This document describes the preparation and analysis of mesoporous microspheres of nickel oxide (NiO) for use as a pseudocapacitor material. Mesoporous α-Ni(OH)2 microspheres were first synthesized via a hydrothermal method, then calcined at different temperatures between 250-500°C to produce NiO microspheres. The 250°C NiO sample exhibited the highest specific surface area of 295 m2/g and highest specific capacitance of 1,140 F/g. Characterization of the materials showed the pseudocapacitive behavior was more evident for NiO prepared at higher calcination temperatures. The high surface area and mesoporous structure of the 250°C
The document describes the design and application of powder composite electrodes made of Cu, Co, Ni, Pt and Ir for use in electrosynthesis and electroanalysis in alkaline solutions. The electrodes were prepared by mixing 95% metal powder with 5% polyvinyl chloride binder. Characterization showed the electrodes had a rough, porous surface and good electrochemical stability, with higher current densities than metal sheet electrodes. Cyclic voltammetry testing demonstrated the composite electrodes had good stability over multiple cycles for electrooxidation reactions like ethanol oxidation in KOH solution. The composite electrodes are suitable for electrochemistry research applications requiring stable, conductive electrodes.
This document summarizes research on using electrodeposited manganese dioxide (MnO2) coatings on porous carbon substrates for capacitive deionization (CDI) applications. Two carbon substrates with different surface areas and morphologies were coated with MnO2 using galvanostatic and cyclic voltammetric deposition. Characterization of the coated electrodes found mixed MnO2 phases present. Testing in half-cell configurations showed that maximum ion uptake per mass was not necessarily optimal for practical CDI applications, where performance per electrode area is more important. The results suggest the structure and deposition method can impact how effectively the electrode volume participates in ion removal reactions.
Aluminum Oxide-Silver Nanoparticle Interfaces for Memristive ApplicationsIOSR Journals
This document summarizes a study on a nonvolatile resistive random access memory device based on the heterojunction of silver nanoparticles and aluminum oxide. The device structure consists of aluminum-aluminum oxide-silver nanoparticles-aluminum. Current-voltage measurements show the device transitions between two states in two steps - a major transition with a resistance ratio of 105 and a minor transition with a ratio of about 101. The memristor operates at low voltages with good uniformity. Scanning electron microscopy, X-ray diffraction and optical absorption characterization confirm the formation of aluminum oxide and silver nanoparticles.
The document summarizes research on the electrochemical deposition of lead dioxide nanostructured thin films. Key findings include:
- Lead dioxide nanostructures were successfully deposited on gold-coated substrates by anodic electrochemical deposition using nitric acid and lead chloride as reactants. The morphology was influenced by deposition parameters like potential, temperature, and pH.
- Deposition at higher temperatures (60°C vs room temperature) resulted in faster growth rates and denser nanostructures, as seen by SEM images.
- Both anodic and cathodic deposition were studied. Cathodic deposition allowed formation of different lead oxide phases depending on conditions, while anodic deposition selectively formed PbO2.
- The work provides a
Recent progress on reduced graphene oxide....suresh kannan
The document summarizes recent progress on using reduced graphene oxide (rGO)-based materials as counter electrodes for dye-sensitized solar cells (DSSCs) as a cost-effective alternative to platinum. It discusses how rGO on its own is not effective as a counter electrode but that adding metal nanoparticles to rGO composites improves their catalytic activity and performance in DSSCs. The document reviews various rGO composites that have been studied, including those with silver, nickel, tungsten and platinum nanoparticles, as well as metal oxides and dichalcogenides. It compares the photovoltaic parameters of DSSCs using these rGO composite counter electrodes to those using conventional platinum counter electrodes
Synthesis and optimisation of ir o2 electrocatalysts by adams fusion method f...materials87
The document describes the synthesis and optimization of iridium dioxide (IrO2) electrocatalysts for oxygen evolution reaction (OER) in solid polymer electrolyte electrolyzers. IrO2 was synthesized using an Adams fusion method by varying synthesis duration (0.5-4 hours) and temperature (250-500°C). Characterization showed that increasing synthesis time and temperature improved crystallinity and increased particle size. Electrochemical testing revealed that IrO2 synthesized for 2 hours at 350°C exhibited the best electrocatalytic activity toward OER compared to a commercial IrO2 catalyst. Higher temperatures and longer times favored larger, more crystalline particles but decreased surface area and activity.
Synthesis and optimisation of ir o2 electrocatalysts by adams fusion method f...sudesh789
This document discusses the synthesis and optimization of iridium dioxide (IrO2) electrocatalysts for use in solid polymer electrolyte electrolyzers through an adaptation of the Adams fusion method. The synthesis duration and temperature were varied to determine their effect on the physical and electrochemical properties of the IrO2 catalysts. X-ray diffraction analysis showed that increasing the synthesis duration and temperature increased the crystallinity and particle size of the IrO2. Chronoamperometry testing revealed that a synthesis of 2 hours at 350°C produced an IrO2 catalyst with better electrocatalytic activity for oxygen evolution than a commercial IrO2 catalyst.
In this work, I am showing a faithful atomistic process of estimating the oxygen migration energetics within BSCF, oxygen migration energy exhibit a strong dependence on different local atomic structures of this doped perovskites. In addition, DFT calculations exhibit the reason of cubic phase stability of this doped perovskite in variable oxygen concentration.
The document describes the design and application of powder composite electrodes made of Cu, Co, Ni, Pt and Ir for use in electrosynthesis and electroanalysis in alkaline solutions. The electrodes were prepared by mixing 95% metal powder with 5% polyvinyl chloride binder. Characterization showed the electrodes had a rough, porous surface and good electrochemical stability, with higher current densities than metal sheet electrodes. Cyclic voltammetry testing demonstrated the composite electrodes had good stability over multiple cycles for electrooxidation reactions like ethanol oxidation in KOH solution. The composite electrodes are suitable for electrochemistry research applications requiring stable, conductive electrodes.
This document summarizes research on using electrodeposited manganese dioxide (MnO2) coatings on porous carbon substrates for capacitive deionization (CDI) applications. Two carbon substrates with different surface areas and morphologies were coated with MnO2 using galvanostatic and cyclic voltammetric deposition. Characterization of the coated electrodes found mixed MnO2 phases present. Testing in half-cell configurations showed that maximum ion uptake per mass was not necessarily optimal for practical CDI applications, where performance per electrode area is more important. The results suggest the structure and deposition method can impact how effectively the electrode volume participates in ion removal reactions.
Aluminum Oxide-Silver Nanoparticle Interfaces for Memristive ApplicationsIOSR Journals
This document summarizes a study on a nonvolatile resistive random access memory device based on the heterojunction of silver nanoparticles and aluminum oxide. The device structure consists of aluminum-aluminum oxide-silver nanoparticles-aluminum. Current-voltage measurements show the device transitions between two states in two steps - a major transition with a resistance ratio of 105 and a minor transition with a ratio of about 101. The memristor operates at low voltages with good uniformity. Scanning electron microscopy, X-ray diffraction and optical absorption characterization confirm the formation of aluminum oxide and silver nanoparticles.
The document summarizes research on the electrochemical deposition of lead dioxide nanostructured thin films. Key findings include:
- Lead dioxide nanostructures were successfully deposited on gold-coated substrates by anodic electrochemical deposition using nitric acid and lead chloride as reactants. The morphology was influenced by deposition parameters like potential, temperature, and pH.
- Deposition at higher temperatures (60°C vs room temperature) resulted in faster growth rates and denser nanostructures, as seen by SEM images.
- Both anodic and cathodic deposition were studied. Cathodic deposition allowed formation of different lead oxide phases depending on conditions, while anodic deposition selectively formed PbO2.
- The work provides a
Recent progress on reduced graphene oxide....suresh kannan
The document summarizes recent progress on using reduced graphene oxide (rGO)-based materials as counter electrodes for dye-sensitized solar cells (DSSCs) as a cost-effective alternative to platinum. It discusses how rGO on its own is not effective as a counter electrode but that adding metal nanoparticles to rGO composites improves their catalytic activity and performance in DSSCs. The document reviews various rGO composites that have been studied, including those with silver, nickel, tungsten and platinum nanoparticles, as well as metal oxides and dichalcogenides. It compares the photovoltaic parameters of DSSCs using these rGO composite counter electrodes to those using conventional platinum counter electrodes
Synthesis and optimisation of ir o2 electrocatalysts by adams fusion method f...materials87
The document describes the synthesis and optimization of iridium dioxide (IrO2) electrocatalysts for oxygen evolution reaction (OER) in solid polymer electrolyte electrolyzers. IrO2 was synthesized using an Adams fusion method by varying synthesis duration (0.5-4 hours) and temperature (250-500°C). Characterization showed that increasing synthesis time and temperature improved crystallinity and increased particle size. Electrochemical testing revealed that IrO2 synthesized for 2 hours at 350°C exhibited the best electrocatalytic activity toward OER compared to a commercial IrO2 catalyst. Higher temperatures and longer times favored larger, more crystalline particles but decreased surface area and activity.
Synthesis and optimisation of ir o2 electrocatalysts by adams fusion method f...sudesh789
This document discusses the synthesis and optimization of iridium dioxide (IrO2) electrocatalysts for use in solid polymer electrolyte electrolyzers through an adaptation of the Adams fusion method. The synthesis duration and temperature were varied to determine their effect on the physical and electrochemical properties of the IrO2 catalysts. X-ray diffraction analysis showed that increasing the synthesis duration and temperature increased the crystallinity and particle size of the IrO2. Chronoamperometry testing revealed that a synthesis of 2 hours at 350°C produced an IrO2 catalyst with better electrocatalytic activity for oxygen evolution than a commercial IrO2 catalyst.
In this work, I am showing a faithful atomistic process of estimating the oxygen migration energetics within BSCF, oxygen migration energy exhibit a strong dependence on different local atomic structures of this doped perovskites. In addition, DFT calculations exhibit the reason of cubic phase stability of this doped perovskite in variable oxygen concentration.
IrO2 as an anodic electrocatalyst for the oxygen evolution reaction (OER) in solid polymer electrolyte (SPE)
electrolysers was synthesised by adapting the Adams fusion method. Optimisation of the IrO2 electrocatalyst was achieved
by varying the synthesis duration (0.5 – 4 hours) and temperature (250 - 500°C). The physical properties of the
electrocatalysts were characterised by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and
x-ray diffraction (XRD). Electrochemical characterisation of the electrocatalysts toward the OER was evaluated by
chronoamperometry (CA). CA analysis revealed the best electrocatalytic activity towards the OER for IrO2 synthesised
for 2 hours at 350oC which displayed a better electrocatalytic activity than the commercial IrO2 electrocatalyst used in this
study. XRD and TEM analyses revealed an increase in crystallinity and average particle size with increasing synthesis
duration and temperature which accounted for the decreasing electrocatalytic activity. At 250°C the formation of an active
IrO2 electrocatalyst was not favoured.
This document summarizes research on the electrical conductivity of Ba-Sr-Co-Fe cathode materials for solid oxide fuel cells (SOFCs). Single phase cubic Ba0.5Sr0.5Co1-xFexO3-δ compositions were synthesized via gel combustion and cation complexation routes. Electrical conductivity measurements showed that conductivity initially increased with temperature up to a maximum then decreased, attributed to oxygen loss from the lattice. Fe substitution had little effect on conductivity. While BSCF shows potential as an SOFC cathode, further work is needed to increase conductivity to meet requirements of current IT-SOFCs.
The document discusses nanoparticles for small molecule electrocatalysis, specifically focusing on oxygen evolution reaction (OER) using Ni-Co hydroxides and oxides. It first provides background on OER and discusses how Co3O4, metal-doped Co3O4, and NiCo2O4 can be used as catalysts. It then outlines the purpose and scope of studying the composition dependence of Ni-Co hydroxides and oxides for OER using stainless steel mesh. The document reviews relevant theory around OER mechanisms and properties of different catalyst materials.
