPa) Score Fatigue Result Score Printability/Repeatability Score Cost (per kg) Score Overall Score
Solid PP 1507.72 --- 20.04 --- infinite --- N/A --- $14.00 --- ---
PLA 3930.26 4 42.66 5 13080 4
No warping, sticks to bed
well, layers stick very well to
each other, fast print speed,
very repeatable
5 (tie) $27.00 5 4.6
CFPLA 6501.44 5 39.52 4 2620 3
No warping, sticks to bed
well, layers do not stick
together well, medium print
speed, difficult to load, not
repeatable (inconclusive)
2 $66.00 2 3.2
3DP PP 1316.54 2 16.89 1 N/A
Lots of warping, does not
stick to bed, layers stick
together reasonably well,
very slow print speed, not
repeatable
1 $50.00 3 1.75
PETG 2269.70 3 34.14 3 (tie) 400000 5
No warping, sticks to bed
well, layers stick very well to
each other, fast print speed,
very repeatable
5 (tie) $48.00 4 4
PCTPE Nylon 73.04 1 34.79 3 (tie) N/A
Requires baking before
and/or after printing
3
$83.79
($38.00 per
pound)
1 2
6. 6
Derrick,Horner,Le,Walters2016
Figure 1 shows stress vs. strain curves of each material, plotted together for easy comparison. Each curve
represents a single tensile test done on one sample of each type of filament. It is shown in this graph how
quickly CFPLA failed in relation to its amount of elongation under stress,a sign of how unyielding it
was.
Figure 1: Stress vs. Strain comparison of tested materials.
Both solid polypropylene and 3DP PP elongated much farther than the other materials, at the expense of
having low tensile strengths and modulus numbers. This translated to AFOs made of these materials
possibly having very limited capacities in terms of giving patients the support their legs needed.
It was clear after finishing the tensile tests that PETGwas the best compromise between 3DP PP's
flexibility and CFPLA's stiffness,and it can be seen from Figure 3 that this was the case. However,like
PLA,there were other factors involved that prevented PETGfrom receiving an overall recommendation.
Figure 2 shows the calculated results of Young's Modulus for every test, color coded by type of material.
CFPLA has the highest modulus by a significant margin, followed by PLA and PETG, respectively. 3DP
PP and solid polypropylene, however, are very similar in terms of this particular property. Unfortunately,
for reasons that will be explained further on in this report, 3DP PP was not a viable option for this project.
7. 7
Derrick,Horner,Le,Walters2016
Figure 2: Young’s Modulus comparison of tested materials.
PLA:
While PLA had the highest tensile strength (42.66 MPa),there were concerns about its overall brittleness
and long-term viability. Brittleness is an issue for this application because if the AFO should fail, a brittle
product would more likely break all the way through and become completely useless to the patient.
Brittleness would also lead to breaks that have sharp edges and points, which could lead to patient injury.
However,its impressive tensile strength and modulus numbers minimize the risk of such incidents,
especially when compared to the other materials.
PLA is also known to be susceptible to biodegradation due to moisture adsorption and UV degradation,
which is cause for concern when the goal was to create a product that could sustain three years of normal
use. But PLA's fantastic test results for flexibility and strength, as witnessed by its solid values for both
modulus (3930.26 MPa) and the fatigue test (13,080 cycles),make it a very compelling alternative to the
current polypropylene product.
Carbon Fiber PLA:
It was assumed that CFPLA would be the optimum material choice for this project, considering carbon
fiber’s extreme rigidity and strength. However,when carbon fiber is blended with PLA,it becomes an
exceedingly brittle material with a tensile strength that is actually less than normal PLA. It also scored
poorly when it came to the fatigue tests,leading to a realistic assumption that a full AFO would not last
the required amount of time under normal demands.
Its high average modulus of 6501.44 MPa was 2571.18 MPa greater than the next highest value, which
belonged to PLA. This difference was greater than the modulus value of PETG and showed how rigid the
material was. However,its complete lack of flexibility could possibly lead to patient discomfort, as Dr.
