Product Name : Aqupol ® PCE Series
Aqupol® PCE Series is aqueous polycarboxylate ether
copolymer for high performance concrete.
It shows excellent performance of water reduction and
slump retention in concrete.
Features
Specifications
Improves the strength concrete through water reducing and slump
retention in concrete.
Effect long distance transportation for a long time.
Reduce slump loss and improve workability.
Promote high early strength.
Decrease bleeding of materials separation.
Introduction
Classification
Aqupol®
PCE Grade
Specifications
Appearance
Solid
Contents (%)
Specific
gravity
Viscosity
( cps )
pH
High range water
reducing
superplasticizer
MAR-650S
Brown
Liquid
50.0±1.0 1.11 ± 0.05
Max. 700 4.0±2.0
MAR-650D Max. 700 5.0±2.0
Water reducing
superplasticizer
with slump
retention
AWR 250(S) Max. 1000 4.0±2.0
AWR 50 Max. 1000 4.0±2.0
AWR 150 Max. 700 4.0±2.0
Slump retention
superplasticizer
MAW-50 Max. 1000 4.0±2.0
Segregation
Reducing Type
Superplasticizer
MAR-500L Max 700 4.0±2.0
High early strength
superplasticizer
MAS-50 MAX 1,500 4.0±2.0
Remarks Visual 105℃, 2hr 25℃
200rpm,25℃
Spindle
#2
pH
meter
2. Tel : +82-42-280-5700
Fax : +82-42-624-2607Tel : +82-42-280-7900 Fax : +82-42-624-2607
Applications
Type Grade Application Remark
Water Reducing
Superplasticizer
MAR – 650D
• High Flowing Concrete
• Higher Water Reducibility
• Higher Early Strength
• Precast Concrete and
Manufactured Concrete
Products
To improve
concrete
performance,
we
recommended
that Aqupol
MAR-650 or,
AWR Series
should be used
with Aqupol
MAW-50 in the
proper ratio.
AWR-650S
AWR –
250(S)
• Water reduing with slump retention
• Not Sensitive at temperature
and various materials
• High flowing concrete
application
AWR – 150
AWR-50
Slump Retention
Superplasticizer
MAW - 50
• Higher Slump/ Flow Retention
Application
• Not Sensitive at Temperature
and Materials variation
• Less Bleeding
• Increases Segregation
Resistance
Segregation
Reducing Type
Superplasticizer
MAR – 500L
• Less Bleeding
• Increases Segregation
Resistance
Early Strength
Superplasticizer MAS - 50
• Excellent Setting Under low Temp
• For Precast Concrete and
Manufactured Concrete Products
Guidance
Normally it can be used with 0.6 to 0.24 wt% of the cement.
The best formulation should be made on job-site after completing enough tests..
It can be used with sodium-based lignin admixture and retarder, inorganic
accelerating hardening agent.
Product Name : Aqupol ® PCE Series
3. Tel : +82-42-280-5700
Fax : +82-42-624-2607Tel : +82-42-280-7900 Fax : +82-42-624-2607
Characteristic
Handling and Storage
Non-flammable & non-toxic. When contacting the skin or clothing, wash them with water.
Keep containers closed when being no use.
When being frozen, it can be used after melting, but the function needs to be confirmed
before use.
Keep containers at room temperature in the house
Caution
Do not allow product to freeze or be stored in temperature below freezing.
If freezing occurs, contact the manufacturer representative.
Product Name : Aqupol ® PCE Series
Slump Retention
WaterReduction
Aqupol ®
AWR-250(S)
Aqupol ®
MAW-50
Aqupol®
MAS 50
Excellent
Excellent
Poor
Aqupol®
MAR 650S
Aqupol®
MAR-500L
Aqupol®
AWR-50
Aqupol ®
AWR-150
Aqupol®
MAR 650D
Packing
220 kg Drum / 1.1 MT Tote Bin / 21MT flexi tank / 20MT ISO
4. Tel : +82-42-280-5700
Fax : +82-42-624-2607Tel : +82-42-280-7900 Fax : +82-42-624-2607
Concrete Test Result
Normal Strength Concrete ~ High Strength Concrete
1. Concrete Mix Design
Strength
W/B
(%)
S/A
(%)
Unit Weight (kg/m3) 20 % AD
( B X % )W C F/A S G
24 Mpa 48.4 48.0 162 285 50 867 947 1.0
27 Mpa 43.8 47.5 160 310 55 848 944 1.0
35 Mpa 40.3 45.0 157 332 59 797 982 1.1
2. Test Results
Strength
Slump
(mm)
Air Content
(%)
Compressive Strength
(Mpa)
Initial 30 min 60 min Initial 60 min 1 day 3 days 7 days 28 days
24 Mpa 190 175 165 4.7 4.2 6.3 17.5 23.4 31.2
27 Mpa 205 195 185 4.4 4.0 7.8 20.5 27.5 36.1
35 Mpa 210 200 190 4.2 3.7 11.5 25.7 35.2 48.6
Product Name : Aqupol ® PCE Series
Fig.1 Concrete Slump (mm) Fig.2 Compressive Strength (Mpa)
150
170
190
210
230
Initial 30 min 60 min
0
10
20
30
40
50
60
1 day 3 days 7 days 28 days
35 Mpa 27 Mpa 24 Mpa
※ AD : Aqupol MAR-650 / Aqupol MAW-50 MIX (70 / 30) (20% Solid Contents, 0.1% defoamer added)
5. Tel : +82-42-280-5700
Fax : +82-42-624-2607Tel : +82-42-280-7900 Fax : +82-42-624-2607
Concrete Test Result
High Flow , High Early Strength application of Ultra High Strength Concrete
1. Concrete Mix Design
Strength
W/B
(%)
S/A
(%)
Unit Weight (kg/m3) 20 % AD
( BX % )W C F/A S/F S G
60 Mpa 27.4 43.5 167 519 92 - 675 883 1.2
80 Mpa 23.5 39.5 160 578 68 34 601 927 1.5
100 Mpa 18.2 35.0 160 774 - 106 483 904 2.1
2. Test Results
Strength
Flow
(mm)
Air Content
(%)
Compressive Strength
(Mpa)
Initial 30 min 60 min Initial 60 min 3 days 7 days 28 days
60 Mpa 640 640 630 2.6 2.4 35.1 58.6 70.1
80 Mpa 660 660 640 1.5 1.3 49.6 72.3 94.9
100 Mpa 660 650 640 1.0 0.8 59.4 85.6 112.4
Product Name : Aqupol ® PCE Series
620
630
640
650
660
670
680
Initial 30 min 60 min
20
40
60
80
100
120
3 days 7 days 28 days
Fig.1 Concrete Flow (mm) Fig.2 Compressive Strength (Mpa)
100 Mpa 80 Mpa 60Mpa
※ AD : Aqupol AWR -350 / Aqupol MAW-50 MIX (60 / 40) (20% Solid Contents, 0.1% defoamer added)