This document describes the synthesis and characterization of Pt-Ru nanoparticles supported on a polyamidoamine (PAMAM) dendrimer functionalized carbon nanofiber (CNF) composite catalyst for application in direct methanol fuel cells. Pt-Ru nanoparticles with an average size of 2.6 nm were uniformly dispersed on the PAMAM/CNF composite support. X-ray diffraction and transmission electron microscopy analysis showed the well-dispersed and small Pt-Ru nanoparticles on the composite support. Cyclic voltammetry measurements demonstrated that the Pt-Ru/PAMAM-CNF composite electrode exhibited better electrocatalytic activity for methanol oxidation compared to a commercially available Pt-Ru/C catalyst. The results suggest
Polyamidoamine (PAMAM) dendrimers has
been anchored on functionalized carbon nanofibers (CNF)
and supported Pt–Ru nanoparticles have been prepared with
NaBH4 as a reducing agent. The samples were characterized
by X-ray diffraction, scanning electron microscopy,
and transmission electron microscopy (TEM) analysis. It
was shown that Pt–Ru particles with small average size
(2.6 nm) were uniformly dispersed on PAMAM/CNF
composite support and displayed the characteristic diffraction
peaks of Pt face-centered cubic structure. The electrocatalytic
activities of the prepared-composites (20% Pt–Ru/PAMAMCNF)
were examined by using cyclic voltammetry for
oxidation of methanol. The electrocatalytic activity of the
CNF-based composite (20% Pt–Ru/PAMAM-CNF) electrode
for methanol oxidation showed better performance than that
of commercially available Johnson Mathey 20% Pt–Ru/C
catalyst. The results imply that CNF-based PAMAM composite
electrodes are excellent potential candidates for
application in direct methanol fuel cells.
Photocatalytic reduction of carbon dioxide to methanol using a ruthenium trin...Pawan Kumar
A ruthenium trinuclear polyazine complex was synthesized and subsequently immobilized through
complexation to a graphene oxide support containing phenanthroline ligands (GO-phen). The developed
photocatalyst was used for the photocatalytic reduction of CO2 to methanol, using a 20 watt white cold
LED flood light, in a dimethyl formamide–water mixture containing triethylamine as a reductive
quencher. After 48 h illumination, the yield of methanol was found to be 3977.57 5.60 mmol gcat
1.
The developed photocatalyst exhibited a higher photocatalytic activity than graphene oxide, which
provided a yield of 2201.40 8.76 mmol gcat
1. After the reaction, the catalyst was easily recovered and
reused for four subsequent runs without a significant loss of catalytic activity and no leaching of the
metal/ligand was detected during the reaction
Highly stable pt ru nanoparticles supported on three-dimensional cubic ordere...suresh899
The cost of the catalysts used in the direct methanol fuel cell
poses a challenge to its widespread use as an energy efficient and environment
friendly fuel conversion technology. In this study, two types of highly ordered
mesoporous carbon CMK-8 (I and II) with high surface area and 3-D
bicontinuous interpenetrating channels were synthesized and deposited with
PtRu nanoparticles using the sodium borohydride reduction method. The
electrocatalytic capabilities for methanol oxidation were investigated using
cyclic voltammetry and chronoamperometry, and the results were compared
with that of PtRu deposited on Vulcan XC-72 using the same preparation
method as well as with commercial PtRu/C (E-TEK) catalyst. Pt Ru/CMK-8-I synthesized by the method developed in this work revealed an
outstanding specific mass activity (487.9 mA/mg) and superior stability
compared with the other supports, thus substantiating its potential to reduce
the costs of DMFC catalysts.
Functionalization of Diazomethyl Aromatic Compounds onto Single Wall Carbon N...drboon
One of the most fascinating and remarkable formulas existing in mathematics is the Euler Formula. It was formulated in 1740, constituting the main factor to reason why humankind can advance in science and mathematics. Accordingly, this research will continue investigating the potentiality of the Euler Formula or "the magical number e." The goal of the present study is to further assess the Euler formula and several of its applications such as the compound interest problem, complex numbers, trigonometry, signals (electrical engineering), and Ordinary Differential Equations. To accomplish this goal, the Euler Formula will be entered into the MATLAB software to obtain several plots representing the above applications. The importance of this study in mathematics and engineering will be discussed, and a case study on a polluted lake will be formulated.
C3N5: A Low Bandgap Semiconductor Containing an Azo-Linked Carbon Nitride Fra...Pawan Kumar
Modification of carbon nitride based polymeric
2D materials for tailoring their optical, electronic and
chemical properties for various applications has gained
significant interest. The present report demonstrates the
synthesis of a novel modified carbon nitride framework with a
remarkable 3:5 C:N stoichiometry (C3N5) and an electronic
bandgap of 1.76 eV, by thermal deammoniation of the melem
hydrazine precursor. Characterization revealed that in the
C3N5 polymer, two s-heptazine units are bridged together with
azo linkage, which constitutes an entirely new and different
bonding fashion from g-C3N4 where three heptazine units are
linked together with tertiary nitrogen. Extended conjugation
due to overlap of azo nitrogens and increased electron density
on heptazine nucleus due to the aromatic π network of heptazine units lead to an upward shift of the valence band maximum
resulting in bandgap reduction down to 1.76 eV. XRD, He-ion imaging, HR-TEM, EELS, PL, fluorescence lifetime imaging,
Raman, FTIR, TGA, KPFM, XPS, NMR and EPR clearly show that the properties of C3N5 are distinct from pristine carbon
nitride (g-C3N4). When used as an electron transport layer (ETL) in MAPbBr3 based halide perovskite solar cells, C3N5
outperformed g-C3N4, in particular generating an open circuit photovoltage as high as 1.3 V, while C3N5 blended with
MAxFA1−xPb(I0.85Br0.15)3 perovskite active layer achieved a photoconversion efficiency (PCE) up to 16.7%. C3N5 was also
shown to be an effective visible light sensitizer for TiO2 photoanodes in photoelectrochemical water splitting. Because of its
electron-rich character, the C3N5 material displayed instantaneous adsorption of methylene blue from aqueous solution reaching
complete equilibrium within 10 min, which is significantly faster than pristine g-C3N4 and other carbon based materials. C3N5
coupled with plasmonic silver nanocubes promotes plasmon-exciton coinduced surface catalytic reactions reaching completion
at much low laser intensity (1.0 mW) than g-C3N4, which showed sluggish performance even at high laser power (10.0 mW).
The relatively narrow bandgap and 2D structure of C3N5 make it an interesting air-stable and temperature-resistant
semiconductor for optoelectronic applications while its electron-rich character and intrasheet cavity make it an attractive
supramolecular adsorbent for environmental applications.
