Substrate tolerant, transparent epoxy resin

1. Product profile :
ATU FAST 100 is an unpigmented epoxy resin binder that is used as an impregnation agent, primer, leveling layer and
for the production of compression resistant mortars, flow mortars, blinding layers for blinded covers. It is also used as a
special sealing material of drain outlets / corners mix with suitable silica powder . It also gives a good bonding between
concrete and PVC pipes, and gives protection from leakage along pipes.
ATU FAST 100
Substrate tolerant, transparent epoxy resin
. PROPERTY PROFILE
 Substrate tolerant
 Good penetration capacity
 Plasticizer-free
 Free From nonylphenol and alkenylphenol
 Can be subject ed to mechnical loads
 Can be subjected to chemical loads
Application examples:
 Consumer markets
 Shops /Roof / basement /sunken areas
 Fabrication halls
 Assembly areas
 Food industry
 Butcher operations
 Bakeries
Recommended Application
 Priming coat -The pure resin is poured generously
over the surface and distributed by suitable means,
e.g. a rubber wiper, so that the pore volume of the
substrate is completely filled. Then work into
the substrate with an epoxy roller. Application rate
depending on substrate and application approx.
0.10-0.50 kg/m².
 Leveling layer/scratch coat: The material which has
been filled up to 1 : 1 parts by weight is distributed
with a smoothing trowel or priming blade and if
necessary worked over with a spiked roller.
Application rate per mm thick layer: approx. 0.85
kg/m² epoxy resin and 0.85 kg/m² Tobslak SBL mix.
 To treat core cutting areas : to seal the core cutting
,the pure resin should be poured onto the surface and
distributed with a suitable tool, e.g. a rubber wiper,
until saturation has been
achieved. The material is then worked into the
substrate with an epoxy roller. Mix with suitable silica
power to fill the gaps. Application rate depending on
substrate. The material can be filled up to 1 : 1.5 parts
by weight.
 Mixing ratio
70 : 30 parts by weight
 Pot-life
At 20 °C and 60% relative humidity approx. 30
minutes. Higher temperatures reduce, lower
temperatures increase pot-life.
 Packaging:
2.5 kg, 5 kg and 25 kg tin containers
 Application rate:
Depending on application between 0.2-0.85 kg/m²
 Shelf-life:
At least 9 months in closed and unmixed, original
containers stored cool but frost-free
 Drying time
At 20 °C and 60% relative humidity: foot traffic after
12 hours, mechanical loads after 3 days, fully cured
after 7 days. At lower temperatures correspondingly
longer. Protect the applied material from moisture
during the curing process (approx. 24 hours at 20 °C)
since the surface may be disturbed and adhesion
reduced otherwise.
 Tools, cleaning
Smoothing trowel, toothed trowel,rubber wiper,
epoxy roller, spiked roller, mixing equipment, also
positive mixer. Clean tools and equipment
immediately while the material is still fresh with
Tob 100 Thinner.
Art. No. SAF 10-1029
Page 1 of 2

2. CHARACTERISTIC DATA OF THE PRODUCT
Comp. A Comp. B Mixture
Density: 1.07 g/cm³ 0.97 g/cm³ 1.08 g/cm³
Viscosity: 900 mPas 500 mPas 750 mPas
1 : 10 mortar*
Compressive strength: 56 N/mm²
Flexural/tensile strength: 23N/mm²
* Epoxy resin mortar with standard sand
Page 2 of 2
Seal the gap between pipe and slab using TOBSLAK
ATU FAST 100 for about 2 inches in diameter.
Pipe Penetration
 Substrate preparation
Substrates should be prepared by suitable chemical or
mechanical means, e.g. steel ball jetting or diamond sanding
so that they fulfil the listed requirements. Missing and
broken out areas in the substrate should be filled/closed
flush with the surface using the Standard PCC System or
with Tobslak PC Mortars.
INDIA
Tobslak India Pvt. Ltd.
305-c, 3rd floor, Irishtech park,sect-48,sohna road,
Gurugram-122018(HR),INDIA
Email: ccin@tobslak.com, www.tobslak.com
GERMANY
Tobslak International,Eschersheimer Landstraße 42,
60322, Frankfurt am Main, Hessen, Germany
Phone:(+49) 3221 1226423
Email:info@tobslak.com; www.tobslak.com
Important: The descriptions, designs, and data contained herein are
presented for your guidance only. Because there are many factors
under your control which may affect processing or application/use it
is necessary for you to make appropriate tests to determine whether
the product is suitable for your particular purpose prior to use. NO
WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED, INCLUDING
WARRANTIES OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR
PURPOSE, ARE MADE REGARDING PRODUCTS DESCRIBED OR
DESIGNS, OR INFORMATION SET FORTH, OR THAT THE PRODUCTS,
DESIGNS, OR DATA MAY BE USED WITHOUT INFRINGING THE
INTELLECTUAL PROPERTY RIGHTS OF OTHERS. IN NO CASE SHALL THE
DESCRIPTIONS, DATA OR DESIGNS PROVIDED BE PRESUMED TO BE A
PART OF OUR TERMS AND CONDITIONS OF SALE. Further, you
expressly understand and agree that the descriptions, designs, and
data furnished by TOBSLAK hereunder are given gratis and TOBSLAK
assumes no obligation or liability for same or results obtained from
use thereof, all such being given to you and accepted by you at your
risk.