A 0.5-µm InGaP Etch Stop Power pHEMT Process Utilizing Multi-Level High
Density Interconnects
Walter A. Wohlmuth, Li Liu, Larry Witkowski, Rick Morton, Thorsten Saeger, Wolfgang Liebl, Mike
Fredd, Domingo Farías, Wayne Struble, Calvin Weichert, John Walkky, Steve Mahon, Otto Berger
TriQuint Semiconductor, 2300 N.E. Brookwood Pkwy., Hillsboro, OR 97124, wwohlmuth@tqs.com, 503-615-9236
Keywords: pHEMT, InGaP, BCB, D-mode
Abstract
A robust and highly manufacturable InGaP etch stop
pHEMT process with 0.5-µm gate lengths on 150 mm substrates
is presented. The process utilizes a double recess approach to
realize high breakdown, depletion-mode transistors with a
nominal gate to drain breakdown voltage of 17 V. The
transistors feature a nominal pinch-off voltage of –800 mV, on-
resistance of 1.8 ohm-mm, extrinisic transconductance of 350
mS/mm, off-capacitance of 0.3 pF/mm, unity current gain cut-
off frequency of 25 GHz, maximum frequency of oscillation of
90 GHz, and IDSS and IMAX values of 200 and 500 mA/mm,
respectively. Passive components include precision 50
ohm/square NiCr resistors, 280 ohm/square epitaxial N-
resistors, and 0.63 fF/um2
MIM capacitors. These devices are
integrated with TriQuint’s high density, planarized,
interconnect architecture enabling tremendous wiring flexibility
and packaging simplicity. The interconnect structure utilizes
benzocyclobutene (BCB) inter-metal dielectrics to form two
levels of thick, global interconnects in addition to one level of
local interconnect. This process, named TQPHT, is offered to
external customers through TriQuint Foundry Services for a
wide variety of applications including in part: high performance
GSM, CDMA, and WLAN switches, medium power amplifiers,
and low-noise amplifiers.
INTRODUCTION
In this paper we discuss the development of a 0.5-µm
InGaP etch stop pHEMT process on 150 mm wafers at
TriQuint Oregon. The development was driven by two
primary factors. The first factor was to transfer the 0.5-µm
AlAs etch stop power pHEMT process on 100 mm wafers
from Texas to Oregon fabrication facilities of TriQuint
converting directly to 150 mm wafers. This facilitated a high
volume, low cost solution available to both internal designers
and external customers through Foundry services. The
second factor involved the optimization of the process and
epitaxy technology for the creation of high performance
GSM, CDMA, and WLAN switch components, low-noise
amplifiers, and medium power amplifiers for both internal
and external customers. The technology transfer and
development also involved converting the interconnect
architecture to one that employs low-dielectric constant
materials based on benzocyclobutene.
PROCESS ARCHITECTURE
The process utilizes MBE on VGF, LEC, or VB
substrates. The growth sequence begins with the formation
of a superlattice buffer of alternating layers of GaAs and
AlGaAs deposited on the substrate. Unintentionally-doped
spacer layers of AlGaAs are placed on either side of the
unintentionally-doped InGaAs channel with Silicon delta-
doped layers placed on both sides of the channel-spacer layer
stack. A transition layer of AlGaAs is placed between the
lower spacer layer and the superlattice buffer to improve
noise performance. A Schottky layer of AlGaAs is placed on
top on the upper spacer layer to target the desired pinch-off
voltage and transconductance. An InGaP etch stop layer is
positioned on top of the Schottky layer followed by an upper
AlGaAs layer and then N+
GaAs ohmic contact layers. An
InGaP etch stop was used instead of an AlAs etch stop to
reduce device on-resistance and to obtain extremely high etch
selectivity [1]. The conduction band offset between the
AlGaAs and InGaP material systems is significantly less than
that between the AlAs and AlGaAs material systems,
permitting the use of a thicker etch stop layer. Typical room
temperature Hall measurements produced sheet carrier
concentrations of 3.15E12 cm-2
and electron mobility in
excess of 6500 cm2
/V•s.
Fabrication begins with the definition of fiducials
and wide recess openings. Upon formation of these features
a blanket film of plasma-assisted chemical vapor deposited
silicon dioxide (POX) is deposited to passivate and protect
the surface from physical and chemical damage during
subsequent process steps. Implant isolation is then
performed. The ohmic contacts are formed within dry etched
openings in the POX using AuGeNiAu alloyed at 400o
C.
Ohmic test is then performed to measure the ungated
transistor current, the ohmic contact resistance, the N+
layer
resistivity, and the N-
layer resistivity. The typical ohmic
contact resistance ranges from 0.10 to 0.15 ohm-mm due to
process variations. The N-
epitaxial resistors are formed
utilizing the openings formed by the wide recess etch.
Typical temperature coefficient of these resistors is 3000 ppm
per degree centigrade referenced to 25o
C with nominal sheet
resistance of 280 ohm/square. The gate feature is created
utilizing a TiPtAu metallization that is placed within dry
etched openings in the POX. The narrow recess into the
AlGaAs material utilizes NH4OH:H2O2:H2O chemistry, which
provides excellent etch selectivity over InGaP and is a
standard wet etch chemistry used for MESFET processes at
TriQuint [2]. The InGaP etch stop is removed in HCl:H2O,
which has a high etch selectivity with respect to AlGaAs [1].
The gate metal is deposited and lifted off. Immediately after
gate formation a blanket coating of plasma-assisted chemical
vapor deposited silicon nitride (PSN) is deposited prior to
Nickel-Chromium (NiCr) thin film, high-precision resistor
formation. These resistors have a temperature coefficient that
is less than 100 ppm/o
C, referenced to 25o
C, over the –40 to
+125o
C temperature range, and possess a sheet resistance of
50 +/- 3 ohm/square. The maximum current and voltage
ratings of the NiCr resistors are 1.0 mA/µm and 50 mV/µm,
respectively. Another blanket coat of PSN is applied after
precision resistor formation for physical and chemical
protection of the NiCr prior to interconnect formation. The
first interconnect metal (Metal0) consists of TiPtAu
metallization and is used primarily as a local interconnect to
the device contacts of the transistors, varactors, resistors, and
Schottky diodes. This metal is also used as the bottom plate
of a high precision MIM capacitor. Another PSN layer is
then deposited to serve as the MIM capacitor dielectric prior
to the formation of the top plate of the MIM capacitor using a
TiPtAu metallization. The MIM dielectric is formed with a
100 nm thick PSN film possessing a relative permittivity of
6.8 and giving a capacitance per unit area of 0.63 +/- 0.10
fF/um2
. A final layer of PSN is deposited prior to proceeding
with the upper layers of global interconnects.
The interconnect architecture proceeds with the
application of a planarizing, interlevel dielectric composed of
benzocyclobutene (BCB). This dielectric is formed using
conventional spin-on techniques and then cured at low
temperature. Once cured, the material is mechanically tough,
exhibits less than 0.25% water absorption, and has a relative
permittivity of approximately 2.7. Inter-level vias are formed
using an Helicon plasma etch system. The vias are
electroplated along with metallic global interconnects.
Patterned field metal is used to delineate the global
interconnect metallic features. A thin dielectric layer of PSN
separates the BCB layers and encapsulates the metal1
features. Upon completion of Via1 and Metal1 a second set
of global interconnects are formed, Via2 and Metal2. The
substrate is then coated with a final passivation PSN layer