This document summarizes a presentation on solid electrolytes. It discusses how solid electrolytes exhibit ionic conductivity through mobile anions or cations, with maximum conductivity between 0.1-10 Ohm-1cm-1. Examples of solid electrolytes mentioned include AgI, β-alumina, and zirconia. Applications discussed include use in batteries, oxygen sensors, and solid oxide fuel cells. The proposed work is to synthesize and characterize Sr and Cu doped LaAlO3 as a potential solid electrolyte material.
This document summarizes the synthesis of zincblende CuInS2 and iron-substituted CuInS2 by reacting colloidal suspensions of binary Cu-S and In-S in ethyleneglycol. Characterization with techniques such as XRD, TEM, UV-Vis and Raman spectroscopy confirmed the formation of phase pure zincblende CuInS2. Following this, quaternary Cu-In-Fe-S with zincblende structure was also synthesized by including iron in the reaction. While zincblende CuInS2 degraded methylene blue dye under visible light, the iron-substituted sample did not show appreciable degradation.
Band edge engineering of composite photoanodes for dye sensitized solar cellsvenkatamanthina
This document discusses engineering the band edges of composite photoanodes for dye-sensitized solar cells through doping. Specifically, it doped ZnO nanorods with cobalt to lower its conduction band minimum and doped TiO2 nanoparticles with zirconium to raise its conduction band minimum in order to overcome an energy barrier preventing electron transfer. Characterization with diffuse reflectance spectroscopy and open circuit voltage measurements under illumination confirmed the doping shifted the band edges as intended. However, dye-sensitized solar cells fabricated with the composite nanostructures did not show improved performance. The paper details a methodology for producing and measuring band edge shifts but notes limitations in applying it to improve device operation.
Zr doped TiO2 nanocomposites for dye sensitized solar cellsvenkatamanthina
This document discusses engineering the band edges of a composite photoanode for dye-sensitized solar cells through doping. ZnO nanorods were doped with cobalt to lower their conduction band minimum energy, and TiO2 nanoparticles were doped with zirconium to raise their conduction band minimum energy. This was done to overcome an energy barrier that previously prevented electron transfer from TiO2 to ZnO in the composite. Characterization showed the doping incorporated into the materials as desired without other changes. Open circuit photovoltage measurements indicated the doping shifted the band energies to enable electron transfer, but devices using the materials did not show improved performance. The methodology for producing and measuring band edge shifts through doping is detailed.
Surface Activation of C-sp3 in Boron-Doped Diamond ElectrodeAlejandro Medel
Abstract C-sp2 (graphite) impurities are undesirable in synthetic diamond electrodes (C-sp3), because they can affect the electrochemical response. In this work, we demonstrate that Csp3 surfaces can be activated successfully by applying an anodic current density corresponding to sufficiently high potential where the hydroxyl radicals (●OH) are generated. The
effectiveness of this activation process was verified by Raman spectroscopy, X-ray diffraction, scanning electron microscopy, and cyclic voltammetry.
The document summarizes a study that characterized the corrosion of a nickel-aluminum (Ni-Al) composite coating compared to a pure nickel coating after 72 hours of immersion in 2M NaCl solution. Electrochemical impedance spectroscopy and potentiodynamic polarization techniques were used, and scanning electron microscopy was used to examine the corrosion product layers. Results showed the Ni-Al composite had a porous, cracked corrosion product layer that decreased corrosion potential and increased corrosion currents compared to the more protective layer formed on pure nickel. Thus, the Ni-Al composite exhibited lower corrosion resistance than pure nickel in the higher chloride concentration solution.
Direct Synthesis Carbon/Metal Oxide Composites for Electrochemical Capacitors...drboon
This paper deals with the study of the carbon/metal oxide composites synthesis for electrochemical capacitor electrode material. Transition metal salts, such as FeCl3 and TiCl3 act as activator in the synthesis of activated carbon from gelam wood sawdust (Melaleuca cajuputi Powell) which also have the functions as substrates for the composites. The surface functionalities of activated carbons were modified using oxidative treatments. The changes on crystallography and surface functionalities were analyzed based on XRD and FTIR data. The electrical conductivities and electrochemical properties were determined using kelvin and cyclic voltammetry methods, respectively. FTIR analyses showed that the activation and oxidation treatments affected their surface functionalities. The XRD analyses showed that oxidative treatments also affected carbons crystallite. The electrical conductivities and electrochemical properties were influenced by their crystallite and surface functionalities. The shape of the cyclic voltammograms varied according to the changes on the surface functionalities and on the metals loading. TEM analyses indicated the existence of nanoparticles metal oxides in the carbon samples.
2021 influence of basic carbon additives on the electrochemical performance ...Ary Assuncao
This study investigates the effect of carbon surface basicity on the electrochemical performance and dynamic charge acceptance of lead-carbon batteries. Five activated carbons with different pH values ranging from 9.5 to 11.1 were prepared by ammonia and hydrogen gas treatments. Cyclic voltammetry showed that the hydrogen evolution reaction activity increased with higher carbon surface basicity. Testing of lead-carbon electrodes found a correlation between carbon pH and dynamic charge acceptance, with higher pH carbons showing improved charge currents and final dynamic charge acceptance. The carbon content also affected charge currents during simulated microcycles, demonstrating that surface chemistry and amount of carbon additive both influence the electrochemical properties and performance of lead-carbon batteries.
Hydrothermal Assisted Microwave Pyrolysis of Water Hyacinth for Electrochemic...drboon
1) Researchers developed a "green" method to produce conductive carbon material from water hyacinth powder for use in electrochemical capacitors. They used hydrothermal assisted microwave pyrolysis to transform the biomass into carbon without significantly changing the pore structure.
2) Characterization showed the carbon contained graphitic carbon nanoparticles and potassium chloride crystals. It also had surface functional groups and electrical conductivity between 0.001-1.5 S/cm, suitable for carbon electrodes.
3) Electrochemical testing found the carbon electrode exhibited non-faradaic capacitive behavior. Its specific capacitance was highest in potassium hydroxide electrolyte and increased by adding graphite or a surface agent.
Electrodeposited nanostructured a-Fe2O3 thin films for solar water splitting:...North Breeze
This document describes a study on the effects of platinum (Pt) doping on the photoelectrochemical performance of nanostructured alpha-iron oxide (α-Fe2O3) thin films deposited via electrodeposition. Un-doped and Pt-doped α-Fe2O3 thin films were characterized using various techniques. The results showed that Pt doping increased the density of small nanoparticles in the films and enhanced the photocurrent density for water splitting by up to a factor of 1.4 compared to un-doped films. The highest photocurrent density of 0.56 mA/cm2 was achieved for a 3% Pt-doped film. Electrochemical impedance analysis also revealed that Pt d
This document describes the room temperature synthesis of copper sulfide (Cu9S5), copper selenide (CuSe), lead sulfide (PbS), and lead selenide (PbSe) by reacting the elemental powders in 2-mercaptoethanol solvent for 24 hours. Characterization by powder X-ray diffraction and Raman spectroscopy showed the products were highly crystalline. Reactions in ethylene glycol also yielded copper sulfide and lead sulfide but reactions in dimercaptoethane did not yield metal chalcogenides. This solvent-mediated room temperature synthesis provides a simple method for producing these metal chalcogenide materials.
Electrochemical properties of myoglobin deposited on multi walled carbon nano...Expand_Lives
We report the direct electrochemical and electrocatalytic properties of myoglobin (MB) on a multi-walled
carbon nanotube/ciprofloxacin (MWCNT/CF) film-modified electrode. A highly homogeneous MWCNT
thin-film was prepared on an electrode surface using ciprofloxacin (CF) as a dispersing agent. MB was
then electrochemically deposited onto the MWCNT/CF-modified electrode. The MB/MWCNT/CF film was
characterized by scanning electron microscopy and UV–visible spectroscopy (UV–vis). UV–vis spectra
confirmed that MB retained its original state on the MWCNT/CF film. Direct electrochemical properties of MB on the MWCNT/CF film were investigated by cyclic voltammetry. The formal potential and
electron transfer rate constant were evaluated in pH 7.2 buffer solution as−0.327 V and 300 s
−1
, respectively. In addition, the MB/MWCNT/CF-modified electrode showed excellent electrocatalytic properties
for the reduction of hydrogen peroxide (H2O2). The MB/MWCNT/CF-modified electrode was used for the
detection of H2O2at concentrations from 1×10
−6
Mto7×10
−4
M in pH 7.2 buffer solution. Overall, the
MB/MWCNT/CF-modified electrode was very stable and has potential for development as a H2O2sensor.
Study the effect of Mn2+ ions on the ac electrical properties of some iron do...IJRES Journal
Oxide glasses doped with transition metal ions are of high interest because of their variant applications in both science and technology fields. However, the normal melt quench method have used to prepared some iron doped phosphate glasses according the following molecular formula: (65-x) mol% P2O5 - 20 mol% Na2O - 15 mol% Fe2O3 - x mol% MnO, Where x= 0, 5,10, 20, 25. The room temperature Mössbauer Effect ME Spectra used to characterized the glassy state homogeneity of these glasses. ME spectra show, for all glasses, no magnetic field participate which mean good glassy state formation. The ac electrical transport properties were also measured, as function of temperature up to 500k. It was found that the ac conductivity increased with the gradual increase of Mn2+ cations, while the electrical activation energy decreased.
This document summarizes the synthesis, characterization, and properties of nickel ferrite (NiFe3O4) nanoparticles. Nickel ferrite was synthesized using a sol-gel technique and sintered at 600°C. X-ray diffraction analysis confirmed the formation of nickel ferrite and showed structural changes due to ion shifting between lattice sites. Scanning electron microscopy images showed agglomerated, porous nanoparticles with an average size of 0.21μm. AC conductivity measurements showed a conductivity of 1.0 x 10-4 S/cm due to dipole polarization. Dielectric properties were also measured as a function of frequency.
Modifying of li ni0.8co0.2o2 cathode material by chemical vapor deposition co...Alexander Decker
The document summarizes research on modifying the cathode material LiNi0.8Co0.2O2 by depositing thin ceramic oxide coatings via chemical vapor deposition to improve its thermal stability. Al2O3 and ZnO coatings were deposited. X-ray diffraction analysis showed the Al2O3 coating did not significantly change the material's structure, while the ZnO coating resulted in a new phase, likely a nickel-zinc compound. Electrochemical testing found the Al2O3-coated material had lower specific capacity in the first cycle but better capacity retention over subsequent cycles compared to the uncoated material. Differential scanning calorimetry also showed the Al2O3 coating reduced the exothermic reaction
This document summarizes the synthesis, characterization, and evaluation of various IrO2-based binary metal oxide electrocatalysts for the oxygen evolution reaction. IrO2, IrxRu1-xO2, IrxSnx-1O2 and IrxTax-1O2 (where x is between 1 and 0.7) were synthesized via an adapted Adams fusion method. X-ray diffraction and electron microscopy showed the materials formed nanocrystalline solid solutions. Electrochemical testing found that adding RuO2, SnO2, or Ta2O5 to IrO2 improved its catalytic performance for oxygen evolution. Specifically, Ir0.7Ru0.3O2 exhibited the best
This document summarizes research on using antimony-impregnated activated carbon as an electrode for detecting heavy metal ions like cadmium and lead using anodic stripping voltammetry. The researchers impregnated activated carbon with different amounts of antimony and found that electrodes with 5% antimony by weight produced the highest peak currents - 29.2 microamps for cadmium and 49.4 microamps for lead in a 100 microgram per liter solution, outperforming previous methods. The results indicate antimony-impregnated activated carbon is an effective working electrode for detecting heavy metals at low concentrations.
