13. Construction Varied flooring concepts are available on demand for different operational requirements and site conditions. Fibrex Construction Chemicals Pvt Ltd
15. Construction Fibrex Construction Chemicals Pvt Ltd Design Life Floors are designed as per the requirement of the industry. Operation Requirements Floor toppings are capable of withstanding static and dynamic loads. Traffic & Mechanical Wear Resistance to impact and abrasion.
16. Construction Fibrex Construction Chemicals Pvt Ltd Constructional Joints Joints of nominal movement such as construction and day work are catered for by flexible sealing and overcoating within the Fibfloor Programme. Floor to Wall Connection Coving is provided between horizontal and vertical surfaces such as floor to walls and around plinths.
17. Construction Fibrex Construction Chemicals Pvt Ltd Surface Design The surface design of the floor are as per the functional and subjective criteria.
18. Construction Fibrex Construction Chemicals Pvt Ltd Chemical Resistance Temperature Withstand extremes of temperature. Slip Resistance Different degrees of slip resistance can be designed into the floor to suit the specific area requirements.
19. Construction Rapid Curing The floors have rapid curing properties. Fibrex Construction Chemicals Pvt Ltd Impact Resistance / Point Loads Resistance to compressive load that are generated by the movement of goods on truck, pallets, etc. Hygiene Floor are totally dust free, without cracks or angled corners and easy cleanable.
21. Construction Fibrex Construction Chemicals Pvt Ltd Floor Coating on Green and Damp Concrete Cannot withstand,results in bubbles,delamination Conductive / Anti – static Special type floors are layed to prevent electrical interference with sensitive electronic equipment, or to avoid a build-up of static electricity.
24. Construction WHEN COATING CEMENTITIOUS SUBSTRATES WITH REACTIVE RESINS, THE SUBSTRATE MOISTURE CONTENT MUST NOT EXCEED 4%. THE CONSEQUENCES OF NON-COMPLIANCE OF THE ABOVE ARE COATING FAILURE AND FINANCIAL LOSS. THESE FAILURES ARE OFTEN TRIGGERED BY A PHENOMENON KNOWN AS “OSMOSIS”. Fibrex Construction Chemicals Pvt Ltd
25. Construction STAGES OF FAILURE PHASE I SINGLE OR MULTIPLE BUBBLES WITH DIAMETERS OF BETWEEN 0.5 CM AND 4CM IN THE COATING WITH A HARD, CURVED, CLOSED SURFACE. PHASE II CRACKED OR WORN BUBBLES WHICH SMELL UNPLEASANT INSIDE, PARTIAL DETACHMENT OF THE FLOORING FROM THE SUBSTRATE. PHASE III VOIDS, EXTENSIVE DELAMINATION OF THE FLOORING FROM THE SUBSTRATE. Fibrex Construction Chemicals Pvt Ltd
26. Construction FACTOR DETERMINE THE OSMOSIS EFFECT IN INDUSTRIAL FLOORING CONSTRUCTION WATER IN LIQUID STATE SOLUBLE SALTS SEM-IPERMEABLE MEMBRANE ALL THE ABOVE THREE CONDITIONS ARE PRESENT DURING INSTALLATION OF REACTIVE RESIN FLOORING ESPECIALLY ON CEMENTITIOUS SUBSTRATE WITH MOISTURE CONTENT ABOVE 4% LIMIT. Fibrex Construction Chemicals Pvt Ltd
27. Construction CONCRETE HUMIDITY NON DESTRUCTIVE TESTING OF MOISTURE OF CONCRETE CAN BE DONE BY USING ELECTRONIC MOISTURE METER. IN FRESH CONCRETE THE MOISTURE CONTENT OF CONCRETE SPECIFIES HOW MUCH WATER CAN THEORETICALLY STILL EVAPORATE. IN HARDENED CONCRETE THE MOISTURE OF CONCRETE RELATES TO THE AMOUNT OF WATER CONTAINED IN THE PORES AND CAPILLARIES. IN NORMAL RELATIVE HUMIDITY CONDITION THIS IS 2 – 4% BY WEIGHT. ADDITIOINAL MOISTURE ENTERS THE CONCRETE RISING THE MOISTURE CONTENT ABOVE 4%. Fibrex Construction Chemicals Pvt Ltd