and bondpad via openings are formed to access test points on
devices and circuits. A representative schematic cross-
section of the process architecture is displayed in Figure 1.
The nominal thickness of Metal1 and Metal2 are 2.0 and 4.0
µm, respectively. The first layer of BCB is nominally 1.0 µm
thick and the second layer is nominally 2.8 µm thick. The
final passivation PSN is a total of 0.8 µm thick.
Figure 1: Schematic cross-section of the TQPHT process
A STEM image of a portion of the transistor and interconnect
architecture is displayed in Figure 2.
ILD PSN1
BCB1
Base dielectrics
BCB2
Metal0
Ohmic Gate
Figure 2: STEM cross-section of pHEMT process.
The excellent degree of planarization of the BCB can clearly
be seen over the gate, ohmic, and metal0 features. The base
dielectrics are composed of a combination of POX and PSN.
Also evident are the wide and narrow recess ledges. Upon
completion of front-side processing, the wafers can be treated
in a number of ways. These options include: thinning the
substrate down to thickness of 4, 7, or 10 mils; sawing out
die; and/or substrate via formation.
Detailed and thorough process qualification has been
completed and passed at wafer level and on packaged
products. The wafer level reliability testing included
autoclave at 121o
C, 100% relative humidity, and 15 psi for 96
hours, high temperature unbiased bake at 275o
C in air for 168
hours, and temperature cycle from –40 to +125o
C for 1000
cycles. The packaged product reliability testing included
HTOL under bias and at 150o
C junction temperature,
preconditioning, autoclave, HAST at 130o
C with 85% relative
humidity for 96 hours, temperature cycle, thermal shock, and
CDM and HBM ESD testing.
DEVICE AND CIRCUIT PERFORMANCE
The D-mode transistor pinch-off voltage (Vp) is
centered at –800 mV with a process window of +/- 200 mV.
The IDSS (Vgs=0.0V) corresponding the centered pinch-off
voltage is 200 mA/mm while the IMAX (Vgs=+1.0V) is 500
mA/mm. The use of wet etch processes rather than dry etch
processes produces transistors with very high channel current
for a given Vp and gate length, as well as nicely formed
transconductance (Gm) curves as a function of Vgs variation.
A representative extrinsic Gm and Ids curve as a function of
Vgs at a fixed Vds of 3.0 V is displayed in Figure 3.
0
50
100
150
200
250
300
350
400
450
500
0
50
100
150
200
250
300
350
-1.5 -1 -0.5 0 0.5 1
Vgs (V)
Ids
Gm
Figure 3: Gm and Ids vs Vgs relationship.
The transconductance has a good plateau in peak value over a
wide range of Vgs values and does not exhibit any spurious
inflection points or additional peaks. The unity current gain
cut-off frequency (ft) is displayed in Figure 4 for Vds equal
to 1.5 and 3.0 V as a function of Vgs.
0
5
10
15
20
25
30
35
-0.6 -0.4 -0.2 0 0.2 0.4 0.6
Vgs (V)
Vds=1.5V
Vds=3.0V
Figure 4: Ft as a function of Vgs for a nominal D-mode pHEMT.
The noise performance of the D-mode transistors
was evaluated and is displayed in Figure 5. Noise figure
(Fmin) below 0.3 dB with associated gain of 15 dB is
obtained at a frequency of 2 GHz. The process is suitable for
LNAs in the L, C, and S frequency bands.
0
0.5
1
1.5
2
0
2
4
6
8
10
12
14
16
18
0 2 4 6 8 10 12
Frequency (GHz)
Fmin
Ga
Figure 5: Noise figure and associated gain of the D-mode pHEMT.
Detailed load-pull measurements were performed
with representative data presented in Figure 6 as a function of
input power (Pin). The data is from a 300 µm device biased
at Vds=8.0V and Ids=IDSS/2 at 1.9 GHz under continuous
wave operation. Peak values of gain, power added efficiency
(Efficiency), and output power (Pout) were determined to be
29 dB, 64%, and 530 mW/mm, respectively, for a given
source and load tuning. Excellent operation was obtained up
to Vds=17 V with output power increasing to beyond 1000
mW/mm. The results indicate that the process can support
general purpose amplifiers in applications including CATV
and VSAT for satellite communications.
0
5
10
15
20
25
30
0
10
20
30
40
50
60
70
-20 -15 -10 -5 0 5
Pin (dBm)
Pout
Gain
Efficiency
Figure 6: Load-pull data of a D-mode pHEMT at 1900 MHz vs Pin.
A high power GSM switch for quad-band cellular
modules has been demonstrated in this process. The switch is
able to accommodate many different systems such as GSM,
E-GSM, PCS, and DCS and is leading a shift away from the
conventional PIN diodes as the selected component to switch
RF signals at the transmit/receive antenna port. PIN diodes
have high insertion loss and require high bias current relative
to pHEMT transistors enabling pHEMTs to become the
technology of choice for cellular phone handsets. The
insertion loss, 2nd
harmonic (H2) suppression, and 3rd
harmonic (H3) suppression levels for a single pole six throw
(SP6T) transmit/receive switch is displayed in Figure 7 at a
control voltage of 2.5V and a frequency of 915 MHz.
SP6T TQ4M4006
TX1 (Vctrl=2.5v F=915MHz)
-120
-110
-100
-90
-80
-70
-60
-50
-40
-30
-20
26 27 28 29 30 31 32 33 34 35 36
Input Power (dBm)
Harmonics(dBc)
-2.0
-1.8
-1.6
-1.4
-1.2
-1.0
-0.8
-0.6
-0.4
-0.2
0.0
InsertionLoss(dB)
H2H3
Loss
Figure 7: Harmonics suppression and insertion loss of a SP6T GSM switch at
2.5V control voltage.
This switch component is used for 850 MHz GSM, 900 MHz
GSM, 1800 MHz DCS, and 1900 MHz PCS systems with
separate arms for each receive band with the transmit arms
combining the GSM signals and the DCS and PCS signals
separately. State-of-the-art insertion loss and harmonic
suppression levels are achieved with this circuit.
A high power antenna switch in a single pole three
throw configuration has also been demonstrated in this
process. This switch is ideally suited to applications where
the antenna of a CDMA handset is to be routed to the Cellular
duplexer, the PCS duplexer and the GPS receiver input. The
switch provides optimized input 3rd
order intercept point
(IP3) and cross modulation for use in CDMA applications.
The input IP3 and current for a single pole three throw switch
is displayed in Figure 8 at a control voltage of 2.5 V and a
frequency of 837 MHz. World class single tone desense and
ESD robustness levels are achieved with this circuit.
TQP4M3007 CDMA SP3T
Tx to Antenna IIP3 (Vctrl = 2.7 V, T= 25 C)
Tx tones at 837 and 838 MHz
60
62
64
66
68
70
72
74
76
78
80
22.0 23.0 24.0 25.0 26.0
Total Tx Input Power (dBm)
IIP3(dBm)
0
5
10
15
20
25
30
35
40
45
50
Current(uA)
Figure 8: Input IP3 and control current for SP3T CDMA switch at 2.7V
control voltage.
CONCLUSIONS
A detailed description of the TQPHT process architecture has
been presented along with representative device and circuit
performance. This robust and highly manufactureable
process can be used for a wide variety of applications.
REFERENCES
[1] A. W. Hanson et al., GaAs IC Technical Digest, pp. 195-197, Nov.
1998.
[2] E. P. Finchem et al. GaAs MANTECH Technical Digest, pp. 163-166.
April 1994.
ACRONYMS
CATV: cable television amplifiers
CDM: charge device model
CDMA: coded division multiple access
DCS: digital communication system
E-GSM: enhanced global system for mobile communications
ESD: electrostatic discharge
GSM: global system for mobile communications
HAST: highly accelerated stress testing
HBM: human body model
HTOL: high temperature operating life
LEC: liquid encapsulated Czochralski
LNA: low-noise amplifiers
MESFET: metal-semiconductor field-effect transistor
PCS: personal communication system
PHEMT: pseudomorphic high-electron mobility transistor
STEM: scanning transmission electron microscopy
VB: vertical Bridgeman
VGF: vertical gradient freeze
VSAT: very small antenna terminals
WLAN: wireless local area network