Springs explained that some flexibility is oftentimes desired.
Figure 1 gives a great visual representation of how brittle CFPLA was compared to PLA. It can be seen
that the point of failure for this particular CFPLA sample occurred around 0.011% elongation, compared
to about 0.021% elongation for PLA. The sharper drop off in the curve for CFPLA in contrast to PLA
8. 8
Derrick,Horner,Le,Walters2016
illustrates how the carbon fiber sample failed at a much more rapid pace,and with little warning, a strong
indication of its extreme brittleness.
There were severalprintability issues with CFPLA as well, most notably that the layers would not stick
together as the extruder moved farther from the bed. There were severalhypotheses for this, including
that the extruder was not at a high enough temperature,the baby-step was set too high, and that the
extruder fans should have been turned off during printing. Overall, the printability results were
inconclusive, but the severe brittleness and lack of flexibility of CFPLA lead to it ultimately being ruled
out as an option.
PETG:
With the second highest average score of 4 out of 5, PETGalso came off as a potential candidate for
recommendation. While its greatest trait was the ease with which it could print products reliably (it was
basically identical to PLA in this regard), it also showed great compromise between strength, flexibility,
and lack of brittleness.
While the PLA samples always broke cleanly during the tensile tests,the PETGsamples would break
cleanly only along the outside layers, and then would stretch considerably until it failed completely. This
suggested that if an AFO made of PETGwere to fail under intense stress,the likelihood of it breaking
cleanly all the way through is smaller than PLA,which means the patient might be able to still use it for a
limited time until needing a replacement, and it would reduce the chance of the patient getting injured by
broken sections of the AFO.
Evidence of this behavior can be seen in Figure 3, which shows one test of a PETGsample during the
tensile test. After the initial point of failure at about 0.023% elongation, the curve begins to plateau again,
an indication of the sample not breaking all the way through and elongating further.
Figure 3: Stress vs. strain curve of PETG
However,Dr. Springs was reluctant to recommend PETGfor his own use, as he had had experience with
the material, and explained that it had a tendency to split after long-term use. This was a trait that could
not be tested with the given resources,so it could not be objectively researched. Nevertheless,this
observation by Dr. Springs did prevent PETGto be chosen as the ideal material over PLA.
0
5
10
15
20
25
30
35
0 0.005 0.01 0.015 0.02 0.025 0.03 0.035
Stress(MPa)
Strain (%)
PETG Stress vs. Strain
Stress-Strain Modulus of Elasticity
9. 9
Derrick,Horner,Le,Walters2016
3D Printed Polypropylene:
As stated above, 3DP PP was taken out of consideration not because of its material properties, but
because it was not feasible to produce a working product with the printer used for this project. The reason
3DP PP could not be printed reliably was the fact that its glass transition temperature Tg was well below
room temperature (-10°C to 0°C depending on sources). Each material’s Tg value is the temperature at
which each one will adhere to the printer bed, and our printer’s bed did not have the ability to be set
below room temperature. This caused 3DP PP to curl away from the bed surface during printing which
lead to severe warping of the printed objects. An attempt was made to create a full AFO, but it was unable
to pass more than a few layers before the print was no longer workable.
There are a few companies in the Spokane area that could possibly outsource the printing of
polypropylene products. However,approaching these companies was larger than the scope of this
particular project, and it is unlikely that Shriners would invest the time and resources necessary to pursue
such a venture for its own patients.
PCTPE Nylon:
The modulus and strength results for nylon given in Table 1 were found from the values posted on the
manufacturer’s (Taulman 3D) website for PCTPE nylon, and not actualtest results from this project. The
reason for this was because there was not enough time to print and test samples for both tensile testing
and fatigue testing, and only one AFO could be printed within this limited timeframe. However,using the
data found online, it is clear that nylon’s strength and flexibility properties would not be appropriate for
use with an AFO. It’s modulus of 73.04 MPa was only 5.5% of the material with the next lowest
modulus, 3DP PP,at 1316.54 MPa on average. This meant there would be considerable flex in the AFO
when a given stress was applied in any direction compared to the other materials, giving very limited
amount of support to the patient.
