Các hợp chất pin điện, galvani, chemical. Hóa lý

1. LOGO
WE ALWAYS THINK AN ENVIRONMENT VALUABLY
2012.12.20
PRODUCT INTRODUCTION
UNICOH SPECIALTY CHEMICALS Co., Ltd

2. Application of coating agent
We always think an environment valuably
1. Types of coating agent for Galvalume
1) Types of coating agent
Items Transparent Coating Color Coating
Containing Cr
Galva Cr ( Uni-Galva-2010A )
-
Galva Cr (Uni-Galva-2010B)
Non-Cr
Cr- Free (Uni-Galfree-2010A)
Unicoat-WAF-2008A
Unicoat-WAF-2008B
Cr- Free (Uni-Galfree-2010B)
Lubricant Galva(Uni-LGF-2010)

3. Application of coating agent
We always think an environment valuably
1. Types of coating agent for Galvalume
2) Transparent and color Type coating agents
Transparent type coating agent
Items
Galva Cr
(Uni-Galva-2010A)
Galva Cr
(Uni-Galva-2010B)
Cr- Free
(Uni-Galfree-2010A)
Cr- Free
(Uni-Galfree-2010B)
Main
ingredient
• Urethane Resin
• Emulsion Resin
• Urethane Resin
• Acrylic Resin
• Urethane Resin
• Special functional
additive
• Urethane Resin
• Acrlyic Resin
Uses
• Building interiors
or exteriors
• Electricity, electronic
appliances
• Automobile parts
• Drain pipe
• Building interiors
or exteriors
• Electricity, electronic
appliances
• Automobile parts
• Drain pipe
• Building interiors
or exteriors
• Electricity, electronic
appliances
• Automobile parts
• Electricity, electronic
appliances especially
need an electric
conductibility and
formability
Cr content 300mg / 100g 300mg / 100g Not contained Not contained

4. Application of coating agent
We always think an environment valuably
1. Types of coating agent for Galvalume
2) Transparent and color Type coating agents
Transparent type coating agent Color type coating agent
Items
Lubricant Galva
(Uni-LGF-2010)
Cr- Free
(UNICOAT-WAF-2008A)
Cr- Free
(UNICOAT-WAF-2008B)
Main ingredient
• Urethane Resin
• Emulsion Resin
• Acrylic Resin
• Urethane Resin
• Acrlyic Resin
• Mineral Pigment
• Urethane Resin
• Emulsion Resin
• Mineral Pigment
Uses
• Building interiors
or exteriors
• Electricity, electronic
appliances
• Use it need a high
workability & formability
• Building interiors
or exteriors
• Electricity, electronic
appliance
• Building interiors
or exteriors
• Electricity, electronic
appliance
Cr content Not contained Not contained Not contained

5. Application of coating agent
We always think an environment valuably
2. Galva Cr (Uni-Galva-2010A)
[ Product name ; Uni-Galva-2010A ]
• Building interiors or exteriors
• Electricity, electronic appliances
• Automobile parts
• Drain pipe
Corrosion Resistance
Q.U.V
Anti-Finger print
Workability & Formability
Chemical Resistance
High Humidity

6. Application of coating agent
We always think an environment valuably
2. Galva Cr (Uni-Galva-2010A)
1) Physical & chemical properties
[ Product name ; Uni-Galva-2010A ]
Main ingredient
• Urethane Resin
• Inorganic compound
• Phosphate
• Cr
Appearance Light yellow-green liquid
Specific Gravity (20oC) 1.03 ± 0.005
p H 8.5 ± 1.0
Viscosity 15±2 sec (#4 Ford Viscosity Cup)
Cr - Content 300mg / 100g
1) Korea Testing & Research Institute for Chemical Industry (TAK-018967)