More Related Content

What's hot

Under ground cables presention
Under ground cables presentionUnder ground cables presention
Under ground cables presentionRazu Khan
 
Trigate transistors and future processors
Trigate transistors and future processors Trigate transistors and future processors
Trigate transistors and future processors Chinmay Chepurwar
 
Underground Cables
Underground Cables Underground Cables
Underground Cables Parth Pawar
 
High voltage cable insulation systems
High voltage cable insulation systemsHigh voltage cable insulation systems
High voltage cable insulation systemsSanket Tambakhe
 
.3mm CSP and LFCSP Reliability
.3mm CSP and LFCSP Reliability.3mm CSP and LFCSP Reliability
.3mm CSP and LFCSP ReliabilityGreg Caswell
 
High Performance Printed Circuit Boards - Lecture #1
High Performance Printed Circuit Boards - Lecture #1High Performance Printed Circuit Boards - Lecture #1
High Performance Printed Circuit Boards - Lecture #1Samsung Electro-Mechanics
 
Design and construction of underground cable transmission line
Design and construction of underground cable transmission lineDesign and construction of underground cable transmission line
Design and construction of underground cable transmission lineFazlur Rahman
 
The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...
The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...
The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...IJECEIAES
 
Medtronic Senior Design Poster
Medtronic Senior Design PosterMedtronic Senior Design Poster
Medtronic Senior Design PosterLawrence Yeh
 
