Cemaric Heating Element For Solar Water Heater, Hard Water Qyality
Specially Designed For Solar Water Heater
A: Instant Hot Water Tap, Traditional Electrical Water Heater, Storage
Water Heater, Boiling Water Heater, Water Dispenser, Coffee Machine,
Beverage Dispenser and House/Apartment/Hotel Water Heating Solution.
B: Industry Boiler, Electric Heating, Electrolyte Heating Source etc.
1. Guaranteed Safety:
Heating wire will be oxidized immediately when the ceramic is broken.
producing leakage current much lower than body safety value: ( 10 mA)
2. High Energy Efficiency:
With high thermal conductivity ceramic, higher energy efficiency was achieved
compared with traditional heater.
3. Corrosion Resisting:
No need for corrosive-resistant coating, silicon nitride ceramic has excellent
anti-acid/alkali properties, never rust.
4. Fast Circulating:
High power was concentrated in a small ceramic heater, and circulating of
water in the tank was accelerated, results in uniform temperature distribution.
5. Anti Incrustation Scale:
The ceramic surface was well polished, avoiding scale adhesion.
6. Intelligent temperature Control:
Integrated temperature control device was used to control the heater according
to water-temperature automatically. No intervention needed.Models:
Item No. Heating Size Install Hole Power Joint
A1 85*17*4mm 17*4mm 2000-2500W 1” 1.25” 1.5”
A2 85*17*4mm 17*4mm 200-800W 1” 1.25” 1.5”
B1 73*30*4mm 30*4mm 2500-3500W 1” 1.25” 1.5”
C1 60*17*4mm 17*4mm 1500-2000W 1” 1.25” 1.5”
D1 102*24*4mm 24*4mm 3000-3800W 1” 1.25” 1.5”
Rated Voltage AC 220/110V 50/60HZ
Rated Power: 200-3800W
Insulation Electric Strength: No breakdown in 60s under 2500V/50HZ
Leakage Current: < 0.025 mA in normal condition, < 10mA
Use of media: Water, Acid and alkali solution, Air, Oils,
Organic solvents, Gas, etc.
Volume Density 3.2-3.3g/cm3
Fracture Toughness 5.0-8.0 MPa*m 1/2
Room Temperature Strength Resistance > 900MPa
High Temperature Strength Resistance > 700MPa
Vickers Hardness 15-20GPa
Relative Dielectric Constant 6-7
Volume Resistivity 10^14 Ω·cm
Thermal Conductivity 20-50W(m*K)
Thermal Expansion Coefficient 3.0*10-6/K