Ch6 sheetmetw proc Erdi Karaçal Mechanical Engineer University of Gaziantep

02/11/14 CHAPTER 6 SHEET METAL
WORKING PROCESSES
1
CHAPTER 6
SHEET METAL WORKING PROCESSES
6.1 INTRODUCTION
ME 333 PRODUCTION PROCESSES II
Sheet metalworking includes cutting and forming operations performed on
relatively thin sheets of metal (0.4-6 mm).
The tooling used to perform sheet metalwork is called punch and die. Most sheet
metal operations are performed on machine tools called presses.
The term stamping press is used to distinguish these presses from forging and
extrusion presses. The sheet metal products are called stampings.
The commercial importance of sheet metalworking is significant.
The number of consumer and industrial products that include sheet metal parts:
automobile and truck bodies, airplanes, railway cars and locomotives, farm
and construction equipment, small and large appliances, office furniture,
computers and office equipment, and more. Sheet metal parts are generally
characterized by high strength, good dimensional tolerances, good surface finish,
and relatively low cost.

WORKING PROCESSES
2
Sheet-metal processing is usually performed at room temperatures (cold working).
The exemptions are when the stock is thick, the metal is brittle, or the deformation
is significant.
These are usually cases of warm working rather than hot working.

WORKING PROCESSES
3
The three major categories of sheet-metal processes:
(1)cutting (shearing, blanking, piercing)
(2)bending
(3)drawing.
Cutting is used to separate large sheets into smaller pieces, to cut out a part
perimeter, or to make holes in a part.
Bending and drawing are used to form sheet metal parts into their required
shapes.
Fig.6.1 Some cutting operations

WORKING PROCESSES
4
Classification of Sheet
Metalworking Processes
Fig.6.2 Basic sheet
metalworking
operations:
(a) bending,
(b) drawing, and
(c) shearing;
(1) as punch first
contacts sheet and
(2) after cutting.
Force and relative
motion are indicated
by F and v

WORKING PROCESSES
5
Classification of Sheet Metalworking Processes
Fig.6.2 Basic processes involved in forming sheet metal components. (a) Processes involving
local deformation.

WORKING PROCESSES
6
6.2. PIERCING AND BLANKING
A commonly used piercing-blanking die set and related terms are shown in the
following figure.
Fig.6.3 Components of a punch and die

WORKING PROCESSES
7
Blanking and punching
Blanking and punching are similar sheet metal cutting operations that involve
cutting the sheet metal along a closed outline.
If the part that is cut out is the desired product, the operation is called blanking and
the product is called blank.
If the remaining stock is the desired part, the operation is called punching. Both
operations are illustrated on the example of producing a washer:
Starting stock
produced by shearing
operation from a big
metal sheet
Fig.6.4 Steps
in production
of washer

Blanking punch diameter= Db-2c
Blanking die diameter= Db
WORKING PROCESSES
8
The cutting of metal between die components is a shearing process in which the
metal is stressed in shear between two cutting edges to the point of fracture, or
beyond its ultimate strength.
The metal is subjected to both tensile and compressive stresses; stretching beyond
the elastic limit occurs; then plastic deformation, reduction in area, and, finally,
fracturing starts and becomes complete.
Hole punch diameter= Dh
Hole die diameter= Dh+2c
Fig.6.5 Shearing of sheet metal
between punch and die

WORKING PROCESSES
9
The cutting of metal between die components is a shearing process in which the
metal is stressed in shear between two cutting edges to the point of fracture, or
beyond its ultimate strength. The metal is subjected to both tensile and
compressive stresses; stretching beyond the elastic limit occurs; then plastic
deformation, reduction in area, and, finally, fracturing starts and becomes complete.
Fig.6.5 Shearing of sheet metal between punch and die

Fig. 6.6. Shearing of sheet metal
between two cutting edges:
(1) just before the punch contacts
WORKING PROCESSES
10
Engineering analysis of metal cutting:
Cutting of sheet metal is accomplished by a shearing action between two sharp edges. The
shearing action is illustrated in the figure:
Fig.6.3 Shearing
work;
(2) punch begins to push into
work, causing plastic
deformation;
(3) punch compresses and
penetrates into work, causing
a smooth cut surface; and
(4) fracture is initiated at the
opposing cutting edges that
separate the sheet.
Symbols v and F indicate motion
and applied force, respectively.

