The document discusses the role of chemicals in the construction industry, focusing on corrosion inhibitors and superplasticizers. It provides an overview of how corrosion inhibitors and superplasticizers improve concrete properties like workability and durability. It also describes CSIR-SERC's research on corrosion inhibitor and superplasticizer performance, including fabric reinforced concrete. The document outlines techniques for evaluating inhibitor efficiency and assessing corrosion in reinforced concrete structures.
Use of chemical admixtures and mineral additives in various kinds of high performance and high strength concrete is essential. I have explained how it works.
Use of chemical admixtures and mineral additives in various kinds of high performance and high strength concrete is essential. I have explained how it works.
Introduction- Classification of cements - Portland Cement
Raw materials of Portland cement - Cement Manufacturing Process - Flow chart of Portland Cement manufacturing process - Cement Manufacturing Video - Mixing and Crushing
Dry Process - Wet Process - Burning Process - View of complete setup - Rotary Klin zones - Chemical Reactions -
Grinding and Packaging - Setting and hardening - Flow chart
Sequence - Chemical Reactions - Special Cement -
A Strategic Approach: GenAI in EducationPeter Windle
Artificial Intelligence (AI) technologies such as Generative AI, Image Generators and Large Language Models have had a dramatic impact on teaching, learning and assessment over the past 18 months. The most immediate threat AI posed was to Academic Integrity with Higher Education Institutes (HEIs) focusing their efforts on combating the use of GenAI in assessment. Guidelines were developed for staff and students, policies put in place too. Innovative educators have forged paths in the use of Generative AI for teaching, learning and assessments leading to pockets of transformation springing up across HEIs, often with little or no top-down guidance, support or direction.
This Gasta posits a strategic approach to integrating AI into HEIs to prepare staff, students and the curriculum for an evolving world and workplace. We will highlight the advantages of working with these technologies beyond the realm of teaching, learning and assessment by considering prompt engineering skills, industry impact, curriculum changes, and the need for staff upskilling. In contrast, not engaging strategically with Generative AI poses risks, including falling behind peers, missed opportunities and failing to ensure our graduates remain employable. The rapid evolution of AI technologies necessitates a proactive and strategic approach if we are to remain relevant.
Embracing GenAI - A Strategic ImperativePeter Windle
Artificial Intelligence (AI) technologies such as Generative AI, Image Generators and Large Language Models have had a dramatic impact on teaching, learning and assessment over the past 18 months. The most immediate threat AI posed was to Academic Integrity with Higher Education Institutes (HEIs) focusing their efforts on combating the use of GenAI in assessment. Guidelines were developed for staff and students, policies put in place too. Innovative educators have forged paths in the use of Generative AI for teaching, learning and assessments leading to pockets of transformation springing up across HEIs, often with little or no top-down guidance, support or direction.
This Gasta posits a strategic approach to integrating AI into HEIs to prepare staff, students and the curriculum for an evolving world and workplace. We will highlight the advantages of working with these technologies beyond the realm of teaching, learning and assessment by considering prompt engineering skills, industry impact, curriculum changes, and the need for staff upskilling. In contrast, not engaging strategically with Generative AI poses risks, including falling behind peers, missed opportunities and failing to ensure our graduates remain employable. The rapid evolution of AI technologies necessitates a proactive and strategic approach if we are to remain relevant.
The Roman Empire A Historical Colossus.pdfkaushalkr1407
The Roman Empire, a vast and enduring power, stands as one of history's most remarkable civilizations, leaving an indelible imprint on the world. It emerged from the Roman Republic, transitioning into an imperial powerhouse under the leadership of Augustus Caesar in 27 BCE. This transformation marked the beginning of an era defined by unprecedented territorial expansion, architectural marvels, and profound cultural influence.
