--------------------------------------------------------ABSTRACT----------------------------------------------------------- This paper treats the production and performance tests of pedal operated pressed briquettes of about 220 mm x 80 mm x 67 mm using agricultural and wood wastes. The densification was achieved by using some mechanical pressure to reduce the volume of vegetable matter and its conversion to a solid form within a pedal operated briquette press designed and constructed for that purpose. The characteristics values of the briquettes such as the effects of the binder proportion in the briquette and its effects on the combustion properties were investigated using ASTME methods. The calorific value of the briquettes ranged between 11.50 MJkg-1 and 14.02 MJkg-1, making them suitable for use as supplementary fuel in small scale industries such as bakeries. It was observed that the percentage composition of the binder greatly affects the friability index of the briquette. The resistance to humidity also played an important role in the briquette combustion abilities. This briquetting technique of agro-residues is one sure way of fighting climate change and provides a sustainable energy source due to the fact that it reduces dependence on fossil fuels and converts waste materials to wealth.

1. The International Journal Of Engineering And Science (IJES)
|| Volume || 5 || Issue || 7 || Pages || PP -42-46 || 2016 ||
ISSN (e): 2319 – 1813 ISSN (p): 2319 – 1805
www.theijes.com The IJES Page 42
Production and Performance Evaluation of Pedal Operated
Pressed Briquettes
1*
Oumarou M. Ben, 1
fasiu A Oluwole, 2
lateef O. Onundi and 3
bamanga Yusuf
1
Department of Mechanical Engineering, University Of Maiduguri, Borno State, NIGERIA
2
Department of Civil and Water Resources Engineering, University Of Maiduguri, Borno State, NIGERIA
3
Advanced Manufacturing Technology Programme, Jalingo, PMB: 1174, Wukari Road, Taraba State
--------------------------------------------------------ABSTRACT-----------------------------------------------------------
This paper treats the production and performance tests of pedal operated pressed briquettes of about 220 mm x
80 mm x 67 mm using agricultural and wood wastes. The densification was achieved by using some mechanical
pressure to reduce the volume of vegetable matter and its conversion to a solid form within a pedal operated
briquette press designed and constructed for that purpose. The characteristics values of the briquettes such as
the effects of the binder proportion in the briquette and its effects on the combustion properties were
investigated using ASTME methods. The calorific value of the briquettes ranged between 11.50 MJkg-1 and
14.02 MJkg-1, making them suitable for use as supplementary fuel in small scale industries such as bakeries. It
was observed that the percentage composition of the binder greatly affects the friability index of the briquette.
The resistance to humidity also played an important role in the briquette combustion abilities. This briquetting
technique of agro-residues is one sure way of fighting climate change and provides a sustainable energy source
due to the fact that it reduces dependence on fossil fuels and converts waste materials to wealth.
Keywords: agro-residues, biomass, briquette, combustion characteristics, sustainable energy.
