This document analyzes quantitative X-ray absorption and emission spectroscopic data to understand the electronic structures of Cu2S and CuS. It finds that Cu2S has a significant amount of Cu2+ sites and some Cu0 centers, which contributes to its electrical conductivity. CuS is shown to have tetrahedral Cu2+ and trigonal Cu1+ sites arranged in crystal planes with alternating charge densities, which may enable its photoluminescence properties. A quantitative molecular orbital approach is able to solve the complicated electronic structures of these materials and correlate them to important physical properties.
This document describes a room temperature method for precisely controlling the composition of copper sulfide materials. Copper(I) sulfide (Cu2S) is first synthesized by dissolving a copper-thiourea precursor in ethylenediamine. The Cu2S is then subjected to controlled chemical oxidation using iodine solutions, allowing the precise synthesis of copper-deficient copper sulfides (Cu2-xS) where x = 0.2, 0.25, 0.88, 1.0. The compositions are characterized using techniques such as powder X-ray diffraction and Raman spectroscopy. This elegant low-temperature approach provides a way to access the range of compositions within the copper-sulfur system for applications
This document describes the room temperature synthesis of copper sulfide (Cu9S5), copper selenide (CuSe), lead sulfide (PbS), and lead selenide (PbSe) by reacting the elemental powders in 2-mercaptoethanol solvent for 24 hours. Characterization by powder X-ray diffraction and Raman spectroscopy showed the products were highly crystalline. Reactions in ethylene glycol also yielded copper sulfide and lead sulfide but reactions in dimercaptoethane did not yield metal chalcogenides. This solvent-mediated room temperature synthesis provides a simple method for producing these metal chalcogenide materials.
This document summarizes research on synthesizing copper sulfide compounds Cu1.8S and CuS from copper-thiourea precursors containing different counteranions (Cl-, NO3-, SO42-). When reacted in ethylene glycol, [Cu4(tu)9](NO3)4 always yielded CuS regardless of conditions. [Cu(tu)3]Cl yielded only Cu1.8S in air or argon, but a mixture of Cu1.8S and CuS under solvothermal conditions. [Cu2(tu)6]SO4 produced a mixture of CuS and Cu1.8S under all conditions tested. The counteranion's oxidizing power
This document describes a one-pot synthesis of wurtzite and chalcopyrite CuFeS2 nanoparticles using a copper thiourea complex and different iron salts. Reactng the copper complex with iron(II) sulfate produces wurtzite CuFeS2, while reacting with iron(III) chloride produces chalcopyrite CuFeS2. Both phases were characterized using techniques like XRD, SEM, TEM, Raman spectroscopy, UV-Vis spectroscopy, and PL spectroscopy. This synthesis allows control over the crystal structure produced and provides phases with potential for tuning optoelectronic and magnetic properties.
This document summarizes the synthesis of zincblende CuInS2 and iron-substituted CuInS2 by reacting colloidal suspensions of binary Cu-S and In-S in ethyleneglycol. Characterization with techniques such as XRD, TEM, UV-Vis and Raman spectroscopy confirmed the formation of phase pure zincblende CuInS2. Following this, quaternary Cu-In-Fe-S with zincblende structure was also synthesized by including iron in the reaction. While zincblende CuInS2 degraded methylene blue dye under visible light, the iron-substituted sample did not show appreciable degradation.
This document summarizes the one-pot synthesis of wurtzite CuInS2 (CIS) using copper-thiourea precursors and indium salts in ethylene glycol. Reactions involving indium sulfate produced high yields of metastable wurtzite and zincblende CIS phases, while reactions with indium acetate were sluggish and produced low yields. Doping studies with non-magnetic gallium and magnetic iron ions were also examined. Gallium-doped CIS samples showed both wurtzite and chalcopyrite phases, while iron-doping resulted in cubic or tetragonal crystal structures depending on conditions. Introduction of iron also produced paramagnetic behavior and photolum
This study examines dissociation pathways in the dication of the amino acid cysteine after site-selective core ionization of the O 1s, N 1s, C 1s, and S 2p orbitals. A photoelectron-ion-ion coincidence experiment was performed. Several dissociation channels were identified, some showing strong site-selective dependence attributed to a combination of nuclear motion in the core-ionized state and Auger processes populating different electronic states in the dication. Fragmentation patterns were analyzed at each core ionization level to determine dissociation pathways and kinetic energy release partitioning between fragments through regression slope analysis.
1) The study investigated the effect of adding zirconium oxide nanoparticles to carbon black electrode materials on surface morphology and electrochemical performance.
2) Scanning electron microscopy showed that adding nanoparticles partially filled gaps between carbon black particles, increasing the specific surface area available for charge storage.
3) Electrochemical analysis found that increasing nanoparticle content initially increased total charge storage due to higher surface area and pseudocapacitive charge storage, but further increases reduced performance due to higher electrode resistance.
This document describes a room temperature method for precisely controlling the composition of copper sulfide materials. Copper(I) sulfide (Cu2S) is first synthesized by dissolving a copper-thiourea precursor in ethylenediamine. The Cu2S is then subjected to controlled chemical oxidation using iodine solutions, allowing the precise synthesis of copper-deficient copper sulfides (Cu2-xS) where x = 0.2, 0.25, 0.88, 1.0. The compositions are characterized using techniques such as powder X-ray diffraction and Raman spectroscopy. This elegant low-temperature approach provides a way to access the range of compositions within the copper-sulfur system for applications
This document describes the room temperature synthesis of copper sulfide (Cu9S5), copper selenide (CuSe), lead sulfide (PbS), and lead selenide (PbSe) by reacting the elemental powders in 2-mercaptoethanol solvent for 24 hours. Characterization by powder X-ray diffraction and Raman spectroscopy showed the products were highly crystalline. Reactions in ethylene glycol also yielded copper sulfide and lead sulfide but reactions in dimercaptoethane did not yield metal chalcogenides. This solvent-mediated room temperature synthesis provides a simple method for producing these metal chalcogenide materials.
This document summarizes research on synthesizing copper sulfide compounds Cu1.8S and CuS from copper-thiourea precursors containing different counteranions (Cl-, NO3-, SO42-). When reacted in ethylene glycol, [Cu4(tu)9](NO3)4 always yielded CuS regardless of conditions. [Cu(tu)3]Cl yielded only Cu1.8S in air or argon, but a mixture of Cu1.8S and CuS under solvothermal conditions. [Cu2(tu)6]SO4 produced a mixture of CuS and Cu1.8S under all conditions tested. The counteranion's oxidizing power
This document describes a one-pot synthesis of wurtzite and chalcopyrite CuFeS2 nanoparticles using a copper thiourea complex and different iron salts. Reactng the copper complex with iron(II) sulfate produces wurtzite CuFeS2, while reacting with iron(III) chloride produces chalcopyrite CuFeS2. Both phases were characterized using techniques like XRD, SEM, TEM, Raman spectroscopy, UV-Vis spectroscopy, and PL spectroscopy. This synthesis allows control over the crystal structure produced and provides phases with potential for tuning optoelectronic and magnetic properties.
This document summarizes the synthesis of zincblende CuInS2 and iron-substituted CuInS2 by reacting colloidal suspensions of binary Cu-S and In-S in ethyleneglycol. Characterization with techniques such as XRD, TEM, UV-Vis and Raman spectroscopy confirmed the formation of phase pure zincblende CuInS2. Following this, quaternary Cu-In-Fe-S with zincblende structure was also synthesized by including iron in the reaction. While zincblende CuInS2 degraded methylene blue dye under visible light, the iron-substituted sample did not show appreciable degradation.
This document summarizes the one-pot synthesis of wurtzite CuInS2 (CIS) using copper-thiourea precursors and indium salts in ethylene glycol. Reactions involving indium sulfate produced high yields of metastable wurtzite and zincblende CIS phases, while reactions with indium acetate were sluggish and produced low yields. Doping studies with non-magnetic gallium and magnetic iron ions were also examined. Gallium-doped CIS samples showed both wurtzite and chalcopyrite phases, while iron-doping resulted in cubic or tetragonal crystal structures depending on conditions. Introduction of iron also produced paramagnetic behavior and photolum
This study examines dissociation pathways in the dication of the amino acid cysteine after site-selective core ionization of the O 1s, N 1s, C 1s, and S 2p orbitals. A photoelectron-ion-ion coincidence experiment was performed. Several dissociation channels were identified, some showing strong site-selective dependence attributed to a combination of nuclear motion in the core-ionized state and Auger processes populating different electronic states in the dication. Fragmentation patterns were analyzed at each core ionization level to determine dissociation pathways and kinetic energy release partitioning between fragments through regression slope analysis.
1) The study investigated the effect of adding zirconium oxide nanoparticles to carbon black electrode materials on surface morphology and electrochemical performance.
2) Scanning electron microscopy showed that adding nanoparticles partially filled gaps between carbon black particles, increasing the specific surface area available for charge storage.
3) Electrochemical analysis found that increasing nanoparticle content initially increased total charge storage due to higher surface area and pseudocapacitive charge storage, but further increases reduced performance due to higher electrode resistance.
This document describes the preparation and analysis of mesoporous microspheres of nickel oxide (NiO) for use as a pseudocapacitor material. Mesoporous α-Ni(OH)2 microspheres were first synthesized via a hydrothermal method, then calcined at different temperatures between 250-500°C to produce NiO microspheres. The 250°C NiO sample exhibited the highest specific surface area of 295 m2/g and highest specific capacitance of 1,140 F/g. Characterization of the materials showed the pseudocapacitive behavior was more evident for NiO prepared at higher calcination temperatures. The high surface area and mesoporous structure of the 250°C
1. A 2D coordination polymer was synthesized using cobalt trimers and the flexible ligand cis,cis-cyclohexane-1,3,5-tricarboxylate.
2. Single crystal X-ray diffraction shows the complex forms a 2D framework with channels and contains trinuclear cobalt secondary building units linked by the ligand.
3. Magnetic characterization reveals spin-canting ferromagnetic behavior at low temperatures based on AC susceptibility measurements. Gas adsorption experiments also show selectivity for CO2 over N2.
Study the effect of Mn2+ ions on the ac electrical properties of some iron do...IJRES Journal
Oxide glasses doped with transition metal ions are of high interest because of their variant applications in both science and technology fields. However, the normal melt quench method have used to prepared some iron doped phosphate glasses according the following molecular formula: (65-x) mol% P2O5 - 20 mol% Na2O - 15 mol% Fe2O3 - x mol% MnO, Where x= 0, 5,10, 20, 25. The room temperature Mössbauer Effect ME Spectra used to characterized the glassy state homogeneity of these glasses. ME spectra show, for all glasses, no magnetic field participate which mean good glassy state formation. The ac electrical transport properties were also measured, as function of temperature up to 500k. It was found that the ac conductivity increased with the gradual increase of Mn2+ cations, while the electrical activation energy decreased.