The empire's roots lie in the city of Rome, founded, according to legend, by Romulus in 753 BCE. Over centuries, Rome evolved from a small settlement to a formidable republic, characterized by a complex political system with elected officials and checks on power. However, internal strife, class conflicts, and military ambitions paved the way for the end of the Republic. Julius Caesar’s dictatorship and subsequent assassination in 44 BCE created a power vacuum, leading to a civil war. Octavian, later Augustus, emerged victorious, heralding the Roman Empire’s birth.
Under Augustus, the empire experienced the Pax Romana, a 200-year period of relative peace and stability. Augustus reformed the military, established efficient administrative systems, and initiated grand construction projects. The empire's borders expanded, encompassing territories from Britain to Egypt and from Spain to the Euphrates. Roman legions, renowned for their discipline and engineering prowess, secured and maintained these vast territories, building roads, fortifications, and cities that facilitated control and integration.
The Roman Empire’s society was hierarchical, with a rigid class system. At the top were the patricians, wealthy elites who held significant political power. Below them were the plebeians, free citizens with limited political influence, and the vast numbers of slaves who formed the backbone of the economy. The family unit was central, governed by the paterfamilias, the male head who held absolute authority.
Culturally, the Romans were eclectic, absorbing and adapting elements from the civilizations they encountered, particularly the Greeks. Roman art, literature, and philosophy reflected this synthesis, creating a rich cultural tapestry. Latin, the Roman language, became the lingua franca of the Western world, influencing numerous modern languages.
Roman architecture and engineering achievements were monumental. They perfected the arch, vault, and dome, constructing enduring structures like the Colosseum, Pantheon, and aqueducts. These engineering marvels not only showcased Roman ingenuity but also served practical purposes, from public entertainment to water supply.
Model Attribute Check Company Auto PropertyCeline George
In Odoo, the multi-company feature allows you to manage multiple companies within a single Odoo database instance. Each company can have its own configurations while still sharing common resources such as products, customers, and suppliers.
Acetabularia Information For Class 9 .docxvaibhavrinwa19
Acetabularia acetabulum is a single-celled green alga that in its vegetative state is morphologically differentiated into a basal rhizoid and an axially elongated stalk, which bears whorls of branching hairs. The single diploid nucleus resides in the rhizoid.
Read| The latest issue of The Challenger is here! We are thrilled to announce that our school paper has qualified for the NATIONAL SCHOOLS PRESS CONFERENCE (NSPC) 2024. Thank you for your unwavering support and trust. Dive into the stories that made us stand out!
Unit 8 - Information and Communication Technology (Paper I).pdfThiyagu K
This slides describes the basic concepts of ICT, basics of Email, Emerging Technology and Digital Initiatives in Education. This presentations aligns with the UGC Paper I syllabus.
June 3, 2024 Anti-Semitism Letter Sent to MIT President Kornbluth and MIT Cor...Levi Shapiro
Letter from the Congress of the United States regarding Anti-Semitism sent June 3rd to MIT President Sally Kornbluth, MIT Corp Chair, Mark Gorenberg
Dear Dr. Kornbluth and Mr. Gorenberg,
The US House of Representatives is deeply concerned by ongoing and pervasive acts of antisemitic
harassment and intimidation at the Massachusetts Institute of Technology (MIT). Failing to act decisively to ensure a safe learning environment for all students would be a grave dereliction of your responsibilities as President of MIT and Chair of the MIT Corporation.
This Congress will not stand idly by and allow an environment hostile to Jewish students to persist. The House believes that your institution is in violation of Title VI of the Civil Rights Act, and the inability or
unwillingness to rectify this violation through action requires accountability.
Postsecondary education is a unique opportunity for students to learn and have their ideas and beliefs challenged. However, universities receiving hundreds of millions of federal funds annually have denied
students that opportunity and have been hijacked to become venues for the promotion of terrorism, antisemitic harassment and intimidation, unlawful encampments, and in some cases, assaults and riots.
