Woven hemp fabric was treated with sodium hydroxide, commercial flame retardant chemical, and
combination of both to increase its fire-retardant properties. Treatments of fire-retardant changed the
properties of woven hemp fabric such as increased its fabric shrinkage and density of fibres which ranges
from 0.67 to 5% and 1.43 to 1.53 g/cm3
respectively. After the treatment, the fire retardancy of the fabric
increased tremendously which was observed by the burning, thermogravimetry and limiting oxygen index
tests. Some of the samples were not burnt when exposed to flame source and the burning rate needed to be
measured under exaggeration of flame at longer time. The limiting oxygen index value increased from 18.6
to 51 after the treatments which explained the scenario happened in the burning tests. Nevertheless, its
mechanical properties decreased slightly that ranges from 18 to 32% and 23 to 39% for warp and weft
respectively compared to untreated fibre.
Effect of titanium dioxide treatment on the properties of 100% cotton knitted...Elias Khalil (ইলিয়াস খলিল)
Titanium dioxide (TiO2) is a white, water insoluble pigment. It is used in paints, plastics, foods, pharmaceuticals and cosmetics. Its main application on textile materials as an ultraviolet ray protecting agents. Titanium dioxide can reflect, scatter or absorb ultraviolet ray. Besides Titanium dioxide also modify the properties of fabrics. In previous research, titanium dioxide was applied mainly by padding mangle method. This paper presents an approach to observe the effect of titanium dioxide treatment 100% cotton knitted (plain jersey) fabric applied by exhaustion method followed by curing and washing. The treated fabrics were then analyzed by Scanning Electron Microscope (SEM) and the tensile strength, pH value and absorbency of the treated and untreated fabrics were checked. It is found that titanium dioxide impairs the better hand feel and absorbency (wetting time) of all treated fabrics increased gradually than untreated fabrics. The treatment increases the strength and keeps the pH of the fabric in acidic medium.
Investigation on effluent characteristics of organic cotton fabric dyeing wit...Elias Khalil (ইলিয়াস খলিল)
Environmental sustainability is the major concern in the age of modern world. For textile and apparel sector, this has been a burning issue for many related concerned bodies. The pretreatment and dyeing process of greige fabrics results in large volume of effluents that has harmful effect on environment. In this study, the ecological parameters of the effluents obtained from scouring and dyeing of 100% organic cotton single jersey knitted fabrics with environmentally low impact Remazol series reactive dyes adopting exhaust dyeing method was investigated. The effluents collected for investigating the ecological parameters include chemical oxygen demand (COD), biological oxygen demand (BOD), total dissolved solids (TDS), total suspended solids (TSS), dissolved oxygen (DO) and alkalinity. The results show that the use of the low impact reactive dyes has greater ecological advantages as it reduces the COD, BOD, TDS, TSS, pH values and increases the DO values of effluents. Organic cotton itself being eco-friendly along with Remazol series sustainable dyes provides the better ecological results. Hence, the results indicated that wet processing of organic cotton knitted fabric with eco-friendly and low impact reactive dyes provide better ecological advantages.
Mechanical Characterization of Biodegradable Linen Fiber CompositesIJMER
Abstract: The conventional materials like iron, mild steel, cast iron etc are having good mechanical properties. Hence they are widely used in structural engineering applications. These conventional materials have some defects like formation of rust, low weight to strength ratio, high production cost. To overcome these defects, engineers started fabricating composite materials. Composites exhibit peculiar properties like different strengths in different directions, rust resistant, high strength to weight ratio, but they pollute the environment. Now the natural fibre composites are widely used in automobile industry. The natural fibres and resins are used to fabricate an eco friendly composite material. Lack of resources and increasing environmental pollution has evoked great interest in the research of materials that are
friendly to our health and environment. Bio polymer composites fabricated from natural fibres is currently
the most promising area in polymer sciences. This is designed to assess the possibility of fibre as reinforcing material in composites. Epoxy resin was made a stiffened panel to conduct tensile test. In this paper it is aimed to explain all possible ways to use natural composites in automobile components. The main advantages of using natural fibers are their degradability and light weight. They are environment friendly and also increase the fuel economy
Mechanical Characterization of Biodegradable Linen Fiber CompositesIJMER
The conventional materials like iron, mild steel, cast iron etc are having good mechanical properties. Hence they are widely used in structural engineering applications. These conventional materials have some defects like formation of rust, low weight to strength ratio, high production cost. To
overcome these defects, engineers started fabricating composite materials. Composites exhibit peculiar
properties like different strengths in different directions, rust resistant, high strength to weight ratio, but
they pollute the environment. Now the natural fibre composites are widely used in automobile industry.
The natural fibres and resins are used to fabricate an eco friendly composite material. Lack of resources
and increasing environmental pollution has evoked great interest in the research of materials that are
friendly to our health and environment. Bio polymer composites fabricated from natural fibres is currently
the most promising area in polymer sciences. This is designed to assess the possibility of fibre as
reinforcing material in composites. Epoxy resin was made a stiffened panel to conduct tensile test. In this
paper it is aimed to explain all possible ways to use natural composites in automobile components. The
main advantages of using natural fibers are their degradability and light weight. They are environment
friendly and also increase the fuel economy
Jute, an eco-friendly and affordable fiber grown profusely in India, possess unique combination of properties suited for the manufacture of non-textile products. However, its contribution for technical applications is limited at present. In this research, an effort has been made to investigate the physical and morphological properties of jute fiber when incorporated in epoxy matrix with a view to widen the share of jute fibers for engineered applications. Composite specimens containing nonwoven jute mat and alkali treated short jute fibers with different weight percentages (1, 2 wt%) were made using epoxy resin. The water absorption, thickness swelling (TS) and morphology [scanning electron microscopy (SEM)] tests of the bio composites were performed. As the fiber fraction ratio was increased the values for water absorption (WA) and thickness swell (TS) were found to be increased. The samples reinforced with 2 wt. percent fiber fractions showed maximum WA and TS in both water environments.
Investigation on physico chemical properties of 100% cotton woven fabric trea...Elias Khalil (ইলিয়াস খলিল)
This paper represents an approach to observe the physic-chemical effects of titanium dioxide (TiO2) applied on 100% cotton woven fabric. Cotton fabric was treated with TiO2 by exhaustion method and followed by necessary curing and washing pro-cesses. The treated fabrics were then analyzed by Scanning Electron Microscope (SEM) and the tensile strength, pH and ab-sorbency of the treated and untreated fabrics were examined. It was found that titanium dioxide impairs the hand feel and absorbency of 100% cotton woven fabrics, wetting time of all treated fabrics increased gradually than untreated fabrics. The treatment increases the tensile strength of 100% cotton woven fabrics. The treatment with titanium dioxide also kept the pH of the fabric in acidic medium.
EFFECT OF FIBER LENGTH ON THE MECHANICAL PROPERTIES OF PALF REINFORCED BISPHE...IAEME Publication
In recent years natural fibers appear to be the outstanding materials which come as the viable and abundant substitute for the expensive and non-renewable synthetic fiber. Natural fibers like sisal, banana, jute, oil palm, kenaf and coir has been used as reinforcement in thermoset composite for applications in consumer goods, furniture, low cost housing and civil structures. Pineapple leaf fiber (PALF) is one of them that have also good potential as reinforcement in thermoset composite. The objective of the present work is to explore the potential of using PALF as reinforcement and investigate the effect of fiber length on mechanical properties of PALF reinforced Bisphenol composite.
Effect of titanium dioxide treatment on the properties of 100% cotton knitted...Elias Khalil (ইলিয়াস খলিল)
Titanium dioxide (TiO2) is a white, water insoluble pigment. It is used in paints, plastics, foods, pharmaceuticals and cosmetics. Its main application on textile materials as an ultraviolet ray protecting agents. Titanium dioxide can reflect, scatter or absorb ultraviolet ray. Besides Titanium dioxide also modify the properties of fabrics. In previous research, titanium dioxide was applied mainly by padding mangle method. This paper presents an approach to observe the effect of titanium dioxide treatment 100% cotton knitted (plain jersey) fabric applied by exhaustion method followed by curing and washing. The treated fabrics were then analyzed by Scanning Electron Microscope (SEM) and the tensile strength, pH value and absorbency of the treated and untreated fabrics were checked. It is found that titanium dioxide impairs the better hand feel and absorbency (wetting time) of all treated fabrics increased gradually than untreated fabrics. The treatment increases the strength and keeps the pH of the fabric in acidic medium.
Investigation on effluent characteristics of organic cotton fabric dyeing wit...Elias Khalil (ইলিয়াস খলিল)
Environmental sustainability is the major concern in the age of modern world. For textile and apparel sector, this has been a burning issue for many related concerned bodies. The pretreatment and dyeing process of greige fabrics results in large volume of effluents that has harmful effect on environment. In this study, the ecological parameters of the effluents obtained from scouring and dyeing of 100% organic cotton single jersey knitted fabrics with environmentally low impact Remazol series reactive dyes adopting exhaust dyeing method was investigated. The effluents collected for investigating the ecological parameters include chemical oxygen demand (COD), biological oxygen demand (BOD), total dissolved solids (TDS), total suspended solids (TSS), dissolved oxygen (DO) and alkalinity. The results show that the use of the low impact reactive dyes has greater ecological advantages as it reduces the COD, BOD, TDS, TSS, pH values and increases the DO values of effluents. Organic cotton itself being eco-friendly along with Remazol series sustainable dyes provides the better ecological results. Hence, the results indicated that wet processing of organic cotton knitted fabric with eco-friendly and low impact reactive dyes provide better ecological advantages.
Mechanical Characterization of Biodegradable Linen Fiber CompositesIJMER
Abstract: The conventional materials like iron, mild steel, cast iron etc are having good mechanical properties. Hence they are widely used in structural engineering applications. These conventional materials have some defects like formation of rust, low weight to strength ratio, high production cost. To overcome these defects, engineers started fabricating composite materials. Composites exhibit peculiar properties like different strengths in different directions, rust resistant, high strength to weight ratio, but they pollute the environment. Now the natural fibre composites are widely used in automobile industry. The natural fibres and resins are used to fabricate an eco friendly composite material. Lack of resources and increasing environmental pollution has evoked great interest in the research of materials that are
friendly to our health and environment. Bio polymer composites fabricated from natural fibres is currently
the most promising area in polymer sciences. This is designed to assess the possibility of fibre as reinforcing material in composites. Epoxy resin was made a stiffened panel to conduct tensile test. In this paper it is aimed to explain all possible ways to use natural composites in automobile components. The main advantages of using natural fibers are their degradability and light weight. They are environment friendly and also increase the fuel economy
Mechanical Characterization of Biodegradable Linen Fiber CompositesIJMER
The conventional materials like iron, mild steel, cast iron etc are having good mechanical properties. Hence they are widely used in structural engineering applications. These conventional materials have some defects like formation of rust, low weight to strength ratio, high production cost. To
overcome these defects, engineers started fabricating composite materials. Composites exhibit peculiar
properties like different strengths in different directions, rust resistant, high strength to weight ratio, but
they pollute the environment. Now the natural fibre composites are widely used in automobile industry.
The natural fibres and resins are used to fabricate an eco friendly composite material. Lack of resources
and increasing environmental pollution has evoked great interest in the research of materials that are
friendly to our health and environment. Bio polymer composites fabricated from natural fibres is currently
the most promising area in polymer sciences. This is designed to assess the possibility of fibre as
reinforcing material in composites. Epoxy resin was made a stiffened panel to conduct tensile test. In this
paper it is aimed to explain all possible ways to use natural composites in automobile components. The
main advantages of using natural fibers are their degradability and light weight. They are environment
friendly and also increase the fuel economy
Jute, an eco-friendly and affordable fiber grown profusely in India, possess unique combination of properties suited for the manufacture of non-textile products. However, its contribution for technical applications is limited at present. In this research, an effort has been made to investigate the physical and morphological properties of jute fiber when incorporated in epoxy matrix with a view to widen the share of jute fibers for engineered applications. Composite specimens containing nonwoven jute mat and alkali treated short jute fibers with different weight percentages (1, 2 wt%) were made using epoxy resin. The water absorption, thickness swelling (TS) and morphology [scanning electron microscopy (SEM)] tests of the bio composites were performed. As the fiber fraction ratio was increased the values for water absorption (WA) and thickness swell (TS) were found to be increased. The samples reinforced with 2 wt. percent fiber fractions showed maximum WA and TS in both water environments.
Investigation on physico chemical properties of 100% cotton woven fabric trea...Elias Khalil (ইলিয়াস খলিল)
This paper represents an approach to observe the physic-chemical effects of titanium dioxide (TiO2) applied on 100% cotton woven fabric. Cotton fabric was treated with TiO2 by exhaustion method and followed by necessary curing and washing pro-cesses. The treated fabrics were then analyzed by Scanning Electron Microscope (SEM) and the tensile strength, pH and ab-sorbency of the treated and untreated fabrics were examined. It was found that titanium dioxide impairs the hand feel and absorbency of 100% cotton woven fabrics, wetting time of all treated fabrics increased gradually than untreated fabrics. The treatment increases the tensile strength of 100% cotton woven fabrics. The treatment with titanium dioxide also kept the pH of the fabric in acidic medium.
EFFECT OF FIBER LENGTH ON THE MECHANICAL PROPERTIES OF PALF REINFORCED BISPHE...IAEME Publication
In recent years natural fibers appear to be the outstanding materials which come as the viable and abundant substitute for the expensive and non-renewable synthetic fiber. Natural fibers like sisal, banana, jute, oil palm, kenaf and coir has been used as reinforcement in thermoset composite for applications in consumer goods, furniture, low cost housing and civil structures. Pineapple leaf fiber (PALF) is one of them that have also good potential as reinforcement in thermoset composite. The objective of the present work is to explore the potential of using PALF as reinforcement and investigate the effect of fiber length on mechanical properties of PALF reinforced Bisphenol composite.
