General introduction CONCRETE is a building Material made from a mixture of gravel ,sand ,cement,water and air ,forming a stone like mass on hardenning. FRESH CONCRETE It is a concrete that has not reached the final setting time.

1. DEPARTMENT OF ENGINEERING SCIENCES AND TECHNOLOGY
AE 217
MATERIALS TECHNOLOGY FOR ENGINEERS
IWRE 2 -GROUP 5
PRESENTATION
2018

2. FRESH CONCRETE

3. PRESENTATION OUTLINES
General introduction
Fresh concrete properties
Fresh concrete Testing
The Admixture
The Hardened mixture
FRESH CONCRETE

4. FRESH CONCRETE
General introduction
CONCRETE
is a building Material made from a
mixture of gravel ,sand ,cement,water
and air ,forming a stone like mass on
hardenning.
FRESH CONCRETE
It is a concrete that has not reached
the final setting time.

5. FRESH CONCRETE

6. The strength of concrete of a given mix
proportions is very seriously affected by
the degree of its compaction;
it is vital, that the consistency (ability
to flow) of the mix be such that, the
concrete can be transported, placed and
finished sufficiently easily and without
segregation.
The first 48 hours are very important for
the performance of the concrete structure.
FRESH CONCRETE

7. Fresh concrete properties
Workability
Slump Loss
Segregation/Bleeding
Plastic Shrinkage
Time of Set
Temperature
FRESH CONCRETE

8. 1. WORKABILITY
The amount of useful internal work necessary to
produce full compaction without occurrence of the
known concrete problems.
The useful internal work is the work or energy
required to overcome the internal friction between the
individual particles in the concrete.
Factors affecting workability
1. Water content of the mix: Adding water increases
workability and decreases strength.
2. Maximum size of aggregate: Less surface area to be
wetted and more water in medium.
3. Grading of aggregate: Poor grading reduces the
consistency.
4. Shape and texture of aggregates: Smooth surfaces give
better workability.
FRESH CONCRETE

9. Measurement of Workability
There are 5 types of test, which can measure workability
indirectly. Unfortunately, there are no accepted tests,
which can measure directly the workability.
1. Slump Test: Gives good results for rich mixes.
2. Compacting Factor Test: Used for low workable concretes.
3. Flow Table Test: Used for high workable concretes.
4. VeBe Test: Used for low workable concretes (fiber
reinforced concrete).
5. Kelly Ball Test: It is practical in field test.
See more details in fresh concrete Testing, next later
FRESH CONCRETE

10. 2.Slump loss
• Slump describes the consistency of
fluidity of a concrete mixture.
• Slump loss is the reduction in slump
from the time of original batching to
the point when concrete is discharged
from a mixture track or other delivery
vehicle
• Slump value represents the workability
property of concrete.
• Slump should be achieved within delivery
time range of 45- 90 min
FRESH CONCRETE

11. Why is controlling slump loss
important?
 Slump is an important consideration for
the contractor as it impacts the ability
to place, consolidate and finish
concrete
 The rate of slump loss should be
predictable so that loads of concrete
arrive the jobsite at a consistency
slump.
 Excess water causes problems with
strength and potential cracking.
FRESH CONCRETE

12. How can the slump loss be controlled?
It is important to understand the concrete material
used and how the fresh concrete properties are
affected by ambient conditions when it is delivered
and placed.
The following is a list of controllable factors that
influence slump loss:
1. Use the correct amount of mixing water needed to
archive the specified slump within tolerances at the
job site with consideration temperature and delivery
time.
2. Maintain aggregate stockpiles through stock rotation
and proper loading procedures to archive consistent
gradation and moisture content of aggregates being
batched .
FRESH CONCRETE

13. 3. Segregation/Bleeding
Segregation is the “Separation of constituent
materials in concrete.”
In concrete technology, segregation is of three
type
1. Separation of Coarse aggregate from the
concrete mixture,
2. Separation of Cement paste from the
concrete during its plastic stage.
3. Separation of water from the concrete mix
(Bleeding in concrete)
FRESH CONCRETE

14. FRESH CONCRETE

15. FRESH CONCRETE
Factors causing segregation in concrete:-
• Transporting concrete mixes for long distances.
• Poorly proportioned mix, where sufficient
matrix is not there to bind the aggregates
• Dropping concrete from more than 1m.
• Vibrating concrete for a long time.
How to minimize segregation in concrete:-
1. Segregation can be controlled by maintaining
proper proportioning the mix.
2. by peculiar handling, placing, transporting,
compacting and finishing,
3. By Using air entraining agents, admixtures and
pozzolanic materials in the mix segregation
controlled to some extent.

16. Bleeding in concrete
Bleeding is a form of segregation in which
water present in the concrete mix is pushed
upwards due to the settlement of cement and
aggregate. The specific gravity of water is
low, due to this water tends to move upwards.
Bleeding ordinarily occurs in the wet mix of
concrete.
The bleeding in concrete is not harmful if
the rate of evaporation of water is equal to
the rate of bleeding. Normal bleeding is
quite good, and it enhances the workability
of concrete.
FRESH CONCRETE

17. FRESH CONCRETE

18. FRESH CONCRETE
How bleeding affects concrete stability:-
 Formation of laitance in concrete, structures may lose
its wearing capacity and decreases its life.
 Forming of water at the top surface of concrete, results
in delaying the surface finishing.
 Concrete becomes permeable and loses its homogeneity.
 Excessive bleeding breaks the bond between the
reinforcement and concrete.
How the bleeding in concrete is controlled:-
 Bleeding in concrete is controlled by Adding minimum
water content in the concrete mix.
 Encouraging the use of air en-training admixtures in the
mix.
 By adding more cement in the mix.