The House of Representatives will not countenance the use of federal funds to indoctrinate students into hateful, antisemitic, anti-American supporters of terrorism. Investigations into campus antisemitism by the Committee on Education and the Workforce and the Committee on Ways and Means have been expanded into a Congress-wide probe across all relevant jurisdictions to address this national crisis. The undersigned Committees will conduct oversight into the use of federal funds at MIT and its learning environment under authorities granted to each Committee.
• The Committee on Education and the Workforce has been investigating your institution since December 7, 2023. The Committee has broad jurisdiction over postsecondary education, including its compliance with Title VI of the Civil Rights Act, campus safety concerns over disruptions to the learning environment, and the awarding of federal student aid under the Higher Education Act.
• The Committee on Oversight and Accountability is investigating the sources of funding and other support flowing to groups espousing pro-Hamas propaganda and engaged in antisemitic harassment and intimidation of students. The Committee on Oversight and Accountability is the principal oversight committee of the US House of Representatives and has broad authority to investigate “any matter” at “any time” under House Rule X.
• The Committee on Ways and Means has been investigating several universities since November 15, 2023, when the Committee held a hearing entitled From Ivory Towers to Dark Corners: Investigating the Nexus Between Antisemitism, Tax-Exempt Universities, and Terror Financing. The Committee followed the hearing with letters to those institutions on January 10, 202
Francesca Gottschalk - How can education support child empowerment.pptxEduSkills OECD
Francesca Gottschalk from the OECD’s Centre for Educational Research and Innovation presents at the Ask an Expert Webinar: How can education support child empowerment?
How to Make a Field invisible in Odoo 17Celine George
It is possible to hide or invisible some fields in odoo. Commonly using “invisible” attribute in the field definition to invisible the fields. This slide will show how to make a field invisible in odoo 17.
1. CSIR-SERC
Role of Chemicals in Modern
Construction Industry
Dr Nagesh R Iyer, Director, CSIR-SERC
&
Ms. B. Bhuvaneshwari, QHS, CSIR-SERC
2. CSIR-SERC
OUTLINE
Role played by the chemicals in construction
industry – in general
Relevance
Market survey
Role of Corrosion inhibitor and Superplasticisers in
construction industry
Trends and Opportunities
Inhibitor and Superplasticiser Research at CSIR-
SERC
Concluding remarks
3. CSIR-SERC
Role played by chemicals in construction industry – in general
1
• Corrosion protection
• Inhibitors, Protective coating for steel
2
• Superplasticiser – Heavy reinforcement – HPC, UHSC (RPC)
• Modern construction (RMC), Foam Concrete-Light weight
structures- Earth quake prone area
• easy mix, workability, mouldability
3
• Adhesives and sealants
• water proof admixtures to seal the crack etc.
4. CSIR-SERC
• Mass concreting
• Pumping of RMC
• Mouldability
• Faster construction
• Minimization of labour
Relevance – Chemical Admixtures
5. CSIR-SERC
2009 2014
Average Annual
Growth Rate,
2009-2014 (percent)
North America 4,684 5,650 3.8
Cental and South Americaa 1,815 2,317 5.0
Western Europe 6,557 7,577 2.9
Central and Eastern Europe 988 1,186 3.5
Middle East and Africaa 1,827 2,399 5.6
Japan 3,560 3,578 0.1
China 7,868 12,106 9.0
Asia/Oceaniaa 3,400 4,339 5.0
Total 30,699 39,152 5.0%
Chemicals and Construction: Building a future together
a Data are estimates based on percentage of GDP by
