The document describes the development of a silver nanoparticle-modified poly ortho-toluidine/carbon paste electrode (n-Ag/POT/MCPE) and its application as an anode for the electrocatalytic oxidation of hydrazine in alkaline media. Scanning electron microscopy images show that the n-Ag/POT/MCPE has a porous surface topology suitable for catalyzing hydrazine oxidation. Cyclic voltammetry experiments demonstrate that the electrode exhibits high anodic and cathodic currents, indicating a large surface area, and is electrochemically active for hydrazine oxidation, with the oxidation current increasing with hydrazine concentration.
A facile synthesis method produced highly active Pd nanoparticle catalysts for oxygen reduction reaction (ORR) in under 5 minutes. An electrode was dipped in separate solutions of reducing agent and Pd ions to deposit amorphous Pd nanoparticles. Repeatedly dipping the electrode increased catalytic activity, with the highest activity achieved after 12 cycles of 20 seconds each. The Pd nanoparticles produced using sodium hypophosphite as the reducing agent showed superior ORR activity compared to commercial Pt/C catalysts.
Potentiometry involves measuring the potential or electromotive force of a sample solution using an electrochemical cell containing a reference electrode and an indicator electrode. The potential is directly proportional to the ion concentration in the solution. Common reference electrodes include the standard hydrogen electrode, silver chloride electrode, and saturated calomel electrode. Indicator electrodes can be metal electrodes or ion-selective electrodes like the glass membrane pH electrode. Potentiometric titration determines the concentration of an analyte by measuring the potential change as a titrant is added, with the endpoint indicated by an abrupt potential shift. Applications of potentiometry include acid-base, redox, complexometric, and precipitation titrations.
This document provides information on potentiometry and potentiometric titration. It discusses the basic principles of potentiometry including electrode potentials and how a potential difference is established between an electrode and solution. It describes the instrumentation used including reference electrodes like calomel and silver-silver chloride electrodes and indicator electrodes like metal, glass membrane, and quinhydrone electrodes. It also discusses different types of potentiometric titrations and provides examples of applications for potentiometry in various industries.
This document describes a potentiometric redox titration experiment to determine the percentage of iron in a sample. Key points:
1. The experiment involves titrating an iron solution with a standardized potassium permanganate solution while monitoring the electrode potential with a multimeter.
2. Graphs of voltage vs volume added are used to determine the equivalence point, from which the concentration of permanganate and percentage of iron can be calculated.
3. Results show the titration curves, first derivative plots used to find the equivalence point, and sample calculations determining 9.95x10-3M KMnO4 and 0.26% iron in the unknown sample.
This document provides an overview of various energy devices and related chemistry concepts covered in the Engineering Chemistry module. It discusses electrochemical cells, electrode materials, semiconductors, lithium-ion batteries, fuel cells, and solar cells. It also covers topics like electrolysis, electroplating, and the preparation and doping of semiconductors.
The presentation discusses the working principle and applications of fuel cells, the oxygen reduction reaction (ORR) in fuel cells, and various electrocatalysts used for ORR. It outlines the working principle of fuel cells, where hydrogen is oxidized at the anode to produce protons and electrons. At the cathode, oxygen reacts with protons and electrons to form water. Various electrocatalysts discussed that catalyze the ORR include platinum, carbon materials like graphite and nanotubes, transition metals and their compounds. The presentation provides details on the mechanisms of ORR on different catalysts and how doping or alloying can influence their activity.
Maiyalagan,Performance of carbon nanofiber supported pd ni catalysts for elec...kutty79
Carbon nanofibers (CNF) supported Pd–Ni nanoparticles have been prepared by chemical reduction
with NaBH4 as a reducing agent. The Pd–Ni/CNF catalysts were characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical
voltammetry analysis. TEM showed that the Pd–Ni particles were quite uniformly distributed on the
surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of
the Pd–Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential
was 200mV lower and the peak current density four times higher for ethanol oxidation for Pd–Ni/CNF
compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 ◦C had a great effect on
increasing the ethanol oxidation activity
1. Electrochemistry examines phenomena resulting from combined chemical and electrical effects. It covers electrolytic and galvanic processes.
2. An electrochemical cell consists of two electrodes and an electrolyte. Charge is transported by electron motion in electrodes and ion motion in electrolytes.
3. At each electrode, an oxidation or reduction half-cell reaction occurs. The overall reaction is the sum of the half reactions. Thermodynamics predicts which reaction will occur as oxidation or reduction.
A facile synthesis method produced highly active Pd nanoparticle catalysts for oxygen reduction reaction (ORR) in under 5 minutes. An electrode was dipped in separate solutions of reducing agent and Pd ions to deposit amorphous Pd nanoparticles. Repeatedly dipping the electrode increased catalytic activity, with the highest activity achieved after 12 cycles of 20 seconds each. The Pd nanoparticles produced using sodium hypophosphite as the reducing agent showed superior ORR activity compared to commercial Pt/C catalysts.
Potentiometry involves measuring the potential or electromotive force of a sample solution using an electrochemical cell containing a reference electrode and an indicator electrode. The potential is directly proportional to the ion concentration in the solution. Common reference electrodes include the standard hydrogen electrode, silver chloride electrode, and saturated calomel electrode. Indicator electrodes can be metal electrodes or ion-selective electrodes like the glass membrane pH electrode. Potentiometric titration determines the concentration of an analyte by measuring the potential change as a titrant is added, with the endpoint indicated by an abrupt potential shift. Applications of potentiometry include acid-base, redox, complexometric, and precipitation titrations.
This document provides information on potentiometry and potentiometric titration. It discusses the basic principles of potentiometry including electrode potentials and how a potential difference is established between an electrode and solution. It describes the instrumentation used including reference electrodes like calomel and silver-silver chloride electrodes and indicator electrodes like metal, glass membrane, and quinhydrone electrodes. It also discusses different types of potentiometric titrations and provides examples of applications for potentiometry in various industries.
This document describes a potentiometric redox titration experiment to determine the percentage of iron in a sample. Key points:
1. The experiment involves titrating an iron solution with a standardized potassium permanganate solution while monitoring the electrode potential with a multimeter.
2. Graphs of voltage vs volume added are used to determine the equivalence point, from which the concentration of permanganate and percentage of iron can be calculated.
3. Results show the titration curves, first derivative plots used to find the equivalence point, and sample calculations determining 9.95x10-3M KMnO4 and 0.26% iron in the unknown sample.
This document provides an overview of various energy devices and related chemistry concepts covered in the Engineering Chemistry module. It discusses electrochemical cells, electrode materials, semiconductors, lithium-ion batteries, fuel cells, and solar cells. It also covers topics like electrolysis, electroplating, and the preparation and doping of semiconductors.
The presentation discusses the working principle and applications of fuel cells, the oxygen reduction reaction (ORR) in fuel cells, and various electrocatalysts used for ORR. It outlines the working principle of fuel cells, where hydrogen is oxidized at the anode to produce protons and electrons. At the cathode, oxygen reacts with protons and electrons to form water. Various electrocatalysts discussed that catalyze the ORR include platinum, carbon materials like graphite and nanotubes, transition metals and their compounds. The presentation provides details on the mechanisms of ORR on different catalysts and how doping or alloying can influence their activity.
Maiyalagan,Performance of carbon nanofiber supported pd ni catalysts for elec...kutty79
Carbon nanofibers (CNF) supported Pd–Ni nanoparticles have been prepared by chemical reduction
with NaBH4 as a reducing agent. The Pd–Ni/CNF catalysts were characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical
voltammetry analysis. TEM showed that the Pd–Ni particles were quite uniformly distributed on the
surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of
the Pd–Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential
was 200mV lower and the peak current density four times higher for ethanol oxidation for Pd–Ni/CNF
compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 ◦C had a great effect on
increasing the ethanol oxidation activity
1. Electrochemistry examines phenomena resulting from combined chemical and electrical effects. It covers electrolytic and galvanic processes.
2. An electrochemical cell consists of two electrodes and an electrolyte. Charge is transported by electron motion in electrodes and ion motion in electrolytes.
3. At each electrode, an oxidation or reduction half-cell reaction occurs. The overall reaction is the sum of the half reactions. Thermodynamics predicts which reaction will occur as oxidation or reduction.
The document discusses pH measurement and the components used. It describes that pH is a measurement of hydrogen ion concentration on a logarithmic scale from 0-14. It also discusses Nernst's equation, which relates electrode potential to ion concentration. The key components used for pH measurement are glass electrodes, reference electrodes like calomel or silver-silver chloride, and buffer solutions. The document provides details on the construction and functioning of these different electrode types.
This document discusses conductometric titration, which is an electrochemical analytical method that measures the electrical conductance of an electrolyte solution. It describes the principles and instrumentation of conductometry, including how conductivity is measured using a conductivity meter or by performing a titration. Some key applications of conductometric titration are determining the end point of acid-base and precipitation titrations, and it has various uses in fields like environmental analysis, food testing, and quality control.