The Effect of Coating and Potting on the Reliability of QFN devices
The Effect of Coating and Potting on the Reliability of QFN devicesThe Effect of Coating and Potting on the Reliability of QFN devices
The Effect of Coating and Potting on the Reliability of QFN devicesGreg Caswell
 

What's hot (20)

Under ground cables presention
Under ground cables presentionUnder ground cables presention
Under ground cables presention
 
High k dielectric
High k dielectricHigh k dielectric
High k dielectric
 
C&I Cables Tests
C&I Cables TestsC&I Cables Tests
C&I Cables Tests
 
Trigate transistors and future processors
Trigate transistors and future processors Trigate transistors and future processors
Trigate transistors and future processors
 
High k dielectric
High k dielectricHigh k dielectric
High k dielectric
 
Underground Cables
Underground Cables Underground Cables
Underground Cables
 
High voltage cable insulation systems
High voltage cable insulation systemsHigh voltage cable insulation systems
High voltage cable insulation systems
 
Wide Bandgap Ceramic Capacitor Update - APEC 2017
Wide Bandgap Ceramic Capacitor Update - APEC 2017Wide Bandgap Ceramic Capacitor Update - APEC 2017
Wide Bandgap Ceramic Capacitor Update - APEC 2017
 
.3mm CSP and LFCSP Reliability
.3mm CSP and LFCSP Reliability.3mm CSP and LFCSP Reliability
.3mm CSP and LFCSP Reliability
 
High Performance Printed Circuit Boards - Lecture #1
High Performance Printed Circuit Boards - Lecture #1High Performance Printed Circuit Boards - Lecture #1
High Performance Printed Circuit Boards - Lecture #1
 
Low cycle fatigue
Low cycle fatigueLow cycle fatigue
Low cycle fatigue
 
Underground cable
Underground cableUnderground cable
Underground cable
 
High voltage underground cables
High voltage underground cablesHigh voltage underground cables
High voltage underground cables
 
Design and construction of underground cable transmission line
Design and construction of underground cable transmission lineDesign and construction of underground cable transmission line
Design and construction of underground cable transmission line
 
The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...
The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...
The Effect of Plasma-Treated Boron Nitride on Partial Discharge Characteristi...
 
Medtronic Senior Design Poster
Medtronic Senior Design PosterMedtronic Senior Design Poster
Medtronic Senior Design Poster
 
The Effect of Coating and Potting on the Reliability of QFN devices
The Effect of Coating and Potting on the Reliability of QFN devicesThe Effect of Coating and Potting on the Reliability of QFN devices
The Effect of Coating and Potting on the Reliability of QFN devices
 
Underground cables
Underground cablesUnderground cables
Underground cables
 
Underground cables
Underground cablesUnderground cables
Underground cables
 
Cathodic Protection
Cathodic ProtectionCathodic Protection
Cathodic Protection
 

Viewers also liked

Sistema informatic
Sistema informaticSistema informatic
Sistema informaticEdu Alias
 
Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1
Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1
Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1Lemon Lee
 
Sales Management For Extreme Sales Results
Sales Management For Extreme Sales ResultsSales Management For Extreme Sales Results
Sales Management For Extreme Sales ResultsCallidus Software
 
Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016
Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016
Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016Mindtrek
 
Uk best sme_mobile_health_app_-_therapy_box
Uk best sme_mobile_health_app_-_therapy_boxUk best sme_mobile_health_app_-_therapy_box
Uk best sme_mobile_health_app_-_therapy_box3GDR
 
Degrees don't matter dude. Learning does
Degrees don't matter dude. Learning doesDegrees don't matter dude. Learning does
Degrees don't matter dude. Learning doesZubin Poonawalla
 
Catalogo de filtros2015 2016
Catalogo de filtros2015 2016Catalogo de filtros2015 2016
Catalogo de filtros2015 2016COLSAISA S.A.S
 
0771. TAJNO ORUŽJE
0771. TAJNO ORUŽJE0771. TAJNO ORUŽJE
0771. TAJNO ORUŽJETompa *
 
Libellus 004. čOvjek Iz Gvajane
Libellus 004. čOvjek Iz GvajaneLibellus 004. čOvjek Iz Gvajane
Libellus 004. čOvjek Iz GvajaneTompa *
 
7 Salesforce Reports Every Inside Sales Manager Should Be Pulling
7 Salesforce Reports Every Inside Sales Manager Should Be Pulling7 Salesforce Reports Every Inside Sales Manager Should Be Pulling
7 Salesforce Reports Every Inside Sales Manager Should Be PullingInsideSales.com
 
Unitats de informacio
Unitats de informacioUnitats de informacio
Unitats de informacioAlex Ramon
 

Viewers also liked (17)

Sistema informatic
Sistema informaticSistema informatic
Sistema informatic
 
INSIDE SALES
INSIDE SALES INSIDE SALES
INSIDE SALES
 
Ecological situetion
Ecological situetionEcological situetion
Ecological situetion
 
Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1
Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1
Eight steps-for-efficient-pcb-manufacturing-and-assemblypart2-1
 
Sales Management For Extreme Sales Results
Sales Management For Extreme Sales ResultsSales Management For Extreme Sales Results
Sales Management For Extreme Sales Results
 
Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016
Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016
Sami Moisio - Physical and Virtual Worlds Are Converging - Mindtrek 2016
 
Uk best sme_mobile_health_app_-_therapy_box
Uk best sme_mobile_health_app_-_therapy_boxUk best sme_mobile_health_app_-_therapy_box
Uk best sme_mobile_health_app_-_therapy_box
 
Androi studio
Androi studioAndroi studio
Androi studio
 
Degrees don't matter dude. Learning does
Degrees don't matter dude. Learning doesDegrees don't matter dude. Learning does
Degrees don't matter dude. Learning does
 