This document describes research on fabricating a novel graphene electrode embedded with zirconium dioxide nanoparticles for electrochemical capacitors. The electrode showed a maximum specific capacitance of 11.84 F g−1. SEM images showed ions redepositing as agglomerates on the electrode surface after one charge/discharge cycle, accompanied by a decrease in surface area. Electrochemical tests confirmed pseudocapacitive behavior and low resistance. The research aims to investigate how electrolyte ion and active material redeposition affects the electrode's charge distribution ability.
1) The document investigates the effect of cation and anion sizes on the charge storage capabilities of graphite nanosheets as electrode materials for electrochemical double layer capacitors.
2) Scanning electron microscope images confirm the layered structure of the graphite nanosheets used, which are 12nm thick with 3.36 Angstrom spacing between layers.
3) Electrochemical measurements using cyclic voltammetry and impedance spectroscopy indicate that the graphite electrodes exhibited better charge storage and delivery in 3M NaCl electrolyte compared to NaOH and KOH electrolytes, due to the smaller ion sizes matching better with the graphite structure.
The document describes the design and application of powder composite electrodes made of Cu, Co, Ni, Pt and Ir for use in electrosynthesis and electroanalysis in alkaline solutions. The electrodes were prepared by mixing 95% metal powder with 5% polyvinyl chloride binder. Characterization showed the electrodes had a rough, porous surface and good electrochemical stability, with higher current densities than metal sheet electrodes. Cyclic voltammetry testing demonstrated the composite electrodes had good stability over multiple cycles for electrooxidation reactions like ethanol oxidation in KOH solution. The composite electrodes are suitable for electrochemistry research applications requiring stable, conductive electrodes.
Vacancy and Copper-doping Effect on Superconductivity for Clathrate MaterialsYang Li
This document summarizes a study on the effects of vacancy and copper doping on superconductivity in clathrate materials. Key findings include:
1) Copper doping of Ba8Si46 decreases the superconducting critical temperature strongly as copper content increases. Theoretical simulations also show copper doping decreases electronic density of states at the Fermi level.
2) Comparison of Ba8Ge46 and Ba8Si46 using theoretical simulations found their electronic structures are very similar, suggesting superconductivity is intrinsic to fully occupied silicon and germanium clathrates.
3) The absence of superconductivity in most germanium clathrates is suggested to arise from vacancy defects which result in
Microstructural and Dielectric Characterization of Sr doped Ba(Fe0.5Ta0.5)O3 ...theijes
Solid state reaction method was used to synthesize Ba1-xSrx(Fe0.5Ta0.5)O3 ceramic(x=0, 0.1, 0.2, 0.3, 0.4 and 0.5). The raw materials of making Sr doped Ba(Fe0.5Ta0.5)O3 were BaCO3, SrCO3, Fe2O3, Ta2O5 (purity better than 99%). Pellet and ring shaped samples prepared from each composition were sintered at 1400 and 1450ºC for 5 hour. The phase formation of Ba1-xSrx(Fe0.5Ta0.5)O3 was checked using X-ray diffraction (XRD) technique and observed a cubic perovskite crystal structure in space group Pm3m (221). Microstructure of the individual compound was examined by the field emission scanning electron micrograph (FESEM). Grain size was found to be varied with Sr content. The lattice parameter decreased with increasing Sr content. Dielectric spectroscopy was applied to investigate the electrical properties of BSFT at room temperature and in a frequency range of 100Hz–100 MHz. An analysis of the dielectric constant εʹ and loss tangent tan with frequency was performed assuming a distribution of relaxation times. The low frequency dielectric dispersion corresponds to the DC electrical conductivity.
Superconductivity in Gallium-substituted Ba8Si46 ClathratesYang Li
We report a joint experimental and theoretical investigation of superconductivity in Ga-substituted type-I silicon clathrates. We prepared samples of the general formula Ba8Si46−xGax, with different values of x. We show that Ba8Si40Ga6 is a bulk superconductor, with an onset at TC=3.3 K. For x=10 and higher, no superconductivity was observed down to T=1.8 K. This represents a strong suppression of superconductivity with increasing Ga content, compared to Ba8Si46 with TC=8 K. Suppression of superconductivity can be attributed primarily to a decrease in the density of states at the Fermi level, caused by a reduced integrity of the sp3-hybridized networks as well as the lowering of carrier concentration. These results are corroborated by first-principles calculations, which show that Ga substitution results in a large decrease of the electronic density of states at the Fermi level, which explains the decreased superconducting critical temperature within the BCS framework. To further characterize the superconducting state, we carried out magnetic measurements showing Ba8Si40Ga6 to be a type-II superconductor. The critical magnetic fields were measured to be Hc1=35 Oe and Hc2=8.5 kOe.We deduce the London penetration depth 3700 Å and the coherence length 200 Å. Our estimate of the electron-phonon coupling reveals that Ba8Si40Ga6 is a moderate phonon-mediated BCS superconductor.
THE UTILISATION OF 2-D RESISTIVITY AND INDUCED POLARIZATION (IP) METHODKasdi Nata Sujono
The document summarizes a study that used 2-D resistivity and induced polarization (IP) methods to determine iron ore bodies at Kampung Melaka, Kuala Lipis, Pahang, Malaysia. Three survey lines totaling 600 meters were divided into lots of 200 meters each. The 2-D resistivity method identified iron ore by its low resistivity, while IP differentiated iron ore and groundwater. Results showed iron ore underlying the surface from 5-30 meters was mostly located in lots 1 and 2 based on their low resistivity. Lot 1 contained 20-25% iron ore, lot 2 contained 30-35% iron ore, and lot 3 contained 15-20% iron ore over each 200-meter
This document discusses evidence for a possible shape transition from prolate to oblate in neutron-rich ruthenium isotopes based on spectroscopy experiments of 109,110,111,112Ru nuclei. The experiments extended existing level schemes to higher spin and excitation energy, allowing observation of band crossings. A band crossing was observed in 111Ru at a similar rotational frequency as the second band crossing in 112Ru, suggesting the alignment of proton g9/2 pairs and a triaxial to oblate shape transition in 111Ru. Comparisons are made to cranked shell model predictions to help interpret the results.
1) Low-lying excited states of the neutron-rich calcium isotopes 48-52Ca have been studied using gamma-ray spectroscopy following inverse kinematics proton scattering experiments.
2) The energies and strengths of the octupole states in these calcium isotopes are remarkably constant, indicating that these states are dominated by proton excitations of the calcium cores.
3) Specific excited states in 49,51,52Ca were analyzed, and spin and parity assignments were made or supported based on comparisons to previous reaction data and theoretical expectations.
Mass spectrometry is a versatile analytical technique used to characterize molecules through determination of molecular weight, elemental composition, and presence of functional groups. It is used for mechanistic studies of gas-phase ion chemistry, as a detector coupled to chromatography instruments, and integrated into vacuum systems. Mass spectrometry involves the steps of sample introduction, ionization, mass analysis, and ion detection/data analysis.
Surface Activation of C-sp3 in Boron-Doped Diamond ElectrodeAlejandro Medel
Abstract C-sp2 (graphite) impurities are undesirable in synthetic diamond electrodes (C-sp3), because they can affect the electrochemical response. In this work, we demonstrate that Csp3 surfaces can be activated successfully by applying an anodic current density corresponding to sufficiently high potential where the hydroxyl radicals (●OH) are generated. The
effectiveness of this activation process was verified by Raman spectroscopy, X-ray diffraction, scanning electron microscopy, and cyclic voltammetry.
Computational Study on the Effect of Axial Ligation Upon the Electronic Struc...Roxana Kincses
This document describes a computational study examining the effect of different axial ligands on the electronic structure of copper(II) porphyrinate complexes. Density functional theory was used to model complexes with nitrite, imidazole, phenol, and water ligands. The results show that axial ligands influence the copper spin density and delocalization in the complex. Ligands like nitrite and phenolate induce more spin delocalization compared to neutral ligands like water and phenol. The strength of axial bonding also varies, with ionic ligands forming stronger bonds than neutral ones involved in hydrogen bonding. This variation in electronic structure induced by different axial ligands could explain changes seen in experimental electron paramagnetic resonance spectra of related complexes.
Reduction of cu o and cu2o with h2 h embedding and kinetics effects in the ...Luciana Pirone
This document summarizes a study that used time-resolved X-ray diffraction, X-ray absorption fine structure spectroscopy, and density functional theory calculations to investigate the reduction of CuO and Cu2O with hydrogen gas. The main findings were:
1) CuO reduces directly to metallic copper without forming intermediate copper suboxides like Cu4O3 or Cu2O under normal hydrogen flow rates.
2) The reduction of CuO is easier than the reduction of Cu2O, with apparent activation energies of 14.5 kcal/mol and 27.4 kcal/mol, respectively.
3) During CuO reduction, the system can reach metastable states and react with hydrogen instead of
The document summarizes a study that demonstrated the ability to tune the size of large-diameter, few-walled nitrogen-doped carbon nanotubes (N-CNTs) from 50-150 nm by varying the transition metal (TM) used during synthesis. Fe produced the largest tubes, followed by Co and Ni, while Mn resulted in a clot-like morphology. Electrocatalytic activity for the oxygen reduction reaction (ORR) followed the trend Fe > Co > Ni > Mn. Fe-derived N-CNTs exhibited the highest surface area and nitrogen incorporation, contributing to their high ORR activity. This work provides a new route for developing advanced nonprecious metal catalysts by controlling carbon nanot
A simple simulation model for oxidative coupling of methaneAlexander Decker
This document describes a study that developed a mathematical model to simulate the oxidative coupling of methane over a La0.6Sr0.4NiO3 perovskite catalyst. The catalyst was prepared using a reverse microemulsion method and characterized using various techniques. Rate equations were developed based on previous studies of similar catalysts. The model can predict that at temperatures of 925°C or higher, with a methane partial pressure of 0.3 and oxygen partial pressure of 0.1, the catalyst will reach around 10% methane conversion and 50% selectivity to C2+ hydrocarbons.
Critical magnetic fields of superconducting aluminum-substituted Ba8Si42Al4 c...Yang Li
This document summarizes a study of the critical magnetic fields of the superconducting aluminum-substituted clathrate Ba8Si42Al4. Key findings include:
1) For the sample Ba8Si42Al4, the critical magnetic fields were measured to be HC1 = 40.2 Oe and HC2 = 66.4 kOe.
2) The London penetration depth was calculated to be 4360 Å and the coherence length was 70 Å.
3) The estimated Ginzburg–Landau parameter of j = 62 revealed that Ba8Si42Al4 is a strong type-II superconductor.
This document discusses theoretical and experimental studies on viologen-containing 1,1'-binaphthyls as potential near-infrared chiroptically switching materials. Theoretical modeling was used to correlate chiroptical properties with molecular geometry, showing maximal properties for a twisting angle of 60° and interchromophoric distance of 3.9 nm. Two chiral molecules containing viologen groups attached to a 1,1'-binaphthyl core through short spacers were synthesized and showed strong circular dichroism bands in the visible and near-infrared regions upon electrochemical reduction, demonstrating their potential as chiroptical switches. The cyclic molecule showed stronger chiroptical properties than the open-ring analogue.