Potentiometry1 for mpharm ist sem notes prakash64742
The document summarizes potentiometry and potentiometric titrations. Potentiometry uses measurement of electrical potential to perform qualitative and quantitative analysis. The potential of a sample is directly proportional to the activity of electroactive ions present, such as pH. Potentiometric titrations involve direct measurement of electrode potential or changes in potential upon titrant addition to determine the endpoint. Common types include acid-base, redox, complexometric, and precipitation titrations. Choice of reference and indicator electrodes depends on the reaction taking place.
Potentiometry is a method of electroanalytical chemistry used to measure electric potential. It involves measuring the potential of electrochemical cells under zero current conditions. Potentiometric titrations determine the endpoint potentiometrically by measuring changes in potential caused by the addition of a titrant. Common applications include acid-base, redox, precipitation, and complexometric titrations. Commercial potentiometers have advantages over simple potentiometers like temperature control and internal calibration.
This document discusses electrolysis and Faraday's law of electrolysis. It provides examples of predicting products of electrolysis for molten salts, aqueous salt solutions, and applying Faraday's law calculations. Key points include:
- During electrolysis, the cation is reduced at the cathode and the anion is oxidized at the anode
- In molten salts, the more easily oxidized/reduced species reacts at each electrode
- In aqueous solutions, overvoltage must be considered in addition to electrode potentials
- Faraday's law states the amount of substance reacted is directly proportional to the quantity of electricity passed through the cell
- Calculations can determine current, time, charge or mass from the other variables using Faraday's constant
Electrochemistry Basics
Table of Contents
1. Introduction
2. Voltaic Cells-Galvanic Cells
3. Cell Potential
4. Balancing Redox Reactions
5. Rules for Assigning Oxidation states
6. Additional Materials
6.1. I. Conversion
6.2. II. Free Energy & Cell Potential
6.3. III. Nernst equation
6.4. At Equilibrium
7. Terminology
8. Reference
9. Outside Links
10. Contributors
As the name suggests, electrochemistry is the study of changes that cause electrons to move. This movement of electrons is called electricity. In electrochemistry, electricity can be generated by movements of electrons from one element to another in a reaction known as a redox reaction or oxidation-reduction react
Potentiometry involves measuring electrode potentials using a reference electrode and indicator electrode. The reference electrode maintains a constant potential while the indicator electrode's potential varies with analyte concentration. Common reference electrodes include the saturated calomel electrode and silver-silver chloride electrode. Indicator electrodes include pH electrodes, ion-selective electrodes, and redox electrodes. Potentiometric measurements are used in clinical chemistry, environmental monitoring, titrations, and various industrial applications like food processing.
This document discusses potentiometry, which is an electroanalytical technique that measures the potential (voltage) of electrochemical cells containing indicator and reference electrodes. It involves using electrodes to measure voltages generated from chemical reactions. Various types of electrodes are described including metal, ion-selective, glass membrane, liquid membrane, and crystalline membrane electrodes. Applications of potentiometry include ion concentration measurements, pH measurements, and potentiometric titrations.
This document provides an overview of electrochemistry. It discusses electron transfer reactions, oxidation and reduction, voltaic cells, cell potentials, and balancing redox reactions. Key points include:
- Electron transfer reactions are oxidation-reduction or redox reactions that result in the generation of an electric current.
- Oxidation is the loss of electrons and reduction is the gain of electrons. Reduction cannot occur without oxidation providing electrons.
- A voltaic cell uses the energy from a spontaneous redox reaction to generate an electric current by transferring electrons through an external circuit between the anode and cathode.
This document summarizes an experiment on using electrocoagulation with iron electrodes to remove mercury from wastewater. Key findings include:
1) Maximum mercury removal of 94.5% was achieved after 40 minutes of electrocoagulation at an applied potential of 9V, agitation of 400 rpm, initial pH of 4.5, and electrolyte concentration of 1.333 g/L.
2) Higher applied potentials and agitation rates decreased mercury removal efficiency due to excessive oxygen generation and unsuitable floc formation.
3) Operating costs were calculated based on energy consumption and electrode material costs. Electrocoagulation was found to be an efficient and fast method for mercury removal compared to conventional techniques.
Introduction to electrochemistry by t. haraToru Hara
This document provides an introduction to electrochemistry. It discusses how electrochemistry involves the conversion of chemical energy to electrical energy, as in primary batteries where a spontaneous reaction between zinc and copper electrodes produces a flow of electrons. It also discusses the reverse process of converting electrical energy to chemical energy, as in secondary batteries that can be recharged. Key concepts covered include oxidation, reduction, standard reduction potentials, anodes, cathodes, and how electrochemical cells work through balanced redox reactions while conserving mass and charge.
This document discusses potentiometric analysis and its applications. Potentiometry involves measuring the potential difference between electrodes placed in a sample solution as the concentration of ions changes, such as during acid-base, redox, complexometric, and precipitation titrations. Some key applications of potentiometry include determining electrolyte levels in clinical samples, analyzing ions in environmental samples like water, and measuring properties in various industries like food processing, detergent manufacturing, and agriculture.
This document provides an overview of potentiometry and related electroanalytical techniques. It defines key concepts like reference electrodes, indicator electrodes, and salt bridges used in potentiometric cells. Equations for electrode potentials are described for various metal-metal ion systems. Membrane electrodes like glass pH electrodes are also summarized. The document concludes with brief discussions of potentiometric titration techniques and voltammetry methods.
The researchers synthesized TiO2 nanotubes (NTs) on Ti foil through anodic oxidation at varying voltages. Pt nanoparticles were deposited on the NTs using two methods, but only one electrode showed reactivity to H2O2. Higher anodization voltages increased NT size but decreased stability, and only undamaged NTs successfully deposited Pt. The electrode with some carbon deposits on the NT surface detected H2O2 at -0.277V, indicating it may be suitable for a lactate biosensor.
The document discusses pH meters and how they are used to measure pH. It provides details on:
- How pH is defined as the negative logarithm of hydrogen ion concentration.
- The first commercial pH meter was produced in 1928 and measured the potential difference between an indicator and reference electrode immersed in solution.
- Common reference electrodes include the saturated calomel electrode and silver/silver chloride electrodes which allow measurement of pH in a variety of solutions.
- Glass membrane electrodes contain a thin glass membrane that generates a potential difference dependent on ion concentration and are commonly used for pH measurements.
- Modern pH electrodes often combine the reference and glass membrane electrodes into a single cylinder for convenience.
This document is a thesis submitted by Okechukwu Pascal Chisom to the Department of Chemical Engineering at Nnamdi Azikiwe University in partial fulfillment of the requirements for a Bachelor's degree in Chemical Engineering. The thesis investigates the use of electrocoagulation technique to remove copper, nickel, and chromium from simulated wastewater. Laboratory experiments are conducted to study the effect of various process parameters such as pH, current density, electrode distance, temperature, charging time, and initial metal ion concentration on the removal efficiency. The results show that electrocoagulation is effective at removing the heavy metals and optimal conditions are identified.
Performance of carbon nanofiber supported pd–ni catalysts for electro oxidati...suresh899
Carbon nanofibers (CNF) supported Pd–Ni nanoparticles have been prepared by chemical reduction
with NaBH4 as a reducing agent. The Pd–Ni/CNF catalysts were characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical
voltammetry analysis. TEM showed that the Pd–Ni particles were quite uniformly distributed on the
surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of
the Pd–Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential
was 200mV lower and the peak current density four times higher for ethanol oxidation for Pd–Ni/CNF
compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 ◦C had a great effect on
increasing the ethanol oxidation activity.
Performance of carbon nanofiber supported pd ni catalysts for electro-oxidati...Science Padayatchi
This document summarizes a study on carbon nanofiber (CNF) supported Pd-Ni catalysts for electro-oxidation of ethanol in alkaline medium. Pd-Ni/CNF catalysts were prepared by chemical reduction and characterized using various techniques. Electrochemical analysis showed the Pd-Ni/CNF catalyst had lower onset potential and 4 times higher peak current density for ethanol oxidation compared to Pd/C. Increasing the temperature from 20 to 60°C greatly enhanced the ethanol oxidation activity of Pd-Ni/CNF.
Performance of carbon nanofiber supported pd–ni catalysts for electro oxidati...sunilove
Carbon nanofibers (CNF) supported Pd–Ni nanoparticles have been prepared by chemical reduction
with NaBH4 as a reducing agent. The Pd–Ni/CNF catalysts were characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical
voltammetry analysis. TEM showed that the Pd–Ni particles were quite uniformly distributed on the
surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of
the Pd–Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential
was 200mV lower and the peak current density four times higher for ethanol oxidation for Pd–Ni/CNF
compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 ◦C had a great effect on
increasing the ethanol oxidation activity.
A new technique to measure oxygen reduction kinetics underneath coatings using hydrogen permeation from the back side. Huge step towards characterising buried interface reactivity.