-------------------------------------------------------------------------------------------------------------------------------------
Date of Submission: 17 May 2016 Date of Accepted: 10 July 2016
---------------------------------------------------------------------------------------------------------------------------------------
I. INTRODUCTION
Throughout the world, the cost of energy sources, their availability and impact on the environment are major
causes for concern. Briquetting can be used as an alternative to fuel-wood as the demand and adverse
environmental effects of the latter, especially in the developing country continue to rise as a result of increasing
population. According to the World Health Organisation (WHO) [1], more than two billion people use biomass
for cooking food, while the smoke from burning biomass is one of the fourth leading causes of disease and death
in the world’s poorest countries. Although the importance of biomass briquettes as substitute fuel for wood, coal
and lignite is well recognized, the numerous failures of briquetting machines in Thailand, Sri- Lanka, Kenya,
Sudan, Brazil and almost all developing countries have inhibited their extensive exploitation [2]. Inegbenebor
[3] compressed fibrous agricultural and wood waste materials with suitable adhesive into solid fuel briquettes in
a compressing machine. Nine samples of fibrous waste materials were prepared into different categories:-
category A (100%sawdust, 100%rice-husk, 50-50% rice-husk/saw-dust using starch as adhesive). Category B
(100% saw-dust, 100% rice-husk, 50-50% rice-husk/saw-dust using gum Arabic as adhesive) and Category C
(100% saw-dust, 100% rice-husk, 50-50% rice-husk/saw-dust using bentonite as adhesive). Results from a water
boiling test (WBT), involving comparison of the burning abilities of the solid fuel briquettes and fire wood of
the same quantity (200 grams) in boiling 1.5 litres of water showed that the solid fuel briquettes bound with
each of the three adhesives; bentonite, gum-Arabic and starch; boiled water to 100o
C (373 K) within a period of
14 to 22 minutes, while firewood did so within a period of 22 to 27 minutes. Aris et al. [4] focused on the
development of briquettes from oil palm waste to enhance its utilization as fuel. Several aspects of improvement
to the physical properties as well as energy content were taken into account in the study. A total of eight tests
were conducted for different ratios of shell, fibre and binder mixtures as well as varying the type of binder
material used. Varying briquettes pressing pressure were also considered in these tests. Results showed good
physical properties in terms of durability, impact and compressive strength for a 36:54:10 ratio by mass of fibre,
shell and waste paper briquette with 5.7% ash 5.24% moisture content. The gross calorific value of 22.4MJkg-1
indicated good energy content of the briquette. The briquette pressing pressure of 159 MPa was used after
discovering that it had an outright positive effect on almost all physical and energy components for all
combinations and proportions tested. Several aspects of agro –residues and other wastes materials briquetting
has received increasing research attention by scholars worldwide [5, 6, 7, 8, 9, 10].

2. Production And Performance Evaluation Of Pedal Operated Pressed Briquettes
www.theijes.com The IJES Page 43
Therefore the objective of this study is the production and performance evaluation of agricultural and wood
wastes based briquettes of about 220 mm length, using a small pedal operated press designed for that purpose.
The physical, chemical, thermal properties and the binder proportions effects of the briquettes were investigated.
II. MATERIALS AND METHODS
2.1. Equipment
A pedal operated briquette press [10], 2 stoves: a local “tripod” stove [11] and a sawdust stove [12]; aluminium
pots. A Metler Toledo AB54 weighting machine with limitations of 10 mg minimum and a maximum of 51
grams, a Casio databank stop watch and a tape rule. 100kg of sawdust and rice husk (i.e.: 50kg of sawdust and
50kg of rice husk) was obtained from a saw mill and from a local paddy rice boiler in Maiduguri, Nigeria.
2.2. Methods
To carry out these tests, the sawdust and rice husk were prepared for densification by dividing them into three
categories as reported by Inegbenebor [3]. Category A is 100% sawdust, category B is 100% rice husk and
category C is 50% sawdust 50%rice husk. Each category was prepared by mixing them with industrial starch as
binder as reported by Olorunisola [7]. For each category, six (6) briquettes were produced using the pedal
operated briquette press. Physical characteristics of the briquettes, like density, length before and after drying
were evaluated. The premixed fibrous waste and binder of mass (m) was weighted by means of a weighting
balance and the fed into the mould through the space between the compactors and the mould until the mould is
completely filled up to an initial height(H). The machine was then operated to compress the fibrous waste in the
mould. After the compression, briquettes were ejected and the final height (h) was measured and recorded. Also
the time (t) taken for the operation is recorded using a Casio databank stop watch. The performance of the
machine was then determined using the following formulae:
True density 𝜌𝑡 =
𝑀
𝑉
− − − − (1)
Apparent density 𝜌 𝑎 =
𝑀
𝑉 𝑂
− − (2)
Percentage increase in density of compressed briquette; 𝜂 𝑑
𝜂 𝑑 =
𝜌 𝑡−𝜌 𝑎
𝜌 𝑎
× 100% − − − − − (3)
Machine capacity, c
𝑐 =
𝑁×60
𝑡
𝑝𝑒𝑟 𝑕𝑜𝑢𝑟 − − − − − −(4)
% 𝑆𝑕𝑟𝑖𝑛𝑘𝑎𝑔𝑒 =
𝑉−𝑉 𝑓
𝑉
--------- (5)
where:
M= mass of mixed fibrous waste, kg;
H=height of mould,
h=height of compressed briquette, mm;
t = time taken to complete one operation, minutes;
𝐴 𝑜=area of mould, 𝑚2
;
𝑉𝑜 =volume of mould, 𝑚3
;
V= volume of compressed briquette,𝑚3
.