Temperature Dependence of the Band-Edge Transitions of ZnCdBeSeOleg Maksimov
This study characterized the temperature dependence of band-edge transitions in three ZnCdBeSe films with varying concentrations of beryllium (Be) using contactless electroreflectance (CER) and piezoreflectance (PzR) measurements from 15-450K. The CER and PzR spectra showed doublet features near the band edge, indicating light-hole and heavy-hole excitonic transitions. Comparing the relative intensities of the PzR and CER spectra allowed identification of the transitions. Analysis of the temperature dependence provided information on how the energy and broadening of the transitions varied with temperature and Be concentration. The results showed that incorporating Be effectively reduced the rate of temperature variation of the energy
Amorphous-nano-crystalline silicon composite thin films (a-nc-Si:H) samples were synthesized by
Plasma Enhanced Chemical Vapor Deposition technique. The measurement of DC conductivities was
accomplished using Dielectric spectroscopy (Impedance Spectroscopy) in wide frequency and temperature range.
In analysis of impedance data, two approaches were tested: the Debye type equivalent circuit with two parallel R
and CPEs (constant phase elements) and modified one, with tree parallel R and CPEs including crystal grain
boundary effects. It was found that the later better fits to experimental results properly describes crystal grains
dielectric effect and hydrogen concentration indicating presence of strain. The amorphous matrix showed larger
resistance and lower capacity than nano-crystal phase. Also it was found that composite silicon thin film cannot
be properly described by equivalent circuit only with resistors and constant phase elements in serial relation
This document describes the preparation and analysis of mesoporous microspheres of nickel oxide (NiO) for use as a pseudocapacitor material. Mesoporous α-Ni(OH)2 microspheres were first synthesized via a hydrothermal method, then calcined at different temperatures between 250-500°C to produce NiO microspheres. The 250°C NiO sample exhibited the highest specific surface area of 295 m2/g and highest specific capacitance of 1,140 F/g. Characterization of the materials showed the pseudocapacitive behavior was more evident for NiO prepared at higher calcination temperatures. The high surface area and mesoporous structure of the 250°C
1. A 2D coordination polymer was synthesized using cobalt trimers and the flexible ligand cis,cis-cyclohexane-1,3,5-tricarboxylate.
2. Single crystal X-ray diffraction shows the complex forms a 2D framework with channels and contains trinuclear cobalt secondary building units linked by the ligand.
3. Magnetic characterization reveals spin-canting ferromagnetic behavior at low temperatures based on AC susceptibility measurements. Gas adsorption experiments also show selectivity for CO2 over N2.
Study the effect of Mn2+ ions on the ac electrical properties of some iron do...IJRES Journal
Oxide glasses doped with transition metal ions are of high interest because of their variant applications in both science and technology fields. However, the normal melt quench method have used to prepared some iron doped phosphate glasses according the following molecular formula: (65-x) mol% P2O5 - 20 mol% Na2O - 15 mol% Fe2O3 - x mol% MnO, Where x= 0, 5,10, 20, 25. The room temperature Mössbauer Effect ME Spectra used to characterized the glassy state homogeneity of these glasses. ME spectra show, for all glasses, no magnetic field participate which mean good glassy state formation. The ac electrical transport properties were also measured, as function of temperature up to 500k. It was found that the ac conductivity increased with the gradual increase of Mn2+ cations, while the electrical activation energy decreased.
This document describes research on fabricating a novel graphene electrode embedded with zirconium dioxide nanoparticles for electrochemical capacitors. The electrode showed a maximum specific capacitance of 11.84 F g−1. SEM images showed ions redepositing as agglomerates on the electrode surface after one charge/discharge cycle, accompanied by a decrease in surface area. Electrochemical tests confirmed pseudocapacitive behavior and low resistance. The research aims to investigate how electrolyte ion and active material redeposition affects the electrode's charge distribution ability.
1) The document investigates the effect of cation and anion sizes on the charge storage capabilities of graphite nanosheets as electrode materials for electrochemical double layer capacitors.
2) Scanning electron microscope images confirm the layered structure of the graphite nanosheets used, which are 12nm thick with 3.36 Angstrom spacing between layers.
3) Electrochemical measurements using cyclic voltammetry and impedance spectroscopy indicate that the graphite electrodes exhibited better charge storage and delivery in 3M NaCl electrolyte compared to NaOH and KOH electrolytes, due to the smaller ion sizes matching better with the graphite structure.
The document describes the design and application of powder composite electrodes made of Cu, Co, Ni, Pt and Ir for use in electrosynthesis and electroanalysis in alkaline solutions. The electrodes were prepared by mixing 95% metal powder with 5% polyvinyl chloride binder. Characterization showed the electrodes had a rough, porous surface and good electrochemical stability, with higher current densities than metal sheet electrodes. Cyclic voltammetry testing demonstrated the composite electrodes had good stability over multiple cycles for electrooxidation reactions like ethanol oxidation in KOH solution. The composite electrodes are suitable for electrochemistry research applications requiring stable, conductive electrodes.
Vacancy and Copper-doping Effect on Superconductivity for Clathrate MaterialsYang Li
This document summarizes a study on the effects of vacancy and copper doping on superconductivity in clathrate materials. Key findings include:
1) Copper doping of Ba8Si46 decreases the superconducting critical temperature strongly as copper content increases. Theoretical simulations also show copper doping decreases electronic density of states at the Fermi level.
2) Comparison of Ba8Ge46 and Ba8Si46 using theoretical simulations found their electronic structures are very similar, suggesting superconductivity is intrinsic to fully occupied silicon and germanium clathrates.
3) The absence of superconductivity in most germanium clathrates is suggested to arise from vacancy defects which result in
Microstructural and Dielectric Characterization of Sr doped Ba(Fe0.5Ta0.5)O3 ...theijes
Solid state reaction method was used to synthesize Ba1-xSrx(Fe0.5Ta0.5)O3 ceramic(x=0, 0.1, 0.2, 0.3, 0.4 and 0.5). The raw materials of making Sr doped Ba(Fe0.5Ta0.5)O3 were BaCO3, SrCO3, Fe2O3, Ta2O5 (purity better than 99%). Pellet and ring shaped samples prepared from each composition were sintered at 1400 and 1450ºC for 5 hour. The phase formation of Ba1-xSrx(Fe0.5Ta0.5)O3 was checked using X-ray diffraction (XRD) technique and observed a cubic perovskite crystal structure in space group Pm3m (221). Microstructure of the individual compound was examined by the field emission scanning electron micrograph (FESEM). Grain size was found to be varied with Sr content. The lattice parameter decreased with increasing Sr content. Dielectric spectroscopy was applied to investigate the electrical properties of BSFT at room temperature and in a frequency range of 100Hz–100 MHz. An analysis of the dielectric constant εʹ and loss tangent tan with frequency was performed assuming a distribution of relaxation times. The low frequency dielectric dispersion corresponds to the DC electrical conductivity.
Superconductivity in Gallium-substituted Ba8Si46 ClathratesYang Li
We report a joint experimental and theoretical investigation of superconductivity in Ga-substituted type-I silicon clathrates. We prepared samples of the general formula Ba8Si46−xGax, with different values of x. We show that Ba8Si40Ga6 is a bulk superconductor, with an onset at TC=3.3 K. For x=10 and higher, no superconductivity was observed down to T=1.8 K. This represents a strong suppression of superconductivity with increasing Ga content, compared to Ba8Si46 with TC=8 K. Suppression of superconductivity can be attributed primarily to a decrease in the density of states at the Fermi level, caused by a reduced integrity of the sp3-hybridized networks as well as the lowering of carrier concentration. These results are corroborated by first-principles calculations, which show that Ga substitution results in a large decrease of the electronic density of states at the Fermi level, which explains the decreased superconducting critical temperature within the BCS framework. To further characterize the superconducting state, we carried out magnetic measurements showing Ba8Si40Ga6 to be a type-II superconductor. The critical magnetic fields were measured to be Hc1=35 Oe and Hc2=8.5 kOe.We deduce the London penetration depth 3700 Å and the coherence length 200 Å. Our estimate of the electron-phonon coupling reveals that Ba8Si40Ga6 is a moderate phonon-mediated BCS superconductor.
THE UTILISATION OF 2-D RESISTIVITY AND INDUCED POLARIZATION (IP) METHODKasdi Nata Sujono
The document summarizes a study that used 2-D resistivity and induced polarization (IP) methods to determine iron ore bodies at Kampung Melaka, Kuala Lipis, Pahang, Malaysia. Three survey lines totaling 600 meters were divided into lots of 200 meters each. The 2-D resistivity method identified iron ore by its low resistivity, while IP differentiated iron ore and groundwater. Results showed iron ore underlying the surface from 5-30 meters was mostly located in lots 1 and 2 based on their low resistivity. Lot 1 contained 20-25% iron ore, lot 2 contained 30-35% iron ore, and lot 3 contained 15-20% iron ore over each 200-meter
This document discusses evidence for a possible shape transition from prolate to oblate in neutron-rich ruthenium isotopes based on spectroscopy experiments of 109,110,111,112Ru nuclei. The experiments extended existing level schemes to higher spin and excitation energy, allowing observation of band crossings. A band crossing was observed in 111Ru at a similar rotational frequency as the second band crossing in 112Ru, suggesting the alignment of proton g9/2 pairs and a triaxial to oblate shape transition in 111Ru. Comparisons are made to cranked shell model predictions to help interpret the results.
1) Low-lying excited states of the neutron-rich calcium isotopes 48-52Ca have been studied using gamma-ray spectroscopy following inverse kinematics proton scattering experiments.
2) The energies and strengths of the octupole states in these calcium isotopes are remarkably constant, indicating that these states are dominated by proton excitations of the calcium cores.
3) Specific excited states in 49,51,52Ca were analyzed, and spin and parity assignments were made or supported based on comparisons to previous reaction data and theoretical expectations.
Mass spectrometry is a versatile analytical technique used to characterize molecules through determination of molecular weight, elemental composition, and presence of functional groups. It is used for mechanistic studies of gas-phase ion chemistry, as a detector coupled to chromatography instruments, and integrated into vacuum systems. Mass spectrometry involves the steps of sample introduction, ionization, mass analysis, and ion detection/data analysis.
Surface Activation of C-sp3 in Boron-Doped Diamond ElectrodeAlejandro Medel
Abstract C-sp2 (graphite) impurities are undesirable in synthetic diamond electrodes (C-sp3), because they can affect the electrochemical response. In this work, we demonstrate that Csp3 surfaces can be activated successfully by applying an anodic current density corresponding to sufficiently high potential where the hydroxyl radicals (●OH) are generated. The
effectiveness of this activation process was verified by Raman spectroscopy, X-ray diffraction, scanning electron microscopy, and cyclic voltammetry.