This article studies the effect of surface modification of polyester (PET) and silk fabrics by exposing to cold plasma discharge. The cold plasma discharge was proceeded using oxygen/Argon mixed gas as a working gas and different plasma device parameters have been studied such as: different time, different current and different hydrostatic pressure. Treated fabrics are characterized by the measurements and evaluation of mechanical properties, air permeability, Electron Spin Resonance (ESR) and the changes in surface morphological of pretreated fabrics were characterized by Scanning Electron Microscope (SEM) and Energy Dispersive X-Ray Analysis (EDX)). Then the exposed plasma fabrics at optimum conditions were modified with prepared nano-silver. The antibacterial activity for treated fabrics against gram positive bacteria (Staphylococcus aurous) and gram negative bacteria (Escherichia coli) were examined. Also the ultraviolet protection factor (UPF) values increase for both exposed fabrics but the increase is not significant in silk fabrics while antibacterial properties were highly improved by the treatment of fabric. As an applied part for the efficiency of the plasma and nano-treatment, oxygen and oxygen/argon mixed gas plasma and/or nano-silver treated silk samples were separately dyed with Natural Red Lac Dye. Finally, as a metrological part, the uncertainty budget of tensile strength measurement of polyester samples was calculated and analyzed with a well verified traceability via applying all the measurements which are traceable to SI units.
In present scenario natural fibers have received much attention because of their light weight, nonabrasive, combustible, nontoxic, low cost and biodegradable properties. Among the various natural fibers, banana fiber was focused for its pretreatment conditions for preparing perfect fiber. In previously many researchers have found various fibers have been pretreated and they obtain its properties and its applications. In this project banana fiber has been taken as natural fiber and it was pretreated and its properties after pretreatment were obtained. The pretreatment was alkali, sodium hydroxide, potassium permanganate treatment, and bleaching was carried out. Then the composite specimen boards were fabricated by various pretreatment banana fiber, polyethylene and matrix. It undergone to mechanical testing, tensile test, hardness test and also SEM analysis was carried out to check their microstructure. The perfect fiber was found by the obtained results from their properties and bonding nature.
Self-Cleaning Finish on Cotton Textile Using Sol-Gel Derived Tio2 Nano FinishIOSR Journals
Abstract: TiO2 Nano Particles have been synthesized using titanium tetrachloride as precursor through Sol-gel
technique. The characterization of synthesized particles was done in XRD and FTIR analysis. It is revealed from
XRD and FTIT spectroscopy that the TiO2 nano particle formation. Subsequently the synthesized particles were
applied on the Cotton textile plan woven fabrics using pad patch method using 1 wt% of acrylic binder. While
coating three different contraction of TiO2 Nano particles were maintained. The self cleaning action of nano
coated fabric has been quantified by measuring photo catalytic degradation of stain due to visible light
irradiation. %of Decrease in K/S value is increased with respect to increase in TiO2 concentration as well as
duration of visible light irradiation. Keywords: TiO2 Nano particls, Self-cleaning property, Nano-Sol, Photocatalysis
Thermal conductivity Characterization of Bamboo fiber reinforced in Epoxy ResinIOSR Journals
Over a past few decades composites, plastics, ceramics have been the dominant engineering material. The areas of applications of composites materials have grown rapidly and have even found new markets. The current challenge is to make the durable in tough conditions to replace other materials and also to make them cost effective .This has resulted in development of many new techniques currently being used in the industry. While the use of composites it is clear choice in many applications but the selection of material will depend on the factor such as working life, lifetime requirement, complexity of product shape produced, saving the term cost. The availability of natural fiber is abundances and also they are very inexpensive when compared to other advanced manmade fibers. The primary advantage of natural fibers are low density, low cost, biodegradability, acceptable specific properties, less wear during extracting as well as manufacturing composites and wide varieties of natural fibers are locally available. The main focus of this investigation is to determine the thermal conductivity of bamboo fiber reinforced in epoxy resin composites. The test samples were prepared as per ASTM standards using simple hand-layup technique at different fiber weight fractions (10%, 20%30%, 40%50%, 60%). Thermal conductivity (K) of the composites material were determined experimentally and is validated by the results obtained by rule of mixture, E-S model and also by finite element modeling
Green Processing of Dyes: Influence on Physico- Mechanical Properties, Color ...CrimsonpublishersTTEFT
The present article describes the role of dyes in enhancing the various properties of fibers along with their brief history and the recent methodologies used to minimize their negative impact on environmental safety. Since primitive age, natural dyes were used as coloring agents in textile industry. Later, in nineteenth century, synthetic dyes due to their high dyeability, varying shades ability, and comparatively low cost have replaced natural dyes. However, environmental concerns like water and marine pollutions forced the textile industry to develop new methodologies for the utilization of natural dyes with improved properties. Literature reveals that the use of new and advanced techniques have enhanced the dyeability, strength, softness, antimicrobial and other properties of textiles. These are mainly classified in to; a) the chemical modifications of natural dyes, and b) the surface modification of fabrics. In addition to these, the negative and positive impacts of these methods along with the future scope of research have also been discussed.
Effect of Chemical Treatment and Curing Parameters on Mechanical Properties o...IJERA Editor
A brief overview on natural fiber reinforced polymer composites is presented in this work. There is a growing trend to use non conventional and environmental friendly resources for engineering applications. In this scenario Natural fiber are offering a wide range of possibilities. Detailed and thorough study of structure of natural fiber indicates about its hydrophilic nature. Various types of chemical treatment techniques are used by researchers to increase the affinity of reinforcement and matrix .Studies shows that different factors like curing time, temperature, loading condition, fiber orientation etc. affect the properties of natural fiber composites. Lot of work has been carried out with the combination of different fibers and different polymers. Comparative data is presented on properties of different composite.
Effect of Chemical Treatment and Curing Parameters on Mechanical Properties o...IJERA Editor
A brief overview on natural fiber reinforced polymer composites is presented in this work. There is a growing trend to use non conventional and environmental friendly resources for engineering applications. In this scenario Natural fiber are offering a wide range of possibilities. Detailed and thorough study of structure of natural fiber indicates about its hydrophilic nature. Various types of chemical treatment techniques are used by researchers to increase the affinity of reinforcement and matrix .Studies shows that different factors like curing time, temperature, loading condition, fiber orientation etc. affect the properties of natural fiber composites. Lot of work has been carried out with the combination of different fibers and different polymers. Comparative data is presented on properties of different composite.
coir fibers tech has improved so much it can produce micro fibers from petroleum that can be upgraded into artificialleather that can mimic naturalleather
Antibacterial Finishing Of Cotton FabricsKEVSER CARPET
You can find functionalization of antibacterial agents when applied to cotton fabrics,chloroacetate groups, bioactive carboxylic acid, antibacterial activities in these documents.
I found this documents last year while I was searching some datas about antibacterial finishes on warp kniteed blankets , and now I share with you.
Here is now.
Take it and enjoy.
Good lucks.!
Tensile and Impact Properties of Natural Fiber Hybrid Composite MaterialsIJMER
This paper is a review on the tensile and impact properties of natural fiber hybrid composites.
Natural fibers are having good mechanical properties, high specific strength, low cost, bio-degradable
and easily can recyclable through thermal methods. In this paper two different hybrid composites were
manufactured by compression molding and properties of tensile and impact results are conducted as per
ASTM standards. In this project three different fibers such as sisal, jute and glass with thermosets epoxy
resin used with weight ratio of fiber to resin as 15:15:70.Results showed that sisal/glass hybrid composite
has more tensile and impact strength while comparing to sisal/jute hybrid composite.
Modelling and Simulation of Composition and Mechanical Properties of High Ent...msejjournal
Magnesium alloys are high potential materials for application in the aerospace and automotive industries
due to their lightweight properties. They can help to lower dead weight and fuel consumption to contribute
to sustainability and efficiency. It is possible to achieve high specific strength and high stiffness of the
alloys by varying compositions of alloying elements. Applications of magnesium are limited due to its low
strength and relatively low stiffness. This research focuses on a recipe of multi component alloys of
magnesium with varied percentages of Mg, Al, Cu, Mn and Zn obtained from literature and optimizes the
percentage compositions to obtain for high specific strength and specific stiffness. Relationships among
percentage constituents of the alloy components are examined in Matlab R2022b using multiple linear
regression. Optimization is achieved using genetic algorithm to determine the specific strengths and
stiffness. The resulting optimal alloy component percentages by weight are used for microstructure
simulation of thermodynamic properties, diffusion and phase transformations of proposed alloy is done in
MatCalc software version 6.04. Results show potential for improved mechanical properties resulting from
disordered structure in the high entropy magnesium alloy. Future research should focus on production and
characterization of the proposed alloy.
Thermal and Metrological Studies on YTTRIA Stabilized Zirconia Thermal Barrie...msejjournal
Thermal Barrier Coatings (TBCs), routinely prepared from Ceramic based compositions (typically
8%Y2O3-ZrO2or 8YSZ) are being engineered to protect the metallic components from degradation in
applications like gas turbines, jet and automotive engines. With a goal of finding improved TBC materials
a wide variety of ceramics are being researched worldwide. Before physically preparing the TBCs of
uncommon compositions in the laboratory, their suitability to perform can be predicted. Limited
accessibility to detailed and realistic information on the influence of newer compositions (other than 8YSZ)
on TBCs warrants methods to obtain this information.
In this paper, 8YSZ TBCs coated onto aluminium substratesare studied for thermal fatigue, thermal barrier
and materials characteristics to determine the reliability of the coating configuration to withstand the
harshness of test conditions under the framework of experiments. Thereafter, the results have been used to
corroboratethe developed simulation model. Results obtained via thermal tests confirm the suitability of the
model and we can predict the thermal barrier effects of TBCs when prepared from materials other than
YSZ.
More Related Content
Similar to Flammability Characteristics of Chemical Treated Woven Hemp Fabric
This article studies the effect of surface modification of polyester (PET) and silk fabrics by exposing to cold plasma discharge. The cold plasma discharge was proceeded using oxygen/Argon mixed gas as a working gas and different plasma device parameters have been studied such as: different time, different current and different hydrostatic pressure. Treated fabrics are characterized by the measurements and evaluation of mechanical properties, air permeability, Electron Spin Resonance (ESR) and the changes in surface morphological of pretreated fabrics were characterized by Scanning Electron Microscope (SEM) and Energy Dispersive X-Ray Analysis (EDX)). Then the exposed plasma fabrics at optimum conditions were modified with prepared nano-silver. The antibacterial activity for treated fabrics against gram positive bacteria (Staphylococcus aurous) and gram negative bacteria (Escherichia coli) were examined. Also the ultraviolet protection factor (UPF) values increase for both exposed fabrics but the increase is not significant in silk fabrics while antibacterial properties were highly improved by the treatment of fabric. As an applied part for the efficiency of the plasma and nano-treatment, oxygen and oxygen/argon mixed gas plasma and/or nano-silver treated silk samples were separately dyed with Natural Red Lac Dye. Finally, as a metrological part, the uncertainty budget of tensile strength measurement of polyester samples was calculated and analyzed with a well verified traceability via applying all the measurements which are traceable to SI units.
In present scenario natural fibers have received much attention because of their light weight, nonabrasive, combustible, nontoxic, low cost and biodegradable properties. Among the various natural fibers, banana fiber was focused for its pretreatment conditions for preparing perfect fiber. In previously many researchers have found various fibers have been pretreated and they obtain its properties and its applications. In this project banana fiber has been taken as natural fiber and it was pretreated and its properties after pretreatment were obtained. The pretreatment was alkali, sodium hydroxide, potassium permanganate treatment, and bleaching was carried out. Then the composite specimen boards were fabricated by various pretreatment banana fiber, polyethylene and matrix. It undergone to mechanical testing, tensile test, hardness test and also SEM analysis was carried out to check their microstructure. The perfect fiber was found by the obtained results from their properties and bonding nature.
Self-Cleaning Finish on Cotton Textile Using Sol-Gel Derived Tio2 Nano FinishIOSR Journals
Abstract: TiO2 Nano Particles have been synthesized using titanium tetrachloride as precursor through Sol-gel
technique. The characterization of synthesized particles was done in XRD and FTIR analysis. It is revealed from
XRD and FTIT spectroscopy that the TiO2 nano particle formation. Subsequently the synthesized particles were
applied on the Cotton textile plan woven fabrics using pad patch method using 1 wt% of acrylic binder. While
coating three different contraction of TiO2 Nano particles were maintained. The self cleaning action of nano
coated fabric has been quantified by measuring photo catalytic degradation of stain due to visible light
irradiation. %of Decrease in K/S value is increased with respect to increase in TiO2 concentration as well as
duration of visible light irradiation. Keywords: TiO2 Nano particls, Self-cleaning property, Nano-Sol, Photocatalysis
Thermal conductivity Characterization of Bamboo fiber reinforced in Epoxy ResinIOSR Journals
Over a past few decades composites, plastics, ceramics have been the dominant engineering material. The areas of applications of composites materials have grown rapidly and have even found new markets. The current challenge is to make the durable in tough conditions to replace other materials and also to make them cost effective .This has resulted in development of many new techniques currently being used in the industry. While the use of composites it is clear choice in many applications but the selection of material will depend on the factor such as working life, lifetime requirement, complexity of product shape produced, saving the term cost. The availability of natural fiber is abundances and also they are very inexpensive when compared to other advanced manmade fibers. The primary advantage of natural fibers are low density, low cost, biodegradability, acceptable specific properties, less wear during extracting as well as manufacturing composites and wide varieties of natural fibers are locally available. The main focus of this investigation is to determine the thermal conductivity of bamboo fiber reinforced in epoxy resin composites. The test samples were prepared as per ASTM standards using simple hand-layup technique at different fiber weight fractions (10%, 20%30%, 40%50%, 60%). Thermal conductivity (K) of the composites material were determined experimentally and is validated by the results obtained by rule of mixture, E-S model and also by finite element modeling
Green Processing of Dyes: Influence on Physico- Mechanical Properties, Color ...CrimsonpublishersTTEFT
The present article describes the role of dyes in enhancing the various properties of fibers along with their brief history and the recent methodologies used to minimize their negative impact on environmental safety. Since primitive age, natural dyes were used as coloring agents in textile industry. Later, in nineteenth century, synthetic dyes due to their high dyeability, varying shades ability, and comparatively low cost have replaced natural dyes. However, environmental concerns like water and marine pollutions forced the textile industry to develop new methodologies for the utilization of natural dyes with improved properties. Literature reveals that the use of new and advanced techniques have enhanced the dyeability, strength, softness, antimicrobial and other properties of textiles. These are mainly classified in to; a) the chemical modifications of natural dyes, and b) the surface modification of fabrics. In addition to these, the negative and positive impacts of these methods along with the future scope of research have also been discussed.
