La pedagogía praxeológica se centra en la acción educativa, la autonomía y la socialización a través de la reflexión. Propone que la función docente debe ser socializadora, fomentar la autonomía y la reflexión en los estudiantes, y promover valores sociales, políticos y culturales.
Claudia Marquez has over 15 years of experience leading retail operations and teams. She currently serves as Co-Manager for Forever 21, where her responsibilities include store operations, loss prevention, inventory management, and training over 120 associates. Previously, she was Assistant Store Manager and Store Manager for Forever 21 and Agaci, exceeding sales goals and improving customer satisfaction during her tenure.
Spotify was developed in 2006 in Stockholm, Sweden by Daniel Ek and Martin Lorentzon. It is a music, podcast, and video streaming service that provides digitally rights-managed content from record labels and media companies. Spotify works across various platforms and offers a free subscription with limitations, as well as a premium subscription without ads or song limits. It has over 60 million users and continues growing its catalog of playlists and premium subscribers.
Este documento describe las principales redes sociales actuales como Facebook, Twitter, WhatsApp y Google+. Explica que Facebook es la red social más grande con miles de millones de usuarios y se utiliza principalmente para compartir actualizaciones y contenido con amigos. WhatsApp es popular para mensajería, Twitter para compartir actualizaciones breves y Google+ para blogs y contenido multimedia.
La pedagogía praxeológica se centra en la acción educativa, la autonomía y la socialización a través de la reflexión. Propone que la función docente debe ser socializadora, fomentar la autonomía y la reflexión en los estudiantes, y promover valores sociales, políticos y culturales.
Claudia Marquez has over 15 years of experience leading retail operations and teams. She currently serves as Co-Manager for Forever 21, where her responsibilities include store operations, loss prevention, inventory management, and training over 120 associates. Previously, she was Assistant Store Manager and Store Manager for Forever 21 and Agaci, exceeding sales goals and improving customer satisfaction during her tenure.
Spotify was developed in 2006 in Stockholm, Sweden by Daniel Ek and Martin Lorentzon. It is a music, podcast, and video streaming service that provides digitally rights-managed content from record labels and media companies. Spotify works across various platforms and offers a free subscription with limitations, as well as a premium subscription without ads or song limits. It has over 60 million users and continues growing its catalog of playlists and premium subscribers.
Este documento describe las principales redes sociales actuales como Facebook, Twitter, WhatsApp y Google+. Explica que Facebook es la red social más grande con miles de millones de usuarios y se utiliza principalmente para compartir actualizaciones y contenido con amigos. WhatsApp es popular para mensajería, Twitter para compartir actualizaciones breves y Google+ para blogs y contenido multimedia.
Copper and its alloys like bronze and brass are highly versatile materials used in construction, electronics, transportation, and machine tools. Copper alloys can be cut, formed, bent and joined through various fabrication techniques. The main types of bronze are copper alloys with tin, while brass alloys are copper mixed with zinc. Proper handling and cleaning of copper alloy sheets is required to prevent scratches and corrosion.
The heat-affected zone (HAZ) is the area of sheet metal that undergoes chemical and structural changes during cutting due to localized melting. It can cause issues like discoloration, increased hardness, reduced strength, and corrosion. The size of the HAZ depends on factors like the material's thermal diffusivity, amount and duration of heat applied, and beam size - with techniques like laser cutting producing the smallest HAZ. Effects of the HAZ need to be considered for consistent bending angles and crowning during forming.
Le piegatrici ad alto tonnellaggio sono i giganti della lamiera. Impianti e struttura sono portati a lavorare in condizioni gravose. I pezzi piegati sono particolarmente costosi, specialmente con gli acciai altoresistenziali. Ogni errore costa molto caro. Per questo è ancora più importante fare un acquisto informato e consapevole. Ma quali sono i fattori più importanti che devi tenere in considerazione?
