“ExMarm” is specialized in the production, processing and resale
of Greek marble worldwide.
Our company headquarters are located in Nea Smyrni, 2 km from the city
centre of Athens and our production is in Penteli, 15 km form the city centre.
We have a longstanding history of over 70 years in the processing of stone
and we constantly aim to improve our techniques by optimizing every step
of our production. We can deliver the best products and services to our
customers because we understand their needs.
We are active in the whole sale market and we also have strong relationships
with engineering offices, thus giving us the opportunity to understand
better our customer’s needs. Our company is active abroad having executed
projects for an important number of countries in Europe, Americas,
Middle East and North Africa. This is proof that our expertise and
multicultural mentality has helped us penetrate different markets.
OUR COMPANY
02 03
3. Blocks | Slabs | Cut to size | Tiles
We constantly keep you informed of every step of the project and specifically
from the very beginning, by sending you photos of the block that we will
process on your behalf and again for every intermediate step of the project,
up to the final packing, of the cut to size product which will be ready
to be placed on site.
Our vertical production gives us the opportunity to have full quality control
over production in order to serve all our clients in the most professional
manner. We have all kinds of machines from gang saws and monowires
to bridge saws, edge polishers and line polishing machines. With this vast
variety of machinery we are able to monitor internally and step by step
the processing of each project. As a result we deliver the final product
always under strict quality controls which make us confident that we will
satisfy the needs of the most demanding customer.
We have invested also in our after sales services by providing the wholesaler
or the engineering office any assistance related to how to treat marble
that after many years might need minor or important renovation. We are able
to suggest the best products and techniques for the protection or removal
of any marks.
04 05
4. White Snow
WHITE
ARABESCATO
GRECO
WHITE CLOUD
SANTA MARINA
white
DIONYSSOS
white
green veins
DIONYSSOS
white
black veins
DIONYSSOS
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.717 kg/m3
•Absorption coefficient 0,11 %wt •Compressive strength (dry c) 111,00 mpa •Modulus of rapture (dry c) 19,00 mpa •Abration resistance 6,68 mm
•CaO 54,80 • MgO 1,55 • SiO2
1,10 • Fe2
O3
0,14 • Al2
O3
0,20 • K2
O 0,09 • Na2
O 0,04 • MnO 0,02 • LOI 43,05 • CALCITE 98 • QUARTZ 0,5
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.717 kg/m3
•Absorption coefficient 0,11 %wt •Compressive strength (dry c) 111,00 mpa •Modulus of rapture (dry c) 19,00 mpa •Abration resistance 6,68 mm
• CaO 54,80 • MgO 1,55 • SiO2
1,10 • Fe2
O3
0,14 • Al2
O3
0,20 • K2
O 0,09 • Na2
O 0,04 • MnO 0,02 • LOI 43,05 • CALCITE 98 • QUARTZ 0,5
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.717 kg/m3
•Absorption coefficient 0,11 %wt •Compressive strength (dry c) 111,00 mpa •Modulus of rapture (dry c) 19,00 mpa •Abration resistance 6,68 mm