Vf = volume of briquette after drying,𝑚3
.
𝜌𝑡=true density of briquette, k𝑔𝑚−3
𝜌 𝑎=apparent density of briquette, kg𝑚−3
N = number of briquette per operation.
2.3. Proximate analysis.
The proximate analysis determines the moisture content (𝑀𝑜, in weight percent (w/o)) by driving off the free
moisture at~107⁰C for approximately one hour. The volatile matter content (V’,(w/o) is determined by driving
off volatile hydrocarbons CO, 𝐶𝑂2 and combined 𝐻2 𝑂 at ~950⁰C. The briquette sample is then burned and the
inorganic residue is the ash content (A’ (w/o).The fixed carbon (𝐶𝑓
𝑤
𝑜
) is then calculated by difference [13].
𝐶𝑓
𝑤
𝑜
= 100 − 𝑀′(
𝑊
𝑂
)
+ 𝑉′(
𝑤
𝑜
) + 𝐴′ 𝑠(
𝑤
𝑜
) -------- (6)
2.4. Heating or calorific value.
The ash free lower calorific value (LCV) can be calculated to within 2% accuracy by using the Barnard [14]
equation:
𝐿𝐶𝑉 = 18.7 × 1 − 𝐴′
− 𝑀′
− 2.5 × 𝑀′------ (7)
LCV-------- MJ/ kg while elements are in weight %

3. Production And Performance Evaluation Of Pedal Operated Pressed Briquettes
www.theijes.com The IJES Page 44
Furthermore, open burning tests were conducted using two types of stoves; the local “tripod” fuel wood stove
and the sawdust stove under two different conditions:
a.) In a confined not well aerated space and;
b.) In an open space.
2.5. Friability and humidity tests.
Friability and humidity tests were carried out on the samples based on their binder content and not the nature of
their constituents, using the Centre des Recherches Agronomiques (CRA) [5] method. The friability test was
done by repeatedly dropping the samples from a specified height, while the humidity test was done by wrapping
the samples in an aerated grains storage bag for 21 days and placed in a damp environment. The wrapping was
to avoid direct content with water. The disintegration level due to impact with respect to the whole sample size
is the characteristic of importance. In the humidity test too, disintegration (due to humidity) and percentage
elongation are the most important parameters.
III. RESULTS AND DISCUSSION
The machine was able to produce 120 briquettes per hour. Figure 1 shows the three (3) categories of briquettes
based on composition.
(i) (ii) (iii)
Figure 1: produced briquette samples: (i) 100% sawdust (ii) 50% sawdust-50% rice husk (iii) 100% rice husk.
The results of the unbroken and broken briquette combustion tests are respectively as follows:
1a.in a confined space; a heavy smoke was observed to be accompanying the flame.
1b.in an open space; less smoke was produced than the previous tests.
2a.in a confined space; broken into 20 pieces; a slightly reduced smoke was observed to be accompanying the
flame.
2b.in an open space; broken into 20 pieces; it was almost smokeless.