Computational Study on the Effect of Axial Ligation Upon the Electronic Struc...Roxana Kincses
This document describes a computational study examining the effect of different axial ligands on the electronic structure of copper(II) porphyrinate complexes. Density functional theory was used to model complexes with nitrite, imidazole, phenol, and water ligands. The results show that axial ligands influence the copper spin density and delocalization in the complex. Ligands like nitrite and phenolate induce more spin delocalization compared to neutral ligands like water and phenol. The strength of axial bonding also varies, with ionic ligands forming stronger bonds than neutral ones involved in hydrogen bonding. This variation in electronic structure induced by different axial ligands could explain changes seen in experimental electron paramagnetic resonance spectra of related complexes.
Reduction of cu o and cu2o with h2 h embedding and kinetics effects in the ...Luciana Pirone
This document summarizes a study that used time-resolved X-ray diffraction, X-ray absorption fine structure spectroscopy, and density functional theory calculations to investigate the reduction of CuO and Cu2O with hydrogen gas. The main findings were:
1) CuO reduces directly to metallic copper without forming intermediate copper suboxides like Cu4O3 or Cu2O under normal hydrogen flow rates.
2) The reduction of CuO is easier than the reduction of Cu2O, with apparent activation energies of 14.5 kcal/mol and 27.4 kcal/mol, respectively.
3) During CuO reduction, the system can reach metastable states and react with hydrogen instead of
The document summarizes a study that demonstrated the ability to tune the size of large-diameter, few-walled nitrogen-doped carbon nanotubes (N-CNTs) from 50-150 nm by varying the transition metal (TM) used during synthesis. Fe produced the largest tubes, followed by Co and Ni, while Mn resulted in a clot-like morphology. Electrocatalytic activity for the oxygen reduction reaction (ORR) followed the trend Fe > Co > Ni > Mn. Fe-derived N-CNTs exhibited the highest surface area and nitrogen incorporation, contributing to their high ORR activity. This work provides a new route for developing advanced nonprecious metal catalysts by controlling carbon nanot
A simple simulation model for oxidative coupling of methaneAlexander Decker
This document describes a study that developed a mathematical model to simulate the oxidative coupling of methane over a La0.6Sr0.4NiO3 perovskite catalyst. The catalyst was prepared using a reverse microemulsion method and characterized using various techniques. Rate equations were developed based on previous studies of similar catalysts. The model can predict that at temperatures of 925°C or higher, with a methane partial pressure of 0.3 and oxygen partial pressure of 0.1, the catalyst will reach around 10% methane conversion and 50% selectivity to C2+ hydrocarbons.
Critical magnetic fields of superconducting aluminum-substituted Ba8Si42Al4 c...Yang Li
This document summarizes a study of the critical magnetic fields of the superconducting aluminum-substituted clathrate Ba8Si42Al4. Key findings include:
1) For the sample Ba8Si42Al4, the critical magnetic fields were measured to be HC1 = 40.2 Oe and HC2 = 66.4 kOe.
2) The London penetration depth was calculated to be 4360 Å and the coherence length was 70 Å.
3) The estimated Ginzburg–Landau parameter of j = 62 revealed that Ba8Si42Al4 is a strong type-II superconductor.
This document discusses theoretical and experimental studies on viologen-containing 1,1'-binaphthyls as potential near-infrared chiroptically switching materials. Theoretical modeling was used to correlate chiroptical properties with molecular geometry, showing maximal properties for a twisting angle of 60° and interchromophoric distance of 3.9 nm. Two chiral molecules containing viologen groups attached to a 1,1'-binaphthyl core through short spacers were synthesized and showed strong circular dichroism bands in the visible and near-infrared regions upon electrochemical reduction, demonstrating their potential as chiroptical switches. The cyclic molecule showed stronger chiroptical properties than the open-ring analogue.
Temperature Dependence of the Band-Edge Transitions of ZnCdBeSeOleg Maksimov
This study characterized the temperature dependence of band-edge transitions in three ZnCdBeSe films with varying concentrations of beryllium (Be) using contactless electroreflectance (CER) and piezoreflectance (PzR) measurements from 15-450K. The CER and PzR spectra showed doublet features near the band edge, indicating light-hole and heavy-hole excitonic transitions. Comparing the relative intensities of the PzR and CER spectra allowed identification of the transitions. Analysis of the temperature dependence provided information on how the energy and broadening of the transitions varied with temperature and Be concentration. The results showed that incorporating Be effectively reduced the rate of temperature variation of the energy
Amorphous-nano-crystalline silicon composite thin films (a-nc-Si:H) samples were synthesized by
Plasma Enhanced Chemical Vapor Deposition technique. The measurement of DC conductivities was
accomplished using Dielectric spectroscopy (Impedance Spectroscopy) in wide frequency and temperature range.
In analysis of impedance data, two approaches were tested: the Debye type equivalent circuit with two parallel R
and CPEs (constant phase elements) and modified one, with tree parallel R and CPEs including crystal grain
boundary effects. It was found that the later better fits to experimental results properly describes crystal grains
dielectric effect and hydrogen concentration indicating presence of strain. The amorphous matrix showed larger
resistance and lower capacity than nano-crystal phase. Also it was found that composite silicon thin film cannot
be properly described by equivalent circuit only with resistors and constant phase elements in serial relation
My_papers_Nastishin_PRL_2012_Elasticity of Lyotropic Chromonic Liquid Crystal...Myroslava Omelchenko
This document reports on a study that uses a magnetic Frederiks transition technique to measure the elastic constants (splay K1, twist K2, bend K3) of the lyotropic chromonic liquid crystal sunset yellow formed through reversible aggregation of organic molecules in water. The key findings are:
1) K1 and K3 are comparable in magnitude and about an order of magnitude higher than K2.
2) At higher concentrations and lower temperatures, K1 and the ratios K1/K3 and K1/K2 increase, which is attributed to elongation of the self-assembled lyotropic chromonic liquid crystal aggregates.
3) This concentration and temperature dependence of the elastic constants
Artigo que descreve o trabalho feito com o Chandra nos aglomerados de galáxias de Perseus e Virgo sobre a descoberta de uma turbulência cósmica que impede a formação de novas estrelas.
This document summarizes research on photovoltaic structures using thermally evaporated tin sulfide thin films. Key points:
- Tin sulfide films were deposited by thermal evaporation onto glass substrates in thicknesses ranging from 100-300nm.
- The films exhibited n-type conductivity at low thicknesses, transitioning to p-type at higher thicknesses. Bandgaps ranged from 2.1-1.7eV.
- CdS/SnS photovoltaic cells showed open circuit voltages up to 400mV, short circuit current densities up to 0.061mA/cm2, and conversion efficiencies up to 1.49% under 106mW/cm2 illumination.
- The document discusses an undergraduate investigation using point contact spectroscopy (PCS) to study quantum criticality in materials. PCS has traditionally been used to determine scattering information in metals and energy gaps in superconductors. A recent theory suggests PCS may also detect non-Fermi liquid behavior associated with quantum criticality.
- The investigation began by using PCS to study the superconductor FeTe0.55Se0.45 to establish ballistic contacts. It then aimed to use PCS to search for signatures of quantum fluctuations in the quantum critical material YFe2Al10 above the superconductor's critical temperature. This may provide evidence for detecting quantum critical behavior through PCS.
This document summarizes the electrical characteristics of a suspended silicon nanowire single-hole transistor containing silicon nanocrystals less than 10 nm in size. Coulomb diamonds were observed in the electrical measurements at 10 K, indicating single-hole tunneling through a dominant nanocrystal. The Coulomb diamonds had a charging energy of approximately 27 meV. Additionally, resonant tunneling features with an energy spacing of around 10 meV were observed parallel to both edges of the Coulomb diamonds. These features could be associated with either excited hole states or interactions between holes and acoustic phonons in the nanocrystal.
This document presents a study using density functional theory calculations to examine the adsorption of titanium dioxide nanostructures on pure and functionalized single-walled carbon nanotubes. The study finds that TiO2 nanostructures preferentially adsorb to chemical adsorption sites on functionalized SWCNTs, such as epoxy, alcohol, and carboxylate sites, compared to physical adsorption sites on pure SWCNTs, such as top, bridge, and hollow sites. Partial density of states calculations and charge density maps provide insight into the electronic structure and charge transfer between TiO2 nanostructures and SWCNTs. The results provide a theoretical understanding of controlled growth mechanisms of TiO2 nanostructures on carbon nanotube substrates.
1) The document reports on a study of the optical properties of binary CdSe and ternary alloyed CdSxSe1-x nanocrystals synthesized via a one-step hot injection colloidal approach.
2) Spectroscopic characterization of the nanocrystals showed prominent excitonic features in absorption spectra and single, narrow photoluminescence peaks devoid of surface state emissions. X-ray diffraction patterns confirmed a hexagonal wurtzite crystal structure.
3) At the single particle level, the ternary CdSxSe1-x nanocrystals exhibited higher 'on' time fractions and greater photostability than binary CdSe nanocrystals
Study of Microstructural, Electrical and Dielectric Properties of La0.9Pb0.1M...Scientific Review SR
The present work studies the microstructural and electrical properties of La0.9Pb0.1MnO3 and La0.8Y0.1Pb0.1MnO3 ceramics synthesized by solid-state route method. Microstructure and elemental analysis of both samples were carried out by field emission scanning electron microscope (FESEM) and energy dispersive spectroscopy (EDS) method, respectively. Phase analysis by X-ray diffraction (XRD) indicated formation of single phase distorted structure. The XRD data were further analyzed by Rietveld refinement technique. Raman analysis reveals that Y atom substitutes La site into the LPMO with shifting of phonon modes. The temperature variation of resistivity of undoped and Y-doped La0.9Pb0.1MnO3 samples have been investigated. The electrical resistivity as a function of temperature showed that all samples undergo an metal-insulator (M-I) transition having a peak at transition temperature TMI. Y-doping increases the resistivity and the metal-insulator transition temperature (TMI) shifts to lower temperature. The temperature-dependent resistivity for temperatures less than metal-insulator transition is explained in terms the quadratic temperature dependence and for T > TMI, thermally activated conduction (TAC) is appropriate. Variation of frequency dispersion in permittivity and loss pattern due to La-site substitution in LPMO was observed in the dielectric response curve.
1998 epitaxial film growth of the charge density-wave conductor rb0.30 moo3 o...pmloscholte
1) Thin films of the charge density wave compound Rb0.30MoO3 were grown on SrTiO3 (001) substrates using pulsed laser deposition.
2) Initial growth proceeds through the formation of uniform, droplet-shaped islands that are fully relaxed. Thicker films form larger clusters that differ in size and have asymmetric shapes with clear facets.
3) X-ray diffraction shows the films have a preferred out-of-plane growth direction and four in-plane orientations corresponding to the symmetry of the SrTiO3 substrate. The correlation length perpendicular to the charge density wave axis is smaller than the dimensions of the grain clusters in thicker films.
Equation of state for technetium from x‐ray diffraction and first principle c...Konstantin German
This document presents an experimental and theoretical study of the equation of state (EoS) of technetium metal under high pressure. Key points:
1) X-ray diffraction was used to measure the structure of technetium up to 67 GPa in a diamond anvil cell. The hexagonal close-packed structure was found to be stable over this pressure range.