WORKING PROCESSES
11
At the top of the cut surface is a region
called the rollover. This corresponds to
the depression made by the punch in the
work prior to cutting. It is where initial
plastic deformation occured in the work.
Just below the rollover is a relatively small
region called the burnish. This results
from penetration of the punch into the
work before fracture began.
Beneath the burnish is the fractured
zone, a relatively rough surface of the cut
edge where continued downward
movement of the punch caused fracture of
the metal.
Finally, at the bottom of the edge is a
burr, a sharp corner on the edge caused
by elongation of the metal during final
seperation of the two pieces.

Process parameters in sheet metal cutting are clearence between punch and die,
stock thickness, type of metal and its strength and length of the cut
Clearance c in a shearing operation is the space between the mating members of a
die set (e.g.punch and die).
For optimum finish of cut edge, proper clearance is necessary and is a function
of the kind, thickness, and hardness of the work material.
In an ideal cutting operation the punch penetrates the material to a depth equal to
about 1/3 of its thickness before fracture occurs, and forces an equal portion of
the material into the die opening.
Common die clearances (linear clearance) are 2-5% of the material thickness.
Angular clearance is gradient given to the hole in the die such that cut material will
easily be removed. Angular clearance is usually ground from 0.25⁰ to 1.5⁰ per side.
WORKING PROCESSES
12
6.2.1. Engineering Analysis_CLEARANCE

WORKING PROCESSES
13
The correct clearance depends on sheet-metal type and thickness t:
c = a*t
where a is the allowance (a = 0.075 for steels and 0.060 for aluminum alloys).
If the clearance is not set correctly, either an excessive force or an oversized burr
can occur:
Fig.6.7 Effect of clearance:
(Left) clearance too small
causes less than optimal
fracture and excessive forces,
and (Right) clearance too
large causes oversized burr.

WORKING PROCESSES
14
Figure (a) Effect of the clearance, c, between punch and die on the
deformation zone in shearing.
As the clearance increases, the material tends to be pulled into the die rather
than be sheared. In practice, clearances usually range between 2% and 10% of
the thickness of the sheet. (b) Microhardness (HV) contours for a 6.4-mm (0.25-
in) thick AISI 1020 hot-rolled steel in the sheared region.

WORKING PROCESSES
15
The calculated clearance value must be;
-substracted from the die punch diameter for blanking operations or
-added to die hole diameter for punching:
Fig.6.8
Die diameter is enlarged with clearance c in punching.
In blanking, the punch diameter is decreased to account for clearance.
D is the nominal size of the final product.

WORKING PROCESSES
16
An angular clearance must be provided for the die hole to allow parts to drop
through it:
Fig.6.9 Angular clearance
for the die opening in
punching and blanking.

P =pDtS
P =SLt
(for round holes)
(for any contours)
WORKING PROCESSES
17
6.2.2. CUTTING FORCE
The pressure (or stress) required to cut (shear) work material is;
For example to produce a hole of 20mmX20mm in a material 2mm in
thickness with 40 kg/mm2 shear strength:
P= 40 kg/mm2x(2x20+2x20)mmx2mm
P= 40x160 kg= 6400 kg force is required.
where;
S= shear strength of material, kg/mm2
D= hole diameter, mm
L= shear length, mm
t= material thickness, mm

Simple dies
WORKING PROCESSES
18
6.2.3 TOOLS AND DIES FOR CUTTING OPERATIONS
When the die is designed to perform a single operation (for example, cutting,
blanking, or punching) with each stroke of the press, it is referred to as a simple
die:
Fig.6.10 The basic components of the simple blanking and punching dies

Multi-operational dies
WORKING PROCESSES
19
More complicated pressworking dies include:
• compound die to perform two or more operations at a single position of the
metal strip
• progressive die to perform two or more operations at two or more positions of
the metal strip
Fig.6.11 Method of making a simple washer in a compound blanking and punching die

WORKING PROCESSES
20
Multi-operational dies
Schematic illustrations: (a) before and (b) after
blanking a common washer in a compound die.
Note the separate movements of the die (for
blanking) and the punch (for punching the hole in
the washer). (c) Schematic illustration of making a
washer in a progressive die. (d) Forming of the top
piece of an aerosol spray can in a progressive die.
Note that the part is attached to the strip until the
last operation is completed.