This document discusses the structural, vibrational, and microwave dielectric properties of double perovskite ceramics with the formula Ba2Zn1-xCaxWO6 (x = 0-0.4). The samples were sintered at temperatures between 1300-1400°C and characterized using X-ray diffraction, Raman spectroscopy, scanning electron microscopy, and energy dispersive X-ray spectroscopy. The analysis showed that the tolerance factor and temperature coefficient of resonant frequency decreased with increasing calcium content. Microwave dielectric properties such as relative permittivity and quality factor were measured and found to vary with sintering temperature and calcium concentration.
The document describes a method for synthesizing NiFe2O4 nanoparticles fully anchored within a carbon network using a facile pyrolysis technique. Key points:
- NiFe2O4 nanoparticles were synthesized within a carbon network using a polyol-assisted pyrolysis method without an external carbon source.
- Characterization with SEM and TEM showed the NiFe2O4 nanoparticles were uniformly distributed and fully embedded within the carbon network.
- Electrochemical testing showed the NiFe2O4/C anode delivered a reversible capacity of 381.8 mAh/g after 100 cycles at 1C rates and 263.7 mAh/g at a high rate of 5C, demonstrating enhanced performance over bare
IrO2 as an anodic electrocatalyst for the oxygen evolution reaction (OER) in solid polymer electrolyte (SPE)
electrolysers was synthesised by adapting the Adams fusion method. Optimisation of the IrO2 electrocatalyst was achieved
by varying the synthesis duration (0.5 – 4 hours) and temperature (250 - 500°C). The physical properties of the
electrocatalysts were characterised by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and
x-ray diffraction (XRD). Electrochemical characterisation of the electrocatalysts toward the OER was evaluated by
chronoamperometry (CA). CA analysis revealed the best electrocatalytic activity towards the OER for IrO2 synthesised
for 2 hours at 350oC which displayed a better electrocatalytic activity than the commercial IrO2 electrocatalyst used in this
study. XRD and TEM analyses revealed an increase in crystallinity and average particle size with increasing synthesis
duration and temperature which accounted for the decreasing electrocatalytic activity. At 250°C the formation of an active
IrO2 electrocatalyst was not favoured.
This document summarizes research on the electrical conductivity of Ba-Sr-Co-Fe cathode materials for solid oxide fuel cells (SOFCs). Single phase cubic Ba0.5Sr0.5Co1-xFexO3-δ compositions were synthesized via gel combustion and cation complexation routes. Electrical conductivity measurements showed that conductivity initially increased with temperature up to a maximum then decreased, attributed to oxygen loss from the lattice. Fe substitution had little effect on conductivity. While BSCF shows potential as an SOFC cathode, further work is needed to increase conductivity to meet requirements of current IT-SOFCs.
The document discusses nanoparticles for small molecule electrocatalysis, specifically focusing on oxygen evolution reaction (OER) using Ni-Co hydroxides and oxides. It first provides background on OER and discusses how Co3O4, metal-doped Co3O4, and NiCo2O4 can be used as catalysts. It then outlines the purpose and scope of studying the composition dependence of Ni-Co hydroxides and oxides for OER using stainless steel mesh. The document reviews relevant theory around OER mechanisms and properties of different catalyst materials.
This document summarizes a presentation on solid electrolytes. It discusses how solid electrolytes exhibit ionic conductivity through mobile anions or cations, with maximum conductivity between 0.1-10 Ohm-1cm-1. Examples of solid electrolytes mentioned include AgI, β-alumina, and zirconia. Applications discussed include use in batteries, oxygen sensors, and solid oxide fuel cells. The proposed work is to synthesize and characterize Sr and Cu doped LaAlO3 as a potential solid electrolyte material.
This document summarizes the synthesis of zincblende CuInS2 and iron-substituted CuInS2 by reacting colloidal suspensions of binary Cu-S and In-S in ethyleneglycol. Characterization with techniques such as XRD, TEM, UV-Vis and Raman spectroscopy confirmed the formation of phase pure zincblende CuInS2. Following this, quaternary Cu-In-Fe-S with zincblende structure was also synthesized by including iron in the reaction. While zincblende CuInS2 degraded methylene blue dye under visible light, the iron-substituted sample did not show appreciable degradation.
Band edge engineering of composite photoanodes for dye sensitized solar cellsvenkatamanthina
This document discusses engineering the band edges of composite photoanodes for dye-sensitized solar cells through doping. Specifically, it doped ZnO nanorods with cobalt to lower its conduction band minimum and doped TiO2 nanoparticles with zirconium to raise its conduction band minimum in order to overcome an energy barrier preventing electron transfer. Characterization with diffuse reflectance spectroscopy and open circuit voltage measurements under illumination confirmed the doping shifted the band edges as intended. However, dye-sensitized solar cells fabricated with the composite nanostructures did not show improved performance. The paper details a methodology for producing and measuring band edge shifts but notes limitations in applying it to improve device operation.
Zr doped TiO2 nanocomposites for dye sensitized solar cellsvenkatamanthina
This document discusses engineering the band edges of a composite photoanode for dye-sensitized solar cells through doping. ZnO nanorods were doped with cobalt to lower their conduction band minimum energy, and TiO2 nanoparticles were doped with zirconium to raise their conduction band minimum energy. This was done to overcome an energy barrier that previously prevented electron transfer from TiO2 to ZnO in the composite. Characterization showed the doping incorporated into the materials as desired without other changes. Open circuit photovoltage measurements indicated the doping shifted the band energies to enable electron transfer, but devices using the materials did not show improved performance. The methodology for producing and measuring band edge shifts through doping is detailed.
Surface Activation of C-sp3 in Boron-Doped Diamond ElectrodeAlejandro Medel
Abstract C-sp2 (graphite) impurities are undesirable in synthetic diamond electrodes (C-sp3), because they can affect the electrochemical response. In this work, we demonstrate that Csp3 surfaces can be activated successfully by applying an anodic current density corresponding to sufficiently high potential where the hydroxyl radicals (●OH) are generated. The
effectiveness of this activation process was verified by Raman spectroscopy, X-ray diffraction, scanning electron microscopy, and cyclic voltammetry.
The document summarizes a study that characterized the corrosion of a nickel-aluminum (Ni-Al) composite coating compared to a pure nickel coating after 72 hours of immersion in 2M NaCl solution. Electrochemical impedance spectroscopy and potentiodynamic polarization techniques were used, and scanning electron microscopy was used to examine the corrosion product layers. Results showed the Ni-Al composite had a porous, cracked corrosion product layer that decreased corrosion potential and increased corrosion currents compared to the more protective layer formed on pure nickel. Thus, the Ni-Al composite exhibited lower corrosion resistance than pure nickel in the higher chloride concentration solution.
Direct Synthesis Carbon/Metal Oxide Composites for Electrochemical Capacitors...drboon
This paper deals with the study of the carbon/metal oxide composites synthesis for electrochemical capacitor electrode material. Transition metal salts, such as FeCl3 and TiCl3 act as activator in the synthesis of activated carbon from gelam wood sawdust (Melaleuca cajuputi Powell) which also have the functions as substrates for the composites. The surface functionalities of activated carbons were modified using oxidative treatments. The changes on crystallography and surface functionalities were analyzed based on XRD and FTIR data. The electrical conductivities and electrochemical properties were determined using kelvin and cyclic voltammetry methods, respectively. FTIR analyses showed that the activation and oxidation treatments affected their surface functionalities. The XRD analyses showed that oxidative treatments also affected carbons crystallite. The electrical conductivities and electrochemical properties were influenced by their crystallite and surface functionalities. The shape of the cyclic voltammograms varied according to the changes on the surface functionalities and on the metals loading. TEM analyses indicated the existence of nanoparticles metal oxides in the carbon samples.
2021 influence of basic carbon additives on the electrochemical performance ...Ary Assuncao
This study investigates the effect of carbon surface basicity on the electrochemical performance and dynamic charge acceptance of lead-carbon batteries. Five activated carbons with different pH values ranging from 9.5 to 11.1 were prepared by ammonia and hydrogen gas treatments. Cyclic voltammetry showed that the hydrogen evolution reaction activity increased with higher carbon surface basicity. Testing of lead-carbon electrodes found a correlation between carbon pH and dynamic charge acceptance, with higher pH carbons showing improved charge currents and final dynamic charge acceptance. The carbon content also affected charge currents during simulated microcycles, demonstrating that surface chemistry and amount of carbon additive both influence the electrochemical properties and performance of lead-carbon batteries.
Hydrothermal Assisted Microwave Pyrolysis of Water Hyacinth for Electrochemic...drboon
1) Researchers developed a "green" method to produce conductive carbon material from water hyacinth powder for use in electrochemical capacitors. They used hydrothermal assisted microwave pyrolysis to transform the biomass into carbon without significantly changing the pore structure.
2) Characterization showed the carbon contained graphitic carbon nanoparticles and potassium chloride crystals. It also had surface functional groups and electrical conductivity between 0.001-1.5 S/cm, suitable for carbon electrodes.
3) Electrochemical testing found the carbon electrode exhibited non-faradaic capacitive behavior. Its specific capacitance was highest in potassium hydroxide electrolyte and increased by adding graphite or a surface agent.
Electrodeposited nanostructured a-Fe2O3 thin films for solar water splitting:...North Breeze
This document describes a study on the effects of platinum (Pt) doping on the photoelectrochemical performance of nanostructured alpha-iron oxide (α-Fe2O3) thin films deposited via electrodeposition. Un-doped and Pt-doped α-Fe2O3 thin films were characterized using various techniques. The results showed that Pt doping increased the density of small nanoparticles in the films and enhanced the photocurrent density for water splitting by up to a factor of 1.4 compared to un-doped films. The highest photocurrent density of 0.56 mA/cm2 was achieved for a 3% Pt-doped film. Electrochemical impedance analysis also revealed that Pt d
This document describes the room temperature synthesis of copper sulfide (Cu9S5), copper selenide (CuSe), lead sulfide (PbS), and lead selenide (PbSe) by reacting the elemental powders in 2-mercaptoethanol solvent for 24 hours. Characterization by powder X-ray diffraction and Raman spectroscopy showed the products were highly crystalline. Reactions in ethylene glycol also yielded copper sulfide and lead sulfide but reactions in dimercaptoethane did not yield metal chalcogenides. This solvent-mediated room temperature synthesis provides a simple method for producing these metal chalcogenide materials.
Electrochemical properties of myoglobin deposited on multi walled carbon nano...Expand_Lives
We report the direct electrochemical and electrocatalytic properties of myoglobin (MB) on a multi-walled
carbon nanotube/ciprofloxacin (MWCNT/CF) film-modified electrode. A highly homogeneous MWCNT
thin-film was prepared on an electrode surface using ciprofloxacin (CF) as a dispersing agent. MB was
then electrochemically deposited onto the MWCNT/CF-modified electrode. The MB/MWCNT/CF film was
characterized by scanning electron microscopy and UV–visible spectroscopy (UV–vis). UV–vis spectra
confirmed that MB retained its original state on the MWCNT/CF film. Direct electrochemical properties of MB on the MWCNT/CF film were investigated by cyclic voltammetry. The formal potential and
electron transfer rate constant were evaluated in pH 7.2 buffer solution as−0.327 V and 300 s
−1
, respectively. In addition, the MB/MWCNT/CF-modified electrode showed excellent electrocatalytic properties
for the reduction of hydrogen peroxide (H2O2). The MB/MWCNT/CF-modified electrode was used for the
detection of H2O2at concentrations from 1×10
−6
Mto7×10
−4
M in pH 7.2 buffer solution. Overall, the
MB/MWCNT/CF-modified electrode was very stable and has potential for development as a H2O2sensor.