•CaO 54,80 • MgO 1,55 • SiO2
1,10 • Fe2
O3
0,14 • Al2
O3
0,20 • K2
O 0,09 • Na2
O 0,04 • MnO 0,02 • LOI 43,05 • CALCITE 98 • QUARTZ 0,5
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.705 kg/m3
•Absorption coefficient 0,11 %wt •Compressive strength (dry c) 95,00 mpa •Modulus of rapture (dry c) 15,00 mpa •Abration resistance 8,55 mm
•CaO 55,00 • MgO 0,45 • SiO2
0,05 • Fe2
O3
0,14 • Al2
O3
0,40 • K2
O 0,04 • Na2
O 0,03 • MnO 0,02 • LOI 42,76 • CALCITE 96 • DOLOMITE 34 • QUARTZ 1
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.847 kg/m3
•Open porosity coefficient, % vol (din 52102) 0,45 •Water absorption % wt (astm c-97) 0,15 • Compressive strength, mpa (astm c-170) 118
• Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 28 •Abrasion resistance, mm (din 52108 - 20 cycles) 3,29
•CaO 30,00 • MgO 21,10 • SiO2
0,10 • Fe2
O3
0,05 • Al2
O3
0,05 • K2
O 0,01 • Na2
O 0,01 • MnO 0,01 • LOI 46,90 • CALCITE 4 • DOLOMITE 95
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.825 kg/m3
•Water absorption % wt (astm c-97) 0,37 •Compressive strength, mpa (astm c-170) 98,5 •Abrasion resistance, mm (din 52108 - 20 cycles) 0,58
• Flexural strength 7,04 n/mm2
•DOLOMITE 96 • CALCITE 4
06 07
5. White NESTOS
grey NESTOS
beige NESTOS
WHITE
VOLAKAS
WHITE SIVEC
WHITE SEMI
KAVALA
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.680 kg/m3
•Absorption coefficient 0,09 %wt •Compressive strength (dry c) 77,00 mpa •Modulus of rapture (dry c) 17,00 mpa •Abration resistance 6,16 mm
•CaO 55,00 • MgO 0,50 • SiO2
0,70 • Fe2
O3
0,11 • Al2
O3
0,20 • K2
O 0,02 • Na2
O 0,03 • MnO 0,01 • LOI 43,50 • CALCITE 97 • DOLOMITE 1 • QUARTZ 2
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.680 kg/m3
•Absorption coefficient 0,09 %wt •Compressive strength (dry c) 77,00 mpa •Modulus of rapture (dry c) 17,00 mpa •Abration resistance 6,16 mm
•CaO 55,00 • MgO 0,50 • SiO2
0,70 • Fe2
O3
0,11 • Al2
O3
0,20 • K2
O 0,02 • Na2
O 0,03 • MnO 0,01 • LOI 43,50 • CALCITE 97 • DOLOMITE 1 • QUARTZ 2
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.680 kg/m3
•Absorption coefficient 0,09 %wt •Compressive strength (dry c) 77,00 mpa •Modulus of rapture (dry c) 17,00 mpa •Abration resistance 6,16 mm
•CaO 55,00 • MgO 0,50 • SiO2
0,70 • Fe2
O3
0,11 • Al2
O3
0,20 • K2
O 0,02 • Na2
O 0,03 • MnO 0,01 • LOI 43,50 • CALCITE 97 • DOLOMITE 1 • QUARTZ 2
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.711 kg/m3
•Absorption coefficient 0,09 %wt •Compressive strength (dry c) 58,00 mpa •Modulus of rapture (dry c) 16,00 mpa •Abration resistance 1,94 mm
•CaO 54,50 • MgO 0,64 • SiO2
0,20 • Fe2
O3
0,05 • Al2
O3
0,05 • K2
O 0,01 • Na2
O 0,01 • MnO 0,01 • LOI 43,60 • CALCITE 97 • DOLOMITE 1
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.825 kg/m3
•Absorption coefficient 0,19 %wt •Compressive strength (dry c) 139,00 mpa •Modulus of rapture (dry c) 10,00 mpa •Abration resistance 2,20 mm
•CaO 32,00 • MgO 19,00 • SiO2
0,20 • Fe2
O3
0,05 • Al2
O3
0,05 • K2
O 0,01 • Na2
O 0,01 • MnO 0,01 • LOI 46,80 • CALCITE 9 • DOLOMITE 91
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.840 kg/m3
•Absorption coefficient 0,14 %wt •Compressive strength (dry c) 175,62 mpa •Modulus of rapture (dry c) 14,37 MPa
08 09
6. WHITE PIRGOI
WHITE
PIRGOI m.k.