It should be noted that while PCTPE nylon was used for the AFO prototype, further research indicated
that 618 nylon would have been more appropriate to use, given its superior modulus over PCTPE nylon.
The PCTPE nylon that was available to use during the course of the project had been ordered by the
project advisor, and when it was realized that 618 nylon would have been the better material, there was
not enough time left to order it and complete the necessary prints. According to Taulman 3D’s website,
618 nylon has a modulus of 152.99 MPa and a tensile strength of 31.54 MPa,numbers that are still
significantly lower than those of the other tested materials.
Risk/Implementation Issues:
For this project we were mainly focused on the viability of a 3D printed AFO, and not necessarily the
long term use. Therefore,our material choice may not be the most optimal with regards to strength,
weight, durability, and cost. Since the current properties of heat-wrapped polypropylene have been proven
to be sufficient Shriner's patients' needs, any material that can match its strength and durability
characteristics would have worked. However finding a material that can be printed easily that falls into
this category is difficult if not impossible. Based on the data we accumulated, all of our materials were
ruled out either due to inability to print reliably, or due to incompatible strength characteristics. This was
despite adding more materials that were suggested to us later in the process by 3d printing professionals.
We were also worried about the brace failing while a patient is using it, directly harming the patient from
the broken brace or resulting in failure that could lead to a fall, possibly causing a serious health hazard or
fatality, so we opted for a combination of MTS machine tests and bending fatigue tests. Unfortunately
10. 10
Derrick,Horner,Le,Walters2016
this system was not perfect,and results from a long term trial period would be a good idea before
implementing any of our results on an unsuspecting patient. Our initial plan was to test the braces on
ourselves, but due to the medical system's bureaucracy,we were not able to implement this as an option.
While our printer was compatible with a wide range of materials that had a likelihood of satisfying our
requirements, requiring additional parts or modifications to the printer did prove to be an issue. Several
aspects of the printer had to be replaced during the short time we had it and simple modifications were
made to improve our ability to print some of our materials. We limited our modifications to surface
treatments of the bed to improve sticking, but were unable to get a final result with polypropylene due to
the properties of the material while printing. One of the things that unexpectedly took us the longest time
to fix, was the issues we had with software. After spending over a month researching programs it took
our printer instillation technician to help us find the program we needed.
Research:
Preliminary research on the tensile strength of 3D printed PLA was conducted by a student at Gonzaga
University, Luke Blanchart, prior to this project. The research was done using the same MTS machine
and accompanying software as the one used for this project. Supervised by the head of the university’s
mechanical engineering department, Dr. Patrick Ferro, the data was granted to us to by Mr. Blanchart in
order to aid us in our own research.
Additional Internet research was also completed before testing commenced. Research on AFOs and the
reinforcement of such devices using composite materials including PLA and CFPLA was done by Dr.
Kenneth Dalgarno and Dr. Javier Munguia of the School of Mechanical and Systems Engineering at
Newcastle University (Ankle Foot Orthotics Optimization by Means of Composite Reinforcement of Free-
FormStructures,2013). Their research included strength testing of both materials which involved the use
of a 3-point bend test, a test procedure that was not available for this particular project.
Cost Analysis:
One of the largest of areas of focus is the time and cost reduction that is made by 3D printing the AFOs in
comparison to having the model vacuum heat-molded by a separate branch of Shriner's Hospital. This
analysis will only contain the steps beyond the casting of the patient's leg and 3D scan of said cast
because both processes contain these steps.