Study the effect of Mn2+ ions on the ac electrical properties of some iron do...IJRES Journal
Oxide glasses doped with transition metal ions are of high interest because of their variant applications in both science and technology fields. However, the normal melt quench method have used to prepared some iron doped phosphate glasses according the following molecular formula: (65-x) mol% P2O5 - 20 mol% Na2O - 15 mol% Fe2O3 - x mol% MnO, Where x= 0, 5,10, 20, 25. The room temperature Mössbauer Effect ME Spectra used to characterized the glassy state homogeneity of these glasses. ME spectra show, for all glasses, no magnetic field participate which mean good glassy state formation. The ac electrical transport properties were also measured, as function of temperature up to 500k. It was found that the ac conductivity increased with the gradual increase of Mn2+ cations, while the electrical activation energy decreased.
This document summarizes the synthesis, characterization, and properties of nickel ferrite (NiFe3O4) nanoparticles. Nickel ferrite was synthesized using a sol-gel technique and sintered at 600°C. X-ray diffraction analysis confirmed the formation of nickel ferrite and showed structural changes due to ion shifting between lattice sites. Scanning electron microscopy images showed agglomerated, porous nanoparticles with an average size of 0.21μm. AC conductivity measurements showed a conductivity of 1.0 x 10-4 S/cm due to dipole polarization. Dielectric properties were also measured as a function of frequency.
Modifying of li ni0.8co0.2o2 cathode material by chemical vapor deposition co...Alexander Decker
The document summarizes research on modifying the cathode material LiNi0.8Co0.2O2 by depositing thin ceramic oxide coatings via chemical vapor deposition to improve its thermal stability. Al2O3 and ZnO coatings were deposited. X-ray diffraction analysis showed the Al2O3 coating did not significantly change the material's structure, while the ZnO coating resulted in a new phase, likely a nickel-zinc compound. Electrochemical testing found the Al2O3-coated material had lower specific capacity in the first cycle but better capacity retention over subsequent cycles compared to the uncoated material. Differential scanning calorimetry also showed the Al2O3 coating reduced the exothermic reaction
This document summarizes the synthesis, characterization, and evaluation of various IrO2-based binary metal oxide electrocatalysts for the oxygen evolution reaction. IrO2, IrxRu1-xO2, IrxSnx-1O2 and IrxTax-1O2 (where x is between 1 and 0.7) were synthesized via an adapted Adams fusion method. X-ray diffraction and electron microscopy showed the materials formed nanocrystalline solid solutions. Electrochemical testing found that adding RuO2, SnO2, or Ta2O5 to IrO2 improved its catalytic performance for oxygen evolution. Specifically, Ir0.7Ru0.3O2 exhibited the best
This document summarizes research on using antimony-impregnated activated carbon as an electrode for detecting heavy metal ions like cadmium and lead using anodic stripping voltammetry. The researchers impregnated activated carbon with different amounts of antimony and found that electrodes with 5% antimony by weight produced the highest peak currents - 29.2 microamps for cadmium and 49.4 microamps for lead in a 100 microgram per liter solution, outperforming previous methods. The results indicate antimony-impregnated activated carbon is an effective working electrode for detecting heavy metals at low concentrations.
This document discusses the structural, vibrational, and microwave dielectric properties of double perovskite ceramics with the formula Ba2Zn1-xCaxWO6 (x = 0-0.4). The samples were sintered at temperatures between 1300-1400°C and characterized using X-ray diffraction, Raman spectroscopy, scanning electron microscopy, and energy dispersive X-ray spectroscopy. The analysis showed that the tolerance factor and temperature coefficient of resonant frequency decreased with increasing calcium content. Microwave dielectric properties such as relative permittivity and quality factor were measured and found to vary with sintering temperature and calcium concentration.
The document describes a method for synthesizing NiFe2O4 nanoparticles fully anchored within a carbon network using a facile pyrolysis technique. Key points:
- NiFe2O4 nanoparticles were synthesized within a carbon network using a polyol-assisted pyrolysis method without an external carbon source.
- Characterization with SEM and TEM showed the NiFe2O4 nanoparticles were uniformly distributed and fully embedded within the carbon network.
- Electrochemical testing showed the NiFe2O4/C anode delivered a reversible capacity of 381.8 mAh/g after 100 cycles at 1C rates and 263.7 mAh/g at a high rate of 5C, demonstrating enhanced performance over bare
The document characterizes the electrochemical corrosion behavior of a Ni-28wt.%Al composite coating compared to a pure Ni coating after 24 and 72 hours of immersion in 3.5% NaCl solution. Open circuit potential and polarization tests showed that the Al particles in the composite shifted the potential more negatively and increased the anodic dissolution rate after 24 hours compared to pure Ni. However, after 72 hours the composite exhibited lower anodic current density and slightly higher cathodic current than pure Ni. XPS analysis indicated the composite surface rapidly formed a protective Ni(OH)2 layer that thickened over time and became enriched with the highly corrosion resistant Al2O3, decreasing the corrosion rate and susceptibility to pitting for the composite
This document summarizes a study that developed a new hybrid electrocatalyst for oxygen evolution reaction (OER) by anchoring cobalt oxide (Co3O4) nanoparticles onto titanium carbide (Ti3C2) MXene nanosheets. The Co3O4/MXene hybrid (denoted CM) was synthesized using a solvothermal method. Characterization showed uniform distribution of small Co3O4 nanoparticles on MXene nanosheets. Electrochemical tests found the CM catalyst achieved overpotential of 300 mV at 10 mA/cm2 for OER, which was lower than Co3O4 or MXene alone. The enhanced performance was attributed to strong interactions and charge transfer between
This document summarizes the synthesis, structure, and resistivity properties of KxBa1-xNbO3 (0.2x<0.5) and K0.2Sr0.8NbO3 compounds. The compounds were synthesized using high-pressure high-temperature techniques. They crystallize in an ideal perovskite structure with a cubic structure. The a parameter increases with increasing Ba concentration, corresponding to a decrease in Nb valence. Resistivity measurements show semiconducting behavior for the K-containing compounds, but the increase in resistivity with decreasing temperature is smaller for phases with lower Nb valence. BaNbO3 shows metallic-like behavior down to 4.2K.
2018 khodan an-porous monoliths consisting of aluminum oxyhydroxide nanofibrilsAnatoleNKhodan
Abstract We present a study on the chemical and structural transformations in highly porous monolitic materials consisting of the nanofibrils of aluminum oxyhydroxides (NOA, Al2O3·nH2O) in the temperature range 20– 1700 °C. A remarkable property of the NOA material is the preservation of the monolithic state during annealing over the entire temperature range, although the density of the monolith increases from ~0.02 up to ~3 g/cm3, the total porosity decreases from 99.3 to 25% and remains open up to 4 h annealing at the temperature ~1300 °C. The physical parameters of NOA monoliths such as density, porosity, specific area were studied and a simple physical model describing these parameters as the function of the average size of NOA fibrils—the basic element of 3D structure—was proposed. The observed thermally induced changes in composition and structure of NOA were successfully described and two mechanisms of mass transport in NOA materials were revealed. (i) At moderate temperatures (T ≤ 800 °C), the mass transport occurs along a surface of amorphous single fibril, which results in a weak decrease of the length-to-diameter aspect ratio from the initial value ~24 till ~20; the corresponding NOA porosity change is also small: from initial ~99.5 to 98.5%. (ii) At high temperatures (T > 800 °C), the mass transport occurs in the volume of fibrils, that results in changes of fibrils shape to elliptical and strong decrease of the aspect ratio down to ≤ 2; the porosity of NOA decreases to 25%. These two regimes are characterized by activation energies of 28 and 61 kJ/mol respectively, and the transition temperature corresponds to the beginning of γ-phase crystallization at 870 °C.
The document investigates the effects of varying deposition parameters on the structure and corrosion resistance of hydroxyapatite (HA) coatings electrodeposited onto Ti-6Al-4V alloy samples. X-ray diffraction and scanning electron microscopy were used to characterize the crystal structure and morphology of the coatings deposited under different conditions. Potentiodynamic polarization measurements in simulated body fluid evaluated the corrosion behavior. The optimal deposition parameters were found to be an applied voltage of 9 volts, pH value of 5.5, temperature of 25°C, and deposition time of 30 minutes, which yielded coatings with the best structural and corrosion-resistant properties.
2014 Journal of Power Sources 247 (2014) 572-578Alexis B. B
The document summarizes research on the durability of a nickelealuminum layered double hydroxide/carbon (NieAl LDH/C) composite as a cathode material in nickel metal hydride batteries. The composite was prepared using a liquid phase deposition method and optimized to contain 19.2 mol% aluminum. Electrochemical testing was conducted over 869 charge/discharge cycles at two different current regimes: 5 mA for 300 cycles in half-cell conditions and 5.8 mA for 569 cycles in battery regime. The composite exhibited good lifespan and stability, maintaining a capacity retention above 380 mAh/g. Cyclic voltammetry and X-ray diffraction analysis showed that the a-Ni
Few-layered MoSe2 nanosheets an an advanced...suresh kannan
This document summarizes the synthesis and characterization of few-layered molybdenum diselenide (MoSe2) nanosheets as an electrode material for supercapacitors. The MoSe2 nanosheets were synthesized using a facile hydrothermal method. Characterization with Raman spectroscopy, TEM, and XRD confirmed the formation of few-layered nanosheets. Electrochemical testing of the MoSe2 electrode in a symmetric cell configuration showed a maximum specific capacitance of 198.9 F g−1 and capacitance retention of approximately 75% after 10,000 cycles, indicating potential for supercapacitor applications.
Carbon-cuprous oxide composite nanoparticles
were chemically deposited on surface of thin glass tubes of spent
energy saving lamps for solar heat collection. Carbon was
obtained from fly ash of heavy oil incomplete combustion in
electric power stations. Impurities in the carbon were removed by
leaching with mineral acids. The mineral free-carbon was then
wet ground to have a submicron size. After filtration, it was
reacted with concentrated sulfuric/fuming nitric acid mixture on
cold for 3-4 days. Potassium chlorate was then added drop wise on
hot conditions to a carbon slurry followed by filtration.
Nanocarbon sample was mixed with 5% by weight PVA to help
adhesion to the glass surface. Carbon so deposited was doped with
copper nitrate solution. After dryness, the carbon/copper nitrate
film was dipped in hydrazine hydrate to form cuprous oxide -
carbon composite, It was then roasted at 380-400 °C A heat
collector testing assembly was constructed of 5 glass coils
connected in series with a total surface area of 1250 cm2
. Heat
collection was estimated by water flowing in the glass coils that
are coated with the carbon/copper film,. Parameters affecting the
solar collection efficiency such as time of exposure and mass flow
rate of the water were studied. Results revealed that the prepared
glass coil has proven successful energy collector for solar heat.
Thermoelectric Power Studies of Ni-Co Nano Ferrites Synthesized By Citrate-Ge...IOSR Journals
This document reports on a study of the thermoelectric power of nickel-cobalt nanoferrites with the chemical formula Ni1-xCoxFe2O4 (where x = 0, 0.2, 0.4, 0.6, 0.8, 1.0) synthesized using the citrate-gel auto combustion method. X-ray diffraction analysis confirmed the formation of a single cubic spinel phase without impurities. Lattice parameters increased with increasing cobalt content due to the larger ionic radius of Co2+ ions compared to Ni2+ ions. Seebeck coefficient measurements from 320K to above the Curie temperature showed that the materials behaved as n-type semiconductors and the
2014-Nitrogen-doped hollow activated carbon nanofibers as high.pdfAshirvathamD
This document summarizes research on nitrogen-doped hollow activated carbon nanofibers (HACNFs) as electrode materials for supercapacitors. Key findings include:
1) HACNFs were prepared via concentric electrospinning and NH3 activation, resulting in a unique hollow structure and high nitrogen doping (up to 8.2%).