Electrochemical Characterization of Electrocatalysts .pptxMabrook Saleh Amer
This document summarizes an electrochemistry workshop presentation on electrocatalyst characterization. It introduces common electrochemical characterization methods like cyclic voltammetry and discusses key figures of merit for evaluating electrocatalyst activity. Examples are provided of electrocatalyst development for important reactions like hydrogen evolution, oxygen evolution, and oxygen reduction. These include developing non-precious metal catalysts and improving catalyst stability and performance through methods like decreasing platinum loading or synthesizing metal phosphides and metal oxides on supports.
The document discusses pH measurement and the components used. It describes that pH is a measurement of hydrogen ion concentration on a logarithmic scale from 0-14. It also discusses Nernst's equation, which relates electrode potential to ion concentration. The key components used for pH measurement are glass electrodes, reference electrodes like calomel or silver-silver chloride, and buffer solutions. The document provides details on the construction and functioning of these different electrode types.
This document discusses conductometric titration, which is an electrochemical analytical method that measures the electrical conductance of an electrolyte solution. It describes the principles and instrumentation of conductometry, including how conductivity is measured using a conductivity meter or by performing a titration. Some key applications of conductometric titration are determining the end point of acid-base and precipitation titrations, and it has various uses in fields like environmental analysis, food testing, and quality control.
Potentiometry1 for mpharm ist sem notes prakash64742
The document summarizes potentiometry and potentiometric titrations. Potentiometry uses measurement of electrical potential to perform qualitative and quantitative analysis. The potential of a sample is directly proportional to the activity of electroactive ions present, such as pH. Potentiometric titrations involve direct measurement of electrode potential or changes in potential upon titrant addition to determine the endpoint. Common types include acid-base, redox, complexometric, and precipitation titrations. Choice of reference and indicator electrodes depends on the reaction taking place.
Potentiometry is a method of electroanalytical chemistry used to measure electric potential. It involves measuring the potential of electrochemical cells under zero current conditions. Potentiometric titrations determine the endpoint potentiometrically by measuring changes in potential caused by the addition of a titrant. Common applications include acid-base, redox, precipitation, and complexometric titrations. Commercial potentiometers have advantages over simple potentiometers like temperature control and internal calibration.
This document discusses electrolysis and Faraday's law of electrolysis. It provides examples of predicting products of electrolysis for molten salts, aqueous salt solutions, and applying Faraday's law calculations. Key points include:
- During electrolysis, the cation is reduced at the cathode and the anion is oxidized at the anode
- In molten salts, the more easily oxidized/reduced species reacts at each electrode
- In aqueous solutions, overvoltage must be considered in addition to electrode potentials
- Faraday's law states the amount of substance reacted is directly proportional to the quantity of electricity passed through the cell
- Calculations can determine current, time, charge or mass from the other variables using Faraday's constant
Electrochemistry Basics
Table of Contents
1. Introduction
2. Voltaic Cells-Galvanic Cells
3. Cell Potential
4. Balancing Redox Reactions
5. Rules for Assigning Oxidation states
6. Additional Materials
6.1. I. Conversion
6.2. II. Free Energy & Cell Potential
6.3. III. Nernst equation
6.4. At Equilibrium
7. Terminology
8. Reference
9. Outside Links
10. Contributors
As the name suggests, electrochemistry is the study of changes that cause electrons to move. This movement of electrons is called electricity. In electrochemistry, electricity can be generated by movements of electrons from one element to another in a reaction known as a redox reaction or oxidation-reduction react
Potentiometry involves measuring electrode potentials using a reference electrode and indicator electrode. The reference electrode maintains a constant potential while the indicator electrode's potential varies with analyte concentration. Common reference electrodes include the saturated calomel electrode and silver-silver chloride electrode. Indicator electrodes include pH electrodes, ion-selective electrodes, and redox electrodes. Potentiometric measurements are used in clinical chemistry, environmental monitoring, titrations, and various industrial applications like food processing.
This document discusses potentiometry, which is an electroanalytical technique that measures the potential (voltage) of electrochemical cells containing indicator and reference electrodes. It involves using electrodes to measure voltages generated from chemical reactions. Various types of electrodes are described including metal, ion-selective, glass membrane, liquid membrane, and crystalline membrane electrodes. Applications of potentiometry include ion concentration measurements, pH measurements, and potentiometric titrations.
This document provides an overview of electrochemistry. It discusses electron transfer reactions, oxidation and reduction, voltaic cells, cell potentials, and balancing redox reactions. Key points include:
- Electron transfer reactions are oxidation-reduction or redox reactions that result in the generation of an electric current.
- Oxidation is the loss of electrons and reduction is the gain of electrons. Reduction cannot occur without oxidation providing electrons.
- A voltaic cell uses the energy from a spontaneous redox reaction to generate an electric current by transferring electrons through an external circuit between the anode and cathode.
This document summarizes an experiment on using electrocoagulation with iron electrodes to remove mercury from wastewater. Key findings include:
1) Maximum mercury removal of 94.5% was achieved after 40 minutes of electrocoagulation at an applied potential of 9V, agitation of 400 rpm, initial pH of 4.5, and electrolyte concentration of 1.333 g/L.
2) Higher applied potentials and agitation rates decreased mercury removal efficiency due to excessive oxygen generation and unsuitable floc formation.
3) Operating costs were calculated based on energy consumption and electrode material costs. Electrocoagulation was found to be an efficient and fast method for mercury removal compared to conventional techniques.
Introduction to electrochemistry by t. haraToru Hara
This document provides an introduction to electrochemistry. It discusses how electrochemistry involves the conversion of chemical energy to electrical energy, as in primary batteries where a spontaneous reaction between zinc and copper electrodes produces a flow of electrons. It also discusses the reverse process of converting electrical energy to chemical energy, as in secondary batteries that can be recharged. Key concepts covered include oxidation, reduction, standard reduction potentials, anodes, cathodes, and how electrochemical cells work through balanced redox reactions while conserving mass and charge.
This document discusses potentiometric analysis and its applications. Potentiometry involves measuring the potential difference between electrodes placed in a sample solution as the concentration of ions changes, such as during acid-base, redox, complexometric, and precipitation titrations. Some key applications of potentiometry include determining electrolyte levels in clinical samples, analyzing ions in environmental samples like water, and measuring properties in various industries like food processing, detergent manufacturing, and agriculture.
This document provides an overview of potentiometry and related electroanalytical techniques. It defines key concepts like reference electrodes, indicator electrodes, and salt bridges used in potentiometric cells. Equations for electrode potentials are described for various metal-metal ion systems. Membrane electrodes like glass pH electrodes are also summarized. The document concludes with brief discussions of potentiometric titration techniques and voltammetry methods.
The researchers synthesized TiO2 nanotubes (NTs) on Ti foil through anodic oxidation at varying voltages. Pt nanoparticles were deposited on the NTs using two methods, but only one electrode showed reactivity to H2O2. Higher anodization voltages increased NT size but decreased stability, and only undamaged NTs successfully deposited Pt. The electrode with some carbon deposits on the NT surface detected H2O2 at -0.277V, indicating it may be suitable for a lactate biosensor.
The document discusses pH meters and how they are used to measure pH. It provides details on:
- How pH is defined as the negative logarithm of hydrogen ion concentration.
- The first commercial pH meter was produced in 1928 and measured the potential difference between an indicator and reference electrode immersed in solution.
- Common reference electrodes include the saturated calomel electrode and silver/silver chloride electrodes which allow measurement of pH in a variety of solutions.
- Glass membrane electrodes contain a thin glass membrane that generates a potential difference dependent on ion concentration and are commonly used for pH measurements.
- Modern pH electrodes often combine the reference and glass membrane electrodes into a single cylinder for convenience.
This document is a thesis submitted by Okechukwu Pascal Chisom to the Department of Chemical Engineering at Nnamdi Azikiwe University in partial fulfillment of the requirements for a Bachelor's degree in Chemical Engineering. The thesis investigates the use of electrocoagulation technique to remove copper, nickel, and chromium from simulated wastewater. Laboratory experiments are conducted to study the effect of various process parameters such as pH, current density, electrode distance, temperature, charging time, and initial metal ion concentration on the removal efficiency. The results show that electrocoagulation is effective at removing the heavy metals and optimal conditions are identified.
Performance of carbon nanofiber supported pd–ni catalysts for electro oxidati...suresh899
Carbon nanofibers (CNF) supported Pd–Ni nanoparticles have been prepared by chemical reduction
with NaBH4 as a reducing agent. The Pd–Ni/CNF catalysts were characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical
voltammetry analysis. TEM showed that the Pd–Ni particles were quite uniformly distributed on the
surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of
the Pd–Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential
was 200mV lower and the peak current density four times higher for ethanol oxidation for Pd–Ni/CNF
compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 ◦C had a great effect on
increasing the ethanol oxidation activity.