C3N5: A Low Bandgap Semiconductor Containing an Azo-Linked Carbon Nitride Fra...Pawan Kumar
Modification of carbon nitride based polymeric 2D materials for tailoring their optical, electronic and chemical properties for various applications has gained significant interest. The present report demonstrates the synthesis of a novel modified carbon nitride framework with a remarkable 3:5 C:N stoichiometry (C3N5) and an electronic bandgap of 1.76 eV, by thermal deammoniation of the melem hydrazine precursor. Characterization revealed that in the C3N5 polymer, two s-heptazine units are bridged together with azo linkage, which constitutes an entirely new and different bonding fashion from g-C3N4 where three heptazine units are linked together with tertiary nitrogen. Extended conjugation due to overlap of azo nitrogens and increased electron density on heptazine nucleus due to the aromatic π network of heptazine units lead to an upward shift of the valence band maximum resulting in bandgap reduction
Polyamidoamine (PAMAM) dendrimers has
been anchored on functionalized carbon nanofibers (CNF)
and supported Pt–Ru nanoparticles have been prepared with
NaBH4 as a reducing agent. The samples were characterized
by X-ray diffraction, scanning electron microscopy,
and transmission electron microscopy (TEM) analysis. It
was shown that Pt–Ru particles with small average size
(2.6 nm) were uniformly dispersed on PAMAM/CNF
composite support and displayed the characteristic diffraction
peaks of Pt face-centered cubic structure. The electrocatalytic
activities of the prepared-composites (20% Pt–Ru/PAMAMCNF)
were examined by using cyclic voltammetry for
oxidation of methanol. The electrocatalytic activity of the
CNF-based composite (20% Pt–Ru/PAMAM-CNF) electrode
for methanol oxidation showed better performance than that
of commercially available Johnson Mathey 20% Pt–Ru/C
catalyst. The results imply that CNF-based PAMAM composite
electrodes are excellent potential candidates for
application in direct methanol fuel cells.
Photocatalytic reduction of carbon dioxide to methanol using a ruthenium trin...Pawan Kumar
A ruthenium trinuclear polyazine complex was synthesized and subsequently immobilized through
complexation to a graphene oxide support containing phenanthroline ligands (GO-phen). The developed
photocatalyst was used for the photocatalytic reduction of CO2 to methanol, using a 20 watt white cold
LED flood light, in a dimethyl formamide–water mixture containing triethylamine as a reductive
quencher. After 48 h illumination, the yield of methanol was found to be 3977.57 5.60 mmol gcat
1.
The developed photocatalyst exhibited a higher photocatalytic activity than graphene oxide, which
provided a yield of 2201.40 8.76 mmol gcat
1. After the reaction, the catalyst was easily recovered and
reused for four subsequent runs without a significant loss of catalytic activity and no leaching of the
metal/ligand was detected during the reaction
Highly stable pt ru nanoparticles supported on three-dimensional cubic ordere...suresh899
The cost of the catalysts used in the direct methanol fuel cell
poses a challenge to its widespread use as an energy efficient and environment
friendly fuel conversion technology. In this study, two types of highly ordered
mesoporous carbon CMK-8 (I and II) with high surface area and 3-D
bicontinuous interpenetrating channels were synthesized and deposited with
PtRu nanoparticles using the sodium borohydride reduction method. The
electrocatalytic capabilities for methanol oxidation were investigated using
cyclic voltammetry and chronoamperometry, and the results were compared
with that of PtRu deposited on Vulcan XC-72 using the same preparation
method as well as with commercial PtRu/C (E-TEK) catalyst. Pt Ru/CMK-8-I synthesized by the method developed in this work revealed an
outstanding specific mass activity (487.9 mA/mg) and superior stability
compared with the other supports, thus substantiating its potential to reduce
the costs of DMFC catalysts.
Functionalization of Diazomethyl Aromatic Compounds onto Single Wall Carbon N...drboon
One of the most fascinating and remarkable formulas existing in mathematics is the Euler Formula. It was formulated in 1740, constituting the main factor to reason why humankind can advance in science and mathematics. Accordingly, this research will continue investigating the potentiality of the Euler Formula or "the magical number e." The goal of the present study is to further assess the Euler formula and several of its applications such as the compound interest problem, complex numbers, trigonometry, signals (electrical engineering), and Ordinary Differential Equations. To accomplish this goal, the Euler Formula will be entered into the MATLAB software to obtain several plots representing the above applications. The importance of this study in mathematics and engineering will be discussed, and a case study on a polluted lake will be formulated.
C3N5: A Low Bandgap Semiconductor Containing an Azo-Linked Carbon Nitride Fra...Pawan Kumar
Modification of carbon nitride based polymeric
2D materials for tailoring their optical, electronic and
chemical properties for various applications has gained
significant interest. The present report demonstrates the
synthesis of a novel modified carbon nitride framework with a
remarkable 3:5 C:N stoichiometry (C3N5) and an electronic
bandgap of 1.76 eV, by thermal deammoniation of the melem
hydrazine precursor. Characterization revealed that in the
C3N5 polymer, two s-heptazine units are bridged together with
azo linkage, which constitutes an entirely new and different
bonding fashion from g-C3N4 where three heptazine units are
linked together with tertiary nitrogen. Extended conjugation
due to overlap of azo nitrogens and increased electron density
on heptazine nucleus due to the aromatic π network of heptazine units lead to an upward shift of the valence band maximum
resulting in bandgap reduction down to 1.76 eV. XRD, He-ion imaging, HR-TEM, EELS, PL, fluorescence lifetime imaging,
Raman, FTIR, TGA, KPFM, XPS, NMR and EPR clearly show that the properties of C3N5 are distinct from pristine carbon
nitride (g-C3N4). When used as an electron transport layer (ETL) in MAPbBr3 based halide perovskite solar cells, C3N5
outperformed g-C3N4, in particular generating an open circuit photovoltage as high as 1.3 V, while C3N5 blended with
MAxFA1−xPb(I0.85Br0.15)3 perovskite active layer achieved a photoconversion efficiency (PCE) up to 16.7%. C3N5 was also
shown to be an effective visible light sensitizer for TiO2 photoanodes in photoelectrochemical water splitting. Because of its
electron-rich character, the C3N5 material displayed instantaneous adsorption of methylene blue from aqueous solution reaching
complete equilibrium within 10 min, which is significantly faster than pristine g-C3N4 and other carbon based materials. C3N5
coupled with plasmonic silver nanocubes promotes plasmon-exciton coinduced surface catalytic reactions reaching completion
at much low laser intensity (1.0 mW) than g-C3N4, which showed sluggish performance even at high laser power (10.0 mW).