construction industry, extent of informal sector and
technological standards available
World market for construction chemicals (US$ millions)
6. CSIR-SERC
The global construction industry makes up about 9 percent of
the world's GDP and construction is one of the main drivers of
growth in almost every economy
As with other areas of the specialty chemicals sector, the
construction chemicals industry is directly affected by
increased globalization, consolidation and significant
consumption growth in rapidly developing markets
The construction chemicals industry will see continued
opportunities to address energy conservation and
sustainability. Suppliers can benefit from government policies
that require the use of specialty construction chemical
products to aid in energy conservation
Growing awareness of climate change will drive the demand
for energy-saving materials and technologies, chemicals that
increase performance and environment friendly products
Trends and Opportunities
8. CSIR-SERC
1. Repair and Rehabilitation- Retrofit –
grouts, Fibre reinforcement, Fabric
reinforced
2. Chloride extraction: to control
corrosion – to extract chloride –
MAINLY IN MARINE ENVIRONMENT
3. Corrosion Inhibitor: Migrating – High
dose causes deleterious effect
Focus from Top-down
Wire Fabric
Corrosion beneath concrete
Improper use of Sp
9. CSIR-SERC
Chemicals as bonding agent in fabric reinforced concrete
FABcrete - Ongoing research at CSIR-SERC
•New innovative building material with a fabric
reinforcement embedded in a cementitious binder
• Alternate and combining component to common building
materials such as steel or shot fibre reinforced concrete
•Made of fabric meshes of long woven, knitted or even
unwoven, fibre rovings - two directions of glass, carbon
or aramid that are alkali resistant and thus not
vulnerable to corrosion
• Role of polymer modified binder for FABcrete
• Combination of cementitious binder with polymer based binders
• Even dispersion and penetration into the filaments in the fabrics
• Used as gripping agent – adhesive property
11. CSIR-SERC
• During calcination, the volume contracts
Cement Chemistry
CaCO3(s) = CaO(s)+CO2(g)
• During hydration, it swells
CaO(s)+H2O(l) = Ca(OH)2(s)
• Cement – hydraulic binder
12. No sufficient time to react
State of chemical equilibrium is reached
Raw Materials
Lime
Silica
Alumina
Fe2O3
kiln complex products uncombined lime
Uncombined lime
13. CSIR-SERC
• Chemical components in portland cement
form different potential compounds
• Potential compounds responsible for
various physical properties
Function of Chemical Components
14. Four Major Compounds
C3S
C2S
C3A
C4AF
responsible for strength of hydrated cement paste
undesirable – initial reaction with SP & CI
small quantity - does not affect the cement
behaviour
15. CSIR-SERC
Variations in Chemical Constituents
Hardening / Hydration
Setting Time
Corrosion Resistance
Color
Affect Cement Properties
16. Cement Hydration
Reaction of cement with water
Exothermic; heat released is called ‘Heat of
Hydration’
Rate of heat evolution is faster, if the reaction
is quicker
Heat evolved depends on heat of hydration of
individual compounds and on the clinker
morphology
17. Hydration Process (continued)
• Setting – Solidification of the plastic cement
paste
• Initial set – Beginning of solidification-Paste
become unworkable - loss in consistency –
not < 45 min
• Final set – Time taken to solidify completely –
not > 375 min
• Hardening – Strength gain with time – after
final set
18. Beginning of Mechanical
Strength
Transition
settings
Rigid
Final set
Initial set
Time
Limits of Handling
SettingDormant
period
Cement
Capillary
pores Hydration products