2) First-principles calculations were also performed to model the compression behavior of technetium up to 273 GPa.
3) By fitting both the experimental and calculated volume-pressure data to different equations of state, the Vinet equation of state with B0 = 288 GPa and B' = 5.9(
International Journal of Engineering and Science Invention (IJESI)inventionjournals
International Journal of Engineering and Science Invention (IJESI) is an international journal intended for professionals and researchers in all fields of computer science and electronics. IJESI publishes research articles and reviews within the whole field Engineering Science and Technology, new teaching methods, assessment, validation and the impact of new technologies and it will continue to provide information on the latest trends and developments in this ever-expanding subject. The publications of papers are selected through double peer reviewed to ensure originality, relevance, and readability. The articles published in our journal can be accessed online.
This document summarizes a study on the photoelectrochemical properties of nanocrystalline indium selenide (In2Se3) thin films deposited via a chemical bath deposition method. The In2Se3 films exhibited n-type conductivity. Current-voltage measurements in the dark showed non-symmetrical rectifying behavior with a junction ideality factor of 3.85, suggesting the influence of series resistance and structural imperfections. Capacitance-voltage measurements determined a flat band potential of -0.530V versus saturated calomel electrode. Barrier height measurements from reverse saturation current at different temperatures yielded a barrier height. Under 30 mW/cm2 illumination, the cell demonstrated an open circuit voltage of 153mV
This document summarizes a study on the photoelectrochemical properties of nanocrystalline indium selenide (In2Se3) thin films deposited via a chemical bath deposition method. The In2Se3 films exhibited n-type conductivity based on photoelectrochemical characterization including I-V and C-V measurements in dark conditions. These measurements were used to determine properties like the ideality factor, flat band potential, and barrier height. Under illumination, the In2Se3 films showed a maximum power output of 3.1 μW/cm2 with an open circuit voltage of 153 mV and short circuit current of 20 μA.
Impact of CuS counter electrode calcination temperature on quantum dot sensit...TELKOMNIKA JOURNAL
In place of the commercial Pt electrode used in quantum sensitized solar cells, the low-cost CuS cathode is created using electrophoresis. High resolution scanning electron microscopy and X-ray diffraction were used to analyze the structure and morphology of structural cubic samples with diameters ranging from 40 nm to 200 nm. The conversion efficiency of solar cells is significantly impacted by the calcination temperatures of cathodes at 100 °C, 120 °C, 150 °C, and 180 °C under vacuum. The fluorine doped tin oxide (FTO)/CuS cathode electrode reached a maximum efficiency of 3.89% when it was calcined at 120 °C. Compared to other temperature combinations, CuS nanoparticles crystallize at 120 °C, which lowers resistance while increasing electron lifetime.
In place of the commercial Pt electrode used in quantum sensitized solar cells, the low-cost CuS cathode is created using electrophoresis. High resolution scanning electron microscopy and X-ray diffraction were used to analyze the structure and morphology of structural cubic samples with diameters ranging from 40 nm to 200 nm. The conversion efficiency of solar cells is significantly impacted by the calcination temperatures of cathodes at 100 °C, 120 °C, 150 °C, and 180 °C under vacuum. The fluorine doped tin oxide (FTO)/CuS cathode electrode reached a maximum efficiency of 3.89% when it was calcined at 120 °C. Compared to other temperature combinations, CuS nanoparticles crystallize at 120 °C, which lowers resistance while increasing electron lifetime.
Detection of an_unidentified_emission_line_in_the_stacked_xray_spectrum_of_ga...Sérgio Sacani
This document describes the detection of an unidentified emission line in the stacked X-ray spectrum of 73 galaxy clusters observed by XMM-Newton. The line was detected at an energy of 3.55-3.57 keV in independent analyses of the MOS and PN instruments. The line was also seen in Chandra observations of the Perseus cluster. Possible explanations discussed include an atomic transition in thermal plasma, or the decay of sterile neutrino dark matter particles. However, the origin is unclear and requires further observation.
Detection of an_unidentified_emission_line_in_the_stacked_xray_spectrum_of_ga...GOASA
This document describes the detection of an unidentified emission line in the stacked X-ray spectrum of 73 galaxy clusters observed by XMM-Newton. The line was detected at an energy of 3.55-3.57 keV in the combined spectrum. It was also seen independently in subsets of the clusters. The line is very weak, with an equivalent width of about 1 eV, and is within 50-110 eV of several known faint lines, making its nature difficult to determine. Possible explanations discussed include an atomic transition in the thermal plasma of the clusters or the decay of sterile neutrino dark matter particles.
This research article investigates the surface roughness and electrical conductivity of ultra-thin tin dioxide (SnO2) layers deposited by spray pyrolysis. Two sets of samples with different precursor concentrations and volumes were analyzed using X-ray reflectivity. XRR analysis revealed that increasing the precursor volume led to thicker layers with higher electron densities. Higher precursor concentration resulted in denser layers with larger thicknesses. Sheet resistance measurements showed lower values for thicker layers, correlated with their higher electron densities from XRR analysis.
NVESTIGATING FEEDBACK AND RELAXATION IN CLUSTERS OF GALAXIES WITH THE CHANDRA...Kenneth Cavagnolo
Presented in this dissertation is an analysis of the X-ray emission from the intracluster medium (ICM) in clusters of galaxies observed with the Chandra X-ray Observatory. The cluster dynamic state is investigated via ICM temperature inhomogeneity, and ICM entropy is used to evaluate the thermodynamics of cluster cores.
Similar to J Mater Chem C Cu-S 4th paper Prashant (20)
NVESTIGATING FEEDBACK AND RELAXATION IN CLUSTERS OF GALAXIES WITH THE CHANDRA...
J Mater Chem C Cu-S 4th paper Prashant
1. Quantitative X-ray absorption and emission
spectroscopies: electronic structure elucidation of Cu2S
and CuS†
Prashant Kumar,a
Rajamani Nagarajana
and Ritimukta Sarangi*b
Cu2S and CuS have been under intense scrutiny, with the aim of understanding the relationship between
their electronic structures and their commercially important physical properties. Here, X-ray absorption and
emission spectroscopic data have been analyzed using a quantitative, molecular orbital (MO) based
approach to understand the electronic structure of these two complex systems. Cu2S is shown to have a
significant amount of Cu2+
sites and therefore Cu0
centers. The presence of low-valent Cu is correlated
with the electrical conductivity of Cu2S, especially at high temperatures. CuS is shown to have
tetrahedral Cu2+
and trigonal Cu1+
sites, with crystal planes that have alternating high and low charge
on the Cu centers. This alternating charge density may contribute to internal energy transitions required
for photoluminescence properties. The in-depth electronic structure solutions presented here not only
solve a complicated much-debated problem, but also demonstrate the strength of a quantitative MO
based approach to X-ray spectroscopies.
1 Introduction
Copper suldes are economically important ores that have
found widespread use in various technologies, including solar
cell devices, nonlinear optical materials, lithium ion batteries,
nanometer-scale switches, and gas sensors.1–4
They vary widely
in composition (CuxSy) and are also present as non-stoichio-
metric compounds. CuS and Cu2S can be considered as end
members of the stoichiometric copper sulde family.1,5
Despite
their simple chemical formula, both Cu2S (chalcocite) and CuS
(covellite) have complex structures, and several experimental
and theoretical studies have been performed in an attempt to
understand their electronics and bonding.6–13
CuS has a
hexagonal crystalline structure, consisting of alternating layers
of planar CuS3 triangles and CuS4 tetrahedra. While CuS is a
stable composition, Cu2S is unstable towards the formation of
Cu vacancies, even in thermodynamic equilibrium with bulk Cu
metal. The inherent instability of Cu2S and the high mobility of
its Cu centers have been exploited for controlled removal of Cu
from Cu2S and for the generation of the known stoichiometries
in the Cu–S system.14
Room temperature Cu2S is monoclinic
with a complex structure containing 96 copper atoms in a unit
cell.15
The crystallographic characterization of intermediate
Cu2ÀxS (between Cu2S and CuS) systems has been difficult due
to the positions of the copper atoms within the close-packed
sublattice of S atoms, which are not well-dened.
Interestingly, important transitions in properties are
observed depending on the metal to sulfur ratio in Cu2ÀxS
systems. Cu2ÀxS remains diamagnetic for x ¼ 0.0 to 0.2 (ref. 12),
although the reported magnetic behaviour of CuS differs
markedly. CuS and Cu1.8S exhibit photoluminescence, which is
not observed for stoichiometric Cu2S.14,16
A large variation in
electrical conductivity with composition has also been
observed.12
Only CuS exhibits morphology dependent photo-
catalytic properties.17
Recent studies have shown that Cu1.8S is a
good thermoelectric material.18
The presence and variation of
these important properties warrants a thorough correlation
of the electronic structure with the complex crystal structures of
Cu2ÀxS systems.
X-ray absorption spectroscopy (XAS) has been extensively
used as a tool to determine the electronic and geometric
structure of materials.19–21
However, the overwhelming number
of publications on hard X-ray XAS have focused on the
geometric structure, and only qualitative evaluation of the
electronic structures has been performed. In this study, we
investigate the Cu and S K-edge XAS and Cu XES data using a
quantitative molecular orbital (MO) theory based approach to
solve the long-standing debate about their electronic structures
and to correlate these with their interesting physical properties.
a
Materials Chemistry Group, Department of Chemistry, University of Delhi, Delhi,
India, 110007. E-mail: rnagarajan@chemistry.du.ac.in; Fax: +91-11-27666606; Tel:
+91-27662650
b
Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory,
Menlo Park, CA 94025, USA. E-mail: ritis@slac.stanford.edu; Fax: +1 650-926-4100;
Tel: +1 650-926-4621
† Electronic supplementary information (ESI) available: EXAFS data and ts for
Cu2S and CuS. Figure showing the effect of self-absorption on Cu K-edge XAS
data. Details of DFT and TD-DFT calculations for simulation of the XES data.
Analysis of the Cu L-edge XAS data for CuS, [Cu(TMPA)(OH2)](ClO4) and [(Cu
[HB(3,5-Pri
2pz)3)]2(S2)]. See DOI: 10.1039/c3tc00639e
Cite this: J. Mater. Chem. C, 2013, 1,
2448
Received 7th November 2012
Accepted 1st February 2013
DOI: 10.1039/c3tc00639e
www.rsc.org/MaterialsC
2448 | J. Mater. Chem. C, 2013, 1, 2448–2454 This journal is ª The Royal Society of Chemistry 2013
Journal of
Materials Chemistry C
PAPER
Publishedon04February2013.DownloadedbyUniversityofDelhion28/07/201306:30:36.