2) The HACNFs exhibited a high specific capacitance of 197 F/g, 1.33 times that of solid nanofibers, due to their hollow architecture and nitrogen doping.
3) The HACNFs also demonstrated excellent rate capability (72.1% retention at 20 A/g) and cycling stability
The document summarizes a study that demonstrated the ability to tune the size of large-diameter, few-walled nitrogen-doped carbon nanotubes (N-CNTs) from 50-150 nm by varying the transition metal (TM) used during synthesis. Fe produced the largest tubes, followed by Co and Ni, while Mn resulted in a clot-like morphology. Electrocatalytic activity for the oxygen reduction reaction (ORR) followed the trend Fe > Co > Ni > Mn. Fe-derived N-CNTs exhibited the highest surface area and nitrogen incorporation, contributing to their high ORR activity. This work provides a new route for developing advanced nonprecious metal catalysts by controlling carbon nanot
Influence of La3+ substitution on dielectric, ferroelectric and electrocalori...Mohammad Azam
Outline
Motivation
Dielectric properties of materials
Ferroelectric and Antiferroelectric
Electrocaloric Effect (EC)
Sample preparation method
Characterization techniques
Result and Discussion
Future Work
References
Role of the morphology and surface planes on the catalytic activity of spinel...Science Padayatchi
The electrocatalytic activity of the spinel oxide LiMn1.5Ni0.5O4 with
different morphologies (cubic, spherical, octahedral, and truncated octahedral) has been
investigated for the oxygen evolution reaction (OER) in alkaline solutions that is of
interest for metal−air batteries. The OER activity increases in the order truncated
octahedral < cubic < spherical < octahedral, despite a larger surface area (2.9 m2 g−1) for
the spherical sample compared to nearly similar surface areas (0.3−0.7 m2 g−1) for the
other three samples. The high activity of the octahedral sample is attributed to the
regular octahedral shape with low-energy {111} surface planes, whereas the lowest
activity of the truncated octahedral sample is attributed to the high-energy {001} surface
planes. The octahedral sample also exhibits the lowest Tafel slope of 70 mV dec−1 with
the highest durability whereas the truncated octahedral sample exhibits the highest Tafel
slope of 120 mV dec−1 with durability similar to the cubic and spherical samples. The
study demonstrates that the catalytic activities of oxide catalysts could be tuned and
optimized by controlling the surface morphologies/planes via novel synthesis approaches.
Fabrication and electrical characteristic of quaternary ultrathin hf tiero th...Alexander Decker
This document describes the fabrication and electrical characterization of quaternary ultrathin HfTiErO thin films grown by RF sputtering for MOS devices. HfTiErO thin films with different Ti and Er contents were deposited on silicon substrates. The films were annealed at 500°C and 700°C. Atomic force microscopy showed the surface roughness decreased with annealing. X-ray photoelectron spectroscopy analysis showed the chemical compositions. MOS capacitors were fabricated and capacitance-voltage measurements showed the annealed films at 500°C had improved electrical properties like higher dielectric constant. The HfTiErO film with composition HfTi6Er4O annealed at 500°C achieved the best electrical performance of the
Multistage Activation of Anthracite Coal-Based Activated Carbon for High-Perf...GuanrongSong1
An anthracitic coal-derived activated porous carbon is proposed as a promising carbon electrode material for
supercapacitor (SC) applications. The specific capacitance of this activated carbon SC electrode is related to the characteristics, such
as specific surface area, pore size distribution, wettability, and conductivity. In the present work, a series of anthracite-based activated
carbons (ABAC) were prepared via a multistage activation process and used as electrode materials for SCs. The multistage activation
experiment was developed by exploring different activation temperatures, precursor/activating agent mass ratios, and process treating
environments. The electrochemical performance of ABACs was evaluated in a three-electrode testing system. Multiple electrolytes
were utilized, such as 1 M sulfuric acid (H2SO4) and 1 and 6 M potassium hydroxide (KOH) solutions. An optimum ABAC
electrode was obtained, characterized by its largest wettability and superior conductivity, and achieved excellent electrochemical
performance. The three-electrode system exhibited a specific capacitance of 288.52 and 260.30 F/g at 0.5 A/g in the 1 M H2SO4 and
6 M KOH electrolytes, respectively. It was found that moderate multistage activation temperatures are beneficial for the electrolyte
uptake which enhances the specific capacitance. The high content of the oxygen functional groups on the activated carbon surface
greatly improved its specific capacitance due to the increase in wettability. In the 1 M H2SO4 electrolyte, the working electrode
exhibited better performance than in 1 M KOH because the ion diameter in the acidic electrolyte was more suitable for pore
diffusion. The concentrated KOH electrolyte leads to an increase in specific capacitance due to increased ions being adsorbed by a
certain number of the hydrophilic pores. Moreover, the specific capacitance of the optimum ABAC sample remained at 95.4% of the
initial value after 1000 galvanostatic charge−discharge tests at 0.5 A/g, which is superior to the performance of SC grade commercial
carbon.
International Journal of Engineering Research and Applications (IJERA) is an open access online peer reviewed international journal that publishes research and review articles in the fields of Computer Science, Neural Networks, Electrical Engineering, Software Engineering, Information Technology, Mechanical Engineering, Chemical Engineering, Plastic Engineering, Food Technology, Textile Engineering, Nano Technology & science, Power Electronics, Electronics & Communication Engineering, Computational mathematics, Image processing, Civil Engineering, Structural Engineering, Environmental Engineering, VLSI Testing & Low Power VLSI Design etc.
1. Preparation of mesoporous microspheres of NiO with high surface area
and analysis on their pseudocapacitive behavior
Syed Asad Abbasa,b
, Kwang-Deog Junga,b,
*
a
Center for Clean Energy and Chemical Engineering, Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul 136-791, Republic of
Korea
b
Clean Energy and Chemical Engineering, University of Science and Technology, 217 Gajeong-ro Yuseong-gu, Daejeon, Republic of Korea
A R T I C L E I N F O
Article history:
Received 25 August 2015
Received in revised form 26 January 2016
Accepted 9 February 2016
Available online 11 February 2016
Keywords:
Mesoporous microspheres of NiO
a-Ni(OH)2
Oleylamine method
hydrothermal method
Pseudocapacitor
A B S T R A C T
Nickel oxide with a high surface area showing high capacitance is reported here. Mesoporous
microspheres (MMS) of 250NiO, 300NiO, 350NiO, 400NiO and 500NiO are synthesized by calcining
mesoporous a-Ni(OH)2 at 250
C, 300
C, 350
C, 400
C, and 500
C, respectively. The mesoporous a-Ni
(OH)2 was prepared by a hydrothermal method. 250NiO has the highest specific surface area of 295 m2
/g,
and a high specific capacitance of 1,140 F gÀ1
at a current density of 10 A gÀ1
from galvanostatic discharge
measurements. The cyclic voltammetry, galvanostatic discharge measurement and electrochemical
impedance analysis exhibited that the pseudocapacitive behavior is more clarified for NiO prepared at
higher calcination temperature. Apparently, the high specific capacitance of 250NiO results from the
mesoporous pores and high specific surface area enhancing the transportation of ions during the
charging and discharging process to store high energy. The power density and energy density of
the 250NiO are 2.5 kW kgÀ1
and 59 W h kgÀ1
respectively at the current density of 10 A gÀ1
.
ã 2016 Elsevier Ltd. All rights reserved.
1. Introduction
Recently, supercapacitors have received increasing attention
due to their ability to store massive amounts of energy [1–3].
Supercapacitors have distinct advantages over the other storage
devices such as batteries in terms of high power delivery, long life
span, high cycle efficiency and wide working temperature range
[1]. Due to these advantages, supercapacitors meet the energy
storage requirements of electric devices requiring high electric
density such as electric vehicles [4]. Supercapacitors are also useful
for the applications such as backing-up for uninterruptible power,
absorbing power during the short periods of generation such as
regenerative braking, and storing renewable energies such as wind
and solar energy [5].
Based on energy storage principals, an electrochemical capaci-
tor (EC) can be categorized as either a pseudocapacitor or an
electric double layer capacitor [6,7]. Transition metal oxides,
conducting a reversible redox reaction, are generally used as
pseudocapacitors due to their excellent pseudocapacitance
behaviour [8]. RuO2, MnO2, Fe3O4 and Co3O4 have been intensively
studied in the past as peudocapacitance materials [9,10], RuO2 has
been the most extensively studied due to its wide potential
window, long life cycle and high specific capacitance, but it is too
expensive to be used for general purposes [11].
Theoretically, NiO has been known to be a good candidate
to replace RuO2, because the theoretical capacitance of NiO
(2,573 F gÀ1
) is much higher than that of RuO2 (1,360 F gÀ1
for
RuO2Á0.5H2O). NiO has not only a high theoretical capacitance, but
also good thermal and chemical stability [12]. Recently, it was
proposed that NiO or Ni(OH)2 should not be classified as
pseudocapacitive material [13]. On the other hand, nanostructured
Ni(OH)2 was treated as a pseudocapacitor by identifying the charge
storage mechanism rather than basing the claim on the material
type alone [14,15]. Nonetheless, a lot of papers have been published
with the pseudocapacitive nature of NiO. Different kinds of Nickel
oxide morphologies are reported to achieve improved capacitance
values [16]. A high capacitance of 405 F gÀ1
at a current density of
0.5A gÀ1
is reported by Shenglin et al. through mesoporous
nanotubes [17]. Similarly, Shujiang et al. achieved specific
capacitance of 415 F gÀ1
at a current density of 3A gÀ1
using
hollow spheres of NiO with a specific surface area of 62 m2
gÀ1
[18].
Recently, NiO prepared by a microwave-assisted gas/liquid method
showed specific capacitance of 770 F gÀ1
and 585 F gÀ1
at discharge
currents of 2 A gÀ1
and 5 A gÀ1
[19].
* Corresponding author at: Center for Clean Energy and Chemical Engineering,
Korea Institute of Science and Technology, Hwarangno 14-gil 5, Seongbuk-gu, Seoul
136-791, Republic of Korea. Tel.:+ +822 958 5218; fax: +822 958 5219.
E-mail addresses: jkdcat@kist.re.kr, jkdyym@hanmail.net (K.-D. Jung).
http://dx.doi.org/10.1016/j.electacta.2016.02.054
0013-4686/ã 2016 Elsevier Ltd. All rights reserved.
Electrochimica Acta 193 (2016) 145–153
Contents lists available at ScienceDirect
Electrochimica Acta
journal homepage: www.elsevier.com/locate/electacta
2. In the current work, we prepared mesoporous microspheres
(MMS) of NiO with ultra-high capacitance. Alfa nickel hydroxide
spheres are first prepared by a hydrothermal process, followed by
calcination at 250
C, 300
C, 350
C, 400
C, and 500
C to produce
MMS of NiO. The prepared NiO samples are expected to have high
specific capacitance because of their high specific surface area and
mesoporous structures. These characteristics will allow better
contact between electrolyte and electrode for the transfer of
electrons and ions, presumably leading to high energy storage
capacity. The cyclic voltammetry, galvanostatic discharge meas-
urements and electrochemical impedance spectroscopy were
performed to investigate the pseudocapacitive behaviour of the
MMS of NiO.
2. Experimental
2.1. Material Preparation
2.1.1. Synthesis of a-Ni(OH)2
In a typical procedure, 4 mmol (1.164 g) of nickel nitrate
hexahydrate Ni (NO3)2.6H2O was dissolved in 80 mL of ethanol
(99.9%) under continuous magnetic stirring for 10 minutes.