Effect of Chemical Treatment and Curing Parameters on Mechanical Properties o...IJERA Editor
A brief overview on natural fiber reinforced polymer composites is presented in this work. There is a growing trend to use non conventional and environmental friendly resources for engineering applications. In this scenario Natural fiber are offering a wide range of possibilities. Detailed and thorough study of structure of natural fiber indicates about its hydrophilic nature. Various types of chemical treatment techniques are used by researchers to increase the affinity of reinforcement and matrix .Studies shows that different factors like curing time, temperature, loading condition, fiber orientation etc. affect the properties of natural fiber composites. Lot of work has been carried out with the combination of different fibers and different polymers. Comparative data is presented on properties of different composite.
Effect of Chemical Treatment and Curing Parameters on Mechanical Properties o...IJERA Editor
A brief overview on natural fiber reinforced polymer composites is presented in this work. There is a growing trend to use non conventional and environmental friendly resources for engineering applications. In this scenario Natural fiber are offering a wide range of possibilities. Detailed and thorough study of structure of natural fiber indicates about its hydrophilic nature. Various types of chemical treatment techniques are used by researchers to increase the affinity of reinforcement and matrix .Studies shows that different factors like curing time, temperature, loading condition, fiber orientation etc. affect the properties of natural fiber composites. Lot of work has been carried out with the combination of different fibers and different polymers. Comparative data is presented on properties of different composite.
coir fibers tech has improved so much it can produce micro fibers from petroleum that can be upgraded into artificialleather that can mimic naturalleather
Antibacterial Finishing Of Cotton FabricsKEVSER CARPET
You can find functionalization of antibacterial agents when applied to cotton fabrics,chloroacetate groups, bioactive carboxylic acid, antibacterial activities in these documents.
I found this documents last year while I was searching some datas about antibacterial finishes on warp kniteed blankets , and now I share with you.
Here is now.
Take it and enjoy.
Good lucks.!
Tensile and Impact Properties of Natural Fiber Hybrid Composite MaterialsIJMER
This paper is a review on the tensile and impact properties of natural fiber hybrid composites.
Natural fibers are having good mechanical properties, high specific strength, low cost, bio-degradable
and easily can recyclable through thermal methods. In this paper two different hybrid composites were
manufactured by compression molding and properties of tensile and impact results are conducted as per
ASTM standards. In this project three different fibers such as sisal, jute and glass with thermosets epoxy
resin used with weight ratio of fiber to resin as 15:15:70.Results showed that sisal/glass hybrid composite
has more tensile and impact strength while comparing to sisal/jute hybrid composite.
Modelling and Simulation of Composition and Mechanical Properties of High Ent...msejjournal
Magnesium alloys are high potential materials for application in the aerospace and automotive industries
due to their lightweight properties. They can help to lower dead weight and fuel consumption to contribute
to sustainability and efficiency. It is possible to achieve high specific strength and high stiffness of the
alloys by varying compositions of alloying elements. Applications of magnesium are limited due to its low
strength and relatively low stiffness. This research focuses on a recipe of multi component alloys of
magnesium with varied percentages of Mg, Al, Cu, Mn and Zn obtained from literature and optimizes the
percentage compositions to obtain for high specific strength and specific stiffness. Relationships among
percentage constituents of the alloy components are examined in Matlab R2022b using multiple linear
regression. Optimization is achieved using genetic algorithm to determine the specific strengths and
stiffness. The resulting optimal alloy component percentages by weight are used for microstructure
simulation of thermodynamic properties, diffusion and phase transformations of proposed alloy is done in
MatCalc software version 6.04. Results show potential for improved mechanical properties resulting from
disordered structure in the high entropy magnesium alloy. Future research should focus on production and
characterization of the proposed alloy.
Thermal and Metrological Studies on YTTRIA Stabilized Zirconia Thermal Barrie...msejjournal
Thermal Barrier Coatings (TBCs), routinely prepared from Ceramic based compositions (typically
8%Y2O3-ZrO2or 8YSZ) are being engineered to protect the metallic components from degradation in
applications like gas turbines, jet and automotive engines. With a goal of finding improved TBC materials
a wide variety of ceramics are being researched worldwide. Before physically preparing the TBCs of
uncommon compositions in the laboratory, their suitability to perform can be predicted. Limited
accessibility to detailed and realistic information on the influence of newer compositions (other than 8YSZ)
on TBCs warrants methods to obtain this information.
In this paper, 8YSZ TBCs coated onto aluminium substratesare studied for thermal fatigue, thermal barrier
and materials characteristics to determine the reliability of the coating configuration to withstand the
harshness of test conditions under the framework of experiments. Thereafter, the results have been used to
corroboratethe developed simulation model. Results obtained via thermal tests confirm the suitability of the
model and we can predict the thermal barrier effects of TBCs when prepared from materials other than
YSZ.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
New Experiment System for the Interaction Between Soft Rock and Water : A Cas...msejjournal
The strength of rock strongly depends on the water content especially when the rocks contain clay
materials. The interaction between soft rock and water always threaten the soft rock engineering projects.
For this problem, new sets of laboratory experiment systems are developed to simulate the interaction
between soft rock and water or vapor. In this paper, the principles of experiment systems are introduced
with particular reference to the application on soft rock in Mogao Grottoes, one of the world famous
ancient sites in China. Two kinds of rock samples, the sandstone and muddy sandstone, are obtained by insitu sampling system. Then the laboratory experiments are performed under different environment
conditions. By the specific boundary conditions design, the physical-chemical effect and mechanic effect on
water absorption of rock samples are separated for further mechanism study by the experiment system, and
the different hydrological actions of water and vapor under variable experiment environment are obtained.
The interaction mechanism is discussed with assistant methods, such as SEM (Scanning Electron
Microscope), mercury injection test, X-ray diffraction analysis and etc. With the relation between water
content and soft rock strength, the study may provide guidance and basis for the soft rock engineering in
the future.
International Conference on Embedded Systems and VLSI (EMVL 2023)msejjournal
International Conference on Embedded Systems and VLSI (EMVL 2023) will provide an excellent International forum for sharing knowledge and results in theory, methodology and applications of Embedded Systems.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
Modeling, Analyzing and Safety Aspects of Torsion and Noise Effects on Round ...msejjournal
Each material has its own effect and behavior on external impacts like heat, force, tension, compression,
torsion etc. It is important to study and analyze these behaviors before selecting a material for an
engineering application in the design aspects itself. If predicted values analyzed by both mathematical and
software are available it is easy to get the reliable details in the pre design itself. By this one can ensure the
safety of the component and the system also. In this investigation, the effects of torsional loads on mild steel
round shafts with various diameters and lengths have been analyzed. The additional effects like angle of
rotation, rpm and duration also considered to find the optimum predicted value. The data observed by
various experiments are analyzed by design of experiments especially by response surface methodology.
Minitab software is used for canalization. The data are tabulated and kept for future reference. Noise effect
due to the gradual torsional load performed in the gear box and other rotating components is also studied
for healthy working environment. The nature and characteristics of material also be explained by this noise
analysis.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
On Decreasing of Dimensions of Field-Effect Transistors with Several Sourcesmsejjournal
We analyzed mass and heat transport during manufacturing field-effect heterotransistors with several
sources to decrease their dimensions. Framework the result of manufacturing it is necessary to manufacture
heterostructure with specific configuration. After that it is necessary to dope required areas of the heterostructure by diffusion or ion implantation to manufacture the required type of conductivity (p or n). After
the doping it is necessary to do optimize annealing. We introduce an analytical approach to prognosis mass
and heat transport during technological processes. Using the approach leads to take into account nonlinearity of mass and heat transport and variation in space and time (at one time) physical parameters of these
processes
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Using Advanced Inspection Method (Three-Dimensional Ultrasonic) in Recognitio...msejjournal
In this study, using Harfang Code 32 device, the slag catcher pipelines in one of the South Pars phases
were tested. In radiography method of these lines, no clear defect was observed in radiographic films due
to the high thickness of 40 mm. However, marvelous results were obtained using advanced ultrasonic.
Review and analysis of the results will result in high potential of three-dimensional ultrasonic method in
identifying defects in pipelines with high thicknesses and preventing financial and life-threatening risks
during the use of these refineries in the future.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
RESULTS OF FINITE ELEMENT ANALYSIS FOR INTERLAMINAR FRACTURE REINFORCED THERM...msejjournal
The double cantilever beam (DCB) is widely used for fracture toughness testing and it has become popular
for opening-mode (mode I) delamination testing of laminated composites. Delamination is a crack that
forms between the adjacent plies of a composite laminate at the brittle polymer resin. This study was
conducted to emphasize the need for a better understanding of the DCB specimen of different fabric
reinforced systems (carbon fibers) with a thermoplastic matrix (EP, PEI), by using the extended finite
element method (X-FEM). It is well known that in fabric reinforced composites fracture mechanisms
include microcracking in front of the crack tip, fiber bridging and multiple cracking, and both contribute
considerably to the high interlaminar fracture toughness measured. That means, the interlaminar fracture
toughness of a composite is not controlled by a single material parameter, but is a result of a complex
interaction of resin, fiber and interface properties.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Advances in Materials Science and Engineering: An International Journal (MSEJ) msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Advances in Materials Science and Engineering: An International Journal (MSEJ) msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Advances in Materials Science and Engineering: An International Journal (MSEJ)msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Advances in Materials Science and Engineering: An International Journal ...msejjournal
Advances in Materials Science and Engineering: An International Journal (MSEJ) is a quarterly open access peer-reviewed journal that publishes articles which contribute new results in all areas of the Materials Science and Engineering. The journal is devoted to the publication of high quality papers on theoretical and practical aspects of Materials Science and Engineering.
The goal of this journal is to bring together researchers and practitioners from academia and industry to focus on Materials Science and Engineering advancements, and establishing new collaborations in these areas. Original research papers, state-of-the-art reviews are invited for publication in all areas of Materials Science and Engineering.
Industrial Training at Shahjalal Fertilizer Company Limited (SFCL)MdTanvirMahtab2
This presentation is about the working procedure of Shahjalal Fertilizer Company Limited (SFCL). A Govt. owned Company of Bangladesh Chemical Industries Corporation under Ministry of Industries.
Immunizing Image Classifiers Against Localized Adversary Attacksgerogepatton
This paper addresses the vulnerability of deep learning models, particularly convolutional neural networks
(CNN)s, to adversarial attacks and presents a proactive training technique designed to counter them. We
introduce a novel volumization algorithm, which transforms 2D images into 3D volumetric representations.
When combined with 3D convolution and deep curriculum learning optimization (CLO), itsignificantly improves
the immunity of models against localized universal attacks by up to 40%. We evaluate our proposed approach
using contemporary CNN architectures and the modified Canadian Institute for Advanced Research (CIFAR-10
and CIFAR-100) and ImageNet Large Scale Visual Recognition Challenge (ILSVRC12) datasets, showcasing
accuracy improvements over previous techniques. The results indicate that the combination of the volumetric
input and curriculum learning holds significant promise for mitigating adversarial attacks without necessitating
adversary training.
Hierarchical Digital Twin of a Naval Power SystemKerry Sado
A hierarchical digital twin of a Naval DC power system has been developed and experimentally verified. Similar to other state-of-the-art digital twins, this technology creates a digital replica of the physical system executed in real-time or faster, which can modify hardware controls. However, its advantage stems from distributing computational efforts by utilizing a hierarchical structure composed of lower-level digital twin blocks and a higher-level system digital twin. Each digital twin block is associated with a physical subsystem of the hardware and communicates with a singular system digital twin, which creates a system-level response. By extracting information from each level of the hierarchy, power system controls of the hardware were reconfigured autonomously. This hierarchical digital twin development offers several advantages over other digital twins, particularly in the field of naval power systems. The hierarchical structure allows for greater computational efficiency and scalability while the ability to autonomously reconfigure hardware controls offers increased flexibility and responsiveness. The hierarchical decomposition and models utilized were well aligned with the physical twin, as indicated by the maximum deviations between the developed digital twin hierarchy and the hardware.
Water scarcity is the lack of fresh water resources to meet the standard water demand. There are two type of water scarcity. One is physical. The other is economic water scarcity.
Welcome to WIPAC Monthly the magazine brought to you by the LinkedIn Group Water Industry Process Automation & Control.
In this month's edition, along with this month's industry news to celebrate the 13 years since the group was created we have articles including
A case study of the used of Advanced Process Control at the Wastewater Treatment works at Lleida in Spain
A look back on an article on smart wastewater networks in order to see how the industry has measured up in the interim around the adoption of Digital Transformation in the Water Industry.