y = 2r
α 3
rSina
WORKING PROCESSES
21
6.2.4 CENTRE OF PRESSURE
Sheet metal part that to be blanked is of irregular shape the summation of
shearing forces on one side of the center of the ram may greatly exceed the
forces on the other side. This result in bending and undesirable deflections might
happen. Center of pressure is a point, which the summation of shearing forces
will be symmetrical. This point is the center of gravity of the line that is the
perimeter of the blank. It is not the center of gravity of the area.
p
x = y = 2r
p
a
x = a + b
y = h
3
Fig.6.14 Center of pressure for some shapes

å =
x l x l x l x
= + + +
lx
1 1 2 2 3 3
y l y l y l y
= + + +
1 1 2 2 3 3
WORKING PROCESSES
22
Procedure to find center of pressure:
1. Divide cutting edges into line elements, 1,2,3, ...
2. Find the lengths l1, l2, l3, ...
3. Find the center of gravity of each element as x1, x2, x3, ..., y1, y2, y3, ...
4. Calculate the center of pressure from:
å
+ + +
l
l l l
....
....
1 2 3
å =
ly
å
+ + +
l
l l l
....
....
1 2 3

Find the center of pressure and the required cutting force of the following blank
(S=40 kg/mm2 and t=2mm).
x . 189
y . 610
= 35 92 = = 115 98 =
. cm
WORKING PROCESSES
23
EXAMPLE
Element l X Y (l)(x) (l)(y)
1 4.00 0.00 6.25 0.00 25.00
2 4.71 1.50 9.20 7.05 43.33
3 3.20 4.00 7.00 12.80 22.40
4 2.50 4.00 5.00 10.00 12.50
5 3.00 1.50 4.25 4.50 12.75
6 1.57 1.00 0.00 1.57 0.00
TOTAL 18.98 35.92 115.98
. cm
.
18 98
.
18 98
and the cutting force is;
P= LtS 189.8mmx2mmx40kg/mm2 =15184 kg

Since cutting operations are characterized by very high forces exerted over very
short periods of time, it is some times desirable to reduce the force and spread it
over a longer portion of the ram stroke.
Two methods are frequently used to reduce cutting forces and to smooth out the
heavy loads.
WORKING PROCESSES
24
6.2.5 REDUCING CUTTING FORCES
1. Step the punch lengths; the load may thus be reduced approx. 50%.
2. Tapering the punch; grind the face of the punch or die at a small shear angle
with the horizontal. This has the effect of reducing the area in shear at any time,
and may reduce cutting force as much as 50%. The angle chosen should
provide a change in punch length of about 1.5 times of material thickness. It is
usually preferable to a double cut to prevent setup of lateral force components.
Fig.6.15 Different configurations
for reducing the cutting force

WORKING PROCESSES
25
Fig.6.– Effect of different clearances when punching hard and soft alloys

In designing parts to be blanked from strip material, economical strip utilization is of
high importance. The goal should be at least 75% utilization.
WORKING PROCESSES
26
6.3 SCRAP-STRIP LAYOUT FOR BLANKING
where;
t : thickness of the stock,
W: width of the stock,
B: space between part and edge (1.5t),
C: lead of the die (L+B),
L&H: dimensions of the work piece.

Util = Util
Scrap = Scrap % . . X100
WORKING PROCESSES
27
Locating the work piece for maximum economy is very important.
% X100
Total
Total

HOMEWORK:
WORKING PROCESSES
28
If two strips (250 mm and 125 mm width) are available for the production of Æ100
mm blanks, which one have to be preferred for maximum material utilization?

6.4 BENDING
WORKING PROCESSES
29
Bending is defined as the straining of the sheet metal around a straight edge:
Fig.6.15 Bending of sheet metal

WORKING PROCESSES
30
Bending operations involve the processes of V-bending and edge bending:
Fig.6.16 (Left) V-bending, and (Right) edge bending; (1) before and (2) after bending
•V-bending—sheet metal is bent along a straight line between a V-shape punch and die.
•Edge bending—bending of the cantilever part of the sheet around the die edge.