Performance of carbon nanofiber supported pd ni catalysts for electro-oxidati...Science Padayatchi
This document summarizes a study on carbon nanofiber (CNF) supported Pd-Ni catalysts for electro-oxidation of ethanol in alkaline medium. Pd-Ni/CNF catalysts were prepared by chemical reduction and characterized using various techniques. Electrochemical analysis showed the Pd-Ni/CNF catalyst had lower onset potential and 4 times higher peak current density for ethanol oxidation compared to Pd/C. Increasing the temperature from 20 to 60°C greatly enhanced the ethanol oxidation activity of Pd-Ni/CNF.
Performance of carbon nanofiber supported pd–ni catalysts for electro oxidati...sunilove
Carbon nanofibers (CNF) supported Pd–Ni nanoparticles have been prepared by chemical reduction
with NaBH4 as a reducing agent. The Pd–Ni/CNF catalysts were characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical
voltammetry analysis. TEM showed that the Pd–Ni particles were quite uniformly distributed on the
surface of the carbon nanofiber with an average particle size of 4.0 nm. The electro-catalytic activity of
the Pd–Ni/CNF for oxidation of ethanol was examined by cyclic voltammetry (CV). The onset potential
was 200mV lower and the peak current density four times higher for ethanol oxidation for Pd–Ni/CNF
compared to that for Pd/C. The effect of an increase in temperature from 20 to 60 ◦C had a great effect on
increasing the ethanol oxidation activity.
A new technique to measure oxygen reduction kinetics underneath coatings using hydrogen permeation from the back side. Huge step towards characterising buried interface reactivity.
Electrochemical Characterization of Electrocatalysts .pptxMabrook Saleh Amer
This document summarizes an electrochemistry workshop presentation on electrocatalyst characterization. It introduces common electrochemical characterization methods like cyclic voltammetry and discusses key figures of merit for evaluating electrocatalyst activity. Examples are provided of electrocatalyst development for important reactions like hydrogen evolution, oxygen evolution, and oxygen reduction. These include developing non-precious metal catalysts and improving catalyst stability and performance through methods like decreasing platinum loading or synthesizing metal phosphides and metal oxides on supports.
Research efforts direct ethanol fuel cell defcAhmed ElSheikh
The document summarizes research on developing palladium-tin alloy catalysts for ethanol oxidation in alkaline fuel cells. Key findings include:
1) Pd-Sn/C catalysts synthesized using a polyol method showed twice the peak current densities of Pd/C catalysts for ethanol oxidation.
2) The Sn content was found to enhance the charge transfer rate during ethanol oxidation reactions.
3) Ethanol was found to partially oxidize on the Pd-Sn catalysts, forming acetic acid. Future work will focus on facilitating complete ethanol oxidation through DFT calculations and improving synthesis methods.
Electro catalytic performance of pt-supported poly (o-phenylenediamine) micro...sunitha81
Poly (o-phenylenediamine) (PoPD) microrods were obtained by interfacial
polymerization using ferric chloride as oxidant and without any template or
functional dopant. Pt/PoPD nanocatalysts were prepared by the reduction of chloroplatinic
acid with sodium borohydride, and the composite catalysts formed were
characterized by X-ray diffraction and electrochemical methods. The nanocomposite
of Pt/PoPD microrods has been explored for their electro-catalytic performance
towards oxidation of methanol. The electro-catalytic activity of Pt/PoPD was
found to be much higher (current density 1.96 mA/cm2 at 0.70 V) in comparison to
Pt/Vulcan electrodes (the current density values of 1.56 mA/cm2 at 0.71 V) which
may be attributed to the microrod morphology of PoPD that facilitate the effective
dispersion of Pt particles and easier access of methanol towards the catalytic sites.
Electro catalytic performance of pt-supported poly (o-phenylenediamine) micro...Science Padayatchi
1. Poly(o-phenylenediamine) (PoPD) microrods were synthesized through an interfacial polymerization reaction using ferric chloride.
2. Pt nanoparticles were deposited on the PoPD microrods through chemical reduction to create a Pt/PoPD nanocatalyst.
3. Electrochemical tests found that the Pt/PoPD nanocatalyst had higher electrocatalytic activity for methanol oxidation compared to a Pt/carbon catalyst, likely due to the microrod morphology of the PoPD facilitating better dispersion of Pt particles and access of methanol to catalytic sites.
Electrochemical study of anatase TiO2 in aqueous sodium-ion electrolytesRatnakaram Venkata Nadh
In this paper, a basic electro-analytical study on the behavior of anatase TiO2 in aqueous NaOH has been presented using cyclic voltammetry technique (CV). The study has explored the possibility of using TiO2 as anode material for ARSBs in presence of 5 M NaOH aqueous electrolyte. CV profiles show that anatase TiO2 exhibits reversible sodium ion insertion/de-insertion reactions. CV studies of TiO2 anode in aqueous sodium electrolytes at different scan rate shows that the Na+ ion insertion reaction at the electrode is diffusion controlled with a resistive behavior. Proton insertion from aqueous sodium electrolytes into TiO2 cannot be ruled out. To confirm the ion inserted and de-inserted, CV studies are done at different concentration of NaOH and it is found that at lower concentrations of NaOH, proton insertion process competes with Na+ ion insertion process and as the concentration increases, the Na+ ion insertion process becomes the predominant electrode reaction making it suitable anode materials for aqueous sodium batteries in 5 M NaOH.
This document summarizes the synthesis, characterization, and evaluation of various IrO2-based binary metal oxide electrocatalysts for the oxygen evolution reaction. IrO2, IrxRu1-xO2, IrxSnx-1O2 and IrxTax-1O2 (where x is between 1 and 0.7) were synthesized via an adapted Adams fusion method. X-ray diffraction and electron microscopy showed the materials formed nanocrystalline solid solutions. Electrochemical testing found that adding RuO2, SnO2, or Ta2O5 to IrO2 improved its catalytic performance for oxygen evolution. Specifically, Ir0.7Ru0.3O2 exhibited the best
Electro catalytic performance of pt-supported poly (o-phenylenediamine) micro...tshankar20134
This document summarizes research on developing a nanocomposite catalyst of Pt supported on poly(o-phenylenediamine) (PoPD) microrods for electro-oxidation of methanol in fuel cells. PoPD microrods were synthesized through an interfacial polymerization method using ferric chloride. Pt nanoparticles were deposited on the PoPD microrods using sodium borohydride reduction of chloroplatinic acid. Characterization with XRD showed the Pt had a face-centered cubic structure. Electrochemical tests found the Pt/PoPD catalyst had higher catalytic activity and stability for methanol oxidation compared to a Pt/carbon catalyst, which may be due to the microrod morphology facilitating better
The document summarizes research on the electrochemical deposition of lead dioxide nanostructured thin films. Key findings include:
- Lead dioxide nanostructures were successfully deposited on gold-coated substrates by anodic electrochemical deposition using nitric acid and lead chloride as reactants. The morphology was influenced by deposition parameters like potential, temperature, and pH.
- Deposition at higher temperatures (60°C vs room temperature) resulted in faster growth rates and denser nanostructures, as seen by SEM images.
- Both anodic and cathodic deposition were studied. Cathodic deposition allowed formation of different lead oxide phases depending on conditions, while anodic deposition selectively formed PbO2.
- The work provides a
This document summarizes research on using various catalysts to promote the dehydrogenation of cyclohexane to produce hydrogen gas. Key findings include:
- Monometallic silver (Ag) catalysts supported on activated carbon cloth showed increasing hydrogen evolution rates with increasing Ag loading up to 10 wt%, but rates decreased at 15 wt% loading likely due to poorer dispersion.
- Bimetallic catalysts with 1 wt% noble metals (platinum, palladium, rhodium) promoted on 10 wt% Ag/ACC showed enhanced hydrogen evolution rates compared to the monometallic Ag catalyst. In particular, a 10 wt% Ag-1 wt% Pt catalyst produced hydrogen at twice the rate of the 10 wt%
Maiyalagan,Electrochemical oxidation of methanol on pt v2 o5–c composite cata...kutty79
Platinum nanoparticles have been supported on V2O5–C composite through the reduction of chloroplatinic
acid with formaldehyde. The catalyst was characterized by X-ray diffraction and transmission electron
microscopy. Catalytic activity and stability for the oxidation of methanol were studied by using
cyclic voltammetry and chronoamperometry. Pt/V2O5–C composite anode catalyst on glassy carbon electrode
show higher electro-catalytic activity for the oxidation of methanol. High electro-catalytic activities
and good stabilities could be attributed to the synergistic effect between Pt and V2O5, avoiding the electrodes
being poisoned.
This document discusses research on electrodepositing CdSe thin films from an acidic aqueous electrolytic bath containing organic additives, specifically monosodium L-glutamate and choline chloride. The films were characterized using XRD and SEM-EDAX. It was found that both additives led to more uniform and better crystallized deposits than without additives. Films with monosodium L-glutamate showed improved photoresponse in photoelectrochemical tests, while choline chloride led to decreased photoconductivity. The organic ions from the additives are potentially adsorbed on the CdSe, introducing defects that modify the electric properties.