The relatively narrow bandgap and 2D structure of C3N5 make it an interesting air-stable and temperature-resistant
semiconductor for optoelectronic applications while its electron-rich character and intrasheet cavity make it an attractive
supramolecular adsorbent for environmental applications.
C3N5: A Low Bandgap Semiconductor Containing an Azo-Linked Carbon Nitride Fra...Pawan Kumar
Modification of carbon nitride based polymeric 2D materials for tailoring their optical, electronic and chemical properties for various applications has gained significant interest. The present report demonstrates the synthesis of a novel modified carbon nitride framework with a remarkable 3:5 C:N stoichiometry (C3N5) and an electronic bandgap of 1.76 eV, by thermal deammoniation of the melem hydrazine precursor. Characterization revealed that in the C3N5 polymer, two s-heptazine units are bridged together with azo linkage, which constitutes an entirely new and different bonding fashion from g-C3N4 where three heptazine units are linked together with tertiary nitrogen. Extended conjugation due to overlap of azo nitrogens and increased electron density on heptazine nucleus due to the aromatic π network of heptazine units lead to an upward shift of the valence band maximum resulting in bandgap reduction
Polyaniline (PANI) Metal Oxide Nano Composites as a Conducting MaterialRSIS International
The combination of conducting nanoparticles and conducting polymers is a new area of research. The conducting polymer nanocomposites have both advantages of low dimensional systems and organic conductors. With this nanofibre morphology, the dispersibility and processibility of polyanilines can be improved.
The aim of this literature is to provide a survey of previous findings of researchers related to metal oxide nanocomposite polyaniline. In this paper we reviewed the properties, methods of synthesis, and various applications.
Maiyalagan,Electrochemical oxidation of methanol on pt v2 o5–c composite cata...kutty79
Platinum nanoparticles have been supported on V2O5–C composite through the reduction of chloroplatinic
acid with formaldehyde. The catalyst was characterized by X-ray diffraction and transmission electron
microscopy. Catalytic activity and stability for the oxidation of methanol were studied by using
cyclic voltammetry and chronoamperometry. Pt/V2O5–C composite anode catalyst on glassy carbon electrode
show higher electro-catalytic activity for the oxidation of methanol. High electro-catalytic activities
and good stabilities could be attributed to the synergistic effect between Pt and V2O5, avoiding the electrodes
being poisoned.
Nickel Decorated on Phosphorous-Doped Carbon Nitride as an Efficient Photocat...Pawan Kumar
Nickel nanoparticle-decorated phosphorous-doped graphitic carbon nitride (Ni@g-PC3N4)
was synthesized and used as an efficient photoactive catalyst for the reduction of various
nitrobenzenes under visible light irradiation. Hydrazine monohydrate was used as the source
of protons and electrons for the intended reaction. The developed photocatalyst was found to be
highly active and afforded excellent product yields under mild experimental conditions. In addition,
the photocatalyst could easily be recovered and reused for several runs without any detectable
leaching during the reaction.
Electro catalytic performance of pt-supported poly (o-phenylenediamine) micro...sunitha81
Poly (o-phenylenediamine) (PoPD) microrods were obtained by interfacial
polymerization using ferric chloride as oxidant and without any template or
functional dopant. Pt/PoPD nanocatalysts were prepared by the reduction of chloroplatinic
acid with sodium borohydride, and the composite catalysts formed were
characterized by X-ray diffraction and electrochemical methods. The nanocomposite
of Pt/PoPD microrods has been explored for their electro-catalytic performance
towards oxidation of methanol. The electro-catalytic activity of Pt/PoPD was
found to be much higher (current density 1.96 mA/cm2 at 0.70 V) in comparison to
Pt/Vulcan electrodes (the current density values of 1.56 mA/cm2 at 0.71 V) which
may be attributed to the microrod morphology of PoPD that facilitate the effective
dispersion of Pt particles and easier access of methanol towards the catalytic sites.
Synthesis and properties of PolyanilineAwad Albalwi
Polyaniline which is regarding kind of Inherently Conducting Polymers (ICPs), was prepared by
either chemical and electricchemical polymerization in acidic medium. Such solvents were used
and compared the affecting on the conductivity between EB solution in DMF and mcresol solvents by using UVvis spectrum. UVvis
spectra and cyclic voltametry were used to generate
and analyze the spectrum for the polymer films
Electrooxidation of methanol on carbon supported pt ru nanocatalysts prepared...suresh899
Carbon Supported PtRu nanocatalysts have been prepared by simple impregnation reduction method in which Pt and Ru precursors are reduced by ethanol under reflux conditions for different reaction times. The prepared nanocatalysts were characterized by means of XRD, EDAX, ICP-AAS, FESEM and TEM. XRD analyses showed that all nanocatalysts exhibited f.c.c crystal structure, the structure characteristic for pure Pt, except for that reduced at prolonged reaction time of 4h which showed the presence of characteristic peak for Ru metal. The lattice constant calculations indicate that all catalysts are present in unalloyed phase and the average particle size as determined by TEM was in the range of 3.7 nm. The electrocatalytic activities and stability for the prepared nanocatalysts methanol electro-oxidation reaction (MOR) were studied by cyclic voltammetry. The catalysts prepared at 2h reduction time showed higher electrocatalytic activity in terms of mass specific activity and good stability over potential sweep for 100 cycles for methanol electro-oxidation. The results showed that the prepared nanocatalysts are considered as promising electrode catalyst (anode catalyst) for electro-oxidation of methanol in direct methanol fuel cells.
Maiyalagan, Synthesis and electro catalytic activity of methanol oxidation on...kutty79
Template synthesis of various nitrogen containing carbon nanotubes using different nitrogen containing polymers and the variation of nitrogen
content in carbon nanotube (CNT) on the behaviour of supported Pt electrodes in the anodic oxidation of methanol in direct methanol fuel cells was
investigated. Characterizations of the as-prepared catalysts are investigated by electron microscopy and electrochemical analysis. The catalyst with
N-containing CNT as a support exhibits a higher catalytic activity than that carbon supported platinum electrode and CNT supported electrodes.
The N-containing CNT supported electrodes with 10.5% nitrogen content show a higher catalytic activity compared to other N-CNT supported
electrodes. This could be due to the existence of additional active sites on the surface of the N-containing CNT supported electrodes, which favours
better dispersion of Pt particles. Also, the strong metal-support interaction plays a major role in enhancing the catalytic activity for methanol
oxidation.
Polyaniline (PANI) Metal Oxide Nano Composites as a Conducting MaterialRSIS International
The combination of conducting nanoparticles and conducting polymers is a new area of research. The conducting polymer nanocomposites have both advantages of low dimensional systems and organic conductors. With this nanofibre morphology, the dispersibility and processibility of polyanilines can be improved.