Bending is the process by which a straight length is transformed into a curved
length. It is a very common forming process for changing sheet and plate into
channel, tanks, etc.
For a given bending operation the bend radius can not be made smaller than a
certain value, otherwise the metal will crack on the outer tensile surface. Minimum
bend radius is usually expressed in multiples of the sheets thickness. It varies
considerable between different metal and always increases with cold working. Bend
radius is not less than 1 mm and for high strength sheet alloys the minimum bend
radius may be 5t or higher.
WORKING PROCESSES
31
R - bend radius
BA - bend allowance
a - bend angle
L0 - original length
t - sheet thickness
Lf > L0
Lf=L1+L2+BA Rmin>5t practical

where Lb is the length of the blank, L are
the lengths of the straight parts of the
blank, BA is the bend allowance,
WORKING PROCESSES
32
This is the stretching length that occurs
during bending. It must be accounted to
determine the length of the blank,
Fig.6.17 Calculation of bend allowance
where A is the bend angle; t is the sheet thickness;
R is the bend radius; Kba is a factor to estimate stretching,
defined as follows:
Kba = 0.33 for R < 2t
Kba = 0.50 for R ≥ 2t

min = 1 -
r t A
2
( 1
A )
r
A A
A A
r A
2
Springback ratio R t/
= f
= +
o
a
WORKING PROCESSES
33
The minimum bend radius for a given thickness of sheet can be predicted fairly
accurately from the reduction of area measured in tension test, Ar.
1
2
R
2
min
2
r r
t
R
-
= -
for Ar< 0.2,
for Ar> 0.2,
o f
o
A
-
=
Another common problem is springback. It is the dimensional change of the formed
part after pressure of the forming tool has been removed. It results from the change
in strain produced by elastic recovery.
2
R t/
f
o
+
a

WORKING PROCESSES
34
The commonest method of compensating for springback is to bend the part to a
smaller radius of curvature than is desired so that after springback the part has
the proper radius.
Springback is the elastic recovery leading to the increase of the included angle
when the bending pressure is removed.
To compensate for springback two methods are commonly used:
1. Overbending—the punch angle and radius are smaller than the final ones.
2. Bottoming—squeezing the part at the end of the stroke.
Fig.6.18 Springback in bending
Fig.6.19 Compensation of springback by:
(a) and (b) overbending; (c) and (d) bottoming

s 2 a
R t
P oLt
+
WORKING PROCESSES
35
The force required bending a length L about a radius R may be estimated from;
2
tan
2( /2)
=
Bending forces
The maximum bending force is estimated as
where Kbf is the constant that depends on the process, Kbf = 1.33 for V-bending
and Kbf = 0.33 for edge bending; w is the width of bending; D is the die opening
dimension as shown in the figure:
Fig.6.20 Die opening dimension D,
(a) V-bending, (b) edge bending

WORKING PROCESSES
36
Equipment for bending operations
Fig.6.21 Press brake with CNC gauging system Fig.6.22 Dies and stages in the press brake
forming of a roll bead

6.5 DEEP DRAWING (Derin Çekme)
WORKING PROCESSES
37
Deep drawing is the metal working
process used for shaping flat sheets
into cup-shaped articles such as
bathtubs, shell cases, and
automobile fenders. Generally a hold
down or pressure pad is required to
press the blank against the die to
prevent wrinkling. Optional pressure
pad from the bottom may also be
used.
Fig.6.23 Drawing of a cup shaped part

WORKING PROCESSES
38
Deep drawing of a cup-shaped part
Fig.6.24 Deep drawing of a cup-shaped part: (Left) start of the
operation before punch contacts blank, and (Right) end of stroke

WORKING PROCESSES
39
In the deep drawing of a cup the metal
is subjected to three different types of
deformations. In the flange part, as it is
drawn in, the outer circumference must
continuously decrease from that of the
original blank pDo to that of the finish
cup pDp. This means that it is
subjected to a compressive strain in the
hoop (tangential) direction and a tensile
strain in the radial direction. As a result
of these principal strains, there is a
continual increase in the thickness as
the metal moves inward. However, as
the metal pass over the die radius, it is
first bend and then straightened while
at the same time being subjected to a
tensile stress. This plastic bending
under tension results in considerable
thinning. Punch region is under very
little stress.
Fig.6.23 Types of deformations in different region
during deep drawing of a cup shaped part