NO1 Uk best vashikaran specialist in delhi vashikaran baba near me online vas...Amil Baba Dawood bangali
Contact with Dawood Bhai Just call on +92322-6382012 and we'll help you. We'll solve all your problems within 12 to 24 hours and with 101% guarantee and with astrology systematic. If you want to take any personal or professional advice then also you can call us on +92322-6382012 , ONLINE LOVE PROBLEM & Other all types of Daily Life Problem's.Then CALL or WHATSAPP us on +92322-6382012 and Get all these problems solutions here by Amil Baba DAWOOD BANGALI
#vashikaranspecialist #astrologer #palmistry #amliyaat #taweez #manpasandshadi #horoscope #spiritual #lovelife #lovespell #marriagespell#aamilbabainpakistan #amilbabainkarachi #powerfullblackmagicspell #kalajadumantarspecialist #realamilbaba #AmilbabainPakistan #astrologerincanada #astrologerindubai #lovespellsmaster #kalajaduspecialist #lovespellsthatwork #aamilbabainlahore#blackmagicformarriage #aamilbaba #kalajadu #kalailam #taweez #wazifaexpert #jadumantar #vashikaranspecialist #astrologer #palmistry #amliyaat #taweez #manpasandshadi #horoscope #spiritual #lovelife #lovespell #marriagespell#aamilbabainpakistan #amilbabainkarachi #powerfullblackmagicspell #kalajadumantarspecialist #realamilbaba #AmilbabainPakistan #astrologerincanada #astrologerindubai #lovespellsmaster #kalajaduspecialist #lovespellsthatwork #aamilbabainlahore #blackmagicforlove #blackmagicformarriage #aamilbaba #kalajadu #kalailam #taweez #wazifaexpert #jadumantar #vashikaranspecialist #astrologer #palmistry #amliyaat #taweez #manpasandshadi #horoscope #spiritual #lovelife #lovespell #marriagespell#aamilbabainpakistan #amilbabainkarachi #powerfullblackmagicspell #kalajadumantarspecialist #realamilbaba #AmilbabainPakistan #astrologerincanada #astrologerindubai #lovespellsmaster #kalajaduspecialist #lovespellsthatwork #aamilbabainlahore #Amilbabainuk #amilbabainspain #amilbabaindubai #Amilbabainnorway #amilbabainkrachi #amilbabainlahore #amilbabaingujranwalan #amilbabainislamabad
Cosmetic shop management system project report.pdfKamal Acharya
Buying new cosmetic products is difficult. It can even be scary for those who have sensitive skin and are prone to skin trouble. The information needed to alleviate this problem is on the back of each product, but it's thought to interpret those ingredient lists unless you have a background in chemistry.
Instead of buying and hoping for the best, we can use data science to help us predict which products may be good fits for us. It includes various function programs to do the above mentioned tasks.
Data file handling has been effectively used in the program.
The automated cosmetic shop management system should deal with the automation of general workflow and administration process of the shop. The main processes of the system focus on customer's request where the system is able to search the most appropriate products and deliver it to the customers. It should help the employees to quickly identify the list of cosmetic product that have reached the minimum quantity and also keep a track of expired date for each cosmetic product. It should help the employees to find the rack number in which the product is placed.It is also Faster and more efficient way.
Cosmetic shop management system project report.pdf
Flammability Characteristics of Chemical Treated Woven Hemp Fabric
1. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
DOI:10.5121/msej.2018.5101 1
FLAMMABILITY CHARACTERISTICS OF CHEMICAL
TREATED WOVEN HEMP FABRIC
Mohd Iqbal Misnon1, 2
, Md Mainul Islam1
, Jayantha Ananda Epaarachchi1
, Haizhen
Chen3
, Koichi Goda4
, Md Tawhidul Islam Khan5
1
Centre for Future Materials and School of Mechanical and Electrical Engineering, Faculty
of Health, Engineering and Sciences, University of Southern Queensland, Australia
2
Faculty of Applied Sciences, Universiti Teknologi MARA, Malaysia
3
Zhejiang Textile & Fashion College, China
4
Department of Mechanical Engineering, Faculty of Engineering, Yamaguchi University,
Japan
5
Department of Advanced Technology Fusion, Faculty of Science and Engineering, Saga
University, Japan
ABSTRACT
Woven hemp fabric was treated with sodium hydroxide, commercial flame retardant chemical, and
combination of both to increase its fire-retardant properties. Treatments of fire-retardant changed the
properties of woven hemp fabric such as increased its fabric shrinkage and density of fibres which ranges
from 0.67 to 5% and 1.43 to 1.53 g/cm3
respectively. After the treatment, the fire retardancy of the fabric
increased tremendously which was observed by the burning, thermogravimetry and limiting oxygen index
tests. Some of the samples were not burnt when exposed to flame source and the burning rate needed to be
measured under exaggeration of flame at longer time. The limiting oxygen index value increased from 18.6
to 51 after the treatments which explained the scenario happened in the burning tests. Nevertheless, its
mechanical properties decreased slightly that ranges from 18 to 32% and 23 to 39% for warp and weft
respectively compared to untreated fibre.
KEYWORDS
Woven hemp fabric, Fire retardant properties, Fabric properties, Themogravimetry, Limiting oxygen index
& Burning tests
1. INTRODUCTION
The fire protection and retardancy of materials have become a serious issue nowadays in many
industries. The textile industry is no exception in this matter and there are range of requirements
which depend on where the textile material is utilized [1]. In the technical textile application,
fabrics that have good flame resistance properties are mostly made of synthetic fibres such as
glass, carbon and aramids. These high-performance fabrics are commonly used in special
technical requirements and purposes such as materials used in high load bearing application in
building infrastructures, marines and aerospace industries [2].
Hemp is a well-known fibre in the textile industry. It belongs to a group with jute and flax as the
primary material in the production of heavy and medium-weight fabrics in the linen industry.
Hemp is currently used to produce hats, shirts, shoes, backpacks and jeans. It is also used for
producing paper fibres as well as bedding for animals [3]. Hemp composed of 68-74.4% of
cellulose, 15 - 22.4% of lignocellulosic, lower in lignin, pectin and waxes, which makes this fibre
relatively strong [4,5]. It is worth mentioning that even it possesses good properties, there are
2. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
2
fewer works on enhancing its fire retardant properties. Thus, efforts on improving these properties
are necessary since its application is not only limited to apparel and textiles but also in various
engineering fields such as in panel and other composite material productions [5-8]. Observing at
the amount of cellulose content in hemp, one can predict hemp tolerances against flame. There
are no other ways to enhance its fire retardant properties except by employing fire retardant
finishes or treatments.
It is well-known that there are three (3) components of combustion; heat, fuel, and oxygen [9].
These three components form some complex processes in textile combustion. When a textile fibre
is exposed to heat, it pyrolyses at ‘pyrolysis temperature’, while volatile liquids and gases act as
fuels for further combustion. The temperature should be equal to or greater than ‘combustion
temperature’ after pyrolysis to burn flammable volatile liquids in the presence of oxygen thus
producing products such as carbon dioxide and water. Textile fibre is continuously ignited as
long as there is heat from an external source which raises its temperature until it degrades.
Therefore, fire retardant functions to interfere at least one of the three components mentioned
above [2].
Some chemical compounds, for instance, bromides, tri-hydroxide and phosphates are very useful
to enhance the fire retardant of cellulosic fibres [9]. Their role includes, directing thermal
degradation to fuel-poor pyrolytic paths, coating of the substrate to exclude oxygen, preventing
evolution of combustible gases, diluting fuel formed by pyrolysis, and to dissipate heat away
from the flame front [10]. The rate of the initial rise in temperature depends on the specific heat
of the fibre, thermal conductivity, and the latent heat of fusion. Since the 1950s up to present,
many researchers have been conducted on fire retardant chemicals in many aspects such as its
toxicity, durability and new chemical products [2,11,12].
Nevertheless, the most determinant in the selection of fire retardant finishes of the textile material
is cost. Manufacturers are very concerned on how the finishes are applied on the material
especially on natural fibres. Applying complicated finishing on the natural fibre will increase the
cost. Other alternatives are using pre-treated cellulosic fire retardant fibres which are available at
reasonably low cost. Other than that, applying commercial fire retardant chemicals which are
available in the market is a good option.
A simple finishing material that is meant to increase fire retardancy of natural textile fibres is
sodium hydroxide (NaOH). Shafizadeh, et al. [13] in their work, evaluated the mechanistic of fire
retardant and ranked NaOH in their list of retardants. Chen, et al. [14], on the other hand, worked
on the effects of fire retardant addition on the combustion properties of a charring fuel and used
NaOH as the fire retardants. Mostashari, et al. [15] investigated the effect of NaOH deposition on
the cotton the rmogravimetry. These works show that NaOH is recognised as a fire retardant for
natural textile fabric thus it is worth trying it on the hemp fabric. The purpose of this work is to
assess fire retardant properties of wo
ven hemp fabric (WHF) treated with the commercial fire retardant as well as sodium hydroxide
chemicals. It is also to determine the fire retardant performances in between the commercial fire
retardant, sodium hydroxide treatments, and combination of both for hemp fabric. In this work,
three types of treatment were applied on woven hemp fabric including sodium hydroxide
(NaOH), flame retardant (FR) solution and combination of NaOH and FR chemicals. The fabrics
were treated by employing dips and nips method. The fire retardant properties were evaluated by
means of burning test, thermogravimetric analysis as well as limiting oxygen index. Measurement
on the fabric physical properties were also done to understand the changes before and after the
treatments, and tensile test were performed to analyse the WHF mechanical properties affected by
the treatments.
3. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
3
2. MATERIALS AND METHOD
2.1. Materials
A commercial ‘heavy fabric’ grade WHF was supplied by Hemp Wholesale Australia. Table 1
shows the physical properties of the WHF. According to the specifications given by the supplier,
the fabrics were produced from 100% yarn hemp in both warp and weft. The yarns were
converted from cleaned hemp fibre through spinning processes and the twist given was 430 twists
per meter. These yarns were then converted into fabric via weaving processes and the fabrics
were woven by employing loose plain weave (taffeta) structure. Commercial grade NaOH was
supplied by Science Essential Australia while commercial flame retardant (FR) chemical was
supplied by Cyndan Chemicals, Australia. According to the supplier, the main active ingredient in
this flame retardant is ammonium polyphosphate. Information from the technical and material
datasheet says this chemical is water-based, not classified as hazardous, and is environmental
friendly.
Table 1. Physical properties of woven hemp fabric
2.2. Chemical Treatment and Density Measurement
WHF was treated with NaOH, FR and combination of both chemicals (NaOH+FR). For the first
treatment, fabrics were soaked in NaOH solution (10% concentrations) for 3 hours at room
temperature. The fabrics were next washed with distilled water for several times to remove excess
alkali from the fabric. The washed fabrics were dried at room temperature for 8 hours, and then
oven dried at 100°C for another 6 hours. The subsequent neutralisation treatment was abandoned
to retain the alkali cellulose formed on the fabric surface [15]. The dried fabrics were stored in a
sealed plastic bag to avoid atmospheric moisture contamination prior to chemical and thermal
analyses.
For the FR treatment, according to the supplier, the FR can be used as it is by spraying or dipping,
and drying is not necessary. However, in this work, ‘dip and nip’ method was employed to treat
the fabrics. The nipping process was set carefully so that the chemical uptake is consistent and
maintained within the range of 100-105%. The treated fabrics were then left to dry at room
temperature for 8 hours.
Whilst for the combination of NaOH+FR, the fabric was firstly treated with NaOH and followed
by the FR using the procedures mentioned above. The abbreviation for WHF; untreated, treated
with sodium hydroxide, treated with FR chemical and treated with sodium hydroxide combined
with FR are WHF-UT, WHF-NaOH, WHF-FR and WHF-NaOH+FR respectively.
The density of the treated fabrics were measured to determine the changes before and after
treatment using Multipycnometer MVP D160E. Helium gas was used as the displacement
4. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
4
medium. The helium was added to the fibres under vacuum condition to ensure that all interior air
cavities in the submerged fibres (e.g. the fibre lumen) were filled with helium. The data reported
are the average and standard deviation of 3 measurements [16].
The chemical uptake or pick-up for all treated WHF was calculated using Eq. (1) [18,19].
ℎ (%), = × 100 (1)
Where, W2 is the weight of fabric after treatment and W1 is the weight of fabric before treatment
and both should be in dry condition.
The fabric shrinkages after the treatments were measured using Eq. (2) as follows;
ℎ (%), =
! !
!
× 100 (2)
Where, L2 is the length of fabric after treatment and L1 is the length of fabric before treatment.
The weight of each fabric (untreated and treated) was calculated by calculating total weight of
warp and weft yarn. The weight can be measured using the Eq. (3) [16, 17] as follows;
" ℎ# ( $
⁄ ), & =
' (()* )
+
+
' (()* )
+
(3)
Where N is the yarn size, C is the yarn crimp percentage while subscripts 1 and 2 refer to warp
and weft yarn respectively. P is the yarn spacing in mm. The measurement and calculation
procedures for yarn spacing (P) of the WHF are shown in Misnon, et al. [16].
2.3. Flammability Test
Ignition time and burning behaviour as well as flame spread properties were investigated to
determine the flammability properties of treated hemp fabrics. Ignition time and burning
behaviour of the samples were measured using James Heal and Halifax Flammability Tester in
accordance with BS 5438 at 24°C and 65% relative humidity room condition. In this test, a
sample with the dimension of 220 × 170 mm was mounted in a steel frame as shown in Figure
1(a) after being conditioned for 24 hours also at 24°C and 65% relative humidity. A standardized
flame source was applied to the surface from the bottom, and the ignition time was set at 12
seconds. Three (3) specimens from warp and weft samples for each textile fabric were processed
and average was taken for interpretation. The ignition time, flame and smouldering time (after
glows) and burning characteristics were recorded [19].
The spreading of flame test was conducted in accordance with ISO 6941 by mounting the fabric
sample on a steel frame as shown in Figure 1 (b) held vertically on the James and Halifax
Flammability Tester instrument. The specimen was exposed from below to flame source for 12
seconds. At four (4) different spots, a standardized marker thread was placed to determine
spreading rate of flame. Two (2) threads were placed horizontally at two different heights across
the sample surface that were at 300 mm and 600 mm horizontally to measure vertical spreading
flame. The other two (2) threads were placed vertically on both left and right sides of the fabric
specimens to measure the flame spreading rate horizontally [20-23]. When the flame spread and
reached any of mark, the thread was burnt and the respective marker timer was stopped. Three (3)
specimens (600 ×170 mm) of warp and weft for each treated fabric type were conditioned and the
time of flame spreading for both vertical and horizontal were recorded and their average was
measured.
5. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
5
(a) BS 5438 (b) ISO 6941
Figure 1. Steel frame used to mount fabric sample following (a) BS 5438 and (b) ISO 6941
2.4. Thermogravimetric Analysis
Thermogravimetric analyses (TGA) were carried out on a TA Instruments Model TGA Q500,
operating under nitrogen and air atmosphere using a platinum pan. The runs were performed over
a temperature range between 30 and 600°C at 10°C/min heating rate and 20 ml/min flow.
2.5. Limiting Oxygen Index
Limiting oxygen index (LOI) is a method to determine the minimum oxygen concentration in an
oxygen/nitrogen mixture that will sustain the flame. It is a convenient, reproducible, and
inexpensive way of determining the tendency of a material to sustain flame. The LOI test was
carried out using an LOI instrument model number of M606 in accordance with ASTM: D2863.
A test sample of 150 × 50 mm was placed in a transparent test chamber and ignited at the top. The
oxygen concentration in the mixture of oxygen and nitrogen was increased slowly until the
sample sustained burning. The volume fraction of the oxygen in the gas mixture was reported as
the LOI.
2.6. Tensile Test
The tensile properties (ASTM: D5034) of hemp fabrics were characterized using universal testing
machine, MTS Alliance RT/10. A 75 mm wide test specimen was cut in the desired direction
(warp or weft) and then equal numbers of yarns were removed from both sides until the specimen
width was reduced to 50 mm. The same procedure was followed for test strips in both warp and
weft directions. The tensile tests were performed using a gauge length of 75 mm and a crosshead
speed of 10 mm/min. The cross-sectional area used to convert load into stress was calculated
from the test specimen width and the thickness of fabric obtained from the fabric characterization
[24, 25].
Typically, the tensile curve (in stress-strain curve) for most of the textile fabrics initially started in
nonlinear and then its slope increased slowly until finally becoming linear. The mechanical
properties of textile fabrics could not be determined under the nonlinear curve. Therefore, a linear
trend line was drawn to extend the linear part of the curve to the axis of strain in order to
determine the tensile stress, tensile modulus as well as strain at peak of hemp fabric [16, 26].
3. RESULTS AND DISCUSSION
3.1. Treatment Effects on the Physical Properties of Woven Hemp Fabric
Changes of the physical properties of WHFs before and after chemical treatment are shown in
Table 2. The chemical pick-up on WHF was measured based on the changes in weight before and
after treatment with the assumption that there is no yarn lost when the treatment is done. The
6. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
6
weight of WHF fabric which was treated with NaOH (WHF-NaOH) and FR (WHF-FR),
increased by 18.19 and 24.94% respectively whilst the weight of WHF treated with both
chemicals (WHF-NaOH+FR) was recorded even higher which was 30.10% higher due to the
deposition of treatments. The density of treated WHF increased drastically as compared to the
untreated WHF due to effect of the treatment applied on them.
The changes in fabric dimensions were also observed where all the treated samples experienced
shrinkage for both warp and weft directions. The shrinkage from the sample treated with NaOH
(WHF-NaOH) showed the highest among all the samples. The combination of NaOH and FR
treatment shrunk the sample (WHF-NaOH+FR) a bit lower than the NaOH treatment and the least
change was shown by the sample treated with only FR (WHF-FR). Observing the differences in
shrinkage percentages of all the samples, it seems that the NaOH treatment is responsible for the
higher shrinkage. It can be observed that with the NaOH alone, the shrinkage was recorded the
highest whilst FR shows the lowest among all the samples. In the combined treatment, WHF was
firstly treated with NaOH and this process made the fabric shrunk but the shrinkage was a bit
lower than WHF-NaOH most probably due to the FR treatment.
Table 1. Chemical pick-up, fibre density and fabric shrinkage properties of all the WHF samples
During the alkali treatment, NaOH has removed the organic component in the WHF. In the textile
industry, this treatment is similar to ‘mercerisation’ where concentrated alkaline is applied to the
cotton fabric. This process is meant to increase lustre, hygroscopicity, strength as well as the dye
affinity of the cotton fabric [15, 27]. In general, cotton is similar to hemp, which is categorised
under natural textile fibres; thus, similar effect is expected to happen to WHF. Under the action of
this treatment, physicochemical and structural modification of cellulose takes place. Apart from
the hemicellulose and lignin removal and in structural modification by alkali treatment, the
structure of the fibre inter-converts from alpha-cellulose and beta-cellulose mixture to a
thermodynamically favourable cellulose II polymorph [27]. This chemical reaction lead to
formation of alkali cellulose, physical reaction, to intensive swelling of fibres and structural
reactions, and to a change in the arrangement of units in the cellulose macromolecule. When the
fibre swells, its volume undergoes considerable changes; increases in water absorption due to the
increase of pore size and then leads to the increase in cross-section of fibre by 40 to 50% [15, 27].
The Scanning electron microscopic (SEM) images in Figure 2 (a) show the untreated WHF-UT
sample. From the cross-section of the image, the fibres have thin and lenticular shape and its
surface is rough due to hemicellulose and lignin. In contrast, WHF-NaOH sample exhibits the
changes in fibre’s cross-section from elliptical to become rounder suggesting that the fibres were
swollen and the diameter was increased which can be seen from Figure 2 (b). The surface of the
fibres became clean due to the removal of hemicellulose, lignin and fat [15, 27].
From the reduction in hemicellulose and lignin, the percentage of cellulose is presumably
increased. This explains why the fibre density of WHF-NaOH was found a bit higher (1.51 g/cm3
)
in comparison with the untreated fabrics (1.47 g/cm3
). The density of hemp fibre can vary
depending on how much the cellulose content is in the fibres because the higher the cellulose
content the denser the fibre would be [28]. As a consequence from the swollen fibres, the fabric
(WHF-NaOH) experienced shrinkage because the yarn released tension which was developed
during the processes such as yarn spinning, fabric weaving and fabric finishing [29].
7. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
In terms of FR treatment, there were FR particles (marked in red circles) with the si
from several micro- to nanometres deposited on the fibre surface (
fibre cross-section changing from lenticular to become rounder, the surface was observed quite
clean from the hemicellulose and lignin as compared to
the treated WHF leads to the increase of its density and the reason for this is similar to WHF
NaOH. From Table 2, the increment on weight for WHF
recorded 24.94%, which was a bit
The WHF-NaOH+FR samples exhibited the highest chemical pick
treatment with NaOH and FR chemicals. The sputtered surfaces in
due to the reaction between both ch
polyphosphate, the presence of phosphorus (or sulphur) derivatives were able to generate acid or
acid-forming agents [30]. Most of the fire retardant chemicals (for natural biomass/fibre) are a bi
acidic and this is for creating a good durability on the natural fibres and gives some balance for
the treated fibres when subjected to other treatments. However, the acid is not strong enough to
rough the fibres as what happened to the cotton fibre trea
et al. [29]. As for the NaOH treatment, since no neutralisation is happened, the content of the
alkali remaining in the fibre can be said higher suggesting that some reactions between the
chemicals occurred (refer section
surface, is most likely salts, products of the reaction between a generated acid and pure alkali
from FR and NaOH, respectively. The shrinkage of this sample was a little lower than the sample
WHF-NaOH but higher than WHF
alkali and dried before it was treated with FR chemical. In addition, the consequences of the
treatment are the elimination of hemicellulose and lignin on top of additi
surface which latter causes the increment of the density of this sample.
The changes in physical properties due to the treatment definitely change the quality of hemp
fabric. In the application, as the hemp shrinks after the
some allowance before the treatments to make sure the hemp fabric is adequate for their usage.
Since the treated hemp fabrics do not go through any neutralisation process, they cannot be used
as apparel and garment products but can be used in furnishing, backing layer as well as in
technical application such as composite reinforcements and insulations. The cost borne by the
manufactures for using these treated fabrics will be increased due to the additional fabric
treatments.
Cross
Cross
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
In terms of FR treatment, there were FR particles (marked in red circles) with the si
to nanometres deposited on the fibre surface (Figure 2 (c)). Apart from the
section changing from lenticular to become rounder, the surface was observed quite
clean from the hemicellulose and lignin as compared to Figure 2 (a). The increment of weight of
the treated WHF leads to the increase of its density and the reason for this is similar to WHF
, the increment on weight for WHF-FR due to chemical deposition was
recorded 24.94%, which was a bit higher than the WHF-NaOH sample (18.19%).
NaOH+FR samples exhibited the highest chemical pick-up because of the combined
treatment with NaOH and FR chemicals. The sputtered surfaces in Figure 2 (d) were probably
due to the reaction between both chemicals. Since the main reactive chemical in FR is ammonium
polyphosphate, the presence of phosphorus (or sulphur) derivatives were able to generate acid or
. Most of the fire retardant chemicals (for natural biomass/fibre) are a bi
acidic and this is for creating a good durability on the natural fibres and gives some balance for
the treated fibres when subjected to other treatments. However, the acid is not strong enough to
rough the fibres as what happened to the cotton fibre treated with fire retardant as found by
. As for the NaOH treatment, since no neutralisation is happened, the content of the
alkali remaining in the fibre can be said higher suggesting that some reactions between the
ection 2.2). Therefore, the sputter, as shown in WHF
surface, is most likely salts, products of the reaction between a generated acid and pure alkali
from FR and NaOH, respectively. The shrinkage of this sample was a little lower than the sample
NaOH but higher than WHF-FR. This is because the fabric has been firstly treated with
alkali and dried before it was treated with FR chemical. In addition, the consequences of the
treatment are the elimination of hemicellulose and lignin on top of addition of salt on the fibre
surface which latter causes the increment of the density of this sample.
The changes in physical properties due to the treatment definitely change the quality of hemp
fabric. In the application, as the hemp shrinks after the chemical treatments, the users need to add
some allowance before the treatments to make sure the hemp fabric is adequate for their usage.
Since the treated hemp fabrics do not go through any neutralisation process, they cannot be used
t products but can be used in furnishing, backing layer as well as in
technical application such as composite reinforcements and insulations. The cost borne by the
manufactures for using these treated fabrics will be increased due to the additional fabric
(a)
(b)
Cross-section Fibre surface
Cross-section Fibre surface
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
7
In terms of FR treatment, there were FR particles (marked in red circles) with the size ranging
(c)). Apart from the
section changing from lenticular to become rounder, the surface was observed quite
(a). The increment of weight of
the treated WHF leads to the increase of its density and the reason for this is similar to WHF-
FR due to chemical deposition was
up because of the combined
(d) were probably
emicals. Since the main reactive chemical in FR is ammonium
polyphosphate, the presence of phosphorus (or sulphur) derivatives were able to generate acid or
. Most of the fire retardant chemicals (for natural biomass/fibre) are a bit
acidic and this is for creating a good durability on the natural fibres and gives some balance for
the treated fibres when subjected to other treatments. However, the acid is not strong enough to
ted with fire retardant as found by Lam,
. As for the NaOH treatment, since no neutralisation is happened, the content of the
alkali remaining in the fibre can be said higher suggesting that some reactions between the
). Therefore, the sputter, as shown in WHF-NaOH+FR
surface, is most likely salts, products of the reaction between a generated acid and pure alkali
from FR and NaOH, respectively. The shrinkage of this sample was a little lower than the sample
FR. This is because the fabric has been firstly treated with
alkali and dried before it was treated with FR chemical. In addition, the consequences of the
on of salt on the fibre
The changes in physical properties due to the treatment definitely change the quality of hemp
chemical treatments, the users need to add
some allowance before the treatments to make sure the hemp fabric is adequate for their usage.
Since the treated hemp fabrics do not go through any neutralisation process, they cannot be used
t products but can be used in furnishing, backing layer as well as in
technical application such as composite reinforcements and insulations. The cost borne by the
manufactures for using these treated fabrics will be increased due to the additional fabric and
Fibre surface
Fibre surface
8. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
Figure 1. Scanning electron microscopic images
surface views; (a) untreated, (b) NaOH, (c) FR, and (d) NaOH + FR
3.2. Effect of Fire Retardant Treatment on Ignition Time and Burning Behaviour
The differences in the burning behaviour of the untreated and fire retardant treated WHF can be
observed from the ignition time and burning behaviour tests. In this test, the time exposure to
small flame was set for 12 s. The fabric was exposed to flame in
and the results for each sample is the average of 3 specimens.
ignition time for all fabric samples in this work.
Among the samples, only the untreated sample was burnt completely. There are no
differences between the times taken in between warp and weft specimens. The ignition time for
WHF was about 3 to 3.5 s and after the flame source was removed, the fabric burnt rapidly. The
time taken for the whole specimen to burn was between 247 t
extinguished, the fabric continued to smoulder for another 27 s and left a very poor residue
behind. Figure 3 (a) shows the image of the burning test, which was taken when the fabric was
still burning while Figure 3 (b) is after
was burnt with yellow flames, released smoke in white colour and smell like burnt paper, which
is common for natural fibres.
In the case of WHF-NaOH sample, the time taken for the fabric to ign
WHF-UT sample which was about 7 to 8 s. Moreover, typically, the flame only continued for
about 3 to 5 s after the fabric was exposed to flame for 12 s.
for the WHF-NaOH right after the flame was
continued to smoulder for another 42 to 46 s before the fire was totally out. The part that was
exposed to flame source was burnt to ash (including burning during smouldering) and can be seen
in Figure 3 (d). The total burning process for sample WHF
it was extinguished were 57 s and 63 s for both warp and weft directions respectively. Other
characteristics observed during the burning were, the flame was yellow in colour
coloured smoke and produced an intense smell most probably due to the burning of alkali content
Cross
Cross
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
(c)
(d)
Scanning electron microscopic images of all WHF samples fibres in cross-section and fibre
surface views; (a) untreated, (b) NaOH, (c) FR, and (d) NaOH + FR
Effect of Fire Retardant Treatment on Ignition Time and Burning Behaviour
The differences in the burning behaviour of the untreated and fire retardant treated WHF can be
observed from the ignition time and burning behaviour tests. In this test, the time exposure to
small flame was set for 12 s. The fabric was exposed to flame in both warp and weft directions
and the results for each sample is the average of 3 specimens. Table 3 shows the results of
ignition time for all fabric samples in this work.