Initial set Final set
Hardening
Addition
of water
Rigidity
(a)
(b)
Hydration Process (continued)
19. Hydration of Portland Cement (continued)
• Sequence of overlapping chemical reactions
• Hydration reactions of individual clinker
mineral proceed simultaneously at differing
rates and influence each other
• Complex dissolution and precipitation
process
• Leading to continuous paste stiffening and
hardening
21. Hydration of Portland Cement (continued)
SettingDormant period
Minutes HoursAge
Hardening
Days
Ettringite
C4(A,F)H13
CSHPorosity
CSH
Amount
22. Hydration of Calcium Silicates
3 3 2 3
2 3 2 3
2C S + 6H C S H + 3CH
tricalcium Water C-S - H calcium
silicate hydroxide
2C S + 4H C S H +CH
tricalcium Water C-S - H calcium
silicate hydroxide
dicalcium
silicate
23. The principal product is calcium silicate hydrate
• Poorly crystalline material
• Small particle (< 1mm) in any dimension
• Composition varies over a wide range
Calcium hydroxide is a crystalline material with a
fixed composition
Calorimetric curve – rate of heat evolution with time
Heat flow is proportional to rate of reaction
Hydration of Calcium Silicates (continued)
24. Hydration of C3S
Stage 1
• On contact with water, calcium and
hydroxide ions are released from the
surface of C3S grains
• Rapid heat evolution & pH rises over 12
within minutes
• Ceases in 15 minutes
25. Hydration of C3S (continued)
Stage 2
• Dormant period
• Needed to reach critical concentration of
calcium and hydroxide ions
• Hydrolysis slows down in the dormant period
• Responsible for plastic state of concrete
• Lasts between 2 and 4 hours
• Then, C3S reacts again
26. Stage 3
• Acceleration period
• Nuclei forms and hydration products (CH, C-S-H)
begin to crystallize from solution and the reaction of
C3S proceeds rapidly
• CH crystallizes from solution
• C-S-H develops at the surfaces of the C3S grains,
developing a coating
• Maximum rate of heat evolution at 4 to 8 hrs
Hydration of C3S (continued)
27. Hydration of C3S (Alite) (continued)
Stage 4
• Rate of reaction slows down
Stage 5
• Steady state within 12 to 24 hrs
• As coating of C3S grain (hydrate layer) grows water must
flow through the barrier to reach unhydrated C3S
• Eventually water reaches unhydrated C3S through
diffusion
• Diffusion-controlled reactions are slow
• Hydration tends to reach 100% completion asymptotically
28. Hydration of C2S (Belite)
• C2S reacts in the same way as C3S
grains
• Except that the reaction is much
slower
29. Hydration of C3A
• C3A reacts with sulfate ions supplied by
dissolution of gypsum
• Primary initial reaction of C3A
• C3A + 3CSH2 + 26H → C6AS3H32
30. • Ettringite is stable only when there is an
ample supply of sulfate
• If sulfate is consumed before complete
hydration of C3A, ettringite transforms into
monosulfoaluminate
• 2C3A + C6AS3H32 + 4H → 3C4ASH12
Hydration of C3A (continued)
31. Hydration of C4AF (Ferrite)
• Forms same reactions as C3A, but to a lesser
degree
• Uses small amount of gypsum
• C4AF + 2CH +14H C4(A,F)H13 + C2(A,F)H3
• Similar to monosulfoaluminate amorphous
40. CSIR-SERC
CI
ACI
NACE
• Chemical cpd, liquid or powder,
• effectively decreases or slows
down reinforcement corrosion
• needed very small
concentration, as an admixture.
• decrease or slow down the rate
of attack of the metal
• added in admixed form or as
repair material
Corrosion Inhibitors (CI)
41. CSIR-SERC
Corrosion inhibitor (CI) – at a glance
Should be viewed as an additional protective
measure – not as an alternative to the design
specifications for durable concrete
Types
Anodic
Cathodic
Migrating
or
mixed (CI)
CaNO3, CaNO2
Zinc, Calcium, Antimony,
Molybdenum
Aldehyde based, Amine based
42. CSIR-SERC