Time:
The current heat molding process of producing the AFO starts with the 3D scan being sent to a separate
branch of Shiner's Hospital in Portland, Oregon where a foam positive mold is created by a CNC foam
cutter. This foam mold is then used to simulate the patients leg as a heated piece of solid co-polymer
polypropylene is tightly wrapped around the positive mold and the vacuum sealed. The excess material is
cut off to create the hole in the front of the brace for the placement of the leg. This final piece is then sent
back to Shriner's Hospital for final, last minute adjustments. The entire process can take up to 2 weeks
depending on availability of the staff. The setup of the 3D model in Meshmixer and then Simplify with
presets can take a matter of minutes. With the 3D print taking up to 16 hours on a larger model, the 3D
printing process can cut production from a few weeks to a single day.
Cost:
With limited resources from the hospital it is difficult to pinpoint the total savings in dollar amounts by
3D printing the AFO but many assumptions can be made that point to the cost savings from 3D printing.
11. 11
Derrick,Horner,Le,Walters2016
3D printing only uses the required material unlike the heat molded process that has excess
material wasted after trimming away from leg hole (Each AFO uses about 0.5kg of material).
3D printing is all in-house and doesn’t require shipping the AFO from branch to branch.
3D printing is not labor intensive. After setting up the model in software,3D printing only
requires monitoring of the print for the first few layers to check adhesion to the print bed.
3D printing materials are relatively cheap and will continue to decrease in price with the growing
interest in the technology (current pricing of material listed below).
o Cheap PLA 3D printed prototypes can be made to test fit with the patient before using a
more expensive material for the final product.
Final Deliverables:
Based on what Dr. Springs originally requested, our final deliverable will be the full scale AFOs we
printed. Some more additions we are going to present are our material research,from each of the
materials we tried to make an AFO from, as well as our personal recommendation based on our research
and experience with printing. We are also including a comprehensive video on how to get the scan to a
printable file type, and recommending settings on the printer for each material.
Conclusion:
Based on our results, while we feelwe did prove to Dr. Springs that a 3D printable ankle foot orthosis is
possible to print physically, we have insufficient data to recommend any materials we tested. There is
however significant viability in this project for future years. Outlined in our initial proposal was the fact
that further progress could have been possible were it not for our limited timeframe. Not only will the art
of 3D printing evolve with advancements in materials and technology, but our research will be used in
future years for related projects. Shriners Hospital has already agreed to liaison for more projects and we
have several directions in which those projects could take using our initial results.
Future Projects:
One of the test procedures that this project did not have the opportunity of undertaking was the
application of the 3D printed AFOs in field tests. This prevented elaborate research into the long-term
viability of each material, such as normal wear and tear,the effect of humidity and UV radiation, and
damage caused by walking on rough surfaces. While jumping through all the hoops necessary in order to
allow an actualpatient to test a 3D printed AFO prototype may not be the best use of time, an experiment
that could model such a durability test would be an interesting project for future groups to carry out.
Examining patients’ gait cycles is another area of research that can branch from the findings of this
project. Analyzing the areas of maximum stress on an AFO could lead to innovative geometries such as
structural reinforcements, varying thicknesses, and combinations of materials that are only possible with
12. 12
Derrick,Horner,Le,Walters2016
3D printed parts. Dr. Springs has access to software which can diagnose how a certain patient walks and
can from there, the best geometry for the patient’s own AFO can be determined.
While the outsourcing of printed polypropylene AFOs was not within the scope of this project, it is
possible that future groups could look into such measures. This way, a full scale 3DP PP AFO could be
compared to the solid polypropylene model, and durability and strength tests could be successfully
completed.
As 3D printing technology advances,so too will the potential for more research into this topic. It is
entirely possible that new 3D filament materials will be produced in the next few years,materials that
could combine the best attributes of those that were tested for this project, while having superior
durability characteristics. There could also be nonindustrial 3D printers created in the near future that are
capable of printing with polypropylene, therefore outsourcing the manufacturing process would not be
necessary.