7. Application of coating agent
We always think an environment valuably
2. Galva Cr (Uni-Galva-2010A)
2) Properties Evaluation Method
Items Evaluation method
Corrosion
Resistance
(SST)
Plane ▪ KS D 9502, Edge Tape Sealing: 240 Hr – Below 5%
Bending(4t) ▪ KS D 9502, 4t Bending area - 50 Hr - – Below 5%
Erichsen(4mm) ▪ KS D 9502, 4mm - 50Hr - – Below 5%
High temperature and humidity test
▪ High temperature and high humidity test: 60℃, 95%H, 120Hr E<2
 E = SQRT [ L2
+  a2
+  b2
]
QUV ▪ ASTM G-53, 1, 000Hr – Check b value out of L, a, b measured by colorimeter ,△ b < 1
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (2min)
acid resistance ▪ 5% HCl, dropping check (20min)
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test – No peeling off
Erichsen ▪ CCET – 1mm / 6mm and tapping test – No peeling off
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E<2
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E<2
Anti-finger print ▪ Measure an external appearance after painting vaseline ,  E<2

8. Application of coating agent
We always think an environment valuably
2. Galva Cr (Uni-Galva-2010A)
3) Properties Evaluation
Items Evaluation Spec’ Galva Clean
Corrosion
Resistance
(SST)
Plane ▪ 5% NaCl SST – 240Hr Excellent ( No defect )
Bending(4t) ▪ 5% NaCl SST – 50Hr Excellent ( No defect )
Erichsen(4mm) ▪ 5% NaCl SST – 50Hr Excellent ( No defect )
High temperature and humidity test ▪ 600
C, 95%H, 120Hr ,  E < 2 OK ( E = 0.79 )
QUV ▪ ASTM G-53, 1, 000Hr ,  b < 1 OK ( B = 0.54 )
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (2min) OK
acid resistance ▪ 5% HCl, dropping check (20min) OK
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test OK ( No peeling off )
Erichsen ▪ CCET – 1mm / 6mm and tapping test OK ( No peeling off )
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E < 2 OK ( E = 0.38 )
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E < 2 OK ( E = 0.56 )
Anti-finger print ▪ painting vaseline ,  E<2 OK ( E = 1.23 )

9. Application of coating agent
We always think an environment valuably
2. Galva Clean 1 (Uni-Galva-2010A)
4) Properties Evaluation
Corrosion Resistance
(Plain - SST 240Hr)
Corrosion Resistance
(4 - T Bend - SST 50Hr)
Corrosion Resistance
(4mm -Erichsen - SST 50Hr)
temperature and humidity
(600C , 95%H, 120Hr)
Alkali and Acid resistance
(5% NaOH, 5% HCl)
T-Bending
(0T-Bending and tapping test)
Erichsen
(1mm / 6mm and tapping test)
Solvent Resistance
(MEK, Ethanol)
△E = 0.79
alkali resistance
acid resistance
5% NaOH (2min)
5% HCl (20min)
MEK
Ethanol
 E = 0.38
 E = 0.56
( No defect ) ( No defect ) ( No defect )
( No peeling off )
( No peeling off )

10. Application of coating agent
We always think an environment valuably
3. Galva Cr (Uni-Galva-2010B)
[ Product name ; Uni-Galva-2010B]
• Building interiors or exteriors
• Electricity, electronic appliances
• Automobile parts
• Drain pipe
Corrosion Resistance
Q.U.V
Anti-Finger print
Workability & Formability
Chemical Resistance
High Humidity

11. Application of coating agent
We always think an environment valuably
3. Galva Cr (Uni-Galva-2010B)
1) Physical & chemical properties
[ Product name ; Uni-Galva-2010B ]
Main ingredient
• Urethane Resin & Acrylic Resin
• Inorganic compound
• Phosphate
• Cr
Appearance Light yellow-green liquid
Specific Gravity (20℃) 1.03 ± 0.005
p H 8.5 ± 1.0
Viscosity 15±2 sec (#4 Ford Viscosity Cup)
Cr - Content 300mg / 100g
1) Korea Testing & Research Institute for Chemical Industry (TAK-018967)

12. Application of coating agent
We always think an environment valuably
3. Galva Cr (Uni-Galva-2010B)
2) Properties Evaluation Method
Items Evaluation method
Corrosion
Resistance
(SST)
Plane ▪ KS D 9502, Edge Tape Sealing: 500 Hr – Below 5%
Bending(2t) ▪ KS D 9502, 2t Bending area - 100 Hr - – Below 5%
Erichsen(6mm) ▪ KS D 9502, 6mm - 100Hr - – Below 5%
High temperature and humidity test
▪ High temperature and high humidity test: 600
C , 95%H, 120Hr  E<2
 E = SQRT [ L2
+  a2
+  b2
]
QUV ▪ ASTM G-53 1, 000Hr – Check b value out of L, a, b measured by colorimeter , b < 1
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (5min)
acid resistance ▪ 5% HCl, dropping check (30min)
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test – No peeling off
Erichsen ▪ CCET – 1mm / 6mm and tapping test – No peeling off
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E<2
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E<2
Anti-finger print ▪ Measure an external appearance after painting vaseline ,  E<2