Next, 8 mL of oleylamine (Aldrich, 70%) and 40 mL of ethanol
was added simultaneously and under constant stirring to get a
homogeneous solution. The mixed solution was then trans-
ferred and sealed in a 200 mL Teflon coated autoclave and
placed in a convection oven for 15 hours at 180
C. In this study
we also prepared alfa nickel hydroxide at 160
C and 200
C, and
studied the effect of cooking time as well. The resulting green
a-Ni(OH)2 powder was collected after cooling the autoclave at
room temperature. The powder was washed vigorously with
distilled water, cyclohexane and ethanol to remove organics,
ions and other remnants followed by drying at 60
C under
vacuum for four hours.
2.1.2. Synthesis of NiO mesoporous microspheres
Five NiO samples were produced simply by heating a-Ni(OH)2
at the rate of 2
C minÀ1
in air, to five different temperatures:
250
C, 300
C, 350
C, 400
C, and 500
C. The samples prepared at
these different temperatures are designated as 250NiO, 300NiO,
350NiO, 400NiO and 500NiO.
2.2. Materials characterization
In-situ X-ray diffraction (HT-XRD, Pananalytical X’pert Pro,
Netherlands) of powder samples were recorded with Cu Ka
radiation (l= 1.5406 Å) to confirm the formation of NiO. The
morphology and structure of the samples were characterized by
in-situ transmission electron microscopy (TEM, Model No: JEM
3011 (HR), JOEL Ltd, Japan). Specific surface area, pore size
distribution and pore volume were measured by a BET analyzer
(Belsorp II mini, BEL Japan, Inc.). The thermal behavior of the
samples were characterized by a thermogravimetric analysis (TGA,
SDT Q 600 U.S.A.) at a ramping rate of 2
C minÀ1
in air from room
temperature to 700
C.
2.3. Electrochemical Measurements
The working electrode was prepared by mixing 70 wt % of the
prepared NiO (active material), 20 wt % acetylene black (conduct-
ing agent) and 10 wt % polyvinylidene difluoride (PVDF, Aldrich) as
binder. This mixture was then pressed on a glassy carbon electrode
and dried at 60
C for two hours. Electrochemical measurements
were carried out in a typical three-electrode cell.
The cyclic voltammetry (CV) analysis of prepared electrodes
was performed in the potential range from 0.0 V to 0.5 V in aqueous
solution of 2 M KOH with Ag/AgCl as a reference electrode and
platinum foil as a counter electrode.
Galvanostatic charge and discharge measurements were
carried out to determine the electrochemical capacitance in the
three-electrode system at current densities of 3, 5 and 10 A gÀ1
.
Active material as the working electrode, Pt foil electrode as the
counter electrode and Ag/AgCl electrode as the reference electrode
were used in the potential range of 0 V to 0.5 volts in aqueous
solution of 2 M KOH.
Electrochemical impedance spectroscopy (EIS) measurements
were performed at 0.4 V vs Ag/AgCl from 100 kHz to 0.1 Hz in
aqueous solution of 2 M KOH.
Fig. 1. XRD patterns and TEM images of a-Ni(OH)2 samples prepared by hydrothermal reaction at (a) 160
C, (b) 180
C and (c) 200
C.
146 S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153
3. 3. Results and discussion
3.1. Preparation and Characterization of a-Ni(OH)2
Alfa nickel hydroxide was prepared at three different temper-
atures of 160
C, 180
C and 200
C in an autoclave. Fig. 1 shows the
XRD patterns and TEM images of the prepared samples at 160,
180 and 200
C. All three samples show the same XRD patterns. The
characteristic peaks at 2u values of 11.4
(003), 22.8
(006) and
33.5
(006) in the XRD patterns correspond to a-Ni(OH)2 with a
rhombohedral structure (JCPDS card no. 380715). The mesoporous
NiO spherical particles with hairs were resulted from the
hydrothermal reaction at 160
C and 180
C, while the NiO hollow
spheres were prepared at 200
C. The mechanism from oleylamine
in nanoparticle synthesis was suggested as the hollow sphere
appeared first and the core could be filled, increasing the reaction
time [20]. On the other hand, the morphology did not change with
respect to the hydrothermal reaction time here (Fig. S1), but could
be decided by the reaction temperature (Fig.1). Nam et al. prepared
solid CoO at 200
C and hollow Co nanoparticles at 290
C [21]. The
formation of the hollow spheres can be related to the decomposi-
tion reaction of oleylamine as suggested by Nam et al. The resulting
a-Ni(OH)2 samples (Fig.S2) follows a type IV isotherm, which is
typical for mesoporous material [22]. BET surface areas of the
a-Ni(OH)2 samples at 160
C, 180
C and 200
C are 109 m2
gÀ1
,
176 m2
gÀ1
and 109 m2
gÀ1
, respectively. Pore volumes of the
a-Ni(OH)2 samples at 160
C, 180
C and 200
C are 0.20 cm3
/g,
0.44 cm3
gÀ1
, 0.27 cm3
gÀ1
respectively. It should be noted that the
surface area of mesoporous micro sphere (MMS) of a-Ni(OH)2 at
180
C is the highest among the prepared a-Ni(OH)2 samples.
3.2. Preparation and characterization of NiO
Fig. 2 shows thermogravimetric and differential thermal
analysis (TGA and DTA) curves of MMS of a-Ni(OH)2 prepared
by hydrothermal process at 180
C, which had the highest surface
area of 176 m2
/g.
TGA and DTA analysis were conducted with a-Ni(OH)2 sample
prepared at 180
C from room temperature to 700
C. The weight
loss of 3.7 wt % up to 130
C is due to dehydration of adsorbed water
on the a-Ni(OH)2 sample and the DTA curve in that temperature
range show a broad endothermic curve. The weight loss of 24.9 wt
% from 130
C is due to dehydration and dehydroxylation of the
a-Ni(OH)2ÁxH2O. The x value is estimated to be about 0.4.
However, DTA shows both exothermic and endothermic curves
in the temperature range from 150 to 350
C. The exothermic curve
may be due to oxidation of the organic compounds. It was shown
that the oleylamine was decomposed and the functional groups
were complexed with metal during the nanoparticle formation
using oleylamine [23]. Major weight loss is observed at 200
C
$ 260
C, which is due to phase transformation of nickel hydroxide
to nickel oxide according to the following equation [24]:
NiðOHÞ2 ! NiO þ H2O ð1Þ
There are no weight losses in the temperature ranges above 500
C.
Fig. 3 shows XRD patterns of the a-Ni(OH)2 particles prepared
by a hydrothermal method. The XRD patterns were obtained by an
in-situ XRD instrument from 50 to 500
C with steps of 50
C. The
structure of a-Ni(OH)2 did not change up to 200
C, indicating that
the weight loss up to 200
C in the TGA/DTA analysis is not due to
dehydroxylation, but due to water bonded to a-Ni(OH)2.
It is shown that a-Ni(OH)2 is transformed into NiO at 250
C. At
250
C, characteristic peaks of NiO clearly appear and all five
possible peaks are observed on XRD pattern, which are in good
match with JCPDS file (04-005-9695). Individual peaks at 2u values
of 37
, 43
, 62.4
, 74.7
and 78.8
Can be identified as (111), (200),
(220), (311) and (222) planes of NiO, respectively. FWHM (full
width half maximum) of the peak at 43
decreased with increasing
calcination temperature.
The Scherer equation (t= 0.9l/B cosuB) was used to find the
crystal size of NiO prepared at different calcination temperatures.
The crystal size of NiO increased with an increase in calcination
temperature. The crystal sizes of 250NiO, 300NiO, 350NiO, 400NiO
and 500NiO are 1.5 nm, 5.4 nm, 9.9 nm, 15.7 nm and 35.4 nm,
respectively.
Fig. 4 shows the TEM images of the prepared NiO samples using
in-situ transmission electron microscopy (TEM). The morphology
of 250NiO is similar to that of a-Ni(OH)2, although a-Ni(OH)2 is
transformed into NiO as shown in XRD patterns (Fig. 3). The
particle size of 250NiO spheres is ranging from 1.5 mm to 3 mm. The
shape and size of NiO spheres are not changed until the calcination
temperature reached 250
C. The MMS spheres starts to be
agglomerated at the temperature higher than 250
C. The spherical
shape is distorted at 400
C. In HR-TEM (Fig. S3), (111) planes are
mainly observed. The observed lattice spacing of NiO is estimated
to be 0.24 nm. The lattice distance for all the differently calcined
NiO samples is identical. Selected area electron diffraction (SAED)
patterns (Fig. S4) of 250NiO, 300NiO, 350NiO, 400NiO and 500NiO
show that the crystallinity of NiO crystals increased with an
increase in the calcination temperature, corresponding with the
results of XRD analysis.
Isotherm measurements of NiO samples were conducted to
investigate the calcination effect on the specific surface area and
pore size distribution. Fig. 5 shows the isotherms and pore size
Fig. 2. TGA and DTA curves of of a-Ni(OH)2 samples prepared by hydrothermal
reaction at 180
C.
Fig. 3. In situ XRD patterns of of a-Ni(OH)2 samples prepared by hydrothermal
reaction at (a) 50
C, (b) 100
C, (c) 150
C, (d) 200
C, (e) 250
C, (f) 300
C (g) 350
C,
(h) 400
C, (i) 450
C and (j) 500
C.
S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153 147
4. distributions of NiO samples calcined at 250, 300, 350, 400, and
500
C. The pore structure of 250NiO (Fig. 5(a)) is similar to that of
a-Ni(OH)2, indicating that 250NiO also has ink-bottle pores. The
lower closure point increases with increasing calcination temper-
ature, indicating that the pore diameter of NiO samples from
desorption branch increases with increasing the calcination
temperature. The pore diameters of 250NiO, 300NiO, 350NiO,
400NiO and 500NiO are 9.2 nm, 7.1 nm, 7.1 nm, 9.2 nm, and
18.6 nm, respectively as shown in Fig. 5(f). No tensile stress effect
in the isotherms of the NiO samples in Fig. 5 was confirmed by
measuring the isotherms of the NiO samples using Ar isotherm.
However, the PSDs of NiO samples (Fig. 5(f)) are plotted from
adsorption branch for the purpose of comparison with those of
a-Ni(OH)2. Table 1 shows BET surface areas and average pore
volumes of the NiO samples. The surface area and pore volume of
the NiO samples decreased with increasing the calcination
temperature. Interestingly, the BET surface area of MMS of
250NiO is exceptionally large, 295m2
gÀ1
, which was more than
that of a-Ni(OH)2 (176 m2
gÀ1
). During the phase transformation
from Ni(OH)2 to NiO, the apparent sphere size was not much
decreased as shown in Fig. 4. The skeletal Ni(OH)2 volume was
maintained during the removal of H2O and the removed H2O left
pores in NiO, resulting in the increase of the pore volume
(0.44 cm3
gÀ1
of a-Ni(OH)2 and 0.64 cm3
gÀ1
of 250NiO) and the
surface area of the sphere particles. It has been known that
electrochemical capacitance of NiO samples is closely related to
the specific surface area and pore structure [2,25]. Therefore, the
dependency of the electrochemical capacitance on the surface area
and pore structure of the prepared mesoporous NiO samples is
investigated.
3.3. Electrochemical performance
3.3.1. CV measurements
Fig. 6 shows the cyclic voltammetry (CV) analysis of prepared
NiO electrodes. During the anodic and cathodic sweeps, reversible
redox peaks are clearly observed in the all CV curves. These redox
peaks are associated with the reversible reaction (NiO + OHÀ
$
NiOOH + e-) for pseudocapacitance of NiO [26]. In a redox reaction,
Ni2+
is transformed to Ni3+
during charging (oxidation) and during
discharging (reduction) returns back from Ni3+
to Ni2+
[27]. The CV
measurements with 250NiO were conducted at scan rates of 5,
10 and 25 mV sÀ1
as shown in Fig. 6(a). Cathodic sweeps are not in
complete symmetry with the corresponding anodic sweeps due to
some electrochemical irreversibility during the redox process [28].