The aim of this literature is to provide a survey of previous findings of researchers related to metal oxide nanocomposite polyaniline. In this paper we reviewed the properties, methods of synthesis, and various applications.
Maiyalagan,Electrochemical oxidation of methanol on pt v2 o5–c composite cata...kutty79
Platinum nanoparticles have been supported on V2O5–C composite through the reduction of chloroplatinic
acid with formaldehyde. The catalyst was characterized by X-ray diffraction and transmission electron
microscopy. Catalytic activity and stability for the oxidation of methanol were studied by using
cyclic voltammetry and chronoamperometry. Pt/V2O5–C composite anode catalyst on glassy carbon electrode
show higher electro-catalytic activity for the oxidation of methanol. High electro-catalytic activities
and good stabilities could be attributed to the synergistic effect between Pt and V2O5, avoiding the electrodes
being poisoned.
Nickel Decorated on Phosphorous-Doped Carbon Nitride as an Efficient Photocat...Pawan Kumar
Nickel nanoparticle-decorated phosphorous-doped graphitic carbon nitride (Ni@g-PC3N4)
was synthesized and used as an efficient photoactive catalyst for the reduction of various
nitrobenzenes under visible light irradiation. Hydrazine monohydrate was used as the source
of protons and electrons for the intended reaction. The developed photocatalyst was found to be
highly active and afforded excellent product yields under mild experimental conditions. In addition,
the photocatalyst could easily be recovered and reused for several runs without any detectable
leaching during the reaction.
Electro catalytic performance of pt-supported poly (o-phenylenediamine) micro...sunitha81
Poly (o-phenylenediamine) (PoPD) microrods were obtained by interfacial
polymerization using ferric chloride as oxidant and without any template or
functional dopant. Pt/PoPD nanocatalysts were prepared by the reduction of chloroplatinic
acid with sodium borohydride, and the composite catalysts formed were
characterized by X-ray diffraction and electrochemical methods. The nanocomposite
of Pt/PoPD microrods has been explored for their electro-catalytic performance
towards oxidation of methanol. The electro-catalytic activity of Pt/PoPD was
found to be much higher (current density 1.96 mA/cm2 at 0.70 V) in comparison to
Pt/Vulcan electrodes (the current density values of 1.56 mA/cm2 at 0.71 V) which
may be attributed to the microrod morphology of PoPD that facilitate the effective
dispersion of Pt particles and easier access of methanol towards the catalytic sites.
Synthesis and properties of PolyanilineAwad Albalwi
Polyaniline which is regarding kind of Inherently Conducting Polymers (ICPs), was prepared by
either chemical and electricchemical polymerization in acidic medium. Such solvents were used
and compared the affecting on the conductivity between EB solution in DMF and mcresol solvents by using UVvis spectrum. UVvis
spectra and cyclic voltametry were used to generate
and analyze the spectrum for the polymer films
Electrooxidation of methanol on carbon supported pt ru nanocatalysts prepared...suresh899
Carbon Supported PtRu nanocatalysts have been prepared by simple impregnation reduction method in which Pt and Ru precursors are reduced by ethanol under reflux conditions for different reaction times. The prepared nanocatalysts were characterized by means of XRD, EDAX, ICP-AAS, FESEM and TEM. XRD analyses showed that all nanocatalysts exhibited f.c.c crystal structure, the structure characteristic for pure Pt, except for that reduced at prolonged reaction time of 4h which showed the presence of characteristic peak for Ru metal. The lattice constant calculations indicate that all catalysts are present in unalloyed phase and the average particle size as determined by TEM was in the range of 3.7 nm. The electrocatalytic activities and stability for the prepared nanocatalysts methanol electro-oxidation reaction (MOR) were studied by cyclic voltammetry. The catalysts prepared at 2h reduction time showed higher electrocatalytic activity in terms of mass specific activity and good stability over potential sweep for 100 cycles for methanol electro-oxidation. The results showed that the prepared nanocatalysts are considered as promising electrode catalyst (anode catalyst) for electro-oxidation of methanol in direct methanol fuel cells.
Maiyalagan, Synthesis and electro catalytic activity of methanol oxidation on...kutty79
Template synthesis of various nitrogen containing carbon nanotubes using different nitrogen containing polymers and the variation of nitrogen
content in carbon nanotube (CNT) on the behaviour of supported Pt electrodes in the anodic oxidation of methanol in direct methanol fuel cells was
investigated. Characterizations of the as-prepared catalysts are investigated by electron microscopy and electrochemical analysis. The catalyst with
N-containing CNT as a support exhibits a higher catalytic activity than that carbon supported platinum electrode and CNT supported electrodes.
The N-containing CNT supported electrodes with 10.5% nitrogen content show a higher catalytic activity compared to other N-CNT supported
electrodes. This could be due to the existence of additional active sites on the surface of the N-containing CNT supported electrodes, which favours
better dispersion of Pt particles. Also, the strong metal-support interaction plays a major role in enhancing the catalytic activity for methanol
oxidation.
Highly active pd and pd–au nanoparticles supported on functionalized graphene...Science Padayatchi
Highly active Pd and Pd–Au nanoparticles supported on functionalized graphene nanoplatelets for enhanced formic acid oxidation
Similar to Pt ru nanoparticles-supported_pamam_dendrimer_functionalized_carbon_nanofiber_composite_catalysts_and_their_application_to_methanol_oxid (20)
Dynamic and Equilibrium Studies on the sorption of Basic dye (Basic Brown 4) ...madlovescience
Dynamic and Equilibrium Studies on the sorption of Basic dye (Basic Brown 4) onto Multi-walled Carbon Nanotubes Prepared from Renewable Carbon Precursors
How to Make a Field invisible in Odoo 17Celine George
It is possible to hide or invisible some fields in odoo. Commonly using “invisible” attribute in the field definition to invisible the fields. This slide will show how to make a field invisible in odoo 17.
Welcome to TechSoup New Member Orientation and Q&A (May 2024).pdfTechSoup
In this webinar you will learn how your organization can access TechSoup's wide variety of product discount and donation programs. From hardware to software, we'll give you a tour of the tools available to help your nonprofit with productivity, collaboration, financial management, donor tracking, security, and more.
Synthetic Fiber Construction in lab .pptxPavel ( NSTU)
Synthetic fiber production is a fascinating and complex field that blends chemistry, engineering, and environmental science. By understanding these aspects, students can gain a comprehensive view of synthetic fiber production, its impact on society and the environment, and the potential for future innovations. Synthetic fibers play a crucial role in modern society, impacting various aspects of daily life, industry, and the environment. ynthetic fibers are integral to modern life, offering a range of benefits from cost-effectiveness and versatility to innovative applications and performance characteristics. While they pose environmental challenges, ongoing research and development aim to create more sustainable and eco-friendly alternatives. Understanding the importance of synthetic fibers helps in appreciating their role in the economy, industry, and daily life, while also emphasizing the need for sustainable practices and innovation.