• Essentiality of CI- corrosion protection demanded
•Advantages: To provide corrosion protection
•Uniformly mixed throughout the concrete matrix
•Protecting the entire steel surface
•Concrete’s low permeability – protects inhibitor leaching
• Features of ideal CI
• adequate amount to prevent corrosion of embedded
steel
• no adverse effect on properties of fresh & hardened
concrete
Corrosion inhibitor (CI) – at a glance
43. CSIR-SERC
Requirement - To mitigate reinforcement corrosion
Formation of
barrier layers
Oxidation by
passivation of
the surface
Influencing the
environment in
contact with the
metal
• possess strong electron acceptor or donor properties or both
• solubility be such that rapid saturation of the corroding surface
occurs without being readily leached out
• Induce polarization of the respective electrodes at relatively
low current values
• Compatible with the intended system without adverse effects
• Effective at the pH and temperature of the system environment
To be an effective CI
44. CSIR-SERC
forming a film on the metallic surface by adsorption
Complex formation with cement or cementitious material
Inhibitors slow corrosion process - (Electrochemical
evaluation)
Increasing the anodic or cathodic polarization behavior
(Tafel slopes)
Reducing the movement or diffusion of ions to the
metallic surface
Increasing the electrical resistance to the metallic
surface
Inhibitor - Mechanism
45. CSIR-SERC
Techniques to assess
inhibitor efficiency
Electrochemical
Methods
Non-Electrochemical
Method
Impedance – AC method
Linear Polaraisation
Measurement
Weight loss method
Corrosion Rate and Inhibitor
efficiency
Cyclic Voltammetry
46. CSIR-SERC
Potentio-dynamic polarization method
The inhibition efficiency can be calculated from the value of Icorr by
using the formula,
Inhibition efficiency (%)
where Icorr (blank) is the corrosion current in the absence of inhibitor and Icorr (inh)
is the corrosion current in the presence of inhibitor
AC impedance method
The inhibition efficiency can be calculated by using the formula,
Inhibition efficiency (%)
Where the Rt(inh) is the charge transfer resistance in the presence of inhibitor
Rt(blank) is the charge transfer resistance in the absence of inhibitor
Evaluation of inhibition efficiency Electrochemical Methods
47. CSIR-SERC
Techniques to assess corrosion in reinforced concrete structures
• Half cell potential (ASTM C876) : electrochemical technique
survey of the condition is the first step towards its rehabilitation
• Rapid, cost effective and non-destructive survey offers key information
on the evaluation of corrosion and aids in the quality assurance of
concrete rehabilitation and in the prediction of remaining service life
• Assess the severity of steel corrosion to measure the corrosion
potential, since it is qualitatively associated with corrosion rate
Half-cell potential reading vs
Cu/CuSO4
Corrosion activity
Less negative than -0.200 V 90% probability of no corrosion
Between -0.200 V and -0.350 V An increasing probability of
corrosion
More negative than -0.350V 90% probability of corrosion
<-500 mV Severe corrosion
Probability of corrosion according to half-cell readings
48. CSIR-SERC
Measurement of Electrical conductivity of concrete
Rapid chloride permeability system – RCPT
(ASTM C1202 or AASHTO T277 )
• Specifies the rating of chloride permeability of concrete based on
the charge passed through the specimen during six hours of testing
period
• ASTM C1202 recognizes that a correlation between the rapid
chloride permeability test and the 90 day ponding test results is
necessary, while AASHTO T277 does not require this correlation
NDT – IR, Laser, UPV, Electrical measurement, etc.