This document summarizes the electrochemical synthesis and corrosion inhibiting properties of a poly N-methyl aniline coating doped with di-N-propyl malonic acid on stainless steel. Cyclic voltammetry was used to polymerize N-methyl aniline in a solution containing di-N-propyl malonic acid on a stainless steel electrode. An adherent red polymer film was obtained. Electrochemical impedance spectroscopy and potentiodynamic polarization techniques showed that this polymer coating provided excellent corrosion protection of stainless steel in 0.5M sulfuric acid solution, with inhibition efficiencies above 99% as indicated by large increases in charge transfer resistance and decreases in corrosion current density compared to uncoated stainless steel.
The Electrochemical Synthesis and Corrosion Inhibitive Nature of Di N-Propyl ...IOSR Journals
This document summarizes the electrochemical synthesis and corrosion inhibiting properties of a poly N-methyl aniline coating doped with di N-propyl malonic acid on stainless steel. Cyclic voltammetry was used to electrochemically polymerize N-methyl aniline on stainless steel electrodes in a solution containing di N-propyl malonic acid. Electrochemical impedance spectroscopy and potentiodynamic polarization techniques showed that the resulting polymer coating provided excellent corrosion protection for the stainless steel in 0.5M sulfuric acid solution, with inhibition efficiencies above 98%.
This document summarizes research on using antimony-impregnated activated carbon as an electrode for detecting heavy metal ions like cadmium and lead using anodic stripping voltammetry. The researchers impregnated activated carbon with different amounts of antimony and found that electrodes with 5% antimony by weight produced the highest peak currents - 29.2 microamps for cadmium and 49.4 microamps for lead in a 100 microgram per liter solution, outperforming previous methods. The results indicate antimony-impregnated activated carbon is an effective working electrode for detecting heavy metals at low concentrations.
Synthesis, characterisation and evaluation of ir o2 based binary metal oxide ...sunilove
This document describes the synthesis, characterization, and evaluation of various binary metal oxide electrocatalysts for the oxygen evolution reaction in solid polymer electrolyte electrolyzers. Specifically, IrO2, IrxRu1-xO2, IrxSnx-1O2 and IrxTax-1O2 (where 1 ≥ x ≥ 0.7) were synthesized using the Adams fusion method, and then characterized using XRD, SEM, TEM, and electrochemical techniques. XRD analysis showed that solid solutions were formed when RuO2, SnO2, or Ta2O5 were added to IrO2. TEM analysis revealed nanosize particles for all synthesized metal oxides. Electrochemical
Synthesis, characterisation and evaluation of ir o2 based binary metal oxide ...
10.1007_s10008-015-2847-2
1. 1 23
Journal of Solid State
Electrochemistry
Current Research and Development in
Science and Technology
ISSN 1432-8488
Volume 19
Number 8
J Solid State Electrochem (2015)
19:2235-2244
DOI 10.1007/s10008-015-2847-2
Silver nanoparticles/poly ortho-toluidine/
modified carbon paste electrode as a stable
anode for hydrazine oxidation in the
alkaline media
Reza Ojani, Ali Alinezhad, Mohammad
Ja’far Aghajani & Saeid Safshekan
2. 1 23
Your article is protected by copyright and
all rights are held exclusively by Springer-
Verlag Berlin Heidelberg. This e-offprint is
for personal use only and shall not be self-
archived in electronic repositories. If you wish
to self-archive your article, please use the
accepted manuscript version for posting on
your own website. You may further deposit
the accepted manuscript version in any
repository, provided it is only made publicly
available 12 months after official publication
or later and provided acknowledgement is
given to the original source of publication
and a link is inserted to the published article
on Springer's website. The link must be
accompanied by the following text: "The final
publication is available at link.springer.com”.
3. ORIGINAL PAPER
Silver nanoparticles/poly ortho-toluidine/modified carbon paste
electrode as a stable anode for hydrazine oxidation
in the alkaline media
Reza Ojani1
& Ali Alinezhad1
& Mohammad Ja’far Aghajani1
& Saeid Safshekan1
Received: 10 October 2013 /Revised: 20 May 2014 /Accepted: 1 April 2015 /Published online: 24 April 2015
# Springer-Verlag Berlin Heidelberg 2015
Abstract Silver nanoparticles were deposited on the surface
of poly ortho-toluidine (POT) modified carbon paste electrode
(n-Ag/POT/MCPE) by the electrochemical method. The elec-
trocatalytic activity of the prepared modified electrode toward
the hydrazine oxidation in alkaline solutions was evaluated
using cyclic voltammetry (CV) and chronoamperometry
(CHA) methods. The CV experiment showed that the n-Ag/
POT/MCPE electrode is electrochemically active toward the
hydrazine oxidation, and a sharp increment in the current of
hydrazine oxidation was observed with the increase of the
hydrazine concentration. CHA results show stable steady state
current (Iss) for the hydrazine oxidation. A linear dependence
of the Iss upon the hydrazine concentration was found in the
range of 1.0×10−4
to 6.0×10−3
M hydrazine. Results imply
that the n-Ag/POT/MCPE presents stable and significantly
high electroactivity for the hydrazine oxidation.
Keywords Electrocatalysis . Silver nanoparticles . Hydrazine
oxidation . ortho-Toluidine
Introduction
Hydrazine is a highly reactive base and reducing agent which
is primarily used as a high-energy rocket propellant, as a re-
actant in military fuel cells, in nickel plating, in the polymer-
ization of urethane, for removal of halogens from wastewater,
as an oxygen scavenger in boiler feed water to inhibit corro-
sion, and in photographic development [1]. Hydrazine was
historically used as a therapeutic agent in the treatment of
tuberculosis, sickle-cell anemia, and non-specific chronic ill-
nesses [1]. The Environmental Protection Agency (EPA) has
reported hydrazine and its derivatives as environmental pol-
lutants, and the maximum recommended value of hydrazine in
effluents is set to 0.0001 % [2].
Considerable attention has been given to direct liquid fuel
cells, such as the methanol, formic acid, hydrazine, and boro-
hydride systems because of their high energy capacity com-
pared to advanced batteries [3].
For the direct hydrazine fuel cell, its most attractive feature
may be higher theoretical cell voltage of 1.57 V according to
the anode reaction (1) and cathode reaction (2) in alkaline
solutions:
N2H4 þ 4OH−
→N2 gð Þ þ 4H2O þ 4e E¨
¼ −1:16V vs:SHE ð1Þ
O2 þ 2H2O þ 4e → 4OH−
E¨
¼ 0:41V vs:SHE ð2Þ
However, oxidation of hydrazine on the surface of ordinary
electrodes suffers from high overpotential. Thus, there have
been increasing reports for the investigation of hydrazine oxi-
dation by various electrocatalysts [4–9]. Electrooxidation of
hydrazine at gold [10], nickel [11], and mercury [12] electrodes
has been studied. Hydrazine oxidation on single-crystal plati-
num surfaces (1 1 1) and (3 2 2) were studied by Chizuko
Nishihara and coworkers [13]. Their work showed that the
electrochemical oxidation of hydrazine at Pt electrode requires
a higher overpotential. The electrochemical oxidation of hydra-
zine at a silver electrode was reported by Korinek [14].
The electrooxidation of hydrazine at the carbon paste elec-
trode is a simple and cheap approach, but its kinetics are slow
and needs to high overpotentials. In order to resolve this prob-
lem, electrocatalytic modified electrodes based on a variety of
* Reza Ojani
fer-o@umz.ac.ir
1
Electroanalytical Chemistry Research Laboratory, Faculty of
Chemistry, University of Mazandaran, Babolsar, Iran
J Solid State Electrochem (2015) 19:2235–2244
DOI 10.1007/s10008-015-2847-2
Author's personal copy
4. catalysts including metals, polymer films, and metal complexes
were used. Different redox mediators such as various transition
metal hexacyanoferrates [15], ferrocencarboxylic acid [16], and
metal phethalocyanines [17] have been used in modifying car-
bon paste electrodes for hydrazine oxidation. Cobalt complexes
have been applied as mediators to modify carbon paste elec-
trodes in order to obtain a catalytic activity for hydrazine oxi-
dation [18]. A modified carbon paste electrode prepared by
using tetracyanoquinodimethanide adsorbed on silica modified
with titanium oxide showed an excellent catalytic activity and
stability for hydrazine oxidation [19].
A lot of research studies have demonstrated that coating the
electrode surface with conducting polymers (CPs) is an attrac-
tive approach for enhancing the power and scope of electro-
chemically modified electrodes [20, 21]. CP matrices have
been employed as catalyst support materials for the oxidation
of small molecules in place of conventional supports, because
when a catalyst is dispersed in carbon black, a part of the
active sites remains inaccessible to the reactant molecules.
The reason for incorporating metallic particles into the porous
matrixes is to increase the specific area of these materials and
thereby improve catalytic efficiency [22].