How to Split Bills in the Odoo 17 POS ModuleCeline George
Bills have a main role in point of sale procedure. It will help to track sales, handling payments and giving receipts to customers. Bill splitting also has an important role in POS. For example, If some friends come together for dinner and if they want to divide the bill then it is possible by POS bill splitting. This slide will show how to split bills in odoo 17 POS.
Operation “Blue Star” is the only event in the history of Independent India where the state went into war with its own people. Even after about 40 years it is not clear if it was culmination of states anger over people of the region, a political game of power or start of dictatorial chapter in the democratic setup.
The people of Punjab felt alienated from main stream due to denial of their just demands during a long democratic struggle since independence. As it happen all over the word, it led to militant struggle with great loss of lives of military, police and civilian personnel. Killing of Indira Gandhi and massacre of innocent Sikhs in Delhi and other India cities was also associated with this movement.
Palestine last event orientationfvgnh .pptxRaedMohamed3
An EFL lesson about the current events in Palestine. It is intended to be for intermediate students who wish to increase their listening skills through a short lesson in power point.
Ethnobotany and Ethnopharmacology:
Ethnobotany in herbal drug evaluation,
Impact of Ethnobotany in traditional medicine,
New development in herbals,
Bio-prospecting tools for drug discovery,
Role of Ethnopharmacology in drug evaluation,
Reverse Pharmacology.
1. J Solid State Electrochem (2009) 13:1561–1566
DOI 10.1007/s10008-008-0730-0
ORIGINAL PAPER
Pt–Ru nanoparticles supported PAMAM dendrimer
functionalized carbon nanofiber composite catalysts
and their application to methanol oxidation
T. Maiyalagan
Received: 22 August 2008 / Revised: 6 October 2008 / Accepted: 4 November 2008 / Published online: 20 November 2008
# Springer-Verlag 2008
Abstract Polyamidoamine (PAMAM) dendrimers has
been anchored on functionalized carbon nanofibers (CNF)
and supported Pt–Ru nanoparticles have been prepared with
NaBH4 as a reducing agent. The samples were characterized by X-ray diffraction, scanning electron microscopy,
and transmission electron microscopy (TEM) analysis. It
was shown that Pt–Ru particles with small average size
(2.6 nm) were uniformly dispersed on PAMAM/CNF
composite support and displayed the characteristic diffraction
peaks of Pt face-centered cubic structure. The electrocatalytic
activities of the prepared-composites (20% Pt–Ru/PAMAMCNF) were examined by using cyclic voltammetry for
oxidation of methanol. The electrocatalytic activity of the
CNF-based composite (20% Pt–Ru/PAMAM-CNF) electrode
for methanol oxidation showed better performance than that
of commercially available Johnson Mathey 20% Pt–Ru/C
catalyst. The results imply that CNF-based PAMAM composite electrodes are excellent potential candidates for
application in direct methanol fuel cells.
Keywords Methanol oxidation . DMFC . Dendrimers .
Nanostructured materials . Electro-catalyst
Introduction
Fuel cells operate with the electrochemical oxidation of
hydrogen or methanol, as fuels at the anode and the
reduction of oxygen at the cathode are attractive power
T. Maiyalagan (*)
Department of Chemistry, School of Science and Humanities,
VIT University,
Vellore 632014, India
e-mail: maiyalagan@gmail.com
sources due to their high conversion efficiencies, low
pollution, light weight, and high power density. Methanol
offers the advantage of easy storage and transportation
when compared to hydrogen oxygen fuel cell, its energy
density (~2,000 Wh/kg) and operating cell voltage (0.4 V)
are lower than the theoretical energy density (~6,000 Wh/kg)
and the thermodynamic potential (~1.2 V) [1, 2]. However,
the fuel cells could not reach the stage of commercialization
due to the high cost, which is mainly associated with the
noble metal-loaded electrodes and the membrane. In order
to reduce the amount of Pt loading on the electrodes, there
have been considerable efforts to increase the dispersion of
the metal on the support. The catalyst is very often found to
disperse on a conventional carbon support, and the support
material influences the catalytic activity through metal
support interaction [3–5].
New novel carbon support materials such as graphite
nanofibers (GNFs) [6, 7], carbon nanotubes (CNT) [8–12],
carbon nanohorns [13], and carbon nanocoils [14] provide
alternate candidates of carbon support for fuel cell
applications. Bessel et al. [6] and Steigerwalt et al. [7]
used GNFs as supports for Pt and Pt–Ru alloy electrocatalysts. They have observed better activity for methanol
oxidation. The high electronic conductivity of GNF and the
specific crystallographic orientation of the metal particles
resulting from well-ordered GNF support are believed to be
the factors for the observed enhanced electro-catalytic
activity. In heterogeneous catalysis, one of the important
tasks is the determination of the number of active sites in
the catalyst. For a given catalyst, the number of active sites
present is responsible for the observed catalytic activity. A
considerable amount of research has been devoted toward
understanding the number of active sites and the role
played by the carrier of the supported catalysts. The most
efficient utilization of any supported catalyst depends on
2. 1562
the percentage of exposed or the dispersion of the active
component on the surface of the carrier material. Among
the various factors that influence the dispersion of an active
component, the nature of the support and the extent of the
active component loading are of considerable importance.
Without surface modification, most of the carbon nanomaterials lack sufficient binding sites for anchoring precursor
metal ions or metal nanoparticles, which usually lead to poor
dispersion and the aggregation of metal nanoparticles,
especially at high loading conditions. To introduce more
binding sites and surface anchoring groups, an acid oxidation
process was very frequently adopted to treat carbon nanomaterials in a mixed acid aqueous solution, which introduces
surface bound polar hydroxyl and carboxylic acid groups for
subsequent anchoring and reductive conversion of precursor
metal ions to metal nanoparticles [15].
Generally, metal nano-particles have been synthesized for
the purpose of increasing the catalytic surface area in
comparison to bulk metal and have utilized strategies such
as stabilization in a soluble polymer matrix or encapsulation
in dendrimers to protect them from aggregation. Dendrimers
are good candidates for preparing metal nanoparticles because
they can act as structurally and well-defined templates and
robust stabilizers. Polyamidoamine (PAMAM) dendrimers, in
particular, have been used as nanoreactors with effective
nanoparticle stabilization. In addition, encapsulated nanoparticles surfaces are accessible to substrates so that catalytic
reactions can be carried out [16–18].