Among the samples, only the untreated sample was burnt completely. There are no
differences between the times taken in between warp and weft specimens. The ignition time for
WHF was about 3 to 3.5 s and after the flame source was removed, the fabric burnt rapidly. The
time taken for the whole specimen to burn was between 247 to 249 s. When the flame was
extinguished, the fabric continued to smoulder for another 27 s and left a very poor residue
(a) shows the image of the burning test, which was taken when the fabric was
(b) is after the flame extinguished. It was also observed that the fabric
was burnt with yellow flames, released smoke in white colour and smell like burnt paper, which
NaOH sample, the time taken for the fabric to ignite was longer than the
UT sample which was about 7 to 8 s. Moreover, typically, the flame only continued for
about 3 to 5 s after the fabric was exposed to flame for 12 s. Figure 3 (c) shows the burning test
NaOH right after the flame was self-extinguished and it was observed that the fabric
continued to smoulder for another 42 to 46 s before the fire was totally out. The part that was
exposed to flame source was burnt to ash (including burning during smouldering) and can be seen
(d). The total burning process for sample WHF-NaOH from the flame exposure until
it was extinguished were 57 s and 63 s for both warp and weft directions respectively. Other
characteristics observed during the burning were, the flame was yellow in colour, released white
coloured smoke and produced an intense smell most probably due to the burning of alkali content
Cross-section Fibre surface
Cross-section Fibre surface
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
8
section and fibre
Effect of Fire Retardant Treatment on Ignition Time and Burning Behaviour
The differences in the burning behaviour of the untreated and fire retardant treated WHF can be
observed from the ignition time and burning behaviour tests. In this test, the time exposure to
both warp and weft directions
shows the results of
Among the samples, only the untreated sample was burnt completely. There are no notable
differences between the times taken in between warp and weft specimens. The ignition time for
WHF was about 3 to 3.5 s and after the flame source was removed, the fabric burnt rapidly. The
o 249 s. When the flame was
extinguished, the fabric continued to smoulder for another 27 s and left a very poor residue
(a) shows the image of the burning test, which was taken when the fabric was
the flame extinguished. It was also observed that the fabric
was burnt with yellow flames, released smoke in white colour and smell like burnt paper, which
ite was longer than the
UT sample which was about 7 to 8 s. Moreover, typically, the flame only continued for
(c) shows the burning test
extinguished and it was observed that the fabric
continued to smoulder for another 42 to 46 s before the fire was totally out. The part that was
exposed to flame source was burnt to ash (including burning during smouldering) and can be seen
NaOH from the flame exposure until
it was extinguished were 57 s and 63 s for both warp and weft directions respectively. Other
, released white
coloured smoke and produced an intense smell most probably due to the burning of alkali content
Fibre surface
Fibre surface
9. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
9
in the fabric. The fire retardant property of the WHF was improved with NaOH treatment in
comparison with the untreated sample (WHF-UT), in terms of the total burning times.
Table 2. Results of burning behaviour and ignition time
X – Indicates the expected event had not happened.
(a) (b) (c)
(d) (e) (f)
Figure 2. Burning characteristic of WHF sample; (a) WHF-UT sample during the test, (b) WHF-UT
sample after burning and, (c) WHF-NaOH sample smouldering (after glow). (d) WHF-NaOH, (e) WHF-FR
and, (f) WHF-NaOH+FR after burning characteristic test
Based on Table 3, sample WHF-FR shows good properties against the fire. It was observed that
neither ignition nor flame sparked on the fabric sample when exposed to the flame. Only the
charring processes happened to the WHF on the contact point to the flame source, and the
carbonaceous char was spread a bit to the upper part direction of the fabric during exposure to the
flame source. Table 3 (e) shows the WHF-FR sample after flame source exposure and its char
formation size was small compared to the WHF-NaOH sample. It was also observed that the
exposure of WHF-FR to the flame produced white smoke and intense smell similar to the WHF-
NaOH sample. In Figure 3 (f), the WHF sample treated with NaOH and FR chemicals (WHF-
NaOH+FR) exhibited effects comparable with WHF-FR. Neither ignition nor smoulder was
10. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
10
observed during the flame test and it also produced white smoke and intense smell when exposed
to flame source.
In the case of WHF-FR and WHF-NaOH+FR, char was formed which successfully extinguished
the fire. This char is undoubtedly attributed to ammonium polyphosphate and NaOH contents in
the FR chemical [30]. Char formation can make the carbon and hydrogen stay in the condensed
phase thus reducing the mass of volatile combustible degradation fragment evolved. Char also
acts as thermal insulator by remaining on the virgin polymer substrate, absorbing some of the heat
input thereby reducing the heat flux reaching the virgin polymer [31, 32]. As the char surface
temperature increases, re-radiation lost increases significantly therefore assisting to prevent
thermal degradation. Char formed at substrate surfaces also acts as a physical barrier to obstruct
the flow of combustible gases generated from the degradation of the underlying unburnt material
and hindering the access of oxygen to the surface of the polymer [32]. In the case of WHF-NaOH,
it can be said that the extinguishing of fire was not only due to the char formation because there
was smouldering after the fire was put out (Figure 3 (c)). This might be due to some combustible
gas leakages that reacted with oxygen and continued to burn the residual virgin polymer of hemp
fabric (charred parts).
3.3. Spreading of Flame
The spreading of flame was tested for the untreated and all treated WHF samples. The time taken
for flame travel along the fabric was recorded at 3 different marks (yarn tread) which were, at the
height of 300 mm, 600 mm and to the horizontal direction either left or right. The burning rates
were calculated by means of dividing the length of fabrics vertically (600 mm) by their burning
times in seconds [15]. The flame spreading results for all WHF samples are shown in Table 4 and
it was found that only the untreated sample (WHF-UT) was burnt to the whole specimen. It took
only 22 and 23 s for the flame to reach first mark after exposed to the flame source and the total
times to reach the second mark were recorded 46 and 50 s for both warp and weft respectively.
The movement of flame to the horizontal part was slower which recorded as 77 and 74 s in total
of time for both warp and weft specimen respectively. The burning of this WHF-UT sample can
be depicted in Figure 3 (a), when it was exposed to flame source, and Figure 3 (b) when it
reached all three marks. The burning rate of this sample was measured in the range of 1.2 to 1.3
cm s-1
for both warp and weft directions.
In contrast to the untreated WHF-UT sample, any of the treated woven hemp samples did not
reach all three marks because these samples did not burn when they were exposed to the flame
source. Therefore, the burning time cannot be measured for all the treated WHF. With such a
result as what has been discussed in ignition time and burning behaviour test previously, this
flame spreading test results was expected. The short flame source exposure in 12 s did not affect
any treated WHF sample.
Table 3. Flame spreading results of all woven hemp fabrics
X – Indicates the expected event had not happened.
11. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
11
Therefore, in order to investigate further about the WHF flammability properties especially the
burning rate or char burning rate, the flame exposure was decided to be extended from 12 s to 2
minutes (120 s). In this way, particularly for the FR treated fabrics, the burning rate or char
formation rate can be measured under exaggeration of flame. This is also to imitate a real fire
situation in which the hemp fabric may be exposed to continuous fire from other sources such as
burning woods, papers etc. Table 5 shows the results of the spreading flame test of all treated
WHF samples subjected to 2-minute flame exposure. Even with the longer exposure to flame, any
of all types of treated samples did not reach the first mark. The WHF-NaOH sample did burn but
as soon as the flame source was removed, the flame continued for several seconds before
extinguishing with some smouldering for another 20 to 50 s. However, the flame and smoulder
burned the char into ash and this was similar to what has been discussed in Section 3.2.
Table 4. Flame spreading results for all treated samples when subjected to 2-minute flame exposure
X – Indicates the expected event had not happened.
In the case of another two treated samples, it was observed that during the flame source exposure,
chars was formed on the both of WHF-FR and WHF-NaOH+FR samples and were getting bigger
towards the end of exposure. The width and height of the burnt area or char formation on the
treated WHF as well as the char formation rate were measured in order to analyse the different
effects of flame exposure duration (results are shown in Table 6). The recorded figures were an
average of 3 readings for the respective treated WHF sample.
Comparing all the samples in Table 6, the WHF-NaOH sample’s burnt area was bigger than the
other samples when exposed to flame. This can be seen in Figure 4 (c), (d) and (e). The WHF-
NaOH sample burnt width increased by 75%, from 42 mm to 71 mm when exposed to flame for 2
minutes while the height increased by 124.5%, from 98 to 220 mm. For the WHF-FR and WHF-
NaOH+FR samples, the width and height of char formation area were about 50% less than the
WHF-NaOH sample for both flame exposure times. Nevertheless, it was observed that the char
formation from the WHF-NaOH+FR sample was a little lower than the WHF-FR sample
indicating that the combined treatment can give better effect on the fire-retardant properties.
Table 5. Spreading of burnt or char formation for all treated WHF samples
12. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
(c)
Figure 3. Flame spreading test photos, a) and b)
samples, c) WHT-NaOH, d) WHF
Since all the treated WHF samples were exposed longer to the flame source, the char formations
on the fabrics were bigger. Therefore, the
possible to be measured. The char formation rate of the WHF
among all the samples, yet, this rate was far lower than the burning rate of WHF
Error! Reference source not found.
about 55% with the incorporation of FR chemical in comparison with WHF
was possessed by theWHF-NaOH+FR sample. With this
exaggeration of longer flame time, there is no way that all treated WHF could reach even first
mark (300 mm) during this test. Nevertheless, it was shown that all the treatments on the WHF
samples enhanced the flame retardant properties with the best result from the combination of
NaOH+FR, followed by FR and then NaOH.
3.4. Thermal Properties of Untreated and Treated WHF
Studies on the thermal decomposition of the treated fabrics were carried out by thermogravimetric
(TG) and derivatives themogravimetric (DTG) analyses.
DTG curves respectively for all the samples while Table 7 shows the
mass loss rate, mass loss rate and char yield. The TG analysis of untreated WHF (WHF
sample shows that the main pyrolysis started from the onset temperature of degradation at about
220°C until 400°C and temperature at the maximu
the end of the main pyrolysis, the mass loss due to completed cellulose dehydration accounted for
80% at 400°C. The mass loss during this stage was very fast due to the degradation of
hemicellulose and cellulose composition in hemp fibres. As the temperature increased,
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
(a) (b)
(c) (d) (e)
Flame spreading test photos, a) and b) are WHF-UT specimen under flame spreading test, and
NaOH, d) WHF-FR and e) WHF-NaOH+FR after the test
Since all the treated WHF samples were exposed longer to the flame source, the char formations
on the fabrics were bigger. Therefore, the char formation rates of all treated WHF samples were
possible to be measured. The char formation rate of the WHF-NaOH sample was the highest
among all the samples, yet, this rate was far lower than the burning rate of WHF
Error! Reference source not found. Table 4). The char formation rates of WHF dropped
about 55% with the incorporation of FR chemical in comparison with WHF-NaOH and the lowest
NaOH+FR sample. With this char formation rate, in spite of under
exaggeration of longer flame time, there is no way that all treated WHF could reach even first
mark (300 mm) during this test. Nevertheless, it was shown that all the treatments on the WHF
etardant properties with the best result from the combination of
NaOH+FR, followed by FR and then NaOH.
Thermal Properties of Untreated and Treated WHF
Studies on the thermal decomposition of the treated fabrics were carried out by thermogravimetric
(TG) and derivatives themogravimetric (DTG) analyses. Figure 5 (a) and (b) show the TG and
DTG curves respectively for all the samples while Table 7 shows the temperature at maximum
mass loss rate, mass loss rate and char yield. The TG analysis of untreated WHF (WHF
sample shows that the main pyrolysis started from the onset temperature of degradation at about
220°C until 400°C and temperature at the maximum mass loss rate was 379°C (refer
the end of the main pyrolysis, the mass loss due to completed cellulose dehydration accounted for
80% at 400°C. The mass loss during this stage was very fast due to the degradation of
se composition in hemp fibres. As the temperature increased,
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
12
UT specimen under flame spreading test, and
Since all the treated WHF samples were exposed longer to the flame source, the char formations
char formation rates of all treated WHF samples were
NaOH sample was the highest
among all the samples, yet, this rate was far lower than the burning rate of WHF-UT (refer
). The char formation rates of WHF dropped
NaOH and the lowest
char formation rate, in spite of under
exaggeration of longer flame time, there is no way that all treated WHF could reach even first
mark (300 mm) during this test. Nevertheless, it was shown that all the treatments on the WHF
etardant properties with the best result from the combination of
Studies on the thermal decomposition of the treated fabrics were carried out by thermogravimetric
(a) and (b) show the TG and
temperature at maximum
mass loss rate, mass loss rate and char yield. The TG analysis of untreated WHF (WHF-UT)
sample shows that the main pyrolysis started from the onset temperature of degradation at about
m mass loss rate was 379°C (refer Table 7). At
the end of the main pyrolysis, the mass loss due to completed cellulose dehydration accounted for
80% at 400°C. The mass loss during this stage was very fast due to the degradation of
se composition in hemp fibres. As the temperature increased,
13. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
hemicellulose was firstly degraded due to the cellular breakdown and then followed by the
cellulose which degraded at higher temperature because it was highly crystalline
the pyrolysis product of cellulosic were produced in this stage and that included L
major product and combustible gases
Figure 4. (a) TG and (b) DTG curves of untreated and treated WHF samples
Table 6. Temperature at maximum mass loss rate and char yield at 800°C of all WHF samples
The charring reaction or char pyrolysis of WHF
During this process, dewatering and charring reactions wer
production. As the dewatering and decarboxylization continued, water and carbon dioxides were
released, thus producing double bonds, carboxyl and carbonyl products. The carbon content
became higher as the decomposition
is common during the pyrolysis process of cellulosic fibres
As presented in Figure 5, the TG curves for all treated WHF samples indicated that the mass loss
started at a lower temperature (shift of about 20
the case of WHF-NaOH sample, the mass loss started at 200°C, reached the maximum mass loss
rate at the temperature of 360°C and completed dehydration of cellulose accounted 63% at
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
hemicellulose was firstly degraded due to the cellular breakdown and then followed by the
cellulose which degraded at higher temperature because it was highly crystalline [33, 34]
rolysis product of cellulosic were produced in this stage and that included L-Glucose as the
major product and combustible gases [19].