During the faradaic redox reactions various thermodynamic and/or
ion transport barriers occurred, which cause the non-ideal
behavior of pseudocapacitance. Ohmic loss resulting from the
electrolyte diffusion within the porous electrode or electrolyte
concentration depletion can cause the irreversibility of the redox
reaction [29]. The irreversibility is also ascribed to the indication of
phase transformation. In batteries, the cyclic voltamograms are
characterized by faradaic redox peaks, often with rather large
potential separation (greater than 0.1 to 0.2 V) [14,15]. Table 2
shows oxidation potential (EO), reduction potential (ER) and
potential separation (EO-ER). The potential separation of 250NiO
is in the range from 0.18 V to 0.31 V, which indicates that 250NiO
can be treated with battery-type as well as pseudocapacitor. The
potential difference was lower with NiO sample at higher
calcination temperature, which indicates that the capacitance of
NiO at higher calcination temperature corresponds to higher
Fig. 4. TEM images taken (a) 25
C, (b) 200
C, (c) 250
C, (d) 300
C, (e) 400
C and (f) 500
C during in-situ TEM analysis of a-Ni(OH)2 samples from room temperature to
500
C.
148 S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153
5. pseudocapacitive contributions from surface or near-surface
charge storage.
Fig. 6(b) shows the cyclic voltammetry (CV) measurements
with 300NiO, 350NiO, 400NiO and 500NiO at a scan rate of
10mVsÀ1
. All the curves in Fig. 6(b) also show clear redox peaks, but
the current density drops as the calcination temperature is
increased. This decrease in current (i) values can be associated
with a decrease in specific surface area and total pore volume as
shown in Table 1, causing fewer active sites to be available for redox
reaction. The specific capacitances from CV measurements can be
calculated using the following equation:
CCV ¼
1
v  m  DV
Z Vc
Va
idV ð2Þ
Where i is cathodic or anodic current in ampere; DV is the applied
potential window (Va-Vc); Va is anodic potential; Vc is cathodic
potential; v is scan rate in V/s; m is the mass of active material in
grams. Table 3 shows the specific capacitances of the prepared NiO
samples at scan rates of 5 mV sÀ1
, 10 mV sÀ1
and 25 mV sÀ1
. CCV
values are large at the low scan rate of 5 mVsÀ1
and low at
25 mV sÀ1
. The specific capacitance values of 250NiO at the scan
rate of 5 mV sÀ1
, 10 mV sÀ1
and 25 mV sÀ1
were 1200 F gÀ1
, 1100 F
gÀ1
and 806 F gÀ1
, respectively. The specific capacitance decreased
with an increase in scan rate. This decrease of specific capacitance
at the high scan rate has been explained by the ion exchange
mechanism [27]. The OHÀ1
ions have enough time to diffuse into
the NiO electrode at low scan rate, while they did not at high scan
rate. The less accessibility at high scan rate resulted in low
capacitance (Table 3).
Fig. 5. N2 adsorption-desorption isotherms of (a) 250NiO, (b) 300NiO, (c) 350NiO, (d) 400NiO, (e) 500NiO and (f) pore size distribution of all five samples.
Table 1
Specific surface area and pore volume of MMS of NiO.
250NiO 300NiO 350NiO 400NiO 500NiO
Specific Surface Area
(m2
gÀ1
)
295 196.85 133.41 91.79 10.51
Pore Volume
(cm3
gÀ1
)
0.64 0.41 0.30 0.23 0.11
S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153 149
6. 3.3.2. Galvanostatic Measurements
Fig. 7(a) shows galvanostatic discharge curves of 250NiO at
discharge current density of 3 A gÀ1
, 5 AgÀ1
and 10 AgÀ1
in the
potential range of 0.0–0.5 V. The nonlinear discharge curves
indicate the faradaic redox behaviour of NiO [17], which was
ascribed to the pseudocapacitive characteristics of the electrode
[29]. The galvanostatic discharge curve from 0.0 V to 0.2 V was due
to the charge separation between the electrode/electrolyte
interface. The slope change of discharge curve from 0.2 to 0.5 V
was ascribed to the contribution of the redox reaction of NiO with
the electrolyte. The slope at ca. 0.25 V with 250NiO can be assigned
to a battery-type potential plateau [15]. Then, the sloping regions
at potentials above and below $0.25 V correspond to pseudocpa-
citive contributions from surface or near-surface charge storage.
From galvanostatic measurements, capacitance was estimated
by the following equation [30]:
CGM ¼ I Â Dtð Þ= DV Â mð Þ ð3Þ
Where I is the discharge current in amperes; V is the potential
change during the discharge in volts; m is the mass of active
material in grams; t is the time to discharge in seconds.
Fig. 6. Cyclic voltammetry of MMS of NiO: (a) CV curves of MMS of 250NiO at 5 mV sÀ1
, 10 mV sÀ1
and 25 mV sÀ1
. (b) CV curves of MMS of NiO calcined at different
temperatures at a scan rate of 10 mV sÀ1
.
Table 2
Oxidation potential (EO), reduction potential (ER) and (EO-ER) for MMS of NiO with
respect to scan rate.
Sample Scan Rate (mV sÀ1
) EO (V) ER (V) EO À ER (V)
NiO250 5 0.38 0.20 0.18
10 0.41 0.18 0.23
25 0.46 0.15 0.31
NiO300 5 0.34 0.24 0.10
10 0.37 0.23 0.14
25 0.41 0.2 0.21
NiO350 5 0.35 0.23 0.12
10 0.38 0.22 0.16
25 0.42 0.2 0.22
NiO400 5 0.35 0.28 0.07
10 0.36 0.28 0.08
25 0.38 0.28 0.10
NiO500 5 0.35 0.30 0.05
10 0.35 0.30 0.05
25 0.37 0.29 0.08
Table 3
Specific capacitance (CCV) of MMS of NiO from cyclic voltammetry.
250NiO 300NiO 350NiO 400NiO 500NiO
CCV at 5 mV sÀ1
(F gÀ1
) 1200 668 425 230 70
CCV at 10 mVsÀ1
(F gÀ1
) 1100 591 391 191 58
CCV at 25 mVsÀ1
(F gÀ1
) 806 553 348 144 50
Fig. 7. Galvanostatic discharge measurements of MMS of NiO: (a) galvanostatic discharge curves of MMS of 250NiO at 3 A gÀ1
, 5 A gÀ1
and 10 A gÀ1
, (b) galvanostatic discharge
curves of MMS of NiO at a current density of 3 AgÀ1
.
Table 4
Specific capacitance (CGM) of MMS of NiO from galvanostatic discharge measure-
ments.
250NiO 300NiO 350NiO 400NiO 500NiO
CGM at 3 A gÀ1
(F gÀ1
) 1560 816 656 342 53
CGM at 5 A gÀ1
(F gÀ1
) 1370 748 636 336 50
CGM at 10 A gÀ1
(FgÀ1
) 1140 656 592 324 44
150 S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153
7. The specific capacitances of 250NiO are 1,560 F gÀ1,
1,370 F gÀ1
and 1,140 F gÀ1
at scan rates of 3, 5 and 10 A gÀ1
, respectively. The
specific capacitance of 250NiO in this report is the highest value of
any reported capacitance values of NiO as far as we know. Ccv of
250NiO at 25 mV sÀ1
(40 s) was 806 F gÀ1
and the equivalent CGM
(discharge time of 40 s) is estimated to be 1085 F gÀ1
by
extrapolation. Capacitance of CCV is not much different from
CGM. Galvanostatic charge-discharge measurements were also
conducted for 300NiO, 350NiO, 400NiO and 500NiO at the current
density of 3 A gÀ1
to investigate the effect of calcination on specific
capacitance as shown in Fig. 7(b). Table 4 shows the capacitances
of the NiO samples prepared at 250
C, 300
C, 350
C, 400
C and
500
C from galvanostatic measurements. The specific capacitance
value decreased with increasing calcination temperature, which
was due to a decrease in specific surface area and pore volume, and
consequently there are fewer sites of active material available for
redox reaction.
3.3.3. Electrochemical impedance measurements
Fig. 8 shows Nyquist plots, which are fitted by Z-view software
and the parameters are tabulated in Table 5. Equivalent circuit
diagram is shown in Fig. 8 (a). Nyquist plots consist of a semicircle
in the high frequency region while a straight line in low frequency
region. In the equivalent circuit diagram, Rs is the resistance of
electrolyte; Rct is the resistance of charge transfer; W is the
Warburg impedance; Cdl is the double layer capacitance; CPE is the
constant phase element of capacitance (CPE). Rct increased as the
calcination temperature for preparing NiO was increased as shown
in Fig. 8(b) and Table 5. Rct value increased from 0.2 V with
250NiO to 0.33 V with NiO500. Diffusion coefficient (D) of the
samples was calculated using the following relation [31]:
D ¼ R2
T2
=2A2
n4
F4
C2
s2
ð4Þ
Where R is the gas constant; T is the absolute temperature; A is the
surface area of the electrode; n is the number of electrons; C is the
concentration of (OH)À
ions; s is the Warburg factor. The Warburg
factor, s, can be obtained from the slope of Randle’s plot, the
relation of angular frequency vÀ1/2
and Zre. The values of the
calculated diffusion coefficient are 1.08 Â 10À8
cm2
sÀ1
, 1.28 Â 10À8
cm2
sÀ1
, 7.29 Â10À9
cm2
sÀ1
and 7.43 Â10À9
cm2
sÀ1
for 250NiO,
350NiO, 400NiO and 500NiO, respectively. The diffusion coeffi-
cient for NiO is closely related to pore structure. NiO sample with
high porosity and mesopores shows high diffusion coefficient.
Fig. 8(c) shows vertical lines in the Nyquist presentation. The
vertical line of a 90
phase angle indicates an ideal capacitor. The
deviation from the vertical line to phase angles of 90
can
indicate pseudocapacitive behavior. The phase angle is often
presented by a constant phase element (CPE) in Fig. 8(a):
ZCPE ¼
1
CPE À T Â ðjwÞCPEÀP
ð5Þ
CPE-P has been used as an indication of pseudocapacitive
behaviour. When CPE-P is 1, this is ideal capacitor and when CPE-P
is 0.5, this is semi-infinete diffusion [15]. In Table 5, all the CPE-P
values are close to 1.0, indicating that NiO has both the double layer
and pseudocapacitive feature. However, the low Cdl values of NiO
make the double layer contribution of NiO doubtful.
The specific capacitance (Cs) values of NiO electrodes were
calculated from the impedance measurements using the following
relation [32]:
CEIS ¼ 1= 2pfZ
00À Á
ð6Þ
Fig. 8. Electrochemical impedance spectroscopy of MMS of NiO: (a) equivalent circuit model for Nyquist plots. (b) Nyquist plots of NiO, (c) enlarged scale of Nyquist plots of
NiO with enlarged scale, (d) limit capacitance with respect to frequency.
Table 5
Values of parameters from fitted Nyquist plots using equivalent circuit model in
Fig. 8(a).
Sample Rs (V) Cdl (F gÀ1
) Rct (V) W0
W0-R W0-T
CPE
CPE-T CPE-P
250 NiO 1.30 0.084 0.20 0.62 0.25 0.65 0.90
350 NiO 1.31 0.077 0.26 0.57 0.4 0.28 0.94
400 NiO 1.26 0.095 0.27 3.77 2.08 0.15 0.95
500 NiO 1.29 0.062 0.33 1.37 0.14 0.080 0.97
S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153 151
8. Where f is the frequency and Z00
is corresponding imaginary part.
The specific capacitance values of NiO from EIS are 371 F gÀ1
,
298 F gÀ1
, 169.8 F gÀ1
and 65.15 F gÀ1
at 0.1 Hz for 250NiO, 350NiO,
400NiO and 500NiO, respectively. The specific capacitance values
from EIS are very low as compared with those from cyclic
voltammetry and gavanostatic discharge measurements, which is
due to inhomogeneities at the atomic level and deeply trapped
counter ions during the impedance analysis [33]. Dependence of
limit capacitance with respect to frequency is shown in Fig. 8(d).