PAMAM dendrimer encapsulated Pt nanoparticles and PtPd
bimetallic nanoaparticles are electrocatalytically active for
oxygen reduction [19–21]. Also dendrimer-encapsulated platinum nanoparticles supported on carbon fiber and nitrogendoped CNT as electrodes for oxygen reduction [22, 23].
In addition, platinum–ruthenium alloys are the best
catalysts for methanol oxidation direct methanol fuel cells
[24, 25]. PAMAM dendrimers were modified with a Nicyclam as novel electrocatalytic material for the electrochemical oxidation of methanol [26]. Kim et al. [27] have
reported the preparation of platinum–dendrimer hybrid
nanowires using alumina templates, which exhibited and
enhanced electro-catalytic activity toward methanol oxidation.
PAMAM dendrimer (PAMAM 4.5)-encapsulated Pt nanoparticles chemically linked to gold substrates through a
cystamine monolayer exhibited electrocatalytic activity toward
the oxidation of methanol [28].The terminal functional groups
of the dendrimers stabilizes metal nanoparticles without
aggregation. In this paper, we make use of the fourthgeneration amine-terminated PAMAM dendrimers (G4-NH2)
to anchor on the functionalized carbon nanofiber (CNF) as a
substrate and then encapsulate Pt–Ru nanoparticles on
dendrimers for the better dispersion of the electrode, which
exhibited very good catalytic activity. These materials are
characterized and studied, using X-ray diffraction (XRD),
J Solid State Electrochem (2009) 13:1561–1566
scanning electron microscopy (SEM), transmission electron
microscopy (TEM), and cyclic voltammetry. The electrochemical properties of the composite electrode (Pt–Ru–
PAMAM/CNF) were compared to those of the commercial
electrode (Pt–Ru/C), using cyclic voltammetry. The 20% Pt–
Ru–PAMAM/CNF exhibited excellent catalytic activity and
stability when compared to the 20 wt.% Pt–Ru/C.
Experimental
Materials
All the chemicals used are of analytical grade. CNFs (grade
PR 24 LHT) are commercially available from Pyrograf,
USA. 1-(3-Dimethyl-aminopropyl)-3-ethyl-carbodiimidehydrochloride (EDC), N-hydroxysuccinimide (NHS), hexachloroplatinic acid, and ruthenium (III) chloride hydrate are
procured from Sigma-Aldrich and used as received. Vulcan
XC-72 carbon black is purchased from Cabot. Methanol
and sulfuric acid are obtained from Fischer Chemicals.
Nafion 5 wt.% solution is obtained from Dupont and is
used as received. Fourth generation amine-terminated
polyamidoamine PAMAM dendrimers (G4-NH2) with the
highest available purity (10 wt.% in methanol) are obtained
from Aldrich and used without further purification.
Functionalization of CNF
The CNF is treated with mixed acid aqueous solution of
HNO3 and H2SO4 in 1:3 ratios under magnetic stirrer for
3 h. It is then washed with water and evaporated to dryness.
Preparation of CNF-PAMAM
Fifty milliliters of 0.1 mg/ml carboxylated CNF containing
100 mg of EDC and 100 mg of NHS is slowly added into a
methanol solution of 20% G4 PAMAM under high speed
agitating.
Preparation of Pt–Ru–PAMAM/CNF catalysts:
6.15 mM H2PtCl6 and 11.8mM RuCl3 and dendrimer
encapsulated CNF are mixed by keeping the solution under
magnetic stirrer for 3 h. Five milliliters of 0.1 M NaBH4 is
added to the solution and kept under evaporation. A
schematic of the detailed procedure for the electrocatalyst
preparation is shown in Fig. 1.
Characterization
The phases and lattice parameters of the catalyst are
characterized by XRD patterns employing Shimadzu XD-
3. J Solid State Electrochem (2009) 13:1561–1566
1563
Fig. 1 Schematic diagram
illustrating synthesis of Pt–Ru–
PAMAM/CNF
D1 diffractometer using Cu Kα radiation (λ=1.5418 Å)
operating at 40 kV and 48 mA. XRD samples are obtained
by depositing composite supported nanoparticles on a glass
slide and drying the latter in a vacuum overnight. The
scanning electron micrographs are obtained using JEOL
JSM-840 model, working at 15 keV. For TEM studies, the
composite dispersed in ethanol are placed on the copper
grid, and the images are obtained using JEOL JEM-3010
model, operating at 300 keV.
Electrochemical measurements
All electrochemical measurements are performed using a BAS
Epsilon potentiostat. A three-electrode cell is used, which
consisted of the glassy carbon (0.07 cm2) as working electrode
and Pt foil and Ag/AgCl (saturated by KCl solution)
electrodes as counter and reference electrodes, respectively,
are used. All the electrochemical experiments are carried out
at room temperature in 0.5 M H2SO4 electrolyte. The
electrolyte solution is purged with high pure nitrogen for
30 min prior to a series of voltammetric experiments.
centered cubic structure can be observed. X-ray scattering
from the CNF support is evidenced by the peak at 26° in
2θ. The diffraction peaks of the catalyst (Pt–Ru/C) are
observed to be sharp with a high intensity indicating high
crystallinity (Fig. 2a). On the contrary, very broad peaks
with weak intensity are observed for PAMAM containing
composites (Pt–Ru/PAMAM-CNF), indicating that they are
not fully crystalline in nature (Fig. 2 b) as observed for the
commercial Pt–Ru/C (JM) (Fig. 2a). Compared with Pt–
Ru/C, the peak intensities of Pt–RuPt–PAMAM/CNF are
lower and the full width at half-maximum (FWHM) for the
peaks are bigger. Bigger FWHM indicates a smaller
average size of metal nanoparticles on PAMAM/CNF
composite. No evidence of peaks related to Ru was found
in these catalysts. The absence of diffraction peaks typical
for Ru can be due to a number of reasons such as Ru not
being dissolved in the Pt lattice, that is, forming a PtRu
alloy and/or the Ru being present in the amorphous form, as
further discussed below [29, 30]. The position of the Pt
(111) peak for the larger (>1.2 nm) sized catalysts is shifted
C (002)
Preparation of the working electrode
Result and discussion
The crystal structures of the catalysts are examined by XRD
as shown in Fig. 2. Characteristic reflections of Pt face-
(a) 20% Pt-Ru-PAMAM/CNF
(b) 20% Pt-Ru/C
Pt (111)
Glassy carbon (GC) (Bas Electrode, 0.07 cm ) is polished to a
mirror finish with 0.05 μm alumina suspensions before each
experiment and served as an underlying substrate of the
working electrode. In order to prepare the composite electrode,
the catalysts are dispersed ultrasonically in water at a
concentration of 1 mg ml−1 and 20-μl aliquot is transferred
on to a polished GC substrate. After the evaporation of water,
the resulting thin catalyst film is covered with 5 wt.% Nafion
solution. Then, the electrode is dried at 353 K and used as the
working electrode. A solution of 1 M CH3OH in 0.5 M
H2SO4 is used to study the methanol oxidation activity.