(a) TG and (b) DTG curves of untreated and treated WHF samples
Temperature at maximum mass loss rate and char yield at 800°C of all WHF samples
The charring reaction or char pyrolysis of WHF-UT tended to be completed above 400 °C.
During this process, dewatering and charring reactions were more dominant than of the L
production. As the dewatering and decarboxylization continued, water and carbon dioxides were
released, thus producing double bonds, carboxyl and carbonyl products. The carbon content
became higher as the decomposition continued thus forming charred residues. This circumstance
is common during the pyrolysis process of cellulosic fibres [18].
, the TG curves for all treated WHF samples indicated that the mass loss
(shift of about 20 – 80°C) in comparison with untreated WHF. In
NaOH sample, the mass loss started at 200°C, reached the maximum mass loss
rate at the temperature of 360°C and completed dehydration of cellulose accounted 63% at
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
13
hemicellulose was firstly degraded due to the cellular breakdown and then followed by the
[33, 34]. Most of
Glucose as the
Temperature at maximum mass loss rate and char yield at 800°C of all WHF samples
UT tended to be completed above 400 °C.
e more dominant than of the L-glucose
production. As the dewatering and decarboxylization continued, water and carbon dioxides were
released, thus producing double bonds, carboxyl and carbonyl products. The carbon content
continued thus forming charred residues. This circumstance
, the TG curves for all treated WHF samples indicated that the mass loss
80°C) in comparison with untreated WHF. In
NaOH sample, the mass loss started at 200°C, reached the maximum mass loss
rate at the temperature of 360°C and completed dehydration of cellulose accounted 63% at
14. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
14
360°C. This was lower than the mass loss temperature of the untreated sample (which exceeded
the limits) suggesting that cellulose oxidation proceeded under this circumstance and then
accompanied by the thermal dehydration of cellulose.
According to Mostashari, et al. [15], NaOH plays the role of ‘dust or wall’ which causes heat
absorption and dissipation at combustion zone (the zone after char pyrolysis), and consequently if
the concentration of NaOH is high enough (in this case, chemical pickup is high), no flame can
propagate. This is because NaOH is highly stable at elevated temperatures and does not
decompose on heating [35]. Hence, for the case of WHF-NaOH sample, NaOH which remains
intact with hemp fibres absorbs and dissipates the heat thus lowering the temperature and
extinguishing out the flame.
Another aspect that should be taken into account is, several flame retardants generate inert gasses
such as CO2, SO2, H2O, NH3, etc. during thermal decomposition. The environment in the area of
inflamed substrate could be diluted by the inert gasses and this situation complicates fuel gas such
as oxygen access into the flammable volatiles of combustion product [12]. This situation creates
flame retardancy and this mechanism is also known as ‘gas dilution theory’ [36]. With respect to
WHF-NaOH, the incorporation of NaOH in hemp fibre allows it to expel water vapour (acts
similarly to inert gas) under burning condition. Therefore, forming of water vapour can absorb a
lot of heat in combustion and this treatment could act as a dehydrating flame retardant agent.
The TGA curves for WHF-FR and WHF-NaOH+FR samples indicate weight loss starting at
almost the same temperature of about 140°C, and this is much earlier namely 80°C and 60°C than
WHF-UT and WHF-NaOH respectively. The maximum mass loss temperatures for both samples
are given in Table 7 at the temperatures of 273°C and 278°C, then finished at about 285 to 310°C
for WHF-FR and WHF-NaOH+FR respectively. It shows that, the main pyrolysis stage for WHF-
FR and WHF-NaOH+FR were commenced and finished earlier than the other two samples. This
was due to ammonium polyphosphate which promotes dephosphorylation and acid-catalyzed
dehydration of samples catalysed by the nitrogen [37, 38]. This was further supported by the
accompanying higher weight loss (~10%) compared to untreated WHF (~ 6%) for temperature up
to 140°C the TG curves. Thus, the incorporation of fire retardant chemical (ammonium
polyphosphate) and combination of NaOH and fire retardant chemical promotes cellulose
dehydration at higher degree than the sample treated with NaOH alone. The char reaction phase
for both WHF-FR and WHF-NaOH+FR samples also occurred earlier than other two samples,
which started at about 285 and 310 °C respectively, and their mass loss also became much slower.
This is because phosphorus in a sample affects the composition of intermediate chars in the
second stage during thermal degradation, slowing down the reaction of the already decomposed
residue [38].
3.5. Limiting Oxygen Index Results
The LOI measurement test is widely used to evaluate the flammability of materials. It shows the
minimum amount of oxygen in oxygen–nitrogen mixture required to support complete
combustion of a vertically held sample that burns downward from the top. The higher the LOI
value, the more effective the flame-retardant treatment [38, 39]. There are no indications stated in
ASTM: D2683 about the level of fire retardant bases on the LOI value. However, according to
Kamath, et al. [9] LOI value more than 28 is generally classified as fire retardant. In accordance
with GB50222-1995 standard method, 1) value of < 21 indicates the material is flammable; 2)
value of ≥ 24 and < 27 indicates the material is combustible, and; 3) value of ≥ 28 indicates the
material is fire retardant. The results of LOI as shown in Table 8 explain the fire-retardant
phenomenon discussed in Section 3.3.
The LOI value for WHF-UT is comparable with the untreated hemp fabric tested by Xu, et al.
[38]. Since the value is lower than the 21, thus the hemp fabric is classified as flammable
15. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
material. That is why untreated hemp was completely burnt and left very minimal residue in the
burning test. Treatment with NaOH on the hemp fabric increased the LOI value to 24 an
clustered under combustible material. When the WHF
test, the ignition of fire produced yellow flame. Even though the flame could be self
smoulder was produced and kept burning char residue (refer
burnt by the exaggeration of other fire sources.
The LOI value for the WHF-FR sample was more than 28, thus this sample is clustered as fire
retardant. During the burning test, there was no ignition or smoulder p
formation of char was noticed. In
compound possessed LOI value of 27 and this figure is just enough to be fire retardant. However,
with the addition of phosphorus percentage an
boron in the formulation, they managed to increase the LOI value of treated hemp fabric up to 41.
Therefore, it can be assumed that either the ammonium polyphosphate content is high or the other
chemical compound exist in the fire retardant chemical which attributed to the highest LOI value
to the WHF in this work. In the case of WHF
content leads to the decrement of LOI value. However, under the burning test, t
characteristics were physically similar with the WHF
Table
3.6. Effect of Chemical Treatment on the Mechanical Properties
The study on the behaviour of WHF can be clustered into three phases. The first phase is the
initial region, demonstrated by a curve with a low slope, the second phase is the linear region of
the curve, which rises steeply until its summit is reached and t
reaches the peak [16, 26].
Figure 6. Typical tensile stress
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March
material. That is why untreated hemp was completely burnt and left very minimal residue in the
burning test. Treatment with NaOH on the hemp fabric increased the LOI value to 24 an
clustered under combustible material. When the WHF-NaOH sample was subjected to burning
test, the ignition of fire produced yellow flame. Even though the flame could be self-
smoulder was produced and kept burning char residue (refer Section 3.3). This fabric can still be
burnt by the exaggeration of other fire sources.
FR sample was more than 28, thus this sample is clustered as fire
retardant. During the burning test, there was no ignition or smoulder produced but the rapid
formation of char was noticed. In Xu, et al. [38], hemp fabric treated with phosphorus only
compound possessed LOI value of 27 and this figure is just enough to be fire retardant. However,
with the addition of phosphorus percentage and other compound such as nitrogen, halogen and
boron in the formulation, they managed to increase the LOI value of treated hemp fabric up to 41.
Therefore, it can be assumed that either the ammonium polyphosphate content is high or the other
und exist in the fire retardant chemical which attributed to the highest LOI value
to the WHF in this work. In the case of WHF-NaOH+FR, there is high probability that the NaOH
content leads to the decrement of LOI value. However, under the burning test, t
characteristics were physically similar with the WHF-FR sample.
Table 8. LOI results of all WHF samples
Effect of Chemical Treatment on the Mechanical Properties
The study on the behaviour of WHF can be clustered into three phases. The first phase is the
initial region, demonstrated by a curve with a low slope, the second phase is the linear region of
the curve, which rises steeply until its summit is reached and the third phase is the curve after it
Typical tensile stress-strain response for, (a) warp and (b) weft of all WHF samples
Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
15
material. That is why untreated hemp was completely burnt and left very minimal residue in the
burning test. Treatment with NaOH on the hemp fabric increased the LOI value to 24 and this is
NaOH sample was subjected to burning
-extinguished,
). This fabric can still be
FR sample was more than 28, thus this sample is clustered as fire
roduced but the rapid
, hemp fabric treated with phosphorus only
compound possessed LOI value of 27 and this figure is just enough to be fire retardant. However,
d other compound such as nitrogen, halogen and
boron in the formulation, they managed to increase the LOI value of treated hemp fabric up to 41.
Therefore, it can be assumed that either the ammonium polyphosphate content is high or the other
und exist in the fire retardant chemical which attributed to the highest LOI value
NaOH+FR, there is high probability that the NaOH
content leads to the decrement of LOI value. However, under the burning test, the burning
The study on the behaviour of WHF can be clustered into three phases. The first phase is the
initial region, demonstrated by a curve with a low slope, the second phase is the linear region of
he third phase is the curve after it
strain response for, (a) warp and (b) weft of all WHF samples
16. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
16
Table 9. Summary of tensile properties for all WHF samples
Figures in bracket indicate standard deviation
Figure 6 shows the typical tensile stress–strain response for all the WHF samples. Each sample
were cut and tested in the warp and weft direction. Table 9 summarizes the average tensile
properties for each WHF samples. The tensile properties reported are the average and standard
deviation from all the specimens.
For the warp direction (Figure 6(a)), every WHF sample possessed different curves due to the
variation in the strain percentage. The strain percentages were varied due to the chemical
treatments applied on each WHF sample which affected their yarn crimp (originally 6% as shown
in Table 1) and disclosed as fabric shrinkage percentage (as shown in Table 2). When the
treatments were applied on the WHF samples, the fibres were swollen and as a consequence, the
whole fabric system experienced shrinkages and this was discussed in detail in Section 3.2. Based
on Table 2, in the warp direction, the WHF-NaOH sample exhibited the highest fabric shrinkage,
followed by WHF-NaOH+FR and the lowest was possessed by WHF-FR. For the sample with
higher fabric shrinkage, it took more time for the yarn to be straightened thus affected the overall
strain percentage (Table 9) of each sample.
In terms of tensile strength, the highest was possessed by the WHF-UT sample and then
decreased by the chemical treatment applied on them. In the case of WHF-NaOH, NaOH
removed hemicellulose and lignin partially from the fibres resulting in easy deformations of
cellulose microfibrils during tensile loading. The presence of hemicellulose and lignin held the
mircrofibrils in position and resisted slippage when subjected to tensile loading. Thus the losses
of some hemicellulose and lignin in fibre weakened the bonding of microfibrils thus resulted in
lower tensile properties as compared to untreated fibres [40, 41]. For the WHF-FR sample, there
is high possibility that some amount of cellulose in the hemp fibre was hydrolysed during the fire
retardant treatment which caused minor degradation then resulting to the decrease in it strength
[11, 29, 42]. This is because the ammonium polyphosphate compound in fire retardant is an
inorganic salt of polyphosphoric acid and it might be dissolved or hydrolysed in acid solution [43,
44]. In the case of WHF-NaOH+FR, since the fabric was firstly treated with NaOH, the strength
was reduced due to the reason discussed above. It was then further decreased a bit due to the FR
treatment but since the fibres was already deposited by NaOH, the FR (ammonium
polyphosphate) reacted majorly with NaOH to produce salt. Therefore, tensile strength of WHF-
NaOH+FR was a bit higher than WHF-FR.
Treatment with NaOH (WHF-NaOH) decreases the tensile modulus due to the elimination of
some hemicellulose and lignin because other than tensile strength, the stiffness of the hemp fibre
17. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
17
is depended on these two compounds [46]. It was worse when the WHF was treated with FR
chemical (WHF-FR) due to the hydrolisation of some cellulose compound. In the case of WHF-
NaOH+FR, higher tensile strength was achieved but possessed lower tensile modulus than WHF-
FR. Since the WHF was firstly treated with NaOH and consecutively with the FR chemical, most
probably FR chemical was responsible for the further elimination of hemicellulose and lignin thus
decreased the tensile modulus of WHF-NaOH+FR sample.
In terms of the weft direction, all mechanical properties shown in Table 9 followed the similar
trend with warp direction except for the tensile strain. The original yarn crimp for weft yarn was
longer (9.3%) than warp (6%) (refer Table 2). It is normal for weft yarn to have a higher yarn
crimp than warp yarn due to the tension arrangement during the process of weaving [16, 26, 43].
After the treatments, all treated samples in weft direction WHF shrunk but the shrinkage
percentages were lower than warp direction. This is due to the higher density of fabric in warp
direction which prevents the weft yarn to shrink further. As a consequence, the built-up pressure
in the weft is getting higher and this is the reason why the tensile strength and modulus of weft
yarn were higher than warp yarn tension. Thus, higher load is needed to overcome the weft yarns'
built-up pressure apart from its higher yarn size (refer Table 1).
4. CONCLUSIONS
Impregnation of NaOH, FR chemical and combination of both demonstrated an improvement in
flame retardant properties of woven hemp fabric. The detailed analyses on the treated woven
hemp fabrics showed several findings which are important for this material to be used not only in
textile and apparel but also in technical and engineering fields. The treatments really affect the
physical properties of the woven hemp fabric. The densities increased from 1.47 to 1.53 g/cm3
depending on the treatments. The fabric also shrunk within the range of 1.67 to 5% and 0.67 to
3% for warp and weft, respectively. The changes are attributed to the changing of physical
properties of woven hemp fibre. The fibre cross-section changed from elliptical to more rounder
and clean surface by NaOH, deposition of particle by FR on the fibre surfaces and salt deposition
by the combination of NaOH and FR treatments.
