2. PERMEABILIDADE AO OXIGÊNIO (DK)
• A FACILIDADE COM QUE O O2 PASSA ATRAVÉS
DE UM MATERIAL
• RELATIVO A CAPACIDADE DE DIFUSÃO DO
OXIGÊNIO (D)
– ‘VELOCIDADE DAS MOLÉCULAS NO
MATERIAL’
• ..E SOLUBILIDADE (K)
– ‘NÚMERO DE MOLÉCULAS NO MATERIAL’
• UNIDADES (CM2 MLO2)/(SEC ML MMHG)
4. TRANSMISSIBILIDADE AO OXYGÊNIO
(DK/T)
• LEVA EM CONTA A ESPESSURA DA LENTE
– ESPESSURA CENTRAL MÉDIA DE 6MM
– GERALMENTE NUMA LENTE DE -3.00di
• DK/T
– CHAMÁVAMOS DE DK/L
• PROPRIEDADE DA LENTE.
• UNIDADES (CM MLO2)/(SEC ML MMHG)
• 10-9 PARTE OFTEN DROPPED
5. 0
5
10
15
20
25
30
35
35 40 45 50 55 60 65 70 75
Water content at 35°C
Dk/t
For -3.00 lenses - will be different for other lens powers
Morgan & Efron, 1998
HIDROGÉIS: DK/T VS CONTEÚDO AQUOSO
6. PureVision
Bausch & Lomb
LENTES DE SILICONE HIDROGEL
1999
Night & Day
CIBA Vision
Acuvue Advance
Johnson & Johnson
O2 Optix
CIBA Vision
Acuvue Oasys
Johnson & Johnson
1999
2004
2004
2005
7. SILICONE HIDROGEL: DK VS CONTEÚDO AQUOSO
Dk DADOS DE EFRON E AL, 2005
DADOS SOBRE O CONTEÚDO AQUOSO FORNECIDO PELOS
FABRICANTES.
8. VS. PERMEABILIDADE AO OXIGÊNIO
For conventional lenses, Dk = 1.67e0.0397W (Morgan and Efron 1998)
Silicone hydrogels after Tighe 1999
0
20
40
60
80
100
120
140
160
0 10 20 30 40 50 60 70 80 90
Water content (%)
Dk
(barrer)
Silicone hydrogels
Conventional hydrogels
9. SIL.HI: DK VS. CONTEÚDO AQUOSO ,
DK VS. PERCENTAGEM DE O2
• CONTEÚDO AQUOSO E DK
0
100
200
10 20 30 40 50 60 70 80 90
Water Content
Dk
silicone hydrogel
hydrogel
(after WJ Benjamin, OD, PhD)
Holden,Mertz?
89
Harvitt, Bonano 87