Intensity (a.u)
2
(a)
(b)
10
20
30
40
50
60
70
2θ (degrees)
Fig. 2 XRD spectra of a Pt–Ru/C, b Pt–Ru–PAMAM/CNF
80
4. 1564
to higher 2θ positions than that for pure Pt that has a
maxima at 39.7645° [31].
The scanning electron micrograph images of commercial
CNFs are shown in Fig. 3a,b. The diameter of the
nanofibers is measured using a Leica Qwin Image Analyzer
and is found to be in the range of 260–250 nm and the
length of about 100 μm. Figure 3c shows the image of Pt–
(a)
(b)
J Solid State Electrochem (2009) 13:1561–1566
Ru–PAMAM/CNF. According to the EDX measurements
(Fig. 4), catalysts prepared in this work contained 20.1 wt.%
of total metal with a Pt/Ru atomic ratio of 1:1.0~1.1, which
agrees well with the stoichiometric ratio of 1:1 used in the
starting mixture.
The TEM image of the prepared Pt–Ru–PAMAM/CNF
catalysts, shown in Fig. 5, reveals that well-dispersed,
spherical particles were anchored onto the external walls of
PAMAM/CNF composite support with an average size of
2.6 nm. There is no agglomeration of Pt–Ru nanoparticles
in the composite, and the Pt–Ru nanoparticles were found
to be uniformly dispersed. In comparison, a commercial
Johnson Matthey Pt–Ru catalyst (20 wt.% on Vulcan) had
an average particle size of 3 nm. The uniform dispersion of
metal nanoparticles on PAMAM/CNF composite is clearly
due to the PAMAM dendrimer, which offers large and
uniform distributed nitrogen-active sites for anchoring
metal ions and metal nanoparticles. In this regard,
PAMAM-functionalized CNF composite are far more
effective supports than the conventional-acid-oxidized
CNF. The conventional-acid oxidation functionalization
leads to the structural damage of CNF, which causes a
large extent of loss in electrical conductivity and thus
potentially reduces the electrocatalytic activity of the
catalyst. The three-dimensional structure, smaller particle
size, and high dispersion of nanoparticles may result in
large valuable Pt surface area and good electrocatalytic
properties toward methanol oxidation.
The electrocatalytic activities for methanol oxidation of
Pt–Ru–PAMAM/CNF and commercial Pt–Ru/C electrocatalysts are analyzed by cyclic voltammetry in an
electrolyte of 0.5 M H2SO4 and 1 M CH3OH at 50 mV/s.
Figure 6 shows the cyclic voltammograms (CVs) of the
synthesized Pt–Ru–PAMAM/CNF and commercial Pt–Ru/C
catalysts in an electrolyte solution of 0.5 M H2SO4 and 1 M
CH3OH. There are two irreversible current peak during the
(c)
Fig. 3 SEM images of a, b CNF and c Pt–Ru–PAMAM/CNF
Fig. 4 EDX spectrum of Pt–Ru–PAMAM/CNF (PtRu 20.1 wt. %; Pt/
Ru=1:1.0~1.1)
5. J Solid State Electrochem (2009) 13:1561–1566
Fig. 5 TEM image of 20% Pt–Ru–PAMAM/CNF catalyst
electro-oxidation of methanol that are typically attributed
on the forward scan peak at around 0.8 V to methanol
electro-oxidation and on the backward peak at 0.6 V to the
faradic oxidation reaction on the Pt of the residual
intermediate species. Both CV curves reveal a similar
shape and peak position, which is also in good agreement
with previous reports for methanol CVs over supported Pt
catalysts. The Pt–Ru–PAMAM/CNF composite shows
higher electrocatalytic activity of methanol oxidation
compared to Pt–Ru/C (JM) catalyst. The enhanced catalytic
activity of Pt–Ru/PAMAM–CNF composite catalyst is due
to higher dispersion of Pt–Ru nanoparticles and may be
better oxidation of CO intermediates during methanol
oxidation [32, 33].
The ratio of the forward anodic peak current (If) to the
reverse anodic peak current (Ib) can be used to describe the
catalyst tolerance to accumulation of carbonaceous species
1565
[34–38]. A higher ratio indicates more effective removal of
the poisoning species on the catalyst surface. The If/Ib ratios
of Pt–Ru–PAMAM/CNF and Pt–Ru/C are 1.36 and 0.87,
respectively, showing better catalyst tolerance of PAMAM/
CNF composites. There is no much decrease in electrocatalytic activity of the Pt–Ru–PAMAM/CNF composite
catalysts on subsequent cycles of methanol oxidation
compared to the Pt–Ru/C catalysts. This not only demonstrates the reproducibility of the results but also the stability
of the nanoparticles on the PAMAM/CNF composite
catalysts.
Similarly, Fig. 7 shows the chronoamperometric studies
of the synthesized sample, which reveals the stability of the
Pt–Ru–PAMAM/CNF catalyst toward the methanol electrooxidation. The results are consistent with the view that
PAMAM is not only stabilizing the Pt–Ru nanoparticles but
is also enhancing the methanol oxidation currents under
chronoamperometric conditions. Pt–Ru nanoparticles are
well stabilized by amine-terminated PAMAM dendrimers.
The high electrocatalytic activity of the Pt–Ru–PAMAM/
CNF composite electrodes prepared in this work is most
probably due to the very high dispersion of PtRu particles
and the extensive presence of RuOxHy.
Conclusions
In summary, well-dispersed Pt–Ru nanoparticles have been
synthesized on PAMAM–CNFs composite. The choice of
the PAMAM G4-NH2 dendrimer template and terminal
amine functional groups provides for uniform preparation
of size monodisperse catalysts and facilitates the controlled
dispersion. The enhancements in activity and stability over
Pt–Ru/PAMAM–CNF catalyst have been solely attributed
to high dispersion Pt–Ru nanoparticles on the composite.