13. Application of coating agent
We always think an environment valuably
3. Galva Cr (Uni-Galva-2010B)
3) Properties Evaluation
Items Evaluation Spec’ Galva Clean
Corrosion
Resistance
(SST)
Plane ▪ 5% NaCl SST – 500Hr Excellent ( No defect )
Bending(2t) ▪ 5% NaCl SST – 100Hr Excellent ( No defect )
Erichsen(6mm) ▪ 5% NaCl SST – 100Hr Excellent ( No defect )
High temperature and humidity test ▪ 60℃ , 95%H, 120Hr , △E < 2 OK (△E = 0.61 )
QUV ▪ ASTM G-53, 1, 000Hr , △b < 1 OK (△B = 0.41 )
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (5min) OK
acid resistance ▪ 5% HCl, dropping check (30min) OK
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test OK ( No peeling off )
Erichsen ▪ CCET – 1mm / 6mm and tapping test OK ( No peeling off )
Solvent
Resistance
MEK ▪ 5 times MEK rubbing, △E < 2 OK (△E = 0.23 )
Ethanol ▪ With 80% ethanol, 5 times rubbing, △E < 2 OK (△E = 0.48 )
Anti-finger print ▪ painting vaseline , △E<2 OK (△E = 1.36 )

14. Application of coating agent
We always think an environment valuably
3. Galva Cr (Uni-Galva-2010B)
4) Properties Evaluation
Corrosion Resistance
(Plain - SST 500Hr)
Corrosion Resistance
(2 - T Bend - SST 100Hr)
Corrosion Resistance
(6mm -Erichsen - SST 100Hr)
temperature and humidity
(60℃ , 95%H, 120Hr)
Alkali and Acid resistance
(5% NaOH, 5% HCl)
T-Bending
(0T-Bending and tapping test)
Erichsen
(1mm / 6mm and tapping test)
Solvent Resistance
(MEK, Ethanol)
alkali resistance
acid resistance
5% NaOH (5min)
5% HCl (30min)
(△E = 0.61 )
MEK
Ethanol
△E = 0.23
△E = 0.48
( No defect ) ( No defect ) ( No defect )
( No peeling off )
( No peeling off )

15. Application of coating agent
We always think an environment valuably
4. Galva Cr-Free (Uni-Galfree-2010A)
[ Product name ; Uni-Galfree-2010A ]
• Building interiors or exteriors
• Electricity, electronic appliances
• Automobile parts
• Drain pipe
Corrosion Resistance
Q.U.V
Anti-Finger print
Workability & Formability
Chemical Resistance
High Humidity

16. Application of coating agent
We always think an environment valuably
4. Galva Cr-Free (Uni-Galfree-2010A)
1) Physical & chemical properties
[ Product name ; Uni-Galfree-2010A ]
Main ingredient
• Urethane Resin & Acrylic Resin
• Inorganic compound
• Phosphate
• Coupling Agent
Appearance Light yellow-blue Liquid
Specific Gravity (20℃) 1.03± 0.005
p H 8.5± 1.0
Viscosity 15±2 sec (#4 Ford Viscosity Cup)
1) Korea Testing & Research Institute for Chemical Industry (TAK-018967)

17. Application of coating agent
We always think an environment valuably
4. Galva Cr-Free (Uni-Galfree-2010A)
2) Properties Evaluation Method
Items Evaluation method
Corrosion
Resistance
(SST)
Plane ▪ KS D 9502, Edge Tape Sealing: 500 Hr – Below 5%
Bending(2t) ▪ KS D 9502, 2t Bending area - 100 Hr - – Below 5%
Erichsen(6mm) ▪ KS D 9502, 6mm - 100Hr - – Below 5%
High temperature and humidity test
▪ High temperature and high humidity test: 600
C , 95%H, 120Hr  E<2
 E = SQRT [ L2
+  a2
+  b2
]
QUV ▪ ASTM G-53 1, 000Hr – Check b value out of L, a, b measured by colorimeter , b < 1
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (5min)
acid resistance ▪ 5% HCl, dropping check (30min)
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test – No peeling off
Erichsen ▪ CCET – 1mm / 6mm and tapping test – No peeling off
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E<2
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E<2
Anti-finger print ▪ Measure an external appearance after painting vaseline ,  E<2