Transforming NOAA Water Prediction for a Water-Prepared Nation
Transforming NOAA Water Prediction for a Water-Prepared NationTransforming NOAA Water Prediction for a Water-Prepared Nation
Transforming NOAA Water Prediction for a Water-Prepared Nation
 
Catalogo de filtros2015 2016
Catalogo de filtros2015 2016Catalogo de filtros2015 2016
Catalogo de filtros2015 2016
 
PPC
PPCPPC
PPC
 
0771. TAJNO ORUŽJE
0771. TAJNO ORUŽJE0771. TAJNO ORUŽJE
0771. TAJNO ORUŽJE
 
Libellus 004. čOvjek Iz Gvajane
Libellus 004. čOvjek Iz GvajaneLibellus 004. čOvjek Iz Gvajane
Libellus 004. čOvjek Iz Gvajane
 
7 Salesforce Reports Every Inside Sales Manager Should Be Pulling
7 Salesforce Reports Every Inside Sales Manager Should Be Pulling7 Salesforce Reports Every Inside Sales Manager Should Be Pulling
7 Salesforce Reports Every Inside Sales Manager Should Be Pulling
 
Unitats de informacio
Unitats de informacioUnitats de informacio
Unitats de informacio
 
Tablet coating power point
Tablet coating power pointTablet coating power point
Tablet coating power point
 

Similar to phempt paper 7.1

Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...
Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...
Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...Kal Tar
 
Insulation and Dielectric Breakdown Design Paper SM54
Insulation and Dielectric Breakdown Design Paper SM54Insulation and Dielectric Breakdown Design Paper SM54
Insulation and Dielectric Breakdown Design Paper SM54Subhash Mahla
 
SmartKem : Organic Semiconductors for Flexible Displays
SmartKem : Organic Semiconductors for Flexible DisplaysSmartKem : Organic Semiconductors for Flexible Displays
SmartKem : Organic Semiconductors for Flexible Displaysdublin44
 
CNT embedded MOS DEVICES for Memory Application
CNT embedded MOS DEVICES for Memory ApplicationCNT embedded MOS DEVICES for Memory Application
CNT embedded MOS DEVICES for Memory ApplicationSoumit Bose
 
Composites in electrical and electronic applications
Composites in electrical and electronic applicationsComposites in electrical and electronic applications
Composites in electrical and electronic applicationsgirish_raghunathan4488
 
Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...
Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...
Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...chrisrobschu
 
Power quality presentation by jmv lps
Power quality presentation by jmv lpsPower quality presentation by jmv lps
Power quality presentation by jmv lpsMahesh Chandra Manav
 
S-Band Radar LDMOS Transistors EuMW2009
S-Band Radar LDMOS Transistors EuMW2009S-Band Radar LDMOS Transistors EuMW2009
S-Band Radar LDMOS Transistors EuMW2009Steven Theeuwen
 
ECE 6030 Device Electronics.docx
ECE 6030 Device Electronics.docxECE 6030 Device Electronics.docx
ECE 6030 Device Electronics.docxwrite31
 
composites applications in electrical and electronics
composites applications in electrical and electronicscomposites applications in electrical and electronics
composites applications in electrical and electronicsgirish_raghunathan4488
 
Introduction gadgets have gained a lot of attention.pdf
Introduction gadgets have gained a lot of attention.pdfIntroduction gadgets have gained a lot of attention.pdf
Introduction gadgets have gained a lot of attention.pdfbkbk37
 
Training Course NX-Air Intro & Safety
Training Course NX-Air Intro & SafetyTraining Course NX-Air Intro & Safety
Training Course NX-Air Intro & SafetyNiels Inderbiethen
 
VPI for turbo generator
VPI for turbo generatorVPI for turbo generator
VPI for turbo generatorRajuEEE
 
Planarized, Extendible, Multilayer Fabrication
Planarized, Extendible, Multilayer FabricationPlanarized, Extendible, Multilayer Fabrication
Planarized, Extendible, Multilayer FabricationAlexander Cohen
 
Jmv presentation smart process plant (fertilizer)
Jmv  presentation  smart process  plant (fertilizer)Jmv  presentation  smart process  plant (fertilizer)
Jmv presentation smart process plant (fertilizer)Mahesh Chandra Manav
 
High voltage graphene nanowall trench mos barrier schottky diode characteriza...
High voltage graphene nanowall trench mos barrier schottky diode characteriza...High voltage graphene nanowall trench mos barrier schottky diode characteriza...
High voltage graphene nanowall trench mos barrier schottky diode characteriza...Conference Papers
 

Similar to phempt paper 7.1 (20)

Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...
Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...
Al gan gan hfe_ts with new ohmic and schottky contacts for thermal stability ...
 
Insulation and Dielectric Breakdown Design Paper SM54
Insulation and Dielectric Breakdown Design Paper SM54Insulation and Dielectric Breakdown Design Paper SM54
Insulation and Dielectric Breakdown Design Paper SM54
 
SmartKem : Organic Semiconductors for Flexible Displays
SmartKem : Organic Semiconductors for Flexible DisplaysSmartKem : Organic Semiconductors for Flexible Displays
SmartKem : Organic Semiconductors for Flexible Displays
 
project
projectproject
project
 
CNT embedded MOS DEVICES for Memory Application
CNT embedded MOS DEVICES for Memory ApplicationCNT embedded MOS DEVICES for Memory Application
CNT embedded MOS DEVICES for Memory Application
 
Composites in electrical and electronic applications
Composites in electrical and electronic applicationsComposites in electrical and electronic applications
Composites in electrical and electronic applications
 
Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...
Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...
Fabrication and Rate Performance of a Microfiber Cathode in a Mg–H2O2 Flowing...
 