Among different materials, metal nanoparticles have
attracted much attention due to their unique properties and
wide varieties of potential applications in various areas includ-
ing catalysis, magnetic materials, information storage, micro-
electronics, and optoelectronics. Among various
nanocatalysts, silver nanoparticles serve as an encouraging
candidate due to its high activity in alkaline solutions. It is
known that silver possesses a higher electrical conductivity
and is approximately 100 times less expensive than platinum
[23]. Several approaches, such as electroless plating and metal
nanowire [24], chemical reduction [25], electrochemical de-
position [26], and ion beam assisted deposition [27], have
been developed to synthesize Ag structures.
In the present study, we have fabricated a nanosilver sup-
ported poly ortho-toluidine modified carbon paste electrode
using electrochemical polymerization and Ag deposition pro-
cesses to obtain a new electrocatalyst for hydrazine oxidation.
Experimental
Reagents and materials
Sodium hydroxide (from Merck), hydrazine hydrate (80 %)
(from Merck), silver nitrate (from Fluka), ortho-toluidine (OT)
(from Merck), and distilled water were used.
Instrumentation
The electrochemical experiments were performed using
potentiostat/galvanostat (BHP 2061-C-Electrochemical
Analysis System, Behpajooh, Iran) coupled with a Pentium
IV personal computer. The utilized three-electrode system was
composed of Ag/AgCl/KCl (sat’d) as reference electrode, a
platinum wire as auxiliary electrode, unmodified carbon paste
electrode, and silver nanoparticles/poly ortho-toluidine/modi-
fied carbon paste electrode (n-Ag/POT/MCPE) as working
electrode substrates.
Synthesis and characterization of the n-Ag/POT/MCPE
The unmodified carbon paste was prepared by thoroughly
mixing 1.0 g carbon powder with paraffin oil in a mortar.
The resulting paste was then inserted in the bottom of a glass
tube. The electrical connection was implemented by a copper
wire lead fitted into the glass tube. A fresh electrode surface
was generated rapidly by extruding a small plug of the paste
out of the tube and smoothing the resulting surface on white
paper until a smooth shiny surface was observed.
The electrochemical preparation of POT films was carried
out by cyclic voltammetry from 0.0 to 1.2 V versus Ag/AgCl/
KCl with the scan rate of 50 mV s−1
in an aqueous solution
containing 3.0 mM OT and 0.5 M H2SO4 up to reach 10 com-
plete cycles. Freshly prepared POT films were washed with
distilled water and monomer-free electrolyte solution. After that,
they were dipped into a 5 mM silver nitrate solution at room
temperature for 20 min. This procedure allowed for physical
adsorption of silver ions into the POT film. In order to stabilize
the silver nanoparticles, the electrode transfer in 0.1 M NaOH
solution and 10 successive potential cycling from −0.4 to 0.9 V
versus Ag/AgCl/KCl with the scan rate of 100 mV s−1
were
performed. Schematic 1 shows the sequence of steps.
Results and discussion
Cyclic voltammetric study of POT/MCPE
The poly ortho-toluidine (POT) film was prepared on the surface
of the carbon paste electrode. Figure 1 shows the typical multi-
sweep cyclic voltammograms during the electropolymerization
of OT in the 0.5 M H2SO4 solution. As can be seen, in the first
anodic sweep, the oxidation of OT occurs as a distinct irrevers-
ible anodic peak (Ep=0.92 V). A part of the oxidation products
of OT is deposited on the electrode, as a POT film. In the second
positive scan of potential, a new anodic peak is found at a po-
tential around 0.44 V which is due to the oxidation of resulting
polymeric film. The oxidation peak current of monomer is de-
creased with increasing of the number of potential cycles. The
decreasing of oxidation current is due to the loss of activity of
the electrode surface when covered with a newly formed poly-
mer film [22]. In the second reverse cycle, the new cathodic
peak is found at a potential around 0.30 V, confirming the initial
deposition of electrooxidized products. Under successive
2236 J Solid State Electrochem (2015) 19:2235–2244
Author's personal copy
5. potential cycling, the peak currents related to the polymer are
significantly increased. Moreover, the monomer oxidation po-
tential is shifted to positive potentials, and its oxidation current
decreased.
Cyclic voltammetric experiments of n-Ag/POT/MCPE
Figure 2 shows scanning cyclic voltammetry (CV) profile of
the n-Ag/POT/MCPE in 0.1 M NaOH solution. It is found that
the n-Ag/POT/MCPE exhibits high anodic and cathodic cur-
rents, showing a large surface area of the modified electrode.
Overlapped CV curves were observed to be increased with
cycling numbers and then to be stable after 10 cycles which
shows the stabilization of catalyst nanoparticles on the POT/
MCPE surface (Fig. 2).
In the anodic oxidation range of silver, four anodic peaks,
A1 at 0.28 V, A2 at 0.35 V, A3 at 0.72 V, and A4 at 0.58 V, were
obtained as shown in Fig. 2. From the cyclic voltammogram
depicted in this figure and the literature, a scheme pathway for
transitions during the potential cycling can be presented as
follows:
The first small anodic peak (A1) which is found as a shoul-
der at around 0.28 Vis related to mix of initial oxidation of Ag
to Ag(OH)2
−
through adsorption of OH−
and formation and
precipitation of a monolayer of Ag2O from supersaturated
solution of Ag(OH)2
−
, which progressively blocks off the dis-
solution reaction of Ag to Ag(OH)2
−
[28, 29].
Ag þ 2OH−
ads→Ag OHð Þ2
−
ads þ e−
ð3Þ
Ag OHð Þ2
−
ads→ Ag OHð Þ2
−
aq→Ag2O ð4Þ
According to Droog [29], the peak A2 is due to the forma-
tion of multilayer of Ag2O caused by the following reaction:
2Ag þ 2OH−
→Ag2O þ H2O þ 2e−
ð5Þ
The further forward potential sweep leads to the arising of
the peak A3 at 0.72 V which is attributed to the formation of
high-valence silver oxide (AgO):
Ag2O þ 2OH−
→2AgO þ H2O þ 2e−
ð6Þ
Scheme 1 Schematic procedure
for construction of the n-Ag/POT/
MCPE
Fig. 1 Electrochemical polymerization of OT in 3.0 mM OT + 0.5 M
H2SO4 solution (at E=0.0 to1.2 V and =0.05 V s−1
)
J Solid State Electrochem (2015) 19:2235–2244 2237
Author's personal copy
6. In the reverse scan, one oxidation peak, A4, and two
reduction peaks, C1 and C2, were delivered at 0.58,
0.40, and 0.05 V, respectively. During the cathodic
sweep, oxidation peak A4 is reported to be attributed
to continuous nucleation and growth of Ag2O film as
a result of direct electrooxidation of Ag metal [30]. Two
cathodic peaks are corresponding to the reduction of
AgO to Ag2O and Ag2O to Ag metal, respectively.
The high reduction current in Fig. 2 indicates the pres-
ence of large active sites on the surface of the n-Ag/
POT/MCPE electrode.
From the above discussions, a scheme pathway for transi-
tions during the potential cycling can be presented as follows:
Anodic transitions:
Ag→Ag OHð Þ2 → Ag2O ð7Þ
Ag→Ag2O→AgO ð8Þ
Cathodic transitions:
AgO→Ag2O ð9Þ
Ag2O→Ag ð10Þ
Fig. 2 Cyclic voltammogram of
n-Ag/POT/MCPE in 0.1 M
NaOH (at =0.1 V s−1
and
E=−0.4 to 0.9 V)
Fig. 3 Typical scanning electron
microscopy (SEM) images of
different electrodes: a bare CPE,
b POT/MCPE, and c, d
n-Ag/POT/MCPE
2238 J Solid State Electrochem (2015) 19:2235–2244
Author's personal copy
7. SEM investigation
Scanning electron micrographs of different electrodes includ-
ing bare CPE, POT/MCPE, and n-Ag/POT/MCPE are shown
in Fig. 3. The morphology for the bare CPE (Fig. 3a) shows
carbon powders enwrapped in paraffin oil and that there are
some holes or cavities on the electrode surface because the
carbon paste is porous. However, more pores on surface to-
pography were observed for POT/MCPE (Fig. 3b). Further-
more, it yields a larger available area and, in the case of intro-
ducing Ag catalyst, with better dispersion. Figure 3c shows
the morphology of the n-Ag/POT/MCPE. According to this
image, the spherical aggregates may be formed through the
settlement of several nanoparticles of Ag. Figure 3d shows the
particle size smaller than 100 nm. Thus, the effective surface
area shows that the presence of the POT gives rise to decrease
Fig. 4 CVs of CPE (a), Ag/MCPE (b), POT/MCPE (c), and n-Ag/POT/
MCPE (d) in 0.1 M NaOH solution in the a absence and b presence of
20 mM hydrazine
Fig. 5 Current–potential curves of n-Ag/POT/MCPE prepared with 1
(a), 2 (b), 3 (c), 4 (d), 5 (e), and 7 mM ( f ) OT (in the presence of
20 mM hydrazine and =20 mV s−1
). Inset: variation of electrocatalytic
peak current of N2H4 oxidation with OT concentration
Fig. 6 Cyclic voltamograms of n-Ag/POT/CPE in 0.1 M NaOH solution
in the presence of 20 mM hydrazine at scan rate of 20 mV s−1
prepared in
5 (a), 7 (b), 10 (c), 12 (d), and 15 (e) cycle numbers of OT polymerization.
