The kind of pipe composite three parts, the steel pipe glue and ceramic. The steel pipe is hot pressing, which is different to section welding bend. The ceramic tiles is 95% high alumina, and the glue is high temperature adhesive up to 100OC.This kind of bend are good for the powder transport and no tile fall off oraging working under 100OC for long time. The service life span is 4 to 5 times than normal steel pipe.

1. Ceramic lining pipe
Kingcera offer optimized wear protection for plant components and pipe systems.
Why wear protection?--- reduce costs and avoid downtime.
Ceramic lining pipe:
The kind of pipe composite three parts, the steel pipe glue and ceramic. The steel pipe is hot pressing, which is different to
section welding bend. The ceramic tiles is 95% high alumina, and the glue is high temperature adhesive up to 100OC.This kind of
bend are good for the powder transport and no tile fall off oraging working under 100OC for long time. The service life span is 4
to 5 times than normal steel pipe.
Ceramic Specification:
Item K-95 K-99 K-ZTA K-Z
Ceramic wear material 94% alumina 98% alumina 80% alumina 99% zirconia
Density 3.65 g/cm3 3.85 g/cm3 4.2 g/cm3 6.1 g/cm3
Porosity ＜ 0.1 ＜ 0.1 ＜ 0.1 ＜ 0.1
Compressive Strength ≥ 1700 Mpa ≥ 1800 Mpa ≥ 2100 Mpa ≥ 2400 Mpa
Rockwell Hardness ≥ 85 HRA ≥ 86 HRA ≥ 90 HRA ≥ 88 HRA
Vickers Hardness ≥ 1000 HV10 ≥ 1100 HV10 ≥ 1200 HV10 ≥ 1150 HV10
Fracture Toughness (KIC) ≥ 4.5 Mpa.m1/2 ≥ 4.8 Mpa.m1/2 ≥ 5.5 Mpa.m1/2 ≥ 7.5 Mpa.m1/2
Bending Strength ≥ 290 Mpa ≥ 290 Mpa ≥ 320 Mpa ≥ 360 Mpa
Wear Volume ≤ 0.05 cm3 ≤ 0.01 cm3 ≤ 0.009 cm3 ≤ 0.007 cm3
ASTM G65 Relative Factor 9-11 9-11 11-14 12-15

2. Services rendered for many branches of industry:
Coal fired power plants Iron and steel industry
Cement industry Chemical industry
Product sketch:
Compare of wear resistant abilities with other common abrasion-resistant materials

3. Clear advantages:
--- Long lifetime
--- Maintenance free operation
--- No operation interruption
--- No production losses
--- Smooth surface to achieve good flowability and to avoid plugs
--- Reduced pressure losses and lower energy cost
The selection of abrasion-resistant Elbows:
DN
Thickness
of steel pip
Thickness
of ceramic
OD
Radius of
curvature
Angle Flange
40 3 5 57 150 0-90° Optional
50 3.5 5 68 200 0-90° Optional
65 3.5 5 83 250 0-90° Optional
80 5.5 5 102 300 0-90° Optional
90 6.5 5 114 350 0-90° Optional
100 5 5 121 400 0-90° Optional
125 5 5 146 450 0-90° Optional
150 4.5 4 168 550 0-90° Optional
200 5 4 219 700 0-90° Optional
250 6 5 273 800 0-90° Optional
300 7 5 325 1000 0-90° Optional
350 8 5 377 1250 0-90° Optional
400 7.5 5 426 1400 0-90° Optional
450 9.5 5 480 1600 0-90° Optional
500 9.5 5 530 1750 0-90° Optional
600 9.5 5 630 2000 0-90° Optional

4. Manufacturing:

5. Customer visiting:

6. Certification:
EXPLORE PROJECT BY COMPANY
Add: No. 8 Lixing West Road, Changsha, Hunan Province, China
Sale manager: Roy Luo Tel: +86-731-84019856 Fax: +86-731-84069186 Moblie: +86-18570396817 E-mail: roy@kingcera.com/roy@jcnmc.com
Web: www.kingcera.com