0.040
(a) 20% Pt-Ru-PAMAM/CNF
Current (A)
0.035
(b) 20% Pt-Ru/C
0.030
0.025
0.020
0.015
(a)
0.010
(b)
0.005
0.000
0
500
1000
1500
2000
2500
3000
3500
Time (s)
Fig. 6 Cyclic voltammogram of a Pt–Ru–PAMAM/CNF and b Pt–
Ru/C in electrolyte solution of 0.5 M H2SO4 with 1 M CH3OH at a
sweep rate of 50 mV/S at room temperature
Fig. 7 Chronoamperometry of a Pt–Ru–PAMAM/CNF, b Pt–Ru/C
polarized at +0.6 V in 0.5 M H2SO4/1 M CH3OH
6. 1566
These findings suggest that Pt–Ru–PAMAM/CNF should
be considered a good electrocatalyst material for direct
methanol fuel cells. Though more work is needed to
understand the fundamentals of the interaction between
metal nanoparticles and dendrimers, particularly Pt–Ru–
PAMAM/CNF, they show a potential as new electrocatalysts for low temperature fuel cells.
References
1. McNicol BD, Rand DAJ, Williams KR (2001) J Power Sources
83:47 doi:10.1016/S0378-7753(01)00882-5
2. Carrette L, Friedrich KA, Stimming U (2001) Fuel Cells (Weinh) 1:5
doi:10.1002/1615-6854(200105)1:1<5::AID-FUCE5>3.0.CO;2-G
3. Uchida M, Aoyama Y, Tanabe N, Yanagihara N, Eda N, Ohta A
(1995) J Electrochem Soc 142:2572 doi:10.1149/1.2050055
4. Antolini E (2007) Appl Catal B Enviromental 724:324
doi:10.1016/j.apcatb.2007.03.002
5. Matsumoto T, Komatsu T, Arai K, Yamazaki T, Kijima M,
Shimizu H, Takasawa Y, Nakamura J (2004) Chem Commun
7:840 doi:10.1039/b400607k
6. Bessel CA, Laubernds K, Rodriguez NM, Baker RTK (2001) J
Phys Chem B 105:1115 doi:10.1021/jp003280d
7. Steigerwalt ES, Deluga GA, Lukehart CM (2002) J Phys Chem B
106:760 doi:10.1021/jp012707t
8. Li WZ, Liang CH, Zhou WJ, Xin Q (2003) J Phys Chem B
107:6292 doi:10.1021/jp022505c
9. Kim C, Kim YJ, Kim YA, Yanagisawam T, Park KC, Endo M,
Dresselhaus MS (2004) J Appl Phys 96:5903 doi:10.1063/1.1804242
10. Wang C, Waje M, Wang X, Tang JM, Haddon RC, Yan YS (2004)
Nano Lett 4:345 doi:10.1021/nl034952p
11. Maiyalagan T (2008) Appl Catal B Enviromental 89:286
doi:10.1016/j.apcatb.2007.11.033
12. Maiyalagan T, Viswanathan B, Varadaraju UV (2005) Electrochem Commun 7:905 doi:10.1016/j.elecom.2005.07.007
13. Yoshitake T, Shimakawa Y, Kuroshima S, Kimura H, Ichihashi T, Kubo
Y (2002) Physica B 323:124 doi:10.1016/S0921-4526(02)00871-2
14. Hyeon T, Han S, Sung YE, Park KW, Kim YW (2003) Angew
Chem Int Ed 42:4352 doi:10.1002/anie.200250856
15. Yu RQ, Chen LW, Liu QP (1998) Chem Mater 10:718
doi:10.1021/cm970364z
16. Knecht MR, Wright DW (2004) Chem Mater 16:4890
doi:10.1021/cm049058t
J Solid State Electrochem (2009) 13:1561–1566
17. Zhao MQ, Crooks RM (1999) Adv Mater 11:217 doi:10.1002/(SICI)
1521-4095(199903)11:3<217::AID-ADMA217>3.0.CO;2-7
18. Zhao MQ, Crooks RM (1999) Chem Mater 11:3379 doi:10.1021/
cm990435p
19. Ye H, Crooks RM (2005) J Am Chem Soc 127:4930 doi:10.1021/
ja0435900
20. Zhao M, Crooks RM (1999) Adv Mater 11:217 doi:10.1002/(SICI)
1521-4095(199903)11:3<217::AID-ADMA217>3.0.CO;2-7
21. Ye H, Crooks RM (2007) J Am Chem Soc 129:3627
22. Ledesma-Garci J, Escalante Garci IL, Rodri FJ, Chapman TW,
Godinez LA (2008) J Appl Electrochem 38:515 doi:10.1007/
s10800-007-9466-2
23. Vijayaraghavan G, Stevenson KJ (2007) Langmuir 23:5279
doi:10.1021/la0637263
24. Wasmus S, Küver A (1999) J Electroanal Chem 461:14
doi:10.1016/S0022-0728(98)00197-1
25. Gasteiger HA, Markovic N, Ross PN, Cairns EJ (1994) J Phys
Chem 98:617 doi:10.1021/j100053a042
26. Gonzalez-Fuentes MA, Manrıquez J, Gutierrez-Granados S,
Alatorre-Ordaz A, Godınez LA (2005) Chem Commun 8:898
doi:10.1039/b412442a
27. Kim JW, Choi E-A, Park S-M (2003) J Electrochem Soc 150:
E202 doi:10.1149/1.1554727
28. Raghu S, Nirmal RG, Mathiyarasu J, Berchmans S, Phani KLN,
Yegnaraman V (2007) Catal Lett 119:40 doi:10.1007/s10562-0079154-1
29. Wang DL, Zhuang L, Lu JT (2007) J Phys Chem C 111:16416
doi:10.1021/jp073062l
30. Guo JS, Sun GQ, Sun SG, Yan SY, Yang WQ, Qi J, Yan YS, Xin Q
(2007) J Power Sources 168:299 doi:10.1016/j.jpowsour.2007.02.085
31. Bock C, Paquet C, Couillard M, Botton GA, MacDougall B
(2004) J Am Chem Soc 126:8028 doi:10.1021/ja0495819
32. Jarvi TD, Stuve EM (1998) In: Lipkowski J, Ross PN (eds)
Electrocatalysis, frontiers of electrochemistry series, Chapter 3.
Wiley-VCH, New York, pp 75–153
33. Mukerjee S, McBreen J (1998) J Electroanal Chem 448:163
doi:10.1016/S0022-0728(97)00018-1
34. Mu Y, Liang H, Hu J, Jiang L, Wan L (2005) J Phys Chem B
109:22212 doi:10.1021/jp0555448
35. Manoharan R, Goodenough JB (1992) J Mater Chem 2:875
doi:10.1039/jm9920200875
36. Liu Z, Ling XY, Su X, Lee JY (2004) J Phys Chem B 108:8234
doi:10.1021/jp049422b
37. Deivaraj TC, Lee JY (2005) J Power Sources 142:43 doi:10.1016/
j.jpowsour.2004.10.010