Inset: variation of electrocatalytic peak current of N2H4 oxidation with
cycle number
Fig. 7 CVs of n-Ag/POT/MCPE prepared in 5 (a), 10 (b), 15 (c), 20 (d),
25 (e), and 30-minute ( f ) accumulation times in the presence of 20 mM
N2H4 and 0.1 M NaOH solution at =20 mV s−1
. Inset: variation of
electrocatalytic peak current of N2H4 oxidation with accumulation times
J Solid State Electrochem (2015) 19:2235–2244 2239
Author's personal copy
8. the aggregation of the Ag nanoparticles, relatively. So, the
effective surface area of the aggregates is improved. These
results are in agreement with electrochemical experiments.
Electrochemical oxidation of hydrazine
Figure 4 reveals the effect of presence of hydrazine on various
electrodes (containing unmodified and modified electrodes).
In the absence of hydrazine (Fig. 4a), no anodic or cathodic
current was observed, but in the presence of N2H4, the oxida-
tion of hydrazine on unmodified electrode occurs in 0.4 V
(Fig. 4b, a). With modified electrodes, the anodic current
gradually increases and oxidation potential is largely changed,
but this shift for n-Ag/POT/MCPE is greater than n-Ag/
MCPE and POT/MCPE (−0.05, 0.0, and 0.02, respectively).
These results suggested that the accumulation of silver nano-
particles on POT has a positive effect on oxidation potential.
The parameters affecting the electrode modification
The OT concentration effect
The effect of OT monomer concentration (1.0–7.0 mM) dur-
ing the electropolymerization for preparation of the POT/
MCPE films with certain thickness was investigated on reac-
tivity of the modified electrodes for N2H4 oxidation. The ob-
tained results for electrocatalytic peak current in this condition
Fig. 8 Current–potential curves
of n-Ag/POT/MCPE in 0.1 M
NaOH solution containing
hydrazine at various scan rates: 10
(a), 20 (b), 30 (c), 40 (d), 50 (e),
and 60 mV s−1
( f ). (condition =
5.0 mM, 20 cycle numbers, and
20-min accumulation time). Inset
A: variation of electrocatalytic
peak current of N2H4 oxidation
with scan rate. Inset B: variation
of electrocatalytic peak current of
N2H4 oxidation with root square
of scan rate
Fig. 9 The plot of hydrazine oxidation peak potential on the n-Ag/POT/
MCPE electrode versus log v
Fig. 10 Electrochemical responses of n-Ag/POT/MCPE in 0.1 M NaOH
in the 0 (a), 1.0 (b), 2.5 (c), 5 (d), 7.5 (e), 10 ( f ), 15 (g), 20 (h), 30 (i), 40
(j), 50 (k), 60 (l), 70 (m), and 80 mM (n) hydrazine (3.0 mM OT, 5.0 mM
AgNO3 solution at E=−0.4 to 0.1, and =20 mV s−1
). Inset: variation of
electrocatalytic peak current of N2H4 with hydrazine oxidation
concentration
2240 J Solid State Electrochem (2015) 19:2235–2244
Author's personal copy
9. show that there is an increase in the electrooxidation peak
current of hydrazine when there is an increase in the monomer
concentration from 1.0 to about 3.0 mM (Fig. 5). A decrease
in N2H4 electrooxidation current can be observed when the
higher monomer concentrations are used. This may be attrib-
uted to the simultaneous formation of some oligomers during
the polymerization of OT in high concentrations [22]. Thus,
formation of the oligomers affects the morphology of the
polymer which decreases the amount of Ag nanoparticles dis-
persed in the film. It also decreases the effective surface area
of the nanocatalyst.
Effect of cycle number of electropolymerization
on the hydrazine oxidation
Electrochemical polymerization offers the possibility of con-
trolling the thickness and homogeneity of POT film on the
electrode surface. The influence of cycle numbers for prepa-
ration of the POT films on the electrocatalytic oxidation of
N2H4 was investigated, and the corresponding results are
shown in Fig. 6. Under the constant accumulation time of
Ag ions, the anodic peak current rises progressively for cycle
numbers up to 10 cycles and drops afterward. This implies
that the electrocatalysis of hydrazine oxidation is sensitive to
thickness of the polymer film. The increase in the anodic peak
current for cycle numbers up to 10 cycles may be due to the
occupation of Ag nanoparticles in the pores of polymers with
the real sizes. The decrease in anodic peak current for N2H4
oxidation beyond 10 cycles may be due to reducing of real
surface area of Ag hydroxide by the excessive presence of
polymers on the electrode surface.
The effect of accumulation time
In order to incorporate Ag ions at the surface of the electrode,
the freshly prepared POT/MCPE was placed in an aqueous
solution of 5.0 mM AgNO3 in an open circuit for several
minutes. The electrocatalytic oxidation peak currents of
N2H4 increased gradually with increasing of accumulation
times. The maximum value was achieved at 20 min and then
decreased, so 20 min was chosen as the optimum time, which
indicated that saturated accumulation on the n-Ag/POT /
MCNTPE had been achieved (Fig. 7).
The scan rate effect
Cyclic voltammograms of n-Ag/POT/MCPE in the presence
of 20 mM hydrazine at the various scan rates were recorded
(Fig. 8). From this figure, it can be seen that with increasing
Table 1 Comparison of the
efficiency of n-Ag/POT/MCPE
with some of the previously
reported electrodes for N2H4
oxidation in alkaline medium
Electrocatalyst Electrolyte Hydrazine
concentration
(mM)
Scan rate
(mV s−1
)
Peak
potential
(V)
Reference
Au/TiO2-NTs/Ti 0.1 M phosphate
buffer (pH 7.0)
0.85 100 0.23 [32]
Ni(OH)2–MnO2/MGCE 0.1 M phosphate
buffer (pH 7.0)
20 20 0.65 [33]
CuO(H)/MCu 0.1 M phosphate
buffer (pH 7.0)
20 50 0.25 [34]
Ni(II)/BA/MWCNT 0.1 M NaOH 2 50 0.53 [35]
n-Ag/POT/MCPE 0.1 M NaOH 20 20 −0.05 This work
Fig. 11 Chronoamperogram plots of different N2H4 concentrations on
the POT/MCPE: absence (a), 10 (b), 20 (c), 30 (d), 40 (e), and 50 mM ( f )
(condition: 3.0 mM OT, at potential step of 0.05 V and t=20 s)
Fig. 12 Chronoamperogram plots of different N2H4 concentrations on
the n-Ag/POT/MCPE: absence (a), 1.0 (b), 10 (c), 15 (d), 20 (e), 30 ( f ),
40 (g), 50 (h), and 60 mM (i) (condition: 3.0 mM OT and 5.0 mM
AgNO3, at potential step of 0.05 V and t=20 s). Inset: variation of
N2H4 oxidation current with N2H4 concentration
J Solid State Electrochem (2015) 19:2235–2244 2241
Author's personal copy
10. the potential scan rate, the peak potential for catalytic oxida-
tion of hydrazine shifts to positive potentials (Fig. 8a). This
clear shift of the peak potential occurred as expected for irre-
versible electrochemical reactions [31]. The obtained cyclic
voltammograms were used to examine the variation of oxida-
tion peak current versus scan rate. The oxidation current of
hydrazine increased linearly with the square root of scan rate
on n-Ag/POT/MCPE (Fig. 8c), suggesting that the reaction is
diffusion control limited.
In order to get the information on the rate-determining step,
Tafel slope, b, was determined using the following equation
valid for a totally irreversible diffusion controlled process
[31]:
Ep ¼ 0:5b log υ þ constant ð11Þ
where b is the Tafel slope and v is the scan rate; the Tafel slope
can also be expressed as
b ¼ 2:3 R T αn Fð Þ−1
ð12Þ
On the basis of these equations, the slope of the plots of Ep
versus log is b/2 which was found equal to 0.137 in this work
(Fig. 9), so b=0.274 V. These slope values indicate a transfer
coefficient equal to 0.25.
The effect of hydrazine concentration
Cyclic voltammetric responses of the n-Ag/POT/MCPE in
0.1 M NaOH solution containing different hydrazine concen-
trations are presented in Fig. 10. It can be seen, upon the
addition of hydrazine, that an enhancement in the anodic cur-
rent was created.
From the CV profile in the absence of hydrazine (Fig. 10,
a) and those in the presence of hydrazine (b–n), it is found that
an enhancement in the anodic current commences at the po-
tential of −0.34 V, showing the high capability of Ag nano-
particles for oxidation of hydrazine in alkaline solution as
shown in reaction (1).