View Article Online
View Journal | View Issue
2. 2 Materials and methods
2.1 Sample preparation
Polycrystalline samples of Cu2S and CuS were prepared as
previously reported.16
The samples were ame sealed in glass
ampules and sent to SSRL for measurement. The ampules were
transferred into a glove box and maintained under a moisture
free, $1 ppm O2 atmosphere. For the Cu K-edge XAS and XES
measurements, polycrystalline samples were nely ground with
BN into a homogeneous mixture and pressed into a 1 mm
aluminum spacer between 37 mm Kapton windows. The
samples were immediately frozen and stored under liquid N2.
During data collection, the samples were maintained at a
constant temperature of $10 K using an Oxford Instruments CF
1208 liquid helium cryostat. For S K-edge XAS studies, poly-
crystalline samples were nely ground inside a glove box using
an agate mortar and pestle and a thin layer was applied on
S-free 37 mm Kapton tape placed on an aluminum frame. The
samples were protected from exposure to air by a 5 mm poly-
propylene window placed over the front of the aluminum frame
over the sample. Samples were transported using sealed jars to
the beamline and exposure to air was minimized during sample
holder transfer into a He purged data measurement chamber.
2.2 Cu K-edge XAS
Cu K-edge XAS spectra for Cu2S and CuS were measured on the
20 pole, 2 T wiggler beamline 7–3 at the Stanford Synchrotron
Radiation Lightsource (SSRL) under standard ring conditions of
3 GeV and $300 mA ring current. A Si(220) double-crystal
monochromator was used for energy selection. Another optical
component used for the experiments was a cylindrical Rh-
coated bent focusing mirror. Spectra were collected in the fully
tuned conguration of the monochromator. Data were collected
in transmission mode using an ionization chamber placed
downstream of the sample. Internal energy calibration was
accomplished by simultaneous measurement of the absorption
of a Cu foil placed between two ionization chambers situated
aer the sample. The rst inection point of the foil spectrum
was set at 8980.3 eV. Spectra presented here are 5 scan and 4
scan averages for Cu2S and CuS, respectively, which were
sufficient to obtain a good signal to noise ratio in the EXAFS
region. A second-order polynomial was t to the pre-edge region
and subtracted from the entire spectrum as background. A
three-region spline of orders 2, 3, and 3 was used to model the
smoothly decaying post-edge region. The data were normalized
using the Pyspline22
program by subtracting a cubic spline and
assigning the edge jump to 1.0 at 9000 eV. Theoretical EXAFS
signals, c(k), were calculated using FEFF23,24
(Macintosh version
8.4) and the X-ray crystal structure of Cu2S and CuS. The theo-
retical models were t to the data using EXAFSPAK.25
The
structural parameters varied during the tting process were the
bond distance (R) and the bond variance s2
, which is related to
the Debye–Waller factor resulting from thermal motion, and
static disorder of the absorbing and scattering atoms. The non-
structural parameter E0 (the energy at which the photoelectron
wave vector k is 0) was also allowed to vary but was restricted to a
common value for every component in a given t. Coordination
numbers were systematically varied in the course of the t but
xed within a given t.
2.3 Cu K-edge XES
Cu K-edge XES data on Cu2S and CuS were measured on the 54
pole, 1 T wiggler beamline 6–2. A liquid nitrogen cooled double
crystal Si(111) monochromator was used to set the incident
energy at 12 keV. Vertical and horizontal focusing mirrors were
used to achieve a beam size of 150 Â 400 mm. Energy calibration
was achieved using a Cu foil. The rst inection point of the
foil spectrum was set at 8980.3 eV. Kb X-ray emission spectra
were measured using the 553 reection of ve spherically bent
(R ¼ 1 m) Si crystal analyzers in combination with a silicon dri
detector aligned in a Rowland geometry, as described previ-
ously.26
The overall energy bandwidth of the X-ray emission
spectrometer was $1.5 eV. The data were normalized with
respect to the Ka line intensity. The Kb1,3 and the Kb2,5 spectra
were recorded separately using different regions with signi-
cant overlap between the two regions for accurate merging of
the two datasets. A signicantly higher number of Kb2,5 scans
were required to achieve similar signal quality.
2.4 S K-edge XAS
S K-edge XAS data were collected on the 20 pole 2 T wiggler
unfocussed beamline 4–3 under standard ring operating
conditions of 3 GeV and $300 mA ring current. A Si(111) double
crystal monochromator was used for energy selection.
Upstream optics includes a Ni-coated vertically collimating and
harmonic rejection mirror. A big challenge at the S K-edge with
uorescence data collection on solid samples with high sulfur
compositions is self-absorption. To avoid self-absorption, the
samples were ground with BN, further diluted by mixing with
mineral oil and spread on the sulfur free tape as a thin layer.
Room temperature measurements were performed on the
sample in uorescence mode using a Lytle detector. The sample
was monitored for potential effects of beam damage and
photoreduction. No beam-damage was observed over the period
of data collection and the rst and the last scans were super-
imposable for both samples. The S K-edge spectra presented
herein are devoid of any oxidized sulfur contamination, which
would lead to intense features in the S K-edge spectra at higher
energies. For example, sulfate, which is a likely candidate in
degraded samples, appears at $2482 eV. No feature was
observed in that energy range, which conrms the purity of the
samples. Energy calibration was achieved using Na2S2O3.5H2O
as the calibrant, which was run at intervals between sample
scans. The rst peak of the Na2S2O3$5H2O spectrum was xed at
2472.02 eV. A second-order polynomial was t to the pre-edge
region and subtracted from the entire spectrum as background.
The data were normalized using the Pyspline22
program by
subtracting a cubic spline and assigning the edge jump to 1.0 at
2490 eV. The areas under the pre-edge peaks were t using the
EDG_FIT subroutine in EXAFSPAK.25
The pre-edge and rising-
edge features were modeled with pseudo-Voigt line-shapes with
a xed 1 : 1 Lorentzian/Gaussian ratio.
This journal is ª The Royal Society of Chemistry 2013 J. Mater. Chem. C, 2013, 1, 2448–2454 | 2449
Paper Journal of Materials Chemistry C
Publishedon04February2013.DownloadedbyUniversityofDelhion28/07/201306:30:36.
View Article Online
3. 3 Results and analysis
3.1 Cu K-edge XAS
Cu K-edge XAS spectra for CuS and Cu2S are shown in Fig. 1A.
The Cu K-rising edge region (8980 to 9000 eV) includes the
dipole allowed 1s / 4p transition, charge transfer shakedown
transitions from Cu-ligand covalent overlap, and long-range
multiple scattering transitions.20,27,28
Although a true under-
standing of all electronic factors affecting the rising-edge energy
has yet to be achieved, it has been empirically observed that the
energy of the rising edge shis to higher energy with an increase
in oxidation state.29
The rising edges for Cu2S and CuS occur at
8982.2 eV and 8984.4 eV, respectively. This 2.2 eV increase
indicates an increase in the oxidation state of Cu in CuS.
However, based on previous XAS, XPS and EPR studies, both
Cu2S and CuS have been described as Cu(I) complexes with little
or no Cu(II) character.6,30,31
To address this issue and to investigate the potential
increase in oxidation state on going from Cu2S to CuS, the Cu K-
edge data for discreet Cu(II) complexes are considered in Fig. 1B,
and energies are tabulated in Table 1. The rising-edge energy
position for a bona-de Cu(II) complex [Cu(TMPA)(OH2)](ClO4)2
(1, ) with light atom ligands (N and O) occurs at 8988.2 eV.28
As
we increase the number of coordinated sulfur atoms to the Cu
center (with no change in oxidation state), the edge shis to
lower energy. For plastocyanin (2, ) (1 Cu–S bond) the rising
edge occurs at 8986.3 eV and for [((TMEDA)Cu)2(S2)2](OTf)2 (3, )
(2 Cu–S bonds) the rising edge occurs at 8985.1 eV.27,32
In CuS,
which has sites with both 4 Cu–S and 3 Cu–S bonds (see Section
3.3), the edge is shied to even lower energy and occurs at
8984.4 eV ( ). This trend shows that heavy atom coordination
(such as S) to the absorbing Cu center shis the rising edge to
lower energy and demonstrates that comparison of rising-edge
data for oxidation state determination should be done on like-
ligand systems only. For example, without consideration of
ligand type, the over 2 eV energy difference between 1 and 3
(both Cu(II) systems) could erroneously be attributed to an
oxidation state change. The Cu K-edge data for CuS and a Cu(I)
complex ([Cu(pyridine)4](ClO4) (4, ))33
(see Fig. 1B) show closely
spaced rising-edge energy positions. Such a comparison might
have been erroneously used in the past to support a Cu(I)
assignment in CuS. However, a correct comparison can only be
made between Cu2S and CuS (the same ligand systems), which
points to an increase in oxidation state and a signicant
amount of Cu(II) in CuS.
Fig. 1A (inset) shows the second derivative spectra of the
expanded pre-edge region. In rst row transition metal
complexes with unoccupied 3d levels, a weak pre-edge transi-
tion is observed just below the onset of the intense rising-edge.
This is an electric-dipole forbidden quadrupole-allowed 1s /
3d transition.34
For Cu(II) systems, a transition to the singly
unoccupied (3d9
conguration) orbital results in a pre-edge at
$8979 eV (typically $100 times weaker than the rising-edge).
Fig. 1A shows a very weak transition at $8979 eV for Cu2S. Due
to its low intensity, this transition is barely evident in the
second derivative spectra and may potentially be attributed to a
small amount (<5%) of oxidized Cu species (see Section 3.2). In
CuS, the pre-edge feature is signicantly more intense and is
shied to higher energy (8979.5 eV). The presence of a pre-edge
feature in CuS indicates 3d9
(Cu2+
) character.
3.2 S K-edge XAS
It has been amply demonstrated in discreet transition metal-S
systems that orbital overlap between a 3d valence hole with an
Fig. 1 (A) The normalized Cu K-edge XAS spectra for Cu2S ( ) and CuS ( ). The
horizontal dotted line shows the rising-edge energy shift. The inset shows the first
derivative spectra. The vertical line shows the presence of a pre-edge feature cor-
responding to a Cu 1s / 3d9
transition. (B) Comparison of the Cu K-rising-edge
region for Cu–S compounds: 1 ( ) (no S ligand), 2 ( ) (1 S ligand), 3 ( ) (2 S ligands),
CuS ( ) (3.5 S ligands), 4 ( ) (no S ligand), Cu2S ( ) and copper foil ( ). The horizontal
dotted line represents the rising-edge intensity for energy measurement.
Table 1 Cu and S K-edge energy positions
Cu K-edge Energyab
(eV)
Cu2S CuS 1 2 3 4
Energy 8982.2 8984.4 8988.2 8986.3 8985.1 8983.8
S K-edge Energyab
(eV)
A B C D E
Cu2S 2470.1 — — 2473.2 2475.0
CuS 2469.9 2470.7 2472.0 2474.4 2476.8
Na2S2 — — 2470.7 — —
Na2S — — — 2472.4 2474.8
a
Energy precision >0.05 eV. b
Energy resolution $0.1 eV. Data on 1, 2, 3,
4, Na2S and Na2S2 have been reported previously.27,28,32,33,35
2450 | J. Mater. Chem. C, 2013, 1, 2448–2454 This journal is ª The Royal Society of Chemistry 2013
Journal of Materials Chemistry C Paper
Publishedon04February2013.DownloadedbyUniversityofDelhion28/07/201306:30:36.