18. Application of coating agent
We always think an environment valuably
4. Galva Cr-Free (Uni-Galfree-2010A)
3) Properties Evaluation
Items Evaluation Spec’ Galva Clean
Corrosion
Resistance
(SST)
Plane ▪ 5% NaCl SST – 500Hr Excellent ( No defect )
Bending(2t) ▪ 5% NaCl SST – 100Hr Excellent ( No defect )
Erichsen(6mm) ▪ 5% NaCl SST – 100Hr Excellent ( No defect )
High temperature and humidity test ▪ 60℃ , 95%H, 120Hr , △E < 2 OK (△E = 0.68 )
QUV ▪ ASTM G-53, 1, 000Hr , △b < 1 OK (△B = 0.43 )
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (5min) OK
acid resistance ▪ 5% HCl, dropping check (30min) OK
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test OK ( No peeling off )
Erichsen ▪ CCET – 1mm / 6mm and tapping test OK ( No peeling off )
Solvent
Resistance
MEK ▪ 5 times MEK rubbing, △E < 2 OK (△E = 0.31 )
Ethanol ▪ With 80% ethanol, 5 times rubbing, △E < 2 OK (△E = 0.43 )
Anti-finger print ▪ painting vaseline , △E<2 OK (△E = 1.21 )

19. Application of coating agent
We always think an environment valuably
4. Galva Cr-Free (Uni-Galfree-2010A)
4) Properties Evaluation
Corrosion Resistance
(Plain - SST 500Hr)
Corrosion Resistance
(2 - T Bend - SST 100Hr)
Corrosion Resistance
(6mm -Erichsen - SST 100Hr)
temperature and humidity
(60℃ , 95%H, 120Hr)
Alkali and Acid resistance
(5% NaOH, 5% HCl)
T-Bending
(0T-Bending and tapping test)
Erichsen
(1mm / 6mm and tapping test)
Solvent Resistance
(MEK, Ethanol)
alkali resistance
acid resistance
5% NaOH (5min)
5% HCl (30min)
( △E = 0.68 )
MEK
Ethanol
△E = 0.31
△E = 0.43
( No defect ) ( No defect ) ( No defect )
( No peeling off )
( No peeling off )

20. Application of coating agent
We always think an environment valuably
5. Galva Cr-Free (Uni-Galfree-2010B)
[ Product name ; Uni-Galfree-2010B ]
• Electricity, electronic appliances
especially need an electric
conductibility and formability
Corrosion Resistance
Q.U.V
Anti-Finger print
Workability & Formability
Chemical Resistance
High Humidity
Electric Conductibility

21. Application of coating agent
We always think an environment valuably
5. Galva Cr-Free (Uni-Galfree-2010B)
1) Physical & chemical properties
[ Produt name ; Uni-Galfree-2010B ]
Main ingredient
• Urethane Resin
• Inorganic compound
• Phosphate
Appearance Light yellow-blue Liquid
Specific Gravity (20℃) 1.03 ± 0.005
p H 8.5 ± 1.0
Viscosity 15±2 sec (#4 Ford Viscosity Cup)
1) Korea Testing & Research Institute for Chemical Industry (TAK-018967)

22. Application of coating agent
We always think an environment valuably
5. Galva Cr-Free (Uni-Galfree-2010B)
2) Properties Evaluation Method
Items Evaluation method
Corrosion
Resistance
(SST)
Plane ▪ KS D 9502, Edge Tape Sealing: 240 Hr – Below 5%
Bending(2t) ▪ KS D 9502, 2t Bending area - 50 Hr - – Below 5%
Erichsen(6mm) ▪ KS D 9502, 6mm - 50Hr - – Below 5%
High temperature and humidity test
▪ High temperature and high humidity test: 60℃, 95%H, 120Hr,  E<2
 E = SQRT [ L2
+  a2
+  b2
]
QUV
▪ ASTM G-53, 1, 000Hr – Check b value out of L, a, b measured by colorimeter ,△  b
< 1
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (2min)
acid resistance ▪ 5% HCl, dropping check (20min)
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test – No peeling off
Erichsen ▪ CCET – 1mm / 6mm and tapping test – No peeling off
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E<2
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E<2
Anti-finger print ▪ Measure an external appearance after painting vaseline ,  E<2
Electric Conductibility ▪ 4 – Point Probe, Less than 0.1 mΩ