19. 4. Plastic shrinkage
Plastic shrinkage is mainly a problem
with large exposed surfaces like floor
slabs and paving placed in
environmental conditions with a high
evaporation rate. The faster water
evaporates from the concrete
Plastic shrinkage cracks typically
occur on horizontal surfaces exposed to
the atmosphere
FRESH CONCRETE

20. FRESH CONCRETE

21. FRESH CONCRETE
There are several corrective procedures listed below to
reduce the risk of experiencing plastic shrinkage cracks.
 Moisten subgrades and forms to prevent absorption.
 Dampen dry aggregates that are absorptive.
 Reduce the temperature of the concrete by
 Precooling aggregate with water.
 Cooling the cement.
 Shading aggregates, water tanks, and lines.
 Avoid over mixing.
 Place concrete early in the morning or late
afternoon.
 Construct temporary walls to reduce wind velocity.
 Provide sunshades for concrete.
 Use evaporation retardant (usually polymers).

22. 5. Temperature
FRESH CONCRETE

23. 6. Time of set
Changing the concrete state from
plastic to hardened state is called
setting of concrete.
The time concrete takes to change
the state is the setting time.
Setting time depend upon
the properties of cement.
To increase or decrease the setting
time admixtures can use in concrete
mix.
FRESH CONCRETE

24. It determine the
time elapsed between
addition of water
and when the paste
ceases to be fluid
and plastic
(initial set)
It determine the
time required for
the paste to achieve
a certain degree of
hardness (final set)
FRESH CONCRETE

25. FRESH CONCRETE

26. Fresh concrete testing
methods
1. Slump Test.
2. Compacting Factor Tests.
3. Flow Table Test.
4. VeBe Test.
5. Kelly Ball Test.
FRESH CONCRETE

27. Slump test
FRESH CONCRETE
A cone 300 mm high is placed on smooth surface
and filled with concrete in 4 layers, which are
compacted in a prescribed manner. The cone is
then removed and the decrease in height of the
unsupported concrete, “Slump” is measured.
Concrete with very low to low workability 0 – 50
mm slump are used for Roads vibrated by power or
hand operated machines.
Concrete with high workability are used in
sections with congested reinforcement where
vibration cannot easily be done

28. FRESH CONCRETE

29. Compacting factor test
FRESH CONCRETE

30. Vebe Test
FRESH CONCRETE

31. FRESH CONCRETE
Flow table test

32. Admixture
• Admixtures are those ingredients
in concrete other than portland
cement, water, and aggregates that
are added to the mixture
immediately before or during
mixing
FRESH CONCRETE

33. Admixtures can be classified by function as
follows:
1. Air-entraining admixtures
2. Water-reducing admixtures
3. Plasticizers
4. Accelerating admixtures
5. Retarding admixtures
6. Hydration-control admixtures
7. Corrosion inhibitors
8. Shrinkage reducers
9. Alkali-silica reactivity inhibitors
10. Coloring admixtures
11. Miscellaneous admixtures such as workability,
bonding, damp proofing, permeability
reducing, grouting, gas-forming, antiwashout,
foaming, and pumping admixtures
FRESH CONCRETE

34. Air-entraining admixtures
Air-entraining admixtures are used to purposely
introduce and stabilize microscopic air bubbles in
concrete. Air entrainment will dramatically improve
the durability of concrete exposed to cycles of
freezing and thawing.
Entrained air greatly improves concrete’s resistance
to surface scaling caused by chemical deicers.
Furthermore, the workability of fresh concrete is
improved significantly, and segregation and bleeding
are reduced or eliminated.
Air-entrained concrete contains minute air bubbles
that are distributed uniformly throughout the cement
paste. Entrained air can be produced in concrete by
use of an air-entraining cement, by introduction of
an air entraining admixture, or by a combination of
both methods.
FRESH CONCRETE

35. water-reducing admixtures
Water-reducing admixtures are used to reduce the
quantity of mixing water required to produce
concrete of a certain slump, reduce water-cement
ratio, reduce cement content, or increase slump.
Typical water reducers reduce the water content by
approximately 5% to 10%. Adding a water-reducing
admixture to concrete without reducing the water
content can produce a mixture with a higher slump.
The rate of slump loss, however, is not reduced
and in most cases is increased Rapid slump loss
results in reduced workability and less time to
place concrete.
An increase in strength is generally obtained with
water-reducing admixtures as the water-cement
ratio is cracks in concrete.
FRESH CONCRETE

36. Hardened concrete
Properties:
• Very Hard (15 – 40 kN/m2)
• Water resistant
• Weather resistant
• High grade concrete is resistant to
abrasion (e.g. by high water flows on
bridge piers)
• Resistant to impact loads (e.g. on roads
• Thermal insulation
• Prevents corrosion
FRESH CONCRETE

37. Hardened concrete Testing
1. Rebound hammer test
2. Cube Test
FRESH CONCRETE

38. FRESH CONCRETE

39. FRESH CONCRETE