Electrochemical and chemical finishes of stainless steel - Gasparini Industri...Gasparini Industries srl
This document discusses various electrochemical and chemical finishing processes for stainless steel, including electropolishing, electrolytic coloring, burnishing, acid etching, painting, enamelling, physical vapor deposition, and metallic coating. Electropolishing smoothes the surface and increases corrosion resistance by removing surface layers in a chemical bath. Electrolytic coloring creates unique colors through interference of light reflecting off the stainless steel's chromium oxide surface layer when its thickness is increased. Burnishing creates a black color through chemical bath treatment. Acid etching creates patterns by chemically removing exposed areas left unprotected during the process. Painting and enamelling provide aesthetic finishes, while physical vapor deposition and metallic coating can apply durable color or corrosion resistant coat
L'acciaio inossidabile, a differenza di altri metalli, contiene una certa percentuale di cromo. Questo elemento legante crea un film di ossido protettivo dello spessore di alcuni atomi. Nonostante sia molto sottile è molto resistente e impedisce la corrosione. Inoltre si autorigenera: se viene rimosso o danneggiato si riforma istantaneamente. Per questo motivo l'acciaio inossidabile può essere utilizzato anche senza essere verniciato. Sono disponibili molte finiture che adattano l'estetica naturale dell'acciaio ai contesti e agli usi più diversi.
Le finiture si possono dividere tra meccaniche, elettriche, elettrochimiche e chimiche. Qui di seguito andiamo ad elencare solamente quelle meccaniche. Le categorie con la cifra 1 sono laminate a caldo, mentre quelle con la cifra 2 sono laminate a freddo. Vengono categorizzate secondo la norma EN 10088-2. Queste sono le finiture meccaniche della lamiera più comuni.
10 modi per evitare graffi e ammaccature piegando l'acciaio inossidabile - Ga...Gasparini Industries srl
L'acciaio inox è un bellissimo materiale. Brillante, resistente, inattaccabile. Ma è anche costoso, difficile da piegare, e facile da graffiare. Quando lavoriamo pezzi che vengono usati per rivestimenti, elettrodomestici e mobili, anche una piccola riga diventa un grosso problema. Come si può tagliare e piegare l'acciaio inossidabile senza rovinarlo?
Copper and its alloys like bronze and brass are highly versatile materials used in construction, electronics, transportation, and machine tools. Copper alloys can be cut, formed, bent and joined through various fabrication techniques. The main types of bronze are copper alloys with tin, while brass alloys are copper mixed with zinc. Proper handling and cleaning of copper alloy sheets is required to prevent scratches and corrosion.
The heat-affected zone (HAZ) is the area of sheet metal that undergoes chemical and structural changes during cutting due to localized melting. It can cause issues like discoloration, increased hardness, reduced strength, and corrosion. The size of the HAZ depends on factors like the material's thermal diffusivity, amount and duration of heat applied, and beam size - with techniques like laser cutting producing the smallest HAZ. Effects of the HAZ need to be considered for consistent bending angles and crowning during forming.
Le piegatrici ad alto tonnellaggio sono i giganti della lamiera. Impianti e struttura sono portati a lavorare in condizioni gravose. I pezzi piegati sono particolarmente costosi, specialmente con gli acciai altoresistenziali. Ogni errore costa molto caro. Per questo è ancora più importante fare un acquisto informato e consapevole. Ma quali sono i fattori più importanti che devi tenere in considerazione?
Electrochemical and chemical finishes of stainless steel - Gasparini Industri...Gasparini Industries srl
This document discusses various electrochemical and chemical finishing processes for stainless steel, including electropolishing, electrolytic coloring, burnishing, acid etching, painting, enamelling, physical vapor deposition, and metallic coating. Electropolishing smoothes the surface and increases corrosion resistance by removing surface layers in a chemical bath. Electrolytic coloring creates unique colors through interference of light reflecting off the stainless steel's chromium oxide surface layer when its thickness is increased. Burnishing creates a black color through chemical bath treatment. Acid etching creates patterns by chemically removing exposed areas left unprotected during the process. Painting and enamelling provide aesthetic finishes, while physical vapor deposition and metallic coating can apply durable color or corrosion resistant coat
L'acciaio inossidabile, a differenza di altri metalli, contiene una certa percentuale di cromo. Questo elemento legante crea un film di ossido protettivo dello spessore di alcuni atomi. Nonostante sia molto sottile è molto resistente e impedisce la corrosione. Inoltre si autorigenera: se viene rimosso o danneggiato si riforma istantaneamente. Per questo motivo l'acciaio inossidabile può essere utilizzato anche senza essere verniciato. Sono disponibili molte finiture che adattano l'estetica naturale dell'acciaio ai contesti e agli usi più diversi.