In this work, a method of measuring burning rate on the fire-retardant sample was established.
Using this method, it was proven that the treated WHF showed good results against the fire.
Nevertheless, WHF treated with FR and combination between NaOH and FR were found to be
better than the NaOH treatment. In terms of thermogravimetric analyses, impregnation of
treatments improved the onset of WHF main pyrolysis from 220 °C to much earlier which is 140
°C. The earlier pyrolysis indicated faster cellulose dehydration and promoted char formation. The
char yield at 800 °C showed that the treatment with the combination of NaOH and FR chemical
could produce good char residue which was 40%. In terms of LOI, the sample treated with FR
chemical showed the highest value (51) among all other samples suggesting that this is fire
retardant material and followed by sample treated with NaOH and FR (49.4). The sample treated
with only NaOH is clustered under combustible because its LOI was lower than 27. In terms of
tensile properties, the treatment reduces the strength of WHF for all tensile parameters ranging
from 18 to 32% and 23 to 39% for warp and weft respectively. All the treatments significantly
improved the fire retardant properties of woven hemp fabric however the mechanical properties
were reduced.
ACKNOWLEDGEMENTS
The authors would like to thank the Ministry of Higher Education, Malaysia and Universiti
Teknologi MARA, Malaysia for providing the scholarship to the first author on doing this work.
18. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
18
REFERENCES
[1] T. M. Kotresh, R. Indushekar, M. S. Subbulakshmi, S. N. Vijayalakshmi, A. S. K. Prasad, and A. K.
Agrawal, "Evaluation of Commercial Flame Retardant Polyester Curtain Fabrics in the Cone
Calorimeter," Journal of Industrial Textiles, vol. 36, no. 1, pp. 47-58, July 1, 2006 2006.
[2] P. Bajaj, "Heat and Flame Protection," in Handbook of Technical Textile, A. R. Horrocks and S. C.
Anand, Eds. North and South America: Woodhead Publishing Limited & The Textile Institute, 2000,
pp. 223-263.
[3] S. J. Kadolph, Textiles, 10th ed. ed. Upper Saddle River, N.J.: Pearson Prentice Hall, 2007.
[4] D. B. Dittenber and H. V. S. GangaRao, "Critical review of recent publications on use of natural
composites in infrastructure," Composites Part A: Applied Science and Manufacturing, vol. 43, no. 8,
pp. 1419-1429, 8// 2012.
[5] O. Faruk, A. K. Bledzki, H.-P. Fink, and M. Sain, "Biocomposites reinforced with natural fibers:
2000–2010," Progress in Polymer Science, vol. 37, no. 11, pp. 1552-1596, 11// 2012.
[6] A. Maslinda, M. A. Majid, M. Ridzuan, M. Afendi, and A. Gibson, "Effect of water absorption on the
mechanical properties of hybrid interwoven cellulosic-cellulosic fibre reinforced epoxy composites,"
Composite Structures, vol. 167, pp. 227-237, 2017.
[7] M. I. Misnon, M. M. Islam, J. A. Epaarachchi, and K.-t. Lau, "Selection of hemp fabric as
reinforcement in composite materials," in Proceedings of the 3rd International Conference on
Mechanical, Industrial and Energy Engineering (ICMIEE 2014), 2014, pp. 1-5: Khulna University of
Engineering & Technology.
[8] H. Hargitai, I. Rácz, and R. D. Anandjiwala, "Development of HEMP Fiber Reinforced
Polypropylene Composites," Journal of Thermoplastic Composite Materials, vol. 21, no. 2, pp. 165-
174, March 1, 2008 2008.
[9] M. G. Kamath, G. S. Bhat, D. V. Parikh, and B. D. Condon, "Processing and Characterization of
Flame Retardant Cotton Blend Nonwovens for Soft Furnishings to Meet Federal Flammability
Standards," Journal of Industrial Textiles, vol. 38, no. 3, pp. 251-262, January 1, 2009 2009.
[10] W. Wu and C. Q. Yang, "Comparison of different reactive organophosphorus flame retardant agents
for cotton. Part II: Fabric flame resistant performance and physical properties," Polymer Degradation
and Stability, vol. 92, no. 3, pp. 363-369, 3// 2007.
[11] A. R. Horrocks, "Flame retardant challenges for textiles and fibres: New chemistry versus innovatory
solutions," Polymer Degradation and Stability, vol. 96, no. 3, pp. 377-392, 3// 2011.
[12] R. Uppal, G. Bhat, K. Akato, D. V. Parikh, S. Nam, and B. Condon, "Flame retardant antibacterial
cotton high-loft nonwoven fabrics," Journal of Industrial Textiles, vol. 41, no. 4, pp. 281-291, April 1,
2012 2012.
[13] F. Shafizadeh, P. S. Chin, and W. F. DeGroot, "Mechanistic Evaluation of Flame Retardants," Fire
Retardant Chemistry, vol. 2, pp. 195-203, 1975.
[14] Y. Chen, A. Frendi, S. S. Tewari, and M. Sibulkin, "Effects of fire retardant addition on the
combustion properties of a charring fuel," Fire Safety Sciences, vol. 3, pp. 527-536, 1991.
[15] S. M. Mostashari, Y. K. Nia, and F. Fayyaz, "Thermogravimetry of deposited caustic soda used as a
flame-retardant for cotton fabric," (in English), Journal of Thermal Analysis and Calorimetry, vol. 91,
no. 1, pp. 237-241, 2008/01/01 2008.
[16] M. I. Misnon, M. M. Islam, J. A. Epaarachchi, and K. T. Lau, "Analyses of woven hemp fabric
characteristics for composite reinforcement," Materials & Design, vol. 66, Part A, no. 0, pp. 82-92,
2/5/ 2015.
[17] X. Chen and G. A. V. Leaf, "Engineering Design of Woven Fabrics for Specific Properties," Textile
Research Journal, vol. 70, no. 5, pp. 437-442, May 1, 2000 2000.
[18] P. Zhu, S. Sui, B. Wang, K. Sun, and G. Sun, "A study of pyrolysis and pyrolysis products of flame-
retardant cotton fabrics by DSC, TGA, and PY–GC–MS," Journal of Analytical and Applied
Pyrolysis, vol. 71, no. 2, pp. 645-655, 6// 2004.
19. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
19
[19] G. Brancatelli, C. Colleoni, M. R. Massafra, and G. Rosace, "Effect of hybrid phosphorus-doped
silica thin films produced by sol-gel method on the thermal behavior of cotton fabrics," Polymer
Degradation and Stability, vol. 96, no. 4, pp. 483-490, 4// 2011.
[20] M. Försth, H. Modin, and B. Sundström, "A comparative study of test methods for assessment of fire
safety performance of bus interior materials," Fire and Materials, vol. 37, no. 5, pp. 350-357, 2013.
[21] R. M. Rossi, G. Bruggmann, and R. Stämpfli, "Comparison of flame spread of textiles and burn injury
prediction with a manikin," Fire and Materials, vol. 29, no. 6, pp. 395-406, 2005.
[22] S. F. Grgac, B. Lozo, and D. Banić, "Flame retardancy of paper obtained with environmentally
friendly agents," Fibres & Textiles in Eastern Europe, vol. 17, no. 3, p. 74, 2009.
[23] A. Cireli et al., "Development of flame retardancy properties of new halogen-free phosphorous doped
SiO2 thin films on fabrics," Journal of Applied Polymer Science, vol. 105, no. 6, pp. 3748-3756,
2007.
[24] M. F. Yahya, J. Salleh, and W. Y. W. Ahmad, "Uniaxial failure resistance of square-isotropic 3D
woven fabric modelled with finite element analysis," in Business, Engineering and Industrial
Applications (ISBEIA), 2011 IEEE Symposium on, 2011, pp. 16-21.
[25] X. Huang and A. Netravali, "Characterization of flax fiber reinforced soy protein resin based green
composites modified with nano-clay particles," Composites Science and Technology, vol. 67, no. 10,
pp. 2005-2014, 8// 2007.
[26] J. Hu, Structure and mechanics of woven fabrics. North America: Published by Woodhead Publishing
Limited in association with The Textile Institute, Woodhead Publishing Ltd, 2004.
[27] P. Zugenmaier, "Cellulose," Crystalline Cellulose and Derivatives: Characterization and Structures,
pp. 101-174, 2008.
[28] B. Madsen, P. Hoffmeyer, A. B. Thomsen, and H. Lilholt, "Hemp yarn reinforced composites – I.
Yarn characteristics," Composites Part A: Applied Science and Manufacturing, vol. 38, no. 10, pp.
2194-2203, 10// 2007.
[29] Y. L. Lam, C. W. Kan, and C. W. M. Yuen, "Flame-retardant finishing in cotton fabrics using zinc
oxide co-catalyst," Journal of Applied Polymer Science, vol. 121, no. 1, pp. 612-621, 2011.
[30] J. Alongi, F. Carosio, and G. Malucelli, "Influence of ammonium polyphosphate-/poly(acrylic acid)-
based layer by layer architectures on the char formation in cotton, polyester and their blends,"
Polymer Degradation and Stability, vol. 97, no. 9, pp. 1644-1653, 9// 2012.
[31] C. E. Anderson, D. E. Ketchum, and W. P. Mountain, "Thermal conductivity of intumescent chars,"
Journal of Fire Sciences, vol. 6, no. 6, pp. 390-410, 1988.
[32] G. Camino, L. Costa, E. Casorati, G. Bertelli, and R. Locatelli, "The oxygen index method in fire
retardance studies of polymeric materials," Journal of Applied Polymer Science, vol. 35, no. 7, pp.
1863-1876, 1988.
[33] M. R. Ishak, S. M. Sapuan, Z. Leman, M. Z. A. Rahman, and U. M. K. Anwar, "Characterization of
sugar palm (Arenga pinnata) fibres," (in English), Journal of Thermal Analysis and Calorimetry, vol.
109, no. 2, pp. 981-989, 2012/08/01 2012.
[34] H. Yang, R. Yan, H. Chen, D. H. Lee, and C. Zheng, "Characteristics of hemicellulose, cellulose and
lignin pyrolysis," Fuel, vol. 86, no. 12–13, pp. 1781-1788, 8// 2007.
[35] A. K. De, A text book of inorganic chemistry. New Age International, 2007.
[36] J. H. Troitzsch, "Overview of flame retardants," Chemistry today, vol. 16, 1998.
[37] B. Kandola, A. Horrocks, D. Price, and G. Coleman, "Flame-retardant treatments of cellulose and
their influence on the mechanism of cellulose pyrolysis," Journal of Macromolecular Science, Part C:
Polymer Reviews, vol. 36, no. 4, pp. 721-794, 1996.
[38] J. Z. Xu et al., "Study on the Thermal Degradation of Cellulosic Fibers Treated with Flame
Retardants," Journal of Fire Sciences, vol. 20, no. 3, pp. 227-235, May 1, 2002 2002.
20. Advances in Materials Science and Engineering: An International Journal (MSEJ), Vol. 5, No. 1, March 2018
20
[39] F. Shukor, A. Hassan, M. Saiful Islam, M. Mokhtar, and M. Hasan, "Effect of ammonium
polyphosphate on flame retardancy, thermal stability and mechanical properties of alkali treated kenaf
fiber filled PLA biocomposites," Materials & Design, vol. 54, pp. 425-429, 2// 2014.
[40] M. M. Kabir, H. Wang, K. T. Lau, and F. Cardona, "Effects of chemical treatments on hemp fibre
structure," Applied Surface Science, vol. 276, no. 0, pp. 13-23, 7/1/ 2013.
[41] B. Madsen, P. Hoffmeyer, and H. Lilholt, "Hemp yarn reinforced composites – II. Tensile properties,"
Composites Part A: Applied Science and Manufacturing, vol. 38, no. 10, pp. 2204-2215, 10// 2007.
[42] C. Q. Yang, Weishu Wei, and G. C. Lickfield, "Mechanical Strength of Durable Press Finished
Cotton Fabric: Part III: Change in Cellulose Molecular Weight," Textile Research Journal, vol. 70, no.
10, pp. 910-915, October 1, 2000 2000.
[43] S. J. Kadolph and A. L. Langford, Textiles, 9th ed. New Jersey:: Prentice Hall, 2001.
[44] J. Zhang et al., "Dissolution of microcrystalline cellulose in phosphoric acid—Molecular changes and
kinetics," Molecules, vol. 14, no. 12, pp. 5027-5041, 2009.
[45] S. J. Christian and S. L. Billington, "Mechanical response of PHB- and cellulose acetate natural fiber-
reinforced composites for construction applications," Composites Part B: Engineering, vol. 42, no. 7,
pp. 1920-1928, 10// 2011.
[46] Z. N. Azwa, B. F. Yousif, A. C. Manalo, and W. Karunasena, "A review on the degradability of
polymeric composites based on natural fibres," Materials & Design, vol. 47, pp. 424-442, 5// 2013.
AUTHOR
Dr Md Mainul Islam is currently a Senior Lecturer in Mechanical Engineering at
University of Southern Queensland (USQ), Australia. He completed his PhD in
Mechanical Engineering with Polymeric Composite Materials major at the
University of Newcastle, Australia. He is a graduate and also former Assistant
Professor in Mechanical Engineering of Khulna University of Engineering &
Technology (KUET), previously known as BIT Khulna, Bangladesh. He got his
MEng degree in Structural Engineering with Fracture Mechanics major from
Kyushu University, Japan. His research interests are in the areas of fibre and
particulate composite materials especially for infrastructure and biomedical applications. He also belongs to
the Centre for Future Materials at USQ. He has over 100 research publications based on his area of
research. He serves as Editorial Board member for several renowned journals and as a Technical
Committee member for several international conferences.