View Article Online
4. appropriate S 3p orbital results in a pre-edge feature in the
S K-edge spectrum.36
This feature is due to a transition from the
S 1s to S 3p orbital, which has gained hole character from
covalent delocalization into the metal, and therefore its occur-
rence directly indicates the presence of 3d hole character in the
metal. As an example, the Cl K-edge XAS spectrum of [CuCl4]2À
has an intense pre-edge feature (reecting the empty 3dx2Ày2
orbital in Cu2+
), whereas [ZnCl4]2À
has none (reecting the lled
3d10
character of Zn2+
).37
This technique has been applied to S
K-edge XAS, where the energy position of the pre-edge feature
has been used to determine the oxidation state of the transition
metal.36
Here, this approach is applied to Cu2S and CuS.
The S K-edge XAS spectra of Cu2S (red) and CuS (black) are
presented in Fig. 2(i). The inset shows the second derivative
spectra. In Cu2S, there are three dominant features at 2470.1,
2473.2, and 2475.0 eV (Table 1). The spectrum of CuS is richer
with 5 dominant features at 2469.9, 2470.7, 2472.0, 2474.4, and
2476.8 eV. In order to understand the spectral differences and
rigorously assign these transitions to electronic states, it is
important to rst evaluate the geometric structure of both
complexes. Cu2S is monoclinic and can be approximated as
hexagonal close packed sulfur atoms with mobile and trigonally
bonded Cu centers (Scheme 1). A close inspection of the crystal
structure shows that there is no interaction between the sulfur
atoms (shortest S–S $3.72 ˚A). Thus, the sulfur atoms in Cu2S are
true monosulde species. Equipped with this structural infor-
mation, we used spectra for Na2S (monosulde, ) as the
S K-edge standard. This alkali metal monosulde has no cova-
lent interaction with the S centers and no pre-edge features in
the S K-edge XAS data.
Fig. 2(ii) shows a comparison of the experimental Cu2S data,
relevant peaks (obtained from pseudo-Voigt ts to the data) and
spectra of the corresponding free ligand Na2S. It has been
previously shown that metal binding leads to a decrease in
intensity and shis to higher energy of S transitions.35
This shi
in energy is due to an increase in positive charge on the S due to
delocalization of negative charge into the metal center. A
similar shi of the S features is observed on going from Na2S to
Cu2S (see Table 1). In addition, a reasonably intense low-lying
pre-edge feature is observed at 2470.1 eV. As discussed above,
the low-energy feature at 2470.1 eV could only be present if a
metal based 3d hole delocalizes with the S 3p orbitals, unam-
biguously demonstrating the presence of Cu2+
(3d9
) ions.
The crystal structure of CuS is more complicated, with
alternating planes of trigonal and tetrahedral Cu centers. Two-
thirds of the Cu centers are in tetrahedral geometry whereas
one-third of the centers are in trigonal planar geometry and
bound to monosulde species only. Thus a second standard,
Na2S2 ( , representing the disulde) was included in the anal-
ysis. Fig. 2(iii) shows a comparison of the CuS S K-edge XAS data
and relevant peaks (obtained from pseudo-Voigt ts) with Na2S
and Na2S2, respectively. These data clearly show signatures of
both disulde (peak C) and monosulde (peak D and F) in the
spectrum of CuS. As expected, both of these signatures shi to
higher energy and become diminished in intensity relative to
the standards. In addition, two distinct pre-edge features are
observed at lower energy (A and B), which arise due to covalent
interaction of a Cu2+
center with the two different types of sulfur
species: disulde (S2)2À
and monosulde (S)2À
. Because the
S2
2À
(À1 formal charge on S) has a lower lying 1s orbital relative
to S2À
(À2 formal charge on S), the higher energy pre-edge
feature corresponds to the S2
2À
3p orbital delocalized with the
Cu2+
hole (see Scheme 1).
3.3 Cu Kb XES
X-ray absorption spectroscopy probes empty molecular levels.38
To obtain a complete one-electron picture of the ground state,
we measured the Cu X-ray emission spectra of Cu2S and CuS to
examine the lled levels of Cu (directly) and S (indirectly). The
data are presented in Fig. 3. The Kb1,3 spectra (Fig. 3A) for Cu2S
and CuS are very similar, with the intense transition at
8907.5 eV resulting from Cu 3p to 1s emission. This emission
leads to a multi-electron spin ip in the Cu 3d level, giving rise
to the formally forbidden low energy shoulder at 8905.3 eV.39
At
lower energy is a transition at $8900 eV for both Cu2S and CuS.
In Fe and Mn containing systems, this feature has been related
Fig. 2 (i) The normalized S K-edge XAS spectra for Cu2S ( ) and CuS ( ). The inset
shows the second derivative. (ii) Cu2S ( ) and Na2S ( ). (iii) CuS ( ), Na2S ( ) and
Na2S2 ( ). Both Cu2S and CuS datasets were fit using Pseudo-Voigt curves (dotted
lines). Peaks related to those in Na2S and Na2S2 have been assigned to the same
alphabet. Peak A (in CuS and Cu2S), which has no counterpart in Na2S, results
from a S2À
1s / Cu2+
3d9
transition. Peak B (in CuS) has no Na2S2 counterpart and
results from a S2
2À
1s / Cu2+
3d9
transition.
This journal is ª The Royal Society of Chemistry 2013 J. Mater. Chem. C, 2013, 1, 2448–2454 | 2451
Paper Journal of Materials Chemistry C
Publishedon04February2013.DownloadedbyUniversityofDelhion28/07/201306:30:36.
View Article Online
5. to 3p–3d exchange interaction.26,40
It has been shown that in
S ¼ 0 species, this feature merges into other weak nal states, to
the lower energy side. The obvious presence of this feature
demonstrates that unpaired spin density is present in both CuS
and Cu2S, attributable directly to the presence of Cu2+
sites.
The Kb2,5 spectra (Fig. 3B), which are composed of multiple
features, show two dominant peaks at 8977.6 eV and 8980.7 eV.
A quantitative analysis of the Kb2,5 spectra has only been
developed for molecular systems using density functional
theory and will not be attempted here because the systems have
crystalline repeating units, and as shown by XAS studies, they
have a mixture of different oxidation states. However, the Kb00
region, which results from a ligand 3s to Cu 1s emission, can be
used to distinguish the ligand types. The Kb00
(Fig. 3B, inset)
feature for Cu2S occurs at 8968.6 eV, and that for CuS is a
broader feature with a peak maximum at 8969.2 eV. A DFT
simulation using simple two- and three-atom models (Fig. S3†)
shows that the Kb00
line for [Cu–S2]À
is $0.9 eV higher than that
for [Cu–S2]À
. Because both Cu–S and Cu–S2 features are present
in CuS, the Kb00
spectrum is shied to higher energy and is
broader. This also conrms the evidence from S K-edge XAS that
sulde (S2À
) and disulde (S2
2À
) are present as discreet units
with individual bonding to the Cu sites.
4 Discussion
4.1 Electronic structure of Cu2S
All experimental data presented above show that Cu2S has Cu2+
centers. But an interesting quantitative difference is observed
between the Cu and S K-edge data. The Cu K-edge energy
position and near absence of a pre-edge feature indicate the
dominant presence of low-valent species (Cu1+
/Cu0
and a small
contribution from Cu2+
), whereas the large S K-edge pre-edge
intensity indicates the presence of signicant Cu2+
species. This
is because in the presence of a mixture of Cu oxidation states,
only the Cu2+
centers that have strong covalent interaction with
S have S K pre-edge features; the low-valent Cu does not
contribute to the data and hence the signature of the Cu2+
feature is large. On the other hand, all Cu oxidation states
contribute to Cu K-edge, obfuscating the signal from the already
weak pre-edge feature.
Importantly, the presence of Cu2+
centers indicates that for
charge compensation, an equal number of sites must be in the
Cu0
state(thepossibility oftheelectron onthedisulde, making a
perdisuldo S2
3À
moiety is remote, as the S–S bond is very short;
Scheme 1 Crystal structures and MO diagram relevant for Cu K- and S K-edge X-ray absorption spectra for Cu2S and CuS. (left panel) The structure of Cu2S shows
randomly packed Cu centers (orange) between sulfur planes (yellow). A close inspection of the crystal structure shows that Cu occurs in two kinds of triangular
coordination: one third of the metal atoms are in distorted triangular coordination within the hexagonal close-packed S layers, and the remaining are in triangular sites
between the layers. (right panel) CuS has tetrahedral Cu centers (blue) bound to sulfide (green) and disulfide (violet) and trigonal centers (magenta) bound only to
sulfides. For the MO diagrams, Cu oxidation states based on the XAS data are color-coded and their approximate relative d-band energies are shown. A partial ground
state wave-function relevant to the XAS data is shown for both complexes. Since only the Cu2+
–S2À
/Cu2+
–S2
2À
overlap leads to pre-edge features in the Cu and S K-
edge, other Cu1+
/Cu0
–S interaction is omitted for clarity. For CuS the difference in energy of the 1s orbital of S2À
and S2
2À
leads to two S K-pre-edge features. A question
mark near Cu1+
represents a lack of X-ray spectral evidence for quantitation.
Fig. 3 (A) The normalized Cu Kb1,3 data for Cu2S ( ) and CuS ( ). The inset shows
the first derivative spectrum and the low-energy shoulder arising from a 3d hole
(8900 eV). (B) The normalized Cu Kb2,5 region. The inset shows the valence to core
Kb00
region. The broader CuS spectra indicate the presence of two distinct types of
S species.
2452 | J. Mater. Chem. C, 2013, 1, 2448–2454 This journal is ª The Royal Society of Chemistry 2013
Journal of Materials Chemistry C Paper
Publishedon04February2013.DownloadedbyUniversityofDelhion28/07/201306:30:36.
View Article Online
6. $2.07 ˚A). Note that no Cu0
(3d10
4s1
) feature is expected in the S K-
edge data and apart from the low Cu K-edge energy of Cu2S, no
direct evidence for Cu0
is available (since there are no reference
data for non-metallic Cu0
systems). Thus, the electronic structure
of Cu2S is [(m À n/2)Cu2+
][(m À n/2)(Cu0
)](nCu+
)(mS2À
), (where
m À n/2 is small). The complex crystal structure of Cu2S precludes
further quantitation of m and n.
Although Cu2S has a heavily delocalized lattice system and
charge delocalization between Cu0
and Cu2+
is expected, it is
important to note that this description is distinct from one
where charge delocalization results in a Cu1+
only system. Such
a delocalized electronic structure will not lead to the S K-pre-
edge feature or the low-energy feature in the Cu K-XES data.