3.3.4. Stability
Turning to the electrochemical stability of the electrode, the
specific discharge capacitance of 250NiO was plotted against the
number of charge/discharge cycles for up to 1,000 cycles at the
high current density of 50 A gÀ1
as shown in Fig. 9(a). The first
10 cycles of the charge/discharge voltage profile are shown in
Fig. 9(b). The specific capacitance of the 250NiO electrode is
maintained at 680 F gÀ1
at the end of 1,000 cycles, which indicates
100% retention of its initial capacitance. This result suggests that
MMS of NiO have excellent stability during the insertion/extraction
of OHÀ
ions through the NiO lattice of the electrode. It is noticed
that during the first 100 cycles, the specific capacitance of MMS of
NiO increased from 650 F gÀ1
to 700 F gÀ1
which indicates the
activation process of NiO electroactive material. These galvano-
static testing results suggest that the prepared MMS of NiO have
high specific capacitance and very good capacitance retention as
well, indicating that NiO is a suitable candidate for supercapacitor
applications.
We also calculated the power density and the energy density,
which were 2.5 kW KgÀ1
and 59 Wh KgÀ1
at a current density of
10 A gÀ1
.
4. Conclusions
MMS of NiO with a high specific surface area could be prepared
from MMS of a-Ni(OH)2 with the specific surface area of 176 m2
/g.
The morphology and structure did not change during the
transformation from a-Ni(OH)2 to NiO by calcining the a-Ni(OH)2.
The MMS of NiO were obtained by calcination of a-Ni(OH)2 at
different temperatures and NiO calcined at 250
C (250NiO) has a
high specific surface area of 295 m2
gÀ1
. Cyclic voltammetry,
galvanostatic measurements and electrochemical impedance
analysis of NiO samples prepared with different calcination
temperatures were conducted to determine the electrochemical
pseudocapacitive behavior. The indication of pseudocapacitance of
NiO was more clarified for NiO sample with higher calcination
temperature. 250NiO has very high capacitance of 1,140 F gÀ1
at a
current density of 10 A gÀ1
which is ascribed to its high surface area
and mesopore structure. The power density and energy density of
250NiO were 2.5 kW KgÀ1
and 59WhKgÀ1
respectively at a current
density of 10 AgÀ1
.
Acknowledgements
This work was financially supported through Korea Institute of
Science and Technology (KIST) and the Korea CCS RD Center
(2014M1A8A1049293) by Ministry of Science, ICT Future
Planning.
Appendix A. Supplementary data
Supplementary data associated with this article can be found, in
the online version, at http://dx.doi.org/10.1016/j.electacta.2016.02.
054.
References
[1] P. Simon, Y. Gogotsi, Materials for electrochemical capacitors, Nat Mater 7
(2008) 845–854.
[2] G. Wang, L. Zhang, J. Zhang, A review of electrode materials for electrochemical
supercapacitors, Chemical Society Reviews 41 (2012) 797–828.
[3] Y. Zhu, C. Cao, S. Tao, W. Chu, Z. Wu, Y. Li, Ultrathin Nickel Hydroxide and Oxide
Nanosheets: Synthesis, Characterizations and Excellent Supercapacitor
Performances, Sci. Rep. 4 (2014).
[4] D. Su, H.-S. Kim, W.-S. Kim, G. Wang, Mesoporous Nickel Oxide Nanowires:
Hydrothermal Synthesis, Characterisation and Applications for Lithium-Ion
Batteries and Supercapacitors with Superior Performance, Chemistry—A
European Journal 18 (2012) 8224–8229.
[5] D.Y. Lee, S.J. Yoon, N.K. Shrestha, S.-H. Lee, H. Ahn, S.-H. Han, Unusual energy
storage and charge retention in Co-based metal–organic-frameworks,
Microporous and Mesoporous Materials 153 (2012) 163–165.
[6] X. Lang, A. Hirata, T. Fujita, M. Chen, Nanoporous metal/oxide hybrid
electrodes for electrochemical supercapacitors, Nat Nano 6 (2011) 232–236.
[7] M.-b. Zheng, J. Cao, S.-t. Liao, J.-s. Liu, H.-q. Chen, Y. Zhao, W.-j. Dai, G.-b. Ji, J.-m.
Cao, J. Tao, Preparation of Mesoporous Co3O4 Nanoparticles via Solid-Liquid
Route and Effects of Calcination Temperature and Textural Parameters on Their
Electrochemical Capacitive Behaviors, The Journal of Physical Chemistry C 113
(2009) 3887–3894.
[8] G.-x. Wang, J. Cai, H.-f. Xu, L. Lu, H. Zhao, Enhanced capacitance of a NiO
electrode prepared in the magnetic field, J Appl Electrochem 44 (2014) 391–
398.
[9] J.-W. Lang, L.-B. Kong, W.-J. Wu, Y.-C. Luo, L. Kang, Facile approach to prepare
loose-packed NiO nano-flakes materials for supercapacitors, Chemical
Communications (2008) 4213–4215.
[10] X. Zhao, B.M. Sanchez, P.J. Dobson, P.S. Grant, The role of nanomaterials in
redox-based supercapacitors for next generation energy storage devices,
Nanoscale 3 (2011) 839–855.
[11] G.Q. Zhang, H.B. Wu, H.E. Hoster, M.B. Chan-Park, X.W. Lou, Single-crystalline
NiCo2O4 nanoneedle arrays grown on conductive substrates as binder-free
electrodes for high-performance supercapacitors, Energy Environmental
Science 5 (2012) 9453–9456.
[12] B. Wang, J.S. Chen, Z. Wang, S. Madhavi, X.W. Lou, Green Synthesis of NiO
Nanobelts with Exceptional Pseudo-Capacitive Properties, Advanced Energy
Materials 2 (2012) 1188–1192.
[13] T. Brousse, D. Bélanger, J.W. Long, To Be or Not To Be Pseudocapacitive? Journal
of The Electrochemical Society 162 (2015) A5185–A5189.
Fig. 9. Stability test of 250NiO: (a) specific capacitance vs. cycle number of MMS of
250 NiO at a current density of 50 A gÀ1
. (b) galvanostatic charge-discharge voltage
profiles of 250NiO at a current density of 50 A gÀ1
.
152 S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153
9. [14] V. Augustyn, P. Simon, B. Dunn, Pseudocapacitive oxide materials for high-rate
electrochemical energy storage, Energy Environmental Science 7 (2014)
1597–1614.
[15] P. Simon, Y. Gogotsi, B. Dunn, Where Do Batteries End and Supercapacitors
Begin? Science 343 (2014) 1210–1211.
[16] C. Yuan, X. Zhang, L. Su, B. Gao, L. Shen, Facile synthesis and self-assembly of
hierarchical porous NiO nano/micro spherical superstructures for high
performance supercapacitors, Journal of Materials Chemistry 19 (2009)
5772–5777.
[17] S. Xiong, C. Yuan, X. Zhang, Y. Qian, Mesoporous NiO with various hierarchical
nanostructures by quasi-nanotubes/nanowires/nanorods self-assembly:
controllable preparation and application in supercapacitors, CrystEngComm
13 (2011) 626–632.
[18] S. Ding, T. Zhu, J.S. Chen, Z. Wang, C. Yuan, X.W. Lou, Controlled synthesis of
hierarchical NiO nanosheet hollow spheres with enhanced supercapacitive
performance, Journal of Materials Chemistry 21 (2011)
6602–6606.
[19] C.-Y. Cao, W. Guo, Z.-M. Cui, W.-G. Song, W. Cai, Microwave-assisted gas/liquid
interfacial synthesis of flowerlike NiO hollow nanosphere precursors and their
application as supercapacitor electrodes, Journal of Materials Chemistry 21
(2011) 3204–3209.
[20] M. Gao, W. Sheng, Z. Zhuang, Q. Fang, S. Gu, J. Jiang, Y. Yan, Efficient Water
Oxidation Using Nanostructured a-Nickel-Hydroxide as an Electrocatalyst,
Journal of the American Chemical Society 136 (2014) 7077–7084.
[21] K.M. Nam, J.H. Shim, H. Ki, S.-I. Choi, G. Lee, J.K. Jang, Y. Jo, M.-H. Jung, H. Song, J.
T. Park, Single-Crystalline Hollow Face-Centered-Cubic Cobalt Nanoparticles
from Solid Face-Centered-Cubic Cobalt Oxide Nanoparticles, Angewandte
Chemie International Edition 47 (2008) 9504–9508.
[22] K.S.W. Sing, Reporting physisorption data for gas/solid systems with special
reference to the determination of surface area and porosity
(Recommendations 1984), Pure and Applied Chemistry (1985) 603.
[23] S. Mourdikoudis, L.M. Liz-Marzán, Oleylamine in Nanoparticle Synthesis,
Chemistry of Materials 25 (2013) 1465–1476.
[24] T.N. Ramesh, X-ray Diffraction Studies on the Thermal Decomposition
Mechanism of Nickel Hydroxide, The Journal of Physical Chemistry B 113
(2009) 13014–13017.
[25] Y. Li, Z. Li, P.K. Shen, Simultaneous Formation of Ultrahigh Surface Area and
Three-Dimensional Hierarchical Porous Graphene-Like Networks for Fast and
Highly Stable Supercapacitors, Advanced Materials 25 (2013) 2474–2480.
[26] S.K. Meher, P. Justin, G. Ranga Rao, Microwave-Mediated Synthesis for
Improved Morphology and Pseudocapacitance Performance of Nickel Oxide,
ACS Applied Materials Interfaces 3 (2011) 2063–2073.
[27] H. Pang, B. Zhang, J. Du, J. Chen, J. Zhang, S. Li, Porous nickel oxide nanospindles
with huge specific capacitance and long-life cycle, RSC Advances 2 (2012)
2257–2261.
[28] X. Li, S. Xiong, J. Li, J. Bai, Y. Qian, Mesoporous NiO ultrathin nanowire networks
topotactically transformed from [small alpha]-Ni(OH) 2 hierarchical
microspheres and their superior electrochemical capacitance properties and
excellent capability for water treatment, Journal of Materials Chemistry 22
(2012) 14276–14283.
[29] W. Yu, X. Jiang, S. Ding, B.Q. Li, Preparation and electrochemical characteristics
of porous hollow spheres of NiO nanosheets as electrodes of supercapacitors,
Journal of Power Sources 256 (2014) 440–448.
[30] Y.Q. Zhang, X.H. Xia, J.P. Tu, Y.J. Mai, S.J. Shi, X.L. Wang, C.D. Gu, Self-assembled
synthesis of hierarchically porous NiO film and its application for
electrochemical capacitors, Journal of Power Sources 199 (2012) 413–417.
[31] M.F. Dupont, A.D. Cross, A. Morel, M. Drozd, A.F. Hollenkamp, S.W. Donne, Mass
Transport Properties of Manganese Dioxide Phases for Use in Electrochemical
Capacitors: Structural Effects on Solid State Diffusion, Journal of The
Electrochemical Society 160 (2013) A1219–A1231.
[32] S. Vijayakumar, S. Nagamuthu, G. Muralidharan, Supercapacitor Studies on NiO
Nanoflakes Synthesized Through a Microwave Route, ACS Applied Materials
Interfaces 5 (2013) 2188–2196.
[33] R. Ding, L. Qi, H. Wang, A facile and cost-effective synthesis of mesoporous
NiCo2O4 nanoparticles and their capacitive behavior in electrochemical
capacitors, J Solid State Electrochem 16 (2012) 3621–3633.
S.A. Abbas, K.-D. Jung / Electrochimica Acta 193 (2016) 145–153 153