Le finiture si possono dividere tra meccaniche, elettriche, elettrochimiche e chimiche. Qui di seguito andiamo ad elencare solamente quelle meccaniche. Le categorie con la cifra 1 sono laminate a caldo, mentre quelle con la cifra 2 sono laminate a freddo. Vengono categorizzate secondo la norma EN 10088-2. Queste sono le finiture meccaniche della lamiera più comuni.
10 modi per evitare graffi e ammaccature piegando l'acciaio inossidabile - Ga...Gasparini Industries srl
L'acciaio inox è un bellissimo materiale. Brillante, resistente, inattaccabile. Ma è anche costoso, difficile da piegare, e facile da graffiare. Quando lavoriamo pezzi che vengono usati per rivestimenti, elettrodomestici e mobili, anche una piccola riga diventa un grosso problema. Come si può tagliare e piegare l'acciaio inossidabile senza rovinarlo?
10 modi per evitare graffi e ammaccature piegando l'acciaio inossidabile - Ga...
Le 4 caratteristiche della lamiera che tu e la tua pressa dovete conoscere - Gasparini Industries srl
1. Le 4 caratteristiche della
lamiera che tu e la tua pressa
DOVETE conoscere
Scopriamo perché non è possibile affidarsi
alle previsioni
2. Uno dei fenomeni inevitabili nelle
presse piegatrici è
la deformazione della struttura.
Stiamo piegando l'acciaio con
dell'altro acciaio, che per ragioni
fisiche avrà una deflessione. In
particolare la traversa superiore
tenderà ad incurvarsi al centro. Il
punzone in quel punto si troverà più
distante dalla matrice e l'angolo
ottenuto sarà maggiore. Il risultato è
che il profilo sarà più chiuso alle
estremità e più largo in centro, e
assomiglierà allo scafo di una barca.
Vedremo come una differenza
anche minima può rendere la
piegatura un processo pieno di
insidie.
3. Questo fenomeno di
deflessione è compensato con
la bombatura: il banco
viene incurvato verso l'alto per
mantenere la matrice a una
distanza costante dalla traversa.
Esistono due tipi di bombatura:
la prima utilizza un sistema
di cunei per
sollevare meccanicamente la
matrice; la seconda sfrutta dei
cilindri idraulici a corsa corta
posti nella traversa inferiore.
4. Ma di quanto compensare? La maggior parte dei costruttori di pressopiegatrici si affida a
delle tabelle, compilate conoscendo la struttura della pressa e le caratteristiche del
materiale dichiarate dalla fonderia. Tutto corretto, in teoria. In pratica, non
funziona perché il comportamento della lamiera non è prevedibile. Ha una propria
variabilità che dipende da una serie di fattori. Conoscerli e possibilmente compensarli è
indispensabile per non sprecare tempo e materiale in test e campioni, soprattutto oggi
dove i quantitativi sono frammentari: ottenere il risultato giusto al primo tentativo diventa
fondamentale.
5. 1. Non tutti gli acciai sono creati uguali
Cosa si intende con acciaio S275? La lamiera è solitamente classificata secondo la sua
tensione di snervamento in MPa. Questo valore è molto variabile, e dipende dalle
impurità nella colata e dalle imperfezioni nelle tecniche produttive. Per evitare il pericolo
di costruire strutture fragili, la normativa UNI EN 10027-1 prevede che quello indicato sia
il valore minimo.
Sotto l'etichetta S275 potrà rientrare qualsiasi acciaio con tensione di snervamento non
inferiore a 275 MPa (e non superiore a 355 MPa, dove inizia la classe S355). Il risultato è
che anche un 320 MPa verrà venduto come S275, nonostante sia il 16% più resistente.