As mentioned in Scheme 1, there are two types of trigonal Cu
centers in Cu2S, one between the sulde layers and one within
the hcp sulde layers.41
Combining this with the electronic
structure description developed here, a direct explanation for
an important physical property of Cu2S evolves. At elevated
temperatures, Cu2S has unusually mobile Cu centers, which
make it a partially ionic conductor. Based on the results shown
here, it is proposed that the mobile Cu centers are dominantly
in the Cu0
state (between the layers) and account for the
unusual conductivity of Cu2S. The Cu2+
sites remain bound to
the sulde lattice (within the layers).
4.2 Electronic structure of CuS
Quantitative Cu and S K-edge XAS and Cu Kb XES data analysis
show that CuS contains discreet Cu2+
, Cu+
, S2À
and S2
2À
species.
These results are in contrast to previous EPR and XPS
studies,6,30,31
which proposed a Cu1+
ground state. However, EPR
data in solution showed the presence of Cu1+
due to reduction
of Cu2+
to Cu1+
in solution. It is likely that the XPS data suffered
beam-induced photoreduction from the low-energy radiation.
Interestingly, Cu L-edge data on CuS have a pre-edge feature
that is similar in energy to the Cu 2p / 3d9
feature in the
discreet Cu–S systems (Fig. S4 and S5†) supporting the presence
of Cu2+
in CuS.
A comparison of the electronic structure developed here with
the geometry reveals an interesting result. In CuS, the trigonal Cu
centers are bound only to monosuldes, whereas the tetrahedral
sites are bound to both mono- and disuldes. The presence of
two pre-edge features in the S K-edge data indicates that either
both trigonal and tetrahedral sites have Cu2+
centers, or only the
tetrahedral site has Cu2+
centers while the trigonal site has only
Cu1+
centers. Of these two models, the second is most consistent
with all the spectroscopy presented here. Charge neutralization
in CuS demands that one of the tetrahedral sites is Cu+
and one is
Cu2+
. Therefore the electronic structure can be described as
(CuTd)+
(CuT)+
(CuTd)2+
(S2)2À
(S)2À
(CuTd ¼ tetrahedral, CuT ¼
trigonal). However, because the bond distances in all tetrahedral
sites areequivalent, a chargedelocalization between the twosites
must be occurring, suggesting the more accurate description:
[(CuTd)2]3+
(CuT)+
(S2)2À
(S)2À
(each CuTd site is Cu1.5+
). It is also
possible that the similarity in bond distances results from static
disorder in the crystal structure leading to an average distance
from crystallography. In either case, the crystal planes in CuS
have alternating high and low charge on the Cu centers, which
may contribute to internal energy transitions required for
photoluminescence properties.
5 Conclusion
Previous X-ray spectroscopy data on copper suldes are fraught
with self-absorption issues and lead to mixed interpretations.
Data have been typically interpreted qualitatively using nger-
printing techniques or by applying theoretical codes to simulate
the spectra in order to obtain the electronic structure. In this
study, an intermediate approach has been developed and
applied to Cu2S and CuS. It is shown that comparative spectral
peak assignment based on data from well-understood discreet
molecules can be a powerful tool for electronic structure
elucidation in unknown materials. This technique is shown to
be successful in arriving at the electronic structure of the indi-
vidual sites in the complex geometry of Cu2S and CuS and has
helped correlate their structure with their function. In future
studies, the electronic structures of Cu2S and CuS developed
here will be extended to intermediate Cu2ÀxS systems to shed
light on their unique physical properties.
This study demonstrates the strength of the molecular
orbital theory approach to understanding bonding and elec-
tronic structure in repeating materials. Since electronic struc-
tures directly correlate with physical properties, the widespread
use of this technique in material systems is proposed.
Acknowledgements
XAS data were obtained at the Stanford Synchrotron Radiation
Lightsource (SSRL), a Directorate of SLAC National Accelerator
Laboratory and an Office of Science User Facility operated for
the U.S. Department of Energy Office of Science by Stanford
University. The SSRL Structural Molecular Biology Program is
supported by the National Institutes of Health, National Center
for Research Resources, Biomedical Technology Program and
by the Department of Energy, Office of Biological and Envi-
ronmental Research (BER). The publication was partially sup-
ported by Grant number 5 P41 RR001209 from the National
Center for Research Resources (NCRR), a component of the
National Institutes of Health (NIH), and its contents are solely
the responsibility of the authors and do not necessarily repre-
sent the official view of NCRR or NIH. PK and RN thank the DST,
Government of India for nancial support.
Notes and references
1 E. H. Roseboom Jr, Econ. Geol., 1966, 61, 641–672.
2 Y. Zhao and C. Burda, Energy Environ. Sci., 2012, 50, 5564–
5576.
3 A. A. Sagade, R. Sharma and I. Sulaniya, J. Appl. Phys., 2009,
105, 043701.
4 T. Sakamoto, H. Sunamura, H. Kawaura, T. Hasegawa,
T. Nakayama and M. Aono, Appl. Phys. Lett., 2003, 82,
3032–3034.
5 R. Goble, Can. Mineral., 1985, 23, 61–76.
This journal is ª The Royal Society of Chemistry 2013 J. Mater. Chem. C, 2013, 1, 2448–2454 | 2453
Paper Journal of Materials Chemistry C
Publishedon04February2013.DownloadedbyUniversityofDelhion28/07/201306:30:36.
View Article Online
7. 6 S. Wei Goh, A. N. Buckley and R. N. Lamb, Miner. Eng., 2006,
19, 204–208.
7 H. Nozaki, K. Shibata and N. Ohhashi, J. Solid State Chem.,
1991, 91, 306–311.
8 H. Fjellv˚ag, F. Grønvold, S. Stølen, A. F. Andresen, R. M¨uller-
K¨afer and S. Simon, Z. Kristallogr., 1988, 184, 111–121.
9 H. J. Gotsis, A. C. Barnes and P. Strange, J. Phys.: Condens.
Matter, 1992, 4, 10461–10486.
10 H. T. Evans, Z. Kristallogr., 1979, 150, 299–320.
11 P. Lukashev, W. R. L. Lambrecht, T. Kotani and M. van
Schilfgaarde, Phys. Rev. B: Condens. Matter, 2007, 76, 195202.
12 K. Okamata and S. Kawai, Jpn. J. Appl. Phys., Part 1, 1973, 12,
1130–1138.
13 Y. Itoh, A. Hayashi, H. Yamagata, M. Matsumura, K. Koga
and Y. Ueda, J. Phys. Soc. Jpn., 1996, 65, 1953–1956.
14 P. Kumar, M. Gusain and R. Nagarajan, Inorg. Chem., 2011,
50, 3065–3070.
15 H. T. Evans Jr, Science, 1979, 203, 356–358.
16 P. Kumar and R. Nagarajan, Inorg. Chem., 2011, 50, 9204–
9206.
17 Z. Cheng, S. Wang, Q. Wang and B. Geng, CrystEngComm,
2010, 12, 144–159.
18 Z. H. Ge, B. P. Zhang, Y. X. Chen, Z. X. Yu, Y. Liu and J. F. Li,
Chem. Commun., 2011, 47, 12697–12699.
19 H. Wende, Rep. Prog. Phys., 2004, 67, 2105–2181.
20 L. S. Kau, D. J. Spira-Solomon, J. E. Penner-Hahn,
K. O. Hodgson and E. I. Solomon, J. Am. Chem. Soc., 1987,
109, 6433–6442.
21 E. A. Stern, in EXAFS, SEXAFS and XANES, ed. D. C.
Koningsberger and R. Prins, John Wiley & Sons, New York,
1988, vol. 1.
22 A. Tenderholt, B. Hedman and K. O. Hodgson, X-ray
Absorption Fine Structure – XAFS13, Stanford University, 2007.
23 J. Mustre de Leon, J. J. Rehr, S. I. Zabinsky and R. C. Albers,
Phys. Rev. B: Condens. Matter, 1991, 44, 4146–4156.
24 J. J. Rehr and R. C. Albers, Rev. Mod. Phys., 2000, 72, 621–654.
25 G. N. George, EXAFSPAK and EDG-t, Stanford Synchrotron
Radiation Laboratory, Stanford Linear Accelerator Center,
Stanford, CA, 2000.
26 N. Lee, T. Petrenko, U. Bergmann, F. Neese and S. DeBeer, J.
Am. Chem. Soc., 2010, 132, 9715–9727.
27 R. Sarangi, J. T. York, M. E. Helton, K. Fujisawa, K. D. Karlin,
W. B. Tolman, K. O. Hodgson, B. Hedman and E. I. Solomon,
J. Am. Chem. Soc., 2008, 130, 676–686.
28 R. Sarangi, M. Benfatto, K. Hayakawa, L. Bubacco,
E. I. Solomon, K. O. Hodgson and B. Hedman, Inorg.
Chem., 2005, 44, 9652–9660.
29 P. J. Donoghue, J. Tehranchi, C. J. Cramer, R. Sarangi,
E. I. Solomon and W. B. Tolman, J. Am. Chem. Soc., 2011,
133, 17602–17605.
30 G. W. Luther 3rd, S. M. Theberge, T. F. Rozan, D. Rickard,
C. C. Rowlands and A. Oldroyd, Environ. Sci. Technol.,
2002, 36, 394–402.
31 J. C. W. Folmer and F. Jellinek, J. Less-Common Met., 1980,
76, 153–162.
32 S. E. Shadle, J. E. Penner-Hahn, H. J. Schugar, B. Hedman,
K. O. Hodgson and E. I. Solomon, J. Am. Chem. Soc., 1993,
115, 767–776.
33 L. S. Kau, K. O. Hodgson and E. I. Solomon, J. Am. Chem. Soc.,
1989, 111, 7103–7109.
34 J. L. DuBois, P. Mukherjee, T. D. P. Stack, B. Hedman,
E. I. Solomon and K. O. Hodgson, J. Am. Chem. Soc., 2000,
122, 5775–5787.
35 R. K. Szilagyi, B. S. Lim, T. Glaser, R. H. Holm, B. Hedman,
K. O. Hodgson and E. I. Solomon, J. Am. Chem. Soc., 2003,
125, 9158–9169.
36 E. I. Solomon, B. Hedman, K. O. Hodgson, A. Dey and
R. K. Szilagyi, Coord. Chem. Rev., 2005, 249, 97–129.
37 B. Hedman, K. O. Hodgson and E. I. Solomon, J. Am. Chem.
Soc., 1990, 112, 1643–1645.
38 U. Bergmann and P. Glatzel, Photosynth. Res., 2009, 102, 255–
266.
39 P. Glatzel and U. Bergmann, Coord. Chem. Rev., 2005, 249,
65–95.
40 M. Roemelt, M. A. Beckwith, C. Duboc, M. N. Collomb,
F. Neese and S. DeBeer, Inorg. Chem., 2012, 51, 680–
687.
41 H. T. Evans Jr, Nature, 1971, 232, 69–70.
2454 | J. Mater. Chem. C, 2013, 1, 2448–2454 This journal is ª The Royal Society of Chemistry 2013
Journal of Materials Chemistry C Paper