Fig. 13 Plot of I versus
t−1/2
obtained from
chronoamperometric experiments
of n-Ag/POT/MCPE in 0.1 M
NaOH solution containing
different concentrations of
hydrazine: 1.0, 10, 15, 20, 30, 40,
50, and 60 mM, respectively
Fig. 14 a Chronoamperometric
response for the n-Ag/POT/
MCPE in the 0.1 M NaOH+
20 mM N2H4 solution at potential
step of 0.05 (t=600 s). b The
chronoamperograms of
n-Ag/POT/MCPE in the 0.1 M
NaOH+20 mM N2H4: after
preparation of modified electrode
(a) and after 5 days (b)
2242 J Solid State Electrochem (2015) 19:2235–2244
Author's personal copy
11. These results show that the prepared n-Ag/POT/MCPE
presents high electroactivity toward the hydrazine oxidation.
Plot of the anodic peak current (Ip) versus added hydrazine
concentrations is shown in insets of Fig. 10 where a well linear
relationship (R2
=0.9914) appears from 1.0 to 50 mM. Also,
Table 1 lists the peak potential shift of some modified elec-
trodes. As can be seen, the prepared electrode presented low
peak potential for the hydrazine oxidation comparison to some
of the previously reported electrodes.
Chronoamperometric investigation
Chronoamperometric study of hydrazine oxidation
on the n-Ag/POT/MCPE
Chronoamperometry (CHA) was used for the hydrazine oxi-
dation at a fixed potential of 0.05 V. Effect of the hydrazine
concentration on chronoamperograms for the POT/MCPE and
n-Ag/POT/MCPE at a potential step of 0.05 V is shown in
Figs. 11 and 12. At this potential, in the absence of hydrazine,
no anodic or cathodic current was observed. With the addition
of hydrazine, there are increases in the anodic currents for
modified electrodes, but this increment for n-Ag/POT/MCPE
is greater than for POT/MCPE (Figs. 11 and 12). These results
shows that chronoamperograms are in good agreement with
cyclic voltammograms. So the ability of Ag nanoparticles in
the improvement of hydrazine oxidation in alkaline media was
demonstrated again.
As can be seen in Fig. 12, an increase in the concentration
of N2H4 from 1.0 to 40 mM caused a linear increase in the
steady state current (R2
=0.9908). The oxidation reaction of
hydrazine results in the visible evolution of N2 gas on the
surfaces of the n-Ag/POT/MCPE and POT/MCPE. Therefore,
the current oscillation at up to 30 mM hydrazine could be
ascribed to the bubbling of N2 gas through the reaction (1).
In order to get more information about the electrocatalytic
process, chronoamperometry was used to evaluate the diffu-
sion coefficient of hydrazine. Chronoamperometric measure-
ments were carried out at different concentrations of hydrazine
on the n-Ag/POT/MCPE by setting the working electrode
potential at 0.05 V. The diffusion coefficient was obtained
according to the Cottrell equation [31]:
I ¼ nFACD
1
.
2
π
−1
.
2
t
−1
.
2
ð13Þ
where n, A, D, and C are the number of electrons (n=4),
geometrical surface area (0.152 cm2
), diffusion coefficient
(cm2
/s), and bulk concentrations (mol/cm3
) of hydrazine, re-
spectively. I is the current controlled by the diffusion of hy-
drazine from the bulk solution to the electrode/solution inter-
face. From the slope of the plot (Fig. 13), the D of hydrazine
was calculated as 2×10−7
cm2
/s.
Stability of the n-Ag/POT/MCPE
Different aspects regarding the stability of the n-Ag/POT/
MCPE were investigated. The long-term stability of modified
electrode was examined by using CHA technique. Figure 14
presents current–time plots for hydrazine oxidation at the n-
Ag/POT/MCPE in 0.1 M NaOH in the presence of 20 mM
N2H4. To evaluate the activity and stability of the n-Ag/POT/
MCPE, chronoamperogram was recorded for a large time win-
dow in the presence of N2H4. It is obvious that the n-Ag/POT/
MCPE exhibits a good stability toward N2H4 oxidation. Also,
the signal responses of the modified electrode were recorded
and studied in a few days. After 5 days, the n-Ag/POT/MCPE
yielded 82 % of the original response.
Conclusion
Silver nanoparticles were deposited on the surface of POT
modified carbon paste electrode using the electrochemical
method. The SEM investigation showed a larger available
area and better dispersion of silver nanoparticles on modified
electrode. Electrooxidation of hydrazine on the n-Ag/POT/
MCPE takes place at −0.05 V while the peak potential of
hydrazine oxidation on the unmodified electrode is 0.4 V.
The cyclic voltammogram and chronoamperometric study
showed an increase in oxidation current with addition of hy-
drazine concentration. Our work showed that nanosilver is a
stable substrate which provides excellent activity for oxidation
of hydrazine. The high electroactivity of the n-Ag/POT/
MCPE could be related to its large surface area. Finally, the
preparation of this modified electrode is cheap, simple, and
affordable by considering the economy.
References
1. Von Burg R, Stout T (1991) J Appl Toxic 11:447–450
2. Amlathe S, Gupta VK (1988) Analyst 113:1481–1483
3. Atwan MH, Northwood DO, Gyenge EL (2007) J Hydrogen
Energy 32:3116–3125
4. Salimi A, Miranzadeh L, Hallaj R (2008) Talanta 75:147–156
5. Salimi A, Abdi K (2004) Talanta 63:475–483
6. Zare HR, Nasirizadeh N (2007) Electrochim Acta 52:4153–4160
7. Yamada K, Yasuda K, Tanaka H, Miyazaki Y, Kobayashi T (2003) J
Power Sources 122:132–137
8. Yamada K, Asazawa K, Yasuda K, Ioroi T, Tanaka H, Miyazaki Y,
Kobayashi T (2003) J Power Sources 115:236–242
9. Salimi A, Hallaj R (2004) Electroanalysis 16:1964–1971
10. Golabi SM, Noor-Mohammadi F (1998) J Solid State Electrochem
2:30–37
11. Felischmann M, Korinek M, Plrtcher D (1972) J Electroanal Chem
34:499–506
12. Eissner U, Gileadi E (1970) J Electroanal Chem 28:81–88
J Solid State Electrochem (2015) 19:2235–2244 2243
Author's personal copy
12. 13. Nishihara C, Raspini IA, Kondoh H, Shindo H, Kaise M, Nozoye H
(1992) J Electroanal Chem 338:299–315
14. Korinek K, Korita J, Nusiloua M (1969) J Electroanal Chem 21:
421–427
15. Sriman Narayanan S, Scholz F (1999) Electroanalysis 11:465–469
16. Khalilzadeh MA, Karimi-Maleh H (2010) Anal Lett 43:186–196
17. Ozoemena KI, Nyokong T (2005) Talanta 67:162–168
18. Pang DW, Deng HB, Wang ZL (1994) Electrochim Acta 39:847–
854
19. Duarte JC, Cássia Silva Luz R, Damos FS, Oliveira AB, Kubota LT
(2007) J Solid State Electrochem 11:631–638
20. Profeti D, Olivi P (2004) Electrochim Acta 49:4979–4985
21. Zhiani M, Rezaei B, Jalili J (2010) J Hydrogen Energy 35:9298–
9305
22. Raoof JB, Ojani R, Abdi S, Hosseini SR (2012) J Hydrogen energy
37:2137–2146
23. Bidault F, Kucernak A (2010) J Power Sources 195:1023–1032
24. Kostowskyj MA, Kirk DW, Thorpe SJ (2010) J Hydrogen Energy
35:5666–5672
25. Demarconnay L, Coutanceau C, Léger JM (2004) Electrochim Acta
49:4513–4521
26. Tang Z, Liu S, Dong S, Wang E (2001) J Electroanal Chem 502:
146–151
27. Liu T, Tang HQ, Cai XM, Zhao J, Li DJ, Li R, Sun XL (2007) Nucl
Instrum Methods Phys Res B 264:282–286
28. Ambrose J, Barradas RG (1974) Electrochim Acta 19:781–786
29. Droog JMM, Alderliesten PT, Bootsma GA (1979) J Electroanal
Chem 99:173–186
30. Stonehart P (1968) Electrochim Acta 13:1789–1803
31. Yi Q, Li L, Yu W, Zhou Z, Xu G (2008) J Mol Catal A Chem 295:
34–38
32. Hosseini M, Momeni MM, Faraji M (2011) J Mol Catal A Chem
335:199–204
33. Anu Prathap MU, Anuraj V, Satpati B, Srivastava R (2013) J
Hazard Mater 262:766–774
34. Karim-Nezhad G, Jafarloo R, Seyed Dorraji P (2009) Electrochim
Acta 54:5721–5726
35. Zhenga L, Songa JF (2009) Talanta 79:319–326
2244 J Solid State Electrochem (2015) 19:2235–2244