Cp1
Cp1Cp1
Cp1
 
Power quality presentation by jmv lps
Power quality presentation by jmv lpsPower quality presentation by jmv lps
Power quality presentation by jmv lps
 
Lightning arresters
Lightning arrestersLightning arresters
Lightning arresters
 
S-Band Radar LDMOS Transistors EuMW2009
S-Band Radar LDMOS Transistors EuMW2009S-Band Radar LDMOS Transistors EuMW2009
S-Band Radar LDMOS Transistors EuMW2009
 
10b
10b10b
10b
 
ECE 6030 Device Electronics.docx
ECE 6030 Device Electronics.docxECE 6030 Device Electronics.docx
ECE 6030 Device Electronics.docx
 
composites applications in electrical and electronics
composites applications in electrical and electronicscomposites applications in electrical and electronics
composites applications in electrical and electronics
 
Introduction gadgets have gained a lot of attention.pdf
Introduction gadgets have gained a lot of attention.pdfIntroduction gadgets have gained a lot of attention.pdf
Introduction gadgets have gained a lot of attention.pdf
 
Training Course NX-Air Intro & Safety
Training Course NX-Air Intro & SafetyTraining Course NX-Air Intro & Safety
Training Course NX-Air Intro & Safety
 
VPI for turbo generator
VPI for turbo generatorVPI for turbo generator
VPI for turbo generator
 
Planarized, Extendible, Multilayer Fabrication
Planarized, Extendible, Multilayer FabricationPlanarized, Extendible, Multilayer Fabrication
Planarized, Extendible, Multilayer Fabrication
 
Jmv presentation smart process plant (fertilizer)
Jmv  presentation  smart process  plant (fertilizer)Jmv  presentation  smart process  plant (fertilizer)
Jmv presentation smart process plant (fertilizer)
 
High voltage graphene nanowall trench mos barrier schottky diode characteriza...
High voltage graphene nanowall trench mos barrier schottky diode characteriza...High voltage graphene nanowall trench mos barrier schottky diode characteriza...
High voltage graphene nanowall trench mos barrier schottky diode characteriza...
 