Inegbenebor [3] found that the solid fuel briquettes burnt with yellow flame with moderate black smoke,
indicating incomplete combustion due to poor air-fuel ratio. He could not ascertain the reason for that. However,
our results show that solid briquettes (SB) cannot burn satisfactorily in the combustion appliance of a particular
customer; they are indeed unsuitable for some cook stoves and give excessive smoke unless broken into small
pieces of 50-60 mm thickness a bit bigger than the 10-20mm thickness suggested by Grover & Mishra [15]. It is
difficult to find a situation where consumers are prepared to shift to new appliances to suit a given design. A
much more adapted briquetting machine would be needed to suit a particular requirement, need or family;
simply showing that briquetting would be a successful family or community affair, which shares common
things. A slight rather persistent brownish change in colour was observed with the category C briquette
containing more binder (Figure 1). However, it was a little bit smokier than the remaining categories. When
broken into pieces a much lower smoke was noticed, which has to do with their shape and sizes as well as areas
of utilization. This may even attract the design of a machine to produce readily available small size briquettes
(i.e. 50 to 60 mm size). Most of the developing countries in the study area produce sugar cane, millet, sorghum,
wheat and groundnut. Shrinkages (table 1) were noticed and the final sizes of the briquettes upon drying were
observed to be 215mm x79 mm x 65mm, 215mm x 78mm x 65mm and 210 mm x 80mm x 67 mm for samples
A, B and C respectively. This slight change in sizes has to be attributed to the binder content as a function of

4. Production And Performance Evaluation Of Pedal Operated Pressed Briquettes
www.theijes.com The IJES Page 45
porosity and not the composition since sample A is 100% sawdust, sample B 100% rice husk also while sample
C is 50/50 sawdust/rice husk. Pressure could have been another reason for the shrinkages if it was not a uniform
one applied for all compactions processes. Changes in the sizes were not proportional as shown by the
percentage shrinkages in Table 1, with changes in lengths being the most important and easily noticeable.
Table 1: Length variation in briquette samples
Sample A Sample B Sample C
Initial length,𝐿 𝑂 (mm) 220 220 220
After drying length,𝐿𝑓 (mm) 215 215 210
% volume shrinkage 6.37 7.56 4.54
To test the briquettes’ resistance to humidity, the briquettes were kept in a relatively damp environment for three
(3) weeks. No increase in the friability was noticed but this should not be seen as a conclusive test; there is need
to carry out a pressure test on hydraulic pressure ram. The proximate analysis of the briquette sample is as
shown (Table 2).
Table 2: proximate analysis tests results
Sample A Sample B Sample C
Moisture (%,mass) 15.411 17.110 17.215
Fixed carbon (%) 10.026 13.550 18.853
Volatile matter (%) 66.528 49.099 48.793
Ash (%) 8.035 20.229 15.135
Sample A with lower ash content is better followed by samples C and B respectively (Table 2), thus showing
better combustion characteristics. The calorific values (Table 3) of the briquettes are high
enough to withstand any given process and even contribute as a supplementary fuel for incineration process in
the case of law calorific value fuels.
Table 3: Average Calorific values of the briquette samples
Sample A Sample B Sample C
Calorific value (MJ/kg) 14.024 11.500 12.229
The average true and apparent densities (table 4) were also found to be 338.2 kg𝑚−3
and 263.04 kg𝑚−3
respectively.
Table 4: Results of performance tests.
S/No. Mass of
Fibrous
waste (kg)
H(mm) h(mm) 𝑉𝑜 𝑚3
v𝑚3
𝜌𝑡 𝜌 𝑎 𝜂 𝑑
1 1.25 90 70 4.752 3.696 338.2 263.0 28.6
2 1.28 90 70 4.752 3.696 346.3 269.4 28.5
3 1.21 90 70 4.752 3.696 327.4 254.63 28.59
4 1.24 90 70 4.752 3.696 335.5 260.9 28.58
5 1.27 90 70 4.752 3.696 343.6 267.26 28.6
average 1.25 90 70 4.752 3.696 338.2 263.04 28.58
(0.027)* (7.394)* (5.779)* (0.043)*
*standard deviations.
