1. New Generation – Car Corrosion Protection
New Solventfree
Underbody and Cavity Protection
2. AGENDA
Market requirements today
Products
• WAXOYL SF
• Advantages
• Handling
• Technical data
• HARDWAX SF
• Advantages
• Handling
• Technical data
3. 1960
Cavity wax
low solid content,
medium corrosion
protection
Factors:
Good sprayability
Easy to work
1980
Solid Content
approx. 40 %
Factors:
Good sprayability
Good corrosion
protection
1990
Solid content
approx. 60-70 %
Factors:
Environmentally
friendly
(VOC-reduction)
Improved corrosion
protection
2000
Waterbased products
(VOC-free)
100% solid content
Factors:
Environmentally friendly
(without VOC),
Good sprayability
MARKET REQUIREMENTS
4. MARKET REQUIREMENTS TODAY
Important points for the customer today
Environment friendly product
• Without safety-label, safety-rules
• Less storage fees
Health friendly products
• Odorless
• Safe to use
Excellent corrosion protection
Easy to use
• Without lenghty preparation (washing, cleaning etc.)
• The use of standard equipment
5. PREMIUM QUALITY CAVITYWAX - WAXOYL SF
Advantages
Good protection against corrosion
UV content for visual inspection
Good penetration into flanges, angles etc.
VOC-free
Cavity Protection with self healing effect
Easy to work with
OEM-approved compound
• OEM-PREMIUM QUALITY
6. WAXOYL SF
Handling
Ready to use
No heating needed in a temperature range from > 0°C
Suitable with HRS-SF Equipment
Technical Data Waxoyl SF
Corrosion protection:
Salt spray-test (steel/zinc) DIN EN ISO 9227 min. 500 hours.
VDA-Alternating-test (key method) min. 10 cycles
Thickness: 75 – 100 µm
Product Data Waxoyl SF
Solid Content: 99 + 1%
Density/15 °C DIN EN ISO 12185 1030+ 0,03 g/ml
Viscosity/23°C 335 + 25 mPas
Flash point ISO 2719 > 120°C
7. WAXOYL SF
WAXOYL SF
The product has excellent penetration
(see the rocker panel), after treatment.
8. UNDERBODYPROTECTION - HARDWAX SF
Advantages
Good protection against corrosion in the underbody area
Contains UV tracer
VOC-free
Low tendency of dripping – easy to apply
penetration in flanges, angles etc.
The underbody can be inspected (the beige product is
transparent)
Flexible surface even after years
OEM-approved compound
• OEM-PREMIUM-QUALITY
9. HARDWAX SF
Handling
Ready to use
No heating needed in a temperature range from > 0°C
Suitable with HRS-SF Equipment
Technical Data HARDWAX SF
Corrosion protection:
Saltspray-test (steel/zinc) DIN EN ISO 9227 min. 480 hours.
VDA-Alternating-test (key method) min. 10 cycles
Thickness: 50 – 1000 µm
Product Data HARDWAX SF
Solid Content: 99 + 1%
Density/15 °C DIN EN ISO 12185 1020+ 0,03 g/ml
Viscosity/23°C 600 + 100 mPas
Flash point ISO 2719 > 120°C
17. Field trial TOPWAX 7
• Trial area:
North-Sea-Harbor area
Industrial district
• Trial time:
9 month outside exposure
• Remove with steam jet
Adjusted 90 °C water temperature
Nozzle distance to the surface
approx. 15 cm without remover
Trial results:
The TOPWAX7 protection film is after 9 month
outside exposure intact. The protection film can
be easily removed with a steam jet
18. Trial result
Intact film after 9 month outside exposure
Removed with steam jet
without remover. The protection film is
completely removed.