Clearance
Clearance c is the distance between the punch and die and is about 10% greater
than the stock thickness:
WORKING PROCESSES
40
c = 1.1t
Holding force
The improper application of the holding force can cause severe defects in the
drawn parts such as (a) flange wrinkling or (b) wall wrinkling if the holding force is
too small, and (c) tearing if the folding force is overestimated.
Fig.6.25 Defects in deep drawing of a cup-shaped part

p 1.1s  h 2 hp 2 + /
WORKING PROCESSES
41
The force on the punch required to produce a cup is the summation of the ideal
force of deformation, the frictional forces, and the force required to produce
ironing. Mathematical calculation of the drawing force is very complex. Following
approximate equation is developed:
P dt( ) n D ( )
d
H d
D
e B o = + æè ç
öø ÷
é
ë ê
ù
û ú
where;
P = total punch load, so= average flow stress,
d = punch diameter, D = blank diameter,
H = hold drawn force, B = force required to bend,
t = wall thickness, m = coefficient of friction,
h = efficiency
Drawing force may be calculated for practical purposes by:
P dt o =s p when LDR » 2 (Limiting Drawing Ratio)

LDR D ö ÷ø
çè
» = + and D = (d 2 +4dh)
2 2
4 4
WORKING PROCESSES
42
The drawability of a metal is measured by the ratio of the blank diameter to the
diameter of the cup drawn from the blank (usually accepted as punch diameter). For
a given material there is a Limiting Drawing Ratio (LDR), representing the largest
blank that can be drawn through a die without tearing.
eh
d
» æ
Where, h is an efficiency term to account for frictional losses. If h=1, then LDR=2.7
while h=0.7, LDR»2 which is used in most practical applications.
Some of the practical considerations which affect drawability:
Rd» 10t
Rp» should be big enough to prevent tearing.
Clearance between punch and die; 20 to 40% greater than “t”.
Hold-down pressure; 2% of so and lubricate die walls
The diameter of blank required to draw a given cup may be obtained approximately
by equating surface areas.
where; h is height of cup.
pD pd pdh

6.5.1 REDRAWING
WORKING PROCESSES
43
If the shape change required by the part design is too severe (limiting drawing ratio is
too high, or LDR is not sufficient to form a desired cup), complete forming of the part
require more than one drawing step. The second drawing step and any further
drawing steps if needed, are referred to as redrawing. Throat angle is 10°-15°.
Redrawing is generally done in decreasing ratios as given below:
(D/d)= 1.43, 1.33, 1.25, 1.19, 1.14 and 1.11.
If these redrawing steps are not enough to reach required cup diameter, annealing
have to be performed and then redrawing can be performed.
Fig.6.26 Redrawing of a cup

6.5.2 EXAMPLE:
Draw 1st 2nd 3rd 4th 5th 6th
Ratio 1.43 1.33 1.25 1.19 1.14 1.10
Solution:
LDR=2 D/d = 200/50 = 4 > 2
So that redrawing is necessary.
1.43 200 1
D
1. 139.86
1.33 139.86 2
D
1 = ® D = =
D
1.25 105.16 3
2 = ® D = =
D
D
3 = ® D = =
D
1.14 70.69 5
4 = ® D = =
D
1.1 62.01 6
D
5 = ® D = =
D
WORKING PROCESSES
44
A Æ 200 mm blank is to be drawn to a 50 mm cup. Estimate the minimum number of
draws required using the drawing ratios given below:
56.38>50
1.43
1
= ® D = =
D
2. 105.16
1.33
2
3. 84.13
1.25
3
D
1.19 84.13 4
4. 70.69
1.19
4
5. 62.01
1.14
5
D
6. 56.38
1.1
6

84.13 = < 2
WORKING PROCESSES
45
Therefore annealing should be applied. But it might be better to anneal the blank
before 6th draw to reduce number of redraws. We know that LDR=2. So that if
annealing is performed after 3rd draw where D3 = 84.13 mm, than ratio to reach
required cup diameter is:
1.68
50
Therefore, after 3rd draw, blank is annealed and then redraw with a ratio of 1.68 to
obtain required cup diameter. The required number of drawing is then 4.

