4. cercon base cercon ceram KISS
It can do everything
The extra class:
Cercon is an all-round material.
The high-performace ceramic, ziconium
oxide has already been in use for along
time - in diverse applications such as the
Space Shuttle, Porsche cars
7. Cercon Base
ZrO2 (Zirconium Oxide)
94%
Y2
O3
(Yttrium Oxide)
5%
HfO2
(Hafnium Oxide)
<0.8%
Aluminium Oxide
<0.2%
Bases come in white or shaded
color
Cercon Base
9. In-Ceram Alumina Crowns/3 Unit 0,7 mm „as thick as
possible“
anterior bridges
In-Ceram Zirkonia Crowns/3 Unit bridges 0,7 mm 5 x 5
mm2
Procera Crowns 0,6 mm -
cercon Crowns/Bridges 0,5 mm 3 x 3 mm2
Occlusal wall
thickness
Indication
Dental Ceramics used in CAD/CAM Systems
ConnectorsProduct
10. High strength through very small grains
High-Performance Structural Ceramics
(Zirconium Oxide, ZrO2)
17. cercon Models must be aligned and
surveyed for proper path of
Insertion
Surveyor
Analyzing
Rod
Represents
What the
Laser can
See at Any
Given point
21. To control the right fitting of the modellation in the
scanning frame use the scanning pattern
22. Inserting the scanning frame into the parallelometerRemove all unnecessary parts off the modelLower scanning frame over the wax modellationSetting wax sticksFix the wax modellation to the scanning frameRemove modellation from the model
25. operating instruction Cercon brain / CAM
Scanning and milling time:
Cercon base12 30 min
Cercon base30 50 min
Cercon base38 65 min
Cercon base47 90min
• course mill:
2,8 mm Ø
• fine mill:
1,0 mm Ø
26.
27. separating the frame work
• the not sintered
material shows a
chalky consistence
• first the frame-
work has to be
separated from
the frame
• therefore sandblasting with
50 µm Al2O3 with 1 bar
pressure has to be applied
onto the gates
30. Product presentation
This and more is possible with CAD
More rapid digitization
More rapid modeling
Adjustable cement gap
Faster and better milling
(new strategy)
More economical use of
blanks (Nesting)
36. Units are place in the Cercon Heat. The
temperature goes up to 13500
C and holds
for 2 hours.
• Put the crown or the framework
with the occlusal side on the
furnace tile.
• Push the start button and the
sintering process begins.
• After 6.5 hours the shrinking
process is done.
43. Kiss: five advantages !
- optimum shade harmony
- easy and fast processing
- only 73 powders for all solutions
- efficient full-assortment
- extrem reliable
44. Economic efficiency :
• Reduced assortment.
• paste opaque or powder opaque
availible
• Fast firing cycles due to higher
heating rate.
• No long term cooling in combination
with concept alloys.
• Time saving during layering due to
the 3 powders layering technique.
• Low investment for the Lab due to
the small assortment and
good reasons for using Kiss
45. Minimum costs – maximum aesthetics.