23. Application of coating agent
We always think an environment valuably
5. Galva Cr-Free (Uni-Galfree-2010B)
3) Properties Evaluation
Items Evaluation Spec’ Galva Clean
Corrosion
Resistance
(SST)
Plane ▪ 5% NaCl SST – 240Hr Excellent ( No defect )
Bending(2t) ▪ 5% NaCl SST – 50Hr Excellent ( No defect )
Erichsen(6mm) ▪ 5% NaCl SST – 50Hr Excellent ( No defect )
High temperature and humidity test ▪ 60℃ , 95%H, 120Hr ,  E < 2 OK ( E = 0.71 )
QUV ▪ ASTM G-53, 1, 000Hr ,  b < 1 OK ( B = 0.38 )
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (2min) OK
acid resistance ▪ 5% HCl, dropping check (20min) OK
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test OK ( No peeling off )
Erichsen ▪ CCET – 1mm / 6mm and tapping test OK ( No peeling off )
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E < 2 OK ( E = 0.33 )
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E < 2 OK ( E = 0.45 )
Anti-finger print ▪ painting vaseline ,  E<2 OK ( E = 1.19 )
Electric Conductibility ▪ 4 – Point Probe, Less than 0.1 mΩ OK ( 0.030mΩ )

24. Application of coating agent
We always think an environment valuably
5. Galva Cr-Free (Uni-Galfree-2010B)
4) Properties Evaluation
Corrosion Resistance
(Plain - SST 240Hr)
Corrosion Resistance
(2 - T Bend - SST 50Hr)
Corrosion Resistance
(6mm -Erichsen – SST 50Hr)
temperature and humidity
(60℃ , 95%H, 120Hr)
Alkali and Acid resistance
(5% NaOH, 5% HCl)
T-Bending
(0T-Bending and tapping test)
Erichsen
(1mm / 6mm and tapping test)
Solvent Resistance
(MEK, Ethanol)
( No defect )
( No defect ) ( No defect ) ( △E = 0.71 )
alkali resistance
acid resistance
5% NaOH (2min)
5% HCl (20min)
MEK
Ethanol
 E = 0.33
 E = 0.45
( No peeling off )
( No peeling off )

25. Application of coating agent
We always think an environment valuably
6. Lubricant Galva (Uni-LGF-2010)
[ Product name ; Uni-LGF-2010 ]
• Building interiors or exteriors
• Electricity, electronic appliances
• Use it need a high workability &
formability
Corrosion Resistance
Q.U.V
Anti-Finger print
Workability & Formability
Chemical Resistance
Water resisting
Electric Conductibility
Lubircity

26. Application of coating agent
We always think an environment valuably
6. Lubricant Galva (Uni-LGF-2010)
1) Physical & chemical properties
[ Produt name ; Uni-LGF-2010 ]
Main ingredient
• Urethane Resin
• Inorganic compound
• Phosphate
• Wax
Appearance White Emulsion Dispersion
Specific Gravity (20℃) 1.03± 0.005
p H 8.5± 1.0
Viscosity 15±2 sec (#4 Ford Viscosity Cup)
1) Korea Testing & Research Institute for Chemical Industry (TAK-018967)