phempt paper 7.1

  • 1. A 0.5-µm InGaP Etch Stop Power pHEMT Process Utilizing Multi-Level High Density Interconnects Walter A. Wohlmuth, Li Liu, Larry Witkowski, Rick Morton, Thorsten Saeger, Wolfgang Liebl, Mike Fredd, Domingo Farías, Wayne Struble, Calvin Weichert, John Walkky, Steve Mahon, Otto Berger TriQuint Semiconductor, 2300 N.E. Brookwood Pkwy., Hillsboro, OR 97124, wwohlmuth@tqs.com, 503-615-9236 Keywords: pHEMT, InGaP, BCB, D-mode Abstract A robust and highly manufacturable InGaP etch stop pHEMT process with 0.5-µm gate lengths on 150 mm substrates is presented. The process utilizes a double recess approach to realize high breakdown, depletion-mode transistors with a nominal gate to drain breakdown voltage of 17 V. The transistors feature a nominal pinch-off voltage of –800 mV, on- resistance of 1.8 ohm-mm, extrinisic transconductance of 350 mS/mm, off-capacitance of 0.3 pF/mm, unity current gain cut- off frequency of 25 GHz, maximum frequency of oscillation of 90 GHz, and IDSS and IMAX values of 200 and 500 mA/mm, respectively. Passive components include precision 50 ohm/square NiCr resistors, 280 ohm/square epitaxial N- resistors, and 0.63 fF/um2 MIM capacitors. These devices are integrated with TriQuint’s high density, planarized, interconnect architecture enabling tremendous wiring flexibility and packaging simplicity. The interconnect structure utilizes benzocyclobutene (BCB) inter-metal dielectrics to form two levels of thick, global interconnects in addition to one level of local interconnect. This process, named TQPHT, is offered to external customers through TriQuint Foundry Services for a wide variety of applications including in part: high performance GSM, CDMA, and WLAN switches, medium power amplifiers, and low-noise amplifiers. INTRODUCTION In this paper we discuss the development of a 0.5-µm InGaP etch stop pHEMT process on 150 mm wafers at TriQuint Oregon. The development was driven by two primary factors. The first factor was to transfer the 0.5-µm AlAs etch stop power pHEMT process on 100 mm wafers from Texas to Oregon fabrication facilities of TriQuint converting directly to 150 mm wafers. This facilitated a high volume, low cost solution available to both internal designers and external customers through Foundry services. The second factor involved the optimization of the process and epitaxy technology for the creation of high performance GSM, CDMA, and WLAN switch components, low-noise amplifiers, and medium power amplifiers for both internal and external customers. The technology transfer and development also involved converting the interconnect architecture to one that employs low-dielectric constant materials based on benzocyclobutene. PROCESS ARCHITECTURE The process utilizes MBE on VGF, LEC, or VB substrates. The growth sequence begins with the formation of a superlattice buffer of alternating layers of GaAs and AlGaAs deposited on the substrate. Unintentionally-doped spacer layers of AlGaAs are placed on either side of the unintentionally-doped InGaAs channel with Silicon delta- doped layers placed on both sides of the channel-spacer layer stack. A transition layer of AlGaAs is placed between the lower spacer layer and the superlattice buffer to improve noise performance. A Schottky layer of AlGaAs is placed on top on the upper spacer layer to target the desired pinch-off voltage and transconductance. An InGaP etch stop layer is positioned on top of the Schottky layer followed by an upper AlGaAs layer and then N+ GaAs ohmic contact layers. An InGaP etch stop was used instead of an AlAs etch stop to reduce device on-resistance and to obtain extremely high etch selectivity [1]. The conduction band offset between the AlGaAs and InGaP material systems is significantly less than that between the AlAs and AlGaAs material systems, permitting the use of a thicker etch stop layer. Typical room temperature Hall measurements produced sheet carrier concentrations of 3.15E12 cm-2 and electron mobility in excess of 6500 cm2 /V•s. Fabrication begins with the definition of fiducials and wide recess openings. Upon formation of these features a blanket film of plasma-assisted chemical vapor deposited silicon dioxide (POX) is deposited to passivate and protect the surface from physical and chemical damage during subsequent process steps. Implant isolation is then performed. The ohmic contacts are formed within dry etched openings in the POX using AuGeNiAu alloyed at 400o C. Ohmic test is then performed to measure the ungated transistor current, the ohmic contact resistance, the N+ layer resistivity, and the N- layer resistivity. The typical ohmic contact resistance ranges from 0.10 to 0.15 ohm-mm due to process variations. The N- epitaxial resistors are formed utilizing the openings formed by the wide recess etch. Typical temperature coefficient of these resistors is 3000 ppm per degree centigrade referenced to 25o C with nominal sheet resistance of 280 ohm/square. The gate feature is created utilizing a TiPtAu metallization that is placed within dry
  • 2. etched openings in the POX. The narrow recess into the AlGaAs material utilizes NH4OH:H2O2:H2O chemistry, which provides excellent etch selectivity over InGaP and is a standard wet etch chemistry used for MESFET processes at TriQuint [2]. The InGaP etch stop is removed in HCl:H2O, which has a high etch selectivity with respect to AlGaAs [1]. The gate metal is deposited and lifted off. Immediately after gate formation a blanket coating of plasma-assisted chemical vapor deposited silicon nitride (PSN) is deposited prior to Nickel-Chromium (NiCr) thin film, high-precision resistor formation. These resistors have a temperature coefficient that is less than 100 ppm/o C, referenced to 25o C, over the –40 to +125o C temperature range, and possess a sheet resistance of 50 +/- 3 ohm/square. The maximum current and voltage ratings of the NiCr resistors are 1.0 mA/µm and 50 mV/µm, respectively. Another blanket coat of PSN is applied after precision resistor formation for physical and chemical protection of the NiCr prior to interconnect formation. The first interconnect metal (Metal0) consists of TiPtAu metallization and is used primarily as a local interconnect to the device contacts of the transistors, varactors, resistors, and Schottky diodes. This metal is also used as the bottom plate of a high precision MIM capacitor. Another PSN layer is then deposited to serve as the MIM capacitor dielectric prior to the formation of the top plate of the MIM capacitor using a TiPtAu metallization. The MIM dielectric is formed with a 100 nm thick PSN film possessing a relative permittivity of 6.8 and giving a capacitance per unit area of 0.63 +/- 0.10 fF/um2 . A final layer of PSN is deposited prior to proceeding with the upper layers of global interconnects. The interconnect architecture proceeds with the application of a planarizing, interlevel dielectric composed of benzocyclobutene (BCB). This dielectric is formed using conventional spin-on techniques and then cured at low temperature. Once cured, the material is mechanically tough, exhibits less than 0.25% water absorption, and has a relative permittivity of approximately 2.7. Inter-level vias are formed using an Helicon plasma etch system. The vias are electroplated along with metallic global interconnects. Patterned field metal is used to delineate the global interconnect metallic features. A thin dielectric layer of PSN separates the BCB layers and encapsulates the metal1 features. Upon completion of Via1 and Metal1 a second set of global interconnects are formed, Via2 and Metal2. The substrate is then coated