Upon friability tests, partly disintegration was noticed on the sample with low binder content. The remaining
samples showed vary little disintegration which was found to be reducing as the higher binder content sample
was tested. Inherent binders and most externally added binder are water soluble [2]. This is the reason why the
sample could not be subjected to direct water contact but the former method adopted. Disintegration was noticed
too on the lower binder content together with a 4 mm elongation, approaching the initial length before
densification. The sample with the highest binder content remained unaltered if not for the fungus that started
forming on its surface; this analysis has shown that the briquettes could be transported over long distances in
Lorries for use not near their production site if produced with the optimum binder content. Furthermore, the
percentage elongation appears to be inversely proportional to the binder content in a sample. To these results

5. Production And Performance Evaluation Of Pedal Operated Pressed Briquettes
www.theijes.com The IJES Page 46
should be added the fact the working pressure plays an important role even though its effect has not been
thoroughly investigated in this work.
IV. CONCLUSION
The briquetting technology will enable agricultural waste to be removed from the environment, thereby
preventing environmental pollution.
The calorific value of the produced briquettes was found to range from 11.50 to 14.02 MJ/kg, making the fuel
briquettes suitable to be used as supplementary fuel in small scale industries.
The briquettes were found to have a good resistance to humidity as the binder content increases.
Briquettes size affects the burning of the briquettes i.e.: the smaller the size of the briquettes the more efficient
was the burning.
ACKNOWLEGDEMENTS
The Authors wish to acknowledge the technical support received from the entire Staff of the Faculty of
Engineering Teaching Workshop, University of Maiduguri, Borno State, Nigeria.
REFERENCES
[1]. World Health Organisation (WHO) (2002) Health Care Waste Management, October, Geneva, Switzerland
[2]. Ericksson M. and Prior M. (1990) The briquetting of agricultural wastes for fuel, FAO environment and energy paper 11, Food
and Agricultural Organization of the United Nations.
[3]. Inegnenebor, A.O. (2002) Production of solid fuel briquettes from agricultural and wood wastes (sawdust and rice husk), African
Journal of Science and Technology, Vol.3 (2), pp: 118-122.
[4]. Aris M.S., S. Hassan, O. Mamat & K. Sabil (2007) Development of fuel briquettes from oil palm wastes, Transaction of the
Wessex Institute, June 20th.
[5]. CRA (Centre de Recherche Agronomiques de I’ État Gembloux) (1987) La Densification de la biomasse (in French),
commission des Communautés Européennes.
[6]. Deiana A.C., Granados D. L., Petkovic L. M., Sardella M. F. and Silva H.S. (2004) Use of grape must as a binder to obtain
activated carbon briquettes; Brazilian journal of chemical engineering. Vol. 21, No.04, pp: 585-591.
[7]. Olorunnisola, A. (2007) Production of fuel briquettes from waste paper and coconut husk admixtures, agricultural engineering
international: the CIGR Ejournal; Manuscript EE06 006. Vol. IX. February 2007.
[8]. Olawole A. K. (2009) Performance of Composite Sawdust Briquette Fuel in a Biomass Stove under Simulated Condition; AU
Journal of Technology, 12(4), pp: 284-288
[9]. Oumarou M.B and Oluwole F.A (2010) Design of a Pedal Operated Briquette Press; Continental Journal of. Engineering
Sciences, No. 5; pp: 61 – 67
[10]. Chesta Tiwari (2011) Producing fuel briquettes from Sugarcane Wastes; Engineers without Borders-UK National Research &
Education Conference” Our Global Future” 4th
Mach.
[11]. Akinbode, F.O. (1991). Testing the efficiency of Nigerian woodstoves, Nigerian Journal of renewable energy, Vol. 2, No.1, pp:
43-48.
[12]. Akinbode, F.O. (1996). The development of a sawdust stove, Nigerian Journal of renewable energy, Vol.4, No.1, pp: 53-57
[13]. Weisman Joel and Roy Eckart (1985) Modern Power Plant engineering, 2nd
Edition, prentice Hall International, New Delhi
[14]. Barnard G. (1985) The use of agricultural residue as fuel, AMBIO Vol. XIV, No. 4, pp: 5
[15]. Grover P.D. & Mishra S.K. (1996) Biomass briquetting: technology and practices, Food and Agriculture Organization of the
United Nations Bangkok, April 1996, field document No.46.