27. Application of coating agent
We always think an environment valuably
6. Lubricant Galva (Uni-LGF-2010)
2) Properties Evaluation Method
Items Evaluation method
Corrosion
Resistance
(SST)
Plane ▪ KS D 9502, Edge Tape Sealing: 240 Hr – Below 5%
Bending(2t) ▪ KS D 9502, 2t Bending area - 50 Hr - – Below 5%
Erichsen(6mm) ▪ KS D 9502, 6mm - 50Hr - – Below 5%
High temperature and humidity test
▪ High temperature and high humidity test: 60℃, 95%H, 120Hr △E<2
△E = SQRT [ △L2
+ △a2
+ △b2
]
QUV ▪ ASTM G-53, 1, 000Hr – Check b value out of L, a, b measured by colorimeter ,△ b < 1
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (2min)
acid resistance ▪ 5% HCl, dropping check (20min)
Formability Cupping ▪ Cup drawing test :
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test – No peeling off
Erichsen ▪ CCET – 1mm / 6mm and tapping test – No peeling off
Solvent
Resistance
MEK ▪ 5 times MEK rubbing, △E<2
Ethanol ▪ With 80% ethanol, 5 times rubbing, △E<2
Anti-finger print ▪ Measure an external appearance after painting vaseline , △E<2

28. Application of coating agent
We always think an environment valuably
6. Lubricant Galva (Uni-LGF-2010)
3) Properties Evaluation
Items Evaluation Spec’ Galva Clean
Corrosion
Resistance
(SST)
Plane ▪ 5% NaCl SST – 240Hr Excellent ( No defect )
Bending(2t) ▪ 5% NaCl SST – 50Hr Excellent ( No defect )
Erichsen(6mm) ▪ 5% NaCl SST – 50Hr Excellent ( No defect )
High temperature and humidity test ▪ 60℃ , 95%H, 120Hr ,  E < 2 OK ( E = 0.76 )
QUV ▪ ASTM G-53, 1, 000Hr ,  b < 1 OK ( B = 0.47 )
Chemical
resistance
alkali resistance ▪ 5% NaOH, dropping check (2min) OK
acid resistance ▪ 5% HCl, dropping check (20min) OK
Formability Cupping ▪ Cup drawing test :
Adhesive
powder
T-Bending ▪ 0T-Bending and tapping test OK ( No peeling off )
Erichsen ▪ CCET – 1mm / 6mm and tapping test OK ( No peeling off )
Solvent
Resistance
MEK ▪ 5 times MEK rubbing,  E < 2 OK ( E = 0.31 )
Ethanol ▪ With 80% ethanol, 5 times rubbing,  E < 2 OK ( E = 0.42 )
Anti-finger print ▪ painting vaseline ,  E<2 OK ( E = 1.24 )

29. Application of coating agent
We always think an environment valuably
6. Lubricant Galva (Uni-LGF-2010)
4) Properties Evaluation
Corrosion Resistance
(Plain - SST 240Hr)
Corrosion Resistance
(2 - T Bend - SST 50Hr)
Corrosion Resistance
(6mm -Erichsen - SST 50Hr)
temperature and humidity
(60℃ , 95%H, 120Hr)
Alkali and Acid resistance
(5% NaOH, 5% HCl)
T-Bending
(0T-Bending and tapping test)
Erichsen
(1mm / 6mm and tapping test)
Formability
(Cup drawing test)
( △E = 0.76 )
( No defect ) ( No defect ) ( No defect )
alkali resistance
acid resistance
5% NaOH (2min)
5% HCl (20min)
BHF : 4.0
Punch Force : 4.7
Depth Height : 25mm
( No peeling off )
( No peeling off )

30. Application of coating agent
We always think an environment valuably
7. Color coating agent ( UNICOAT-WAF-2008A)
WARM GRAY
Items Spec’ Remarks
Condition
Dry Temp’ PMT ( 0
C) 170 ~180
Properties
Electricity
conductibility
Surface Resistance (0.1mΩ↓) O
Corrosion
Resistance
SST 120 Hrs
(W-R, below 5%)
NO(5%↓)
Alkalinity
Resistance
pH12(60℃/2min)-SONY Spec
(SST 48Hrs)
No peeling,
blister and W-R
Solvent
Resistance
MEK 20th
rubbing,
no peeling
No peeling
Darkening
Resistance
(120hrs)
ΔE<2 OK (1.24)
ΔL<2 OK (0.72)
Sweat
Resistance
The high temperature and high
humidity during 48 hours after
dropped the artificial sweat
0.05ml
O
PB-1
No white rust and peeling off
after treated NaOH 3%
O
Coefficient of
friction
Draw bead test Coefficient < 2 OK
• Building interiors or exteriors
• Electricity, electronic appliance
1) Properties Evaluation