with a final passivation PSN layer and bondpad via openings are formed to access test points on devices and circuits. A representative schematic cross- section of the process architecture is displayed in Figure 1. The nominal thickness of Metal1 and Metal2 are 2.0 and 4.0 µm, respectively. The first layer of BCB is nominally 1.0 µm thick and the second layer is nominally 2.8 µm thick. The final passivation PSN is a total of 0.8 µm thick. Figure 1: Schematic cross-section of the TQPHT process A STEM image of a portion of the transistor and interconnect architecture is displayed in Figure 2. ILD PSN1 BCB1 Base dielectrics BCB2 Metal0 Ohmic Gate Figure 2: STEM cross-section of pHEMT process. The excellent degree of planarization of the BCB can clearly be seen over the gate, ohmic, and metal0 features. The base dielectrics are composed of a combination of POX and PSN. Also evident are the wide and narrow recess ledges. Upon completion of front-side processing, the wafers can be treated in a number of ways. These options include: thinning the substrate down to thickness of 4, 7, or 10 mils; sawing out die; and/or substrate via formation. Detailed and thorough process qualification has been completed and passed at wafer level and on packaged products. The wafer level reliability testing included autoclave at 121o C, 100% relative humidity, and 15 psi for 96 hours, high temperature unbiased bake at 275o C in air for 168 hours, and temperature cycle from –40 to +125o C for 1000 cycles. The packaged product reliability testing included HTOL under bias and at 150o C junction temperature, preconditioning, autoclave, HAST at 130o C with 85% relative humidity for 96 hours, temperature cycle, thermal shock, and CDM and HBM ESD testing.
  • 3. DEVICE AND CIRCUIT PERFORMANCE The D-mode transistor pinch-off voltage (Vp) is centered at –800 mV with a process window of +/- 200 mV. The IDSS (Vgs=0.0V) corresponding the centered pinch-off voltage is 200 mA/mm while the IMAX (Vgs=+1.0V) is 500 mA/mm. The use of wet etch processes rather than dry etch processes produces transistors with very high channel current for a given Vp and gate length, as well as nicely formed transconductance (Gm) curves as a function of Vgs variation. A representative extrinsic Gm and Ids curve as a function of Vgs at a fixed Vds of 3.0 V is displayed in Figure 3. 0 50 100 150 200 250 300 350 400 450 500 0 50 100 150 200 250 300 350 -1.5 -1 -0.5 0 0.5 1 Vgs (V) Ids Gm Figure 3: Gm and Ids vs Vgs relationship. The transconductance has a good plateau in peak value over a wide range of Vgs values and does not exhibit any spurious inflection points or additional peaks. The unity current gain cut-off frequency (ft) is displayed in Figure 4 for Vds equal to 1.5 and 3.0 V as a function of Vgs. 0 5 10 15 20 25 30 35 -0.6 -0.4 -0.2 0 0.2 0.4 0.6 Vgs (V) Vds=1.5V Vds=3.0V Figure 4: Ft as a function of Vgs for a nominal D-mode pHEMT. The noise performance of the D-mode transistors was evaluated and is displayed in Figure 5. Noise figure (Fmin) below 0.3 dB with associated gain of 15 dB is obtained at a frequency of 2 GHz. The process is suitable for LNAs in the L, C, and S frequency bands. 0 0.5 1 1.5 2 0 2 4 6 8 10 12 14 16 18 0 2 4 6 8 10 12 Frequency (GHz) Fmin Ga Figure 5: Noise figure and associated gain of the D-mode pHEMT. Detailed load-pull measurements were performed with representative data presented in Figure 6 as a function of input power (Pin). The data is from a 300 µm device biased at Vds=8.0V and Ids=IDSS/2 at 1.9 GHz under continuous wave operation. Peak values of gain, power added efficiency (Efficiency), and output power (Pout) were determined to be 29 dB, 64%, and 530 mW/mm, respectively, for a given source and load tuning. Excellent operation was obtained up to Vds=17 V with output power increasing to beyond 1000 mW/mm. The results indicate that the process can support general purpose amplifiers in applications including CATV and VSAT for satellite communications. 0 5 10 15 20 25 30 0 10 20 30 40 50 60 70 -20 -15 -10 -5 0 5 Pin (dBm) Pout Gain Efficiency Figure 6: Load-pull data of a D-mode pHEMT at 1900 MHz vs Pin.
  • 4. A high power GSM switch for quad-band cellular modules has been demonstrated in this process. The switch is able to accommodate many different systems such as GSM, E-GSM, PCS, and DCS and is leading a shift away from the conventional PIN diodes as the selected component to switch RF signals at the transmit/receive antenna port. PIN diodes have high insertion loss and require high bias current relative to pHEMT transistors enabling pHEMTs to become the technology of choice for cellular phone handsets. The insertion loss, 2nd harmonic (H2) suppression, and 3rd harmonic (H3) suppression levels for a single pole six throw (SP6T) transmit/receive switch is displayed in Figure 7 at a control voltage of 2.5V and a frequency of 915 MHz. SP6T TQ4M4006 TX1 (Vctrl=2.5v F=915MHz) -120 -110 -100 -90 -80 -70 -60 -50 -40 -30 -20 26 27 28 29 30 31 32 33 34 35 36 Input Power (dBm) Harmonics(dBc) -2.0 -1.8 -1.6 -1.4 -1.2 -1.0 -0.8 -0.6 -0.4 -0.2 0.0 InsertionLoss(dB) H2H3 Loss Figure 7: Harmonics suppression and insertion loss of a SP6T GSM switch at 2.5V control voltage. This switch component is used for 850 MHz GSM, 900 MHz GSM, 1800 MHz DCS, and 1900 MHz PCS systems with separate arms for each receive band with the transmit arms combining the GSM signals and the DCS and PCS signals separately. State-of-the-art insertion loss and harmonic suppression levels are achieved with this circuit. A high power antenna switch in a single pole three throw configuration has also been demonstrated in this process. This switch is ideally suited to applications where the antenna of a CDMA handset is to be routed to the Cellular duplexer, the PCS duplexer and the GPS receiver input. The switch provides optimized input 3rd order intercept point (IP3) and cross modulation for use in CDMA applications. The input IP3 and current for a single pole three throw switch is displayed in Figure 8 at a control voltage of 2.5 V and a frequency of 837 MHz. World class single tone desense and ESD robustness levels are achieved with this circuit. TQP4M3007 CDMA SP3T Tx to Antenna IIP3 (Vctrl = 2.7 V, T= 25 C) Tx tones at 837 and 838 MHz 60 62 64 66 68 70 72 74 76 78 80 22.0 23.0 24.0 25.0 26.0 Total Tx Input Power (dBm) IIP3(dBm) 0 5 10 15 20 25 30 35 40 45 50 Current(uA) Figure 8: Input IP3 and control current for SP3T CDMA switch at 2.7V control voltage. CONCLUSIONS A detailed description of the TQPHT process architecture has been presented along with representative device and circuit performance. This robust and highly manufactureable process can be used for a wide variety of applications. REFERENCES [1] A. W. Hanson et al., GaAs IC Technical Digest, pp. 195-197, Nov. 1998. [2] E. P. Finchem et al. GaAs MANTECH Technical Digest, pp. 163-166. April 1994. ACRONYMS CATV: cable television amplifiers CDM: charge device model CDMA: coded division multiple access DCS: digital communication system E-GSM: enhanced global system for mobile communications ESD: electrostatic discharge GSM: global system for mobile communications HAST: highly accelerated stress testing HBM: human body model HTOL: high temperature operating life LEC: liquid encapsulated Czochralski LNA: low-noise amplifiers MESFET: metal-semiconductor field-effect transistor PCS: personal communication system PHEMT: pseudomorphic high-electron mobility transistor STEM: scanning transmission electron microscopy VB: vertical Bridgeman VGF: vertical gradient freeze VSAT: very small antenna terminals WLAN: wireless local area network