The versatility of Versacryl
•Download as PPTX, PDF•
2 likes•2,495 views
Replacing anterior teeth with a treatment provisional can be a esthetic nightmare if clasps are all you have for retention. Versacryl offers lingual clasping options for those situations where a facial clasp just wont cut it. For a virtually unbreakable provisional, try the vacuum formed surgical tray material as a frame option.
Recommended
Recommended
More Related Content
Viewers also liked
Viewers also liked (15)
More from Thomas Zaleske
More from Thomas Zaleske (12)
Recently uploaded
Recently uploaded (20)
The versatility of Versacryl
- 1. Versacryl A multiple use soft liner material www.matrixdentallab.com
- 2. Laboratory Kit Self cure or Heat cure Ratios softness adjusted by hard-soft liquid ratios www.matrixdentallab.com
- 3. Treatment Provisionals Two Styles www.matrixdentallab.com
- 4. Claspless treatment provisionals Vacuum Form surgical Self cure resin w/ tray w/ Versacryl Versacryl www.matrixdentallab.com
- 5. Conventional Self Cure Style Layered Versacryl for undercut retention and Diamond D self curing resin. www.matrixdentallab.com
- 6. Conventional Self Cure Style Decide where to place Versacryl. Soak model. www.matrixdentallab.com
- 7. hardener / softener liquids larger undercuts, more softness smaller undercuts, more hardener www.matrixdentallab.com
- 8. Dedicate pipettes, never use for any other monomers
- 9. Engage undercuts Versacryl should be the consistency of honey when adapted to cast in order to slightly run and fill inter- proximal areas. www.matrixdentallab.com
- 10. Engage undercuts Before it stiffens, wet fingers and lightly finger adapt and mold to model and into undercuts. www.matrixdentallab.com
- 11. Hard acrylic veneer Prime Versacryl with hardener liquid and sprinkle adapt Diamond D self curing repair resin or preference self cure resin. Make sure to cover Versacryl with an adequate thickness of self curing resin for strength
- 13. Cure Warm water bath 105-110f 20-25 psi for 20 minutes www.matrixdentallab.com
- 14. Final product Dual lamination effect, undercut retention www.matrixdentallab.com
- 15. Newer Version Thermal Formed Treatment Provisional
- 16. Duplicate master. Remove palatal area in preparation for thermoforming.
- 17. Before vacuum forming In order the increase the vacuum adaption take a lathe mounted fiber cutting disk and cut 1mm channels or grooves on the bottom of the model. This will allow vacuum to draw around the periphery of the model better. www.matrixdentallab.com
- 18. Thank Dan for that tip!
- 20. Vacuum adapt surgical tray material .100 or .120 (polyesther teraphalte) Available from Keystone Industries www.matrixdentallab.com
- 21. Gross trim and mark areas for shape and Versacryl adaption www.matrixdentallab.com
- 22. Scallop away areas where Versacryl will engage undercuts. www.matrixdentallab.com
- 23. The strength of the P.E.T. is throughout the appliance www.matrixdentallab.com
- 25. Preparing P.E.T frame to accept Versacryl www.matrixdentallab.com
- 26. The amount of free standing Versacryl will also effect the amount of rigidity. Always prime area accepting Versacryl with hardner liquid just before adapting Versacryl to frame. www.matrixdentallab.com
- 27. Select appropriate hardness www.matrixdentallab.com
- 29. Wet finger adapted www.matrixdentallab.com
- 30. Cure Warm water bath 105-110f 20-25 psi for 20 minutes www.matrixdentallab.com
- 31. Pumice and polish www.matrixdentallab.com
- 34. Questions or Sample 1-800-333-3131 Ask for Carl
- 35. Specialization in removable prosthet Fabrication, education, and consulti Thomas R Zaleske 219-310-8296 lab 630-531-8197 cell matrixdental@comcast.net www.matrixdentallab.com