6.6 OTHER SHEET-METAL FORMING OPERATIONS
WORKING PROCESSES
46
The Guerin process involves the use of a thick rubber pad to form sheet metal
over a positive form block:
Fig.6.27 The Guerin process: (Left) start of the operation before
rubber pad contacts sheet, and (Right) end of stroke
The Guerin process

WORKING PROCESSES
47
Examples of equipment and products manufactured by the Guerin process:
Fig.6.28 Rubber pad press showing
forming tools on the press table
Fig.6.29 A large number of different components
can be made simultaneously during one press cycle
with rubber pad presses
Advantages: small cost of tooling
Limitations: for relatively shallow shapes
Area of application: small-quantity production

WORKING PROCESSES
48
It is similar to Guerin process but instead of rubber pad a rubber diaphragm
filled with fluid is used:
Fig.6.30 Hydroform process:
(1) start-up, no fluid in the cavity;
(2) press closed, cavity pressurized
with hydraulic fluid;
(3) punch pressed into work to form
part.
Symbols:
v - velocity,
F – applied force, and
p - hydraulic pressure
Hydroforming
Advantages: small cost of tooling
Limitations: simple shapes

Stretch forming
In stretch forming the sheet metal is stretched and bent to achieve the desired shape:
WORKING PROCESSES
49
FFiigg..66..3311 SSttrreettcchh ffoorrmmiinngg:: ((11)) ssttaarrtt ooff tthhee pprroocceessss;; ((22)) ffoorrmm ddiiee iiss pprreesssseedd iinnttoo tthhee wwoorrkk
ccaauussiinngg iitt ttoo ssttrreettcchheedd aanndd bbeenntt oovveerr tthhee ffoorrmm.. SSyymmbboollss:: vv - vveelloocciittyy,, FFddiiee - aapppplliieedd ffoorrccee
Advantages: small cost of tooling, large parts
Limitations: simple shapes

Spinning
Spinning is a metal forming process in which an axially symmetric part is gradually
shaped over a mandrel by means of a rounded tool or roller:
WORKING PROCESSES
50
FFiigg..66..3322 In spinning operation, flat circular blanks are often formed into hollow shapes such
as photographic reflectors. In a lathe, tool is forced against a rotating disk, gradually forcing
the metal over the chuck to conform to its shape. Chucks and follow blocks are usually
made of wood for this operation
Advantages: small cost of tooling, large parts (up to 5 m or more)
Limitations: only axially symmetric parts

HIGH-ENERGY-RATE FORMING (HERF)
These are metal forming processes in which large amount of energy is applied in a
very short time. Some of the most important HREF operations include:
Explosive forming
It involves the use of an explosive charge placed in water to form sheet into the die cavity.
WORKING PROCESSES
51
FFiigg..66..3333 Explosive forming: (1) set-up, (2) explosive is detonated, and (3) shock wave forms
part

Explosively formed elliptical dome 3-m in diameter being removed from
the forming die
WORKING PROCESSES
52
FFiigg..66..3344 Explosively formed
elliptical dome 3-m in diameter
being removed from the forming die
Advantages: small cost of tooling, large parts
Limitations: skilled and experienced labor
Area of application: large parts typical of the aerospace industry

Electrohydraulic forming
This is a HREF process in which a shock wave to deform the work into a die cavity is
generated by the discharge of electrical energy between two electrodes submerged in
water. Similar to explosive forming, but applied only to small part sizes.
WORKING PROCESSES
53
FFiigg..66..3355 Setup of electrohydraulic forming

Electromagnetic forming
The sheet metal is deformed by the mechanical force of an electromagnetic field
induced in the workpiece by a coil:
WORKING PROCESSES
54
FFiigg..66..3366 Electromagnetic
forming: (1) set-up in which
coil is inserted into tubular
workpiece surrounded by
die, (2) formed part
Advantages: can produce shapes, which cannot be
produced easily by the other processes
Limitations: suitable for magnetic materials
Area of application: most widely used HERF process to
form tubular parts

HOMEWORK:
WORKING PROCESSES
55
If two strips (250 mm and 125 mm width) are available for the production of Æ100
mm blanks, which one have to be preferred for maximum material utilization?

WORKING PROCESSES
56
THE END

WORKING PROCESSES
57

Ch6 sheetmetw proc Erdi Karaçal Mechanical Engineer University of Gaziantep

Recommended

Recommended

More Related Content

What's hot

What's hot (20)

Similar to Ch6 sheetmetw proc Erdi Karaçal Mechanical Engineer University of Gaziantep

Similar to Ch6 sheetmetw proc Erdi Karaçal Mechanical Engineer University of Gaziantep (20)

More from Erdi Karaçal

More from Erdi Karaçal (20)

Recently uploaded

Recently uploaded (20)

Ch6 sheetmetw proc Erdi Karaçal Mechanical Engineer University of Gaziantep