6. Questa maggiore resistenza del materiale richiede alla pressa uno sforzo più elevato, che
produrrà inevitabilmente una deformazione della traversa superiore. Per esempio,
passando da un acciaio da 275 MPa a uno da 320 MPa avremo una differenza di 0,05 mm
in altezza. Potrà sembrare un valore trascurabile, ma per ottenere un errore di 1° su 90°
basta davvero poco:
In altre parole, uno spessore inferiore a quello di un foglio di carta (che misura circa 0,1
mm) provoca già differenze molto evidenti. Teniamo a mente che cave strette come
queste sono usate per piegare lamiere sottili in applicazioni che richiedono solitamente
qualità molto elevata.
Apertura cava Profondità per Δ=1°
6 mm 0,04 mm
10 mm 0,05 mm
12 mm 0,07 mm
7. 2. Non tutte le lamiere escono col buco
I dati di targa dell'acciaio che acquistiamo, attendibili o meno, perdono completamente di
significato quando modifichiamo la lamiera. I fori cambiano la resistenza alla
deformazione lungo la linea di piega, sia nel caso di taglio termico che per asportazione di
truciolo.
Se poi nello stesso pezzo abbiamo alcune pieghe su parti piene e altre che cadono sulle
parti vuote, è impossibile fare pronostici. Le punzonature inoltre introducono
anche tensioni interne che rendono ancora più difficile gestire la bombatura pensata
come quota fissa di deformazione.
8. 3. Le condizioni contano
L'acciaio è un materiale vivo. La direzione di laminazione crea delle fibre nella struttura,
perciò piegare una lamiera in parallelo o perpendicolare a questa direzione avrà
effetti diversi sia nella forza di piega che nel ritorno elastico.
Una lastra appena decapata ha una resistenza più alta rispetto a una che ha subito
un invecchiamento e una ossidazione superficiale, anche dopo poche settimane.
Oltretutto, non è la stessa cosa piegare un acciaio rovente o uno esposto al gelo
invernale: la temperatura influisce nelle condizioni di lavorazione e porta a risultati
diversi
9. Anche le stesse caratteristiche dimensionali sono estremamente variabili,
soprattutto per quanto riguarda lo spessore. A tale proposito, la normativa EN
10051:1991+A1:1997 divide la lamiera in varie classi. Prendiamo ad esempio
l'acciaio tra i 260 e i 340 MPa, negli spessori fino a 2 mm, e con larghezze tra
1201 e 1500 mm:
Categoria A1 A B C D
Tolleranza
(mm)
± 0,14 mm ± 0,19 mm ± 0,22 mm ± 0,25 mm ± 0,27 mm
In sostanza, una lastra da 2 mm nominali può avere uno spessore variabile del 14% nel
caso migliore, e del 31% nel caso peggiore.
10. 4. Chi di taglio ferisce, di taglio perisce.
Mentre la cesoiatura modifica le fibre della lamiera, il taglio al plasma, al laser o
l'ossitaglio generano uno shock termico localizzato sui bordi del foglio e sul perimetro dei
fori, che non può essere ignorato.
Per questi motivi, una buona pressa piegatrice non può e non deve basarsi su nessun tipo
di banca dati, e non può fare affidamento su nessun software di calcolo o previsione. Non
esiste algoritmo in grado di prevedere il comportamento della lamiera. Pensare che
l'acciaio si comporti come un materiale perfetto e immutabile è un sogno che porta
presto a un brusco risveglio.
Se la piegatura non è perfetta, le saldature sono più difficili, la verniciatura si complica e
il montaggio diventa più difficile, specialmente in caso di assemblaggi con tolleranze
molto strette. Aumentano anche gli sprechi di materiale e le ore di lavoro necessarie.
11. Questi 4 fattori possono ridurre i margini di un'azienda, se vengono ignorati invece
che affrontati. Il piegatore e la pressa devono conoscere a fondo il materiale, saper
reagire ai cambiamenti ed adattarsi per garantire sempre il risultato ottimale.
12. Gasparini Industries s.r.l.
Via F. Filzi, 33
31036 – Istrana (Treviso – TV)
Italia – Italy
t (+39) 0422 8355
f (+39) 0422 835700
e info@gasparini.it
Codice Fiscale, Partita IVA: IT 04364470262 – REA: TV
343703
gasparini.it
Migliora le tue lavorazioni su
www.gasparini.it – presse piegatrici e
cesoie idrauliche