49. CSIR-SERC
Prerequisites for Repairing
• Pores are responsible for transport of aggressive
substances such as chloride, oxygen and moisture,
which can cause deterioration
• Pore solution, its chemistry and types present in the
concrete should be analysed
• Compatibility of repair system
50. CSIR-SERC
• Required Dosage optimisation
(electrochemical and Non
electrochemical)
• Compatibility studies between CI
and Cementious materials such
as hydration, setting Time, Leach
out study
• Durability aspects
Do and Don’t in Use of CI
Do’s Dont's
• Improper Dosage results in
adverse effects
• inconsistent corrosion rate
• Unprecended hydration
and offset setting time
• Use of expired CI
• Use of different CI for a
particular work
51. CSIR-SERC
Corrosion inhibitor research at CSIR-SERC
Synthesis of polymer based inhibitor towards reinforcement corrosion
• Presently used Inhibitors: inorganic based-Calcium nitrate,
Calcium nitrite
• Organic based – MCI – amines, ester based
• Current research: synthesis of di-aniline based CI
• Electrochemical evaluation – simulated pore solution
• Results are compared with already available CI’s
• High efficiency, even with very small concentration
• Mechanism – study is under progress
• Long term effect is also in progress
53. CSIR-SERC
Chemical Admixture - Additive to concrete mixture – to enhance concrete
properties – fresh or hardened stage
• ex: Superplasticisers, Corrosion Inhibitors, Set Retarders, Set
Accelerators, Alkali-Silica Mitigating Inhibitors, Air-entraining agents,
etc.,
• imparts extreme workability without the addition of extra water, to
produce ‘flowing concrete’, or
• Allows large reduction of the water content to be made without loss of
workability; or
• permits simultaneous increase in both workability and strength without
incurring substantial extra cost
Chemical Admixture - Introduction
Organic compounds of high molecular weight - Synthetic
Technically - an admixture, which when added to concrete either
Superplasticisers
54. CSIR-SERC
How super are superplasticiser
SP
• When used to produce easily placed concrete, it can
transform a 2-inch slump conventional mix into an 8-
inch-slump flowing mix
SP
• When used as a water-reducing agent, it permits 20 to 30
percent of the water in a normal mix to be eliminated
without losing slump or workability
SP
• If it is used as cement savers, 10 to 15 percent
reduction in cement is possible, while
maintaining the same strength of concrete
56. CSIR-SERC
PMS n = condensation number (50-60)
given mol. wt in the range of
20,000
Form of sodium salt –soluble in
water – due to the presence of
sulphonate groups on the side
chains
PNS Similar in many ways to PMS
category – with simple
repeating unit
n = 5 -10 giving mol. wt in the
order of 2000
Chemical Structure of PMS & PNS
57. CSIR-SERC
Allow 40% reduction of water – due to their chemical structure, which enables
good particle dispersion
Mainly composed by a methyl-polyethylene glycol copolymer (side chain) grafted
with methacrylic copolymer (main chain)
PEO group affords a non uniform distribution of electron cloud, which gives
chemical polarity to the side chains
Number of length of side chains are flexible parameters- easy to change
Side chains have a huge amount of PEO units, lower with higher molar mass w.r.
to charge density of polymer – enables poor performance on cement suspensions
To have both parameters at the same time – long side chain and high charge
density – keep no. of main chain units much higher than no. of side chains units
Chemical Structure - PCE (contd….)
PCE
58. CSIR-SERC
Mode of Action
PNS, PMS – Electrostatic repulsion
PCE – Steric stabilization – due to the presence of bulky group
Mechanism of PNS and PMS
• Very large molecules (colloidal size) – dissolves in water to give ions with a very high
negative charge (anions)
• Configuration of anions not known – sulphonated groups (anions) oriented outwards
into the water
• Anions – attracted to the surface of cement grains – at the normal levels of admixture
usage
• Adsorbed in sufficient numbers form a complete monolayer around them
• Combination of electrostatic repulsion and large ionic size (provide physical
separation) brings about rapid dispersion of the individual cement grains
• Water trapped within the original floccs is released and contribute to the mobility of
the cement paste – hence increases the workability of concrete
• Not much reduction in the surface tension of water – little tendency to excessive air
entrainment even at high dosage
59. CSIR-SERC
Backbone - Negatively charged-
permits adsorption on the positively
charged colloidal particles
As a consequence of adsorption –
changes in zeta potential of suspended
particles – due to adhesion of the
polymer on the particle surfaces –
ensures to the side chains possibility to
exert repulsion forces, which disperse
suspended particles and avoid friction
Forces directly detected using Atomic
Force Microscope – liquid
environment (model substances)
Mechanism of PCE
60. CSIR-SERC
How to use SPs?