WHITE SEMI
NAXOS
WHITE PIRGOI
SPLASH
BROWN
KAPANDRITI
WHITE NAXOS
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.510 kg/m3
•Water absorption % wt (astm c-97) 1,11 •Compressive strength, mpa (astm c-170) 68
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 8 •Abrasion resistance, mm (din 52108 - 20 cycles) 3,96
•CaO 47,90 • MgO 0,21 • SiO2
5,30 • Fe2
O3
1,84 • Al2
O3
1,50 • K2
O 0,19 • Na2
O 0,04 • MnO 0,11 • LOI 41,50 • CALCITE 90 • QUARTZ 5 • FELDSPAR 5,0
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.710 kg/m3
•Water absorption % wt (astm c-97) 0,09 •Compressive strength, mpa (astm c-170) 89
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 13 •Abrasion resistance, mm (din 52108 - 20 cycles) 8,56
•CaO 55,60 • MgO 0,50 • SiO2
0,07 • Fe2
O3
0,14 • Al2
O3
0,02 • K2
O 0,02 • Na2
O 0,04 • MnO 0,02 • LOI 43,00 • CALCITE 98 • QUARTZ 2
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.710 kg/m3
•Water absorption % wt (astm c-97) 0,09 •Compressive strength, mpa (astm c-170) 89
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 13 •Abrasion resistance, mm (din 52108 - 20 cycles) 8,56
•CaO 55,60 • MgO 0,50 • SiO2
0,07 • Fe2
O3
0,14 • Al2
O3
0,02 • K2
O 0,02 • Na2
O 0,04 • MnO 0,02 • LOI 43,00 • CALCITE 98 • QUARTZ 2
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.846 kg/m3
•Open porosity coefficient, % vol (din 52102) 0,49 •Water absorption % wt (astm c-97) 0,17 •Compressive strength, mpa (astm c-170) 125
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 30 •Abrasion resistance, mm (din 52108 - 20 cycles) 3,51
•CaO 34,00 • MgO 18,00 • SiO2
0,50 • Fe2
O3
0,07 • Al2
O3
0,12 • K2
O 0,01 • Na2
O 0,03 • MnO 0,01 • LOI 45,80 • CALCITE 3 • DOLOMITE 97
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.846 kg/m3
•Open porosity coefficient, % vol (din 52102) 0,49 •Water absorption % wt (astm c-97) 0,17 •Compressive strength, mpa (astm c-170) 125
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 30 •Abrasion resistance, mm (din 52108 - 20 cycles) 3,51
•CaO 34,00 • MgO 18,00 • SiO2
0,50 • Fe2
O3
0,07 • Al2
O3
0,12 • K2
O 0,01 • Na2
O 0,03 • MnO 0,01 • LOI 45,80 • CALCITE 3 • DOLOMITE 97
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.846 kg/m3
•Open porosity coefficient, % vol (din 52102) 0,49 •Water absorption % wt (astm c-97) 0,17 •Compressive strength, mpa (astm c-170) 125
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 30 •Abrasion resistance, mm (din 52108 - 20 cycles) 3,51
•CaO 34,00 • MgO 18,00 • SiO2
0,50 • Fe2
O3
0,07 • Al2
O3
0,12 • K2
O 0,01 • Na2
O 0,03 • MnO 0,01 • LOI 45,80 • CALCITE 3 • DOLOMITE 97 10 11
7. BEIGE VRATSA
BEIGE SPECIAL
BEIGE LEVADIA
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.623 kg/m3
•Absorption coefficient 0,65 %wt •Compressive strength (dry c) 135,00 mpa •Modulus of rapture (dry c) 8,00 mpa •Abration resistance 3,89 mm