Laboratory trial mixes must be needed – absence of
accumulated experience with SPs – function by dispersing
cement particles – efficiently in concrete rich in cement and
other cementitious materials
Reproportion of mix (to make cement-sand paste thicker
and less soupy) – must for conventionally proportioned
mixes for high slump –to prevent bleeding
Major effect- bleeding – to control - add fines (by absorbing
water)
Smaller size coarse aggregate – inhibits segregations – less
buoyant - Pozozlans addition – 4 to 5 % more of finer
fractions of sand-to prevent segregation
Maximum dosage of SPs beyond which segregation is
inevitable
Selection of coarse fine aggregate – improve workability and
finishability, even with low slump
How to control the negative effect?
61. CSIR-SERC
• Required Dosage optimisation
(slump, Marsh cone, flowability
desirable for particular mix
grade )
• Compatibility studies between SP
and Cementious materials (Zeta
potential, hydration, setting
Time, Leach out study)
• Durability aspects
Do and Don’t in Use of SP
Do’s Dont's
• Improper Dosage results in
adverse effects
• Inconsistent setting time
• Unprecended hydration
• Use of expired SP
• Use of different SP for a
particular work
62. CSIR-SERC
Conventional superplasticisers PCE
PMS
derivatives of petroleum by
product
• Scarcity due to demand of petroleum
derivatives
• Non-biodegradable
Non - environment friendly
due to aldehyde emission
PNS
Emergence of Alternate SP
Weakness of available sps
Strength -
Emergence of new
alternate
Environment friendly
superplasticiser
Bio-polymer
63. CSIR-SERC
Work at CSIR-Structural Engineering Research Centre
EMPOWER Project : Bottom up approach for the synthesis
of multifunctional admixtures towards green construction
Survey - Most abundant bio-renewable and major
biopolymer on earth – Cellulose - Major constituent: cotton,
wood, baggase and biomass
Poly dispersed linear glucose polymer chains – form
hydrogen bonded supramolecular structures
Future Work : planned based on the literature survey
conducted – availability of resources, green solvent
66. CSIR-SERC
Characterization of Cement
XRD – X-ray diffraction: Bogues compounds : Phases of cement
XRD spectrum
2
C
o
u
n
t
s
• C3S : 47.90%
• C2S : 21.50%
• C3A : 3.13%
•C4AF: 14.37%
68. CSIR-SERC
Consistency and Setting time of Cement- SPs
Name of the Super
Plasticizer
w/c Consistency
(mm)
Initial
Setting Time
Final Setting
Time
Control 0.31 13 2 hrs 20 min 5 hrs 20 min
Control 0.32 23 2 hrs 15 min 5 hrs
Cellulose SP (0.5%) 0.28 19 3 hrs 5 hrs
PC SP (0.5%) 0.25 19 3 hrs 20 min 7 hrs
PNF SP (0.5%) 0.25 21 1 hrs 40 min 36 hrs
69. CSIR-SERC
Future Programme of Work
Structural Modifications – Changes in Chemical
Functionalities
Multi Functional Properties – Retarders, Corrosion inhibitor,
Internal moist curing – controlled release - mechanism etc
71. CSIR-SERC
NANO CELLULOSE – NATURE NANO
“Bottom-up approach towards green construction”
• Developing technology for sustainable construction materials
• Synthesis of superplasticisers using biopolymer
• Synthesizing Corrosion Inhibitor - Self – healing mechanism
• Autogenic healing of cracks at nano level - Crystal growth
mechanism
Inhibitor loading
Crystalline array
Treatment Methods
72. CSIR-SERC
Concluding Remarks
Importance of corrosion inhibitors
and superplasticisers in construction
industry
Mechanisms
Proper usage – do’s & dont’s
R&D at CSIR-SERC
73. CSIR-SERC
Increased urbanization, especially in emerging
countries, will drive public infrastructure and housing
projects
Safety, Durability, Asthetics of structures are mainly
brought by the chemicals
Working together - chemical and construction
industries can continue to build a better, safer and
more sustainable world – Homogeneous solution for
Heterogeneous problem
Concluding Remarks (continued)