•CaO 54,50 • MgO 0,30 • SiO2
1,00 • Fe2
O3
0,21 • Al2
O3
0,32 • K2
O 0,00 • Na2
O 0,00 • MnO 0,05 • LOI 43,50 • CALCITE 98 • DOLOMITE 1 • QUARTZ 1
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.700 kg/m3
•Absorption coefficient 3,78 %wt •Compressive strength (dry c) 787 mpa •Modulus of rapture (dry c) 108 kg/cm2
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.670 kg/m3
•Water absorption % wt (astm c-97) 1,27 •Compressive strength, mpa (astm c-170) 101
•Modulus of rupture under flexure(flexural strength) - wet condition, mpa (astm c-99) 6 •Abrasion resistance, mm (din 52108 - 20 cycles) 3,21
•CaO 33,00 • MgO 19,00 • SiO2
0,70 • Fe2
O3
0,10 • Al2
O3
0,1 • K2
O 0,20 • Na2
O 0,11 • MnO 0,01 • LOI 46,00 • CALCITE 12 • DOLOMITE 88 • QUARTZ 25 • CHROMITE 6 12 13
GREEN OASSIS
GREEN TINOS
GREEN VERIA
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.802 kg/m3
•Absorption coefficient 0,41 %wt •Compressive strength (dry c) 111,00 mpa •Modulus of rapture (dry c) 24,00 mpa •Abration resistance 2,50 mm
•CaO 23,50 • MgO 22,50 • SiO2
24,00 • Fe2
O3
5,60 • Al2
O3
0,60 • K2
O 0,04 • Na2
O 0,04 • MnO 0,11 • LOI 23,50 • CALCITE 35 • DOLOMITE 1
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.701 kg/m3
•Water absorption % wt (astm c-97) 0,22 •Compressive strength (dry c) 94,00 mpa •Modulus of rapture (dry c) 20,00 mpa •Abration resistance 2,86 mm
•CaO 16,75 • MgO 26,60 • SiO2
28,65 • Fe2
O3
7,25 • Al2
O3
0,50 • K2
O 0,04 • Na2
O 0,04 • MnO 0,12 • LOI 20,15 • CALCITE 53 • CHROMITE 2,00 • Fe OXIDES etc. 10
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.945 kg/m3
•Absortion coefficient wt% 0,21 •Compressive strength (dry c) 1364 mpa • Modulus of rapture kg/cm2 388
•CaO 14,80 • MgO 3,80 • SiO2
43,00 • Fe2
O3
8,50 • Al2
O3
14,20 • K2
O 0,75 • Na2
O 3,30 • MnO 0,17 • LOI 20,15 • CALCITE 31 • DOLOMITE 40,00 • QUARTZ 25 • CHROMITE 6
8. 14
BLACK
LEVADIA
BLACK
MACEDONIA
GREY ALIVERY
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.690 kg/m3
•Absorption coefficient 0,01 %wt •Compressive strength (dry c) 98,00 mpa •Modulus of rapture (dry c) 31,00 mpa •Abration resistance 3,78 mm
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.690 kg/m3
•Absorption coefficient 0,54 %wt •Compressive strength (dry c) 106,00 mpa •Modulus of rapture (dry c) 15,00 mpa •Abration resistance 5,59 mm
•CaO 54,50 • MgO 0,70 • SiO2
1,00 • Fe2
O3
0,10 • Al2
O3
0,26 • K2
O 0,04 • Na2
O 0,09 • MnO 0,00 • LOI 43,50 • CALCITE 96 • DOLOMITE 4
LAB TESTS DATA
PHYSICAL & MECHANICAL PROPERTIES
•Apparent density 2.714 kg/m3
•Absorption coefficient 0,12 %wt •Compressive strength (dry c) 99,00 mpa •Modulus of rapture (dry c) 19,00 mpa •Abration resistance 7,54 mm
•CaO 54,30 • MgO 0,90 • SiO2
0,13 • Fe2
O3
0,28 • Al2
O3
0,60 • K2
O 0,12 • Na2
O 0,03 • MnO 0,02 • LOI 43,00 • CALCITE 93 • DOLOMITE 4 • QUARTZ 2